JP3128652B2 - Stress buffer material and protective equipment using the same - Google Patents
Stress buffer material and protective equipment using the sameInfo
- Publication number
- JP3128652B2 JP3128652B2 JP02238253A JP23825390A JP3128652B2 JP 3128652 B2 JP3128652 B2 JP 3128652B2 JP 02238253 A JP02238253 A JP 02238253A JP 23825390 A JP23825390 A JP 23825390A JP 3128652 B2 JP3128652 B2 JP 3128652B2
- Authority
- JP
- Japan
- Prior art keywords
- stress
- putty
- buffer
- protector
- bouncing putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 《発明の目的》 〈産業上の利用分野〉 本発明は例えば各種衝撃保護具やサポータなど、一部
に急激な応力が掛かるものに適用できる応力緩衝素材に
関する。DETAILED DESCRIPTION OF THE INVENTION <Purpose of the Invention><Industrial application field> The present invention relates to a stress buffer material that can be applied to a part to which a sudden stress is applied, such as various types of impact protectors and supporters.
〈発明の背景〉 従来使用されていた緩衝材にはゴム、弾性プラスチッ
クス、スポンジ等がある。しかしこれら素材はいずれも
弾性は有するものの、その形状が固定されているため、
これら素材を使用した保護具などでは保護部位の凹凸加
減によってはフィット感が得られず、保護部位と保護具
との形状の相違から保護部位が摩れたり、その部分に違
和感を感じる場合などがあった。<Background of the Invention> Conventionally used cushioning materials include rubber, elastic plastics, and sponge. However, although these materials have elasticity, their shapes are fixed,
With protective equipment using these materials, a fit cannot be obtained depending on the degree of unevenness of the protective part, and the protective part may be worn out due to the difference in shape between the protective part and the protective equipment, or the part may feel uncomfortable. there were.
一方、遅い応力変化には極めて柔軟に変形するもの
の、早い応力変化には強い抵抗を示す素材としてバウン
シングパテが知られている。この素材はその物性からし
て緩衝材として優れていることが予想されるが、自己保
形性が弱いため、例えばこのものをそのままサポータの
内部素材として使用する場合には、一旦は保護部位の凹
凸にフィットするものの、再度サポータを同じ部位に装
着する際には、その間にパテが重力に従って流動してし
まい、再度サポータを保護部位にフィットさせるのに時
間を要したり、場合によっては流動したパテを手でほぼ
均一状態に直してから装着しなければならないというこ
とも予想された。またバウンシングパテは、緩衝材とし
て利用するには、そのもの自体の重量が重いこと、価格
が高いことという欠点も有している。そこで、このよう
な不都合があるがために、バウンシングパテは優れた特
性を持ちながらも現実には緩衝材としての実用化はなさ
れておらず、実際には子供用の玩具やレオロジー測定用
の研究用教材としてしか使用されていなかった。On the other hand, a bouncing putty is known as a material which deforms very flexibly with a slow stress change but shows a strong resistance to a fast stress change. Although this material is expected to be excellent as a cushioning material due to its physical properties, it has poor self-preserving properties. Although it fits the irregularities, when the supporter is attached to the same site again, the putty flows according to the gravity during that time, and it takes time to fit the supporter again to the protection site, or it may flow in some cases It was also expected that the putty would have to be fixed by hand before being put on. In addition, the bouncing putty has disadvantages that it is heavy in weight itself and expensive in order to be used as a cushioning material. Therefore, due to these inconveniences, bouncing putty has excellent characteristics but has not been practically used as a cushioning material in practice, and is actually used for research on toys for children and rheology measurement. It was used only as a teaching material.
〈開発を試みた技術的事項〉 本発明はこのような背景に鑑みなされたものであっ
て、自己保形性が弱いため、そのままでは緩衝材として
適用できないバウンシングパテに一定の混入物を加えれ
ば、遅い応力変化には柔軟に変形し、早い応力変化には
高い弾性乃至剛性に近い性質を有するというバウンシン
グパテの特徴的利点を失うことなく、自己保形性を有す
るように成ることに着目し、このものを利用して実用可
能な応力緩衝素材並びにこれを用いた保護具の開発を試
みたものである。<Technical matters attempted to be developed> The present invention has been made in view of such a background, and because a self-retaining property is weak, if a certain contaminant is added to a bouncing putty that cannot be used as a cushioning material as it is. Attention is paid to the fact that it becomes self-retaining without losing the characteristic advantage of bouncing putty that it deforms flexibly for slow stress changes and has high elasticity or near rigidity for fast stress changes. The use of this material has been attempted to develop a practically usable stress buffering material and a protective device using the same.
《発明の構成》 〈目的達成の手段〉 本出願に係る第一の発明たる応力緩衝素材は、遅い応
力変化にはきわめて柔軟に変形するが、早い応力変化に
は強い抵抗を示して高い弾性乃至剛性に近い性質を有す
る変形自在なパテ状物質であるパウンシングパテに、自
己保形性を与えるための有弾性微小中空球体を混入した
ことを特徴として成るものである。<< Structure of the Invention >><Means for Achieving the Object> The stress buffering material according to the first invention of the present application deforms very flexibly for a slow stress change, but exhibits a high resistance to a fast stress change and has high elasticity. The present invention is characterized in that elastic fine hollow spheres for imparting self-retaining property are mixed into a pounding putty, which is a deformable putty-like substance having properties close to rigidity.
また本出願に係る第二の発明たる応力緩衝素材を用い
た保護具は、衝撃等の応力を受ける箇所に、遅い応力変
化にはきわめて柔軟に変形するが、早い応力変化には強
い抵抗を示して高い弾性乃至剛性に近い性質を有する変
形自在なパテ状物質であるバウンシングパテに、自己保
形性を与えるための有弾性微小中空球体を混入したもの
を封入した緩衝部を形成したことを特徴として成るもの
である。In addition, the protector using the stress buffering material according to the second invention of the present application shows that a portion receiving a stress such as an impact deforms very flexibly in a slow stress change, but shows a strong resistance to a fast stress change. The cushioning part is formed by enclosing a bouncing putty, which is a deformable putty-like substance having properties close to high elasticity or rigidity, mixed with elastic micro hollow spheres for giving self-retaining property. It consists of.
更に本出願に係る第三の発明たる応力緩衝素材を用い
た保護具は、前記要件に加えて前記緩衝部がサポータの
一部に形成されることを特徴として成るものである。Further, the protective device using the stress buffer material according to the third invention of the present application is characterized in that, in addition to the above requirements, the buffer portion is formed in a part of the supporter.
更に本出願に係る第四の発明たる応力緩衝素材を用い
た保護具は、前記要件に加えて前記緩衝部が頸椎保護具
の一部に形成されることを特徴として成るものである。Further, the protective device using the stress buffer material according to the fourth invention of the present application is characterized in that, in addition to the above requirements, the buffer portion is formed in a part of the cervical vertebra protective device.
これら発明によって前記目的を達成しようとするもの
である。The present invention aims to achieve the above object.
〈発明の作用〉 本発明では、バウンシングパテに有弾性微小中空球体
を混入することにより、自己保形性を有するようにな
り、しかもバウンシングパテに比べて比重の小さな素材
が得られる。<Effect of the Invention> In the present invention, by mixing the elastic hollow microspheres into the bouncing putty, the bouncing putty has a self-retaining property, and a material having a lower specific gravity than the bouncing putty can be obtained.
またこのような応力緩衝素材をサポータの緩衝部に適
用することにより、サポータを装着する際には、緩衝部
が保護部位の凹凸加減にしたがって保護部位に加わる外
力を平均するように封入体内を流動して保護部位にフィ
ットする。そして格別に応力分布に変化がないか、掛か
っていた外力がなくなった状態では、重力による流動を
生じることなく、一旦賦形された形状を保持する。一
方、衝撃等の早い応力が掛かった場合には、応力緩衝素
材が高い弾性乃至剛性に近い性質を示し、保護部位を適
度にホールドするとともに、衝撃が大きな受圧面に分散
するようにして保護部位を保護する。In addition, by applying such a stress buffer material to the buffer part of the supporter, when mounting the supporter, the buffer part flows through the enclosure so that the external force applied to the protection part is averaged according to the unevenness of the protection part. To fit the protection site. Then, when there is no particular change in the stress distribution or when there is no applied external force, the shape once formed is maintained without causing flow due to gravity. On the other hand, when a high stress such as an impact is applied, the stress buffering material exhibits a property of high elasticity or close to rigidity, holds the protection portion appropriately, and disperses the impact on a large pressure receiving surface to protect the protection portion. To protect.
〈実施例〉 以下本発明を図示の実施例に基づいて具体的に説明す
る。符号1は本発明たる応力緩衝素材を用いた保護具た
るサポータであって、一例として第1、4図では足首A
に使用した状態を示す。このものは横長の布製の基材2
に対して、実質的に応力緩衝作用をなす緩衝部3を一例
としてサポータの長手方向に四列形成したものである。
尚、緩衝部3の形成される側の面をうら面と定義し、反
対側の面をおもて面と定義する。基材2のうら面の片側
の端部には、例えば鉤状の係止部を多数有する係止片5
が設けられ、この係止片5と表面がループ状に形成され
たおもて面との間で面ファスナが形成されている。また
緩衝部3には本発明の応力緩衝素材6たるバウンシング
パテ(bouncing putty)に有弾性微小中空球体を混入
したものを封入してある。<Example> Hereinafter, the present invention will be specifically described based on an illustrated example. Reference numeral 1 denotes a supporter as a protective device using the stress buffering material according to the present invention. As an example, in FIGS.
Shows the state used. This is a horizontally long cloth substrate 2
On the other hand, as an example, four rows are formed in the longitudinal direction of the supporter as an example of the buffer portions 3 which substantially perform the stress buffering action.
The surface on which the buffer portion 3 is formed is defined as the back surface, and the opposite surface is defined as the front surface. At one end of the back surface of the base material 2, for example, a locking piece 5 having a large number of hook-shaped locking portions
Are provided, and a hook-and-loop fastener is formed between the locking piece 5 and the front surface whose surface is formed in a loop shape. Further, the shock absorber 3 is formed by enclosing a bouncing putty, which is a stress buffering material 6 of the present invention, into which elastic hollow microspheres are mixed.
ここで応力緩衝素材6を構成するバウンシングパテと
有弾性微小中空球体について説明する。本発明における
バウンシングパテとは、米国特許第2541851号等に開示
されるもので、遅い応力変化にはきわめて柔軟に変形す
るが、早い応力変化には強い抵抗を示して高い弾性乃至
剛性に近い性質を有する変形自在なパテ状物質をいう。
このもののこのような性質は、親水性と疎水性の基が平
衡状態にあることに起因すると考えられる。このものの
構造は疎水性のメチル基等を有し、その大部分が架橋し
ているシリコーンの網状組織と、ホウ素混合物の粘着性
液体反応生産物及びメチルシリコーン等から成る組織と
の二層構造を有する。そして親水性反応生成物は、架橋
したシリコーンの隙間に相を作っている。またこのもの
の特有な性質は親水性と疎水性の両基の間での摩擦が大
きいことに起因すると考えられる。即ちこのものを例え
ば硬い面の上に落下させた時には、親水性の基と疎水性
の基との間の摩擦力が大きくはたらく結果、各分子がす
べることがないため、弾力性のある固体のような性質を
示し、更にハンマーで打つなどの鋭い衝撃下では一種の
剛性に近い性質を示すのである。その一方、徐々に圧力
が掛かると、摩擦力に勝ってホウ素成分が網状組織の網
目の間を流れ出ることができるため、きわめて柔軟に変
形するのである。バウンシングパテの成分の一例につい
て示すと以下のようになる。Here, the bouncing putty and the elastic micro hollow sphere constituting the stress buffer material 6 will be described. The bouncing putty in the present invention is disclosed in U.S. Pat.No. 2,254,851 and the like, and deforms very flexibly for a slow stress change, but shows strong resistance to a fast stress change and has a property close to high elasticity or rigidity. Is a deformable putty-like substance having
It is believed that such properties of this are due to the equilibrium between the hydrophilic and hydrophobic groups. The structure of this product has a two-layered structure consisting of a silicone network having hydrophobic methyl groups and the like, the majority of which is crosslinked, and a structure consisting of an adhesive liquid reaction product of a boron mixture and methyl silicone. Have. And the hydrophilic reaction product forms a phase in the interstices of the crosslinked silicone. It is also considered that the unique property of this is due to a large friction between both hydrophilic and hydrophobic groups. That is, when this is dropped on, for example, a hard surface, the frictional force between the hydrophilic group and the hydrophobic group works so much that each molecule does not slip, so that an elastic solid It exhibits such properties, and further exhibits a kind of rigidity under a sharp impact such as hitting with a hammer. On the other hand, when pressure is gradually applied, the boron component can flow out between the meshes of the network over the frictional force, so that the boron component deforms very flexibly. An example of the components of the bouncing putty is as follows.
ホウ素含有シロキサン 50〜80% 顔料+二酸化ケイ素 10〜30% ジオルガノポリシロキサン 0〜15% 高級脂肪酸 他 1% またバウンシングパテは、オルガノポリシロキサンを
ホウ素の混合物で処理することによって得られ、熱や触
媒のいずれか一方又は双方を適宜与えることによって連
続的に得られる。ここでホウ素の混合物はピロホウ酸、
無水ホウ酸、ホウ酸、エチルホウ酸塩、その他ホウ酸エ
ステル等を含むが、製品に望まれる特質によって特定の
ホウ素混合物を選択できる。Boron-containing siloxane 50-80% Pigment + silicon dioxide 10-30% Diorganopolysiloxane 0-15% Higher fatty acids, etc. 1% Also bouncing putty is obtained by treating organopolysiloxane with a mixture of boron, The catalyst is continuously obtained by appropriately providing one or both of the catalysts. Here, the mixture of boron is pyroboric acid,
Specific boron mixtures can be selected depending on the properties desired for the product, including boric anhydride, boric acid, ethyl borate, other borate esters, and the like.
以下バウンシングパテの製法の一例を示す。尚、製法
中使用されるオルガノポリシロキサンは、油性のメチル
シロキサンであり、このものはほぼ純粋なジメチルシリ
コーンハロゲン化合物の加水分解等によって得られ、そ
の構造は端部が(CH3)3SiO0.5で中間部が(CH3)2SiO
によって表わされるものである。まずジメチルシリコー
ンオイル75部(重量部を表す。以下同じ)とピロホウ酸
10部とを混合し、この混合物を150℃で2時間オーブン
で加熱する。加熱の終わり頃には混合物はある程度弾力
性のあるゲルになる。このゲル45部に対して90部のリト
ポン(白色顔料)と0.9部の過酸化ベンゾイルとを固ま
りになるまで混ぜ合わせるとともに、このものに更に45
部のジメチルシリコーンオイルと0.9部の過酸化ベンゾ
イルを加えて更に固まり状にする。固まったものを100
度乃至150度でオーブンで2時間熱する。このようにし
て出来上がったものを手の指でこねることによりパテ状
になり高い粘着性と反発力とを有するようになる。尚、
加水分解できるアルキルホウ酸塩又は同量の触媒を使う
とメチルシリコーンオイル中にホウ素混合物を分散させ
る場合に便利である。尚、ホウ素混合物の量や触媒量、
更には加熱時間等を変えることによって、親水性と疎水
性との成分割合が変化するので、その結果たる応力緩衝
素材の弾力性と柔軟性とをコントロールすることができ
るようになる。またグリセリンやオレイン酸等の親水性
や疎水性の物質を追加することによっても、その弾力性
や柔軟性を調整することができる。The following is an example of a method for producing a bouncing putty. The organopolysiloxane used in the production method is an oily methylsiloxane, which is obtained by hydrolysis of a substantially pure dimethylsilicone halogen compound or the like. The structure of the organopolysiloxane is (CH 3 ) 3 SiO 0.5 And the middle part is (CH 3 ) 2 SiO
Is represented by First, 75 parts of dimethyl silicone oil (representing parts by weight; the same applies hereinafter) and pyroboric acid
10 parts and the mixture is heated in an oven at 150 ° C. for 2 hours. At the end of the heating the mixture becomes a somewhat elastic gel. To 45 parts of this gel, 90 parts of lithopone (white pigment) and 0.9 parts of benzoyl peroxide are mixed until a solid mass is obtained.
Parts of dimethyl silicone oil and 0.9 parts of benzoyl peroxide are added to make a further mass. 100 solidified
Heat in oven at 2 degrees to 150 degrees. By kneading the finished product with the fingers of the hand, it becomes putty and has high adhesiveness and resilience. still,
The use of hydrolyzable alkyl borates or the same amount of catalyst is convenient for dispersing the boron mixture in methyl silicone oil. Incidentally, the amount of the boron mixture and the amount of the catalyst,
Further, by changing the heating time and the like, the component ratio between hydrophilicity and hydrophobicity changes, so that the elasticity and flexibility of the resulting stress buffer material can be controlled. The elasticity and flexibility can also be adjusted by adding a hydrophilic or hydrophobic substance such as glycerin or oleic acid.
次に有弾性微小中空球体は、例えばスウェーデン、エ
クスパンセル社が開発したエクスパンセル(登録商
標)、松本油脂製薬株式会社製造のマツモトマイクロス
フェアー(登録商標)に代表される粉体である。エクス
パンセルは1980年より製造されたビニリデンクロライド
とアクリロニトリルとのコポリマーを殻とし、膨張材と
してイソブタンを内包、カプセル化して作られた有機系
の微小中空球体である。エクスパンセルには未膨張(未
発泡)のものと、膨張済み(発泡済み)のものがある
が、膨張済みのものは平均粒度40μ、粒径範囲10〜100
μであり、未膨張のものが平均粒度10μ、粒径範囲5〜
30μであるのと比較して大きく、且つ膨張済みのものは
緩衝性に優れているため、本実施例では膨張済みの乾燥
したEXPANCEL−DE551を使用している。またエクスパン
セルは、殻壁が0.1μ程度で弾性があるので、荷重が掛
かると圧縮されるが、荷重を掛けるのをやめると元に戻
る性質を有するため、このものをバウンシングパテに混
入すると耐衝撃性や緩衝性が高まるのである。尚、エク
スパンセルは球体であるため他の充填材より遥かに優れ
た応力分布が得られる。またマツモトマイクロスフェア
ーは、大きく塩化ビニリデン共重合物を殻壁として低沸
点炭化水素を内包するものと、低沸点炭化水素を塩化ビ
ニリデンを含まない殻壁で内包するものとがあり、その
中でもF−80EDは、粒径範囲20〜80μの膨張済み(発泡
済み)のものであり、前出のEXPANCEL−DE551とほぼ同
等に用いることができる。これら有弾性微小中空球体は
バウンシングパテの調整いかんにもよるが、通常、バウ
ンシングパテ100(重量)部に対し、1部乃至10部が添
加混合される。尚、有弾性微小中空球体をバウンシング
パテに混入するには混練機等を用いて行なう。因みにバ
ウンシングパテは前述したようにそれ単体では自己保形
性が弱く、放置しておくと流動してしまうが、これに有
弾性微小中空球体を混入して応力緩衝素材6とすること
により、自己保形性を有するようになるため、このもの
を緩衝材として利用することが可能となるのである。ま
たバウンシングパテは、それ自体比較的比重が大きい
が、比重の小さな有弾性微小中空球体を混入することに
より、比較的比重の小さな応力緩衝素材6を得ることが
できるため、これを緩衝材として使用すれば、実用に適
した軽量な緩衝材を得ることができるのである。尚、バ
ウンシングパテにエクスパンセルやマツモトマイクロス
フェアー等を添加した応力緩衝素材6は、バウンシング
パテ単体の場合に比較して、フィルム封入品を製造する
場合にも優れた点を有する。即ち、二枚のフィルムの間
に応力緩衝素材6を挟み込んだ封入品を製造する場合に
は、一般的にはフィルム+応力緩衝素材+フィルムの三
層状のシートを、適宜枠形状の凹凸の金型を使用して上
下のフィルムを熱溶着して製造するが、この場合凹凸の
金型を上下から挟み込む時に、バウンシングパテにエク
スパンセルやマツモトマイクロスフェアー等を添加した
応力緩衝素材6では、バウンシングパテ単体に比べて切
れが良いため、熱溶着がしっかりと行なわれ、また量産
も可能になるのである。Next, the elastic micro hollow sphere is a powder represented by, for example, Expancel (registered trademark) developed by Expancel, Sweden, and Matsumoto Microsphere (registered trademark) manufactured by Matsumoto Yushi Pharmaceutical Co., Ltd. . EXPANCEL is an organic micro hollow sphere made from a copolymer of vinylidene chloride and acrylonitrile, produced in 1980, and encapsulated and encapsulated with isobutane as an expanding material. There are unexpanded (unexpanded) and expanded (expanded) types of EXPANCEL. The expanded type has an average particle size of 40μ and a particle size range of 10 to 100.
μ, the unexpanded one has an average particle size of 10 μ, and the particle size range is 5 to 5.
In this example, the expanded EXPANCEL-DE551 was used because it was larger than 30 μm, and the expanded one had excellent buffering properties. Expancel has a shell wall of about 0.1μ and has elasticity, so it is compressed when a load is applied.However, when this is mixed into a bouncing putty, it has the property of returning to its original state when the load is stopped. The impact resistance and the cushioning property are improved. Note that since the Expancel is a sphere, a stress distribution far superior to other fillers can be obtained. In addition, Matsumoto microspheres are classified into two types: those containing a vinylidene chloride copolymer as a shell wall and containing low-boiling hydrocarbons, and those containing low-boiling hydrocarbons in a shell wall containing no vinylidene chloride. -80ED is inflated (foamed) having a particle size range of 20 to 80 µ, and can be used almost in the same manner as EXPANCEL-DE551 described above. Depending on the adjustment of the bouncing putty, 1 to 10 parts of these elastic micro hollow spheres are usually added and mixed with 100 (weight) parts of the bouncing putty. The elastic micro hollow spheres are mixed into the bouncing putty using a kneader or the like. Incidentally, as described above, the bouncing putty itself has a weak self-preserving property and flows when left alone. However, by adding elastic hollow microspheres to the stress-buffering material 6, the bouncing putty is self-retained. Since it has shape retention properties, it can be used as a cushioning material. The bouncing putty itself has a relatively large specific gravity, but by mixing elastic micro hollow spheres having a small specific gravity, a stress buffer material 6 having a relatively small specific gravity can be obtained. Then, a lightweight cushioning material suitable for practical use can be obtained. In addition, the stress buffer material 6 which added Expancel, Matsumoto microspheres, etc. to a bouncing putty also has an excellent point in producing a film-enclosed product as compared with the case of a bouncing putty alone. That is, when manufacturing an encapsulated product in which the stress buffering material 6 is sandwiched between two films, generally, a three-layer sheet of film + stress buffering material + film is appropriately formed of a frame-shaped irregular metal. The upper and lower films are heat-sealed using a mold, but in this case, when the uneven mold is sandwiched from above and below, the stress buffering material 6 in which an expancel or Matsumoto microsphere is added to the bouncing putty, Since the cutting performance is better than that of a bouncing putty, heat welding is performed firmly and mass production is possible.
次に緩衝部3における封入状態について説明すると、
本実施例では第1、2、4図に示すように二枚のフィル
ム7の間に四列に応力緩衝素材6を設け、他の部分を熱
溶着したものである。またこのようにして形成される緩
衝部3の形態は、上記形態の他、第3図(a)に示すよ
うにサポータの長手方向と直角の向きに複数配列した
り、また第3図(b)に示すように長方形を複数組み合
わせるように形成したり、更には第3図(c)に示すよ
うに突起状のものを全体的に配置して形成するようにし
てもよい。また緩衝部3が形成されるうら面側にも補強
及び肌触り感を高めるため、布を張るようにしてもよ
い。Next, the sealing state in the buffer unit 3 will be described.
In this embodiment, as shown in FIGS. 1, 2, and 4, the stress buffer material 6 is provided in four rows between two films 7, and the other portions are heat-welded. Further, in addition to the above-described embodiments, the form of the buffer section 3 formed in this manner may be a plurality of arrangements in a direction perpendicular to the longitudinal direction of the supporter as shown in FIG. 3), a plurality of rectangles may be formed in combination, or further, as shown in FIG. 3 (c), protrusions may be formed as a whole. Further, a cloth may be stretched on the back surface side on which the buffer portion 3 is formed in order to reinforce and enhance the touch.
本発明たる応力緩衝素材を用いた保護具たるサポータ
1は以上のような構造を有するものであって、このもの
を使用する場合には第1、4図に示すように、例えば足
首に対してサポータのうら面側をあてた状態で巻き付
け、係止片5を基材2のおもて面に係止させる。このよ
うにした時には、足首の形状に応じて応力緩衝素材6が
緩衝部3内を移動するため足首にフィットするようにな
る。また足首に衝撃が掛かった場合には、応力緩衝素材
6が強い抵抗を示し、高い弾性乃至剛性に近い性質を持
つようになるため、足首が固定される状態となって捻挫
や骨折等が防止される。The supporter 1 as a protector using the stress buffering material according to the present invention has the above-mentioned structure. When this supporter is used, as shown in FIGS. The supporter is wrapped with the back side of the supporter facing, and the locking piece 5 is locked to the front surface of the substrate 2. In such a case, the stress buffer material 6 moves in the buffer portion 3 according to the shape of the ankle, and thus fits the ankle. Further, when an impact is applied to the ankle, the stress buffering material 6 exhibits strong resistance and has a property of high elasticity or close to rigidity, so that the ankle is fixed and a sprain or a fracture is prevented. Is done.
次に本発明たる応力緩衝素材を用いた保護具の他の実
施例として頸椎保護具10について説明する。このものは
第5図に示すように板状の可撓性材料を筒状にした際
に、首の回りにフィットするように形成された保護具本
体11と、この保護具本体11を首回りに巻いたときに、顎
の下部に位置する顎保持板12とを具えて成る。尚、頸椎
保護具10を首に取り付けた状態で首と接する側を保護具
本体11のうら面と定義し、反対側の面をおもて面と定義
する。保護具本体11の両端部には一組の面テープ13が設
けられ、これにより頸椎保護具10を首回りに巻いた状態
で固定できるようになっている。また顎保持板12は、ほ
ぼU字状に曲がった状態で保護具本体11に止め具14で固
定されている。このような頸椎保護具10において、保護
具本体11のうら面のうち頸椎乃至後頭部に当接する側の
全面と、胸から肩にかけて当接する縁の部分、及び顎保
護板12の顎に当接する側の全面には、それぞれ止め具14
で係止することにより緩衝部3が設けられる。この緩衝
部3は、前記サポータ1におけるものと同様、バウンシ
ングパテに有弾性微小中空球体を混入した応力緩衝素材
6を封入して成るものである。尚、封入してある応力緩
衝素材6が偏らないように、偏在防止接合部15を所々に
形成してある。Next, a cervical vertebra protector 10 will be described as another embodiment of the protector using the stress buffer material according to the present invention. This protector body 11 is formed so as to fit around a neck when a plate-like flexible material is formed into a tubular shape as shown in FIG. And a chin holding plate 12 positioned below the chin when wound around the chin. The side that comes into contact with the neck with the cervical spine protector 10 attached to the neck is defined as the back surface of the protector body 11, and the opposite surface is defined as the front surface. A pair of face tapes 13 is provided at both ends of the protector main body 11, so that the cervical vertebra protector 10 can be fixed while being wrapped around the neck. The chin holding plate 12 is fixed to the protector main body 11 with a stopper 14 while being bent in a substantially U-shape. In such a cervical vertebra protector 10, of the back surface of the protector main body 11, the entire surface in contact with the cervical vertebra or occipital region, the edge portion in contact from the chest to the shoulder, and the side in contact with the chin of the chin protection plate 12. Stoppers 14
The buffer portion 3 is provided by locking with. As in the case of the supporter 1, the buffer section 3 is formed by enclosing a stress buffering material 6 in which elastic micro hollow spheres are mixed in a bouncing putty. In addition, the uneven distribution preventing joint 15 is formed in some places so that the encapsulated stress buffer material 6 is not uneven.
本発明たる応力緩衝素材を用いた保護具たる頸椎保護
具10は以上述べたような構造を有するものであって、こ
のものを使用する場合には、面テープ13を外した状態で
前方から首に嵌め込むとともに顎保持板12の上に顎が保
持されるようにし、この状態で面テープ13を貼り付け
る。このようにした時には、首の形状に応じて応力緩衝
素材6が緩衝部3内を移動するため首にフィットするよ
うになる。また首に衝撃が掛かった場合には、応力緩衝
素材6が強い抵抗を示し、高い弾性乃至剛性に近い性質
を持つようになるため、首がしっかりと固定される状態
となるため、首が保護される。The cervical vertebra protector 10 as a protector using the stress buffering material according to the present invention has the above-described structure.When this protector is used, the neck from the front with the surface tape 13 removed is used. And the chin is held on the chin holding plate 12, and the surface tape 13 is attached in this state. In this case, the stress buffer material 6 moves in the buffer portion 3 according to the shape of the neck, so that the stress buffer material 6 fits the neck. In addition, when a shock is applied to the neck, the stress buffering material 6 exhibits a strong resistance and has a property of high elasticity or close to rigidity, so that the neck is firmly fixed and the neck is protected. Is done.
尚、以上の実施例は本発明をサポータの一部に適用し
たものであるが、その他にもバット、テニスラケット等
打球運動具のグリップ、グローブ等の把持部における掌
保護部位、野球用その他の捕球用グローブ、その他のグ
ローブ、格闘技用防具、ヘルメット、座席シート、ヘッ
ドレスト等のフィット性とホールド性と緩衝性とが要求
される部位の保護具としても適用できるものである。Although the above embodiment is an application of the present invention to a part of the supporter, in addition to the above, a bat, a grip of a hitting exercise device such as a tennis racket, a palm protection portion in a grip portion such as a glove, a baseball and other components The present invention can also be applied to a glove for catching a ball, other gloves, martial arts armor, a helmet, a seat, a headrest, and other parts that require fitting, holding, and cushioning properties.
《発明の効果》 本発明では、遅い応力変化に対して緩衝部が柔軟に変
形し、早い応力変化には強い抵抗を示し、且つ高い弾性
乃至剛性に近い性質を示す従来ないタイプの応力緩衝素
材6を保護具の緩衝部3に適用したから、保護具を取り
付ける時や通常の使用状態のときには、保護部位の形状
に応じて緩衝部3がフィットし、保護具との摩れを生じ
たり、違和感を感じたりすることがない。<< Effects of the Invention >> In the present invention, the buffer portion is flexibly deformed with respect to a slow stress change, exhibits a strong resistance to a fast stress change, and has a non-conventional type of stress buffering material exhibiting properties close to high elasticity or rigidity. 6 is applied to the cushioning part 3 of the protective equipment, the buffering part 3 fits according to the shape of the protective part when the protective equipment is attached or in a normal use state, and the friction with the protective equipment occurs. There is no feeling of discomfort.
また、ハウンシングパテの単体をそのまま緩衝材とし
て適用した場合とは異なり、一旦保護部位にフィットし
た形状は外力が掛からない限り保持し続けるから、応力
緩衝素材の偏りを均一化する手間が省けたり、フィット
するのに掛かる時間が短くなるため、次回以降のサポー
タの装着時にも初めからフィット感が得られる。Also, unlike the case where the single piece of the honing putty is used as a cushioning material as it is, the shape once fitted to the protection site is kept as long as no external force is applied, so that the work of equalizing the bias of the stress buffering material can be omitted. Since the time required for fitting is shortened, a feeling of fitting can be obtained from the beginning even when the supporter is mounted next time.
一方、保護具に衝撃等の応力が掛かった場合には、保
護部位がしっかりと固定されるとともに、応力緩衝素材
6が衝撃を柔らげるため、保護部位に力が掛かったり、
振動が伝わったりすることがない。On the other hand, when a stress such as an impact is applied to the protective device, the protection portion is firmly fixed, and the stress buffering material 6 softens the impact.
Vibration is not transmitted.
第1図は本発明の応力緩衝素材を用いた保護具の使用状
態を示す斜視図、第2図は同上裏面図、第3図は緩衝部
の形態を異ならせた種々の実施例を示す裏面図、第4図
は本発明の応力緩衝素材が足首に作用する状態を示す縦
断面図、第5図は本発明の応力緩衝素材を頸椎保護具に
適用した実施例を示す側面図である。 1;サポータ 2;基材 3;緩衝部 5;係止片 6;応力緩衝素材 7;フィルム 10;頸椎保護具 11;保護具本体 12;顎保持板 13;面テープ 14;止め具 15;偏在防止接合部 A;足首FIG. 1 is a perspective view showing a use state of a protector using the stress buffering material of the present invention, FIG. 2 is a rear view of the same, and FIG. 3 is a rear view showing various embodiments in which the form of a buffer portion is different. FIG. 4 is a longitudinal sectional view showing a state where the stress buffer material of the present invention acts on the ankle, and FIG. 5 is a side view showing an embodiment in which the stress buffer material of the present invention is applied to a cervical vertebra protector. 1; supporter 2; base material 3; buffer 5; locking piece 6; stress buffering material 7; film 10; cervical vertebra protector 11; protector body 12; chin support plate 13; surface tape 14; stopper 15; uneven distribution Prevention joint A; ankle
Claims (4)
が、早い応力変化には強い抵抗を示して高い弾性乃至剛
性に近い性質を有する変形自在なパテ状物質であるバウ
ンシングパテに、自己保形性を与えるための有弾性微小
中空球体を混入したことを特徴とする応力緩衝素材。1. A bouncing putty, which is a deformable putty-like substance having a high resistance or a property close to high elasticity and exhibiting a high resistance to a fast stress change while being extremely flexible against a slow stress change. A stress buffer material characterized by mixing elastic micro hollow spheres for giving shape.
化にはきわめて柔軟に変形するが、早い応力変化には強
い抵抗を示して高い弾性乃至剛性に近い性質を有する変
形自在なパテ状物質であるバウンシングパテに、自己保
形性を与えるための有弾性微小中空球体を混入したもの
を封入した緩衝部を形成したことを特徴とする応力緩衝
素材を用いた保護具。2. A deformable putty having high elasticity or near rigidity in a portion receiving stress such as an impact, which is very flexibly deformed for a slow stress change, but has a high resistance to a fast stress change. A protective device using a stress-buffering material, wherein a buffer portion is formed by enclosing a bouncing putty, which is a substance, into which elastic micro hollow spheres for imparting self-retaining properties are mixed.
ことを特徴とする請求項2記載の応力緩衝素材を用いた
保護具。3. The protective device according to claim 2, wherein said buffer portion is formed in a part of a supporter.
ることを特徴とする請求項2記載の応力緩衝素材を用い
た保護具。4. The protector using a stress buffer material according to claim 2, wherein said buffer portion is formed in a part of the cervical vertebra protector.