JP3194110U - Seal for deformed / three-dimensional curved surface using transfer seal - Google Patents
Seal for deformed / three-dimensional curved surface using transfer seal Download PDFInfo
- Publication number
- JP3194110U JP3194110U JP2014004526U JP2014004526U JP3194110U JP 3194110 U JP3194110 U JP 3194110U JP 2014004526 U JP2014004526 U JP 2014004526U JP 2014004526 U JP2014004526 U JP 2014004526U JP 3194110 U JP3194110 U JP 3194110U
- Authority
- JP
- Japan
- Prior art keywords
- transparent film
- film layer
- layer
- seal
- transparent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
【課題】任意画像の印刷が可能な転写シールを利用し、柔軟性と堅牢性のある異形・3次元曲面対応シールを提供する。【解決手段】被着体に貼着する面側から順に、粘着剤層7、不透明白色又は不透明色彩色又は透明の塗着層B、第1透明膜層A、反転印刷された転写シール面の印刷層5を第1透明膜層に接したシート基材3、シート基材の正画像が見える面に形成した第2透明膜層C、及び第2透明膜層の上に形成した第3透明膜層Dとからなる。反転印刷層のシート基材を、背面に不透明又は透明な塗着層がある第1透明膜層と第2透明膜層で挟着し、さらに第2透明膜層の上に第3透明膜層を設けることで、画像の鮮明化と、正画像の可視化、曲面対応の柔軟性と堅牢性を達成した。【選択図】図1Disclosed is a deformable / three-dimensional curved surface seal having flexibility and robustness using a transfer seal capable of printing an arbitrary image. An adhesive layer 7, an opaque white or opaque colored or transparent coating layer B, a first transparent film layer A, and a reversely printed transfer seal surface are sequentially arranged from the surface side to be adhered to an adherend. The sheet substrate 3 in contact with the first transparent film layer, the second transparent film layer C formed on the surface on which the positive image of the sheet substrate can be seen, and the third transparent film formed on the second transparent film layer It consists of a film layer D. A sheet substrate of the reverse printing layer is sandwiched between a first transparent film layer and a second transparent film layer having an opaque or transparent coating layer on the back surface, and a third transparent film layer is further formed on the second transparent film layer. By providing this, the image was sharpened, the positive image was visualized, and the flexibility and robustness for curved surfaces were achieved. [Selection] Figure 1
Description
本考案は、任意画像の印刷が可能な転写シールを利用した所望の位置に粘着が簡便な異形・3次元曲面対応シールに関する。 The present invention relates to a deformable / three-dimensional curved surface seal that can be easily adhered to a desired position using a transfer seal capable of printing an arbitrary image.
普及しているインクジェットプリンターを用いて、好みで任意の画像や図柄、文字を印刷できる転写シールの印刷シートを利用して作製するシールで、湾曲面や若干の凹凸面を有する被着体にも歪みなく対応できる柔軟性があり、被着体に合わせてカットがしやすく、印刷面の画像が鮮明で丈夫な異形・3次元曲面対応シールに関するものである。 It is a sticker made using a printing sheet of a transfer sticker that can print any image, pattern, or character as desired using a popular inkjet printer. It can also be used on adherends with curved surfaces or slightly uneven surfaces. The present invention relates to a seal for deformed / three-dimensional curved surfaces that has flexibility to cope with distortion, is easy to cut in accordance with an adherend, and has a clear and durable printed surface image.
従来、プリンターによって任意の模様が印刷可能な印刷シートと、この印刷シートを皮膚に貼付可能な貼着手段を装備する「タトゥーシール」(特開2000−160111号)や、一般家庭に普及しているインクジェットプリンターや複写機、水性又は油性の筆記用具を用いて、需要者が誰でも希望のオリジナルな転写シールを簡便に作成・使用できる転写シール用キットとその転写使用法(特開2001−199194号 特許第3266197号 平14.1.11)があった。 Conventionally, a “tattoo seal” (Japanese Patent Laid-Open No. 2000-160111) equipped with a printing sheet on which an arbitrary pattern can be printed by a printer, and a sticking means capable of sticking the printing sheet to the skin, has been widely used in general households. A transfer seal kit that allows any user to easily create and use an original transfer seal desired by an ink-jet printer, copying machine, water-based or oil-based writing instrument, and its transfer usage method (Japanese Patent Laid-Open No. 2001-199194) Japanese Patent No. 3266197 Hei 14.1.11).
従来技術による「タトゥーシール」・「転写シール」の商品名で市販される製品が備える転写目的の印刷用シートは、インク受容層である薄膜のシート基材に、水で湿らして分離できる離型吸水紙が積層一体化した構造である。 The printing sheet for transfer purposes provided in the products marketed under the trade names of “tattoo seal” and “transfer seal” according to the prior art is a film sheet substrate that is an ink receiving layer, which can be separated by moistening with water. This is a structure in which water-absorbing paper is laminated and integrated.
希望の画像を被着体に転写したい場合は、これらの転写シールと両面粘着シートの組み合わせや、転写シール用キットで行っていた。
図6は、従来技術による係る市販製品が備える、転写シールとしての印刷用シート(1)と粘着シート(2)の模式断面図で、図中の矢印は、反転印刷面に粘着シートを張ることを示し、図7は、その転写シールを被着体(T)に貼り付けた状態の側面断面図である。
図6で示すように、従来技術による係る市販製品でシールを作成するには反転印刷面に粘着層を張って、被着体(T)に貼り付けることで行っている。
When a desired image is to be transferred to an adherend, the transfer seal and double-sided pressure-sensitive adhesive sheet are combined or a transfer seal kit is used.
FIG. 6 is a schematic cross-sectional view of a printing sheet (1) and an adhesive sheet (2) as a transfer seal provided in a commercial product according to the prior art, and the arrows in the figure indicate that the adhesive sheet is stretched on the reverse printing surface. FIG. 7 is a side sectional view showing a state in which the transfer seal is attached to the adherend (T).
As shown in FIG. 6, in order to create a seal with a commercial product according to the prior art, an adhesive layer is stretched on the reverse printing surface, and is adhered to the adherend (T).
需要者が手持ちのインクジェットプリンター等の機器で個々の嗜好を投影させた任意画像の印刷を当該印刷用シートに施し、係る市販製品が備える両面粘着シートを用いて目的の被着体(T)に貼着後、貼り付け状態にある印刷用シートを水で湿らして離型吸水紙(剥離紙)を分離することで、被着体(T)への貼着は薄膜のシート基材のみとなり、結果として、当該シート基材に印刷された任意画像が被着体(T)と一体化しているように見える薄い装飾体となる。 A user prints an arbitrary image in which individual preferences are projected by a device such as an ink jet printer held by the customer on the printing sheet, and the target adherend (T) is used by using a double-sided pressure-sensitive adhesive sheet provided in the commercial product. After adhering, the printing sheet in the affixed state is moistened with water to separate the release water-absorbing paper (release paper), so that the adhering to the adherend (T) is only a thin film base material. As a result, it becomes a thin decorative body in which the arbitrary image printed on the sheet base material appears to be integrated with the adherend (T).
特開2001−199194号「転写シール用キットとその転写使用法」では、粘着面に空気が封じ込められて、気泡による波打ち状態や皺寄り状態を改良するために、シート基材への4層のコーティングや空気抜き用の凸凹状の粗面化が行われている。 In Japanese Patent Laid-Open No. 2001-199194, “transfer seal kit and transfer method thereof”, air is confined to the adhesive surface, and in order to improve the wavy state and the wrinkled state due to bubbles, Uneven surface roughening is performed for coating and air venting.
従来技術の転写シールとなる印刷用シートは、薄膜のシート基材に不透明な離型吸水紙を積層することで、プリンター装置の印刷に適合する所定の厚さを確保している。
使用する際には、印刷用シートの一面に任意画像を反転印刷し、被着体(T)への貼着手段としての両面粘着シートを印刷用シートの印刷面に貼付し、画像周辺を適当な大きさにカットし被着体(T)に貼付してから印刷シートの離型吸水紙である剥離紙を剥がすことになる。
A printing sheet serving as a transfer seal according to the prior art has a predetermined thickness suitable for printing by a printer apparatus by laminating an opaque release water-absorbing paper on a thin sheet base material.
When using, reverse print an arbitrary image on one side of the printing sheet, stick a double-sided pressure-sensitive adhesive sheet as a means of sticking to the adherend (T) on the printing side of the printing sheet, and properly surround the image The release paper, which is the release water-absorbing paper of the printing sheet, is peeled off after being cut to a proper size and attached to the adherend (T).
そのため、被着体(T)に貼る場合に離型吸水紙である不透明な剥離紙が上面側になるために、目的の被着体(T)に貼付する印刷面上の任意画像が目視できなくなり、目的の被着体(T)における所望位置への貼付作業は、微調整が大変困難になる上、貼付後に剥離しての修正再作業は、薄膜であるシート基材の破損を招きやすく、施工性の点で問題があった。 Therefore, since an opaque release paper, which is a release water-absorbing paper, is on the top side when pasted on the adherend (T), an arbitrary image on the print surface to be pasted on the target adherend (T) can be visually observed. Fine adjustment is very difficult for the pasting operation to the desired position on the target adherend (T), and correction and rework after peeling after the pasting tends to cause damage to the sheet base material which is a thin film. There was a problem in terms of workability.
また、従来の薄膜であるシート基材は伸縮性に乏しく、目的の被着体(T)が異形・3次元曲面(半球面の様に2方向に曲率を有する形状)等である場合には、その形状に馴染み難い。
十分馴染みえないまま貼付した状態で印刷用シートに積層された離型吸水紙を剥離すると、任意画像の印刷をした薄膜のシート基材に、曲面のしわ、弛み、または浮き上がりや破損等が生じてしまい、所望の仕上がりが得られないという問題があった。
図8の上段の写真は、ネイルチップ(つけ爪)の先端部分に従来シールを貼付した状態の拡大図であるが、シールは薄く、ネイルチップ(つけ爪)が3次元曲面を有する形状で曲面であるためもあって、しわや破損ができることを示している。
In addition, the sheet base material which is a conventional thin film has poor stretchability, and the target adherend (T) is an irregular shape, a three-dimensional curved surface (a shape having a curvature in two directions like a hemispherical surface) or the like. It is difficult to get used to the shape.
If the release water-absorbing paper laminated on the printing sheet is peeled off while not being familiar enough, wrinkles, slack, lifting, breakage, etc. of the curved surface will occur on the thin-film sheet substrate on which any image is printed. Therefore, there is a problem that a desired finish cannot be obtained.
The upper photo in FIG. 8 is an enlarged view of a state where a conventional seal is pasted on the tip of the nail tip (false nail), but the seal is thin and the nail tip (false nail) has a three-dimensional curved surface. This means that wrinkles and damage can be achieved.
更に、任意画像の印刷機器として、係る市販製品が指定するインクジェット記録方式のプリンターは、装備する専用インクの性質として透過性を有し、更に、白色の印刷が不可能であることから、当該市販製品が備える印刷用シートの印刷面に当たる透視可能で無色透明なシート基材に印刷される任意画像が白色部分を有する場合、その印刷画像の白色部分は無色透明となりまた、他の部分においても印刷色によっては当該専用インクの性質である透過性が影響することで、目的の被着体(T)の地色が不均一な白色や白色以外の色を有する場合、所望の色彩が再現できないという問題があった。 Furthermore, as a printing device for arbitrary images, an ink jet recording system printer designated by such a commercial product has transparency as a property of the dedicated ink to be equipped, and further, since white printing is impossible, When an arbitrary image printed on a transparent, colorless and transparent sheet base material that hits the printing surface of the printing sheet provided in the product has a white portion, the white portion of the printed image becomes colorless and transparent, and also prints in other portions. Depending on the color, the transparency, which is the property of the dedicated ink, affects the desired color when the ground color of the target adherend (T) has a non-uniform white color or a color other than white. There was a problem.
このような問題の解決に応えうるものとして、白色の両面粘着シートを備えた市販製品があり、例えば、エレコム株式会社「タトゥーシール(品番:EJP−TATA4W)」、エーワン合同会社「転写シール(品番:51207)」等がある。 As a solution to such a problem, there are commercially available products equipped with a white double-sided pressure-sensitive adhesive sheet. For example, ELECOM Co., Ltd. : 51207) ".
任意画像の印刷を施した透視可能で無色透明なシート基材と白色以外の色を有する目的の被着体(T)の間に貼着手段として位置する両面粘着シートを白色にすることで、目的の被着体(T)の色に影響されることなく任意画像本来の色彩を再現させる効果を期待したものであるが、係る市販製品が備える白色の両面粘着シートはキメが荒く、所望の色彩の再現は依然困難であり、小さくなるほど画像の鮮明さが要求される装飾を補う背景色としては、特に不適切であった。 By making the double-sided pressure-sensitive adhesive sheet white as a sticking means between a transparent, colorless and transparent sheet base material on which an arbitrary image has been printed and a target adherend having a color other than white (T), Expected to reproduce the original color of an arbitrary image without being affected by the color of the target adherend (T), but the white double-sided PSA sheet provided by such commercial products is rough and has a desired texture. Color reproduction is still difficult, and it is particularly inappropriate as a background color to supplement decorations that require a clearer image as the image gets smaller.
両面粘着層を白色にしても、圧接でその白色が不均等になることもあり、むしろ白色はムラになり、模様を感じさせる不均一色彩になっている。 Even if the double-sided pressure-sensitive adhesive layer is white, the white color may become uneven due to the pressure contact. Rather, the white color becomes uneven and has a non-uniform color that makes the pattern feel.
本考案は上記従来のこのような不都合を改善し、従来技術による製品の利用時に生じる問題点を解決するためになされたものであり、目的の被着体(T)における所望位置への貼着作業の微調整が簡便であって、異形・3次元曲面の形状を有する各種被着体(T)にも貼着できる任意画像の印刷が可能な転写シールを利用した所望の位置に粘着が簡便な異形・3次元曲面対応シールを提供することを目的とする。 The present invention has been made in order to improve the above-described conventional inconveniences and solve the problems that occur when using products according to the prior art, and is applied to a desired position on a target adherend (T). Easy adjustment of work, easy adhesion at desired position using transfer sticker that can print arbitrary images that can be attached to various adherends (T) with irregular or three-dimensional curved shapes An object of the present invention is to provide a seal corresponding to a deformed / three-dimensional curved surface.
本考案の目的は、異形・3次元曲面(半球面の様に2方向に曲率を有する形状)の形状を有する各種被着体(T)、例えば3次元曲面である人体の爪 爪に貼るネイルチップ(つけ爪)、小型携帯機器のボタン、機器に設けられたブランド用立体小突起、といった比較的小型で貼布位置が定められた被着体(T)へ適するシールであって、曲面などへの追随性に優れた柔軟性を有し、画像が鮮明であり、かつ簡便に所望の位置に貼着できるシールの開発である。
特に貼着面積の小さい被着体(T)に好適で、任意画像の印刷が可能な転写シールを利用し、所望の特定位置に粘着が簡便にできる異形・3次元曲面対応シールの開発である。
The object of the present invention is to apply various adherends (T) having a deformed shape and a three-dimensional curved surface (a shape having a curvature in two directions like a hemisphere), for example, a nail to be applied to a nail of a human body having a three-dimensional curved surface. It is a seal suitable for adherends (T) that are relatively small in size, such as a chip (false nail), a button of a small portable device, and a three-dimensional small projection for a brand provided on the device, and having a curved surface, etc. It is the development of a seal that has excellent flexibility in following, has a clear image, and can be easily attached to a desired position.
It is particularly suitable for adherends (T) with a small sticking area and uses a transfer sticker that can print arbitrary images, and develops a sticker for deformed and three-dimensional curved surfaces that can easily stick to a specific position. .
本考案は、次の1〜6の6層からなることを特徴とする転写シールを利用した異形・3次元曲面対応シールである。
1:シート基材に形成された画像が反転印刷された印刷層。
2:前記シート基材の印刷層の上に形成した第1透明膜層。
3:前記第1透明膜層の上に形成した不透明白色又は不透明色彩色又は透明の塗着層。
4:前記塗着層の上に形成した粘着剤層。
5:前記反転印刷した画像が正画像として目視できる当該前記シート基材の面を被覆する第2透明膜層。
6:第2透明膜層の上に形成した第3透明膜層。
The present invention is a deformable / three-dimensional curved surface seal using a transfer seal characterized by comprising the following six layers of 1-6.
1: Print layer in which an image formed on a sheet base material is reversely printed.
2: The 1st transparent film layer formed on the printing layer of the said sheet | seat base material.
3: Opaque white or opaque colored or transparent coating layer formed on the first transparent film layer.
4: A pressure-sensitive adhesive layer formed on the coating layer.
5: The 2nd transparent film layer which coat | covers the surface of the said sheet | seat base material which can visually recognize the said reverse printed image as a normal image.
6: A third transparent film layer formed on the second transparent film layer.
さらに、前記塗着層が、不透明な水性アクリル絵の具で無毒性の蛍光物質を含んでいる塗着層であることも特徴のひとつである。 Further, it is one of the characteristics that the coating layer is a coating layer containing an opaque water-based acrylic paint and containing a non-toxic fluorescent material.
又、前記第1透明膜層、第2透明膜層、第3透明膜層の一つ以上が、常温で空気中で揮発する香り成分を含んでいる転写シールを利用した異形・3次元曲面対応シールを提案する。 In addition, one or more of the first transparent film layer, the second transparent film layer, and the third transparent film layer can handle irregular or three-dimensional curved surfaces using a transfer seal containing a scent component that volatilizes in air at room temperature. Suggest a seal.
具体的には、転写シールのシート基材に、インクジェット記録方式のプリンターで任意の画像が反転印刷された印刷層と、前記シート基材の印刷層の表面の上に即ち上層になるように、トップコートとして乾性油を成分に含有する市販の例えば透明ネイルエナメルよる第1透明膜層と、前記第1透明膜層の表面の上に即ち上層になるように、不透明で白色の水性アクリル絵の具の塗着層を形成している。
なお、塗着層は、基本は不透明白色であるが、稀に被着体(T)が白色でその地色を利用したい場合があるが、画像の鮮明度が許容範囲であればその場合の塗着層は透明材や半透明材、或いは不透明色彩色で代替形成してもよい。
Specifically, on the sheet base material of the transfer seal, a printing layer in which an arbitrary image is reversely printed by a printer of an ink jet recording system, and on the surface of the printing layer of the sheet base material, that is, an upper layer, A first transparent film layer made of, for example, a transparent nail enamel, which contains a drying oil as a top coat, and an opaque white aqueous acrylic paint on the surface of the first transparent film layer, that is, an upper layer. A coating layer is formed.
The coating layer is basically opaque white, but in rare cases the adherend (T) may be white and the background color is used. However, if the sharpness of the image is within an allowable range, The coating layer may be alternatively formed with a transparent material, a translucent material, or an opaque color.
その前記不透明で白色の水性アクリル絵の具の塗着層の上層に、両面粘着シートによる粘着剤層を形成する。 A pressure-sensitive adhesive layer made of a double-sided pressure-sensitive adhesive sheet is formed on the coating layer of the opaque white aqueous acrylic paint.
反転印刷した任意画像が正画像として目視できる当該前記シート基材の印刷層の裏面(保護材である離型吸水紙を剥離した面)に、前記第1透明膜層と同様の、トップコートとして乾性油を成分に含有する市販の透明ネイルエナメルの第2透明膜層を形成し、前記第2透明膜層の表面の上に即ち上層になるように、前記第1・第2透明膜層と同様の、トップコートとして乾性油を成分に含有する市販の透明ネイルエナメルの第3透明膜層を形成している。 As a top coat, similar to the first transparent film layer, on the back surface (the surface from which the release water-absorbing paper as a protective material is peeled off) of the printed sheet of the sheet base material in which the reversely printed arbitrary image can be viewed as a normal image Forming a second transparent film layer of a commercially available transparent nail enamel containing a drying oil as a component, and on the surface of the second transparent film layer, that is, as an upper layer, the first and second transparent film layers; Similarly, a third transparent film layer of a commercially available transparent nail enamel containing a drying oil as a top coat is formed.
即ち本考案の転写シールを利用した異形・3次元曲面対応シールは、被着体(T)に貼着する面側から順に、粘着剤層、塗着層、第1透明膜層、反転印刷された面の印刷層を第1透明膜層に接するシート基材、第2透明膜層、第3透明膜層とからなり、この6層から成ることを要旨とする。
反転印刷された画像の印刷シートは、白い背面をもって鮮明で上下面を第1透明膜層と第2透明膜層で挟着され、正画像を視認できる状態で第3透明膜層に被覆されて被着体(T)に貼付される。
粘着剤層には、カットラインなどが線引き記入できる剥離紙が付設されてカットしやすいものも提案する。
That is, the deformed / three-dimensional curved surface seal using the transfer seal of the present invention is printed in reverse order from the surface side to be adhered to the adherend (T), the adhesive layer, the coating layer, the first transparent film layer. The printed layer on the back surface is composed of a sheet base material in contact with the first transparent film layer, a second transparent film layer, and a third transparent film layer, and the summary is composed of these six layers.
The printed sheet of the reversely printed image is clear with a white back surface, and the upper and lower surfaces are sandwiched between the first transparent film layer and the second transparent film layer, and the third transparent film layer is coated so that a normal image can be visually recognized. Affixed to the adherend (T).
We also propose an adhesive layer that is easy to cut with release paper attached to the cut line.
本考案に係る異形・3次元曲面対応シールよれば次の技術的効果が得られる。
本考案では、シート基材の図案等印刷層に、硬化後に耐水性を有する柔軟な塗膜を形成するトップコートと称される乾性油を成分に含有する市販の透明ネイルエナメルによる第1透明膜層(A)と第2透明膜層(C)で挟み、積層することで、異形・3次元曲面への追随性に優れた柔軟性と、粘着体としての堅牢性を向上させている。
第1透明膜層(A)と第2透明膜層(C)で印刷層を挟むことで、柔軟性と十分な表面備えて表面保護を増大させている。
According to the modified / three-dimensional curved surface seal according to the present invention, the following technical effects can be obtained.
In the present invention, a first transparent film made of a commercially available transparent nail enamel containing a drying oil called a top coat, which forms a flexible coating film having water resistance after curing, on a printed layer such as a design of a sheet base material By sandwiching and laminating between the layer (A) and the second transparent film layer (C), flexibility excellent in followability to a deformed / three-dimensional curved surface and robustness as an adhesive body are improved.
By sandwiching the print layer between the first transparent film layer (A) and the second transparent film layer (C), the surface protection is increased with flexibility and sufficient surface.
更に、図案図柄印刷層であるシート基材下に、例えば塗装用のスプレー機材であるエアーブラシを手段に、不透明で白色の水性アクリル絵の具による均一で薄膜の塗着層(B)を形成することにより、目的の被着体(T)の色に影響されることなく任意画像本来の色彩が再現可能となり、小さくなるほど画像の鮮明さが求められる装飾体としての品質を所望の水準まで向上させている。
更に、第2透明膜層(C)の表面の上にトップコートとして第3透明膜層(D)を形成している。
Furthermore, under the sheet base material, which is a design pattern printing layer, a uniform thin film coating layer (B) is formed with an opaque white aqueous acrylic paint using, for example, an air brush which is a spray equipment for painting. Thus, the original color of an arbitrary image can be reproduced without being influenced by the color of the target adherend (T), and the quality as a decorative body that requires a clearer image as the size decreases is improved to a desired level. Yes.
Further, a third transparent film layer (D) is formed as a top coat on the surface of the second transparent film layer (C).
第3透明膜層(D)は、被着体(T)の性質によっては、本考案の積層構造を備えた粘着体を目的の被着体(T)に貼着後に最上部の第2透明膜層(C)上に積層することもでき、又被着体(T)に貼着前に最上部の第2透明膜層(C)上に積層することもできるが、いずれの積層も、より一層の堅牢性の向上と、整えられた表面が光の反射を強め、装飾体としての艶を向上させる、美麗的効果がある。
また、前記の手段により前記シート基材(3)の表裏面に透明膜層を積層したことで、異形・3次元曲面、例えば半球面の様に2方向に曲率を有する形状等を有する各種被着体(T)、例えば3次元曲面である人体の爪といった被着体(T)への追随性に優れた柔軟性と、簡便に所望の位置に貼着できる優れた施工性と堅牢性がある。
爪などを装飾するシールとして使用するものでは、耐水性と柔軟性があり、貼着と剥離を数回繰り返すことができるという実用的効果もある。
本考案の実際の効果を示すために、図5として、本考案の転写シールを利用した異形・3次元曲面対応シールを、3次元曲面を有する形状で曲面のネイルチップ(つけ爪)に施した試作例の写真を示す。
曲面に歪みなく極めて鮮明に詳細に転写している。
図8では、上段に従来のシールの貼付状態を示し、下段に本考案のシールの貼付状態を拡大した比較写真を示すが、下段の写真に示す本考案のシールは厚みと柔軟性・こすれ耐久性・耐水性が増し、しわや破損のない貼付が可能になっている。
Depending on the properties of the adherend (T), the third transparent film layer (D) may be the second transparent uppermost portion after the pressure-sensitive adhesive body having the laminated structure of the present invention is attached to the target adherend (T). It can be laminated on the film layer (C), or can be laminated on the uppermost second transparent film layer (C) before being attached to the adherend (T). There is a beautiful effect that further enhances the fastness and the prepared surface enhances the reflection of light and improves the gloss as a decorative body.
Further, by laminating transparent film layers on the front and back surfaces of the sheet base material (3) by the above-mentioned means, various coatings having irregular or three-dimensional curved surfaces, for example, shapes having curvatures in two directions such as a hemispherical surface. Flexibility excellent in followability to adherend (T) such as a human body nail which is a three-dimensional curved surface, and excellent workability and robustness which can be easily attached to a desired position is there.
What is used as a seal for decorating nails and the like has water resistance and flexibility, and also has a practical effect that the sticking and peeling can be repeated several times.
In order to show the actual effect of the present invention, as shown in FIG. 5, a deformed / three-dimensional curved surface seal using the transfer seal of the present invention is applied to a curved nail tip (false nail) in a shape having a three-dimensional curved surface. A photograph of a prototype is shown.
It is transferred to the curved surface in a very clear detail without distortion.
In FIG. 8, the upper part shows the pasted state of the conventional seal, and the lower part shows an enlarged comparison of the pasted state of the seal of the present invention. And water resistance are increased, and it is possible to apply without wrinkles or damage.
以下、本考案に係る転写シールを利用した異形・3次元曲面対応シールを実施するための最良の形態及び実施例を図面の図1〜図5、図8に基づき詳細に説明する。 BEST MODE FOR CARRYING OUT THE INVENTION The best mode and embodiment for implementing a deformed / three-dimensional curved surface seal using a transfer seal according to the present invention will be described in detail with reference to FIGS.
従来の転写シールとなる印刷用シート(1)は、図6・図7に示すように薄膜のシート基材(3)に離型吸水紙である剥離紙(4)を積層している構成である。
反転印刷して使用するが印刷図柄を可視できるようにするために剥離紙は白色で、印刷や紙送りのための厚みを必要とする。
この構成では、目的の被着体(T)に貼付するときは剥離紙が上になるので印刷面上の任意画像が目視できなくなり、目的の被着体(T)における所望位置への貼付作業は、微調整が大変困難になる上、シール自体が極薄軟弱でかつ粘着剤があるため取り扱いが難しい面があり、貼付後に剥離しての再作業などは、薄膜であるシート基材(3)の破損を招きやすく、施工性の点で問題があった。
A conventional printing sheet (1) serving as a transfer seal has a structure in which a release paper (4) which is a release water-absorbing paper is laminated on a thin sheet substrate (3) as shown in FIGS. is there.
The reverse paper is used for reversal printing, but the release paper is white and needs a thickness for printing and paper feeding in order to make the printed pattern visible.
In this configuration, when attaching to the target adherend (T), the release paper is on top, so that an arbitrary image on the printing surface cannot be seen, and the target adherend (T) is attached to a desired position. In addition, fine adjustment is very difficult, and the seal itself is extremely thin and weak and has an adhesive, which makes it difficult to handle. The sheet base material (3 ) Was easily damaged, and there was a problem in terms of workability.
そこで本考案では、図2で示すように転写シートである印刷用シート(1)の印刷面に当たるシート基材(3)の下に積層一体化された該離型吸水紙である剥離紙(4)を、目的の被着体(T)への貼着前に剥離し、上下から透明膜層で挟着し、さらに上面に透明膜層を積層形成することで、当該シート基材(3)に反転印刷(バックプリント)した任意画像を、前記シート基材(3)の裏面から所望の正画像として目視できるように構成した。
本考案の異形・3次元曲面対応シールは、正画像として目視しながらその正画像を目的の被着体(T)における所望位置へ合わせて配置することができるので、その貼着作業では、位置の微調整が簡便にできる。
Therefore, in the present invention, as shown in FIG. 2, the release paper (4) which is the release water-absorbing paper laminated and integrated under the sheet base material (3) corresponding to the printing surface of the printing sheet (1) which is a transfer sheet. ) Before being attached to the target adherend (T), sandwiched by a transparent film layer from above and below, and further laminated with a transparent film layer on the upper surface, whereby the sheet substrate (3) An arbitrary image reversely printed (backprinted) on the back of the sheet base material (3) was configured to be visible as a desired positive image.
The sticker for deformed / three-dimensional curved surface according to the present invention can be arranged to match a desired position on the target adherend (T) while viewing as a positive image. Can be easily fine-tuned.
本考案に係る転写シールを利用した異形・3次元曲面対応シールを実施するための最良の形態は、次の1〜6の6層からなる形態のシールである。
1:シート基材(3)に形成された画像が反転印刷された印刷層(5)。
2:前記シート基材(3)の印刷層の上に形成した第1透明膜層(A)。
3:前記第1透明膜層(A)の上に形成した不透明白色又は不透明色彩色又は透明の塗着層(B)。
4:前記塗着層(B)の上に形成した粘着剤層(7)。
5:前記反転印刷した画像が正画像として目視できる当該前記シート基材の面を被覆する第2透明膜層(C)。
6:第2透明膜層(C)の上に形成した第3透明膜層(D)。
第1透明膜層(A)、第2透明膜層(C)、第3透明膜層(D)は、速乾性で、
乾性油を成分に含有する透明ネイルエナメルであるが、その組成である塗膜形成要素・可塑剤・溶剤は、その混合割合を各層の性能・役目に応じて調整している。
いずれの透明膜層も、被膜の強度(耐こすれ性)や光沢付与、画像の鮮明化のためのトップコートとしての透明層であるが、第1透明膜層(A)、第2透明膜層(C)は速乾度を強め、第3透明膜層(D)は固形化に優れ、耐こすれ性を強くするように組成を調整している。
The best mode for carrying out the deformed / three-dimensional curved surface seal using the transfer seal according to the present invention is a seal having the following 6 layers.
1: Print layer (5) in which the image formed on the sheet substrate (3) is reversely printed.
2: The 1st transparent film layer (A) formed on the printing layer of the said sheet | seat base material (3).
3: Opaque white or opaque color or transparent coating layer (B) formed on the first transparent film layer (A).
4: A pressure-sensitive adhesive layer (7) formed on the coating layer (B).
5: The 2nd transparent film layer (C) which coat | covers the surface of the said sheet | seat base material which the said reverse printed image can visually recognize as a normal image.
6: A third transparent film layer (D) formed on the second transparent film layer (C).
The first transparent film layer (A), the second transparent film layer (C), and the third transparent film layer (D) are quick-drying,
Although it is a transparent nail enamel containing a drying oil as a component, the composition ratio of the film-forming element, plasticizer and solvent is adjusted according to the performance and role of each layer.
Each of the transparent film layers is a transparent layer as a top coat for coating strength (rubbing resistance), glossiness, and image sharpening. The first transparent film layer (A) and the second transparent film layer (C) strengthens quick-drying, and the third transparent film layer (D) is excellent in solidification, and the composition is adjusted to enhance the rub resistance.
後述する実施例1を示す図1、図2のように、転写シールを利用した異形・3次元曲面対応シール(10)は、被着体(T)に貼着する面側から順に、粘着剤層(7)、不透明白色の塗着層(B)、第1透明膜層(A)、反転印刷された転写シール面の印刷層を前記第1透明膜層(A)に接したシート基材(3)、シート基材(3)の正画像が見える面に形成した第2透明膜層(C)、第3透明膜層(D)とからなる。
粘着剤層(7)は、剥離紙(9)でカバーされている。
As shown in FIGS. 1 and 2 showing Example 1 to be described later, the deformed / three-dimensional curved surface corresponding seal (10) using a transfer seal is in order from the surface side to be adhered to the adherend (T). A sheet substrate in which a layer (7), an opaque white coating layer (B), a first transparent film layer (A), and a printed layer of a reversely printed transfer seal surface are in contact with the first transparent film layer (A) (3) It consists of a second transparent film layer (C) and a third transparent film layer (D) formed on the surface of the sheet substrate (3) where the positive image can be seen.
The pressure-sensitive adhesive layer (7) is covered with a release paper (9).
背面に白色塗着層(B)がある第1透明膜層(A)でカバーされた印刷された正画像の見えるシート基材(3)の上に第2透明膜層(C)を設けて、背面に白色塗着層(B)がある第1透明層(A)と第2透明層(C)でシート基材(3)を挟着している。
白色の塗着層(B)は、第1透明膜層(A)の平面に均一に塗着されて、任意の図柄の背面となり、図柄の鮮明化、浮き出しに有効になる。正画像の視認にも有用である。
塗着層(B)は、不透明白色が基本であるが、赤色や金色、銀色、金属色等様々な不透明色彩色、そして透明の層に形成することも可能ではある。
転写シールである印刷シート(1)へのインクジェットプリンターでの印刷インクでは、白色はプリント表現ができないので、塗着層(B)の白色彩は、実は極めて繊細に印刷画像に影響する。
剥離紙(4)を剥がし正画像が視認できるシート基材(3)の面に第2透明膜層(C)を形成し、さらにその上に第3透明膜層(D)を形成する。
画像の鮮明化と、正画像の可視化、曲面対応の柔軟性と被着体(T)への付着性を増し、全体の堅牢性を達成している。
A second transparent film layer (C) is provided on a sheet base material (3) on which a printed normal image can be seen covered with a first transparent film layer (A) having a white coating layer (B) on the back surface. The sheet base material (3) is sandwiched between the first transparent layer (A) and the second transparent layer (C) having the white coating layer (B) on the back surface.
The white coating layer (B) is uniformly coated on the plane of the first transparent film layer (A), becomes the back of an arbitrary pattern, and is effective for sharpening and raising the pattern. It is also useful for visual recognition of normal images.
The coating layer (B) is basically opaque white, but can also be formed in various opaque colors such as red, gold, silver, and metal, and a transparent layer.
In the printing ink of the ink jet printer onto the printing sheet (1) which is a transfer seal, white cannot be printed, so the white color of the coating layer (B) actually affects the printed image very delicately.
The release paper (4) is peeled off, the second transparent film layer (C) is formed on the surface of the sheet substrate (3) where the normal image can be visually recognized, and the third transparent film layer (D) is further formed thereon.
The image is sharpened, the positive image is visualized, the flexibility corresponding to the curved surface, and the adhesion to the adherend (T) are increased, thereby achieving the overall robustness.
ここで図1〜図5 及び図8に示す実施例1について説明する。
実施例1は、被着体(T)が、湾曲した女性用のネイルチップ(つけ爪)である場合の、量産形態で作成される転写シールを利用した異形・3次元曲面対応シールである。
ネイルチップ(つけ爪)は、親指、人差し指、中指、薬指、小指と若干大きさや湾曲度の異なる模造形状を5個2セットの10個で構成される。
このネイルチップ(つけ爪)に、指ごとに異なる柄を連続的に印刷し転写する製作法が採用できる例である。
実施例1では、転写シール(1)を準備し、そのシート基材(3)に、インクジェット記録方式のプリンターで任意の画像が反転印刷された印刷層(5)を作成する。
印刷層(5)はシート基材(3)の離型吸水紙である剥離紙(4)のない一面に印刷された表層部を指す。
印刷されていない部分は保護層(6)となる。
印刷層(5)は、例えば各ネイルチップ(つけ爪)の大きさ合わせた形状で、各ネイルチップ(つけ爪)にいろんな花柄を反転して描いた図柄や写真で、パソコンによるソフトやコピー&ペーストで一度にセット単位で多数を描いたものである。
シート基材(3)に貼付されている離型吸水紙である剥離紙(4)を剥がした面からは、正画像が視認できる。
Here, the first embodiment shown in FIGS. 1 to 5 and FIG. 8 will be described.
Example 1 is a deformed / three-dimensional curved surface seal using a transfer seal created in a mass production form when the adherend (T) is a curved female nail tip (pawl nail).
The nail tip (false nail) is composed of 10 pieces of 5 sets and 2 sets of imitation shapes slightly different in size and curvature from the thumb, index finger, middle finger, ring finger, and little finger.
This is an example in which a manufacturing method of continuously printing and transferring different patterns for each finger on this nail chip (false nail) is adopted.
In Example 1, a transfer seal (1) is prepared, and a printed layer (5) in which an arbitrary image is reversely printed by an ink jet recording type printer is formed on the sheet base material (3).
The printed layer (5) refers to a surface layer portion printed on one surface of the sheet base material (3) without the release paper (4) which is a release water-absorbing paper.
The unprinted part becomes the protective layer (6).
The printed layer (5) is, for example, a shape and size of each nail chip (false nail), with various flower patterns on each nail chip (false nail), and a graphic or photo that is printed on a computer. A large number of sets are drawn at a time using paste.
A positive image can be visually recognized from the surface which peeled off the release paper (4) which is the release water-absorbing paper stuck on the sheet base material (3).
前記シート基材(3)の印刷層(5)の上層に、トップコートとして乾性油を成分に含有する市販の透明ネイルエナメルよる第1透明膜層(A)を形成する。
トップコートは、ニトロセルロースと樹脂からなる塗膜形成要素・脂肪族多塩基酸のエステルなどの可塑剤・溶剤が主要成分で、成分調整で、耐こすれ性や柔軟性、密着性を調整している。
トップコートには、常温で揮発する香り成分を溶剤とともに数%混合することで、近づくと香る程度の微芳香を付与できる。
下層面を保護することが、トップコートの主な役割になる。
A first transparent film layer (A) made of a commercially available transparent nail enamel containing a drying oil as a top coat as a component is formed on the printed layer (5) of the sheet substrate (3).
The top coat consists mainly of plasticizers and solvents such as nitrocellulose and resin film-forming elements, aliphatic polybasic acid esters, etc., and by adjusting the components, the rubbing resistance, flexibility and adhesion are adjusted. Yes.
The top coat can be given a slightly fragrant fragrance as it approaches by mixing several percent of a scent component that volatilizes at room temperature together with a solvent.
The main role of the top coat is to protect the lower surface.
そして前記第1透明膜層(A)の上層に、不透明で白色の水性アクリル絵の具の塗着層(B)を形成する。
塗着層(B)は、顔料をアクリル樹脂エマルションで練り上げたもので、第1透明膜層への塗布に良好な、乾燥前は親水性でありながら、乾燥後は耐水性の被膜を形成する白色不透明層である。
なお、塗着層(B)は、カラー画像の鮮明化のための背景色であるので、大半の場合は白色である。
さらに、実施例1では示していないが、塗着層(B)は、被着体(T)の地色の関係から白色以外に赤色や金色、銀色、金属色等様々な不透明色彩色、半透明淡色そして透明の層に形成することも可能である。
塗着層(B)の色合いは、印刷画像と被着体(T)の地色で適宜選択できる。
Then, an opaque white aqueous acrylic paint coating layer (B) is formed on the first transparent film layer (A).
The coating layer (B) is obtained by kneading a pigment with an acrylic resin emulsion, which is good for application to the first transparent film layer and forms a water-resistant film after drying while being hydrophilic before drying. It is a white opaque layer.
In addition, since the coating layer (B) is a background color for sharpening a color image, it is white in most cases.
Furthermore, although not shown in Example 1, the coating layer (B) has various opaque color colors such as red, gold, silver, and metal, other than white, semi-colored due to the ground color of the adherend (T). It is also possible to form a transparent light-colored and transparent layer.
The hue of the coating layer (B) can be appropriately selected depending on the printed image and the background color of the adherend (T).
前記塗着層(B)の色調は、不透明な水性アクリル絵の具で無毒性の蛍光物質を含ませたものでも可能である。
蛍光物質は、蛍光塗料、蓄光塗料などで、アクリル樹脂に混合して、画像背景に多様な変化を作出できる。
画像が蛍光するなどの対応シールもできる。
The color tone of the coating layer (B) may be an opaque water-based acrylic paint containing a non-toxic fluorescent material.
Fluorescent materials are fluorescent paints, phosphorescent paints, etc., and can be mixed with acrylic resin to create various changes in the image background.
Corresponding stickers such as fluorescent images are also available
第1透明膜層(A)は、前記印刷層(5)の上にトップコートとして乾性油を成分に含有する市販の透明ネイルエナメルを均等に塗着した構成である。
トップコートは、界面活性剤の効果を持つ溶剤成分を含むことで、水性アクリル絵具で描かれた部分に影響を与えることなく、保護膜を形成する。
本考案では、このトップコートとしての第1透明膜層(A)、第2透明膜層(C)、第3透明膜層(D)の柔軟性能が、シール(10)の、被着体(T)の形状・異形・曲面への対応性能を左右するので、塗膜形成要素・可塑剤・溶剤の割合調合で、各層(A)(C)(D)の性能を調整している。
同時に塗る厚みの調整も行われる。
A 1st transparent film layer (A) is the structure which apply | coated uniformly the commercially available transparent nail enamel which contains a drying oil as a component as a topcoat on the said printing layer (5).
The top coat includes a solvent component having the effect of a surfactant, and thus forms a protective film without affecting the portion drawn with the aqueous acrylic paint.
In the present invention, the flexible performance of the first transparent film layer (A), the second transparent film layer (C), and the third transparent film layer (D) as the top coat is determined by the adherend ( Since the performance to cope with the shape, irregular shape, and curved surface of T) is affected, the performance of each layer (A), (C), and (D) is adjusted by the blending ratio of the coating film forming element, the plasticizer, and the solvent.
At the same time, the thickness to be applied is adjusted.
この構成によれば第1透明膜層(A)は、均等平滑で凹凸なく形成される薄い膜層であり、シート基材(3)の印刷面の表面に傷や歪みが生じるのを防止すると共にその印刷面の画像を歪みなく視認させることができる。
更に第1透明膜層(A)は、塗着層(B)の白色面全体を、均等化した透過率で視認できる。
第1透明膜層(A)は無色透明で、塗着層(B)の白色を部位によって濃淡に見えないように均等に透視できる薄膜であるから、前記シート基材(3)の任意画像の色彩と図柄が、その画像のどの部位でもはっきり視認できる。
According to this configuration, the first transparent film layer (A) is a thin film layer that is uniformly smooth and formed without unevenness, and prevents the surface of the printing surface of the sheet substrate (3) from being scratched or distorted. At the same time, the image on the printed surface can be viewed without distortion.
Furthermore, the 1st transparent film layer (A) can visually recognize the white surface whole of the coating layer (B) with the equalized transmittance | permeability.
The first transparent film layer (A) is colorless and transparent, and is a thin film that can be seen through evenly so that the white color of the coating layer (B) does not appear shaded depending on the site. Colors and designs are clearly visible at any part of the image.
塗着層(B)の塗着方法は、塗装用のスプレー機材であるエアーブラシによって不透明で白色の水性アクリル絵の具を前記第1透明膜層(A)に吹き付け塗着する。
塗着層(B)は、薄く不透明白色に、第1透明膜層(A)に吹き付け均一に面塗装して形成する。塗着面にムラが無いように丁寧に白色面を形成する。
The coating layer (B) is coated by spraying an opaque white water-based acrylic paint onto the first transparent film layer (A) with an air brush which is a spray equipment for painting.
The coating layer (B) is formed by spraying the first transparent film layer (A) uniformly on the surface in a thin, opaque white. Carefully form a white surface so that there is no unevenness on the coated surface.
前記不透明で白色の水性アクリル絵の具の塗着層(B)の上層には、両面粘着シートによる粘着剤層(7)を形成する。
粘着剤層(7)は、前記塗着層(B)への貼着に良好な粘着力を有し、水分によって粘着力が低下しない柔軟な粘着材質から成り、シート基材(3)に形成した図案等の印刷層(5)に、第1透明膜層(A)及び塗着層(B)を順次積層したことで、当該図案層が水分に触れて滲んでしまうといったトラブルを防止している。
その結果、目的の被着体(T)への貼着前に、適宜水分を与え、当該シート基材(3)から離型吸水紙(4)を剥離することが可能となっている。
An adhesive layer (7) made of a double-sided adhesive sheet is formed on the upper layer of the opaque white aqueous acrylic paint coating layer (B).
The pressure-sensitive adhesive layer (7) is made of a flexible pressure-sensitive adhesive material that has a good adhesive force for adhering to the coating layer (B) and does not decrease in adhesive strength due to moisture, and is formed on the sheet substrate (3). By sequentially laminating the first transparent film layer (A) and the coating layer (B) on the printed layer (5) of the designed pattern, etc., it is possible to prevent troubles such that the design layer touches moisture. Yes.
As a result, before adhering to the target adherend (T), moisture can be appropriately applied to release the release water-absorbing paper (4) from the sheet base material (3).
被着体(T)に接合するために、塗着層(B)の上層に粘着剤層(7)を設けているが、その材質としては水気がある場所での使用や用途であるので、耐水性の接着剤を用いるのが好ましい。
耐水性があればボンドや工作用のりなど特には限定されない。
粘着剤層(7)には、剥離紙(9)が付設されている。
因みに請求項に、粘着剤層(7)の剥離紙(9)を記載していないのは、その記載の有無で技術的範囲を広狭相違させない趣旨である。
In order to join the adherend (T), the adhesive layer (7) is provided on the upper layer of the coating layer (B), but the material is used or used in a place with moisture, It is preferable to use a water-resistant adhesive.
As long as it has water resistance, there is no particular limitation such as bonding or work glue.
A release paper (9) is attached to the adhesive layer (7).
Incidentally, the reason why the release paper (9) of the pressure-sensitive adhesive layer (7) is not described in the claims is that the technical scope does not differ widely depending on the presence or absence of the description.
反転印刷した任意画像が正画像として目視できる当該前記シート基材(3)の印刷層(5)の裏面に、前記第1透明膜層(A)と同様組成の、トップコートとして乾性油を成分に含有する市販の透明ネイルエナメルの第2透明膜層(C)を形成する。
シート基材(3)は、第1透明膜層(A)と第2透明膜層(C)で挟着された構成になる。
On the back surface of the printed layer (5) of the sheet base material (3) where a reverse printed arbitrary image can be viewed as a normal image, a dry oil as a top coat having the same composition as the first transparent film layer (A) is used as a component. To form a second transparent film layer (C) of a commercially available transparent nail enamel.
The sheet substrate (3) is configured to be sandwiched between the first transparent film layer (A) and the second transparent film layer (C).
さらに、前記第2透明膜層(C)の上層に、前記第1透明膜層(A)、第2透明膜層(C)と同様組成の、トップコートとして乾性油を成分に含有する市販の透明ネイルエナメル等を用いた第3透明膜層(D)が形成される。
第2透明膜層(C)の乾燥後に、第3透明膜層(D)が塗布積層される。
これらが、6つの層が一体となったかたちで構成されている。
Furthermore, a commercially available product containing a drying oil as a top coat of the same composition as the first transparent film layer (A) and the second transparent film layer (C) on the second transparent film layer (C). A third transparent film layer (D) using transparent nail enamel or the like is formed.
After the second transparent film layer (C) is dried, the third transparent film layer (D) is applied and laminated.
These are made up of six layers in one piece.
次に本考案に係る転写シールを利用した異形・3次元曲面対応シールの製作過程の一例を示す図3(工程写真)を用いて、その工程を説明する。
この製作過程は、例えばネイルチップ(つけ爪)の側面に貼る一枚の写真を用いた一点物シールの製作例である。
Next, the process will be described with reference to FIG. 3 (process photograph) showing an example of a manufacturing process of a deformed / three-dimensional curved surface compatible seal using the transfer seal according to the present invention.
This manufacturing process is, for example, a manufacturing example of a one-point object seal using a single photograph attached to the side surface of a nail tip (false nail).
工程1:まず被着体(T)にシール貼着したい画像をパソコンのピクチャーファイルから選択する。
シールにしたい画像を選んだら、パソコンに取り込み、画像加工ができるソフトで、必要な調整を画像に施す。
工程2:転写シートである印刷シート(1)にインクジェットプリンター(染料インクタイプ)で、反転印刷する。
工程3:当該印刷された選択図を任意の大きさにカットする。
「印刷した画像」+「周囲余白1cm」を目安に、印刷シート(1)をカットする。
工程3−1:カットした後、トップコートとして第1透明膜層(A)を形成する。
余白部分を含め全体にトップコート(調整された透明ネイルエナメル)を塗布、吹付などで塗る。
工程4:前記第1透明膜層(A)の面の上にエアーブラシにより白色絵の具を吹付けて塗着層(B)を形成する。
第1透明膜層(A)であるトップコートが乾いたら、エアーブラシを使い、カットしたシート全体に、水性アクリル絵の具の白色を吹き付ける。均一な白色面を形成する。
工程5:前記塗着層(B)に粘着フィルムを貼付けて粘着剤層(7)を形成する。
吹き付けた絵の具が乾いたら、その白色面の塗着層(B)上に、粘着フィルムとして市販の糊フィルムを貼る。
糊フィルムは、あらかじめ作業中の印刷シート(1)より、やや大きめにカットして準備しておく。
貼り付け後は、そのフィルム上を柔らかい布でこすり、印刷シート(1)とよく密着させる。
工程6:シート基材(3)の剥離紙(4)を次の手順で外す。
糊フィルムを貼り付けた印刷シート(1)を水に浸け、印刷シート(1)の剥離紙(4)部分を外す。
印刷画像は第1透明膜層(A)で被覆されているが、万が一水分に影響を受ける場合があるので、数秒浸けたら取り出し、ペーパーで余分な水分を取り除いたら、また水に浸けるという作業を3〜4回繰り返す。
印刷シート(1)の表面部に残った水分はライト照明の熱などを利用して、素早く乾燥させる。
工程7:剥離紙(4)を外した後は、その表面にトップコート塗布して前記第2透明膜層(C)を形成する。
剥離紙(4)に接していた印刷シート(1)表面部に、トップコートを塗る作業である。
工程7−1:第2透明膜層(C)が乾燥した時点で第3透明膜層(D)を形成する。
また第3透明膜層(D)は、被着体(T)の性質によっては、工程7迄の積層構造を備えた粘着体を目的の被着体(T)に貼着後に第2透明膜層(C)上に第3透明膜層(D)を積層することもできる。
第3透明膜層(D)は、保護膜としての性能が求められる。
この段階で、6層からなる転写シールを利用した異形・3次元曲面対応シールが形成される。
工程8:工程7−1で6層に形成したシールは、糊フィルム側の剥離紙をはがして、被着体(T)に貼り付けて使用される。
Step 1: First, an image to be attached to the adherend (T) is selected from a picture file of a personal computer.
Once you have selected the image you want to use as a sticker, you can import it into a computer and apply the necessary adjustments to the image.
Step 2: Reverse printing is performed on the printing sheet (1), which is a transfer sheet, using an ink jet printer (dye ink type).
Step 3: The printed selection diagram is cut into an arbitrary size.
Cut the printed sheet (1) using “printed image” + “surrounding margin 1 cm” as a guide.
Step 3-1: After cutting, the first transparent film layer (A) is formed as a top coat.
Apply the top coat (adjusted transparent nail enamel), including the blank area, by spraying.
Step 4: A white paint is sprayed on the surface of the first transparent film layer (A) with an air brush to form a coating layer (B).
When the top coat, which is the first transparent film layer (A), is dried, an air brush is used to spray the white color of the water-based acrylic paint on the entire cut sheet. Form a uniform white surface.
Process 5: An adhesive film is affixed on the said coating layer (B), and an adhesive layer (7) is formed.
When the sprayed paint dries, a commercially available glue film is pasted as an adhesive film on the white coating layer (B).
The glue film is prepared in advance by cutting it slightly larger than the working printing sheet (1).
After pasting, the film is rubbed with a soft cloth and brought into close contact with the printed sheet (1).
Step 6: The release paper (4) of the sheet substrate (3) is removed by the following procedure.
The printing sheet (1) with the glue film attached is dipped in water, and the release paper (4) portion of the printing sheet (1) is removed.
The printed image is covered with the first transparent film layer (A), but it may be affected by moisture, so take it out for a few seconds, remove it after removing excess moisture with paper, and soak it in water again. Repeat 3-4 times.
Moisture remaining on the surface of the printed sheet (1) is quickly dried using the heat of light illumination.
Step 7: After removing the release paper (4), a top coat is applied to the surface to form the second transparent film layer (C).
The top coat is applied to the surface of the printed sheet (1) that has been in contact with the release paper (4).
Step 7-1: When the second transparent film layer (C) is dried, the third transparent film layer (D) is formed.
Further, depending on the properties of the adherend (T), the third transparent film layer (D) may be a second transparent film after the pressure-sensitive adhesive body having the laminated structure up to step 7 is adhered to the target adherend (T). A 3rd transparent film layer (D) can also be laminated | stacked on a layer (C).
The third transparent film layer (D) is required to have a performance as a protective film.
At this stage, a deformed / three-dimensional curved surface seal using a transfer seal composed of six layers is formed.
Step 8: The seal formed in 6 layers in Step 7-1 is used by peeling off the release paper on the glue film side and attaching it to the adherend (T).
シールが薄すぎて扱いにくいという課題は、第1透明膜層(A)、第2透明膜層(C)、第3透明膜層(D)の形成時に、その調整されたトップコートを塗り重ねることでシールの厚みが微妙に増し、取り扱いが楽になる。
なお、第3透明膜層(D)を形成するときに、図示していないが別途用意した小ビーズや花柄片等の立体的装飾片を包み込んで立体的に付設したものも提供できる。
さらに、前記第1透明膜層(A)、第2透明膜層(C)、第3透明膜層(D)の一つ以上に、常温で空気中に揮発する香り成分を練り込み或いは混合して、微かに芳香する異形・3次元曲面対応シールも提案できる。
このような工程で、一点物でも6層を形成して、柔軟で画像の鮮明な転写シールを利用した異形・3次元曲面対応シールが作成できる。
The problem that the seal is too thin and difficult to handle is that the adjusted top coat is applied repeatedly when the first transparent film layer (A), the second transparent film layer (C), and the third transparent film layer (D) are formed. This slightly increases the thickness of the seal and makes it easier to handle.
In addition, when forming a 3rd transparent film layer (D), although not shown in figure, what wrapped and attached three-dimensional decoration pieces, such as a small bead and a floral pattern piece provided separately, can also be provided.
Furthermore, a fragrance component that volatilizes in air at room temperature is kneaded or mixed into one or more of the first transparent film layer (A), the second transparent film layer (C), and the third transparent film layer (D). Also, we can propose a slightly fragrant seal for deformed and 3D curved surfaces.
With such a process, even a single object can be formed into 6 layers, and a deformed / three-dimensional curved surface compatible seal using a transfer seal with a clear image can be created.
従来の薄膜であるシールは、図6、図7で示すように、目的の被着体(T)が異形・3次元曲面等である場合には、柔軟性が不十分でその形状に馴染み難く、十分馴染みえないまま貼付した状態で印刷用シート(1)に積層された離型吸水紙(4)を剥離すると歪みが生じていた。
前述のように任意画像の印刷をした薄膜のシート基材(3)に、図8上段の従来シールの貼付写真のように曲面のしわ、弛み、または浮き上がりや破損等が生じてしまい、所望の仕上がり得られないという問題があった。
As shown in FIGS. 6 and 7, when the target adherend (T) is an irregular shape, a three-dimensional curved surface, etc., the conventional thin film seal is insufficient in flexibility and is not easily adapted to the shape. When the release water-absorbing paper (4) laminated on the printing sheet (1) was peeled off without being sufficiently familiar, distortion occurred.
As described above, the thin film sheet substrate (3) on which an arbitrary image has been printed may be wrinkled, loosened, lifted or damaged as shown in the photograph of the conventional sticker in the upper part of FIG. There was a problem that it could not be finished.
そこで本考案では、シート基材(3)の上層には第2透明膜層(C)と第3透明膜層(D)を重ねて塗着した構成とした。
第3透明膜層(D)を、前記第2透明膜層(C)上にさらに積層することにより、画像の全周囲の囲繞により一層の堅牢性の向上と、全体に均等な柔軟性があり、整えられた表面が光の反射を強め、装飾体としての艶を向上させ、美麗的効果が向上している。
図5に示す本考案に係る試作品シール写真のように、本考案に係るシールの画像は従来にない鮮明さがあり、つけ爪の小さな面でも髪の毛や羽毛までもが視認できる。
凸状曲面でも凹状曲面でも画像の輪郭や色調が背景色とは区別されてしっかり視認できる。
しかも、本考案のシールは、図8の下段の写真のように、曲面に対応して湾曲し、曲面に馴染み、しわや割れができずに綺麗に貼着できる。
Therefore, in the present invention, the second transparent film layer (C) and the third transparent film layer (D) are overlaid on the upper layer of the sheet base material (3).
By further laminating the third transparent film layer (D) on the second transparent film layer (C), there is a further improvement in robustness by the surrounding of the entire periphery of the image, and there is equal flexibility throughout. The prepared surface enhances the reflection of light, improves the gloss as a decorative body, and improves the aesthetic effect.
Like the prototype seal photograph according to the present invention shown in FIG. 5, the image of the seal according to the present invention has a clearness that has not existed in the past, and even hair and feathers can be visually recognized even on a small surface of a false nail.
The contour and color tone of the image are distinguished from the background color and can be clearly seen on both the convex and concave curved surfaces.
In addition, the seal of the present invention is curved corresponding to the curved surface as shown in the lower photograph of FIG.
本考案に利用できる両面粘着シートについて説明する。
市販製品には、貼着手段である両面粘着シートの色が、無色透明タイプと白色タイプの2種類の製品があり、前記の本考案の作成手順に沿って第1透明膜層(A)と塗着層(B)を備えた図案層に積層する粘着剤層(7)としての両面粘着シートは、任意色のアクリル絵の具により形成した当該塗着層(B)の発色をより確実にする背景色としての目的で、白色タイプを備える製品を選択することにより、その効果が期待できる。
The double-sided pressure-sensitive adhesive sheet that can be used in the present invention will be described.
There are two types of commercially available products, the color of the double-sided pressure-sensitive adhesive sheet, which is a sticking means, a colorless and transparent type and a white type, and the first transparent film layer (A) and The double-sided pressure-sensitive adhesive sheet as the pressure-sensitive adhesive layer (7) laminated on the design layer provided with the coating layer (B) is a background that more reliably develops the color of the coating layer (B) formed with an acrylic paint of any color The effect can be expected by selecting a product with a white type for the purpose of color.
また、前記の、本考案に使用できる市販製品が任意画像の印刷機器として指定するインクジェット記録方式のプリンターが備える専用インクの、透過性を有し、白色の印刷が不可能である性質が原因による、任意画像本来の色彩が再現できない問題については、塗着層(B)の色味色彩を工夫して対応する。
本考案における貼布目的の被着体(T)の地色が、白色、もしくは白色に近い色を有する場合には、前記の本考案の作製手順における、係る印刷用シートの第1透明膜層(A)を積層した印刷面全体に、塗装用のスプレー機材であるエアーブラシを用いて不透明で白色の水性アクリル絵の具を吹き付けて不透明白色の塗着層(B)を形成する段階(工程4)を、例えば透明アクリルを用いて塗着して透明な塗着層(B)を形成し、更に、粘着層(7)として無色透明タイプの両面粘着シート選択することにより、被着体(T)の地色を活用出来る場合がある。
In addition, due to the property of the exclusive ink included in the printer of the inkjet recording method that the commercial product that can be used in the present invention is designated as a printing device for arbitrary images, it has transparency and cannot be printed in white. The problem that the original color of the arbitrary image cannot be reproduced is dealt with by devising the tint color of the coating layer (B).
When the ground color of the adherend (T) for the purpose of application in the present invention is white or a color close to white, the first transparent film layer of the printing sheet in the production procedure of the present invention described above A step of forming an opaque white coating layer (B) by spraying an opaque white water-based acrylic paint on the entire printed surface on which (A) is laminated using an air brush which is a spray equipment for painting (step 4) Is coated using, for example, transparent acrylic to form a transparent coating layer (B), and further, a colorless and transparent type double-sided pressure-sensitive adhesive sheet is selected as the pressure-sensitive adhesive layer (7). You may be able to take advantage of the ground color.
透明な塗着層(B)と透明タイプの両面粘着シートを組み合わせることで、係る市販製品が備える印刷用シートの印刷面に当たる無色透明なシート基材に印刷した任意画像以外の部分は無色透明になるので、目的の被着体(T)への貼着作業前に、当該基材シートに印刷した任意画像の周囲余白等の装飾に必要のない所望部分を簡便にカットすることができ、かつ被着体(T)の地色が視認でき、無駄な貼着面を取り除くことで、目的の被着体(T)への貼着作業がより簡便になる効果も期待できる。 By combining the transparent coating layer (B) and the transparent type double-sided pressure-sensitive adhesive sheet, the portions other than the arbitrary image printed on the colorless and transparent sheet base material corresponding to the printing surface of the printing sheet included in the commercial product are colorless and transparent. Therefore, before attaching to the target adherend (T), it is possible to easily cut a desired portion that is not necessary for decoration such as a margin of an image printed on the base sheet, and The ground color of the adherend (T) can be visually recognized, and by removing a useless sticking surface, an effect of making the sticking work to the target adherend (T) easier can be expected.
但し、工程4の段階で、不透明白色絵の具に替えて透明アクリルにするのは、画像の色彩と被着体(T)の地色が一色たりとも重ならない場合や、画像が多色カラーで被着体(T)が、均質な白色、もしくは白色に近い色を有する場合に限り可能な代替手段である。
しかも、一概に色彩が重複しない場合や白色の場合と言っても、色彩には多数の種類や段階があり、相互に干渉し合うので画像の鮮明化にはかなり難しい選択になる。
塗着層(B)に白色以外の色や透明を選択するときは、特に被着体(T)の地色を生かしたい場合に限定される。
However, transparent acrylic instead of opaque white paint in the step 4 is used when the color of the image does not overlap with the ground color of the adherend (T) or the image is covered with multi-colored color. This is a possible alternative only if the kimono (T) has a homogeneous white or near white color.
Moreover, even if the colors generally do not overlap or in the case of white, there are many types and stages of colors, and they interfere with each other, making it a very difficult choice for sharpening the image.
When a color other than white or transparent is selected for the coating layer (B), it is limited particularly when the ground color of the adherend (T) is to be utilized.
前記の本考案の作製手順における、係る塗着層(B)を形成する段階(工程4)において、白色塗材を透明塗材等にするという代替は、その組成を異質なものにしない限り、本考案の特性である柔軟性、施工性、堅牢性を著しく損なう弊害を伴うことはない。 In the step of forming the coating layer (B) in the preparation procedure of the present invention (step 4), the substitution of the white coating material as a transparent coating material, etc., unless the composition is different, There are no negative effects that significantly impair the flexibility, workability, and robustness that are the characteristics of the present invention.
前記の通り、本考案では、市販製品が備える両面粘着シートの色は、その都度、適宜選択ができることから、特に限定はされない。 As above-mentioned, in this invention, since the color of the double-sided adhesive sheet with which a commercial product is equipped can be suitably selected each time, it is not specifically limited.
また、従来技術による既に万人向けの画像が印刷済みの状態で市販されているネイルや模型等を用途とする装飾用シールにおいても、前記の本考案の作製手順を応用することにより、本考案の所望の位置に粘着が簡便な異形・3次元曲面対応シールを作成することができる。 In addition, the present invention can be applied to decorative stickers for nails and models that have already been printed with images for everyone according to the prior art by applying the production procedure of the present invention. It is possible to create a deformed / three-dimensional curved surface-compatible seal with easy adhesion at a desired position.
本考案の任意画像の印刷が可能な転写シールを利用した所望の位置に粘着が簡便な異形・3次元曲面対応シールは、曲面や粗面でもしっかりと貼着できるので、人体の爪、爪に貼るネイルチップ(つけ爪)、小型携帯機器のボタン、機器に設けられたブランド用立体小突起、といった比較的小型で厳密に貼布位置が定められた被着体(T)に適用できる。
しかもパソコンソフトによって任意の画像を選択できるので、細密な芸術作品で一点創作品や、従前できなかった極微細な画像、写真の再現シールが可能である。
更に、印刷シートへの、各層の塗布加工は、積層技術の応用であるので、量産することもでき、大きさの制限を受けることもなく、シールを利用する分野を広げることができる。
The deformed / three-dimensional curved surface compatible sticker that can easily stick to the desired position using the transfer sticker that can print any image of the present invention can be firmly attached even on curved or rough surfaces. The present invention can be applied to an adherend (T) that is relatively small and has a precisely determined application position, such as a nail chip (pawl) to be attached, a button of a small portable device, and a three-dimensional small projection for a brand provided on the device.
In addition, since any image can be selected by the personal computer software, it is possible to create a single-point creation with a fine art work, an ultra-fine image that could not be done before, and a photo reproduction sticker.
Furthermore, since the coating process of each layer on the printing sheet is an application of the lamination technique, it can be mass-produced, and the field of using the seal can be expanded without being limited in size.
(1) 印刷用シート(転写シール)
(2) 粘着シート
(3) シート基材
(4) 剥離紙(離型吸水紙)
(5) 印刷層
(6) 保護層
(7) 粘着剤層
(10) 異形・3次元曲面対応シール
(9) 剥離紙
(A) 第1透明膜層
(B) 塗着層
(C) 第2透明膜層
(D) 第3透明膜層
(T) 被着体
(1) Printing sheet (transfer sticker)
(2) Adhesive sheet (3) Sheet base material (4) Release paper (release release paper)
(5) Print layer (6) Protective layer (7) Adhesive layer (10) Seal for deformed / three-dimensional curved surface (9) Release paper (A) First transparent film layer (B) Adhesive layer (C) Second Transparent film layer (D) Third transparent film layer (T) Substrate
Claims (3)
1:シート基材に形成された画像が反転印刷された印刷層。
2:前記シート基材の印刷層の上に形成した第1透明膜層。
3:前記第1透明膜層の上に形成した不透明白色又は不透明色彩色又は透明の塗着層。
4:前記塗着層の上に形成した粘着剤層。
5:前記反転印刷した画像が正画像として目視できる当該前記シート基材の面を被覆する第2透明膜層。
6:第2透明膜層の上に形成した第3透明膜層。 A deformed / three-dimensional curved surface seal using a transfer seal characterized by comprising the following six layers of 1-6.
1: Print layer in which an image formed on a sheet base material is reversely printed.
2: The 1st transparent film layer formed on the printing layer of the said sheet | seat base material.
3: Opaque white or opaque colored or transparent coating layer formed on the first transparent film layer.
4: A pressure-sensitive adhesive layer formed on the coating layer.
5: The 2nd transparent film layer which coat | covers the surface of the said sheet | seat base material which can visually recognize the said reverse printed image as a normal image.
6: A third transparent film layer formed on the second transparent film layer.