JP2016215142A - Faucet - Google Patents
Faucet Download PDFInfo
- Publication number
- JP2016215142A JP2016215142A JP2015103750A JP2015103750A JP2016215142A JP 2016215142 A JP2016215142 A JP 2016215142A JP 2015103750 A JP2015103750 A JP 2015103750A JP 2015103750 A JP2015103750 A JP 2015103750A JP 2016215142 A JP2016215142 A JP 2016215142A
- Authority
- JP
- Japan
- Prior art keywords
- coating film
- faucet
- blasting
- projected
- grains
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、表面の塗装にウェットブラスト処理を施した水栓に関するものである。 The present invention relates to a faucet having a surface blasted by wet blasting.
特許文献１には、水栓の本体の表面にニッケルメッキ層を設けるとともに、そのニッケルメッキ層の表面にさらにクロームメッキ層を設けた構成において、前記ニッケルメッキ層にエマルジョン粒子の凹凸の付着跡を残した水栓が開示されている。この付着跡を残すことによって、水栓の本体表面が艶消し状になるとしている。 In Patent Document 1, a nickel plating layer is provided on the surface of the faucet body, and a chrome plating layer is further provided on the surface of the nickel plating layer. The remaining faucet is disclosed. By leaving this adhesion mark, the surface of the main body of the faucet is said to be matte.
特許文献１の艶消しの技術は、メッキ層に対する処理であるため、塗装された水栓にこの技術を適用することはできない。水栓の塗膜の表面を艶消しにするためには、エアのブラスト流に投射粒体を乗せたドライブラストが考えられる。 Since the matting technique of Patent Document 1 is a treatment for a plated layer, this technique cannot be applied to a painted faucet. In order to make the surface of the faucet coating surface matt, a drive last in which projecting particles are placed in an air blast flow can be considered.
ところが、ドライブラストにおいて、粒径の小さな投射粒体は、質量が小さいためにブラスト流に乗りにくい。このため、ドライブラストにおいては、投射粒体として粒径の大きなものが用いられる。その結果、艶消しが荒削りになり、高級感のある外観や、肌触りのよい艶消し表面を得ることはできない。 However, in the drive last, a projection particle having a small particle diameter is difficult to ride on a blast flow because of its small mass. For this reason, in the drive last, a thing with a large particle size is used as a projection particle. As a result, the matte becomes rough, and a high-quality appearance and a matte surface with a good touch cannot be obtained.
また、ドライブラストにおいては、塗膜表面への投射粒体の衝突によって、その塗膜表面は過熱されたり、酸化されたりする。このため、塗膜の表面に黒ずみ等の変色が生じる。また、ブラスト流内に投射粒体以外の不純物が混入された場合は、その不純物によっても塗膜表面が変色される。これらのことから、水栓の塗膜の外観が著しく低下される。そして、前記のように、塗膜表面が過熱されるため、塗膜として熱に弱い材質のものは使用できない。 In the drive last, the surface of the coating film is overheated or oxidized due to the collision of the projected particles with the surface of the coating film. For this reason, discoloration such as darkening occurs on the surface of the coating film. Moreover, when impurities other than a projection particle body are mixed in a blast flow, the coating-film surface is discolored also by the impurities. For these reasons, the appearance of the coating film on the faucet is significantly reduced. And since the coating-film surface is overheated as mentioned above, the thing of a material weak to a heat | fever cannot be used as a coating film.
加えて、投射粒体として大きな粒径のものを用いるしかないため、塗膜の表面が深く抉られるように削られるだけではなく、塗膜以外のところ，例えばメッキ面もダメージを受ける。そして、塗膜の表面が深く削られるため、塗膜の表面に印刷が施されている場合は、その印刷が削り去られて、一部または全部が消滅するおそれもある。 In addition, since it is necessary to use a projection particle having a large particle size, not only the surface of the coating film is sharpened but also the parts other than the coating film, for example, the plated surface are damaged. And since the surface of a coating film is deeply shaved, when printing is given to the surface of a coating film, the printing may be scraped off and there exists a possibility that one part or all may lose | disappear.
また、前記のように、投射粒体は質量が大きいために、図４に示すように、その投射粒体１６が塗膜１５の表面に食い込み、このため、塗膜１５の表面がざらついて肌触りが悪化することもある。 Further, as described above, since the projected particles have a large mass, as shown in FIG. 4, the projected particles 16 bite into the surface of the coating film 15, and thus the surface of the coating film 15 is rough and soft to the touch. May get worse.
さらに、塗膜の表面上をドライブラスト流が高速で流れるため、静電気の発生を避けることができず、このため、ドライブラストの作業位置には静電気による電荷を放電するための対策が必要になる。加えて、ドライブラストによって前記作業位置及びその周囲の作業空間内に粉塵が舞い散ることになり、集塵機等の粉塵対策も必要になる。 Furthermore, since the drive last flow flows on the surface of the coating film at a high speed, the generation of static electricity cannot be avoided. For this reason, it is necessary to take measures to discharge the charge due to static electricity at the drive last work position. . In addition, dust is scattered by the drive last in the work position and the work space around it, and it is necessary to take measures against dust such as a dust collector.
本発明の目的は、前記の問題点を解消して、塗膜表面が好適に艶消し処理された水栓を提供することにある。 An object of the present invention is to solve the above-mentioned problems and provide a water faucet in which the coating film surface is suitably matted.
上記の目的を達成するために、本発明においては、表面に塗膜を設けた水栓において、塗膜にはウェットブラストによる艶消し処理が施されたことを特徴とする。
従って、本発明によれば、ドライブラスト加工とは異なり、ブラスト処理において細かい粒径の投射粒体を用いることができるため、きめが細かく、肌触りの良い艶消し表面を得ることができる。また、ブラスト流がウェットであるため、投射粒体の衝突によって塗膜表面が過熱されたり、酸化されたり、不純物の影響を受けたりすることを抑制できて、塗膜表面が変色されることを防止できる。また、投射粒体として粒径が小さく、質量が小さいものを用いることができるため、投射粒体が塗膜表面に食い込みにくく、たとえ食い込んだとしてもブラスト液体によって洗い流されるため、良好な肌触りの塗膜面を得ることができる。
In order to achieve the above object, the present invention is characterized in that, in a faucet having a coating film on the surface, the coating film has been subjected to a matte treatment by wet blasting.
Therefore, according to the present invention, unlike the drive blast process, a projection particle having a fine particle diameter can be used in the blasting process, so that a matte surface having a fine texture and a good touch can be obtained. In addition, since the blast flow is wet, it is possible to suppress the coating surface from being overheated, oxidized, or affected by impurities due to the collision of the projected particles, and the coating surface can be discolored. Can be prevented. In addition, since it is possible to use a projection particle having a small particle size and a small mass, it is difficult for the projection particle to bite into the surface of the coating film. A film surface can be obtained.
本発明によれば、外観が良好で肌触りのよい塗膜面を備えた水栓を実現できるという効果を発揮する。 According to the present invention, it is possible to realize a faucet having a coating film surface having a good appearance and a good touch.
本発明を具体化した実施形態を図面に従って説明する。
図１に示すように、水栓１１は、本体部１２と、吐水口１３と、操作レバー１４とを備え、それらの外表面にはエポキシ，アクリル，フッ素系等の合成樹脂よりなる白色等の塗装が施されて、塗膜１５が設けられている。塗膜１５の表面には、艶消し処理が施されている。
An embodiment embodying the present invention will be described with reference to the drawings.
As shown in FIG. 1, the faucet 11 includes a main body portion 12, a water discharge port 13, and an operation lever 14. Coating is performed and a coating film 15 is provided. The surface of the coating film 15 is matted.
そこで、塗装方法及び艶消し処理の方法について説明する。
前記水栓１１の表面に塗膜１５を形成する場合は、前記本体部１２（図２参照）、吐水口１３、操作レバー１４等の組立て前の各部品に粉体塗装が施され、粉体の加熱、溶融、硬化を経て塗膜１５が形成される。そして、塗膜１５が硬化した後、各部品に対してウェットブラストが施される。
Therefore, a coating method and a matting method will be described.
When the coating film 15 is formed on the surface of the faucet 11, powder coating is applied to each part before assembly such as the main body 12 (see FIG. 2), the water discharge port 13, the operation lever 14 and the like. The coating film 15 is formed through heating, melting and curing. And after the coating film 15 hardens | cures, wet blasting is given with respect to each component.
このウェットブラストにおいては、図３に示すように、水道水にアルミナ等のセラミックよりなる投射粒体１６が混入されたスラリが部品に対して投射される。前記投射粒体１６は、粒径が正規分布で１０〜５０μｍ（ミクロンメートル）のものが用いられる。ここで、粒径が３０〜５０μｍの場合は、粒径が大きめであるため、投射時間を短くでき、粒径が１０〜２０μｍあるいは３０μｍ未満の場合は、きめの細かい艶消し表面を得ることができる。そして、前記スラリがブラストノズルから０．２〜０．６Ｍｐａ（メガパスカル）の圧力で噴出され、５０〜１５０ｍｍ（ミリメートル）前方にある部品に９０度の角度で投射される。 In this wet blasting, as shown in FIG. 3, slurry in which projecting particles 16 made of ceramic such as alumina are mixed with tap water is projected onto the component. As the projecting particles 16, particles having a normal distribution of 10 to 50 μm (micron meter) are used. Here, when the particle size is 30 to 50 μm, the particle size is large, so the projection time can be shortened. When the particle size is 10 to 20 μm or less than 30 μm, a fine matte surface can be obtained. it can. Then, the slurry is ejected from the blast nozzle at a pressure of 0.2 to 0.6 Mpa (megapascal), and is projected at an angle of 90 degrees onto a component 50 to 150 mm (millimeters) ahead.
このようにすれば、図３に示すように、投射粒体１６が塗膜１５の表面に衝突して、その塗膜１５の表面が艶消し処理される。そして、塗膜１５に衝突された投射粒体１６はスラリによって流される。投射終了後、部品は水洗され、残留されたスラリが流れ落とされる。 If it does in this way, as shown in FIG. 3, the projection granule 16 will collide with the surface of the coating film 15, and the surface of the coating film 15 is matted. And the projection particle body 16 collided with the coating film 15 is poured by slurry. After the projection, the parts are washed with water, and the remaining slurry is washed away.
このようにすれば、部品の塗膜１５の表面は光沢を抑えた艶消し状態になる。そして、このような部品が組付けられて、水栓１１となる。
そして、本実施形態においては、以下の効果がある。
If it does in this way, the surface of the coating film 15 of components will be in the matte state which suppressed glossiness. Such parts are assembled to form the faucet 11.
The present embodiment has the following effects.
（１）ウェットブラストによって塗膜１５の表面を粗面化して、艶消し加工が施されている。このため、光沢を抑制した高級感のある外観の水栓１１を得ることができる。この場合、ウェットブラストは、細かい粒径の投射粒体１６を用いることができるため、きめが細かく、肌触りの良い艶消し表面を得ることができる。このため、水栓１１が設置される流し台の表面が艶消し加工されている場合、水栓１１の外観を流し台の外観とマッチさせることができる。 (1) The surface of the coating film 15 is roughened by wet blasting and is matted. For this reason, it is possible to obtain a faucet 11 having a high-quality appearance with suppressed gloss. In this case, since the wet blasting can use the projection particles 16 having a fine particle size, a matte surface having a fine texture and a good touch can be obtained. For this reason, when the surface of the sink on which the faucet 11 is installed is matted, the appearance of the faucet 11 can be matched with the appearance of the sink.
（２）投射粒体１６は液体よりなるブラスト流に乗せられて塗膜１５に衝突される。従って、投射粒体１６の衝突によって塗膜１５の表面が過熱されたり、酸化されたりすることを防止できる。従って、塗膜１５の表面が黒ずんだりすることなく、変色されることを防止できて、塗膜１５の塗料が保有する本来の色による装飾効果やデザイン性を維持できる。また、前記のように、塗膜１５の表面の過熱を防止できるため、塗膜１５として熱に弱い材質のものでも使用できる。 (2) The projected particles 16 are put on a blast flow made of a liquid and collide with the coating film 15. Therefore, it is possible to prevent the surface of the coating film 15 from being overheated or oxidized by the collision of the projecting particles 16. Accordingly, the surface of the coating film 15 can be prevented from being discolored without being darkened, and the decoration effect and design by the original color possessed by the coating material of the coating film 15 can be maintained. Moreover, since the overheating of the surface of the coating film 15 can be prevented as described above, the coating film 15 can be made of a material that is weak against heat.
（３）たとえ、スラリ中に投射粒体１６以外の不純物が混入されていても、その不純物はスラリによって洗い流される。従って、不純物による塗膜１５の表面の変色を防止できる。 (3) Even if impurities other than the projecting particles 16 are mixed in the slurry, the impurities are washed away by the slurry. Therefore, discoloration of the surface of the coating film 15 due to impurities can be prevented.
（４）投射粒体１６として細かな粒径のものが用いられることができるため、その投射粒体１６は、塗膜の表面を深く抉ることはなく、薄く削るだけであるため、塗膜１５の表面に印刷が施されていても、その印刷を削り去ることなく残すことができる。 (4) Since the thing of a fine particle size can be used as the projection particle | grains 16, since the projection particle | grains 16 do not scramble the surface of a coating film deeply, but are only shaving thinly, the coating film 15 Even if the surface is printed, it can be left without being scraped off.
（５）投射粒体１６の粒径を小さくできるため、塗膜１５の表面だけではなく、塗膜１５以外の部分に対する不要なダメージを抑えることができる。
（６）投射粒体１６として粒径が小さく、質量が小さいものを用いることができるため、投射粒体１６は塗膜１５の表面に食い込みにくく、しかもスラリによって洗い流されるため、投射粒体１６が塗膜１５の表面に食い込むことを防止できる。従って、塗膜１５の表面のざらつきを防止して良好な肌触りの塗膜１５を得ることができる。
(5) Since the particle size of the projected particle 16 can be reduced, unnecessary damage not only to the surface of the coating film 15 but also to portions other than the coating film 15 can be suppressed.
(6) Since a particle having a small particle size and a small mass can be used as the projected particle 16, the projected particle 16 is unlikely to bite into the surface of the coating film 15 and is washed away by the slurry. Biting into the surface of the coating film 15 can be prevented. Accordingly, it is possible to prevent the surface of the coating film 15 from being rough and to obtain the coating film 15 having a good touch.
（７）塗膜１５の表面に油脂分が付着していても、その油脂分をスラリによって洗い流すことができるため、脱脂加工が不要になる。
（８）艶消し処理がウェットブラストであるため、静電気が生じることを回避でき、放電等の静電気対策が不要になる。
(7) Even if oils and fats adhere to the surface of the coating film 15, since the oils and fats can be washed away by slurry, degreasing is unnecessary.
(8) Since the matte treatment is wet blasting, it is possible to avoid the generation of static electricity and eliminate the need for countermeasures against static electricity such as electric discharge.
（９）艶消し処理がウェットブラストであるため、投射粒体１６が粒径の小さなものであっても、作業空間内に粉塵が舞い散ることを防止できる。従って、集塵機等の粉塵対策を施さなくても、良好な作業環境を得ることができる。 (9) Since the matte treatment is wet blasting, dust can be prevented from scattering in the work space even if the projected particles 16 have a small particle size. Therefore, a good working environment can be obtained without taking dust measures such as a dust collector.
（１０）塗膜１５の表面が艶消しされるため、部品表面の波打ち等の大きな凹凸を目立たなくできて、外観品質を向上できる。
（１１）スラリ中に防錆剤等の機能性材料を混入させることができる。
(10) Since the surface of the coating film 15 is matted, large irregularities such as undulations on the part surface can be made inconspicuous, and the appearance quality can be improved.
(11) Functional materials such as rust preventives can be mixed in the slurry.
なお、本発明は前記実施形態に限定されるものではなく、以下のような態様で具体化することも可能である。
・ブラスト液体として、水道水以外の液体、例えば蒸留水やオイルを用いること。
In addition, this invention is not limited to the said embodiment, It is also possible to embody in the following aspects.
-Use a liquid other than tap water, such as distilled water or oil, as the blast liquid.
・水滴や噴霧よりなるブラスト流に投射粒体１６を乗せて艶消し加工すること。
・部品や部位に応じて投射粒体１６の粒径を変更すること。このようにすれば、１つの水栓であっても、部分的に艶消し度合いを変化させることができる。
-Putting the projection particles 16 on a blast flow consisting of water droplets or spraying and matting.
-Change the particle size of the projection particle 16 according to parts and parts. In this way, even with a single faucet, the matte degree can be partially changed.
・投射粒体１６としてアルミナ以外のセラミック粒体、例えば窒化ケイ素を用いること。 -Ceramic particles other than alumina, such as silicon nitride, are used as the projection particles 16.
１１…水栓、１５…塗膜、１６…投射粒体。 11 ... Faucet, 15 ... Coating film, 16 ... Projection granule.
Claims (5)
前記塗膜にはウェットブラストによる艶消し処理が施されている水栓。 In a faucet with a coating on the surface,
A faucet in which the coating film has been matted by wet blasting.