JP3126333B2 - Printing blanket - Google Patents

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

The present invention is suitable for use in a high-speed printing press such as a high-speed offset rotary printing press.
The present invention relates to a seamless printing blanket.

[0002]

2. Description of the Related Art As a printing blanket particularly suitable for the above-mentioned high-speed printing machine and the like, there is a cylindrical blanket having no seams in a circumferential direction. Such a cylindrical printing blanket has a porous and seamless compressible layer containing an elastomer such as rubber on the outer peripheral surface of a cylindrical sleeve mounted on a blanket cylinder shaft of a printing machine, or a non-stretchable elastic layer. By appropriately laminating a non-stretchable layer or the like formed by spirally winding the wire in the circumferential direction, and by laminating a seamless surface printing layer containing an elastomer such as rubber on the uppermost layer as well. Be composed.

Among the above, a so-called air type printing blanket having a porous compressible layer below the surface printing layer is, for example, as shown by a two-dot chain line in FIG.
The compressive stress at the nip deformation part caused by the pressure contact with the plate cylinder or the like is lower than that of the solid type having no compressible layer (shown by a broken line in the figure). The above air-type printing blanket when a distortion amount at the nip deformed portion, as shown in FIG changes from epsilon ₁ to epsilon _2, the variation of the compression stress P _a1 → P _a2 are those solid type _Is smaller than the variation P _s1 → P _s2 of the compressive stress at

[0004] Therefore, air-type printing blankets have good shock absorbing properties, and are excellent in the effect of preventing, for example, an impact or the like generated when a gear of a printing machine is fed from affecting printing accuracy. In addition, the solid type printing blanket causes a so-called bulge due to stress concentration on the surface printing layer at the nip deformed portion, misregistration due to circumferential elongation, poor paper feed, double, deformation of halftone dot pattern. There is a possibility that printing failures (especially thickening of halftone dots) may occur, but in the case of the air type, the above-mentioned printing failures occur because the compressive layer functions to reduce stress concentration on the surface printing layer. It also has the effect of preventing occurrence.

The above-mentioned compressible layer is made of, for example, (i) a foaming agent which decomposes upon heating to generate gas.
Foaming of the matrix rubber that constitutes the compressible layer, or
(ii) a mixture of hollow microparticles in a matrix rubber and the like, each pore having an independent pore structure, and (iii) a solvent (such as salt) that does not affect the rubber. In the case of water), particles extractable by a matrix rubber are dispersed in a matrix rubber, and after vulcanization, the above-mentioned particles are extracted, which is formed by a so-called leaching method. is there.

[0006]

However, in order to form a compressible layer, any of the above-mentioned structures requires a number of complicated steps. However, there is a problem that productivity is lower than that of the solid type. It is an object of the present invention to provide a novel printing blanket which has excellent productivity because it has a simpler structure than an air-type printing blanket and has excellent compression characteristics similar to an air-type printing blanket. Is to provide.

[0007]

According to the present invention, there is provided a printing blanket having a cylindrical shape with no seams in a circumferential direction, comprising (a) an elastomer and having a seam in a circumferential direction. (B) a non-stretchable layer formed by arranging hollow fibers having cavities therein in a certain direction, disposed below the surface print layer, and It is characterized by having at least.

[0008] In the printing blanket of the present invention having the above structure, the non-stretchable layer is formed by arranging hollow fibers having cavities therein in a predetermined direction as described above. Since the cavities act like the pores of a conventional compressible layer, the compressible layer can be omitted. Therefore, the printing blanket of the present invention has a simpler structure than the air-type printing blanket and thus has excellent productivity, and has excellent compression characteristics similar to those of the air-type printing blanket. .

[0009]

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a printing blanket of the present invention will be described with reference to the drawings showing an example of the embodiment. The printing blanket 1 of this example is formed on the outer peripheral surface of a cylindrical sleeve 10 as shown in FIG. 2, and as shown in FIG.
A base layer 11, a non-stretchable layer 12, and a surface printing layer 13 are laminated in this order.

The non-stretchable layer 12 is formed by spirally winding a single fiber hollow fiber HF1 on the base layer 11 in a circumferential direction. In the present invention, a hollow fiber HF2 in which a plurality of hollow fibers hf are integrated as shown in FIG. 1B may be used instead of the hollow fiber HF1. Examples of the hollow fiber HF2 include a fiber bundle in which a plurality of hollow fibers hf are converged and integrated in parallel without intentionally twisting, or a twisted yarn in which a plurality of hollow fibers hf are twisted. Can be

As the hollow fiber HF1 constituting the single fiber hollow fiber HF1 or the hollow fiber HF2, any of various conventionally known synthetic resin fibers having a cavity therein can be used. For example, the single fiber hollow fiber H
Both the hollow fiber Ff and the hollow fiber hf constituting the hollow fiber HF2 have a circular outer cross section, and only one hollow is provided at the center of the hollow fiber having a circular cross section continuously in the length direction. Each of the hollow fiber HF1 and the hollow fiber hf has an advantage that stress characteristics against compression become uniform.

However, the shape of the cross section of the outer diameter and the cross section of the cavity may be various shapes other than the circular shape. The number of internal cavities is not limited to one, and two or more cavities may be formed so as to be parallel to each other. Further, the cavities may be intermittent rather than continuous. Examples of the synthetic resin constituting the hollow fibers HF1 and HF2 include:
For example, polyester, rayon, nylon, aromatic polyamide, acrylic resin and the like can be mentioned.

Specific examples of such hollow fibers HF1 and HF2 are not limited to those described in, for example,
5028, JP-A-54-50620, JP-A-57-61717, JP-A-63-175110
Japanese Patent Application Laid-Open No. 3-90613, or "New Sup" (trade name, manufactured by Toyobo Co., Ltd.), and "RX2" (trade name, manufactured by Toyobo Co., Ltd.)
1, "Esmarble" (trade name, also manufactured by Toyobo Co., Ltd.), triangular hollow fiber for carpet, also manufactured by Toyobo Co., Ltd., triangular hollow fiber for carpet, manufactured by Asahi Kasei Corporation, carpet also manufactured by Asahi Kasei Corporation Square hollow fiber.

When the non-stretchable layer 12 is formed of a single fiber hollow fiber HF1, the outer diameter of the hollow fiber HF1 is
0.1 to 1.0 mm, preferably 0.25 to 1.0 mm.
More preferably, it is 0.7 mm. If the outer diameter of the hollow fiber HF1 is less than the above range, the size of the cavity formed therein is limited. Therefore, as shown in the example in the figure, the hollow fiber HF1 is wound by only one layer in the circumferential direction. Non-stretchable layer 12
When the non-stretchable layer 12 is formed, the porosity of the non-stretchable layer 12 becomes small, and the compression characteristics of the printing blanket may be reduced. Conversely, when the outer diameter of the hollow fiber HF1 exceeds the above range, the porosity of the non-stretchable layer 12 is large,
Compressive stress may be too low to provide sufficient blanketness to the printing blanket.

The inner diameter of the hollow in the single-fiber hollow fiber HF1 is appropriately determined according to the outer diameter, the arrangement of the hollow, and the like.
It may be set, but as shown in the figure, in the case of only one cavity formed at the center of the hollow fiber HF1, 0.05 to 0.
It is preferably 5 mm, more preferably 0.12 to 0.4 mm. If the inner diameter of the cavity is less than the above range, the compression properties of the printing blanket may be reduced as described above. Conversely, if the inner diameter of the cavity exceeds the above range, there is a possibility that a sufficient solid inking property cannot be imparted to the printing blanket as described above.

When two or more cavities are formed in the hollow fiber so as to be parallel to each other, the inner diameter of each cavity may be smaller than the above range. On the other hand, the non-stretchable layer 12
When a plurality of hollow fibers hf are formed by a hollow fiber HF2 converged in parallel or twisted, the outer diameter of the hollow fiber HF2 is 0.1 to 1.0 mm.
Is preferably, and more preferably, 0.25 to 0.7 mm.

When the outer diameter of the hollow fiber HF2 is less than the above range, the size of the cavity formed inside each hollow fiber hf is limited, although it depends on the number of the hollow fibers hf constituting the hollow fiber HF2. In particular, the hollow fiber HF2 is
When the non-stretchable layer 12 is formed by winding only the layer, the porosity of the non-stretchable layer 12 becomes small, and the compression property of the printing blanket may be reduced. On the other hand, when the outer diameter of the hollow fiber HF2 exceeds the above range, the porosity of the non-stretchable layer 12 is large, the compressive stress becomes too low, and the solidity of the blanket for printing is sufficient. May not be provided.

The hollow fiber hf constituting the hollow fiber HF2
The outer diameter and the number are not particularly limited, and the outer diameter and the number may be set according to the relationship with the outer diameter of the hollow fiber HF2 described above. For example, a plurality of hollow fibers hf having an outer diameter of about 40 μm are converged or twisted to form an outer diameter of 0.1 μm.
When the hollow fiber HF2 of about 5 mm is configured, the number of hollow fibers hf is about 100 to 150.

The non-stretchable layer 12 composed of the hollow fibers HF1 or HF2 can be formed by a method similar to the conventional one. That is, the non-stretchable layer 12 is made of the hollow fiber H
F1 or the hollow fiber HF2 is formed by spirally winding the rubber glue around the base layer 11 coated with the rubber glue while applying tension, and then vulcanizing and fixing the rubber glue.

Although the porosity of the non-stretchable layer 12 is not particularly limited in the present invention, it is preferably from 10 to 80%, more preferably from 20 to 70%. If the porosity of the non-stretchable layer 12 is less than the above range, the compressive properties of the printing blanket may be reduced. If the porosity exceeds the above range, the compressive stress becomes too low, and There is a possibility that sufficient solid inking property cannot be imparted to the blanket.

The porosity (%) is determined by the cross-sectional area of the cross-section of the non-stretchable layer 12 (cross-section shown in FIG. 1A) of the cylindrical printing blanket 1 in the plane direction including the rotation axis. S ₁
And the total S of the cross-sectional area of the hollow fiber HF in the cross section.
_From (2), it can be obtained by the following equation (1).

[0022]

(1) Porosity (%) = S ₂ / S ₁ × 100 (1) Sleeve 10, base layer 11 and surface printing layer 1, which together with the non-stretchable layer 12 constitute the printing blanket 1.
3 can have the same configuration as the conventional one. For example, the sleeve 10 may be formed of a very thin metal material such as a nickel thin plate, or formed of glass fiber reinforced plastic.

The base layer 11 and the surface printing layer 13 are each formed in a seamless cylindrical shape using an elastomer such as vulcanized rubber. In order to form the two layers in a seamless cylindrical shape using vulcanized rubber, for example, an unvulcanized rubber paste for each layer is formed on the base, that is, on the sleeve 10 in the case of the base layer 11, In the case of the surface printing layer 13, it may be applied directly on the non-stretchable layer 12 or on one side via an adhesive rubber paste, dried, and then vulcanized. In addition, the unvulcanized rubber sheet formed from the rubber compound for each layer is vulcanized while being wound on the above-mentioned base via rubber glue for bonding, and the circumferential seam is integrally welded. It may be.

As the rubber constituting the base layer 11, oil-resistant rubbers such as acrylonitrile-butadiene copolymer rubber (NBR), chloroprene rubber (CR), and urethane rubber (U) are preferably used. . On the other hand, as the rubber constituting the surface printing layer 13, oil-resistant rubbers such as NBR, CR and U are preferably used, and polysulfide rubber (T), hydrogenated NBR, and the like can also be used.

The thickness of each of the above layers may be about the same as that of the prior art.
Specifically, the thickness of the base layer 11 is 0.5 to 2.0 mm
It is preferable that the thickness of the surface printing layer 15 is about 0.1 to 0.6 mm. Each of the above-described layers constituting the printing blanket 1 is sequentially laminated from a layer close to the sleeve 10 to an outer layer. Each layer may be vulcanized each time it is formed, or a plurality of layers may be vulcanized collectively.

The cylindrical printing blanket 1 is used by extrapolating to a blanket cylinder shaft of a printing press. Various additives can be blended into the rubber compound and the rubber paste of each layer constituting the printing blanket 1 of the example described above in the same manner as in the related art. Such additives include, for example, vulcanizing agents, vulcanization accelerators, vulcanization accelerating assistants, vulcanization retardants and other agents for vulcanizing rubber, as well as anti-aging agents, reinforcing agents, fillers, and softening agents. Agents, plasticizers and the like. The amounts of these additives may be the same as in the conventional case.

Among the above, the vulcanizing agents include, for example, sulfur, organic sulfur-containing compounds, organic peroxides, etc. Among them, the organic sulfur-containing compounds include, for example, N, N'-
Examples include dithiobismorpholine, and examples of the organic peroxide include benzoyl peroxide, dicumyl peroxide, and the like. Examples of the vulcanization accelerator include thiuram vulcanization accelerators such as tetramethylthiuram disulfide and tetramethylthiuram monosulfide;
Dithiocarbamic acids such as zinc dibutyldithiocarbamate, zinc diethyldithiocarbamate, sodium dimethyldithiocarbamate and tellurium diethyldithiocarbamate; 2-mercaptobenzothiazole, N-cyclohexyl-2-benzothiazolesulfenamide and the like Thiazoles; organic accelerators such as thioureas such as trimethylthiourea and N, N'-diethylthiourea;
Alternatively, inorganic accelerators such as slaked lime, magnesium oxide, titanium oxide, and litharge (PbO) can be used.

Examples of the vulcanization accelerator include metal oxides such as zinc white, stearic acid, oleic acid, and the like.
And fatty acids such as cottonseed fatty acids. Examples of the vulcanization retarder include aromatic organic acids such as salicylic acid, phthalic anhydride and benzoic acid; N-nitrosodiphenylamine,
And nitroso compounds such as -nitroso-2,2,4-trimethyl-1,2-dihydroquinone and N-nitrosophenyl-β-naphthylamine.

Examples of antiaging agents include imidazoles such as 2-mercaptobenzimidazole; phenyl-α-naphthylamine, N, N′-di-β-naphthyl-
amines such as p-phenylenediamine and N-phenyl-N'-isopropyl-p-phenylenediamine; di-t
-Butyl-p-cresol, and phenolized nophenols.

As the reinforcing agent, carbon black is mainly used, and inorganic reinforcing agents such as silica-based or silicate-based white carbon, zinc white, surface-treated precipitated calcium carbonate, magnesium carbonate, talc, clay, etc. Alternatively, organic reinforcing agents such as coumarone indene resin, phenol resin, and high styrene resin (styrene-butadiene copolymer having a high styrene content) can be used.

Examples of the filler include inorganic fillers such as calcium carbonate, clay, barium sulfate, diatomaceous earth, mica, asbestos, and graphite; and organic fillers such as recycled rubber, powdered rubber, asphalts, styrene resin, and glue. Agents and the like. Examples of the softener include fatty acids (stearic acid, lauric acid, etc.),
Various softening agents of vegetable oil type, mineral oil type and synthetic type such as cottonseed oil, tall oil, asphalt substance, paraffin wax and the like can be mentioned.

Examples of the plasticizer include various plasticizers such as dibutyl phthalate, dioctyl phthalate and tricresyl phosphate. In addition to the above, for example, a tackifier, a dispersant, a solvent, and the like may be appropriately blended with the rubber. In addition, the configuration of the printing blanket of the present invention is not limited to the example of the diagram described above,
Various design changes can be made without changing the gist of the present invention.

The non-stretchable layer 12 may be formed by winding two or more layers of the above-mentioned various kinds of hollow fibers in the circumferential direction. 2
One or more non-stretchable layers may be disposed adjacent to each other or may be disposed apart from each other in each layer constituting the printing blanket. Further, the non-stretchable layer may be formed by, for example, arranging a plurality of single fibers in parallel, instead of spirally winding a single fiber hollow fiber, a fiber bundle, a twisted yarn, or the like.

As described above, when two or more hollow fibers are wound to form a non-stretchable layer, the dimensions such as the outer diameter of the hollow fibers may be less than the above ranges.
In the present invention, the configuration of a layer other than the non-stretchable layer can be appropriately changed. In short, as long as the non-stretchable layer disposed below the surface printing layer is formed by arranging the hollow fibers in a certain direction, other configurations are not particularly limited in the present invention.

[0035]

The present invention will be described below based on examples and comparative examples. Example 1 Inner diameter 169.5 mm, length 910 mm, thickness 0.15 m
m, on a peripheral surface of a cylindrical nickel sleeve, Chemloc manufactured by Lord Chemical Co., Ltd.
k) After winding an unvulcanized rubber sheet having a thickness of 2.0 mm made of an NBR rubber compound through an adhesive layer having a two-layer structure of a layer of 205 and a layer of Chemlock 252X, The sheet was vulcanized in a wrapped state, and the surface after vulcanization was polished to form a circumferentially seamless base layer having a total thickness of 1.20 mm including the adhesive layer.

Next, an adhesive layer (thickness: 0.05 mm) is formed on the base layer with NBR-based rubber glue, and the outer diameter of the adhesive layer is circular, and only one is formed at the center thereof. A single fiber hollow fiber made of an acrylic resin having a hollow having a circular cross section continuously along the length direction [outer diameter 0.50 mm, inner diameter 0.30 mm, RX21 manufactured by Toyobo Co., Ltd.]
While applying a tension of 450 ± 10 gf, and spirally wound so that the distance between adjacent hollow fibers [L in FIG. 1 (a)] is 0.05 mm or less.

Then, after vulcanizing with the above-mentioned surface wrapped, an adhesive layer (thickness 0.05 mm) was formed thereon with a rubber paste containing unvulcanized NBR. The rubber paste for the surface print layer containing NBR was pasteurized and dried, and then vulcanized with its surface wrapped. Then, the surface of the surface printing layer after vulcanization is polished, and on the base layer, a non-stretchable layer having a thickness of 0.60 mm, comprising a hollow fiber and adhesive layers above and below the hollow fiber, and a thickness of 0.25 mm of,
A surface printing layer having no seams in the circumferential direction is laminated in this order, and has a layer configuration shown in FIG.
Produced a seamless cylindrical printing blanket.

Examples 2 to 7 As shown in Table 1 below, in the same manner as in Example 1 except that single-fiber hollow fibers having different outer diameters and hollow inner diameters (both made of acrylic resin) were used. A seamless cylindrical printing blanket having the layer configuration shown in FIG. 1 (a) was manufactured. Example 8 Polyester hollow fiber having a circular outer diameter cross section and a single hollow at the center of the hollow fiber continuously extending in the length direction instead of the monofilament hollow fiber [external diameter 40 μm,
Inner diameter 15 μm, Toyobo Co., Ltd. esmarble]
100 to 150 hollow fibers converged in parallel (outer diameter 0. 1).
A seamless cylindrical printing blanket was produced in the same manner as in Example 1 except that 50 mm) was used.

Examples 9 to 17 As shown in Tables 2 and 3 below, 100 to 150 hollow fibers (both made of polyester) having different hollow inner diameters were twisted and hollow fibers (both having an outer diameter of 0.50 mm) were used. ) Was used in the same manner as in Example 1 except that (1) was used to produce a seamless cylindrical printing blanket.

Comparative Example 1 The procedure of Example 1 was repeated, except that a single cotton hollow fiber (diameter 0.500 mm, 16-count / 4-twist) was used instead of the single-fiber hollow fiber. A solid, seamless cylindrical printing blanket was produced. Comparative Example 2 On the outer peripheral surface of a cylindrical nickel sleeve having the same dimensions as that used in Example 1, an adhesive layer having a two-layer structure of the above-mentioned Chemlock 205 layer and Chemlock 252X layer was provided. Made of NBR rubber compound, 2.0m thick
m, after wrapping an unvulcanized rubber sheet, vulcanizing with the surface of the sheet wrapped, polishing the surface after vulcanization, a total thickness of 1.10 mm including the adhesive layer, A seamless base layer was formed in the circumferential direction.

Next, an adhesive layer (thickness: 0.05 mm) was formed on the base layer with NBR-based rubber paste, and the same NBR-based rubber paste containing salt grains was pasted thereon. After drying and vulcanizing with its surface wrapped, leaching treatment is performed to extract the salt particles by immersing them in 70 ° C. hot water for 12 hours, and then dried to obtain a 0.30 mm thick matrix rubber. JIS C hardness of 90
°, a compressible layer having a continuous pore structure with a porosity of 40% and having no seams in the circumferential direction.

Next, an adhesive layer (thickness: 0.05 mm) was formed on the compressible layer with NBR-based rubber glue, and a normal cotton thread (having a diameter of 0.250 m) having no hollow inside was formed thereon.
m) was spirally wound while applying a tension of 450 ± 10 gf such that the distance between adjacent hollow fibers was 0.05 mm or less. Then, after vulcanizing with the above-mentioned surface wrapped, an adhesive layer (thickness 0.05 mm) is formed thereon with a rubber paste containing unvulcanized NBR, and this also contains NBR. The rubber paste for the surface printing layer was coated and dried, and then vulcanized with its surface wrapped. Then, the surface of the surface printing layer after vulcanization is polished, and on the base layer, a non-stretchable layer having a thickness of 0.3 mm made of cotton yarn and adhesive layers above and below the base layer, and a thickness of 0.25 mm
And a surface printing layer having no seams in the circumferential direction were laminated in this order to produce an air-type, seamless cylindrical printing blanket.

With respect to the printing blankets manufactured in each of the above Examples and Comparative Examples, the following tests were performed to evaluate the characteristics. Compression characteristic test Examples 1 and 8 and Comparative Examples 1 and 2
In a state where the printing blanket 1 is extrapolated to the cylinder shaft 21 of the test apparatus 2 shown in FIG. 3, an impression cylinder 22 as a model of a plate cylinder is pressed against the surface thereof, and the printing blanket 1 is distorted. The compression stress (kgf) generated in accordance with the amount of strain (mm) was measured.

FIG. 5 shows the results. In FIG. 5, the solid curve shows the result of Example 8, the two-dot chain curve shows the result of Example 1 and Comparative Example 2, and the one-dot chain curve shows the result of Comparative Example 1. As apparent from FIG. 5, the printing blanket of Example 1 has the same simple structure as that of Comparative Example 1 which is a solid type, but Comparative Example 2 which is an air type.
It has the same excellent compression characteristics as those of Example 1, and the printing blanket of Example 8 is the same as that of Example 1 and Comparative Example 1 described above.
In addition to having the same simple structure as that of Comparative Example 2, it was confirmed that it had better compression characteristics than Comparative Example 2.

Measurement of Perimeter Change Rate The perimeter change rate of the printing blanket of each example and comparative example was measured using the test apparatus 2 shown in FIG. That is, in a state where each printing blanket 1 is externally mounted on the barrel 21 of the test apparatus 2 in the same manner as described above,
The cylinder shaft 21 was rotated by a predetermined number of revolutions in a state where the impression cylinder 22 as a model of the plate cylinder was pressed into contact with a predetermined press amount.
Then, the rate of change (%) of the circumferential length of the printing blanket 1 was determined from the resulting shift in the amount of rotation between the cylinder shaft 21 and the impression cylinder 22.

The measurement conditions are as follows. Diameter of cylinder shaft 21: 169.520 mm Diameter of impression cylinder 22: 173.915 mm Amount of impression cylinder 22 pushed into printing blanket 1: 0.
1 mm Rotation speed of trunk shaft 21: 100 r. p. m. Number of rotations of the torso shaft 21: 500 times At the time of measurement, is the deviation of the rotation amount of the impression cylinder 22 with respect to the torso shaft 21 in the forward direction (the impression cylinder 22 rotates more than the torso shaft 21) every 100 rotations? , The negative direction (the impression cylinder 22 rotates less than the cylinder shaft 21) was confirmed. As a result, it was found that the deviation of the rotation amount was positive in each case.

The printing blanket having such a large perimeter change rate, because of the insufficient compression characteristics described above, makes the printed image unclear and deteriorates the printing quality. Therefore, the smaller the circumference change rate, the better. The specific numerical value is preferably 0.20% or less, particularly preferably 0.15% or less. Measurement of brightness standard deviation The printing blanket of each example and comparative example was mounted on a high-speed offset rotary printing press, and using black oil-based ink,
Solid printing of 3 × 3 mm was performed on the surface of high quality paper.

The standard deviation of the luminance of the solid portion of the printed matter was measured using an image processing apparatus (LA555 manufactured by Pierce Co., Ltd.). The smaller the standard deviation of the luminance, the better the solid inking property. Based on the finding that there was, the solid inking property of the printing blankets of Examples and Comparative Examples was evaluated. Specifically, those having a luminance standard deviation of less than 20.0, particularly 19.5 or less, were evaluated as having good solid inking property.

The above results are shown in Tables 1 to 4. In the table, the porosity (%) of the non-stretchable layer is calculated by the equation (1) as described above.
Required by

[0050]

(2) Porosity (%) = S ₂ / S ₁ × 100 (1) Among the above, the cross-sectional area S ₁ of the non-stretchable layer 12 is determined by the outer diameter of the hollow fiber and the thickness of the adhesive layer above and below the hollow fiber. (Both 0.05m
m) and the product of the thickness of the non-stretchable layer and the width of the non-stretchable layer (that is, the length of the sleeve 910 mm). Further, the total cross-sectional area S ₂ of the hollow fiber HF is determined by the product of the cross-sectional area of the hollow fiber and the number of turns of the hollow fiber HF (how many times the hollow fiber HF is wound on the base layer).

The porosity of the non-stretchable layers of Comparative Examples 1 and 2 using a non-hollow cotton yarn is naturally 0 (%).

[0052]

[Table 1]

[0053]

[Table 2]

[0054]

[Table 3]

[0055]

[Table 4]

[0056]

As described above, according to the present invention, the present invention is excellent in productivity because it has a simpler structure than the air type printing blanket, and has the same effect as the air type printing blanket. This has a specific effect that a printing blanket having excellent compression characteristics can be provided.

[Brief description of the drawings]

FIG. 1 is a view showing an example of an embodiment of a printing blanket of the present invention, wherein FIG.
FIG. 2B is a cross-sectional view of a hollow fiber in which a plurality of hollow fibers are converged in parallel and integrated, which can be used in place of the single fiber hollow fiber used in FIG.

FIG. 2 is a perspective view showing the entire printing blanket of the above example.

FIG. 3 is a front view of an apparatus for measuring compression characteristics of printing blankets manufactured in Examples and Comparative Examples.

FIG. 4 is a graph showing the compression characteristics of printing blankets having various structures, that is, the relationship between the amount of distortion and the compression stress.

FIG. 5 is a graph showing the relationship between the amount of distortion and the compressive stress in the printing blankets of Examples and Comparative Examples.

[Explanation of symbols]

 Reference Signs List 1 blanket for printing 13 surface printing layer 12 non-stretchable layer HF1, HF2 hollow fiber hf hollow fiber

──────────────────────────────────────────────────続 き Continued on the front page (72) Inventor Takamichi Sagawa 41-1, Shimizu, Uozumi-cho, Akashi-shi, Hyogo Pref. No. 5 (56) References JP-A-5-301483 (JP, A) JP-A-6-198837 (JP, A) (58) Fields investigated (Int. Cl. ⁷ , DB name) B41N 10/00- 10/04

Claims (5)

(57) [Claims] 1. A blanket printing blanket having a circumferentially seamless cylindrical shape, comprising: (a) a surface printing layer formed of an elastomer and having a circumferentially seamless cylindrical shape; A blanket for printing, comprising at least a non-stretchable layer formed by arranging hollow fibers in a certain direction, disposed below the printing layer. 2. The printing blanket according to claim 1, wherein the hollow fiber is a single fiber made of a synthetic resin having a cavity therein, and has an outer diameter of 0.1 to 1.0 mm. 3. The hollow fiber is formed by converging a plurality of hollow fibers made of a synthetic resin having a cavity therein in parallel, and has an outer diameter of 0.1 to 1.0 mm. A printing blanket according to claim 1. 4. The hollow fiber is formed by twisting a plurality of hollow fibers made of a synthetic resin having a cavity therein,
The printing blanket according to claim 1, wherein the outer diameter is 0.1 to 1.0 mm. 5. The printing blanket according to claim 1, further comprising a base layer, which is disposed below the non-stretchable layer and includes an elastomer and has a circumferentially seamless cylindrical shape.