JP2023095852A - 架橋スチレン性ブロック共重合体 - Google Patents
架橋スチレン性ブロック共重合体 Download PDFInfo
- Publication number
- JP2023095852A JP2023095852A JP2023061713A JP2023061713A JP2023095852A JP 2023095852 A JP2023095852 A JP 2023095852A JP 2023061713 A JP2023061713 A JP 2023061713A JP 2023061713 A JP2023061713 A JP 2023061713A JP 2023095852 A JP2023095852 A JP 2023095852A
- Authority
- JP
- Japan
- Prior art keywords
- sbcs
- sbc
- compatible
- composition
- resins
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
薄肉弾性浸漬製品は、伝統的に、天然ゴム(NR)、ポリクロロプレン(CR)、ポリイソプレン(IR)、ポリウレタン(PU)、ニトリルブタジエンゴム(NBR)、スチレン系ブロック共重合体(SBC)、これらの混合物、又はこれらの積層体で作られている。
薄肉弾性膜は、通常、水分散液(ラテックス)又は1以上の適当な溶媒の溶液のいずれかであってもよい重合体の液体混合物に、適切な形状の型を浸漬することにより、所期の用途(手袋、コンドーム、その他)に成形される。硬い膜は、水又は他の溶媒の蒸発後に形成される。
通常、材料、配合条件及び薄肉膜への変換プロセスの組合せが、得られる製品の性能を定める。
SBCは、ゴムの機械的特性と熱可塑性樹脂の加工特性を有する熱可塑性エラストマーに分類される。これらの特性は、その分子構造に起因する。SBCは少なくとも3つのブロックから成り、それは、通常は2つの硬いポリスチレン末端ブロックと1つの柔らかいエラストマー(ポリブタジエン、ポリイソプレン-水素添加又は非水素添加)中間ブロックである。より一般的なSBCは、スチレン-エチレン/ブチレン-スチレン(SEBS)、スチレン-ブタジエン-スチレン(SBS)及びスチレン-イソプレン-スチレン(SIS)のような直鎖状3ブロック共重合体であるが、他のアーキテクチャ(たとえば、3以上のブロックで構成される共重合体)及び他の構造(星形又は放射状)も可能である。
上記特許に記載されているSBCで製造された製品には重要な欠点がある。ネットワークが化学的架橋ではなく物理的架橋のみで形成されているため、ある種の有機溶媒と接触すると、ガラス状のポリスチレンドメインは、柔らかくなり、凝集力を失う。
ある側面では、この開示は、1以上のSBC及び1以上のSBCのスチレン系末端ブロックと相溶性の1以上の重合体を含むエラストマー性スチレン系ブロック共重合体(SBC)組成物であって、
当該ブロック共重合体組成物は、物理的及び化学的に架橋されており、
当該化学的な架橋はSBCの鎖間の共有結合を含み、かつ、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含む、
SBC組成物を提供する。
当該相溶性重合体混合物は、物理的及び化学的に架橋されており、
当該化学的な架橋はSBCの鎖間の共有結合を含み、かつ、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含む、
混合物を提供する。
(a) 1以上のSBC、
(b) 1以上のSBCのポリスチレン末端ブロックと相溶性の1以上の重合体、及び
(c) 1以上のSBCの鎖間に共有結合を誘導できる1以上の架橋剤
含むエラストマー性スチレン系ブロック共重合体組成物を提供する。
ましくは、3,000g/mol未満である。
プロパントリス(3-メルカプトプロピオネート)、ペンタエリスリトールテトラキス(3-メ
ルカプトプロピオネート)、エトキシ化トリメチロールプロパントリ(3-メルカプトプロピオネート)などの官能性チオール、及び、ビニル基又はアリル基を有する他の多機能化合物、並びにこれらの混合物からなる群から選択されてもよい。
ステルのようなその他のものからなる群から選択されてもよい。
.85~0.90の比重を有する薬用白色油である。
・相溶性重合体:0.25~100phr、好ましくは5~50phr
・可塑剤/可撓化剤:0~200phr、好ましくは20~75phr
・架橋剤:0.01~5phr、好ましくは0.05~1phr
・光開始剤:0~5phr、好ましくは0~2phr。
有し、かつ、当該薄膜は実質的に有機溶媒に不溶である。
本組成物、構成要素、物品及び/又は方法を開示し、記載する前に、特に明記しない限り、本発明は特定の組成物、成分、物品、方法などに限定されるものではなく、特に断りのない限り変化する可能性があることを理解されたい。また、本明細書で使用される用語は、特定の態様を説明することのみを目的としており、限定することを意図していないことも理解されたい。
ここで、当該ブロック共重合体組成物は物理的及び化学的に架橋され、
当該化学的な架橋はSBCの鎖間の共有結合を含み、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含み;
当該1以上のSBCは、SIS、SBS、SIBS、S-イソブチレン-S、SEBS、SEPS、SEEPS、又は、中間ラバーブロックにグラフトされた反応性基、例えば、カルボン酸、アミン、アルコール、マレイン酸無水物、エポキシ、イソシアン酸塩、及びアジリジン若しくはこれらの組合せで官能基化されたSBCからなる群から選択され、かつ、当該1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択される。
ここで、当該ブロック共重合体組成物は、物理的及び化学的に架橋されており、
当該化学的な架橋はSBCの鎖間の共有結合を含み、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含み、
当該1以上のSBCは、SIS、SBS、SIBS、S-イソブチレン-S、SEBS、SEPS、SEEPS、又は、中間ラバーブロックにグラフトされた反応性基、例えば、カルボン酸、アミン、アルコール、マレイン酸無水物、エポキシ、イソシアン酸塩、及びアジリジン若しくはこれらの組合せで官能基化されたSBCからなる群から選択され、かつ、当該1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の分子量(Mn)を有する。
ここで、当該ブロック共重合体組成物は、物理的及び化学的に架橋されており、
当該化学的な架橋はSBCの鎖間の共有結合を含み、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含み、
当該少なくとも1つのSBCは、化学的な架橋を可能にする二重結合のような反応性官能基をそのエラストマー性中間ブロック中に含み、かつ、
当該1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の分子量(Mn)を有する。
ここで、当該ブロック共重合体組成物は、物理的及び化学的に架橋されており、
当該化学的な架橋はSBCの鎖間の共有結合を含み、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含み、
当該少なくとも1つのSBCは、化学的な架橋を可能にする二重結合のような反応性官能基をそのエラストマー性中間ブロック中に含み、かつ、
当該1以上の相溶性重合体は、ポリスチレン樹脂、αメチルスチレン樹脂、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体及びこれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の分子量(Mn)を有する。
ここで、当該相溶性重合体混合物は、物理的及び化学的に架橋されており、
当該化学的な架橋はSBCの鎖間の共有結合を含み、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含み、
当該1以上のSBCは、SIS、SBS、SIBS、S-イソブチレン-S、SEBS、SEPS、SEEPS、又は、中間ラバーブロックにグラフトされた反応性基、例えば、カルボン酸、アミン、アルコール、マレイン酸無水物、エポキシ、イソシアン酸塩及びアジリジン若しくはこれらの組合せで官能基化されたSBCからなる群から選択され、かつ、
当該1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択される。
ここで、当該相溶性重合体混合物は、物理的及び化学的に架橋されており、
当該化学的な架橋はSBCの鎖間の共有結合を含み、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含み、
当該1以上のSBCは、SIS、SBS、SIBS、S-イソブチレン-S、SEBS、SEPS、SEEPS、又は、中間ラバーブロックにグラフトされた反応性基、例えば、カルボン酸、アミン、アルコール、マレイン酸無水物、エポキシ、イソシアン酸塩及びアジリジン若しくはこれらの組合せで官能基化されたSBCからなる群から選択され、かつ、
当該1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の分子量(Mn)を有する。
ここで、当該相溶性重合体混合物は、物理的及び化学的に架橋されており、
当該化学的な架橋はSBCの鎖間の共有結合を含み、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含み、
当該少なくとも1つのSBCは、化学的な架橋を可能にする二重結合のような反応性官能基をそのエラストマー性中間ブロック中に含み、かつ、
当該1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の分子量(Mn)を有する。
ここで、当該相溶性重合体混合物は、物理的及び化学的に架橋されており、
当該化学的な架橋はSBCの鎖間の共有結合を含み、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含み、
当該少なくとも1つのSBCは、化学的な架橋を可能にする二重結合のような反応性官能基をそのエラストマー性中間ブロック中に含み、かつ、
当該1以上の相溶性重合体は、ポリスチレン樹脂、αメチルスチレン樹脂、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体及びこれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の分子量(Mn)を有する。
(a) 1以上のSBC、
(b) 1以上のSBCのポリスチレン末端ブロックと相溶性の1以上の重合体、かつ、(c) 1以上のSBCの鎖間に共有結合を誘導できる1以上の架橋剤、
を含むエラストマー性スチレン系ブロック共重合体組成物が提供され、
ここで、当該1以上のSBCは、SIS、SBS、SIBS、S-イソブチレン-S、SEBS、SEPS、SEEPS、又は、中間ラバーブロックにグラフトされた反応性基、例えば、カルボン酸、アミン、アルコール、マレイン酸無水物、エポキシ、イソシアン酸塩及びアジリジン、又はこれらの組合せで官能基化されたSBCからなる群から選択され、
当該1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択され、かつ、
当該1以上の架橋剤は、少なくとも2つの炭素-炭素二重結合を含む、芳香族、脂肪族及びヘテロ原子のモノマー及びオリゴマー、例えば、トリメチロールプロパントリアクリレート(TMPTA)、トリメチロールプロパントリメタクリレート(TMPTMA)、エポキシアクリレート、ウレタンアクリレート、トリアリルシアヌレート、トリアリルイソシアヌレートなどの多官能性アクリレート、1,8-ジメルカプト-3,6-ジオキサオクタン、
トリメチロールプロパントリス(3-メルカプトプロピオネート)、ペンタエリスリトールテトラキス(3-メルカプトプロピオネート)、エトキシ化トリメチロールプロパントリ(3-メ
ルカプトプロピオネート)などの官能性チオール、及び、ビニル基又はアリル基を有する他の多機能化合物、並びにこれらの混合物からなる群から選択される。
(a) 1以上のSBC、;
(b) 1以上のSBCのポリスチレン末端ブロックと相溶性の1以上の重合体、及び、(c) 1以上のSBCの鎖間に共有結合を誘導できる1以上の架橋剤、
を含むエラストマー性スチレン系ブロック共重合体組成物が提供され、
ここで、当該1以上のSBCは、SIS、SBS、SIBS、S-イソブチレン-S、SEBS、SEPS、SEEPS、又は、中間ラバーブロックにグラフトされた反応性基、例えば、カルボン酸、アミン、アルコール、マレイン酸無水物、エポキシ、イソシアン酸塩及びアジリジン、又はこれらの組合せで官能基化されたSBCからなる群から選択され、
当該1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択され、
当該1以上の架橋剤は、少なくとも2つの炭素-炭素二重結合を含む、芳香族、脂肪族及びヘテロ原子のモノマー及びオリゴマー、例えば、トリメチロールプロパントリアクリレート(TMPTA)、トリメチロールプロパントリメタクリレート(TMPTMA)、エポキシアクリレート、ウレタンアクリレート、トリアリルシアヌレート、トリアリルイソシアヌレートなどの多官能性アクリレート、1,8-ジメルカプト-3,6-ジオキサオクタン、
トリメチロールプロパントリス(3-メルカプトプロピオネート)、ペンタエリスリトールテトラキス(3-メルカプトプロピオネート)、エトキシ化トリメチロールプロパントリ(3-メ
ルカプトプロピオネート)などの官能性チオール、及び、ビニル基又はアリル基を有する他の多機能化合物、並びにこれらの混合物、からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の
分子量(Mn)を有する。
(a) 1以上のSBC、
(b) 1以上のSBCのポリスチレン末端ブロックと相溶性の1以上の重合体、かつ、(c) 1以上のSBCの鎖間に共有結合を誘導できる1以上の架橋剤、
を含むエラストマー性スチレン系ブロック共重合体組成物が提供され、
ここで、当該少なくとも1つのSBCは、化学的な架橋を可能にする二重結合のような反応性官能基をそのエラストマー性中間ブロック中に含み、
当該1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択され、かつ、
当該1以上の架橋剤は、少なくとも2つの炭素-炭素二重結合を含む、芳香族、脂肪族及びヘテロ原子のモノマー及びオリゴマー、例えば、トリメチロールプロパントリアクリレート(TMPTA)、トリメチロールプロパントリメタクリレート(TMPTMA)、エポキシアクリレート、ウレタンアクリレート、トリアリルシアヌレート、トリアリルイソシアヌレートなどの多官能性アクリレート、1,8-ジメルカプト-3,6-ジオキサオクタン、
トリメチロールプロパントリス(3-メルカプトプロピオネート)、ペンタエリスリトールテトラキス(3-メルカプトプロピオネート)、エトキシ化トリメチロールプロパントリ(3-メ
ルカプトプロピオネート)などの官能性チオール、及び、ビニル基又はアリル基を有する他の多機能化合物、並びにこれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の分
子量(Mn)を有する。
(a) 1以上のSBC、
(b) 1以上のSBCのポリスチレン末端ブロックと相溶性の1以上の重合体、かつ、(c) 1以上のSBCの鎖間に共有結合を誘導できる1以上の架橋剤、
を含むエラストマー性スチレン系ブロック共重合体組成物が提供され、
ここで、当該少なくとも1つのSBCは、化学的な架橋を可能にする二重結合のような反応性官能基をそのエラストマー性中間ブロック中に含み、
当該1以上の相溶性重合体は、ポリスチレン樹脂、αメチルスチレン樹脂、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体及びこれらの混合物からなる群から選択され、かつ、
当該1以上の架橋剤は、少なくとも2つの炭素-炭素二重結合を含む、芳香族、脂肪族及びヘテロ原子のモノマー及びオリゴマー、例えば、トリメチロールプロパントリアクリレート(TMPTA)、トリメチロールプロパントリメタクリレート(TMPTMA)、エポキシアクリレート、ウレタンアクリレート、トリアリルシアヌレート、トリアリルイソシアヌレートなどの多官能性アクリレート、1,8-ジメルカプト-3,6-ジオキサオクタン、
トリメチロールプロパントリス(3-メルカプトプロピオネート)、ペンタエリスリトールテトラキス(3-メルカプトプロピオネート)、エトキシ化トリメチロールプロパントリ(3-メ
ルカプトプロピオネート)などの官能性チオール、及び、ビニル基又はアリル基を有する他の多機能化合物、並びにこれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の分
子量(Mn)を有する。
(a) 1以上のSBC、
(b) 1以上のSBCのポリスチレン末端ブロックと相溶性の1以上の重合体、かつ、(c) 1以上のSBCの鎖間に共有結合を誘導できる1以上の架橋剤、
を含むエラストマー性スチレン系ブロック共重合体組成物が提供され、
ここで、当該1以上のSBCは、SIS、SBS又はそれらの混合物からなる群から選択され、
当該少なくとも1つのSBCは、化学的な架橋を可能にする二重結合のような反応性官能基をそのエラストマー性中間ブロック中に含み、かつ、
当該1以上の相溶性重合体は、ポリスチレン樹脂、αメチルスチレン樹脂、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体及びこれらの混合物からなる群から選択され、かつ、
当該1以上の架橋剤は、1,8-ジメルカプト-3,6-ジオキサオクタン、トリメチロールプロ
パントリス(3-メルカプトプロピオネート)、ペンタエリスリトールテトラキス(3-メルカ
プトプロピオネート)、エトキシ化トリメチロールプロパントリ(3-メルカプトプロピオネート)などの官能性チオール、及びそれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol
未満の分子量(Mn)を有する。
ここで、当該1以上のSBCは、SIS、SBS、SIBS、S-イソブチレン-S、SEBS、SEPS、SEEPS、又は、中間ラバーブロックにグラフトされた反応性基、例えば、カルボン酸、アミン、アルコール、マレイン酸無水物、エポキシ、イソシアン酸塩及びアジリジン、又はこれらの組合せで官能基化されたSBCからなる群から選択され、
当該1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択され、かつ、
当該1以上の架橋剤は、少なくとも2つの炭素-炭素二重結合を含む、芳香族、脂肪族及びヘテロ原子のモノマー及びオリゴマー、例えば、トリメチロールプロパントリアクリレート(TMPTA)、トリメチロールプロパントリメタクリレート(TMPTMA)、エポキシアクリレート、ウレタンアクリレート、トリアリルシアヌレート、トリアリルイソシアヌレートなどの多官能性アクリレート、1,8-ジメルカプト-3,6-ジオキサオクタン、
トリメチロールプロパントリス(3-メルカプトプロピオネート)、ペンタエリスリトールテトラキス(3-メルカプトプロピオネート)、エトキシ化トリメチロールプロパントリ(3-メ
ルカプトプロピオネート)などの官能性チオール、及び、ビニル基又はアリル基を有する他の多機能化合物、並びにこれらの混合物からなる群から選択される。
ここで、当該1以上のSBCは、SIS、SBS、SIBS、S-イソブチレン-S、SEBS、SEPS、SEEPS、又は、中間ラバーブロックにグラフトされた反応性基、例えば、カルボン酸、アミン、アルコール、マレイン酸無水物、エポキシ、イソシアン酸塩及びアジリジン、又はこれらの組合せで官能基化されたSBCからなる群から選択され、
当該1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択され、かつ、
当該1以上の架橋剤は、少なくとも2つの炭素-炭素二重結合を含む、芳香族、脂肪族及びヘテロ原子のモノマー及びオリゴマー、例えば、トリメチロールプロパントリアクリレート(TMPTA)、トリメチロールプロパントリメタクリレート(TMPTMA)、エポキシアクリレート、ウレタンアクリレート、トリアリルシアヌレート、トリアリルイソシアヌレートなどの多官能性アクリレート、1,8-ジメルカプト-3,6-ジオキサオクタン、
トリメチロールプロパントリス(3-メルカプトプロピオネート)、ペンタエリスリトールテトラキス(3-メルカプトプロピオネート)、エトキシ化トリメチロールプロパントリ(3-メ
ルカプトプロピオネート)などの官能性チオール、及び、ビニル基又はアリル基を有する他の多機能化合物、並びにこれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の分
子量(Mn)を有する。
ここで、当該少なくとも1つのSBCは、化学的な架橋を可能にする二重結合のような反応性官能基をそのエラストマー性中間ブロック中に含み、かつ、
当該1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択され、かつ、
当該1以上の架橋剤は、少なくとも2つの炭素-炭素二重結合を含む、芳香族、脂肪族及びヘテロ原子のモノマー及びオリゴマー、例えば、トリメチロールプロパントリアクリレート(TMPTA)、トリメチロールプロパントリメタクリレート(TMPTMA)、エポキシアクリレート、ウレタンアクリレート、トリアリルシアヌレート、トリアリルイソシアヌレートなどの多官能性アクリレート、1,8-ジメルカプト-3,6-ジオキサオクタン、
トリメチロールプロパントリス(3-メルカプトプロピオネート)、ペンタエリスリトールテトラキス(3-メルカプトプロピオネート)、エトキシ化トリメチロールプロパントリ(3-メ
ルカプトプロピオネート)などの官能性チオール、及び、ビニル基又はアリル基を有する他の多機能化合物、並びにこれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の分
子量(Mn)を有する。
ここで、当該少なくとも1つのSBCは、化学的な架橋を可能にする二重結合のような反応性官能基をそのエラストマー性中間ブロック中に含み、かつ、
当該1以上の相溶性重合体は、ポリスチレン樹脂、αメチルスチレン樹脂、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体及びこれらの混合物からなる群から選択され、かつ、
当該1以上の架橋剤は、少なくとも2つの炭素-炭素二重結合を含む、芳香族、脂肪族及びヘテロ原子のモノマー及びオリゴマー、例えば、トリメチロールプロパントリアクリレート(TMPTA)、トリメチロールプロパントリメタクリレート(TMPTMA)、エポキシアクリレート、ウレタンアクリレート、トリアリルシアヌレート、トリアリルイソシアヌレートなどの多官能性アクリレート、1,8-ジメルカプト-3,6-ジオキサオクタン、
トリメチロールプロパントリス(3-メルカプトプロピオネート)、ペンタエリスリトールテトラキス(3-メルカプトプロピオネート)、エトキシ化トリメチロールプロパントリ(3-メ
ルカプトプロピオネート)などの官能性チオール、及び、ビニル基又はアリル基を有する他の多機能化合物、並びにこれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の分
子量(Mn)を有する。
ここで、当該少なくとも1つのSBCは、化学的な架橋を可能にする二重結合のような反応性官能基をそのエラストマー性中間ブロック中に含み、かつ、
当該1以上の相溶性重合体は、ポリスチレン樹脂、αメチルスチレン樹脂、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体及びこれらの混合物からなる群から選択され、かつ、
当該1以上の架橋剤は、1,8-ジメルカプト-3,6-ジオキサオクタン、トリメチロールプロ
パントリス(3-メルカプトプロピオネート)、ペンタエリスリトールテトラキス(3-メルカ
プトプロピオネート)、エトキシ化トリメチロールプロパントリ(3-メルカプトプロピオネート)などの官能性チオール、及びそれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol
未満の分子量(Mn)を有する。
、当該薄膜は実質的に有機溶媒に不溶である。
この開示によれば、SBC組成物又は相溶性重合体混合物は、1.0MPa未満又は0.70MPa未満の100%伸び率を有してもよい。
劣化していない膜で測定)を超える破断力を有してもよい。
この開示の態様によれば、組成物は、PHR(100ゴムあたり)で表され、ゴムは1以上のSBCである。組成物中の成分の例示的な範囲は以下のものを含む:
・相溶性重合体:0.25~100phr、好ましくは5~50phr
・可塑剤/可撓化剤:0~200phr、好ましくは20~75phr
・架橋剤:0.01~5phr、好ましくは0.05~1phr
・光開始剤:0~5phr、好ましくは0~2phr。
本明細書に開示の薄肉弾性浸漬製品、例えば手袋、特に医療用手袋、及びコンドームは、約10~約500ミクロン又は約150~約250ミクロンの厚さであってもよい。
以下の実施例は、本明細書で開示された組成物を説明し、また、この開示を説明することを意図している。実施例は、決して、この開示の範囲を限定するものとして解釈されるべきではない。
以下の実施例は、この開示によれば、組成物の改善された性能(機械的性質及び耐薬品性)を示す。
、及びトリメチルプロパントリス(3-メルカプトプロピオネート)としての架橋剤を、メチルシクロヘキサン及びトルエンの混合物(8:2)に溶解し、18重量%の固形分を有する溶液を調製した。
1) スワブ試験:0.5gの純粋なメタクリル酸メチル単量体を綿棒に浸み込ませ、前もってわずかに張力をかけた膜に塗布した。接触時間は、わずかな圧力の下で、10秒であった。試験を3回繰り返し、その後、膜の抵抗性を試験した。
2) 膨潤試験:膜から直径25mmのディスクを切り取り、20mlのMEKを含むビーカー中に5分間、わずかに攪拌しながら入れた。5分後、ディスクを取り外し、その外面をティッシュできれいにし、ディスクの直径を測定した。膨潤率を、100×(膨潤後の直径(mm)-25)/25として測定した。
機械的性質を、手術用手袋のASTM 3577に従って測定した。老化していない合成2型材料
では、引張強度の下限は17MPaである。
結果を以下の表に示す。
ト)で効率的に化学架橋できることを示す。
- SBC単独(試料1)
- 架橋剤を配合しないで相溶性重合体と組み合わせたSBC(試料2)
- 相溶性重合体を配合しないで架橋剤と組み合わせたSBC(試料4)
より大きな機械的性質を示すことを物語る。
試料1~4で使用されているSBS共重合体を置き換えるために、粘度45mPas(濃度10%のトルエン中、25℃)のスチレン-イソプレンジブロック共重合体を含むスチレン-イソプレン-スチレン共重合体(SIS)を使用した。
数=2.8)に基づき、可塑剤も可撓化剤も含まない。架橋剤は、1phrのトリメチロールプロパントリメタクリレートである。
以下の重合体の組合せを用い、多層膜を製造した:
- 上記試料3に記載のスチレン-ブタジエン-スチレンブロック共重合体組成物からなる厚さ80±10μmの第1層
- 高分子量スチレン-エチレン/ブチレン-スチレン(SEBS)からなる厚さ140±20μmの第2層。
このSEBSは、粘度75cp(5%のトルエン)の放射状構造で、31%のポリスチレンを含む。相溶性重合体は、25phrのスチレン及び置換スチレン(Mn=800g/mol、多
分散性指数=2.8)に基づき、可塑剤の量は60phrである。架橋剤は、0.2phrのトリメチルプロパントリス(3-メルカプトプロピオネート)である。多層膜に、40kGy
±3の電子線照射を行った。この膜の分析の結果、20.5MPaの引張強度とスワブ試験での優れた耐性が示された。
以下に、出願当初の特許請求の範囲に記載された発明を付記する。
[1] 1以上のスチレン系ブロック共重合体(SBC)、及び1以上のSBCのスチレン系末端ブロックと相溶性の1以上の重合体を含むエラストマー性スチレン系ブロック共重合体組成物であって、
当該ブロック共重合体組成物は、物理的及び化学的に架橋されており、
当該化学的な架橋はSBCの鎖間の共有結合を含み、かつ、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含む、
スチレン系ブロック共重合体組成物。
[2] 1以上のSBC、1以上のSBCの1以上のポリスチレン末端ブロックと相溶性の1以上の重合体、及び、1以上のSBCの鎖間に共有結合を誘導できる1以上の架橋剤を含む、エラストマー性スチレン系ブロック共重合体組成物。
[3] 1以上のSBC、及び1以上のSBCのスチレン系末端ブロックと相溶性の1以上の重合体を含む相溶性重合体混合物であって、
当該相溶性重合体混合物は、物理的及び化学的に架橋されており、
当該化学的な架橋はSBCの鎖間の共有結合を含み、かつ、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含む、
相溶性重合体混合物。
[4] 1以上のSBC、1以上のSBCの1以上のポリスチレン末端ブロックと相溶性の1以上の重合体、及び、1以上のSBCの鎖間に共有結合を誘導できる1以上の架橋剤を結合する工程を含むSBC組成物を製造する方法。
[5] 1以上のSBCのエラストマー性中間ブロックと適合性のある1以上の可塑剤及び/又は可撓化剤をさらに含む、[1]若しくは[2]に記載の組成物、[3]に記載の混合物、又は[4]に記載の方法。
[6] 前記1以上のSBCは、独立して、完全に不飽和の、部分的に不飽和の、又は完全に飽和のエラストマー性中間ブロックを含む、[1]、[2]若しくは[5]のいずれかに記載の組成物、[3]若しくは[5]のいずれかに記載の混合物、又は[4]若しくは[5]のいずれかに記載の方法。
[7] 前記1以上のSBCは、完全に飽和のエラストマー性中間ブロックを含み、当該完全に飽和のエラストマー性中間ブロックは、放射線にさらされた場合、例えば、電子線照射を受けた場合に切断可能である、[1]、[2]、[5]若しくは[6]のいずれかに記載の組成物、[3]、[5]若しくは[6]のいずれかに記載の混合物、又は[4]~[6]のいずれかに記載の方法。
[8] 前記1以上のSBSは、SIS、SBS、SIBS、S-イソブチレン-S、SEBS、SEPS、SEEPS、又は、中間ラバーブロックにグラフトされた反応性基、例えば、カルボン酸、アミン、アルコール、マレイン酸無水物、エポキシ、イソシアン酸塩及びアジリジン並びにこれらの組合せで官能基化されたSBCからなる群から選択される、[1]、[2]若しくは[5]~[7]のいずれかに記載の組成物、[3]若しくは[5]~[7]のいずれかに記載の混合物、又は[4]~[7]のいずれかに記載の方法。
[9] 前記1以上のSBCは、100,000g/molを超える分子量(Mn)である、[1]、[2]若しくは[5]~[8]のいずれかに記載の組成物、[3]~[8]のいずれかに記載の混合物、又は[4]~[8]のいずれかに記載の方法。
[10] 前記少なくとも1のSBCは、炭素-炭素二重結合のような反応性官能基を含むエラストマー性中間ブロックを有する、[1]、[2]若しくは[5]~[9]のいずれかに記載の組成物、[3]~[9]のいずれかに記載の混合物、又は[4]~[9]のいずれかに記載の方法。
[11] 前記相溶性重合体の数平均分子量(Mn)は10,000g/mol未満であり、より好
ましくは、3,000g/mol未満である、[1]、[2]若しくは[5]~[10]のいずれかに記載の組成物、[3]~[10]のいずれかに記載の混合物、又は[4]~[10]のいずれかに記載の方法。
[12] 前記相溶性重合体は幅広い分子量の多分散性指数を有し、例えば、2.0を超える、3.0を超える、4.0を超える、又は5.0を超える、[1]、[2]若しくは[5]~[11]のいずれかに記載の組成物、[3]~[11]のいずれかに記載の混合物、又は[4]~[11]のいずれかに記載の方法。
[13] 前記相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペンフェノール類、及びこれらの混合物からなる群から選択される、[1]、[2]若しくは[5]~[12]のいずれかに記載の組成物、[3]~[12]のいずれかに記載の混合物、又は[4]~[12]のいずれかに記載の方法。
[14] 前記少なくとも1のSBCは、化学的な架橋を可能にする二重結合をそのエラストマー性中間ブロック中に含み、かつ、前記1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択され、当該SBCは100,000g/molを超える分子量(Mn)を有し、かつ、当該相溶性重合体は10,000g/mol未満の分子量(Mn)を有する、[1
]、[2]若しくは[5]~[13]のいずれかに記載の組成物、[3]~[13]のいずれかに記載の混合物、又は[4]~[13]のいずれかに記載の方法。
[15] 前記架橋剤は、トリメチロールプロパントリアクリレート(TMPTA)、トリメチロールプロパントリメタクリレート(TMPTMA)、エポキシアクリレート、ウレタンアクリレート、トリアリルシアヌレート、トリアリルイソシアヌレートなどの多官能性アクリレート、1,8-ジメルカプト-3,6-ジオキサオクタン、トリメチロールプロパン
トリス(3-メルカプトプロピオネート)、ペンタエリスリトールテトラキス(3-メルカプト
プロピオネート)、エトキシ化トリメチロールプロパントリ(3-メルカプトプロピオネート)などの官能性チオール、及び、ビニル基又はアリル基を有する他の多機能化合物、並びにこれらの混合物からなる群から選択される、[2]及び[5]~[14]のいずれかに記載の組成物又は[4]~[14]のいずれかに記載の方法。
[16] 前記架橋剤は、金属塩、有機アミン、有機ジアミン、及び有機ポリアミンからなる群から選択されるアミン架橋剤、又はポリオールである、[2]及び[5]~[14]のいずれかに記載の組成物又は[4]~[14]のいずれかに記載の方法。
[17] 前記架橋剤は、従来の硫黄、金属酸化物、及びゴムの加硫に一般的に用いられる促進剤から選択される、[2]及び[5]~[14]のいずれかに記載の組成物又は[4]~[14]のいずれかに記載の方法。
[18] 前記架橋剤は、主鎖にエーテル又はエステル基を含む、ジチオール、トリチオール及びテトラチオール分子から選択される、[2]及び[5]~[14]のいずれかに記載の組成物又は[4]~[14]のいずれかに記載の方法。
[19] 前記組成物は、例えば紫外線、電子線、ガンマ線又はX線などの放射線の照射により架橋される、[5]~[18]のいずれかに記載の方法。
[20] 前記架橋反応は、ラジカル型光開始剤の1つ又は混合物によって開始又は促進される、[5]~[19]のいずれかに記載の方法。
[21] 前記架橋光開始剤は、モノアシルホスフィンオキシド、ビスアシルホスフィンオキシド、2,4,6-トリメチルベゾイルジフェニルホスフィンオキシドのようなアシルホスフィンオキシド、又は、2-ヒドロキシメチル-1-フェニルプロパノン、ベンゾイルギ酸メ
チル及びフェニルグリオキシル酸メチルエステルのようなその他のものからなる群から選択される、[20]に記載の方法。
[22] 前記可塑剤は、SBCの中間ブロック(エラストマー性ブロック)と適合性のある液体飽和ポリオレフィン又はその混合物を含む、[5]~[18]のいずれかに記載の組成物、[3]~[14]のいずれかに記載の混合物、又は[5]~[21]のいずれかに記載の方法。
[23] 前記可塑剤は、可塑化油、好ましくは鉱物可塑化油、特にパラフィン性若しくはナフテン性の化合物又はそれらの混合物から形成される液体飽和炭化水素の精製混合物から形成される鉱物油を含む、[5]~[18]若しくは[22]のいずれかに記載の組成物、[3]~[14]若しくは[22]のいずれかに記載の混合物、又は[5]~[22]のいずれかに記載の方法。
[24] 前記可撓化剤は、ポリブタジエン、ポリイソプレン、ポリイソブテン、プロピレン及びエチレンのアモルファスポリオレフィン共重合体、ブチルゴム、並びにエラストマーブロックとの十分な適合性を有することが知られている他のエラストマーから選択される、[5]~[18]、[22]若しくは[23]のいずれかに記載の組成物、[3]~[14]、[22]若しくは[23]のいずれかに記載の混合物、又は[5]~[23]のいずれかに記載の方法。
[25] 潤滑剤、帯電防止剤、一次及び二次酸化防止剤、着色剤又は処理剤などの、ポリマー業界、特に手袋業界で従来使用されている他の補助剤をさらに含む、[1]、[2]、[5]~[18]若しくは[22]~[24]のいずれかに記載の組成物、[3]~[14]若しくは[22]~[24]のいずれかに記載の混合物、又は[4]~[24]のいずれかに記載の方法。
[26] [1]、[2]、[5]~[18]、若しくは[22]~[25]のいずれかに記載の少なくとも1のSBC組成物、又は[3]~[14]若しくは[22]~[25]に記載の混合物から、浸漬製品を製造する方法であって、製造される浸漬製品の外形に対応する外側型を、事前に特定可能な期間、1以上のSBC組成物又は相溶性重合体混合物を含む浸漬溶液に浸漬し、その後、前記浸漬製品を前記溶液から取り出し、乾燥する、方法。
[27] 乾燥させた製品を放射線、好ましくは電子線照射にさらすことをさらに含む[26]に記載の方法。
[28] 1以上のSBC組成物又は相溶性重合体混合物を含む薄膜であって、当該薄膜は、ASTM 3577に従って評価した場合、17MPaを超える引張強度を有し、当該薄膜は
実質的に有機溶媒に不溶である、薄膜。
[29] 前記膜は、約10ミクロン~約500ミクロンの厚さである[28]に記載の薄膜。
[30] 前記膜の少なくとも80%、又は95%が有機溶剤に不溶である[28]又は[29]に記載の薄膜。
[31] 薄膜であって、[1]、[2]、[5]~[18]若しくは[22]~[24]のいずれかに記載の1以上のSBC組成物、又は[3]~[14]若しくは[22]~[24]のいずれかに記載の相溶性重合体混合物を含む、薄膜。
[32] 前記膜は、約10ミクロン~約500ミクロンの厚さである[31]に記載の薄膜。
[33] 前記膜は、約150ミクロン~約250ミクロンの厚さである[31]に記載の薄膜。
[34] 前記薄膜は、ASTM 3577に従って評価した場合、17MPaを超える引張強度
を有し、前記薄膜は実質的に有機溶媒に不溶である[30]~[33]のいずれかに記載の薄膜。
[35] 多層膜であって、当該多層膜は1以上の層を含み、当該1以上の層は、[1]、[2]、[5]~[18]若しくは[22]~[25]のいずれかに記載のSBC組成物、又は[3]~[14]若しくは[22]~[25]のいずれかに記載の相溶性重合体混合物を含む、多層膜。
[36] 多層膜であって、当該多層膜は1以上の層を含み、当該1以上の層はSBC組成物又は相溶性重合体混合物を含み、当該組成物又は相溶性重合体混合物は少なくとも17MPaの引張強度を有し、当該組成物又は相溶性重合体混合物は実質的に有機溶媒に不溶である、多層膜。
[37] 多層膜であって、当該多層膜は、[28]~[34]のいずれかに記載のいくつかの薄膜を含む多層膜。
[38] 前記1以上の層は、天然ゴム、ポリブタジエン、ポリイソプレン、ポリクロロプレン、ブチルゴム、ポリウレタン、アクリル酸重合体及び共重合体、シリコーンエラストマー、他のSBC、環状ブロック共重合体(CBC)並びにそれらの混合物からなる群から選択される、[35]~[37]のいずれかに記載の多層膜。
[39] 製造物品であって、[1]、[2]、[5]~[18]、若しくは[22]~[25]のいずれかに記載の1以上のSBC組成物、又は[3]~[14]若しくは[22]~[25]のいずれかに記載の相溶性重合体混合物を含む、製造物品。
[40] 前記物品は、医療用手袋、コンドームなどの医療機器、又は実験室用手袋や清潔な工業用手袋などの個人用保護具である、[39]に記載の製造物品。
Claims (37)
- 1以上のスチレン系ブロック共重合体(SBC)、及び1以上のSBCのスチレン系末端ブロックと相溶性の1以上の重合体を含むエラストマー性スチレン系ブロック共重合体組成物であって、
前記1以上のSBCは、100,000g/molを超える分子量(Mn)であり、
前記相溶性重合体の数平均分子量(Mn)は10,000g/mol未満であり、
当該ブロック共重合体組成物は、物理的及び化学的に架橋されており、
当該化学的な架橋はSBCの鎖間の共有結合を含み、
当該物理的な架橋は、1以上のSBCのスチレン系末端ブロックと前記末端ブロックと相溶性の1以上の重合体の間の非共有結合相互作用を含み、かつ、
当該ブロック共重合体組成物は、1以上のSBCのエラストマー性中間ブロックと適合性のある1以上の可塑剤及び/又は可撓化剤を含み、前記1以上の可塑剤及び/又は可撓化剤は20~75phrの量で使用される、
スチレン系ブロック共重合体組成物。 - 1以上のSBC、1以上のSBCの1以上のポリスチレン末端ブロックと相溶性の1以上の重合体、及び、1以上のSBCの鎖間に共有結合を誘導できる1以上の架橋剤を含む、エラストマー性スチレン系ブロック共重合体組成物であって、
前記1以上のSBCは、100,000g/molを超える分子量(Mn)であり、
前記相溶性重合体の数平均分子量(Mn)は10,000g/mol未満であり、
当該ブロック共重合体組成物は、1以上のSBCのエラストマー性中間ブロックと適合性のある1以上の可塑剤及び/又は可撓化剤を含み、前記1以上の可塑剤及び/又は可撓化剤は20~75phrの量で使用される、
スチレン系ブロック共重合体組成物。 - 前記1以上のSBCは、独立して、完全に不飽和の、部分的に不飽和の、又は完全に飽和のエラストマー性中間ブロックを含む、請求項1又は2に記載の組成物。
- 前記1以上のSBCは、完全に飽和のエラストマー性中間ブロックを含み、当該完全に飽和のエラストマー性中間ブロックは、放射線にさらされた場合、例えば、電子線照射を受けた場合に切断可能である、請求項1~3のいずれか一項に記載の組成物。
- 前記1以上のSBCは、SIS、SBS、SIBS、S-イソブチレン-S、SEBS、SEPS、SEEPS、又は、中間ラバーブロックにグラフトされた反応性基、例えば、カルボン酸、アミン、アルコール、マレイン酸無水物、エポキシ、イソシアン酸塩及びアジリジン並びにこれらの組合せで官能基化されたSBCからなる群から選択される、請求項1~4のいずれか一項に記載の組成物。
- 前記少なくとも1のSBCは、炭素-炭素二重結合のような反応性官能基を含むエラストマー性中間ブロックを有する、請求項1~5のいずれか一項に記載の組成物。
- 前記相溶性重合体の数平均分子量(Mn)は3,000g/mol未満である、請求項1~6のいずれか一項に記載の組成物。
- 前記相溶性重合体の分子量の多分散性指数は2.0~3.0である、請求項1~7のいずれか一項に記載の組成物。
- 前記相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペンフェノール類、及びこれらの混合物からなる群から選択される、請求項1~8のいずれか一項に記載の組成物。
- 前記少なくとも1のSBCは、化学的な架橋を可能にする二重結合をそのエラストマー性中間ブロック中に含み、かつ、前記1以上の相溶性重合体は、ポリスチレン樹脂、クマロン-インデン樹脂、ポリインデン樹脂、ポリ(メチルインデン)樹脂、ビニルトルエン-αメチルスチレン樹脂、αメチルスチレン樹脂、ポリフェニレンエーテル、αメチルスチレンやパラメチルスチレンのようなアルキルアレーン単量体の共重合体、ロジンエステル、スチレン化テルペン類、ポリテルペン類、テルペン フェノール類、及びこれらの混合物からなる群から選択され、かつ、当該相溶性重合体は10,000g/mol未満の分子量(M
n)を有する、請求項1~9のいずれか一項に記載の組成物。 - 前記架橋剤は、トリメチロールプロパントリアクリレート(TMPTA)、トリメチロールプロパントリメタクリレート(TMPTMA)、エポキシアクリレート、ウレタンアクリレート、トリアリルシアヌレート、トリアリルイソシアヌレート、1,8-ジメルカプト-3,6-ジオキサオクタン、トリメチロールプロパントリス(3-メルカプトプロピオネート)
、ペンタエリスリトールテトラキス(3-メルカプトプロピオネート)、エトキシ化トリメチロールプロパントリ(3-メルカプトプロピオネート)などの官能性チオール、及びこれらの混合物からなる群から選択される、請求項2~10のいずれか一項に記載の組成物。 - 前記架橋剤は、金属塩、有機アミン、有機ジアミン、及び有機ポリアミンからなる群から選択されるアミン架橋剤、又はポリオールである、請求項2~11のいずれか一項に記載の組成物。
- 前記架橋剤は、従来の硫黄、金属酸化物、及びゴムの加硫に一般的に用いられる促進剤から選択される、請求項2~12のいずれか一項に記載の組成物。
- 前記架橋剤は、主鎖にエーテル又はエステル基を含む、ジチオール、トリチオール及びテトラチオール分子から選択される、請求項2~13のいずれか一項に記載の組成物。
- 前記可塑剤は、SBCの中間ブロック(エラストマー性ブロック)と適合性のある液体飽和ポリオレフィン又はその混合物を含む、請求項1~14のいずれか一項に記載の組成物。
- 前記可塑剤は、可塑化油、好ましくは鉱物可塑化油、特にパラフィン性若しくはナフテン性の化合物又はそれらの混合物から形成される液体飽和炭化水素の精製混合物から形成される鉱物油を含む、請求項1~15のいずれか一項に記載の組成物。
- 前記可撓化剤は、ポリブタジエン、ポリイソプレン、ポリイソブテン、プロピレン及びエチレンのアモルファスポリオレフィン共重合体、ブチルゴム、並びにエラストマーブロックとの十分な適合性を有することが知られている他のエラストマーから選択される、請求項1~16のいずれか一項に記載の組成物。
- 潤滑剤、帯電防止剤、一次及び二次酸化防止剤、着色剤又は処理剤をさらに含む、請求項1~17のいずれか一項に記載の組成物。
- 1以上のSBC、1以上のSBCの1以上のポリスチレン末端ブロックと相溶性の1以上の重合体、及び、1以上のSBCの鎖間に共有結合を誘導できる1以上の架橋剤を結合する工程を含むSBC組成物を製造する方法であって、
前記1以上のSBCは、100,000g/molを超える分子量(Mn)であり、前記相溶性重合体の数平均分子量(Mn)は10,000g/mol未満であり、当該SBC組成物は、1以上のS
BCのエラストマー性中間ブロックと適合性のある1以上の可塑剤及び/又は可撓化剤を含み、前記1以上の可塑剤及び/又は可撓化剤は20~75phrの量で使用される、
方法。 - 前記組成物は、例えば紫外線、電子線、ガンマ線又はX線などの放射線の照射により架橋される、請求項19に記載の方法。
- 前記架橋反応は、ラジカル型光開始剤の1つ又は混合物によって開始又は促進される、請求項19又は20に記載の方法。
- 前記架橋光開始剤は、モノアシルホスフィンオキシド、ビスアシルホスフィンオキシド、2,4,6-トリメチルベゾイルジフェニルホスフィンオキシドのようなアシルホスフィンオキシド、又は、2-ヒドロキシメチル-1-フェニルプロパノン、ベンゾイルギ酸メチル及び
フェニルグリオキシル酸メチルエステルのようなその他のものからなる群から選択される、請求項19~21のいずれか一項に記載の方法。 - 請求項1~18のいずれか一項に記載の少なくとも1のSBC組成物から、浸漬製品を製造する方法であって、製造される浸漬製品の外形に対応する外側型を、事前に特定可能な期間、1以上のSBC組成物又は相溶性重合体混合物を含む浸漬溶液に浸漬し、その後、前記浸漬製品を前記溶液から取り出し、乾燥する、方法。
- 乾燥させた製品を放射線、好ましくは電子線照射にさらすことをさらに含む請求項23に記載の方法。
- 請求項1~18のいずれか一項に記載の1以上のSBC組成物又は相溶性重合体混合物を含む薄膜であって、当該薄膜は、ASTM 3577に従って評価した場合、17MPaを超え
る引張強度を有し、当該薄膜は実質的に有機溶媒に不溶である、薄膜。 - 前記膜は、10ミクロン~500ミクロンの厚さである請求項25に記載の薄膜。
- 前記膜の少なくとも80%、又は95%が有機溶剤に不溶である請求項25又は26に記載の薄膜。
- 薄膜であって、請求項1~18のいずれか一項に記載の1以上のSBC組成物を含む、薄膜。
- 前記膜は、10ミクロン~500ミクロンの厚さである請求項28に記載の薄膜。
- 前記膜は、150ミクロン~250ミクロンの厚さである請求項28に記載の薄膜。
- 前記薄膜は、ASTM 3577に従って評価した場合、17MPaを超える引張強度を有し、
前記薄膜は実質的に有機溶媒に不溶であり、有機溶剤に対して、薄膜の少なくとも80%が不溶性である、又は薄膜の少なくとも95%が不溶性である請求項28~30のいずれか一項に記載の薄膜。 - 多層膜であって、当該多層膜は1以上の層を含み、当該1以上の層は、請求項1~18のいずれか一項に記載のSBC組成物を含む、多層膜。
- 多層膜であって、当該多層膜は1以上の層を含み、当該1以上の層は、請求項1~18のいずれか一項に記載のSBC組成物を含み、当該組成物又は相溶性重合体混合物は少なくとも17MPaの引張強度を有し、当該組成物又は相溶性重合体混合物は実質的に有機溶媒に不溶である、多層膜。
- 多層膜であって、当該多層膜は、請求項25~31のいずれか一項に記載のいくつかの薄膜を含む多層膜。
- 前記1以上の層は、天然ゴム、ポリブタジエン、ポリイソプレン、ポリクロロプレン、ブチルゴム、ポリウレタン、アクリル酸重合体及び共重合体、シリコーンエラストマー、他のSBC、環状ブロック共重合体(CBC)並びにそれらの混合物からなる群から選択される、請求項32~34のいずれか一項に記載の多層膜。
- 製造物品であって、請求項1~18のいずれか一項に記載の1以上のSBC組成物を含む、製造物品。
- 前記物品は、医療用手袋、コンドームなどの医療機器、又は実験室用手袋や清潔な工業用手袋などの個人用保護具である、請求項36に記載の製造物品。