JP2014037109A - Laminated polyester film - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a polyester film as a film in which excellent transparency, sliding property and adhesiveness to various kinds of surface functional layers are demanded, and which can be suitably used, for example, for a member such as a prism and a microlens used in a backlight unit of a liquid crystal display or the like.SOLUTION: A laminated polyester film is provided, which includes: a coating layer formed by applying a coating liquid containing particles having no heat resistance on at least one surface of an unstretched polyester film and then stretching the film in at least a single direction; and a coating layer formed from a coating liquid containing a urethane resin on the above coating layer or on an opposite surface side to the above coating layer.

Description

  The present invention relates to a laminated polyester film, in particular, a laminate having excellent transparency and good adhesion to a surface functional layer such as a prism layer or a microlens layer used in a backlight unit of a liquid crystal display. It relates to a polyester film.

  Since polyester film has excellent transparency, strength, etc., it is used as a base material for prism lens film, microlens film, light diffusion film, antireflection film, hard coat film, electromagnetic wave shield film, touch panel, molding, etc. It has been. In recent years, more excellent transparency is being demanded particularly for films used for forming a surface functional layer, such as a member such as a backlight unit of a liquid crystal display, an in-mold transfer film, and an in-mold label film.

  Conventionally, a technique of incorporating particles into a polyester film for the purpose of easy slipping has been common (Patent Documents 1 and 2). However, in the case of the method of incorporating particles in the polyester film, the haze of the film becomes high and becomes whitish, or when observed under a fluorescent lamp, graininess due to the particles is seen and visibility is deteriorated. In some cases, the luminance may decrease due to light scattering by the particles.

  In order to solve these problems, a film that does not contain particles in a polyester film has also been proposed (Patent Document 3). However, in the case of a film containing no particles, there is a drawback that the slipperiness is poor and the film is easily damaged. A proposal has been made to form a coating layer containing particles on a uniaxially stretched polyester film to impart slipperiness. However, before the coating layer is formed, the slipperiness cannot be improved, and it is applied from film formation by melt extrusion. In the meantime, the slipperiness is poor and scratches are inevitable.

  In order to impart higher performance, various surface functional layers are usually formed on the polyester film. In recent years, liquid crystal displays have been widely used as display devices for televisions, personal computers, digital cameras, mobile phones and the like. Since these liquid crystal displays do not have a light emitting function by a liquid crystal display unit alone, a method of displaying by irradiating light using a backlight from the back side is widespread.

  A prism sheet is used to improve the optical efficiency of the backlight and increase the brightness. As the transparent base film, a polyester film is generally used in consideration of transparency and mechanical properties. In order to improve the adhesion between the base polyester film and the prism layer, these intermediate layers are easily bonded. In general, a conductive coating layer is provided. As an easily adhesive coating layer, for example, polyester resins, acrylic resins, and urethane resins are known (Patent Documents 4 to 6).

  As a method for forming the prism layer, for example, an active energy ray-curable coating material is introduced into a prism type, irradiated with active energy rays while being sandwiched between polyester films, the resin is cured, and the prism type is removed to remove polyester. The method of forming on a film is mentioned. In the case of such a method, it is necessary to use a solventless active energy ray-curable coating material in order to form the prism type with precision. However, solvent-free paints are less likely to penetrate and swell into easily-adhesive coating layers laminated on polyester films and have insufficient adhesion compared to solvent-based paints.

JP 2006-169467 A JP 2006-77148 A JP 2000-229355 A JP-A-8-281890 Japanese Patent Laid-Open No. 11-286092 JP 2000-229395 A

  The present invention has been made in view of the above circumstances, and the problem to be solved is excellent transparency and slipperiness, and good adhesion to various surface functional layers such as a prism layer and a microlens layer. Is to provide a suitable polyester film.

  As a result of intensive studies in view of the above circumstances, the present inventors have found that the use of a polyester film having a specific configuration can easily solve the above-described problems, and have completed the present invention.

  That is, the gist of the present invention is to have a coating layer formed on at least one side of an unstretched polyester film by stretching a coating solution containing non-heat-resistant particles and then stretching in at least one direction. Or it exists in the laminated polyester film characterized by having the coating layer formed from the coating liquid containing a urethane resin in the surface opposite to the said coating layer.

  According to the polyester film of the present invention, it is possible to provide a film having excellent transparency and slipperiness, and excellent adhesion to various surface functional layers such as a prism layer and a microlens layer, and its industrial value is high.

  The polyester film constituting the polyester film in the present invention may have a single layer structure or a multilayer structure, and may have four or more layers as long as the gist of the present invention is not exceeded other than the two-layer or three-layer structure. It may be a multilayer and is not particularly limited. For example, it is possible to change the raw material of the surface layer and the intermediate layer into a three-layer structure for the purpose of effectively improving various properties using a polyester film with high functionality as the surface layer raw material.

  The polyester used in the present invention may be a homopolyester or a copolyester. In the case of a homopolyester, those obtained by polycondensation of an aromatic dicarboxylic acid and an aliphatic glycol are preferred. Examples of the aromatic dicarboxylic acid include terephthalic acid and 2,6-naphthalenedicarboxylic acid, and examples of the aliphatic glycol include ethylene glycol, diethylene glycol, and 1,4-cyclohexanedimethanol. Typical polyester includes polyethylene terephthalate and the like. On the other hand, the dicarboxylic acid component of the copolyester includes isophthalic acid, phthalic acid, terephthalic acid, 2,6-naphthalenedicarboxylic acid, adipic acid, sebacic acid, oxycarboxylic acid (for example, p-oxybenzoic acid, etc.), etc. 1 type or 2 types or more are mentioned, As a glycol component, 1 type or 2 types or more, such as ethylene glycol, diethylene glycol, propylene glycol, butanediol, 4-cyclohexane dimethanol, neopentyl glycol, is mentioned.

There is no restriction | limiting in particular as a polymerization catalyst of polyester, A conventionally well-known compound can be used, For example, an antimony compound, a titanium compound, a germanium compound, a manganese compound, an aluminum compound, a magnesium compound, a calcium compound etc. are mentioned. Among these, titanium compounds and germanium compounds are preferable because they have high catalytic activity, can be polymerized in a small amount, and the amount of metal remaining in the film is small, so that the brightness of the film becomes high. Furthermore, since a germanium compound is expensive, it is more preferable to use a titanium compound.

  In the polyester layer of the film of the present invention, particles can be blended mainly for the purpose of imparting slidability and preventing scratches in each step, but from the viewpoint of transparency, particles are not blended. It is preferable that When the particles are blended, the kind of the particles to be blended is not particularly limited as long as it is a particle capable of imparting slipperiness, and specific examples thereof include, for example, silica, calcium carbonate, magnesium carbonate, barium carbonate, sulfuric acid. Examples thereof include inorganic particles such as calcium, calcium phosphate, magnesium phosphate, kaolin, aluminum oxide, and titanium oxide, and organic particles such as acrylic resin, styrene resin, urea resin, phenol resin, epoxy resin, and benzoguanamine resin. Furthermore, precipitated particles obtained by precipitating and finely dispersing a part of a metal compound such as a catalyst during the polyester production process can also be used.

  Moreover, when mix | blending particle | grains, the average particle diameter of particle | grains is 3 micrometers or less normally, Preferably it is the range of 0.01-1.5 micrometers. When the average particle diameter exceeds 3 μm, the film brightness decreases when the transparency of the film deteriorates, when the graininess due to the particles occurs and the visibility deteriorates, or when light scattering by the particles occurs. There is a case.

  The content of the particles depends on the average particle size, but in the polyester film layer containing the particles, it is usually in the range of 1000 ppm or less, preferably in the range of 500 ppm or less, more preferably in the range of 50 ppm or less (intentionally contained). Do not). If it exceeds 1000 ppm, the transparency may deteriorate, the graininess caused by particles may occur and the visibility may deteriorate, or the brightness of the film may decrease due to light scattering by the particles.

The shape of the particles to be used is not particularly limited, and any of a spherical shape, a block shape, a rod shape, a flat shape, and the like may be used. Moreover, there is no restriction | limiting in particular about the hardness, specific gravity, a color, etc.
These series of particles may be used in combination of two or more as required.

  The method for adding particles to the polyester layer is not particularly limited, and a conventionally known method can be adopted. For example, it can be added at any stage for producing the polyester constituting each layer, but it is preferably added after completion of esterification or transesterification.

  The polyester film of the present invention may contain an ultraviolet absorber in order to improve the weather resistance of the film, for example, to prevent deterioration of the liquid crystal or the like of a liquid crystal display used for a touch panel or the like. The ultraviolet absorber is not particularly limited as long as it is a compound that absorbs ultraviolet rays and can withstand the heat applied in the production process of the polyester film.

  As the ultraviolet absorber, there are an organic ultraviolet absorber and an inorganic ultraviolet absorber. From the viewpoint of transparency, an organic ultraviolet absorber is preferable. Although it does not specifically limit as an organic type ultraviolet absorber, For example, a cyclic imino ester type, a benzotriazole type, a benzophenone type etc. are mentioned. From the viewpoint of durability, a cyclic imino ester type and a benzotriazole type are more preferable. It is also possible to use two or more ultraviolet absorbers in combination.

  In the polyester film of the present invention, conventionally known antioxidants, antistatic agents, thermal stabilizers, lubricants, dyes, pigments, etc. may be added to the polyester film in the present invention as necessary in addition to the above-mentioned particles and ultraviolet absorbers. Can do.

  Although the thickness of the polyester film in this invention will not be specifically limited if it can be formed into a film as a film, Usually, 10-300 micrometers, Preferably it is the range of 25-250 micrometers.

Next, although the manufacture example of the polyester film in this invention is demonstrated concretely, it is not limited to the following manufacture examples at all. That is, a method of drying the polyester raw material pellets described above and cooling and solidifying the molten film extruded from the die with a cooling roll using a single screw extruder is preferable. In this case, in order to improve the flatness of the film, it is preferable to improve the adhesion between the film and the rotary cooling drum, and an electrostatic application adhesion method or a liquid application adhesion method is preferably employed. Next, the obtained unstretched film is stretched in the biaxial direction. In that case, first, a coating solution containing non-heat-resistant particles is applied to the unstretched film and dried to form a coating layer. Thereafter, the film is stretched in one direction by a roll or tenter type stretching machine. The stretching temperature is usually 70 to 120 ° C., preferably 80 to 110 ° C., and the stretching ratio is usually 2.5 to 7 times, preferably 3.0 to 6 times. Next, the film is stretched in the direction perpendicular to the first stretching direction. In that case, the stretching temperature is usually 70 to 170 ° C., and the stretching ratio is usually 3.0 to 7 times, preferably 3.5 to 6 times. is there. Subsequently, heat treatment is performed at a temperature of 180 to 270 ° C. under tension or under relaxation within 30% to obtain a biaxially oriented film.
In the above-described stretching, a method in which stretching in one direction is performed in two or more stages can be employed.
In that case, it is preferable to carry out so that the draw ratios in the two directions finally fall within the above ranges.

  In the present invention, the simultaneous biaxial stretching method can be adopted for the production of the polyester film constituting the polyester film. In the simultaneous biaxial stretching method, a coating solution containing non-heat-resistant particles is applied to the unstretched film, and the machine direction and the width direction are usually controlled at 70 to 120 ° C., preferably 80 to 110 ° C. The stretching ratio is 4 to 50 times, preferably 7 to 35 times, and more preferably 10 to 25 times. Subsequently, heat treatment is performed at a temperature of 170 to 270 ° C. under tension or relaxation within 30% to obtain a stretched oriented film. With respect to the simultaneous biaxial stretching apparatus that employs the above-described stretching method, a conventionally known stretching method such as a screw method, a pantograph method, or a linear driving method can be employed.

  In the present invention, a coating layer (hereinafter sometimes abbreviated as a first coating layer) is formed from a coating solution containing non-heat-resistant particles on at least one surface of an unstretched polyester film, and then at least in one direction. After stretching, a coating layer formed from a coating solution containing a urethane resin (hereinafter sometimes abbreviated as a second coating layer) is formed on the coating layer and / or on the side opposite to the coating layer. Is an essential requirement.

  The present inventors include particles in a polyester film, and as a method for ensuring transparency and slipperiness, a change in the average particle diameter of the particles, a change in the addition amount of the particles, a layer of the polyester film containing the particles ( In the three-layer structure, only the outermost layer contains particles, and while improving the transparency, the method of changing the thickness of the slippery) has been studied, but both ensure high transparency and sufficient slipperiness. It was a difficult result.

  The first coating layer (non-heat-resistant particles) of the present invention is formed at the initial stage of the film production process, so that the first coating layer is formed on the unstretched film formed after melt extrusion and before the high temperature treatment. In these various processes, it is used to ensure sufficient slipperiness.

  In addition, usually when particles are present, they appear whitish due to light scattering, but when non-heat-resistant particles are used, they can be melted at a high temperature to reduce the particle size, deform, or be eliminated in a later step. In addition, they found that it was possible to reduce whitishness and realized high transparency.

  The formation of the first coating layer in the film of the present invention can be carried out at any stage from after the unstretched film formed after melt extrusion to before high temperature treatment. In particular, in order to prevent damage due to the roll, it is preferable to carry out at an initial stage. Moreover, in the method of extending | stretching by making it contact with films, such as a roll, since the damage to a film becomes large, forming in the step before extending | stretching is preferable.

  Furthermore, in order to increase transparency, it is necessary to treat at a temperature higher than the heat-resistant temperature (temperature at which heat is deformed) in order to reduce, deform, or eliminate the particle size by melting the non-heat-resistant particles in the subsequent process. Is preferable.

  The first coating layer in the film of the present invention is not limited to the following, for example, in sequential biaxial stretching, after the unstretched film is formed, the first coating layer is formed at an initial stage, and then A more suitable polyester film can be produced by performing the first stretching and then performing the high temperature treatment after the second stretching.

  The first coating layer in the film of the present invention may be formed on only one side of the film or may be formed on both sides in order to overcome, for example, a more easily damaged part. Moreover, in the case of both surfaces, the formation location may be the same or different.

  The non-heat resistant particles used in the present invention are particles having low heat resistance, and the particles are deformed at a high temperature. In particular, in the production process of the polyester film, the particles are deformed or dissolved in a process where the temperature after film formation is high. However, for example, when selecting a method of stretching in contact with a film such as a roll in the first stretching, it is necessary to maintain a sufficient shape as particles in order to exhibit slipperiness in the stretching process. Some heat resistance is necessary.

  That is, the thermal characteristics required for the non-heat resistant particles are preferably those that do not undergo thermal deformation at a temperature of less than 120 ° C. and that undergo thermal deformation at a temperature of 120 ° C. or higher.

  The softening point of the non-heat resistant particles is preferably in the range of 120 to 270 ° C, more preferably in the range of 150 to 250 ° C, and still more preferably in the range of 180 to 230 ° C. When the temperature is lower than 120 ° C., when a method of stretching by contacting with a film such as a roll in the first stretching is selected, depending on the stretching temperature, thermal deformation of the particles may occur, and the slipping property is deteriorated. There are concerns. On the other hand, if the temperature exceeds 270 ° C., the final product may be a film in which the particles are not thermally deformed and remain whitish.

  The non-heat resistant particle is not particularly limited as long as it can maintain the above-mentioned thermal characteristics, but in general, the organic particles, i.e. Heat-resistant organic particles are preferred. In consideration of control of the size and shape of the particles and dispersibility in various solvents including water, the organic particles are more preferably of a high molecular type, that is, non-heat resistant polymer particles.

  As the non-heat-resistant polymer particles, cross-linked or non-cross-linked polymer particles can be used as long as the gist of the present invention is not impaired, but in order to make the thermal characteristics more suitable for the purpose of the present invention. More preferably, it is a non-crosslinked type, that is, a non-heat resistant non-crosslinked polymer particle.

  The non-crosslinking in the non-heat-resistant non-crosslinked polymer particles is a polymer particle that does not have a three-dimensional structure or has few heat resistance and does not have high heat resistance. For example, in the case of particles made of a polymerizable monomer as described later, the crosslinkable polymerizable monomer is preferably less than 5% by weight of the entire polymerizable monomer, and more preferably in the range of less than 1% by weight.

  As the polymer of the non-heat-resistant non-crosslinked polymer particles, conventionally known compounds can be used. For example, acrylic resin, styrene resin, vinyl resin, epoxy resin, urea resin, phenol resin, polyester resin, polyurethane resin , Polycarbonate resin, polyether resin and the like. Among these polymers, an acrylic resin, a styrene resin, and a vinyl resin formed from a polymerizable monomer having a carbon-carbon double bond are more preferable from the viewpoint that a compound having a desired thermal characteristic can be easily produced. In addition, in the case of these resins, since they are thermally deformed by high-temperature treatment, it is possible to prevent the particles from falling off. Furthermore, not only the function as particles, but also, for example, adhesion to various surface functional layers formed thereon It is also possible to develop other performances such as increasing.

  The polymerizable monomer having a carbon-carbon double bond refers to various carboxyl group-containing monomers such as acrylic acid, methacrylic acid, crotonic acid, itaconic acid, fumaric acid, maleic acid, citraconic acid, and salts thereof; 2 -Various hydroxyl group-containing monomers such as hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, monobutylhydroxyfumarate, monobutylhydroxyitaconate; Various (meth) acrylates such as (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, butyl (meth) acrylate, lauryl (meth) acrylate; (meth) acrylamide, diacetone acrylamide, N -Methylol Various nitrogen-containing compounds such as chloramide or (meth) acrylonitrile; various styrene derivatives such as styrene, α-methylstyrene, divinylbenzene, vinyltoluene, various vinyl esters such as vinyl propionate; γ-methacrylic Various silicon-containing polymerizable monomers such as loxypropyltrimethoxysilane, vinyltrimethoxysilane, etc .; phosphorus-containing vinyl monomers; various vinyl halides such as vinyl fluoride, vinyl chloride, and biridene chloride; butadiene And various conjugated dienes.

  Among these, an acrylic resin obtained by polymerizing a (meth) acrylic polymerizable monomer as a main component is optimal. Also, a styrene / acrylic resin having a (meth) acrylic polymerizable monomer as a main component and copolymerized with a styrene derivative can be suitably used.

  That is, in the film of the present invention, the best form of the non-heat-resistant particles used for forming the first coating layer is the non-heat-resistant non-crosslinked acrylic resin particles and the non-heat-resistant non-crosslinked styrene / acrylic resin particles as described above. It is.

  When non-heat resistant non-crosslinked acrylic resin particles are used, the glass transition point of the resin particles is preferably in the range of 0 to 150 ° C, more preferably in the range of 50 to 120 ° C. When the temperature is lower than 0 ° C, there is a concern that the slipperiness cannot be sufficiently exhibited. When the temperature exceeds 150 ° C, there is a concern that the thermal deformation of the particles is not sufficient.

  The average particle diameter of the non-heat-resistant particles depends on the film thickness and cannot be generally specified, but is preferably in the range of 0.01 to 3 μm, more preferably in the range of 0.03 to 1 μm, and still more preferably 0.00. It is the range of 05-0.5 micrometer. When the average particle size is less than 0.01 μm, the slipperiness may not be sufficiently obtained. When the average particle size exceeds 3 μm, the particles are not sufficiently deformed and a whitish film remains. May end up.

  In the formation of the first coating layer in the film of the present invention, it is preferable to use various polymers and adhesive compounds in combination in order to hold the particles on the film. In particular, it is preferable to use a polymer in combination for the purpose of improving the appearance of coating, improving the transparency, and further improving the adhesion with various layers provided on the coating layer.

  Specific examples of the polymer include polyester resin, acrylic resin, urethane resin, polyvinyl (polyvinyl alcohol, etc.), polyalkylene glycol, polyalkyleneimine, methylcellulose, hydroxycellulose, and starches. Among these, it is preferable to use a polyester resin, an acrylic resin, or a urethane resin from the viewpoint of particle retention and adhesion. Moreover, when considering familiarity with a polyester film, a polyester resin is optimal.

  The polyester resin includes, for example, those composed of the following polyvalent carboxylic acid and polyvalent hydroxy compound as main constituent components. That is, as the polyvalent carboxylic acid, terephthalic acid, isophthalic acid, orthophthalic acid, phthalic acid, 4,4′-diphenyldicarboxylic acid, 2,5-naphthalenedicarboxylic acid, 1,5-naphthalenedicarboxylic acid, and 2,6 -Naphthalenedicarboxylic acid, 2,7-naphthalenedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, 2-potassium sulfoterephthalic acid, 5-sodium sulfoisophthalic acid, adipic acid, azelaic acid, sebacic acid, dodecanedicarboxylic acid, glutar Acid, succinic acid, trimellitic acid, trimesic acid, pyromellitic acid, trimellitic anhydride, phthalic anhydride, p-hydroxybenzoic acid, trimellitic acid monopotassium salt and ester-forming derivatives thereof can be used. As the polyvalent hydroxy compound, ethylene Recall, 1,2-propylene glycol, 1,3-propylene glycol, 1,3-propanediol, 1,4-butanediol, 1,6-hexanediol, 2-methyl-1,5-pentanediol , Neopentyl glycol, 1,4-cyclohexanedimethanol, p-xylylene glycol, bisphenol A-ethylene glycol adduct, diethylene glycol, triethylene glycol, polyethylene glycol, polypropylene glycol Polytetramethylene glycol, polytetramethylene oxide glycol, dimethylolpropionic acid, glycerin, trimethylolpropane, sodium dimethylolethylsulfonate, potassium dimethylolpropionate, and the like can be used. One or more compounds may be appropriately selected from these compounds, and a polyester resin may be synthesized by a conventional polycondensation reaction.

  The acrylic resin is a polymer composed of a polymerizable monomer having a carbon-carbon double bond, as typified by acrylic and methacrylic monomers. These may be either a homopolymer or a copolymer. Moreover, the copolymer of these polymers and other polymers (for example, polyester, polyurethane, etc.) is also included. For example, a block copolymer or a graft copolymer. Alternatively, a polymer (possibly a mixture of polymers) obtained by polymerizing a polymerizable monomer having a carbon-carbon double bond in a polyester solution or a polyester dispersion is also included. Similarly, a polymer (in some cases, a mixture of polymers) obtained by polymerizing a polymerizable monomer having a carbon-carbon double bond in a polyurethane solution or polyurethane dispersion is also included. Similarly, a polymer obtained by polymerizing a polymerizable monomer having a carbon-carbon double bond in another polymer solution or dispersion (in some cases, a polymer mixture) is also included. Moreover, in order to improve adhesiveness, it is also possible to contain a hydroxyl group and an amino group.

  The polymerizable monomer having a carbon-carbon double bond is not particularly limited, but particularly representative compounds include, for example, acrylic acid, methacrylic acid, crotonic acid, itaconic acid, fumaric acid, maleic acid, citracone. Various carboxyl group-containing monomers such as acids, and salts thereof; 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, monobutyl hydroxyl fumarate, Various hydroxyl group-containing monomers such as monobutylhydroxy itaconate; various monomers such as methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, butyl (meth) acrylate, lauryl (meth) acrylate ( (Meth) acrylic acid esters; Various nitrogen-containing compounds such as meth) acrylamide, diacetone acrylamide, N-methylolacrylamide or (meth) acrylonitrile; various styrene derivatives such as styrene, α-methylstyrene, divinylbenzene, vinyltoluene, vinyl propionate Various vinyl esters such as: Various silicon-containing polymerizable monomers such as γ-methacryloxypropyltrimethoxysilane, vinyltrimethoxysilane, etc .; Phosphorus-containing vinyl monomers; Various such as vinyl chloride and biridene chloride And various conjugated dienes such as butadiene.

  The urethane resin is a polymer compound having a urethane bond in the molecule. Usually, urethane resin is prepared by reaction of polyol and isocyanate. Examples of the polyol include polycarbonate polyols, polyester polyols, polyether polyols, polyolefin polyols, and acrylic polyols. These compounds may be used alone or in combination.

  Polycarbonate polyols are obtained from a polyhydric alcohol and a carbonate compound by a dealcoholization reaction. Examples of the polyhydric alcohols include ethylene glycol, 1,2-propylene glycol, 1,3-propylene glycol, 1,2-butanediol, 1,3-butanediol, 1,4-butanediol, 1,5-pentane. Diol, 1,6-hexanediol, 1,4-cyclohexanediol, 1,4-cyclohexanedimethanol, 1,7-heptanediol, 1,8-octanediol, 1,9-nonanediol, 1,10-decane Diol, neopentyl glycol, 3-methyl-1,5-pentanediol, 3,3-dimethylol heptane and the like can be mentioned. Examples of the carbonate compound include dimethyl carbonate, diethyl carbonate, diphenyl carbonate, and ethylene carbonate. Examples of polycarbonate polyols obtained from these reactions include poly (1,6-hexylene) carbonate, poly (3- And methyl-1,5-pentylene) carbonate.

  Polyester polyols include polycarboxylic acids (malonic acid, succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, sebacic acid, fumaric acid, maleic acid, terephthalic acid, isophthalic acid, etc.) or their acid anhydrides. Product and polyhydric alcohol (ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol, butanediol, 1,3-butanediol, 1,4-butanediol, 2,3-butanediol, 2-methyl-1,3-propanediol, 1,5-pentanediol, neopentyl glycol, 1,6-hexanediol, 3-methyl-1,5-pentanediol, 2-methyl-2,4-pentanediol 2-methyl-2-propyl-1 3-propanediol, 1,8-octanediol, 2,2,4-trimethyl-1,3-pentanediol, 2-ethyl-1,3-hexanediol, 2,5-dimethyl-2,5-hexanediol 1,9-nonanediol, 2-methyl-1,8-octanediol, 2-butyl-2-ethyl-1,3-propanediol, 2-butyl-2-hexyl-1,3-propanediol, cyclohexane Diol, bishydroxymethylcyclohexane, dimethanolbenzene, bishydroxyethoxybenzene, alkyl dialkanolamine, lactone diol, etc.).

  Examples of polyether polyols include polyethylene glycol, polypropylene glycol, polyethylene propylene glycol, polytetramethylene ether glycol, polyhexamethylene ether glycol, and the like.

  Among the above polyols, polycarbonate polyols and polyester polyols are more preferably used in order to improve adhesion to various topcoat layers.

  Examples of the polyisocyanate compound used for obtaining the urethane resin include aromatic diisocyanates such as tolylene diisocyanate, xylylene diisocyanate, methylene diphenyl diisocyanate, phenylene diisocyanate, naphthalene diisocyanate, and tolidine diisocyanate, α, α, α ′, α ′. -Aliphatic diisocyanates having aromatic rings such as tetramethylxylylene diisocyanate, aliphatic diisocyanates such as methylene diisocyanate, propylene diisocyanate, trimethylhexamethylene diisocyanate, hexamethylene diisocyanate, cyclohexane diisocyanate, methylcyclohexane diisocyanate, isophorone diisocyanate, dicyclohexyl Methanzi Cyanate, alicyclic diisocyanates such as isopropylidene dicyclohexyl diisocyanates. These may be used alone or in combination.

  A chain extender may be used when synthesizing the urethane resin, and the chain extender is not particularly limited as long as it has two or more active groups that react with an isocyanate group. Alternatively, a chain extender having two amino groups can be mainly used.

  Examples of the chain extender having two hydroxyl groups include aliphatic glycols such as ethylene glycol, propylene glycol and butanediol, aromatic glycols such as xylylene glycol and bishydroxyethoxybenzene, and esters such as neopentyl glycol hydroxypivalate. And glycols such as glycols. Examples of the chain extender having two amino groups include aromatic diamines such as tolylenediamine, xylylenediamine, and diphenylmethanediamine, ethylenediamine, propylenediamine, hexanediamine, 2,2-dimethyl-1,3- Propanediamine, 2-methyl-1,5-pentanediamine, trimethylhexanediamine, 2-butyl-2-ethyl-1,5-pentanediamine, 1,8-octanediamine, 1,9-nonanediamine, 1,10- Aliphatic diamines such as decane diamine, 1-amino-3-aminomethyl-3,5,5-trimethylcyclohexane, dicyclohexylmethanediamine, isoprobilitincyclohexyl-4,4′-diamine, 1,4-diaminocyclohexane, 1 , 3-Bisaminomethylcyclohexa And alicyclic diamines such as

The urethane resin in the present invention may use a solvent as a medium, but preferably uses water as a medium. In order to disperse or dissolve the urethane resin in water, there are a forced emulsification type using an emulsifier, a self-emulsification type in which a hydrophilic group is introduced into the urethane resin, and a water-soluble type. In particular, a self-emulsification type in which an ionic group is introduced into the skeleton of a urethane resin to form an ionomer is preferable because of excellent storage stability of the liquid and water resistance, transparency, and adhesion of the resulting coating layer.
Examples of the ionic group to be introduced include various groups such as a carboxyl group, sulfonic acid, phosphoric acid, phosphonic acid, quaternary ammonium salt, and the like, and a carboxyl group is preferable. As a method for introducing a carboxyl group into a urethane resin, various methods can be taken in each stage of the polymerization reaction. For example, there are a method of using a carboxyl group-containing resin as a copolymer component during prepolymer synthesis, and a method of using a component having a carboxyl group as one component such as polyol, polyisocyanate, and chain extender. In particular, a method in which a desired amount of carboxyl groups is introduced using a carboxyl group-containing diol depending on the amount of this component charged. For example, dimethylolpropionic acid, dimethylolbutanoic acid, bis- (2-hydroxyethyl) propionic acid, bis- (2-hydroxyethyl) butanoic acid and the like are copolymerized with a diol used for polymerization of a urethane resin. Can do. The carboxyl group is preferably in the form of a salt neutralized with ammonia, amine, alkali metal, inorganic alkali or the like. Particularly preferred are ammonia, trimethylamine and triethylamine. In such a polyurethane resin, a carboxyl group from which the neutralizing agent has been removed in the drying step after coating can be used as a crosslinking reaction point by another crosslinking agent. Thereby, it is possible to further improve the durability, solvent resistance, water resistance, blocking resistance, and the like of the obtained coating layer, as well as excellent stability in a liquid state before coating.

  Moreover, in the 1st application layer in this invention, in order to improve an intensity | strength, you may use a crosslinking agent together. As the crosslinking agent used in combination, various known crosslinking agents can be used, and examples thereof include an oxazoline compound, an epoxy compound, a melamine compound, an isocyanate compound, a carbodiimide compound, and a silane coupling compound.

  The oxazoline compound is a compound having an oxazoline group in the molecule, and a polymer containing an oxazoline group is particularly preferable, and can be prepared by polymerization of an addition polymerizable oxazoline group-containing monomer alone or with another monomer. Addition polymerizable oxazoline group-containing monomers include 2-vinyl-2-oxazoline, 2-vinyl-4-methyl-2-oxazoline, 2-vinyl-5-methyl-2-oxazoline, 2-isopropenyl-2-oxazoline, 2-isopropenyl-4-methyl-2-oxazoline, 2-isopropenyl-5-ethyl-2-oxazoline, and the like can be mentioned, and one or a mixture of two or more thereof can be used. Among these, 2-isopropenyl-2-oxazoline is preferred because it is easily available industrially. The other monomer is not limited as long as it is a monomer copolymerizable with an addition polymerizable oxazoline group-containing monomer. For example, alkyl (meth) acrylate (the alkyl group includes a methyl group, an ethyl group, an n-propyl group, an isopropyl group, (meth) acrylic acid esters such as n-butyl group, isobutyl group, t-butyl group, 2-ethylhexyl group, cyclohexyl group); acrylic acid, methacrylic acid, itaconic acid, maleic acid, fumaric acid, crotonic acid, styrene Unsaturated carboxylic acids such as sulfonic acid and its salts (sodium salt, potassium salt, ammonium salt, tertiary amine salt, etc.); Unsaturated nitriles such as acrylonitrile, methacrylonitrile; (meth) acrylamide, N-alkyl ( (Meth) acrylamide, N, N-dialkyl (meth) acrylamide, As the alkyl group, unsaturated amides such as methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group, t-butyl group, 2-ethylhexyl group and cyclohexyl group); vinyl acetate Vinyl esters such as vinyl propionate; vinyl ethers such as methyl vinyl ether and ethyl vinyl ether; α-olefins such as ethylene and propylene; halogen-containing α, β-unsaturated monomers such as vinyl chloride, vinylidene chloride and vinyl fluoride And α, β-unsaturated aromatic monomers such as styrene and α-methylstyrene, and the like, and one or more of these monomers can be used.

  The epoxy compound is a compound having an epoxy group in the molecule, and examples thereof include condensates of epichlorohydrin with ethylene glycol, polyethylene glycol, glycerin, polyglycerin, bisphenol A and the like hydroxyl groups and amino groups, There are polyepoxy compounds, diepoxy compounds, monoepoxy compounds, glycidylamine compounds, and the like. Examples of the polyepoxy compound include sorbitol polyglycidyl ether, polyglycerol polyglycidyl ether, pentaerythritol polyglycidyl ether, diglycerol polyglycidyl ether, triglycidyl tris (2-hydroxyethyl) isocyanate, glycerol polyglycidyl ether, trimethylolpropane. Examples of the polyglycidyl ether and diepoxy compound include neopentyl glycol diglycidyl ether, 1,6-hexanediol diglycidyl ether, resorcin diglycidyl ether, ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, and propylene glycol diglycidyl ether. , Polypropylene glycol diglycidyl ether, poly Examples of tetramethylene glycol diglycidyl ether and monoepoxy compounds include allyl glycidyl ether, 2-ethylhexyl glycidyl ether, phenyl glycidyl ether, and glycidyl amine compounds such as N, N, N ′, N′-tetraglycidyl-m-xylyl. Examples include range amine and 1,3-bis (N, N-diglycidylamino) cyclohexane.

  The melamine compound is a compound having a melamine skeleton in the compound. For example, an alkylolized melamine derivative, a compound partially or completely etherified by reacting an alcohol with an alkylolated melamine derivative, and these Mixtures can be used. As alcohol used for etherification, methyl alcohol, ethyl alcohol, isopropyl alcohol, n-butanol, isobutanol and the like are preferably used. Moreover, as a melamine compound, either a monomer or a multimer more than a dimer may be sufficient, or a mixture thereof may be used. Further, a product obtained by co-condensing urea or the like with a part of melamine can be used, and a catalyst can be used to increase the reactivity of the melamine compound.

  The isocyanate compound is a compound having an isocyanate derivative structure typified by isocyanate or blocked isocyanate. Examples of isocyanate include aromatic isocyanates such as tolylene diisocyanate, xylylene diisocyanate, methylene diphenyl diisocyanate, phenylene diisocyanate, and naphthalene diisocyanate, and aromatic rings such as α, α, α ′, α′-tetramethylxylylene diisocyanate. Aliphatic isocyanates such as aliphatic isocyanate, methylene diisocyanate, propylene diisocyanate, lysine diisocyanate, trimethylhexamethylene diisocyanate, hexamethylene diisocyanate, cyclohexane diisocyanate, methylcyclohexane diisocyanate, isophorone diisocyanate, methylene bis (4-cyclohexyl isocyanate), isopropylidene dicyclohexyl diisocyanate Ne Alicyclic isocyanates such as bets are exemplified. Further, polymers and derivatives such as burettes, isocyanurates, uretdiones, and carbodiimide modified products of these isocyanates are also included. These may be used alone or in combination. Among the above isocyanates, aliphatic isocyanates or alicyclic isocyanates are more preferable than aromatic isocyanates in order to avoid yellowing due to ultraviolet rays.

  When used in the state of blocked isocyanate, the blocking agent includes, for example, bisulfites, phenolic compounds such as phenol, cresol, and ethylphenol, and alcohols such as propylene glycol monomethyl ether, ethylene glycol, benzyl alcohol, methanol, and ethanol. Compounds, active methylene compounds such as dimethyl malonate, diethyl malonate, methyl acetoacetate, ethyl acetoacetate, acetylacetone, mercaptan compounds such as butyl mercaptan and dodecyl mercaptan, lactam compounds such as ε-caprolactam and δ-valerolactam , Amine compounds such as diphenylaniline, aniline, ethyleneimine, acetanilide, acid amide compounds of acetic acid amide, formaldehyde, acetoald Examples include oxime compounds such as oxime, acetone oxime, methyl ethyl ketone oxime, and cyclohexanone oxime, and these may be used alone or in combination of two or more.

  In addition, the isocyanate compound in the present invention may be used alone, or may be used as a mixture or bond with various polymers. In the sense of improving the dispersibility and crosslinkability of the isocyanate compound, it is preferable to use a mixture or a bond with a polyester resin or a urethane resin.

  A carbodiimide-based compound is a compound having a carbodiimide structure, and is used for improving adhesion with a surface functional layer such as a hard coat layer that can be formed on a coating layer, and for improving wet heat resistance of the coating layer. It is what The carbodiimide compound is a compound having one or more carbodiimide or carbodiimide derivative structures in the molecule, but a polycarbodiimide compound having two or more in the molecule is more preferable for better adhesion and the like.

  The carbodiimide compound can be synthesized by a conventionally known technique, and generally a condensation reaction of a diisocyanate compound is used. The diisocyanate compound is not particularly limited, and any of aromatic and aliphatic compounds can be used. Specifically, tolylene diisocyanate, xylene diisocyanate, diphenylmethane diisocyanate, phenylene diisocyanate, naphthalene diisocyanate, hexa Examples include methylene diisocyanate, trimethylhexamethylene diisocyanate, cyclohexane diisocyanate, methylcyclohexane diisocyanate, isophorone diisocyanate, dicyclohexyl diisocyanate, and dicyclohexylmethane diisocyanate.

  Furthermore, in order not to lose the effect of the present invention, in order to improve the water solubility and water dispersibility of the polycarbodiimide compound, adding a surfactant, polyalkylene oxide, quaternary ammonium salt of dialkylamino alcohol, You may add and use hydrophilic monomers, such as a hydroxyalkyl sulfonate.

  These cross-linking agents are used in a design that improves the performance of the coating layer by reacting in the drying process or film forming process. It can be inferred that unreacted products of these crosslinking agents, compounds after the reaction, or mixtures thereof exist in the finished coating layer.

  Regarding the formation of the first coating layer in the film of the present invention, a coating solution prepared by adjusting the solid content concentration to about 0.1 to 80% by weight using the above-described series of compounds as a solution or a dispersion of a solvent is used as an unstretched polyester. It is preferable to produce a polyester film in the manner of application on the film. In consideration of being inline in particular, it is more preferable that the solution is an aqueous solution or a water dispersion, but the coating solution contains a small amount of an organic solvent for the purpose of improving the dispersibility in water and improving the film forming property. You may do it. Moreover, only one type of organic solvent may be used, and two or more types may be used as appropriate.

The amount of the non-heat-resistant particles constituting the first coating layer in the film of the present invention is not particularly limited as long as the object is achieved. Further, since it depends on the thermal characteristics and size of the particles to be used and the film thickness of the first coating layer, it cannot be generally stated. However, the amount of only one side is a film after drying (before stretching), preferably 0. range 01~200mg / ^{m 2,} more preferably from 0.1~150mg / ^{m 2,} more preferably in the range of 1~70mg / ^{m 2.}

Moreover, since the coating amount of the first coating layer (after drying and before stretching) depends on the size of the particles, the stretching ratio, etc., it cannot be generally stated, but is preferably 0.001 to 5 g / m ² or less. The range is more preferably in the range of 0.01 to 3 g / m ² , still more preferably in the range of 0.05 to 1 g / m ² , and most preferably in the range of 0.1 to 0.7 g / m ² . When the coating amount is out of the above range, there are concerns about blocking, deterioration of the coating appearance, and dropout of particles.

  In the film of the present invention, as a method for forming the first coating layer, for example, a conventionally known coating method such as reverse gravure coating, direct gravure coating, roll coating, die coating, bar coating, curtain coating, spray coating or the like is used. be able to.

  Moreover, when forming a 1st application layer in a film, you may perform surface treatments, such as a corona treatment and a plasma treatment, as needed.

  Moreover, in this invention, after forming a 1st coating layer and extending | stretching at least to one direction, a 2nd coating layer is formed in order to provide various performances. The second coating layer may be formed on the surface side on which the first coating layer is formed, or may be formed on the opposite surface side of the first coating layer. Moreover, you may form only in the single side | surface side of a film, and may form in both surfaces. Regarding the second coating layer, it may be provided by in-line coating, which treats the film surface during the process of forming a polyester film, or may be applied off-system on a once produced film. . Since the coating can be performed simultaneously with the film formation, the production can be handled at a low cost, and therefore inline coating is preferably used.

  The in-line coating in the formation of the second coating layer is not limited to the following. For example, in the sequential biaxial stretching, the coating treatment can be performed particularly before the lateral stretching after the longitudinal stretching is finished. When the second coating layer is provided on the polyester film by in-line coating, coating can be performed simultaneously with film formation, and the coating layer can be processed at a high temperature in the heat treatment step of the stretched polyester film. The properties such as adhesion to various surface functional layers that can be formed on the coating layer and heat-and-moisture resistance can be improved. Further, when coating is performed before transverse stretching, the thickness of the coating layer can be changed by the stretching ratio, and thin film coating can be performed more easily than offline coating. That is, a film suitable as a polyester film can be produced by in-line coating, particularly coating before stretching.

  That is, as one of the preferable production methods in the present invention, for example, an unstretched film is formed after melt extrusion, and then a first coating layer is formed and then longitudinal stretching is performed to further form a second coating layer, Then, it is the method of processing at high temperature, after performing horizontal extending | stretching.

  The 2nd application layer in the film of the present invention is provided in order to improve adhesiveness with various surface functional layers, such as a prism layer and a micro lens layer.

  As the urethane resin used for forming the second coating layer, the above-described urethane resin that can be used for forming the first coating layer can be used. Among these, from the viewpoint of particularly good adhesion, a urethane resin having a polycarbonate structure and a urethane resin having a polyester structure are preferable, and a urethane resin having a polycarbonate structure is more preferable.

  From the viewpoint of adhesion, the urethane resin used for forming the second coating layer preferably has a glass transition point (hereinafter sometimes referred to as Tg) of 10 ° C. or lower, more preferably 0 ° C. or lower. It is a range. If a material having a Tg higher than 10 ° C. is used, the adhesion may be insufficient. The measurement of Tg mentioned here refers to a temperature at which E ″ is maximized by preparing a dry film of urethane resin and performing dynamic viscoelasticity measurement.

  In forming the second coating layer, it is preferable to contain a crosslinking agent in order to strengthen the coating layer of the coating layer and improve the heat and heat resistance after forming the surface functional layer such as the prism layer and the microlens layer. Examples of the crosslinking agent include the oxazoline compounds, epoxy compounds, melamine compounds, isocyanate compounds, carbodiimide compounds, silane coupling compounds, and the like that can be used in the formation of the first coating layer. In a preferred embodiment of the present invention, an oxazoline compound is used for a urethane resin containing a carboxyl group. Moreover, in order to improve adhesiveness, it is more preferable to use an oxazoline compound and another crosslinking agent, especially an epoxy compound or a melamine compound in combination.

  For the formation of the second coating layer, in addition to the urethane resin described above in order to improve the coating appearance, improve the visibility when various prism layers, microlens layers, etc. are formed on the coating surface, and improve the transparency. These polymers can also be used in combination. As the polymer, it is possible to use the above-described polymer that can be used for forming the first coating layer.

  In the film of the present invention, particles can be used in combination with the formation of the second coating layer for the purpose of blocking the coating layer and improving the slipperiness. The average particle size is preferably in the range of 1.0 μm or less, more preferably 0.5 μm or less, particularly preferably 0.2 μm or less from the viewpoint of the transparency of the film. Moreover, when it is necessary to raise the effect of improving slipperiness, it is preferable to use particles having an average particle size larger than the film thickness of the coating layer. Specific examples of the particles include silica, alumina, kaolin, calcium carbonate, heat-resistant organic particles, and the like.

  Further, in the range not impairing the gist of the present invention, the above-mentioned coating layer is formed with an antifoaming agent, a coating property improving agent, a thickener, an organic lubricant, an antistatic agent, an ultraviolet absorber, an oxidation as necessary. Inhibitors, foaming agents, dyes, pigments and the like can be used.

  As a ratio with respect to the total nonvolatile components in the coating liquid for forming the second coating layer, the urethane resin is usually in the range of 20% by weight or more, preferably in the range of 30 to 90% by weight, more preferably in the range of 40 to 80% by weight. It is. If it is outside the above range, the adhesion may not be sufficient.

  As a ratio with respect to all the non-volatile components in the coating liquid for forming the second coating layer, the crosslinking agent is usually in the range of 70% by weight or less, preferably in the range of 10 to 60% by weight, more preferably in the range of 20 to 50% by weight. It is. Adhesion can be improved by using in this range.

  Analysis of the final form of the non-heat-resistant particles used for forming the first coating layer, and other components in the first and second coating layers, for example, TOF-SIMS, ESCA, fluorescent X-rays, various surfaces, It can be performed by cross-sectional observation or the like.

  When the second coating layer is provided by in-line coating, the above-mentioned series of compounds is applied as an aqueous solution or water dispersion, and a coating solution adjusted to a solid content concentration of about 0.1 to 50% by weight is applied onto the polyester film. It is preferable to produce a polyester film as described above. Moreover, in the range which does not impair the main point of this invention, a small amount of organic solvents may be contained in the coating liquid for the purpose of improving dispersibility in water, improving film-forming properties, and the like. Only one type of organic solvent may be used, or two or more types may be used as appropriate.

Respect laminated polyester film of the present invention, the coating amount of the second coating layer provided on the polyester film is usually 0.002~1.0g / ^{m 2,} more preferably 0.005 to 0.5 / ^{m 2,} further Preferably it is the range of 0.01-0.2 g / m < ² >. If the coating amount is less than 0.002 g / m ^2, sufficient adhesion may not be obtained, and if it exceeds 1.0 g / m ² , the appearance, transparency, and film blocking properties may be deteriorated. There is sex.

  In the present invention, as a method for providing the second coating layer, a conventionally known coating method such as reverse gravure coating, direct gravure coating, roll coating, die coating, bar coating, curtain coating, spray coating or the like can be used.

  In the present invention, the drying and curing conditions for forming the second coating layer on the polyester film are not particularly limited. For example, when the coating layer is provided by off-line coating, it is usually 3 at 80 to 250 ° C. The heat treatment should be performed for ˜40 seconds, preferably 100 to 180 ° C. for 3 to 40 seconds.

  On the other hand, when forming a 2nd application layer by in-line coating, it is good to heat-process normally for 3 to 200 seconds at 70-270 degreeC.

  Further, irrespective of off-line coating or in-line coating, heat treatment and active energy ray irradiation such as ultraviolet irradiation may be used in combination as required. The polyester film constituting the polyester film in the present invention may be subjected to surface treatment such as corona treatment or plasma treatment in advance.

  The polyester film in the present invention can be used for applications requiring excellent transparency, and its internal haze is preferably in the range of 0.0 to 1.0%, more preferably 0.0 to 0.5%. More preferably, it is 0.0 to 0.3% of range. When the internal haze exceeds 1.0%, even if various surface functional layers are provided on the film, the haze cannot be sufficiently lowered, and the whitish color remains as a film. Cannot be achieved.

  The haze of the polyester film in the present invention cannot be generally stated when various surface functional layers are provided on the film because the surface haze can be lowered, but is preferably in the range of 0.0 to 2.0%, more preferably. Is in the range of 0.0 to 1.5%, more preferably in the range of 0.0 to 1.0%. If it exceeds 2.0%, the appearance of the film may be poor, or even if various surface functional layers are provided, the haze cannot be lowered sufficiently, and the visibility may be insufficient.

  In general, a prism layer, a microlens layer, or the like is provided on the second coating layer of the laminated polyester film of the present invention in order to improve luminance. In recent years, various shapes have been proposed for the prism layer in order to improve the luminance efficiently. Generally, prism layers are formed by arranging prism rows having a triangular cross section in parallel. Similarly, various shapes of the microlens layer have been proposed, but in general, a large number of hemispherical convex lenses are provided on the film. Any layer can have a conventionally known shape.

  Examples of the shape of the prism layer include a triangular cross section having a thickness of 10 to 500 μm, a pitch of prism rows of 10 to 500 μm, and an apex angle of 40 ° to 100 °. As the material used for the prism layer, conventionally known materials can be used, for example, those made of an active energy ray-curable resin, such as monofunctional (meth) acrylate, bifunctional (meth) acrylate, Examples include polyfunctional (meth) acrylates, polyester resins, epoxy resins, polyester (meth) acrylates, epoxy (meth) acrylates, (meth) acrylate resins such as urethane (meth) acrylates, and the like.

  The composition containing the active energy ray-curable (meth) acrylate is not particularly limited. For example, known active energy ray curable monofunctional (meth) acrylate, bifunctional (meth) acrylate, polyfunctional (meth) acrylate mixed one or more types, active energy ray curable prism and resin for microlenses What is marketed as a material, or what added the other component in the range which does not impair the objective of this embodiment other than these can be used.

  The active energy ray-curable monofunctional (meth) acrylate is not particularly limited. For example, methyl (meth) acrylate, n-butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, lauryl (meth) ) Acrylate, stearyl (meth) acrylate, cyclohexyl (meth) acrylate, alkyl (meth) acrylate such as isobornyl (meth) acrylate, hydroxyethyl (meth) acrylate, hydroxypropyl (meth) acrylate, hydroxybutyl (meth) acrylate, etc. Alkyl (meth) acrylate, methoxyethyl (meth) acrylate, ethoxyethyl (meth) acrylate, methoxypropyl (meth) acrylate, ethoxypropyl (meth) acrylate, etc. Amino group-containing (meth) acrylates such as xylalkyl (meth) acrylate, benzyl (meth) acrylate, aromatic (meth) acrylate such as phenoxyethyl (meth) acrylate, diaminoethyl (meth) acrylate, diethylaminoethyl (meth) acrylate, Methoxyethylene glycol (meth) acrylate, phenoxy polyethylene glycol (meth) acrylate, ethylene oxide modified (meth) acrylate such as phenylphenol ethylene oxide modified (meth) acrylate, glycidyl (meth) acrylate, tetrahydrofurfuryl (meth) acrylate, Examples include (meth) acrylic acid.

  The active energy ray-curable difunctional (meth) acrylate is not particularly limited, and for example, 1,4-butanediol di (meth) acrylate, neopentyl glycol di (meth) acrylate, 1,6- Hexanediol di (meth) acrylate, 1,9-nonanediol di (meth) acrylate, alkanediol di (meth) acrylate such as tricyclodecane dimethylol di (meth) acrylate, bisphenol A ethylene oxide modified di (meth) acrylate Bisphenol F ethylene oxide modified di (meth) acrylate and other bisphenol modified di (meth) acrylate, polyethylene glycol di (meth) acrylate, polypropylene glycol di (meth) acrylate, urethane di (meth) acrylate And epoxy di (meth) acrylate.

  The active energy ray-curable polyfunctional (meth) acrylate is not particularly limited. For example, dipentaerythritol hexa (meth) acrylate, pentaerythritol tetra (meth) acrylate, ditrimethylolpropane tetra (meth) acrylate , Pentaerythritol tri (meth) acrylate, trimethylolpropane tri (meth) acrylate, isocyanuric acid ethylene oxide modified tri (meth) acrylate, ε-caprolactone modified tris (acryloxyethyl) isocyanurate Acrylate, pentaerythritol triacrylate hexamethylene diisocyanate urethane prepolymer, pentaerythritol triacrylate toluene diisocyanate urea Down prepolymers, urethane acrylates such as dipentaerythritol pentaacrylate hexamethylene diisocyanate urethane prepolymer, and the like.

  Other components contained in the composition containing the active energy ray-curable compound are not particularly limited. Examples thereof include inorganic or organic fine particles, polymerization initiators, polymerization inhibitors, antioxidants, antistatic agents, dispersants, surfactants, light stabilizers, and leveling agents. In addition, when the film is dried after film formation in the wet coating method, an arbitrary amount of solvent can be added.

  Examples of the shape of the microlens layer include a hemispherical shape having a thickness of 10 to 500 μm and a diameter of 10 to 500 μm, but may have a shape such as a cone or a polygonal pyramid. As the material used for the microlens layer, conventionally known materials can be used as in the prism layer, and examples thereof include an active energy ray curable resin.

  EXAMPLES Hereinafter, although an Example demonstrates this invention further in detail, this invention is not limited to a following example, unless the summary is exceeded. The measurement method and evaluation method used in the present invention are as follows.

(1) Method for measuring the intrinsic viscosity of polyester 1 g of polyester from which other polymer components and pigments incompatible with polyester have been removed are precisely weighed, and 100 ml of a mixed solvent of phenol / tetrachloroethane = 50/50 (weight ratio) is added. And dissolved at 30 ° C.

(2) Measuring method of average particle diameter of particles The film was observed using an electron microscope (S-4500 manufactured by HITACHI), and the average value of the particle diameters of 10 particles was defined as the average particle diameter. The non-heat resistant particles were observed on the film before the high temperature process, that is, after the longitudinal stretching and before the transverse stretching.

(3) Measuring method of internal haze Using haze meter HZ-2 manufactured by Suga Test Instruments Co., Ltd., the film was immersed in ethanol and measured according to JIS K 7136.

(4) Measuring method of haze It measured by JISK7136 using the haze meter HM-150 by Murakami Color Research Laboratory.

(5) Film surface roughness (Sa)
Using a three-dimensional non-contact surface shape measurement system (MN537N-M100, manufactured by Ryoka System Co., Ltd.), the roughness Sa of the film on the cooled and solidified surface side before the high-temperature process, that is, after the longitudinal stretching and before the transverse stretching is determined. It was measured. When the Sa is less than 5 nm, the slipperiness is poor, and there is a concern that scratches may occur when coming into contact with a roll or the like in a stretching process or the like. A more preferable form is 5 nm or more.

(6) Transparency evaluation method When the film is visually observed under a three-wavelength light region type fluorescent lamp, the particle feeling (dots due to particles in the film) is not observed and there is a clear feeling. The case where there was a particle feeling or the case where whitishness was observed was taken as x.

(7) Adhesion evaluation method of second coating layer For forming a prism layer, 47 parts by weight of phenoxyethyl acrylate, ethylene glycol modified, on a mold member in which a large number of prism rows with a pitch of 50 μm and apex angle of 65 ° are arranged in parallel An active energy ray-curable composition composed of 50 parts by weight of bisphenol A acrylate (ethylene glycol chain = 8) and 3 parts by weight of diphenyl (2,4,6-trimethylbenzoyl) phosphine oxide is disposed. The laminated polyester film is laminated in such a direction that the coating layer comes into contact with the active energy ray curable resin, the active energy ray curable composition is uniformly stretched by a roller, and the ultraviolet ray is irradiated from the ultraviolet ray irradiation device. Was cured. Subsequently, the film was peeled off from the mold member to obtain a film on which a prism layer was formed. The obtained film was treated in an environment of 80 ° C. and 90% RH for 50 hours, then 10 × 10 cross-cut was made on the prism layer, and 18 mm wide tape (cello tape made by Nichiban Co., Ltd.) (Registered Trademark) CT-18) is attached, and the peeled surface is peeled off rapidly at a peel angle of 180 degrees. If the peeled area is less than 5%, ◎, if it is less than 5% and less than 20%, If it was 20% or more and less than 50%, it was rated as Δ, and if it was 50% or more, it was marked as x.

The polyester used in the examples and comparative examples was prepared as follows.
<Method for producing polyester (A)>
100 parts by weight of dimethyl terephthalate, 60 parts by weight of ethylene glycol, 30 ppm of ethyl acid phosphate with respect to the resulting polyester, and 100 ppm of magnesium acetate tetrahydrate with respect to the resulting polyester as the catalyst at 260 ° C. in a nitrogen atmosphere at 260 ° C. The reaction was allowed to proceed. Subsequently, 50 ppm of tetrabutyl titanate was added to the resulting polyester, the temperature was raised to 280 ° C. over 2 hours and 30 minutes, the pressure was reduced to 0.3 kPa in absolute pressure, and melt polycondensation was further carried out for 80 minutes. 0.63 polyester (A) was obtained.

<Method for producing polyester (B)>
100 parts by weight of dimethyl terephthalate, 60 parts by weight of ethylene glycol, and magnesium acetate tetrahydrate as a catalyst were subjected to an esterification reaction at 225 ° C. in a nitrogen atmosphere at 900 ppm with respect to the produced polyester. Subsequently, 3500 ppm of orthophosphoric acid was added to the produced polyester, and 70 ppm of germanium dioxide was added to the produced polyester. The temperature was raised to 280 ° C. over 2 hours and 30 minutes, and the pressure was reduced to an absolute pressure of 0.4 kPa. After 85 minutes of melt polycondensation, polyester (B) having an intrinsic viscosity of 0.64 was obtained.

<Method for producing polyester (C)>
In the production method of the polyester (A), the same method as the production method of the polyester (A) is used except that 0.5% by weight of silica particles having an average particle size of 0.1 μm is added to the produced polyester before melt polymerization. Thus, polyester (C) was obtained.

<Method for producing polyester (D)>
In the production method of the polyester (A), the same method as the production method of the polyester (A) is used except that 0.5% by weight of silica particles having an average particle diameter of 3.2 μm is added to the produced polyester before melt polymerization. Thus, polyester (D) was obtained.

Examples of compounds constituting each coating layer are as follows.
(Example compounds)
Non-heat-resistant particles: (IA) Non-heat-resistant non-crosslinked acrylic particles having an average particle size of 0.09 μm, a softening point of 210 ° C., and a glass transition point of 60 ° C. copolymerized with a composition of methyl methacrylate / butyl acrylate = 80/20 Non-heat-resistant particles: (IB) Non-heat-resistant non-crosslinked styrene / acrylic resin particles having an average particle size of 0.37 μm, a softening point of 220 ° C., and a glass transition point of 110 ° C., copolymerized with a composition of methyl methacrylate / styrene = 70/30 Silica particles: (IC) Silica particles having an average particle size of 0.30 μm Silica particles: (ID) Silica particles having an average particle size of 0.07 μm

・ Polyester resin: (IIA)
Water dispersion of polyester resin copolymerized with the following composition: Monomer composition: (acid component) terephthalic acid / isophthalic acid / 5-sodium sulfoisophthalic acid // (diol component) ethylene glycol / 1,4-butanediol / diethylene glycol = 56/40/4 // 70/20/10 (mol%)

・ Acrylic resin: (IIB)
Aqueous dispersion of acrylic resin polymerized with the following composition: Emulsion polymer of ethyl acrylate / n-butyl acrylate / methyl methacrylate / N-methylol acrylamide / acrylic acid = 65/21/10/2/2 (% by weight) (emulsifier: Anionic surfactant)

・ Urethane resin (IIC)
Hydran AP-40 (manufactured by DIC Corporation), which is a carboxylic acid water-dispersed polyester polyurethane resin
-Urethane resin: (IID)
A prepolymer consisting of 1,6 hexanediol and diethyl carbonate having a number average molecular weight of 2000 polycarbonate polyol, 2 parts neopentyl glycol, 2 parts isophorone diisocyanate and 2 parts dimethylol butanoic acid in triethylamine. Water dispersion of urethane resin with a Tg of -30 ° C and urethane resin obtained by adding and chain-extending with isophoronediamine: (IIE)
Consisting of 80 parts of polycarbonate polyol having a number average molecular weight of 2000 consisting of 1,6-hexanediol and diethyl carbonate, 4 parts of polyethylene glycol having a number average molecular weight of 400, 12 parts of methylenebis (4-cyclohexylisocyanate), and 4 parts of dimethylolbutanoic acid. Urethane resin neutralized with triethylamine, water dispersion of urethane resin having Tg of -30 ° C

・ Hexamethoxymethylmelamine (IIIA)

・ Oxazoline compounds: (IIIB)
Acrylic polymer having an oxazoline group and a polyalkylene oxide chain Epocros WS-500 (manufactured by Nippon Shokubai Co., Ltd., containing about 38% by weight of 1-methoxy-2-propanol solvent)

Epoxy compound: (IIIC) Denacol EX-521 (manufactured by Nagase ChemteX Corporation), which is polyglycerol polyglycidyl ether

Example 1:
A mixed raw material in which polyesters (A) and (B) are mixed at a ratio of 97% and 3%, respectively, is used as a raw material for the outermost layer (surface layer), and polyesters (A) and (B) are respectively at a ratio of 97% and 3%. Each of the mixed raw materials is fed to two extruders as a raw material for the intermediate layer, melted at 285 ° C., and then two types and three layers (surface layer / intermediate layer / Coextruded and cooled and solidified with a layer structure of (surface layer = 1: 18: 1 discharge amount) to obtain an unstretched film. Thereafter, an aqueous coating solution A1 shown in Table 1 below was applied to both sides of the unstretched film and dried to obtain a film having a first coating layer having a coating amount (after drying) of 0.2 g / m ² . Next, the film was stretched 3.4 times in the longitudinal direction at a film temperature of 85 ° C. using the roll peripheral speed difference, and then the aqueous coating solution B1 shown in Table 2 below was applied to both surfaces of the longitudinally stretched film. guided, transversely stretched 4.0 times at 120 ° C., 230 subjected to heat setting at ° C., 2% relaxation in the transverse direction, the coating amount of the coating layer (after drying and stretching) of 0.03 g / ^{m 2} A polyester film having a thickness of 125 μm and having a second coating layer was obtained. When the obtained polyester film was evaluated, the transparency was good, the roughness of the film after longitudinal stretching was sufficient, and the adhesion was also good. The properties of this film are shown in Table 5 below.

Examples 2-24:
In Example 1, it manufactured like Example 1 except having changed an application agent composition into an application agent composition shown in Tables 1-3, and obtained a polyester film. As shown in Table 5 below, the finished polyester film had good transparency, sufficient film roughness after longitudinal stretching, and good adhesion.

Example 25:
A mixed raw material in which polyesters (A), (B), and (C) were mixed at a ratio of 96%, 3%, and 1%, respectively, was used as a raw material for the outermost layer (surface layer), and polyesters (A) and (B) were each 97 %, 3% of the mixed raw material is used as an intermediate layer raw material, each is supplied to two extruders, melted at 285 ° C., and then on a cooling roll set at 40 ° C. Coextruded with a layer structure of layers (surface layer / intermediate layer / surface layer = 1: 18: 1 discharge amount) and cooled and solidified to obtain an unstretched film. Thereafter, an aqueous coating solution A1 shown in Table 1 below was applied to both sides of the unstretched film and dried to obtain a film having a first coating layer having a coating amount (after drying) of 0.2 g / m ² . Next, the film was stretched 3.4 times in the longitudinal direction at a film temperature of 85 ° C. using the roll peripheral speed difference, and then the aqueous coating solution B1 shown in Table 2 below was applied to both surfaces of the longitudinally stretched film. guided, transversely stretched 4.0 times at 120 ° C., 230 subjected to heat setting at ° C., 2% relaxation in the transverse direction, the coating amount of the coating layer (after drying and stretching) of 0.03 g / ^{m 2} A polyester film having a thickness of 125 μm and having a second coating layer was obtained. When the obtained polyester film was evaluated, the transparency was good, the roughness of the film after longitudinal stretching was sufficient, and the adhesion was also good. The properties of this film are shown in Table 5 below.

Comparative Example 1:
In Example 1, it manufactured like Example 1 except not providing a 1st coating layer in an unstretched film, and obtained the polyester film. When the finished polyester film was evaluated, as shown in Table 6 below, the film after longitudinal stretching had a small roughness and was likely to be damaged.

Comparative Examples 2-5:
In Example 1, it manufactured like Example 1 except having changed a coating agent composition into the coating agent composition shown in following Table 1, 2, 4, and obtained the polyester film. As shown in Table 6, the finished polyester film has a high haze and a whitish film, a case where the film is not sufficiently rough after longitudinal stretching, and a case where the adhesion is poor. It was.

Comparative Example 6:
A mixed raw material in which polyesters (A), (B), and (D) were mixed at a ratio of 92%, 3%, and 5%, respectively, was used as a raw material for the outermost layer (surface layer), and polyesters (A) and (B) were each 97 %, 3% of the mixed raw material is used as an intermediate layer raw material, each is supplied to two extruders, melted at 285 ° C., and then on a cooling roll set at 40 ° C. Coextruded with a layer structure of layers (surface layer / intermediate layer / surface layer = 1: 18: 1 discharge amount) and cooled and solidified to obtain an unstretched film. Next, the film was stretched 3.4 times in the longitudinal direction at a film temperature of 85 ° C. using the roll peripheral speed difference, and then the aqueous coating solution B1 shown in Table 2 below was applied to both surfaces of the longitudinally stretched film. guided, transversely stretched 4.0 times at 120 ° C., 230 subjected to heat setting at ° C., 2% relaxation in the transverse direction, the coating amount of the coating layer (after drying and stretching) of 0.03 g / ^{m 2} A polyester film having a thickness of 125 μm was obtained. When the obtained polyester film was evaluated, a particle feeling was observed and the film was whitish. The properties of this film are shown in Table 6 below.

  The film of the present invention has excellent transparency and slipperiness, for example, applications that require adhesion with surface functional layers such as prism layers and microlens layers used in backlight units of liquid crystal displays, etc. Can be suitably used.

Claims (1)

After having applied a coating solution containing non-heat-resistant particles on at least one side of an unstretched polyester film, it has a coating layer formed by stretching in at least one direction, on the coating layer or on the opposite side of the coating layer A laminated polyester film comprising a coating layer formed from a coating solution containing a urethane resin on the side.