JP2523313B2 - Resin rotary welding member - Google Patents
Resin rotary welding memberInfo
- Publication number
- JP2523313B2 JP2523313B2 JP8747187A JP8747187A JP2523313B2 JP 2523313 B2 JP2523313 B2 JP 2523313B2 JP 8747187 A JP8747187 A JP 8747187A JP 8747187 A JP8747187 A JP 8747187A JP 2523313 B2 JP2523313 B2 JP 2523313B2
- Authority
- JP
- Japan
- Prior art keywords
- flange portion
- rotary welding
- welding member
- columnar
- mounting plane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 〈本発明の産業上の利用分野〉 本発明は、例えばスタッドや留め具などのように、フ
ランジ部の片面に柱状部を有し、取付平面にフランジ部
の裏面を押し付けた状態で高速回転させて、取付平面と
フランジ部裏面間の摩擦熱によって溶融させて取付平面
に固定する樹脂製回転溶着部材に関する。DETAILED DESCRIPTION OF THE INVENTION <Field of Industrial Application of the Present Invention> The present invention has a columnar portion on one side of a flange portion, such as a stud or a fastener, and a back surface of the flange portion on a mounting plane. The present invention relates to a resin rotary welding member that is rotated at a high speed in a pressed state, melted by frictional heat between a mounting plane and a rear surface of a flange portion, and fixed to the mounting plane.
〈従来技術〉 従来より、第10図に示すスタッドあるいは第11図に示
す留め具などの回転溶着部材１は、円板状のフランジ部
２と、フランジ部２から側方へ突出した係合片３、３
と、フランジ部２の中央から突出した柱状部４とが合成
樹脂で一体成形されたものであった。そして、第12図に
示すように、合成樹脂などの基板５の取付平面Ａに回転
溶着部材１をのせ、回転溶着機６の先端の当接部材７を
回転溶着部材１のフランジ部２に当接して取付平面Ａへ
押し付けた状態で、回転溶着機６の先端の係合部材８の
係合溝8a、8aに回転溶着部材１の係合片３、３を入れて
係合部材８を高速回転させると、係合溝8a、8aに係合片
３、３が係合して、係合部材８と共に回転溶着部材１も
高速回転する。このため、取付平面Ａとフランジ部２の
背面間の回転摩擦熱で接触面が溶融し互いに溶着した状
態になる。回転を停止すると、溶着した樹脂が冷えて固
化し、この結果、取付平面Ａに回転溶着部材１のフラン
ジ部２が分離不能に固定される。<Prior Art> Conventionally, a rotary welding member 1 such as a stud shown in FIG. 10 or a fastener shown in FIG. 11 has a disc-shaped flange portion 2 and an engagement piece protruding laterally from the flange portion 2. Three and three
And the columnar portion 4 protruding from the center of the flange portion 2 were integrally molded of synthetic resin. Then, as shown in FIG. 12, the rotary welding member 1 is placed on the mounting plane A of the substrate 5 of synthetic resin or the like, and the abutting member 7 at the tip of the rotary welding machine 6 is contacted with the flange portion 2 of the rotary welding member 1. With the contacting member pressed against the mounting plane A, the engaging pieces 3, 3 of the rotary welding member 1 are inserted into the engaging grooves 8a, 8a of the engaging member 8 at the tip of the rotary welding machine 6 to move the engaging member 8 at high speed. When rotated, the engagement pieces 3 and 3 engage with the engagement grooves 8a, 8a, and the rotary welding member 1 rotates at high speed together with the engagement member 8. Therefore, the contact surfaces are melted and welded to each other by the rotational frictional heat between the mounting plane A and the back surface of the flange portion 2. When the rotation is stopped, the welded resin cools and solidifies, and as a result, the flange portion 2 of the rotary welding member 1 is inseparably fixed to the mounting plane A.
このようにして、基板５に固定した回転溶着部材１に
は、例えばスタッドの場合には、第13図のように、柱状
部４の穴にネジ９をネジ込んで板10などを取付けるのに
用い、例えば留め具の場合には、第14図のように、柱状
部４の係止部11、11を板10の穴12の縁部によって内方へ
撓ませつつ押込み、穴12を通過させて係止部11、11の弾
性復帰によって係止部11、11の段部11′、11′で穴12の
縁部を係止させて板10を取付けるのに用いる。In this way, for example, in the case of a stud, the rotary welding member 1 fixed to the substrate 5 is used to mount the plate 10 by screwing the screw 9 into the hole of the columnar portion 4 as shown in FIG. For example, in the case of a fastener, as shown in FIG. 14, the locking portions 11, 11 of the columnar portion 4 are pushed inward while being bent inward by the edge portion of the hole 12 of the plate 10 and passed through the hole 12. It is used to mount the plate 10 by locking the edges of the holes 12 by the step portions 11 ', 11' of the locking portions 11, 11 by elastic return of the locking portions 11, 11.
〈本考案が解決しようとする問題点〉 しかして、このような回転溶着部材１では、フランジ
部２に関しては、溶融しやすいことが要求されるのに対
し、逆に、柱状部４に関しては、第13図及び第14図の如
きネジ９、板10などの取付けにおける強度のために、硬
度が大きいことが要求される。<Problems to be Solved by the Present Invention> In such a rotary welding member 1, the flange portion 2 is required to be easily melted, while conversely, the columnar portion 4 is A high hardness is required for the strength in mounting the screw 9, the plate 10 and the like as shown in FIGS. 13 and 14.
しかるには、従来の回転溶着部材１は前記したように
同一材質の合成樹脂で全体が一体成形されたものである
ため、溶着しやすいように溶融度の大きい材質で回転溶
着部材１を形成すると、柱状部４における取付け強度が
弱くなって、ネジ９が抜けはずれたり、板10がはずれた
りする問題があり、逆に取付け強度を強くするために硬
度の大きい材質で回転溶着部材１を作成すると、回転溶
着しようとしても、フランジ部２が容易に溶融せず、溶
着が困難となり、長時間押圧回転する間に、基板５が湾
曲、膨出などの現象を生じたりする問題があった。However, since the conventional rotary welding member 1 is integrally formed of synthetic resin of the same material as described above, if the rotary welding member 1 is formed of a material having a high degree of melting so as to facilitate welding, There is a problem that the mounting strength in the columnar portion 4 becomes weak and the screw 9 comes off and the plate 10 comes off. On the contrary, if the rotary welding member 1 is made of a material having a high hardness to increase the mounting strength, Even if an attempt is made by rotary welding, the flange portion 2 does not melt easily, welding becomes difficult, and there arises a problem that the substrate 5 causes a phenomenon such as bending or swelling during pressing and rotation for a long time.
本発明はこれらの問題点を解決した回転溶着部材を提
供することを目的としている。An object of the present invention is to provide a rotary welding member that solves these problems.
〈手段〉 前記目的を達成するために、本発明では 円板状のフランジ部の表面側中央に柱状部を有し、取
付平面にフランジ部の裏面を押付けて回転させてフラン
ジ部の裏面が取付平面への押圧回転による摩擦熱によっ
て溶着される樹脂製回転溶着部材において、 前記フランジ部と前記柱状部とを、フランジ部の溶融
度が大きく、柱状部の硬度が大きいそれぞれ異なる材質
の樹脂で、インサート成形あるいは嵌込みによって一体
的に結合し、 取付平面に対して前記フランジ部の裏面を取付けて前
記フランジ部と柱状部とを一体的に回転させて、前記フ
ランジ部の裏面を取付平面に溶着するようにしたことを
特徴としている。<Means> In order to achieve the above object, in the present invention, a disc-shaped flange portion has a columnar portion at the center of the front surface side, and the rear surface of the flange portion is mounted by pressing the rear surface of the flange portion against the mounting plane and rotating the same. In a resin rotary welding member that is welded by frictional heat due to pressure rotation to a flat surface, the flange portion and the columnar portion, the melting degree of the flange portion is large, the resin of different hardness of the columnar portion is large, It is integrally joined by insert molding or fitting, the back surface of the flange portion is attached to the mounting plane, the flange portion and the columnar portion are integrally rotated, and the back surface of the flange portion is welded to the mounting plane. It is characterized by doing so.
〈作用〉 このようにしたため、取付面に樹脂製回転溶着部材の
フランジ部の裏面を押圧して高速回転させると、異なる
二つの材質で一体的に結合された回転溶着部材のフラン
ジ部が溶融度の大きい材質で形成されているので容易に
溶融して溶着し、柱状部は硬度の大きい材質で形成され
ているので、柱状部へのネジや板などの取付けが強固に
なる。<Action> Therefore, when the back surface of the flange portion of the resin rotary welding member is pressed against the mounting surface to rotate at high speed, the flange portion of the rotary welding member integrally formed of two different materials is melted. Since it is made of a material having a large hardness, it is easily melted and welded, and since the columnar portion is made of a material having a high hardness, the screws, plates, etc. are firmly attached to the columnar portion.
〈本発明の実施例〉 以下、図面に基づいて本発明の実施例を説明する。<Examples of the Present Invention> Examples of the present invention will be described below with reference to the drawings.
第１図は本発明の一実施例を示している。 FIG. 1 shows an embodiment of the present invention.
まず、第１図に示すように、フランジ部21の周縁面の
上部から突設された係止片22、22と、結合手段であるフ
ランジ部21の中央上面に突設された突起部23と該突起部
23の上端に突設された鍔部24とを、溶融度の大きい材質
の合成樹脂（例えばPBT）で一体成形する。First, as shown in FIG. 1, locking pieces 22, 22 projecting from the upper part of the peripheral surface of the flange portion 21, and a projecting portion 23 projecting on the central upper surface of the flange portion 21 which is the coupling means. The protrusion
A flange 24 protruding from the upper end of 23 is integrally molded with a synthetic resin (for example, PBT) having a high melting degree.
次に、フランジ部21の中央上面において、結合手段で
ある前記突起部23及び鍔部24とを覆うように、硬度の大
きい材質の合成樹脂（例えばPOM）によって、インサー
ト成形して第２図に示すように、穴25aを備えた柱状部2
5を、あるいは、第３図に示すように、係止部25b、25b
を備えた柱状部25を一体的に成形する。Next, the upper surface of the center of the flange portion 21 is insert-molded with a synthetic resin (for example, POM) having a high hardness so as to cover the projecting portion 23 and the flange portion 24 which are the coupling means, and as shown in FIG. As shown, column 2 with holes 25a
5, or as shown in FIG. 3, locking portions 25b, 25b
The columnar portion 25 provided with is integrally molded.
このように異なる二つの材質の合成樹脂の２色成形に
よって回転溶着部材20を形成する。In this way, the rotary welding member 20 is formed by two-color molding of two different synthetic resins.
この回転溶着部材20を取付平面Ａに回転溶着するに
は、第12図で示したのと同様に合成樹脂などの基板５の
取付平面Ａに、本発明の回転溶着部材20をのせ、回転溶
着機６の先端の当接部材７を異なる材質のフランジ部21
と柱状部25が一体的に結合された本発明の回転溶着部材
20のフランジ部21に当接して、取付平面Ａへ押し付け、
回転溶着機６の先端の係合部材８の係合溝8a、8aにフラ
ンジ部21の係合片22、22を入れて係合部材８を高速回転
させることによって、フランジ部21と柱状部25とを一体
的に高速回転させて、取付平面Ａにフランジ部21の背面
を溶着させる。In order to rotationally weld the rotary welding member 20 to the mounting plane A, the rotary welding member 20 of the present invention is placed on the mounting plane A of the substrate 5 made of synthetic resin or the like as shown in FIG. The abutting member 7 at the tip of the machine 6 has a flange portion 21 made of a different material.
The rotary welding member of the present invention in which the columnar portion 25 and the columnar portion 25 are integrally connected.
Abut the flange portion 21 of 20 and press it against the mounting plane A,
By inserting the engagement pieces 22, 22 of the flange portion 21 into the engagement grooves 8a, 8a of the engagement member 8 at the tip of the rotary welding machine 6 and rotating the engagement member 8 at a high speed, the flange portion 21 and the columnar portion 25 And are integrally rotated at high speed to weld the back surface of the flange portion 21 to the mounting plane A.
しかして、本発明ではフランジ部21と柱状部25とを異
なる材質の樹脂を予め一体的に結合したものであり、フ
ランジ部21は溶融度の大きい材質の合成樹脂で成形され
ているため、摩擦熱で容易に溶融して、溶着され、柱状
部25は硬度の大きい材質の合成樹脂で成形されているた
め、第13図の如くネジ止めした場合でも、あるいは第14
図の如く板を取付けた場合でも、強固になされる。Therefore, in the present invention, the flange portion 21 and the columnar portion 25 are integrally combined with different resins in advance, and since the flange portion 21 is formed of a synthetic resin having a high degree of melting, friction is increased. It is easily melted by heat and welded, and the columnar portion 25 is formed of a synthetic resin having a high hardness. Therefore, even if it is screwed as shown in FIG.
Even if a plate is attached as shown in the figure, it is made strong.
〈本発明の他の実施例〉 前記実施例では、フランジ部を先に成形した後に、柱
状部を成形した例を説明したが、これと逆にしてもよ
い。<Other Embodiments of the Present Invention> In the above embodiments, an example in which the flange portion is first formed and then the columnar portion is formed has been described, but this may be reversed.
即ち、スタッドを例にすると、第４図に示すように、
先に、穴26aを備えた柱状部26と、結合手段である柱状
部26の下端から突設された鍔部27と鍔部27の周端面から
突設された突起部28とを、硬度の大きい材質の合成樹脂
で一体成形する。That is, taking the stud as an example, as shown in FIG.
First, the columnar portion 26 provided with the hole 26a, the flange portion 27 protruding from the lower end of the columnar portion 26 which is a coupling means, and the protrusion portion 28 protruding from the peripheral end surface of the flange portion 27, It is integrally molded with a large synthetic resin.
次に、第５図に示すように、柱状部26の下部及び鍔部
27、突起部28を覆うように、インサート成形してフラン
ジ部29と、フランジ部29の周端部上部に突設された係止
部30、30とを、溶融度の大きい材質の合成樹脂で一体成
形する。Next, as shown in FIG. 5, the lower portion of the columnar portion 26 and the collar portion.
27, the flange portion 29, which is insert-molded so as to cover the protrusion portion 28, and the locking portions 30 and 30 projectingly provided on the upper end of the peripheral end portion of the flange portion 29, are made of a synthetic resin having a high melting degree. Mold integrally.
第６図は留め具の例を示すもので、係止部31a、31aを
備えた柱状部31を先に成形した後、フランジ部32及び係
止片33、33を一体成形した場合を示している。FIG. 6 shows an example of the fastener, showing a case where the columnar portion 31 having the locking portions 31a, 31a is molded first, and then the flange portion 32 and the locking pieces 33, 33 are integrally molded. There is.
なお、以上の実施例では、異なる２つの材質の合成樹
脂による２色成形の場合を示したが、第７図に示すよう
に、別個に成形した第１、第２の成形体を結合手段の嵌
込みによって結合させてもよい。In the above embodiment, the case of two-color molding using synthetic resins of two different materials is shown. However, as shown in FIG. 7, the first and second molded bodies molded separately are used as the joining means. You may connect by fitting.
即ち、硬度の大きい合成樹脂で、柱状部40と、結合手
段である嵌込部41と嵌込部41から外方へ突設された突起
部41aとから成る第１成形体42を一体成形する。これと
は別に、溶融度の大きい材質の合成樹脂で、円形の嵌合
穴43aを有するフランジ部43と、フランジ部43の周端面
上部に突設された係止片44とから成る第２成形体45を一
体成形する。That is, the first molded body 42, which is made of synthetic resin having a high hardness, is integrally formed from the columnar portion 40, the fitting portion 41 serving as the coupling means, and the projection portion 41a protruding outward from the fitting portion 41. . Separately from this, a second molding which is made of a synthetic resin having a high degree of melting and is composed of a flange portion 43 having a circular fitting hole 43a and a locking piece 44 projecting above the peripheral end surface of the flange portion 43. The body 45 is integrally molded.
次に、第８図に示すように、第１成形体42の嵌込部41
を第２成形体45の嵌合穴43aに嵌込んで結合する。この
際、第１成形体42の突起部41aが強く嵌合穴43aに喰い込
んで分離困難に結合される。Next, as shown in FIG. 8, the fitting portion 41 of the first molded body 42.
Is fitted into the fitting hole 43a of the second molded body 45 to be coupled. At this time, the projecting portion 41a of the first molded body 42 strongly digs into the fitting hole 43a and is coupled in a manner difficult to separate.
第９図はこの嵌込みによる他の実施例を示している。
即ち、硬度の大きい材質の樹脂から成る柱状部40の嵌合
穴40aに、溶融度の大きい材質の樹脂から成るフランジ
部43の結合手段である嵌込軸43aを嵌込んで結合する。FIG. 9 shows another embodiment by this fitting.
That is, the fitting shaft 43a, which is a coupling means of the flange portion 43 made of a resin having a high degree of melting, is fitted and fitted into the fitting hole 40a of the columnar portion 40 made of a resin having a high hardness.
なお、第７〜９図ではスタッドを例にとって説明した
が、留め具でもよいことは勿論である。また、第７〜９
図において嵌合のために、その他の種々の形状にしても
よいことは勿論である。In addition, although the stud has been described as an example in FIGS. 7 to 9, it is needless to say that a fastener may be used. Also, 7th to 9th
Of course, various other shapes may be used for fitting in the drawing.
以上、本発明の実施例を説明したが、本発明の回転溶
着部材は、以上の形状に限らず、他の形状の留め具、ス
タッドなどでもよいことは勿論である。Although the embodiment of the present invention has been described above, it is needless to say that the rotary welding member of the present invention is not limited to the above shape and may be a fastener, a stud or the like having another shape.
〈本発明の効果〉 以上説明したように、円板状のフランジ部の表面側中
央に柱状部を有し、取付平面にフランジ部の裏面を押付
けて回転させてフランジ部の裏面が取付平面への押圧回
転による摩擦熱によって溶着される樹脂製回転溶着部材
において、 前記フランジ部と前記柱状部とを、フランジ部の溶融
度が大きく、柱状部の硬度が大きいそれぞれ異なる材質
の樹脂で、インサート成形あるいは嵌込みによって一体
的に結合し、 取付平面に対して前記フランジ部の裏面を押付けて前
記フランジ部と柱状部とを一体的に回転させて、前記フ
ランジ部の裏面を取付平面で溶着するようにしたため、
溶着されるフランジ部が溶融度の大きい樹脂で、柱状部
が硬度の大きい樹脂で形成されているから、取付面への
回転溶着が容易でありながら、柱状部へのネジや板の取
付けを強固に行なうことができる。<Effects of the Present Invention> As described above, the disk-shaped flange portion has the columnar portion at the center on the front surface side, and the rear surface of the flange portion is pressed against the mounting plane to rotate so that the rear surface of the flange portion becomes the mounting plane. In a resin rotary welding member that is welded by frictional heat due to pressing rotation of the flange, the flange portion and the columnar portion are insert-molded with resins of different materials having a high degree of melting of the flange portion and a high hardness of the columnar portion. Alternatively, they may be integrally joined by fitting, and the back surface of the flange portion may be pressed against the mounting plane to integrally rotate the flange portion and the columnar portion so that the back surface of the flange portion is welded on the mounting plane. Because
Since the flange to be welded is made of a resin with a high degree of melting and the columnar part is made of a resin with a high hardness, it is easy to rotationally weld to the mounting surface, but the screw or plate is firmly attached to the columnar part. Can be done
第１、２図は本発明の一実施例を示し、第１図は先に成
形するフランジ部を示す斜視図、第２図（ａ）はこのフ
ランジ部上にさらに成形した回転溶着部材を示す斜視
図、同図（ｂ）はその断面図である。第３図は本発明の
他の実施例を示す斜視図である。 第４、５図は本発明のさらに他の実施例を示し、第４図
は先に成形する柱状部を示す斜視図、第５図（ａ）はこ
の柱状部にさらに成形した回転溶着部材を示す斜視図、
同図（ｂ）はその断面図である。第６図はさらに本発明
の他の実施例を示す斜視図である。 第７図は本発明のさらに他の実施例の結合前の状態を示
す斜視図、第８図は結合後の状態を示す斜視図である。
第９図は本発明のさらに他の実施例を示す断面図であ
る。 第10、11図はそれぞれ従来の樹脂製回転溶着部材を示す
斜視図である。第12図は回転溶着部材による回転溶着動
作を示す断面図である。第13、14図は、柱状部への板の
取付け状態を示す断面図である。 20……回転溶着部材、21……フランジ部、22……係止
片、23……突起部、24……鍔部、25……柱状部、25a…
…穴、25b……係止部、26……柱状部、27……鍔部、28
……突起部、29……フランジ部、30……係止部、31……
柱、40……柱状部、41……嵌込部、42……第１成形体、
43a……嵌合穴、43……フランジ部、44……係止片、45
……第２成形体。FIGS. 1 and 2 show an embodiment of the present invention, FIG. 1 is a perspective view showing a flange portion to be previously formed, and FIG. 2 (a) shows a rotary welding member further formed on the flange portion. A perspective view and the same figure (b) are sectional drawings. FIG. 3 is a perspective view showing another embodiment of the present invention. 4 and 5 show still another embodiment of the present invention, FIG. 4 is a perspective view showing a columnar portion to be previously molded, and FIG. 5 (a) shows a rotary welding member further molded to this columnar portion. Perspective view,
FIG. 2B is a sectional view thereof. FIG. 6 is a perspective view showing another embodiment of the present invention. FIG. 7 is a perspective view showing a state before coupling of still another embodiment of the present invention, and FIG. 8 is a perspective view showing a state after coupling.
FIG. 9 is a sectional view showing still another embodiment of the present invention. 10 and 11 are perspective views showing a conventional resin rotary welding member, respectively. FIG. 12 is a sectional view showing the rotary welding operation by the rotary welding member. 13 and 14 are cross-sectional views showing how the plate is attached to the columnar portion. 20 …… Rotary welding member, 21 …… Flange part, 22 …… Locking piece, 23 …… Projection part, 24 …… Flange part, 25 …… Column part, 25a…
… Hole, 25b …… Locking part, 26 …… Columnar part, 27 …… Brim part, 28
...... Projection part, 29 ...... Flange part, 30 ...... Locking part, 31 ......
Pillar, 40 …… Column part, 41 …… Insertion part, 42 …… First molded body,
43a …… Mating hole, 43 …… Flange part, 44 …… Locking piece, 45
...... Second molded body.
Claims (1)
を有し、取付平面にフランジ部の裏面を押付けて回転さ
せてフランジ部の裏面が取付平面への押圧回転による摩
擦熱によって溶着される樹脂製回転溶着部材において、 前記フランジ部と前記柱状部とを、フランジ部の溶融度
が大きく、柱状部の硬度が大きいそれぞれ異なる材質の
樹脂で、インサート成形あるいは嵌込みによって一体的
に結合し、 取付平面に対して前記フランジ部の裏面を押付けて前記
フランジ部と柱状部とを一体的に回転させて、前記フラ
ンジ部の裏面を取付平面に溶着するようにしたことを特
徴とする樹脂製回転溶着部材。1. A disc-shaped flange portion has a columnar portion in the center of the front surface side, and the rear surface of the flange portion is rotated by pressing the rear surface of the flange portion against the mounting plane, and the rear surface of the flange portion is pressed by the frictional heat of the mounting plane. In the resin-made rotary welding member to be welded, the flange portion and the columnar portion are integrally formed by insert molding or fitting by resin of different materials having a large degree of melting of the flange portion and a large hardness of the columnar portion. It is characterized in that the rear surface of the flange portion is pressed against the mounting plane to integrally rotate the flange portion and the columnar portion, and the rear surface of the flange portion is welded to the mounting plane. Resin rotary welding member.