JP2016168829A - Production method of plastic lens, positioning method of film, and composite - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a production method of a plastic lens, with which a film is simply positioned, generation of a defective product is suppressed, and a production cost is reduced.SOLUTION: In a production method of a plastic lens, a first curable composition 14 is placed on a formation face 12a of a first mold substrate 12 for the purpose of forming a lens surface, the first mold substrate 12 and a film 16 are separated from each other by pushing and expanding the first curable composition 14 on an entire surface of the formation face 12a by using the film 16 by a predetermined distance, outer edges of the first mold substrate 12, the film 16, and a second mold substrate 18 are covered with a fixing member 20, the second mold substrate 18 is arranged such that it is separated from the film 16 by a predetermined distance and is placed opposite thereto, a second curable composition is injected in a gap 22 between the film 16 and the second mold substrate 18, substrate layers 24, 26 are formed on both faces of the film 16 by curing the first curable composition layer 14b and the injected second curable composition, and the plastic lens is taken out by removing the fixing member 20, the first mold substrate 12, and the second mold substrate 18.SELECTED DRAWING: Figure 1

Description

  The present invention relates to a plastic lens manufacturing method, a film positioning method, and a composite. Especially, it is related with the manufacturing method of a plastic polarizing lens, the positioning method of a polarizing film, and a laminated composite.

  The polarizing lens can prevent transmission of reflected light. Therefore, it is used to protect eyes by blocking strong reflected light outdoors such as ski resorts and fishing, and to ensure safety by blocking reflected light from oncoming vehicles when driving a car.

  As a plastic polarizing lens, a polarizing lens having a sandwich structure including a plastic lens base on both sides of a polarizing film has been proposed. In the case of a plastic polarizing lens for correcting vision, a semi-finished polarizing lens in which a polarizing film is installed as close to the objective surface (convex surface on the front side) as possible is usually manufactured by a lens manufacturer. Subsequently, the eyepiece surface (recessed concave surface) of the semi-finished polarized lens is polished at a processing place or retail store called a lab to be processed into a polarized lens having a desired power. In the production of a semi-finished polarizing lens, it is extremely important to set a polarizing film without deviation in a position as close as possible to the objective surface of the lens. If the polarizing film is set at a position deeper than the objective surface of the lens, the spectacle lens becomes thick and the aesthetic appearance is impaired. If the polarizing film is set unevenly and the distance from the object plane varies, there will be many defects in which the polarizing film is exposed from the eyepiece surface during the back-side polishing process to process the lens with the desired power. Resulting in. For this reason, attempts have been conventionally made to arrange the polarizing film as accurately as possible in the vicinity of the objective surface of the lens.

  For example, Patent Document 1 or Patent Document 2 describes a method of positioning a polarizing film using a specific mold including a member for separating the polarizing film and the mold by a predetermined distance.

  Patent Document 3 or Patent Document 4 describes a method of positioning a polarizing film using a gasket member having a specific shape for separating the polarizing film and the mold by a predetermined distance.

  Patent Document 5 describes a method in which an outer edge portion of a polarizing film has a predetermined shape, the polarizing film is fixed in the mold by the shape, and the polarizing film is positioned.

  Patent Document 6 uses a polarizing film having a plurality of resin protrusions of substantially the same height at opposite positions on the front and back sides, and positions the polarizing film by bringing two mold substrates into contact with the resin protrusions from both sides of the polarizing film. How to do is described.

  Patent Document 7 describes a method in which a polarizing film is moved while adsorbing and holding with a suction pad in order to suppress curling of the polarizing film, then placed in a mold, and the polarizing film is positioned with a spacing ring. Yes.

Japanese Patent Laid-Open No. 2005-99687 JP 2007-168310 A JP 2008-93825 A JP 2009-45886 A JP 2008-281791 A JP 2009-3303 A JP 2009-103773 A

  However, the methods of the cited references 1 to 7 require a specific shape mold or a specific shape gasket, or the polarizing film needs to be processed into a predetermined shape, so that the manufacturing process is complicated. Furthermore, there was room for improvement in terms of reducing the manufacturing cost.

  Moreover, even if a polarizing film is set in the state from which the distance from an objective surface has dispersion | variation with the method of the cited references 1-7, it is very difficult to confirm the defect in the obtained semifinished polarizing lens. is there. If a defect cannot be confirmed in the semi-finished polarizing lens, a defect in which the polarizing film is exposed from the eyepiece surface when it is polished in a lab or a retail store will be found, which will damage the trust of customers. Even if the position of the polarizing film can be confirmed before shipping to the customer, in order to improve the yield and productivity of the product, the defect due to the position of the polarizing film must be confirmed before the semi-finished polarizing lens is obtained. It was hoped to check.

That is, the present invention is described below.
[1] placing a first curable composition on the formation surface of the first mold substrate having a formation surface for forming a lens surface;
The step of spreading the first curable composition over the entire surface of the forming surface with a film, and separating the first mold substrate and the film by a predetermined distance through the formed first curable composition layer. When,
The outer edge of the first mold substrate, the outer edge of the film, and the outer edge of the second mold substrate having a forming surface to form the other surface of the lens are fixed by covering them with a fixing member, and the film And disposing the second mold substrate so as to face each other at a predetermined distance;
Semi-curing the first curable composition layer;
Injecting a second curable composition into the gap between the film and the second mold substrate;
Curing the semi-cured first curable composition layer and the injected second curable composition to form a base layer on both surfaces of the film;
Removing the fixing member, the first mold substrate and the second mold substrate and taking out the plastic lens;
A method for manufacturing a plastic lens, comprising:
[2] The method for producing a plastic lens according to [1], wherein the semi-cured first curable composition has a storage elastic modulus at 20 ° C. of 0.01 Pa to 100,000 Pa.
[3] The method for producing a plastic lens according to [1], wherein the semi-cured first curable composition has a storage elastic modulus at 20 ° C. of 0.1 Pa to 1,000 Pa.
[4] The plastic lens according to [1], wherein the first curable composition is a (thio) urethane-based material, and the degree of polymerization of the semi-cured first curable composition is 30 to 70%. Manufacturing method.
[5] Before or after the step of placing the first curable composition on the formation surface of the first mold substrate,
The manufacturing method of the plastic lens in any one of [1]-[4] including the process of mounting the spacer for positioning the said film on this formation surface.
[6] The method of manufacturing a plastic lens according to [5], wherein the spacer has a ring shape and is placed along an outer peripheral edge on the formation surface of the first mold substrate.
[7] The method for manufacturing a plastic lens according to any one of [1] to [6], wherein the fixing member is a tape or a gasket.
[8] In the step of placing the first curable composition,
The method for producing a plastic lens according to any one of [1] to [7], wherein the viscosity of the first curable composition at 20 ° C. measured with a B-type viscometer is 1 to 500 mPa · s.
[9] The method for producing a plastic lens according to any one of [1] to [8], wherein the film is a shaped polarizing film.
[10] The method for producing a plastic lens according to [9], wherein the polarizing film is a polyvinyl alcohol film or a thermoplastic polyester film.
[11] A step of placing a curable composition on the formation surface of a mold substrate having a formation surface for forming a lens surface;
Spreading the curable composition over the entire surface of the forming surface with a film, and separating the mold substrate and the film by a predetermined distance through the formed curable composition layer;
Semi-curing the curable composition;
A method for positioning a film.
[12] The film positioning method according to [11], wherein the film is a shaped polarizing film.
[13] A mold substrate having a forming surface for forming a lens surface;
A semi-cured curable composition layer formed over the entire surface of the mold substrate; and
With film,
Is a composite layered in order.
[14] The composite according to [13], wherein the film is a shaped polarizing film.

  In the present invention, semi-curing means a state in which fluidity is lost in the process of polymerization of a liquid curable composition into a resin (about 1 g of the curable composition is placed on a glass plate and tilted to about 45 °. Is a state in which the curable composition does not move). In terms of numerical values, the storage elastic modulus at 20 ° C. is generally in the range of 0.01 Pa to 100,000 Pa. When the curable composition is a (thio) urethane-based material, the polymerization degree is generally in the range of 30 to 70%. The degree of polymerization is the result of analysis / measurement by differential thermal analysis of what percentage of heat generation has occurred with respect to the total amount of heat generated until polymerization is completed and generation of polymerization heat is completed.

  According to the method for producing a plastic lens of the present invention, the curable composition is pressed evenly with a film, spread over the entire formation surface of the mold substrate, and the mold substrate and the film are interposed through the curable composition. Can be separated from each other by a predetermined distance, the film can be reliably positioned by a simple method, the occurrence of defective products can be suppressed, and the manufacturing cost can be reduced.

  Furthermore, according to the film positioning method of the present invention, the distance between the polarizing film and the object plane side and its variation can be easily checked at the intermediate stage before obtaining the semi-finished lens. Yield and productivity can be improved, and defects that the polarizing film is exposed from the eyepiece surface in laboratories and retail stores can be drastically reduced.

  The plastic lens manufacturing method or film positioning method of the present invention is not limited to the case of passing through a semi-finished lens, but also in the case of directly manufacturing a lens with a desired power (finish lens), or manufacturing a non-degree lens for sunglasses. Also useful.

It is a schematic process sectional drawing which shows the manufacturing method of the plastic lens in 1st Embodiment. It is a general | schematic process sectional drawing which shows the manufacturing method of the plastic lens in 2nd Embodiment.

Hereinafter, embodiments of the present invention will be described with reference to the drawings. In all the drawings, the same reference numerals are given to the same components, and the description will be omitted as appropriate.
The positioning of the film shown in the present invention means setting the position of the film in the lens using the film.

[First Embodiment]
The manufacturing method of the plastic lens of this embodiment has the following processes.
Step a: A predetermined amount of the first curable composition 14 is placed on the formation surface 12a of the first mold substrate 12 having the formation surface 12a for forming the objective surface of the lens (FIG. 1A). .
Step b: The first curable composition 14 is spread over the entire surface 12a by the film 16, and the first mold substrate 12 and the film 16 are separated by a predetermined distance via the first curable composition layer 14a. (FIG. 1B).
Step c: fixing the outer edge of the first mold substrate 12, the outer edge of the film 16, and the outer edge of the second mold substrate 18 for forming the other surface of the lens with the fixing member 20, and fixing the film The second mold substrate 18 is disposed so as to face the space 16 at a predetermined distance (FIG. 1C).
Step d: The first curable composition 14a is semi-cured to form a semi-cured layer 14b (FIG. 1 (d)).
Step e: A second curable composition is injected into the gap 22 between the film 16 and the second mold substrate 18 (FIG. 1E).
Step f: The semi-cured layer 14b of the first curable composition and the injected second curable composition are cured to form the base material layers 24 and 26 on both surfaces of the film 16 (FIG. 1 (f )).
Step g: The fixing member 20, the first mold substrate 12 and the second mold substrate 18 are removed, and the plastic lens is taken out (FIG. 1 (g)).

(Process a)
First, a predetermined amount of the first curable composition 14 is placed on the formation surface 12a of the first mold substrate 12 having the formation surface 12a for forming the objective surface of the lens.
The first mold substrate 12 is generally made of glass.

  The formation surface 12a of the first mold substrate 12 is a concave surface having a predetermined curved surface shape. In the present embodiment, an example in which the forming surface 12a is a concave surface for forming the objective surface (convex surface) of the lens will be described. The forming surface 12a may be a convex surface for forming the objective surface (concave surface) of the lens.

  The first curable composition 14 is obtained by mixing a monomer and an additive such as a catalyst and, if necessary, degassing and filtering. In the present embodiment, the curable composition can also be referred to as a polymerizable composition.

  The monomers are not particularly limited as long as they can be cast polymerized, but (thio) urethane monomers, allyl monomers, episulfide monomers, (meth) acrylic monomers, urethane urea monomers, epoxy monomers Etc. You may mix and use these.

The (thio) urethane monomer is a mixture of an iso (thio) cyanate compound and an active hydrogen compound. Examples of the iso (thio) cyanate compound include hexamethylene diisocyanate, 2,2,4-trimethylhexane diisocyanate, and 2,4. , 4-trimethylhexamethylene diisocyanate, lysine diisocyanatomethyl ester, lysine triisocyanate, m-xylylene diisocyanate, α, α, α ', α'-tetramethylxylylene diisocyanate, bis (isocyanatomethyl) naphthalene, mesi Tylylene triisocyanate, bis (isocyanatomethyl) sulfide, bis (isocyanatoethyl) sulfide, bis (isocyanatomethyl) disulfide, bis (isocyanatoethyl) disulfide, bis (isocyanatome Thio) methane, bis (isocyanatoethyl thio) methane, bis (isocyanatoethyl) ethane, bis (isocyanatomethyl thio) aliphatic polyisocyanate compounds such as ethane;
Isophorone diisocyanate, bis (isocyanatomethyl) cyclohexane, dicyclohexylmethane-4,4′-diisocyanate, cyclohexane diisocyanate, methylcyclohexane diisocyanate, dicyclohexyldimethylmethane isocyanate, 2,5-bis (isocyanatomethyl) bicyclo- [2.2. 1] -heptane, 2,6-bis (isocyanatomethyl) bicyclo- [2.2.1] -heptane, 3,8-bis (isocyanatomethyl) tricyclodecane, 3,9-bis (isocyanatomethyl) ) Alicyclic polyisocyanate compounds such as tricyclodecane, 4,8-bis (isocyanatomethyl) tricyclodecane, 4,9-bis (isocyanatomethyl) tricyclodecane;
Aromatic polyisocyanate compounds such as 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 4,4′-diphenylmethane diisocyanate, diphenyl sulfide-4,4-diisocyanate;
2,5-diisocyanatothiophene, 2,5-bis (isocyanatomethyl) thiophene, 2,5-diisocyanatotetrahydrothiophene, 2,5-bis (isocyanatomethyl) tetrahydrothiophene, 3,4-bis ( Isocyanatomethyl) tetrahydrothiophene, 2,5-diisocyanato-1,4-dithiane, 2,5-bis (isocyanatomethyl) -1,4-dithiane, 4,5-diisocyanato-1,3-dithiolane, 4, Examples include heterocyclic polyisocyanate compounds such as 5-bis (isocyanatomethyl) -1,3-dithiolane.
Examples of the active hydrogen compound include a polyol compound and a polythiol compound. The polyol compound is one or more aliphatic or alicyclic alcohols, specifically, linear or branched aliphatic alcohols, alicyclic alcohols, these alcohols and ethylene oxide, propylene oxide, ε- Examples include alcohol to which caprolactone is added.

  Examples of linear or branched aliphatic alcohols include ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol, 1,3-propanediol, 2,2-dimethyl-1, 3-propanediol, 2,2-diethyl-1,3-propanediol, 1,2-butanediol, 1,3-butanediol, 1,4-butanediol, 3-methyl-1,3-butanediol, 1,2-pentanediol, 1,3-pentanediol, 1,5-pentanediol, 2,4-pentanediol, 2-methyl-2,4-pentanediol, 3-methyl-1,5-pentanediol, 1,6-hexanediol, 2,5-hexanediol, glycerol, diglyce Lumpur, polyglycerol, trimethylolpropane, pentaerythritol, di- (trimethylol propane), and the like.

  Examples of the alicyclic alcohol include 1,2-cyclopentanediol, 1,3-cyclopentanediol, 3-methyl-1,2-cyclopentanediol, 1,2-cyclohexanediol, and 1,3-cyclohexanediol. 1,4-cyclohexanediol, 4,4′-bicyclohexanol, 1,4-cyclohexanedimethanol and the like.

  A compound obtained by adding these alcohol and ethylene oxide, propylene oxide, or ε-caprolactone may be used. For example, ethylene oxide adduct of glycerol, ethylene oxide adduct of trimethylolpropane, ethylene oxide adduct of pentaerythritol, propylene oxide adduct of glycerol, propylene oxide adduct of trimethylolpropane, propylene oxide adduct of pentaerythritol, Examples include caprolactone-modified glycerol, caprolactone-modified trimethylolpropane, and caprolactone-modified pentaerythritol.

Examples of the polythiol compound include methanedithiol, 1,2-ethanedithiol, 1,2,3-propanetrithiol, 1,2-cyclohexanedithiol, bis (2-mercaptoethyl) ether, tetrakis (mercaptomethyl) methane, Diethylene glycol bis (2-mercaptoacetate), diethylene glycol bis (3-mercaptopropionate), ethylene glycol bis (2-mercaptoacetate), ethylene glycol bis (3-mercaptopropionate), trimethylolpropane tris (2-mercapto) Acetate), trimethylolpropane tris (3-mercaptopropionate), trimethylolethane tris (2-mercaptoacetate), trimethylolethane tris (3-mercaptopro Onate), pentaerythritol tetrakis (2-mercaptoacetate), pentaerythritol tetrakis (3-mercaptopropionate), bis (mercaptomethyl) sulfide, bis (mercaptomethyl) disulfide, bis (mercaptoethyl) sulfide, bis (mercaptoethyl) ) Disulfide, bis (mercaptopropyl) sulfide, bis (mercaptomethylthio) methane, bis (2-mercaptoethylthio) methane, bis (3-mercaptopropylthio) methane, 1,2-bis (mercaptomethylthio) ethane, 1, 2-bis (2-mercaptoethylthio) ethane, 1,2-bis (3-mercaptopropylthio) ethane, 1,2,3-tris (mercaptomethylthio) propane, 1,2,3-tris (2-merca Toethylthio) propane, 1,2,3-tris (3-mercaptopropylthio) propane, 4-mercaptomethyl-1,8-dimercapto-3,6-dithiaoctane, 5,7-dimercaptomethyl-1,11-dimercapto 3,6,9-trithiaundecane, 4,7-dimercaptomethyl-1,11-dimercapto-3,6,9-trithiaundecane, 4,8-dimercaptomethyl-1,11-dimercapto-3 , 6,9-trithiaundecane, tetrakis (mercaptomethylthiomethyl) methane, tetrakis (2-mercaptoethylthiomethyl) methane, tetrakis (3-mercaptopropylthiomethyl) methane, bis (2,3-dimercaptopropyl) sulfide 2,5-dimercaptomethyl-1,4-dithiane, 2,5-dimerca Puto-1,4-dithiane, 2,5-dimercaptomethyl-2,5-dimethyl-1,4-dithiane, and their esters of thioglycolic acid and mercaptopropionic acid, hydroxymethyl sulfide bis (2-mercaptoacetate) ), Hydroxymethyl sulfide bis (3-mercaptopropionate), hydroxyethyl sulfide bis (2-mercaptoacetate), hydroxyethyl sulfide bis (3-mercaptopropionate), hydroxymethyl disulfide bis (2-mercaptoacetate), Hydroxymethyl disulfide bis (3-mercaptopropionate), hydroxyethyl disulfide bis (2-mercaptoacetate), hydroxyethyl disulfide bis (3-mercaptopropionate), 2-mer Ptoethyl ether bis (2-mercaptoacetate), 2-mercaptoethyl ether bis (3-mercaptopropionate), thiodiglycolic acid bis (2-mercaptoethyl ester), thiodipropionic acid bis (2-mercaptoethyl ester) ), Dithiodiglycolic acid bis (2-mercaptoethyl ester), dithiodipropionic acid bis (2-mercaptoethyl ester), 1,1,3,3-tetrakis (mercaptomethylthio) propane, 1,1,2,2 -Aliphatic polythiol compounds such as tetrakis (mercaptomethylthio) ethane, 4,6-bis (mercaptomethylthio) -1,3-dithiane, tris (mercaptomethylthio) methane, tris (mercaptoethylthio) methane;
1,2-dimercaptobenzene, 1,3-dimercaptobenzene, 1,4-dimercaptobenzene, 1,2-bis (mercaptomethyl) benzene, 1,3-bis (mercaptomethyl) benzene, 1,4- Bis (mercaptomethyl) benzene, 1,2-bis (mercaptoethyl) benzene, 1,3-bis (mercaptoethyl) benzene, 1,4-bis (mercaptoethyl) benzene, 1,3,5-trimercaptobenzene, 1,3,5-tris (mercaptomethyl) benzene, 1,3,5-tris (mercaptomethyleneoxy) benzene, 1,3,5-tris (mercaptoethyleneoxy) benzene, 2,5-toluenedithiol, 3, Aromatic poly, such as 4-toluenedithiol, 1,5-naphthalenedithiol, 2,6-naphthalenedithiol Ol compound;
2-methylamino-4,6-dithiol-sym-triazine, 3,4-thiophenedithiol, bismuthiol, 4,6-bis (mercaptomethylthio) -1,3-dithiane, 2- (2,2-bis (mercapto) And heterocyclic polythiol compounds such as methylthio) ethyl) -1,3-dithietane.

  Examples of allyl monomers include allyl diglycol carbonate (diethylene glycol diallyl carbonate), neopentyl glycol diallyl carbonate, pentaerythritol allyl carbonate, diallyl phthalate, and the like.

Examples of episulfide monomers include bis (1,2-epithioethyl) sulfide, bis (1,2-epithioethyl) disulfide, bis (epithioethylthio) methane, bis (epithioethylthio) benzene, and bis [4- Epithioethylthio compounds such as (epithioethylthio) phenyl] sulfide, bis [4- (epithioethylthio) phenyl] methane;
Bis (2,3-epithiopropyl) sulfide, bis (2,3-epithiopropyl) disulfide, bis (2,3-epithiopropylthio) methane, 1,2-bis (2,3-epithiopropyl) Thio) ethane, 1,2-bis (2,3-epithiopropylthio) propane, 1,3-bis (2,3-epithiopropylthio) propane, 1,3-bis (2,3-epithio) Propylthio) -2-methylpropane, 1,4-bis (2,3-epithiopropylthio) butane, 1,4-bis (2,3-epithiopropylthio) -2-methylbutane, 1,3- Bis (2,3-epithiopropylthio) butane, 1,5-bis (2,3-epithiopropylthio) pentane, 1,5-bis (2,3-epithiopropylthio) -2-methylpentane 1,5-bis (2, -Epithiopropylthio) -3-thiapentane, 1,6-bis (2,3-epithiopropylthio) hexane, 1,6-bis (2,3-epithiopropylthio) -2-methylhexane, , 8-bis (2,3-epithiopropylthio) -3,6-dithiaoctane, 1,2,3-tris (2,3-epithiopropylthio) propane, 2,2-bis (2,3- Epithiopropylthio) -1,3-bis (2,3-epithiopropylthiomethyl) propane, 2,2-bis (2,3-epithiopropylthiomethyl) -1- (2,3-epithio Propylthio) butane, 1,5-bis (2,3-epithiopropylthio) -2- (2,3-epithiopropylthiomethyl) -3-thiapentane, 1,5-bis (2,3-epi Thiopropylthio) -2,4-bis ( , 3-epithiopropylthiomethyl) -3-thiapentane, 1- (2,3-epithiopropylthio) -2,2-bis (2,3-epithiopropylthiomethyl) -4-thiahexane, 1, 5,6-Tris (2,3-epithiopropylthio) -4- (2,3-epithiopropylthiomethyl) -3-thiahexane, 1,8-bis (2,3-epithiopropylthio)- 4- (2,3-epithiopropylthiomethyl) -3,6-dithiaoctane, 1,8-bis (2,3-epithiopropylthio) -4,5-bis (2,3-epithiopropylthio) Methyl) -3,6-dithiaoctane, 1,8-bis (2,3-epithiopropylthio) -4,4-bis (2,3-epithiopropylthiomethyl) -3,6-dithiaoctane, 1, 8-bis (2,3-epithiop Lopyrthio) -2,5-bis (2,3-epithiopropylthiomethyl) -3,6-dithiaoctane, 1,8-bis (2,3-epithiopropylthio) -2,4,5-tris ( 2,3-epithiopropylthiomethyl) -3,6-dithiaoctane, 1,1,1-tris [[2- (2,3-epithiopropylthio) ethyl] thiomethyl] -2- (2,3- Epithiopropylthio) ethane, 1,1,2,2-tetrakis [[2- (2,3-epithiopropylthio) ethyl] thiomethyl] ethane, 1,11-bis (2,3-epithiopropylthio) ) -4,8-bis (2,3-epithiopropylthiomethyl) -3,6,9-trithiaundecane, 1,11-bis (2,3-epithiopropylthio) -4,7-bis (2,3-epithiopropylthiomethyl) 3,6,9-trithiaundecane, 1,11-bis (2,3-epithiopropylthio) -5,7-bis (2,3-epithiopropylthiomethyl) -3,6,9-tri Chain aliphatic 2,3-epithiopropylthio compounds such as thiaundecane;
1,3-bis (2,3-epithiopropylthio) cyclohexane, 1,4-bis (2,3-epithiopropylthio) cyclohexane, 1,3-bis (2,3-epithiopropylthiomethyl) Cyclohexane, 1,4-bis (2,3-epithiopropylthiomethyl) cyclohexane, 2,5-bis (2,3-epithiopropylthiomethyl) -1,4-dithiane, 2,5-bis [[ 2- (2,3-epithiopropylthio) ethyl] thiomethyl] -1,4-dithiane, 2,5-bis (2,3-epithiopropylthiomethyl) -2,5-dimethyl-1,4- Cycloaliphatic 2,3-epithiopropylthio compounds such as dithiane;
1,2-bis (2,3-epithiopropylthio) benzene, 1,3-bis (2,3-epithiopropylthio) benzene, 1,4-bis (2,3-epithiopropylthio) benzene 1,2-bis (2,3-epithiopropylthiomethyl) benzene, 1,3-bis (2,3-epithiopropylthiomethyl) benzene, 1,4-bis (2,3-epithiopropyl) Thiomethyl) benzene, bis [4- (2,3-epithiopropylthio) phenyl] methane, 2,2-bis [4- (2,3-epithiopropylthio) phenyl] propane, bis [4- ( 2,3-epithiopropylthio) phenyl] sulfide, bis [4- (2,3-epithiopropylthio) phenyl] sulfone, 4,4′-bis (2,3-epithiopropylthio) biphenyl, etc. Aromatic 2 , 3-epithiopropylthio compound;
Bis (2,3-epithiopropyl) ether, bis (2,3-epithiopropyloxy) methane, 1,2-bis (2,3-epithiopropyloxy) ethane, 1,2-bis (2, 3-epithiopropyloxy) propane, 1,3-bis (2,3-epithiopropyloxy) propane, 1,3-bis (2,3-epithiopropyloxy) -2-methylpropane, 1,4 -Bis (2,3-epithiopropyloxy) butane, 1,4-bis (2,3-epithiopropyloxy) -2-methylbutane, 1,3-bis (2,3-epithiopropyloxy) butane 1,5-bis (2,3-epithiopropyloxy) pentane, 1,5-bis (2,3-epithiopropyloxy) -2-methylpentane, 1,5-bis (2,3-epi Thiopropyloxy) 3-thiapentane, 1,6-bis (2,3-epithiopropyloxy) hexane, 1,6-bis (2,3-epithiopropyloxy) -2-methylhexane, 1,8-bis (2, 3-epithiopropyloxy) -3,6-dithiaoctane, 1,2,3-tris (2,3-epithiopropyloxy) propane, 2,2-bis (2,3-epithiopropyloxy) -1 , 3-bis (2,3-epithiopropyloxymethyl) propane, 2,2-bis (2,3-epithiopropyloxymethyl) -1- (2,3-epithiopropyloxy) butane, 1, 5-bis (2,3-epithiopropyloxy) -2- (2,3-epithiopropyloxymethyl) -3-thiapentane, 1,5-bis (2,3-epithiopropyloxy) -2, 4-bis (2, -Epithiopropyloxymethyl) -3-thiapentane, 1- (2,3-epithiopropyloxy) -2,2-bis (2,3-epithiopropyloxymethyl) -4-thiahexane, 1,5, 6-Tris (2,3-epithiopropyloxy) -4- (2,3-epithiopropyloxymethyl) -3-thiahexane, 1,8-bis (2,3-epithiopropyloxy) -4- (2,3-epithiopropyloxymethyl) -3,6-dithiaoctane, 1,8-bis (2,3-epithiopropyloxy) -4,5-bis (2,3-epithiopropyloxymethyl) 3,6-dithiaoctane, 1,8-bis (2,3-epithiopropyloxy) -4,4-bis (2,3-epithiopropyloxymethyl) -3,6-dithiaoctane, 1,8- Screw( 2,3-epithiopropyloxy) -2,5-bis (2,3-epithiopropyloxymethyl) -3,6-dithiaoctane, 1,8-bis (2,3-epithiopropyloxy) -2 , 4,5-tris (2,3-epithiopropyloxymethyl) -3,6-dithiaoctane, 1,1,1-tris [[2- (2,3-epithiopropyloxy) ethyl] thiomethyl]- 2- (2,3-epithiopropyloxy) ethane, 1,1,2,2-tetrakis [[2- (2,3-epithiopropyloxy) ethyl] thiomethyl] ethane, 1,11-bis (2 , 3-epithiopropyloxy) -4,8-bis (2,3-epithiopropyloxymethyl) -3,6,9-trithiaundecane, 1,11-bis (2,3-epithiopropyloxy) ) -4,7-Bis 2,3-epithiopropyloxymethyl) -3,6,9-trithiaundecane, 1,11-bis (2,3-epithiopropyloxy) -5,7-bis (2,3-epithiopropyl) Chain aliphatic 2,3-epithiopropyloxy compounds such as oxymethyl) -3,6,9-trithiaundecane;
1,3-bis (2,3-epithiopropyloxy) cyclohexane, 1,4-bis (2,3-epithiopropyloxy) cyclohexane, 1,3-bis (2,3-epithiopropyloxymethyl) Cyclohexane, 1,4-bis (2,3-epithiopropyloxymethyl) cyclohexane, 2,5-bis (2,3-epithiopropyloxymethyl) -1,4-dithiane, 2,5-bis [[ 2- (2,3-epithiopropyloxy) ethyl] thiomethyl] -1,4-dithiane, 2,5-bis (2,3-epithiopropyloxymethyl) -2,5-dimethyl-1,4- A cycloaliphatic 2,3-epithiopropyloxy compound such as dithiane; and
1,2-bis (2,3-epithiopropyloxy) benzene, 1,3-bis (2,3-epithiopropyloxy) benzene, 1,4-bis (2,3-epithiopropyloxy) benzene 1,2-bis (2,3-epithiopropyloxymethyl) benzene, 1,3-bis (2,3-epithiopropyloxymethyl) benzene, 1,4-bis (2,3-epithiopropyl) Oxymethyl) benzene, bis [4- (2,3-epithiopropyloxy) phenyl] methane, 2,2-bis [4- (2,3-epithiopropyloxy) phenyl] propane, bis [4- ( 2,3-epithiopropyloxy) phenyl] sulfide, bis [4- (2,3-epithiopropyloxy) phenyl] sulfone, 4,4′-bis (2,3-epithiopropyloxy) bi And aromatic 2,3-epithiopropyloxy compounds such as phenyl.
Episulfide monomers are sometimes used together with active hydrogen compounds such as polythiols.

Examples of (meth) acrylic monomers include ethylene glycol di (meth) acrylate, propylene glycol di (meth) acrylate, butylene glycol di (meth) acrylate, neopentyl glycol di (meth) acrylate, hexylene glycol di (meth) ) Poly (meth) acrylates of alkane polyols such as acrylate, trimethylolpropane tri (meth) acrylate, pentaerythritol tetra (meth) acrylate,
Diethylene glycol di (meth) acrylate, triethylene glycol di (meth) acrylate, polyethylene glycol di (meth) acrylate, dipropylene glycol di (meth) acrylate, polypropylene glycol di (meth) acrylate, dibutylene glycol di (meth) acrylate, And polyoxyalkane polyol poly (meth) acrylates such as dipentaerythritol hexa (meth) acrylate.
The (meth) acrylic monomer may be used together with an active hydrogen compound such as polythiol or an allylic monomer.

  The urethane urea monomer is a mixture of an iso (thio) cyanate compound, an amine compound, and an active hydrogen compound. Examples of the iso (thio) cyanate compound and the active hydrogen compound include the aforementioned compounds, Ethylenediamine, diethylenetriamine, triethylenetriamine, tetraethylenepentamine, pentaethylenehexamine, piperazine, morpholine, substituted morpholine, piperidine, substituted piperidine, diethylenediamine, 2-amino-1-ethylpiperazine, 2,4-diamino-3,5 -Diethyltoluene, 2,6-diamino-3,5-diethyltoluene, diisopropyltoluenediamine, methylenedianiline, dimethylthiotoluenediamine, 4,4'-methylenebis (2-chloroaniline), 4,4 '-Methylenebis (2,6-dimethylaniline), 4,4'-methylenebis (2,6-diethylaniline), 4,4'-methylenebis (2-ethyl-6-methylaniline), 4,4'-methylenebis (2,6-diisopropylaniline), 4,4′-methylenebis (2-isopropyl-6-methylaniline), 4,4′-methylenebis (3-chloro-2,6-diethylaniline) and the like. .

Examples of the epoxy monomer include a phenolic epoxy compound obtained by a condensation reaction of a polyhydric phenol compound such as bisphenol A glycidyl ether and bisphenol F glycidyl ether and an epihalohydrin compound; hydrogenated bisphenol A glycidyl ether, hydrogenated bisphenol F glycidyl. Alcohol-based epoxy compounds obtained by condensation of polyhydric alcohol compounds such as ether and cyclohexanedimethanol with epihalohydrin compounds; 3,4-epoxycyclohexylmethyl-3 ′, 4′-epoxycyclohexanecarboxylate and 1,2-hexahydro Glycidyl ester epoxy compounds obtained by condensation of polyhalogen organic acid compounds such as diglycidyl phthalate and epihalohydrin compounds; primary and secondary compounds Amine based epoxy compound obtained by condensation of the emission compound with an epihalohydrin compound, and the like. In addition, aliphatic polyhydric epoxy compounds such as vinylcyclohexene diepoxide such as 4-vinyl-1-cyclohexane diepoxide can be used.
Epoxy monomers are sometimes used together with active hydrogen compounds such as polythiols and polyamines.

Examples of other monomers include polythietane compounds.
Further, a plurality of these monomers may be included.

As a catalyst, although the catalyst to be used differs depending on the monomer system, a known and publicly used catalyst can be used.
For example, in the case of (thio) urethane monomers, tin compounds such as dimethyltin dichloride, dibutyltin dichloride, dioctyltin dichloride, dibutyltin dilaurate, dibutyltin diacetate, amine compounds such as dicyclohexylmethylamine, dimethylcyclohexylamine, etc. Is preferred.
In the case of allylic monomers and (meth) acrylic monomers, benzoyl peroxide, dicumyl peroxide, lauroyl peroxide, di-t-butyl peroxyazelate, t-butyl peroxy-2-ethylhexanoate, t-butyl peroxylaurate, t-butyl peroxybenzoate, t-butyl peroxy-3,5,5-trimethylhexanoate, t-butyl peroxyacetate, diisopropyl peroxydicarbonate, bis (4-t -Butylcyclohexyl) peroxydicarbonate, organic peroxides such as t-butylperoxyisopropylcarbonate, azobisisobutyronitrile, 2,2'-azobis (2-cyclopropylpropionitrile), 2,2 ' -Azobis (4-methoxy-2,4-dimethyl) Ruvaleronitrile), 2,2′-azobis (2,4-dimethylvaleronitrile) and other azo compounds, benzophenone, 4,4-diethylaminobenzophenone, 1-hydroxycyclohexyl phenyl ketone, 2,2-dimethoxy-2-phenyl Acetophenone, isoamyl p-dimethylaminobenzoate, methyl 4-dimethylaminobenzoate, benzoin, benzoin ethyl ether, benzoin isobutyl ether, benzoin isopropyl ether, 2,2-diethoxyacetophenone, methyl o-benzoylbenzoate, 2-hydroxy Photopolymerization initiators such as 2-methyl-1-phenylpropan-1-one, 2,4,6-trimethylbenzoyldiphenylphosphine oxide, and bisacylphosphine oxide are used.
In the case of episulfide monomers, triethylamine, tri-n-butylamine, tri-n-hexylamine, N, N-diisopropylethylamine, triethylenediamine, triphenylamine, N, N-dimethylethanolamine, N, N-diethylethanol Amine, N, N-dibutylethanolamine, N, N-dimethylbenzylamine, diethylbenzylamine, N, N-dimethylcyclohexylamine, N, N-diethylcyclohexylamine, N-methyldicyclohexylamine, N-methylmorpholine, N -Isopropylmorpholine, pyridine, N, N-dimethylaniline, β-picoline, N, N'-dimethylpiperazine, N-methylpiperidine, 2,2'-bipyridyl, hexamethylenetetramine, 1,8-diazabicyclo Tertiary amines such as (5,4,0) -7-undecene, trimethylphosphine, triethylphosphine, tri-n-propylphosphine, triisopropylphosphine, tri-n-butylphosphine, triphenylphosphine, tribenzylphosphine, 1, Phosphines such as 2-bis (diphenylphosphino) ethane, 1,2-bis (dimethylphosphino) ethane, quaternary ammonium salts such as tetramethylammonium bromide, tetrabutylammonium chloride, tetrabutylammonium bromide, tetramethylphosphonium Quaternary phosphonium salts such as bromide, tetrabutylphosphonium chloride, tetrabutylphosphonium bromide, dimethyltin dichloride, dibutyltin dichloride, dibutyltin dilaurate, dibuty Lewis acids such as tin diacetate, tetrachlorotin, dibutyltin oxide, diacetoxytetrabutyldistanoxane, zinc chloride, acetylacetone zinc, aluminum chloride, aluminum fluoride, triphenylaluminum, tetrachlorotitanium, calcium acetate, 2, 2′-azobis (2-cyclopropylpropionitrile), 2,2′-azobis (4-methoxy-2,4-dimethylvaleronitrile), 2,2′-azobis (2,4-dimethylvaleronitrile), radical polymerization catalysts such as t-butylperoxy-2-ethylhexanoate, n-butyl-4,4′-bis (t-butylperoxy) valerate, t-butylperoxybenzoate, diphenyliodonium hexafluorophosphoric acid, Diphenyliodonium hexafluoroarsenate, diphenyliodonium Hexafluoroantimonate, triphenylsulfonium tetrafluoroborate, triphenylsulfonium hexafluorophosphate, cationic polymerization catalysts and mixtures thereof such as triphenylsulfonium hexafluoroarsenate and the like.
The amount of catalyst added is usually in the range of 1 ppm to 5%.

Examples of other additives include an internal mold release agent, an ultraviolet absorber, a dye, a light control pigment, and a specific wavelength cut pigment.
Examples of the internal mold release agent include acidic phosphate esters. Examples thereof include phosphoric acid monoesters and phosphoric acid diesters, which can be used alone or in combination of two or more. MR internal mold release agent from Mitsui Chemicals, ZeleCUN from STEPAN, JP series from Johoku Chemical Industry, Phosphanol series from Toho Chemical Industry, AP, DP series from Daihachi Chemical Industry, etc. An internal mold release agent for MR manufactured by Mitsui Chemicals, and ZelecUN manufactured by STEPAN are more preferable. The amount added is usually in the range of 0.001 to 3 parts by weight, preferably 0.01 to 0.5 parts by weight, per 100 parts by weight of the curable composition.

  The ultraviolet absorber is preferably a benzotriazole compound, a triazine compound, a benzophenone compound or a benzoate compound, more preferably a benzotriazole compound. The amount added is usually in the range of 0.01 to 5 parts by weight, preferably 0.05 to 2 parts by weight with respect to 100 parts by weight of the curable composition.

  The first curable composition 14 is a mixture of a monomer and an additive such as a catalyst, and is usually degassed under a reduced pressure of about 0.1 to 100 Torr for about 0.1 to 5 hours, usually 0.1 to 10 μm. It is used after filtering with a filter of the degree.

  The viscosity of the first curable composition at 20 ° C. measured with a B-type viscometer is usually in the range of 1 to 500 mPa · s, preferably in the range of 10 to 200 mPa · s. Within this range, the first curable composition 14 can be easily spread on the forming surface 12a, and the first mold substrate 12 and the film 16 can be easily separated uniformly.

  The amount for placing the first curable composition 14 is calculated from the area of the forming surface 12a, the desired separation distance between the first mold substrate 12 and the film 16, and the specific gravity of the first curable composition. . In addition, the diameter of the 1st mold board | substrate 12 is about 60-90 mm normally, and a separation distance is normally set to the range of 0.1-3.0 mm, Preferably it is 0.2-2.0 mm.

(Process b)
The first curable composition 14 is spread over the entire surface 12a with the film 16 to form the first curable composition layer 14a, and the first mold substrate is interposed through the first curable composition layer 14a. 12 and the film 16 are separated by a predetermined distance (FIG. 1B).

Examples of the film 16 include a polarizing film, a light control (photochromic) film, a colored film, a specific wavelength cut film, and the like, and a polarizing film is particularly preferable.
Examples of the polarizing film include a thermoplastic polyester film such as a polyvinyl alcohol film or polyethylene terephthalate. These polarizing films are uniaxially stretched, and the thickness is usually about 10 to 300 μm. The polarizing film may be used as a sheet laminated with a thermoplastic material such as polycarbonate, triacetyl cellulose, or polyamide.

  As the film 16, a film having a predetermined curved surface shape formed at a predetermined temperature is preferably used. Usually, it has the same curved surface shape as the forming surface 12a of the first mold substrate 12, but it may have a curved surface shape with a smaller radius of curvature than 12a. For the purpose of improving the adhesive strength with the base material layer, the film has primer coating treatment, chemical treatment (gas or chemical treatment), corona discharge treatment, plasma treatment, ultraviolet irradiation treatment, electron beam irradiation treatment, rough surface You may use it, after performing 1 type, or 2 or more types of pre-processing chosen from chemical conversion treatment, a flame treatment, etc. Among these pretreatments, one or more selected from primer coating treatment, chemical treatment such as alkali, corona discharge treatment, and plasma treatment are particularly preferable.

In order to spread the 1st curable composition 14 over the whole surface of the formation surface 12a, if the whole film 16 can be pressed from upper direction, it will not specifically limit. Usually, pressing by the weight of the film is sufficient, but pressing may be performed from above in a state of being attached to a pressing member having a curved surface similar to that of the film 16.
It is easily confirmed by visual observation that the first mold substrate 12 and the film 16 are separated from each other by a predetermined distance.

(Process c)
The outer edge of the first mold substrate 12, the outer edge of the film 16, and the outer edge of the second mold substrate 18 for forming the other surface of the lens are covered with a fixing member 20, so that these are fixed. The second mold substrate 18 is disposed so as to face each other at a distance (FIG. 1C).
The second mold substrate 18 is generally made of glass. It may be the same as or different from the first mold substrate 12.

  Examples of the fixing member 20 include a tape and a gasket. In the case of a tape, the tape is wound so as to cover the outer edge of the first mold substrate 12, the outer edge of the film 16, and the outer edge of the second mold substrate 18, and these are fixed.

  Tapes are usually polyethylene, polypropylene, polyethylene terephthalate, polyethylene isophthalate, polyethylene naphthalate, polyphenylene sulfide, polyester, polycarbonate, polyvinyl chloride, Teflon (registered trademark), polysiloxane resin, polyimide resin, cellulose, etc., and their A base substrate such as a mixed / copolymer is applied with a siloxane-based, (meth) acrylic-based, epoxy-based or rubber-based adhesive. For the purpose of reducing the water vapor permeability of the tape, for example, silicon oxide or the like is deposited to form a quartz film, etc., or an organic coating agent, an inorganic coating agent, or a mixture thereof is coated, Bonding another base material having a low water vapor permeability is also performed. The thickness of the tape is usually in the range of 10 to 200 μm from the viewpoint of operability, dimensional stability of the molded product, airtightness in the vicinity of the overlap portion boundary line, strength, and the like.

As the gasket, a molded product obtained by using a thermoplastic resin can be suitably used, and an olefin-based elastomer is used from the viewpoints of moldability, flexibility, heat resistance, monomer stability, price, and the like. Is preferred. Specific examples of the olefin elastomer include a polyethylene elastomer made of low density polyethylene, a polypropylene elastomer in which a rubber component is finely dispersed in a polypropylene homopolymer, an ethylene-vinyl acetate copolymer, and an ethylene-alkyl acrylate copolymer. Can be mentioned.
The gasket used in the present embodiment does not need to have a special shape as described in Patent Document 3 or Patent Document 4, and a normal-shaped gasket used for manufacturing a white lens that does not sandwich a film is used as it is. Can be used.
Thereby, a gap 22 surrounded by the film 16, the second mold substrate 18, and the fixing member 20 is formed.

(Process d)
The first curable composition 14 is semi-cured to form a semi-cured layer 14b (FIG. 1 (d)).
Thereby, the film 16 can be positioned. Semi-curing refers to curing to a state where the position of the film 16 does not move with heat or ultraviolet rays.

The storage elastic modulus at 20 ° C. of the semi-cured first curable composition is usually 0.01 Pa to 100,000 Pa from the viewpoint that the film does not move in the subsequent process and the performance such as the surface accuracy of the lens obtained. The range of 0.1 Pa to 1,000 Pa is particularly preferable.
In the case where the first curable composition is a (thio) urethane-based material, from the viewpoint described above, the semi-curing is usually selected in the range of a polymerization degree of 30 to 70%, particularly preferably in the range of 40 to 60%. The degree of polymerization is measured by performing differential thermal analysis to determine what percentage of heat generation has occurred relative to the total amount of heat generated until polymerization is completed and generation of polymerization heat is completed.

  A semi-cured first layer 12 formed over the entire surface of the first mold substrate 12 having the formation surface 12a for forming the objective surface of the lens and the formation surface 12a of the first mold substrate 12 by the steps a to d. A composite in which the 1-curable composition layer (semi-cured layer 14b) and the film 16 are laminated in order is obtained.

  In this composite, the first curable composition layer 14 a is semi-cured, and the film 16 is positioned with respect to the formation surface 12 a of the first mold substrate 12. Since the complex can be transported, the subsequent steps can be performed elsewhere.

  In addition, after the lens product is obtained, the position of the film is checked in advance by visually checking the separation distance between the forming surface 12a and the film 16 at the stage of the composite as an intermediate, and the eyepiece It is possible to know in advance whether or not a defect in which the film is exposed from the eyepiece surface will not occur in the final product whose surface has been polished. This dramatically improves the yield and productivity of lens products.

(Process e)
The second curable composition is injected into the gap 22 between the film 16 and the second mold substrate 18 by a predetermined means (not shown) (FIG. 1 (e)).
As the second curable composition, a monomer and an additive such as a catalyst are mixed and deaerated or filtered as necessary, and those exemplified for the first curable composition 14 can be used. The first curable composition 14 and the second curable composition may be the same or different.

(Process f)
The semi-cured layer 14b of the first curable composition and the injected second curable composition are cured to form the base material layers 24 and 26 on both surfaces of the film 16 (FIG. 1 (f)).
Curing is performed by heat or ultraviolet light. In the case of thermosetting, the temperature is generally gradually increased from low temperature to 80 to 150 ° C. over 6 to 50 hours.

(Process g)
After curing, the fixing member 20, the first mold substrate 12 and the second mold substrate 18 are removed to obtain a plastic lens in which the base material layer 24 and the base material layer 26 are laminated on both sides of the film 16 (FIG. 1 (g)). ).
The obtained lens is subjected to annealing treatment by heating the released lens for the purpose of relaxing distortion or the like, if necessary. The annealing temperature is usually in the range of 80 to 150 ° C, preferably in the range of 90 to 130 ° C. The annealing time is usually in the range of 0.5 to 10 hours, preferably in the range of 1 to 6 hours.

In the first embodiment, the outer edge of the first mold substrate 12, the outer edge of the film 16, and the outer edge of the second mold substrate 18 for forming the other surface of the lens are covered with the fixing member 20. A description will be given by an example in which the step c of fixing and disposing the second mold substrate 18 to face the film 16 at a predetermined distance is performed, and then the step d of semi-curing the first curable composition 14 is performed. However, step c may be performed after step d.
A plastic lens can be manufactured by the above process.

[Second Embodiment]
The manufacturing method of the plastic lens of this embodiment has the following processes.
Step a: A predetermined amount of the first curable composition 14 is placed on the formation surface 12a of the first mold substrate 12 having the formation surface 12a for forming the objective surface of the lens (FIG. 2A). .
Step b: The spacer 13 is placed on the formation surface 12a of the first mold substrate 12 having the formation surface 12a for forming the objective surface of the lens (FIG. 2B).
Step c: The first curable composition 14 is spread over the entire surface 12a with the film 16, and the first mold substrate 12 and the film 16 are separated by a predetermined distance via the first curable composition layer 14a. (FIG. 2C).
Step d: By covering the outer edge of the first mold substrate 12, the outer edge of the spacer 13, the outer edge of the film 16, and the outer edge of the second mold substrate 18 for forming the other surface of the lens with the fixing member 20. These are fixed, and the second mold substrate 18 is disposed so as to face the film 16 with a predetermined distance (FIG. 2D).
Step e: The first curable composition layer 14a is semi-cured (FIG. 2 (e)).
Step f: The second curable composition is injected into the gap 22 between the film 16 and the second mold substrate 18 (FIG. 2 (f)).
Step g: The semi-cured layer 14b of the first curable composition and the injected second curable composition are cured to form the base material layers 24 and 26 on both surfaces of the film 16 (FIG. 2 (g)). ).
Step h: The fixing member 20, the first mold substrate 12 and the second mold substrate 18 are removed, and the plastic lens is taken out (FIG. 2 (h)).
Process a, process c, process d, process e, process f, process g, and process h are the same as those in the first embodiment, and a description thereof is omitted.

(Process b)
On the forming surface 12a for forming the objective surface of the lens, a spacer 13 for placing the film 16 more accurately is placed (FIG. 2B).
By placing the spacer 13 along the outer peripheral edge of the forming surface 12a for forming the objective surface of the lens, the film 16 can be positioned more reliably.

The spacer 13 can take various forms as long as it can be placed along the outer peripheral edge of the forming surface 12a for forming the objective surface of the lens. A ring shape is preferably used, but may be a plurality of blocks.
The spacer 13 can be used as long as it has a predetermined height, can withstand the heat of polymerization curing, and does not adversely affect the lens. However, due to ease of molding, cost, etc., polyethylene (PE), polypropylene Plastics such as (PP), polyvinyl chloride (PVA), ethylene / vinyl acetate copolymer resin (EVA), polytetrafluoroethylene (PTFE) are preferably used.
When the spacer 13 is in close contact with the lens taken out in the step h, the sourer is removed in a polishing step or a lens shape processing (polishing processing to a shape matching the frame).

  In 2nd Embodiment, the process surface a which mounts the 1st curable composition 14 is implemented on the formation surface 12a of the 1st mold board | substrate 12, and the formation surface 12a for forming the objective surface of a lens is used after that. Although the example in which the step b of placing the spacer 13 on the formation surface 12a of the first mold substrate 12 is described has been described, the step a may be performed after the step b is performed.

  Similarly to the first embodiment, also in the second embodiment, the outer edge of the first mold substrate 12, the outer edge of the film 16, and the outer edge of the second mold substrate 18 for forming the other surface of the lens are fixed. These are fixed by covering with the member 20, and the step d of disposing the second mold substrate 18 so as to face the film 16 at a predetermined distance is performed, and then the first curable composition layer 14a is semi-cured. However, the process d may be performed after the process e is performed.

  The plastic lens obtained in the present embodiment is used with a coating layer on one side or both sides as required. Examples of the coating layer include a primer layer, a hard coat layer, an antireflection film layer, an antifogging coat layer, a stainproof layer, and a water repellent layer. These coating layers may be used singly or in a multilayered form. When a coating layer is applied to both sides, a similar coating layer or a different coating layer may be applied to each surface.

  Each of these coating layers contains an ultraviolet absorber for the purpose of protecting the lens and eyes from ultraviolet rays, an infrared absorber for the purpose of protecting the eyes from infrared rays, a light stabilizer and an antioxidant for the purpose of improving the weather resistance of the lens, Dyes and pigments for the purpose of enhancing the fashionability of the lens, photochromic dyes and photochromic pigments, antistatic agents, and other known additives may be used in combination for the purpose of enhancing the performance of the lens. Various leveling agents may be used for the purpose of improving coatability.

The primer layer is generally formed between the lens base material and the hard coat layer for the purpose of improving the adhesion of the hard coat layer and the impact resistance of the lens. It is about 1-10 micrometers.
The primer layer is formed by, for example, a coating method or a dry method. In the application method, a primer layer is formed by applying the primer composition by a known application method such as spin coating or dip coating, followed by solidification. In the dry method, it is formed by a known dry method such as a CVD method or a vacuum deposition method. When forming the primer layer, the surface of the lens may be subjected to pretreatment such as alkali treatment, plasma treatment, or ultraviolet treatment as necessary for the purpose of improving adhesion.

  The primer composition is preferably a material in which the solidified primer layer has high adhesion to the lens substrate, and usually a primer composition mainly composed of a urethane resin, an epoxy resin, a polyester resin, a melanin resin, or a polyvinyl acetal. Things are used. The primer composition can be used in the absence of a solvent, but an appropriate solvent that does not affect the lens may be used for the purpose of adjusting the viscosity of the composition.

The hard coat layer is a coating layer intended to give the lens surface functions such as scratch resistance, abrasion resistance, moisture resistance, warm water resistance, heat resistance, weather resistance, etc. It is about 0.3 to 30 μm.
The hard coat layer is usually formed by applying a hard coat composition by a known application method such as spin coating or dip coating, followed by curing. Examples of the curing method include thermal curing, a curing method by irradiation with energy rays such as ultraviolet rays and visible rays, and the like. When forming the hard coat layer, pretreatment such as alkali treatment, plasma treatment, and ultraviolet treatment may be performed on the coated surface (lens substrate or primer layer) as necessary for the purpose of improving adhesion. .

  As hard coat compositions, generally, there are curable organosilicon compounds and fine oxide particles such as Si, Al, Sn, Sb, Ta, Ce, La, Fe, Zn, W, Zr, In, and Ti. A mixture of (including complex oxide fine particles) is often used. In addition to these, amines, amino acids, metal acetylacetonate complexes, organic acid metal salts, perchloric acids, perchloric acid salts, acids, metal chlorides and polyfunctional epoxy compounds may also be used. Good. The hard coat composition can be used without a solvent, but an appropriate solvent that does not affect the lens may be used.

The antireflection layer is usually formed on the hard coat layer as necessary. The antireflection layer includes an inorganic type and an organic type. In the case of an inorganic type, generally, an inorganic oxide such as SiO ₂ or TiO ₂ is used for vacuum deposition, sputtering, ion plating, ion It is often formed by a dry method such as a beam assist method or a CVD method. In the case of an organic type, generally, it is often formed by a wet process using a composition containing an organosilicon compound and silica-based fine particles having internal cavities.

The antireflection layer may be a single layer or a multilayer, but when used as a single layer, the refractive index is preferably at least 0.1 lower than the refractive index of the hard coat layer. In order to effectively exhibit the antireflection function, it is preferable to use a multilayer antireflection film. In that case, a low refractive index film and a high refractive index film are usually laminated alternately. Also in this case, the refractive index difference between the low refractive index film and the high refractive index film is preferably 0.1 or more. Examples of the high refractive index film include ZnO, TiO ₂ , CeO ₂ , Sb ₂ O ₅ , SnO ₂ , ZrO ₂ , and Ta ₂ O ₅ , and examples of the low refractive index film include an SiO ₂ film. It is done. The film thickness is usually about 50 to 150 nm.

Furthermore, the plastic lens obtained in the present embodiment may be subjected to outer periphery polishing, back surface polishing, antistatic treatment, dyeing treatment, light control treatment, and the like, if necessary.
Such a plastic lens is useful as a polarizing lens for eyeglasses, particularly as a polarizing lens for correcting vision.

  As mentioned above, although embodiment of this invention was described, these are the illustrations of this invention, In the range which does not impair the effect of this invention, various structures other than the above are employable.

  EXAMPLES The present invention will be described in more detail below with reference to examples, but the present invention is not limited to these examples.

<Preparation of curable composition-1>
50.6 parts by weight of m-xylylene diisocyanate, 4,8-dimercaptomethyl-1,11-dimercapto-3,6,9-trithiaundecane and 4,7-dimercaptomethyl-1,11-dimercapto-3 , 6,9-trithiaundecane and 5,7-dimercaptomethyl-1,11-dimercapto-3,6,9-trithiaundecane 49.4 parts by weight, dibutyltin dichloride as a curing accelerator After stirring and dissolving 01 parts by weight, 0.15 parts by weight of Zelec UN (registered trademark, manufactured by Stepan) as a mold release agent, and 1.50 parts by weight of Seesorb 709 (manufactured by Sipro Kasei) as an ultraviolet absorber. Then, defoaming treatment was performed under reduced pressure to prepare curable composition-1. The viscosity at 20 ° C. was 30 mPa · s (measured 1 hour after stirring and dissolution).

<Preparation of curable composition-2>
50.6 parts by weight of bis (isocyanatomethyl) bicyclo- [2.2.1] -heptane (mixture of 2,5-isomer and 2,6-isomer), pentaerythritol tetrakis (3-mercaptopropionate) 23 .9 parts by weight, 25.5 parts by weight of 4-mercaptomethyl-1,8-dimercapto-3,6-dithiaoctane, 0.03 parts by weight of dibutyltin dichloride as a curing accelerator, Zelec UN (registered trademark, Stepan) 0.15 parts by weight, and Seesorb 709 (Cipro Kasei Co., Ltd.) 1.50 parts by weight as a UV absorber were mixed and dissolved, and then defoamed under reduced pressure to obtain curable composition-2. Got ready. The viscosity at 20 ° C. was 40 mPa · s (measured 1 hour after stirring and dissolution).

<Preparation of curable composition-3>
100.0 parts by weight of RAV 7AT (Acomon), 0.40 parts by weight of paroyl IPP-27 (CR) (NOF) as a curing accelerator, and 0.10 parts by weight of Siasorb UV24 (manufactured by Cytec) as an ultraviolet absorber After mixing and dissolving, defoaming treatment was performed under reduced pressure to prepare curable composition-3.

<Preparation of attached polarizing film-1>
A polyethylene terephthalate polarizing film (thickness: 140 microns) was preliminarily heat-treated at 140 ° C., and then formed into a curved shape of 6C (curve) at a forming temperature of 160 ° C. by a hot press method. After the polarizing film is cut according to the size of the mold, the front and back surfaces of the polarizing film are irradiated with plasma for 20 seconds each using a plasma irradiation surface modification device (PS-601SW type: manufactured by Wedge Co., Ltd.). After washing, it was air dried. Samprene IB-422 (a polyester polyurethane coating agent manufactured by Sanyo Chemical Industries) was coated on both sides of this polyethylene terephthalate polarizing film and dried at about 50 to 60 ° C. to obtain a shaped polarizing film-1.

<Preparation of attached polarizing film-2>
A polarizing film made of polyvinyl alcohol (thickness: 37 microns) was heated at a temperature of 100 ° C. for 0.5 hours using a hot-air circulating oven. The heated film body was made to absorb moisture and shaped into a curved shape of 6C (curve) using a glass mold. The polarizing film was cut according to the size of the mold and then dried under conditions of a temperature of 80 ° C. and a pressure of 30 torr to obtain a shaped polarizing film-2.

<Example-1>
A 3 μm Teflon filter is formed on the glass first mold substrate (outer diameter: 81.0 mm, forming surface curvature: 133.5 mm, center thickness: 4.0 mm) for forming the objective surface of the lens. 4.5 g of the curable composition-1 passed was placed, and then along the outer peripheral edge of the formation surface of the first mold substrate, a low density polyethylene ring spacer (outer diameter: 81.0 mm, inner diameter: 77.5 mm, height: 0.8 mm).
The placed curable composition-1 is spread over the entire surface of the first mold substrate with the shaped polarizing film-1, and then the outer edge of the first mold substrate, the outer edge of the spacer, and the polarizing film Covering the outer edge and the outer edge of the second glass mold substrate (outer diameter: 81.0 mm, forming surface curvature: 85.0 mm, center thickness: 5.0 mm) for forming the other surface of the lens These were fixed by winding with a tape “Sliontec 6263” manufactured by Hitachi Maxell.
In this state, the curable composition-1 was semi-cured by leaving it at 25 to 35 ° C. for 14 hours. The distance between the polarizing film and the first mold substrate during semi-curing was confirmed visually.
In order to grasp the storage elastic modulus of the curable composition-1 at the time of semi-curing, a separate simulated polymerization was performed, and the elastic modulus was measured with a rheometer, so that the curable composition-1 at the time of semi-curing was stored at 20 ° C. It was confirmed that the elastic modulus was 10 Pa. Further, about 1 g of the semi-cured curable composition was placed on a glass plate and tilted at 45 ° and allowed to stand for 1 minute, but the curable composition did not move. Furthermore, the differential thermal analysis performed separately confirmed that the degree of polymerization of the curable composition-1 at the time of semi-curing was 46%.
Subsequently, the newly prepared curable composition-1 was injected through a 3 μm Teflon filter so that the gap between the polarizing film and the second mold substrate was filled.
This lens casting mold is placed in a hot-air circulating oven, heated from 15 ° C. to 110 ° C. over 30 hours, then maintained at 110 ° C. for 3 hours, and after slow cooling, the lens casting mold from the oven Was taken out. The polarizing lens was released by removing the tape, the first mold substrate and the second mold substrate from the lens casting mold, and annealed at 110 ° C. for 2 hours to obtain a polarizing lens.
When the polarizing lens was cut and the position of the polarizing film was confirmed, both the outer peripheral portion and the center point were set at a depth of 0.8 mm from the object plane.

<Example-2>
A 3 μm Teflon filter is formed on the glass first mold substrate (outer diameter: 81.0 mm, forming surface curvature: 133.5 mm, center thickness: 4.0 mm) for forming the objective surface of the lens. Then, 3.0 g of the curable composition-2 passed therethrough was placed, and then a silicone ring spacer (outer diameter: 81.0 mm, inner diameter: 77. 5 mm, height: 0.5 mm) was placed.
The placed curable composition-2 is spread over the entire surface of the first mold substrate with the shaped polarizing film-2, and then the outer edge of the first mold substrate, the outer edge of the spacer, and the polarizing film Covering the outer edge and the outer edge of the second glass mold substrate (outer diameter: 81.0 mm, forming surface curvature: 85.0 mm, center thickness: 5.0 mm) for forming the other surface of the lens These were fixed by winding with a tape “Sliontec 6263” manufactured by Hitachi Maxell.
In this state, the curable composition-2 was semi-cured by leaving it at 30 to 40 ° C. for 17 hours. The distance between the polarizing film and the first mold substrate during semi-curing was confirmed visually. Further, about 1 g of a curable composition that was separately semi-cured under the same conditions was placed on a glass plate and left at 45 ° for 1 minute, but the curable composition did not move.
Subsequently, the newly prepared curable composition-2 was injected through a 3 μm Teflon filter so that the gap between the polarizing film and the second mold substrate was filled.
This lens casting mold is placed in a hot air circulation oven, heated from 15 ° C. to 120 ° C. over 17 hours, then maintained at 120 ° C. for 3 hours, and after slow cooling, the lens casting mold from the oven Was taken out. The polarizing lens was released by removing the tape, the first mold substrate and the second mold substrate from the lens casting mold, and annealed at 120 ° C. for 2 hours to obtain a polarizing lens.
When the polarizing lens was cut and the position of the polarizing film was confirmed, both the outer peripheral portion and the center point were set at a depth of 0.5 mm from the object plane.

<Example-3>
A 3 μm Teflon filter is formed on the glass first mold substrate (outer diameter: 81.0 mm, forming surface curvature: 75.7 mm, center thickness: 4.0 mm) for forming the objective surface of the lens. Then, 3.0 g of the curable composition-3 passed therethrough was placed, and then a silicone ring spacer (outer diameter: 81.0 mm, inner diameter: 77. 5 mm, height: 0.5 mm) was placed.
With the shaped polarizing film-2 treated with a silane coupling agent (manufactured by Shin-Etsu Chemical Co., Ltd., Shin-Etsu Silicone KBM-503), the placed curable composition-3 is pushed over the entire surface of the first mold substrate. Then, the second mold substrate for forming the outer edge of the first mold substrate, the outer edge of the spacer, the outer edge of the polarizing film, and the other surface of the lens (outer diameter: 81.0 mm, forming surface curvature: 88.5 mm, The outer edge of the center thickness: 4.0 mm) was fixed by winding with a tape “Sliontec 6263” manufactured by Hitachi Maxell.
In this state, the curable composition-3 was semi-cured by leaving it at 25 to 35 ° C. for 10 hours. The distance between the polarizing film and the first mold substrate during semi-curing was confirmed visually. Further, about 1 g of a curable composition that was separately semi-cured under the same conditions was placed on a glass plate and left at 45 ° for 1 minute, but the curable composition did not move.
Subsequently, the newly prepared curable composition-3 was injected through a 3 μm Teflon filter so that the gap between the polarizing film and the second mold substrate was filled.
This lens casting mold is placed in a hot-air circulating oven, heated from 25 ° C. to 80 ° C. over 18 hours, then maintained at 80 ° C. for 2 hours, and after slow cooling, the lens casting mold from the oven Was taken out. The polarizing lens was released by removing the tape, the first mold substrate and the second mold substrate from the lens casting mold, and annealed at 90 ° C. for 5 hours to obtain a polarizing lens.
When the polarizing lens was cut and the position of the polarizing film was confirmed, both the outer peripheral portion and the center point were set at a depth of 0.5 mm from the object plane.

12 First mold substrate 12a Forming surface 13 Spacer 14 First curable composition 14a First curable composition layer 14b Semi-cured layer 16 Film 18 Second mold substrate 20 Fixing member 22 Gap 24, 26 Base material layer

Claims (14)

Placing the first curable composition on the formation surface of the first mold substrate having a formation surface for forming a lens surface;
The step of spreading the first curable composition over the entire surface of the forming surface with a film, and separating the first mold substrate and the film by a predetermined distance through the formed first curable composition layer. When,
The outer edge of the first mold substrate, the outer edge of the film, and the outer edge of the second mold substrate having a forming surface to form the other surface of the lens are fixed by covering them with a fixing member, and the film And disposing the second mold substrate so as to face each other at a predetermined distance;
Semi-curing the first curable composition layer;
Injecting a second curable composition into the gap between the film and the second mold substrate;
Curing the semi-cured first curable composition layer and the injected second curable composition to form a base layer on both surfaces of the film;
Removing the fixing member, the first mold substrate and the second mold substrate and taking out the plastic lens;
A method for manufacturing a plastic lens, comprising:   2. The method for producing a plastic lens according to claim 1, wherein the semi-cured first curable composition has a storage elastic modulus at 20 ° C. of 0.01 Pa to 100,000 Pa. 3.   The method for producing a plastic lens according to claim 1, wherein a storage elastic modulus at 20 ° C of the semi-cured first curable composition is 0.1 Pa to 1,000 Pa.   The method for producing a plastic lens according to claim 1, wherein the first curable composition is a (thio) urethane-based material, and the degree of polymerization of the semi-cured first curable composition is 30 to 70%. . Before or after the step of placing the first curable composition on the formation surface of the first mold substrate,
The manufacturing method of the plastic lens in any one of Claims 1-4 including the process of mounting the spacer for positioning the said film on this formation surface.   The method of manufacturing a plastic lens according to claim 5, wherein the spacer has a ring shape and is placed along an outer peripheral edge on the formation surface of the first mold substrate.   The method for manufacturing a plastic lens according to claim 1, wherein the fixing member is a tape or a gasket. In the step of placing the first curable composition,
The method for producing a plastic lens according to claim 1, wherein the viscosity of the first curable composition at 20 ° C. measured with a B-type viscometer is 1 to 500 mPa · s.   The method for producing a plastic lens according to claim 1, wherein the film is an attached polarizing film.   The method for producing a plastic lens according to claim 9, wherein the polarizing film is a polyvinyl alcohol film or a thermoplastic polyester film. Placing a curable composition on the forming surface of a mold substrate having a forming surface for forming a lens surface;
Spreading the curable composition over the entire surface of the forming surface with a film, and separating the mold substrate and the film by a predetermined distance through the formed curable composition layer;
Semi-curing the curable composition;
A method for positioning a film.   The film positioning method according to claim 11, wherein the film is an attached polarizing film. A mold substrate having a forming surface for forming a lens surface;
A semi-cured curable composition layer formed over the entire surface of the mold substrate; and
With film,
Is a composite layered in order.   The composite according to claim 13, wherein the film is a shaped polarizing film.