JP3122976B2 - Transparent, conductive, moisture-proof laminated sheet - Google Patents
Transparent, conductive, moisture-proof laminated sheetInfo
- Publication number
- JP3122976B2 JP3122976B2 JP04242776A JP24277692A JP3122976B2 JP 3122976 B2 JP3122976 B2 JP 3122976B2 JP 04242776 A JP04242776 A JP 04242776A JP 24277692 A JP24277692 A JP 24277692A JP 3122976 B2 JP3122976 B2 JP 3122976B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- conductive
- transparent
- film
- laminated sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】[0001]
【産業上の利用分野】本発明は、主として、静電気によ
る障害を受け易い物品、例えば、ICやLSI等の電子
部品用の包装袋として利用される積層シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a laminated sheet mainly used as an article which is easily affected by static electricity, for example, a packaging bag for electronic parts such as ICs and LSIs.
【0002】[0002]
【従来の技術】ICやLSI等の電子部品の包装袋に
は、包装袋内の電子部品の静電気障害を防止するために
導電性を有する包装用材、例えば、ポリオレフィン系樹
脂シートからなる基材と該基材の片面あるいは両面に積
層されているカーボンブラックが内填されているポリオ
レフィン系樹脂フィルムとの積層シートや、アルミニウ
ム箔と2軸延伸ポリエステルフィルムとの積層シート等
が利用されている。2. Description of the Related Art Packaging bags for electronic components such as ICs and LSIs include a packaging material having conductivity, for example, a base material made of a polyolefin-based resin sheet, in order to prevent electrostatic damage of the electronic components in the packaging bag. A laminated sheet of a polyolefin-based resin film containing carbon black, which is laminated on one or both sides of the substrate, and a laminated sheet of an aluminum foil and a biaxially stretched polyester film are used.
【0003】[0003]
【発明が解決しようとする課題】ところで、静電気障害
を受け易い物品の中には、例えば、磁気ディスク等のよ
うに、静電気に対して敏感なだけでなく湿気や酸素によ
る酸化の障害を受け易いものもあり、包装袋に対しては
静電気障害に対する防止性能と共に水蒸気および酸素に
対するバリヤー性能と、包装袋内の内容物を確認するこ
とのできる透明性とを兼備することが要求される。Some of the articles that are susceptible to electrostatic damage are not only sensitive to static electricity but also susceptible to oxidation by moisture and oxygen, such as magnetic disks. Some packaging bags are required to have both a barrier performance against water vapor and oxygen, as well as a protection performance against static electricity damage, and a transparency capable of confirming the contents in the packaging bag.
【0004】しかるに、前述のカーボンブラックが内填
されているポリオレフィン系樹脂フィルムを利用した積
層シートは、水蒸気バリヤー性および酸素バリヤー性が
不十分なだけで無く包装袋内の内容物を確認し得る透明
性が得られない。また、アルミニウム箔が積層されてい
る積層シートは、水蒸気バリヤー性および酸素バリヤー
性については良好な性質を有するものの、包装袋内の内
容物を目視によって確認するに必要な透明性が得られな
い。[0004] However, the above-mentioned laminated sheet using a polyolefin-based resin film in which carbon black is embedded can not only have insufficient steam barrier properties and oxygen barrier properties but also confirm the contents in the packaging bag. Transparency cannot be obtained. Further, although the laminated sheet on which the aluminum foil is laminated has good steam barrier properties and oxygen barrier properties, it does not provide the transparency required for visually checking the contents in the packaging bag.
【0005】これに対して本発明は、静電気障害に対す
る防止性能は勿論のこと、水蒸気および酸素に対するバ
リヤー性、さらには、包装袋内の内容物を目視によって
確認するに必要な透明性においても優れた性質を有する
積層シートを提供する。On the other hand, the present invention is excellent in not only the performance against electrostatic damage, the barrier property against water vapor and oxygen, but also the transparency required for visually confirming the contents in the packaging bag. To provide a laminated sheet having the following properties.
【0006】[0006]
【課題を解決するための手段】請求項1の発明は、酸化
錫,酸化珪素または酸化アルミニウムによる厚さ20〜
400Åの蒸着層を有する第1の基材用フィルムと、厚
さ20〜400Åのアルミニウム蒸着層を有する第2の
基材用フィルムとを、第1の基材用フィルムの酸化錫,
酸化珪素または酸化アルミニウムによる蒸着層面と第2
の基材用フィルムのアルミニウム蒸着層面とが接当する
ようにして接着させた積層シートからなる基材シート
と、該基材シートの一方の面に形成されている透明な導
電性インキ層と、該透明な導電性インキ層の表面に多数
のドット状をなすようにして積層されている表面樹脂層
と、前記基材シートの他方の面に形成されている線状低
密度ポリエチレンフィルム層と、該線状低密度ポリエチ
レンフィルム層に積層されている線状のパターン印刷層
からなる導電性塗料層とを有する透明・導電・防湿性積
層シートからなる。According to the first aspect of the present invention, tin oxide, silicon oxide or aluminum oxide having a thickness of 20 to 50 mm is used.
A first base film having a vapor deposition layer of 400 ° and a second base film having an aluminum vapor deposition layer having a thickness of 20 to 400 ° were formed by tin oxide of the first base film.
Silicon oxide or aluminum oxide deposited layer surface and second
A base sheet made of a laminated sheet adhered in such a manner that the aluminum vapor-deposited layer surface of the base film is brought into contact with the base sheet, and a transparent conductive ink layer formed on one surface of the base sheet, A surface resin layer that is laminated to form a large number of dots on the surface of the transparent conductive ink layer, and a linear low-density polyethylene film layer formed on the other surface of the base sheet, A transparent / conductive / moisture-proof laminated sheet having a conductive paint layer composed of a linear pattern printing layer laminated on the linear low-density polyethylene film layer.
【0007】請求項2の発明は、請求項1の発明の透明
・導電・防湿性積層シートの構成において、透明な導電
性インキ層の表面に多数のドット状をなすようにして積
層されている表面樹脂層が、厚さ1〜100μ、ドット
の幅(a) が100〜1000μ、隣接するドットとドッ
トとの間の間隔(b) が50〜200μで、かつ、{ドッ
トの幅 (a)/隣接するドットとドットとの間の間隔(b)
}=1〜20に形成されている積層シートからなる。According to a second aspect of the present invention, in the structure of the transparent / conductive / moisture-proof laminated sheet according to the first aspect of the present invention, a large number of dots are laminated on the surface of the transparent conductive ink layer. The surface resin layer has a thickness of 1 to 100 μm, a dot width (a) of 100 to 1000 μm, an interval (b) between adjacent dots of 50 to 200 μm, and a dot width of (a) / Spacing between adjacent dots (b)
積 層 = 1 to 20.
【0008】請求項3の発明は、請求項1または請求項
2の発明の透明・導電・防湿性積層シートの構成におい
て、基材シートの他方の面に形成されている線状低密度
ポリエチレンフィルム層が厚さ20〜100μの線状低
密度ポリエチレン樹脂フィルムからなり、該線状低密度
ポリエチレンフィルム層に積層されている線状のパター
ン印刷層からなる導電性塗料層が、白色導電性チタン酸
カリウムウィスカーを含有する導電性塗料で形成されて
いる積層シートからなる。A third aspect of the present invention is the linear low-density polyethylene film formed on the other surface of the base sheet in the structure of the transparent, conductive and moisture-proof laminated sheet according to the first or second aspect of the present invention. The layer is formed of a linear low-density polyethylene resin film having a thickness of 20 to 100 μm, and the conductive coating layer formed of a linear pattern printing layer laminated on the linear low-density polyethylene film layer is a white conductive titanate. It is composed of a laminated sheet formed of a conductive paint containing potassium whiskers.
【0009】前記構成からなる本発明の透明・導電・防
湿性積層シートを利用する包装袋は、該積層シートにお
ける表面樹脂層が包装袋の外側表面層となるようにし
て、すなわち、該積層シートにおける線状のパターン印
刷層からなる導電性塗料層面が包装袋内の内容物と接す
るようにして包装袋に利用される。[0009] The packaging bag using the transparent, conductive and moisture-proof laminated sheet of the present invention having the above-mentioned structure is arranged so that the surface resin layer in the laminated sheet becomes the outer surface layer of the packaging bag. Is used for the packaging bag such that the surface of the conductive paint layer composed of the linear pattern printing layer is in contact with the contents in the packaging bag.
【0010】本発明の透明・導電・防湿性積層シートに
おいて、酸化錫,酸化珪素または酸化アルミニウムによ
る厚さ20〜400Åの蒸着層を有する第1の基材用フ
ィルムと、厚さ20〜400Åのアルミニウム蒸着層を
有する第2の基材用フィルムとを接着させた積層シート
からなる基材シートは、例えば、2軸延伸ポリエステル
フィルム,2軸延伸ナイロンフィルム,2軸延伸ポリプ
ロピレンフィルム等の2軸延伸フィルムに、酸化錫,酸
化珪素または酸化アルミニウムによる蒸着層を形成した
厚さ10〜75μ程度のフィルムと、2軸延伸ポリエス
テルフィルム,2軸延伸ナイロンフィルム,2軸延伸ポ
リプロピレンフィルム等の2軸延伸フィルムにアルミニ
ウム蒸着層を形成した厚さ12〜50μ程度のフィルム
とを、各蒸着フィルムの蒸着層面同士をウレタン系接着
剤で貼着する等して得られる。In the transparent / conductive / moisture-proof laminated sheet of the present invention, a first base material film having a deposited layer of tin oxide, silicon oxide or aluminum oxide having a thickness of 20 to 400 ° is provided. A base sheet composed of a laminated sheet in which a second base film having an aluminum vapor-deposited layer is bonded to a second base film is, for example, a biaxially oriented polyester film, a biaxially oriented nylon film, a biaxially oriented polypropylene film or the like. A film having a thickness of about 10 to 75 μm in which a deposited layer of tin oxide, silicon oxide or aluminum oxide is formed on the film, and a biaxially oriented film such as a biaxially oriented polyester film, a biaxially oriented nylon film, and a biaxially oriented polypropylene film. And a film having a thickness of about 12 to 50 μm on which an aluminum vapor deposition layer is formed. It is obtained by, for example, adhering the vapor-deposited layers of the film to each other with a urethane adhesive.
【0011】第1の基材用フィルムと第2の基材用フィ
ルムとの積層シートからなる基材シートにおける酸化
錫,酸化珪素または酸化アルミニウムによる厚さ20〜
400Åの蒸着層により、水蒸気,酸素及び炭酸ガスに
対する良好なバリヤー性が奏される。また、20〜40
0Åのアルミニウム蒸着層により電磁波シールド性が奏
される。さらに、第1の基材用フィルムと第2の基材用
フィルムとにおける2軸延伸フィルムにより、包装袋に
必要とされるに十分な耐突き刺し性等の機械的強度が具
備される。[0011] The base sheet made of a laminated sheet of the first base film and the second base film is made of tin oxide, silicon oxide or aluminum oxide having a thickness of 20 to
The 400 ° vapor deposition layer provides good barrier properties against water vapor, oxygen and carbon dioxide. In addition, 20-40
Electromagnetic wave shielding is provided by the aluminum vapor deposition layer of 0 °. Furthermore, the biaxially stretched film in the first base material film and the second base material film provides sufficient mechanical strength such as puncture resistance required for the packaging bag.
【0012】第1の基材用フィルムと第2の基材用フィ
ルムとの積層シートからなる基材シートの一方の面に形
成されている透明な導電性インキ層は、本発明の透明・
導電・防湿性積層シートを利用する包装袋に外部からの
要因による静電気障害を防止するもので、例えば、酸化
錫,酸化錫−アンチモン系,チタン酸カリウム系等によ
る導電性及び透明性において優れた性質を有する物質を
混合した塗料層として形成される。なお、この導電性イ
ンキ層は、該導電性インキ層を形成するための塗料中の
導電性粉末の量や塗料の塗布量等の調整により、導電性
インキ層の表面抵抗値が106 Ω/ □ 以下となるよう
にして形成されることが一応の目安であり、例えば、グ
ラビアコート法,3本リバース法等により厚さ1〜5μ
程度に形成される。[0012] The transparent conductive ink layer formed on one surface of the base sheet made of a laminated sheet of the first base film and the second base film is the transparent conductive ink layer of the present invention.
It prevents static electricity damage caused by external factors in a packaging bag using a conductive and moisture-proof laminated sheet. For example, it has excellent conductivity and transparency due to tin oxide, tin oxide-antimony system, potassium titanate system and the like. It is formed as a paint layer mixed with a substance having properties. The conductive ink layer has a surface resistance value of 10 6 Ω / by adjusting the amount of the conductive powder in the paint for forming the conductive ink layer and the amount of the paint applied. □ It is a rough guide to form it as follows. For example, the thickness is 1 to 5 μm by a gravure coating method, a three-reverse method, or the like.
Formed to the extent.
【0013】透明な導電性インキ層の表面に多数のドッ
ト状をなすようにして積層されている表面樹脂層、すな
わち、本発明の透明・導電・防湿性積層シートによる包
装袋を得る場合に該包装袋の外側表面層となる表面樹脂
層は、前記積層シートに対して耐摩耗性,光沢,滑り性
等の諸特性をもたらすものであり、例えば、ポリウレタ
ン,塩化ビニル・酢酸ビニル共重合体,ポリスチレン,
ポリアミド,ポリエステル等の熱可塑性樹脂や、フェノ
ール樹脂,エポキシ樹脂等の硬化型樹脂等による厚さ1
〜100μの多数のドット群によって形成され、通常、
透明な導電性インキ層の表面にグラビアコート法による
網目塗工を行なうことによって形成される。When a surface resin layer laminated in the form of a number of dots on the surface of a transparent conductive ink layer, that is, a packaging bag made of the transparent, conductive, and moisture-proof laminated sheet of the present invention, the above-mentioned method is used. The surface resin layer serving as the outer surface layer of the packaging bag provides various properties such as abrasion resistance, gloss, and slipperiness to the laminated sheet. For example, polyurethane, vinyl chloride / vinyl acetate copolymer, polystyrene,
Thickness 1 made of thermoplastic resin such as polyamide or polyester, or curable resin such as phenol resin or epoxy resin
Formed by a number of dot groups of ~ 100μ, usually
The transparent conductive ink layer is formed by performing network coating by gravure coating on the surface.
【0014】表面樹脂層を構成している多数のドット群
は、ドットの幅が100〜1000μ、隣接するドット
とドットとの間の間隔が50〜200μで、かつ、
「(ドットの幅)/ (ドットとドットとの間の間隔)」
が1〜20程度に形成される。A large number of dots forming the surface resin layer have a dot width of 100 to 1000 μ, an interval between adjacent dots of 50 to 200 μ, and
"(Dot width) / (interval between dots)"
Are formed in about 1 to 20.
【0015】多数のドット群によって構成される表面樹
脂層の厚さや、単一のドットの幅、隣接するドット同士
の間の間隔等が前述の各規定から外れると、表面樹脂層
の存在が積層シートの表面抵抗値を引き上げることにな
り、導電性インキ層の表面抵抗値と略同程度の表面抵抗
値を積層シートの表面抵抗値として維持し得なくなった
り、あるいは、表面樹脂層による導電性インキ層に対す
る表面保護作用が不十分になったりする。なお、表面樹
脂層を構成している各単一のドットの幅、及び、隣接す
るドット同士の間の間隔は、[図2]において斜線で表
示される各ドットにおいて、符号aで表示されるドット
の最大幅がドットの幅 (a)であり、符号bで表示される
ドットの縁部から隣接するドットの縁部迄の最短距離
が、隣接するドットとドットとの間の間隔 (b)である。If the thickness of the surface resin layer composed of a large number of dot groups, the width of a single dot, the interval between adjacent dots, and the like deviate from the above-mentioned respective rules, the presence of the surface resin layer is determined. The surface resistance of the sheet is raised, and the surface resistance of the laminated sheet cannot be maintained as substantially as the surface resistance of the conductive ink layer. The surface protection effect on the layer may be insufficient. Note that the width of each single dot constituting the surface resin layer and the interval between adjacent dots are indicated by a symbol a in each dot indicated by oblique lines in FIG. 2. The maximum width of the dot is the width of the dot (a), and the shortest distance from the edge of the dot indicated by the symbol b to the edge of the adjacent dot is the distance between adjacent dots (b) It is.
【0016】本発明の透明・導電・防湿性積層シートに
おいては、基材シートの他方の面に形成されている線状
低密度ポリエチレンフィルム層と、該線状低密度ポリエ
チレンフィルム層に積層されている線状のパターン印刷
層からなる導電性塗料層とが積層シートの裏面樹脂層と
なるもので、該裏面樹脂層における導電性塗料層面が包
装袋の内容物と接する側となるようにして利用される。In the transparent / conductive / moisture-proof laminated sheet of the present invention, a linear low-density polyethylene film layer formed on the other surface of the base sheet, and the linear low-density polyethylene film layer are laminated on the linear low-density polyethylene film layer. The conductive paint layer composed of a linear pattern printing layer is used as the backside resin layer of the laminated sheet, and the conductive paint layer surface of the backside resin layer is used on the side in contact with the contents of the packaging bag. Is done.
【0017】この線状低密度ポリエチレンフィルム層と
該線状低密度ポリエチレンフィルム層に積層されている
線状のパターン印刷層からなる導電性塗料層とによる裏
面樹脂層は、本発明の透明・導電・防湿性積層シートを
利用して得られる包装袋において、包装袋内の内容物と
包装袋との間の摩擦による静電気障害を防止する作用を
果たし、また同時に、本発明の透明・導電・防湿性積層
シートを利用する包装袋の封緘部が、前記導電性塗料層
で積層されていない部分の線状低密度ポリエチレンフィ
ルム層によるヒートシールによって形成され得るような
熱溶着特性をもたらす。前記線状低密度ポリエチレンフ
ィルム層は、先の封緘部を形成する際の熱溶着特性と本
発明の透明・導電・防湿性積層シートによるスムーズな
製袋特性とを具備させるに十分な厚さ、具体的には、1
0〜100μ程度に形成される。The backside resin layer composed of the linear low-density polyethylene film layer and the conductive paint layer composed of a linear pattern printing layer laminated on the linear low-density polyethylene film layer is a transparent / conductive resin according to the present invention. -In a packaging bag obtained by using the moisture-proof laminated sheet, it acts to prevent static electricity damage due to friction between the contents in the packaging bag and the packaging bag, and at the same time, the transparent, conductive and moisture-proof of the present invention. The sealing portion of the packaging bag using the conductive laminated sheet has a heat-sealing property that can be formed by heat sealing with a linear low-density polyethylene film layer in a portion not laminated with the conductive paint layer. The linear low-density polyethylene film layer has a thickness sufficient to provide the heat-sealing property when forming the sealing portion and the smooth, bag-forming property of the transparent, conductive, and moisture-proof laminated sheet of the present invention, Specifically, 1
It is formed to a size of about 0 to 100 μ.
【0018】線状低密度ポリエチレンフィルム層に積層
されている線状のパターン印刷層からなる導電性塗料層
は、具体的には、白色導電性チタン酸カリウムウイスカ
ーを含有する導電性塗料による線状のパターン印刷層に
されるのが好適である。The conductive coating layer comprising a linear pattern printing layer laminated on the linear low-density polyethylene film layer is, for example, a linear coating made of a conductive coating containing white conductive potassium titanate whiskers. It is preferable to use a pattern printing layer.
【0019】[0019]
【作用】本発明の透明・導電・防湿性積層シートは、該
積層シートにおける表面樹脂層側が包装袋の外側表面側
となるようにして、すなわち、線状のパターン印刷層か
らなる導電性塗料層を具備する線状低密度ポリエチレン
フィルム層側が包装袋内の内容物と接する側となるよう
にして利用され、例えば、ICやLSI等の電子部品の
包装体を得る際の包装用材として使用される。The transparent / conductive / moisture-proof laminated sheet of the present invention is arranged such that the surface resin layer side of the laminated sheet is the outer surface side of the packaging bag, that is, a conductive paint layer comprising a linear pattern printing layer. The linear low-density polyethylene film layer having the following is used such that the side thereof comes into contact with the contents in the packaging bag, and is used, for example, as a packaging material for obtaining a package of an electronic component such as an IC or LSI. .
【0020】本発明の透明・導電・防湿性積層シートに
おいては、該積層シート中の酸化錫,酸化珪素または酸
化アルミニウムによる蒸着層を有する第1の基材用フィ
ルムが水蒸気,酸素及び炭酸ガス等に対するバリヤー性
を果たし、アルミニウム蒸着層を有する第2の基材用フ
ィルムが電磁波シールド性を果たし、またこれらの第1
の基材用フィルムと第2の基材用フィルムとが同時に、
包装用材に必要とされる耐突き刺し性等の機械的強度を
具備させる。In the transparent / conductive / moisture-proof laminated sheet of the present invention, the first base film having a vapor deposited layer of tin oxide, silicon oxide or aluminum oxide in the laminated sheet is formed of water vapor, oxygen and carbon dioxide gas. The second substrate film having an aluminum vapor-deposited layer fulfills an electromagnetic wave shielding property, and the first
The base material film and the second base material film are simultaneously
Provide the packaging material with mechanical strength such as piercing resistance required for the packaging material.
【0021】また、基材シートと多数のドット状をなす
ようにして積層されている表面樹脂層との間に形成され
ている透明な導電性インキ層の存在が、本発明の透明・
導電・防湿性積層シートを利用して得られる包装袋に、
外部からの要因による静電気障害を防止する作用を果た
す。Further, the presence of the transparent conductive ink layer formed between the base material sheet and the surface resin layer laminated so as to form a large number of dots is considered to be the present invention.
Packaging bags obtained using conductive and moisture-proof laminated sheets,
It acts to prevent static electricity damage due to external factors.
【0022】また、本発明の透明・導電・防湿性積層シ
ートによる包装袋を得る場合に、包装袋の外側表面層と
なる表面樹脂層が、耐摩耗性,光沢,滑り性等の諸特性
をもたらす。特に、この表面樹脂層の存在が積層シート
の表面抵抗値を引き上げる要因となるために、従来は、
導電性インキ層の表面には保護作用を奏するに十分な厚
さの表面保護層を形成することができなかったが、本発
明の透明・導電・防湿性積層シートにおける表面樹脂層
は多数のドット群によって形成されているために、表面
保護層を導電性インキ層の表面の全体に亙って形成する
場合に比較してその厚さをより厚くすることができ、表
面樹脂層による優れた表面保護作用が果たされる。Further, when a packaging bag made of the transparent, conductive and moisture-proof laminated sheet of the present invention is obtained, the surface resin layer, which is the outer surface layer of the packaging bag, has various properties such as abrasion resistance, gloss and slipperiness. Bring. In particular, since the presence of this surface resin layer causes a rise in the surface resistance value of the laminated sheet, conventionally,
Although a surface protective layer having a thickness sufficient to exert a protective action could not be formed on the surface of the conductive ink layer, the surface resin layer in the transparent, conductive, and moisture-proof laminated sheet of the present invention had a large number of dots. Since the surface protective layer is formed by the group, the thickness can be made thicker as compared with the case where the surface protective layer is formed over the entire surface of the conductive ink layer. A protective effect is achieved.
【0023】さらに、基材シートの他方の面に形成され
ている「線状低密度ポリエチレンフィルム層に積層され
ている線状のパターン印刷層からなる導電性塗料層」
が、本発明の透明・導電・防湿性積層シートを利用する
包装袋内の内容物と包装袋との間に発生する摩擦による
静電気障害を防止する作用を果たし、また、基材シート
の他方の面に形成されている線状低密度ポリエチレンフ
ィルム層のうちの線状のパターン印刷層からなる導電性
塗料層で被覆されていない部分の熱溶着特性によって、
本発明の透明・導電・防湿性積層シートによる包装袋の
封緘部をヒートシールによって形成し得るような熱溶着
特性が果たされる。Further, the "conductive paint layer comprising a linear pattern printing layer laminated on the linear low density polyethylene film layer" formed on the other surface of the base sheet.
Has an effect of preventing static electricity damage due to friction generated between the contents in the packaging bag and the packaging bag using the transparent / conductive / moisture-proof laminated sheet of the present invention, and the other of the base sheet. Of the linear low-density polyethylene film layer formed on the surface, by the heat welding characteristics of the part not covered with the conductive paint layer consisting of the linear pattern printing layer,
The heat-sealing property is achieved such that the sealed portion of the packaging bag using the transparent, conductive and moisture-proof laminated sheet of the present invention can be formed by heat sealing.
【0024】さらにまた、請求項3の発明の透明・導電
・防湿性積層シートは、線状低密度ポリエチレンフィル
ム層面に形成されている線状のパターン印刷層からなる
導電性塗料層が、白色導電性チタン酸カリウムウィスカ
ーを含有する導電性塗料層からなるものであり、該導電
性塗料層による静電防止作用が高温,高湿度雰囲気中に
おいても低下するようなことがなく、汎用の静電防止剤
の塗布や汎用の静電防止剤の内填によっては奏され得な
い作用、すなわち、雰囲気中の温度や湿度に影響を受け
ることのない恒久的な静電防止作用を果たす。Further, in the transparent / conductive / moisture-proof laminated sheet according to the third aspect of the present invention, the conductive paint layer comprising a linear pattern printing layer formed on the surface of the linear low-density polyethylene film has a white conductive layer. A conductive paint layer containing conductive potassium titanate whiskers, and the antistatic effect of the conductive paint layer does not decrease even in a high-temperature, high-humidity atmosphere. It exerts a function that cannot be achieved by applying an agent or filling a general-purpose antistatic agent, that is, a permanent antistatic effect that is not affected by the temperature or humidity in the atmosphere.
【0025】[0025]
【実施例】以下、本発明の透明・導電・防湿性積層シー
トの具体的な構成を、製造実施例に基づいて説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS The concrete constitution of the transparent, conductive and moisture-proof laminated sheet of the present invention will be described below based on production examples.
【0026】「実施例1」酸化錫・アンチモン系顔料
(三菱マテリアル (株) :T−1)100重量部と、塩
化ビニルの含有量が80重量%の塩化ビニル・酢酸ビニ
ル共重合体樹脂とポリメチルメタクリレート樹脂との混
合樹脂(混合重量比:1/1)33重量部と、分散剤
(ホモゲール L 1820)1.5重量部とを、トル
エンとメチルエチルケトンとの等量の混合溶剤に溶解
し、透明な導電性インキ層形成用の塗料(A)を調整し
た。Example 1 100 parts by weight of tin oxide / antimony pigment (Mitsubishi Materials Corporation: T-1) and a vinyl chloride / vinyl acetate copolymer resin having a vinyl chloride content of 80% by weight 33 parts by weight of a mixed resin (mixing weight ratio: 1/1) with a polymethyl methacrylate resin and 1.5 parts by weight of a dispersing agent (Homogel L 1820) are dissolved in an equal amount of a mixed solvent of toluene and methyl ethyl ketone. The paint (A) for forming a transparent conductive ink layer was prepared.
【0027】次いで、[図1]において、アルミニウム
蒸着層「導電性:200Ω」を有する厚さ25μの2軸
延伸ポリエチレンテレフタレートフィルムからなる透明
な第2の基材用フィルム「熱線遮断フィルム:ルミクー
ル Mタイプ (# 25)FB−50シルバー」2の2
軸延伸ポリエチレンテレフタレートフィルム面に、前述
の塗料(A)をグラビアコート法によって塗工し、厚さ
3μの透明な導電性インキ層3を形成し、続いて、該透
明な導電性インキ層3の表面に、下記組成(B)による
表面樹脂層形成用の塗工剤をグラビアコートでの網目コ
ート法によって塗工し、厚さ3μ,ドットの幅(a) 50
0〜600μ、隣接するドット同士の間の間隔(b) 80
〜100μからなる多数のドット群による表面樹脂層4
を形成した。Next, in FIG. 1, a transparent second base film made of a biaxially stretched polyethylene terephthalate film having a thickness of 25 μm and having an aluminum deposited layer “conductivity: 200 Ω” “Heat shielding film: Lumicool M” Type ( # 25) FB-50 Silver "2 of 2
The above-mentioned paint (A) is applied to the surface of the axially stretched polyethylene terephthalate film by a gravure coating method to form a transparent conductive ink layer 3 having a thickness of 3 μm. A coating agent for forming a surface resin layer having the following composition (B) is applied to the surface by a mesh coating method using a gravure coat, and has a thickness of 3 μm and a dot width (a) of 50.
0 to 600 μ, spacing between adjacent dots (b) 80
Surface resin layer 4 composed of a large number of dot groups of 100 μm
Was formed.
【0028】 塗工剤(B) セルロースアセテート・・・・・・・・・・・・・・・・・・・・1.2重量部 塩化ビニル・酢酸ビニル共重合体樹脂・・・・10.0重量部 ウレタン樹脂・・・・・・・・・・・・・・・・・・・・・・・・・・・・1.4重量部 ポリエステルポリオール・・・・・・・・・・・・・・・・・・3.0重量部 可塑剤・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・2.0重量部 ワックス・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・1.0重量部 メチルエチルケトン・・・・・・・・・・・・・・・・・・・・30.3重量部 トルエン・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・21.6重量部 酢酸エチル・・・・・・・・・・・・・・・・・・・・・・・・・・・・29.6重量部Coating agent (B) Cellulose acetate 1.2 parts by weight Vinyl chloride / vinyl acetate copolymer resin 10 0.0 parts by weight Urethane resin 1.4 parts by weight Polyester polyol 3.0 parts by weight Plasticizer 2.0 parts by weight wax 1.0 part by weight methyl ethyl ketone 30.3 parts by weight Toluene 21.6 parts by weight ethyl acetate ... 29.6 parts by weight
【0029】しかる後に、先の第1の基材用フィルム2
のアルミニウム蒸着層面に、酸化錫蒸着層を有する厚さ
12μの2軸延伸ポリエチレンテレフタレートフィルム
からなる第1の基材用フィルム5の酸化錫蒸着層面をウ
レタン系接着剤層6によって積層した。なお、符号10
で表示される部分が第1の基材用フィルム5と第2の基
材用フィルム2とによる基材シートである。Thereafter, the first base material film 2
Of the first base material film 5 made of a biaxially stretched polyethylene terephthalate film having a thickness of 12 μm and having a tin oxide vapor-deposited layer, was laminated with a urethane-based adhesive layer 6. Note that reference numeral 10
The portion indicated by is a base sheet made of the first base film 5 and the second base film 2.
【0030】さらに、第1の基材用フィルム5の2軸延
伸ポリエチレンテレフタレートフィルム面に対し、厚さ
20μのポリエチレン樹脂の押出しコート層7を利用
し、裏面に白色導電性チタン酸カリウムウィスカーを含
有する塗工剤による平行線状のパターン印刷層からなる
導電性塗料層9を有する厚さ30μの線状低密度ポリエ
チレン樹脂フィルムすなわち静電気シールドフィルム
(大塚化学 (株) :フィルスタット)8を、前記導電性
塗料層9が最外層となるようにして貼着し、本発明の1
実施例品たる透明・導電・防湿性積層シート1を得た。Further, a 20 μm-thick polyethylene resin extrusion coat layer 7 is used on the biaxially oriented polyethylene terephthalate film surface of the first base film 5, and white conductive potassium titanate whisker is contained on the back surface. A 30 μm thick linear low-density polyethylene resin film having an electrically conductive coating layer 9 consisting of a parallel linear pattern printing layer made of a coating agent to be changed, that is, an electrostatic shielding film (Otsuka Chemical Co., Ltd .: Filstat) 8 The conductive paint layer 9 is adhered so as to be the outermost layer.
Example 1 A transparent, conductive and moisture-proof laminated sheet 1 as an example product was obtained.
【0031】[実験]前述の実施例で得られた各透明・
導電・防湿性積層シートの諸物性を[表1]に示す。な
お、[表1]に示す物性は下記の通りの方法によって測
定した値である。EXPERIMENTS
Table 1 shows various physical properties of the conductive and moisture-proof laminated sheet. The physical properties shown in Table 1 are values measured by the following methods.
【0032】1: 表面固有抵抗(Ω/ □) アドバンテスト製TR8601 2: 半減期(秒) スタチックオネストメーター(TOA製S−5109) 3: 表面層脱落試験 セロファン粘着テープによる試験 4: 突き刺し強度(kg) 食品衛生法20号 5: ヒートシール強度(kg/15mm幅) 6: 透湿度(g/m2 ・day) JIS Z 0208 7: 酸素透過度(g/m2 ・day ・atm)23
℃,0%RH 8: 静電シールド特性(V) MIL−B−1705C1: Surface specific resistance (Ω / □) TR8601 manufactured by Advantest 2: Half life (second) Static honest meter (S-5109 manufactured by TOA) 3: Surface layer detachment test Cellophane adhesive tape test 4: Puncture strength ( kg) Food Sanitation Law No. 20 5: Heat seal strength (kg / 15 mm width) 6: Moisture permeability (g / m 2 · day) JIS Z 0208 7: Oxygen permeability (g / m 2 · day · atm) 23
° C, 0% RH 8: Electrostatic shielding characteristics (V) MIL-B-1705C
【0033】[0033]
【表1】 [Table 1]
【0034】「実施例2」実施例1による透明・導電・
防湿性積層シート1の構成において、酸化錫蒸着層を有
する厚さ12μの2軸延伸ポリエチレンテレフタレート
フィルムからなる第1の基材用フィルム5の代わりに、
酸化アルミニウム蒸着層を有する厚さ12μの2軸延伸
ポリエチレンテレフタレートフィルムを第1の基材用フ
ィルムとして利用する以外は全て実施例1の透明・導電
・防湿性積層シートと対応する構成を具備する本発明の
透明・導電・防湿性積層シートの別の実施例品を得た。"Example 2"
In the structure of the moisture-proof laminated sheet 1, instead of the first base film 5 composed of a biaxially stretched polyethylene terephthalate film having a thickness of 12 μm having a tin oxide vapor-deposited layer,
Except for using a biaxially stretched polyethylene terephthalate film having a thickness of 12 μm having an aluminum oxide vapor-deposited layer as a first base film, a book having a configuration corresponding to the transparent, conductive, and moisture-proof laminated sheet of Example 1 Another example of the transparent, conductive and moisture-proof laminated sheet of the invention was obtained.
【0035】[0035]
【効果】本発明の透明・導電・防湿性積層シートは、主
として包装袋用の包装用材として利用されるもので、外
部からの要因による静電気障害を防止し、また、包装袋
内の内容物と包装用材との間の摩擦による静電気障害を
防止し、しかも、内容物を包装袋の外部から視認し得る
透明性を有し、さらに、水蒸気,酸素,炭酸ガス等に対
するバリヤー性、耐突き刺し性,表面保護性等の機械的
性能において優れ、かつ、ヒートシールによる封緘性能
をも有している。The transparent, conductive, and moisture-proof laminated sheet of the present invention is mainly used as a packaging material for a packaging bag, and prevents static electricity damage due to external factors. Prevents static electricity damage due to friction with the packaging material, and has transparency so that the contents can be visually recognized from the outside of the packaging bag. Furthermore, it has barrier properties against water vapor, oxygen, carbon dioxide gas, etc. It is excellent in mechanical performance such as surface protection and has sealing performance by heat sealing.
【0036】本発明の透明・導電・防湿性積層シート
は、これらの特性により特に静電気による障害を受け易
い物品、例えばICやLSI等の電子部品を包装する包
装袋として利用され、これらの物品の保存性能において
極めて優れた性質を有する。The transparent / conductive / moisture-proof laminated sheet of the present invention is used as a packaging bag for packaging electronic components such as ICs and LSIs which are particularly susceptible to static electricity due to these characteristics. It has extremely excellent properties in storage performance.
【0037】さらに、本発明の透明・導電・防湿性積層
シートは、静電シールド特性(MIL−B−1705)
に関して30V以下の数値を有し、MIL規格の静電シ
ールド特性をクリヤーする包装袋となるため、利用価値
に優れた効果を有する。Further, the transparent, conductive and moisture-proof laminated sheet of the present invention has an electrostatic shielding property (MIL-B-1705).
Has a numerical value of 30 V or less, and is a packaging bag that clears the electrostatic shielding characteristics of the MIL standard, and thus has an excellent effect of utility value.
【図1】本発明の透明・導電・防湿性積層シートの1実
施例品を模型的に示す断面図である。FIG. 1 is a cross-sectional view schematically showing a transparent, conductive and moisture-proof laminated sheet according to an embodiment of the present invention.
【図2】本発明の透明・導電・防湿性積層シートにおけ
る表面保護層のドット群の状態を説明する平面図であ
る。FIG. 2 is a plan view illustrating a state of a dot group of a surface protective layer in the transparent, conductive, and moisture-proof laminated sheet of the present invention.
1…透明・導電・防湿性積層シート 2…厚さ20〜400Åのアルミニウム蒸着層を有する
第2の基材用フィルム 3…透明な導電性インキ層 4…多数のドット群による表面樹脂層 5…酸化錫,酸化珪素または酸化アルミニウムによる厚
さ20〜400Åの蒸着層を有する第1の基材用フィル
ム 6…接着剤層 7…ポリエチレン樹脂の押出しコート層 8…線状低密度ポリエチレンフィルム層 9…線状のパターン印刷層からなる導電性塗料層 10…基材シートDESCRIPTION OF SYMBOLS 1 ... Transparent / conductive / moisture-proof laminated sheet 2 ... Second base film having a 20 to 400 mm thick aluminum vapor-deposited layer 3 ... Transparent conductive ink layer 4 ... Surface resin layer composed of many dot groups 5 ... First base material film having a deposited layer of 20 to 400 mm thick of tin oxide, silicon oxide or aluminum oxide 6 ... Adhesive layer 7 ... Extruded coat layer of polyethylene resin 8 ... Linear low density polyethylene film layer 9 ... Conductive paint layer consisting of a linear pattern printing layer 10 ... Base sheet
Claims (3)
ウムによる厚さ20〜400Åの蒸着層を有する第1の
基材用フィルムと、厚さ20〜400Åのアルミニウム
蒸着層を有する第2の基材用フィルムとを、第1の基材
用フィルムの酸化錫,酸化珪素または酸化アルミニウム
による蒸着層面と第2の基材用フィルムのアルミニウム
蒸着層面とが接当するようにして接着させた積層シート
からなる基材シートと、該基材シートの一方の面に形成
されている透明な導電性インキ層と、該透明な導電性イ
ンキ層の表面に多数のドット状をなすようにして積層さ
れている表面樹脂層と、前記基材シートの他方の面に形
成されている線状低密度ポリエチレンフィルム層と、該
線状低密度ポリエチレンフィルム層に積層されている線
状のパターン印刷層からなる導電性塗料層とを有するこ
とを特徴とする透明・導電・防湿性積層シート。1. A film for a first substrate having a deposited layer of tin oxide, silicon oxide or aluminum oxide having a thickness of 20 to 400 °, and a second substrate having a deposited layer of aluminum having a thickness of 20 to 400 °. It is composed of a laminated sheet in which a film is adhered such that the surface of the first base material film made of tin oxide, silicon oxide or aluminum oxide comes into contact with the surface of the second base material film. A base sheet, a transparent conductive ink layer formed on one surface of the base sheet, and a surface which is laminated on the surface of the transparent conductive ink layer so as to form a number of dots. A resin layer, a linear low-density polyethylene film layer formed on the other surface of the base sheet, and a linear pattern printing layer laminated on the linear low-density polyethylene film layer. A transparent, conductive and moisture-proof laminated sheet comprising a conductive paint layer comprising
ドット状をなすようにして積層されている表面樹脂層
が、厚さ1〜100μ、ドットの幅(a) が100〜10
00μ、隣接するドットとドットとの間の間隔(b) が5
0〜200μで、かつ、{ドットの幅 (a)/隣接するド
ットとドットとの間の間隔(b) }=1〜20であること
を特徴とする請求項1記載の透明・導電・防湿性積層シ
ート。2. A surface resin layer having a large number of dots laminated on the surface of a transparent conductive ink layer having a thickness of 1 to 100 μm and a dot width (a) of 100 to 10
00μ, interval (b) between adjacent dots is 5
2. The transparent, conductive and moisture-proof according to claim 1, wherein 0 to 200 [mu] and {dot width (a) / interval between adjacent dots (b)} = 1 to 20. Laminated sheet.
る線状低密度ポリエチレンフィルム層が厚さ20〜10
0μの線状低密度ポリエチレン樹脂フィルムからなり、
該線状低密度ポリエチレンフィルム層に積層されている
線状のパターン印刷層からなる導電性塗料層が、白色導
電性チタン酸カリウムウィスカーを含有する導電性塗料
層からなることを特徴とする請求項1または請求項2記
載の透明・導電・防湿性積層シート。3. The linear low-density polyethylene film layer formed on the other surface of the substrate sheet has a thickness of 20 to 10 mm.
0μ linear low density polyethylene resin film,
The conductive paint layer comprising a linear pattern printing layer laminated on the linear low density polyethylene film layer, wherein the conductive paint layer comprises a white conductive potassium titanate whisker. The transparent / conductive / moisture-proof laminated sheet according to claim 1 or 2.