JP2008024677A - Colored composite powder and cosmetic compounded with the same - Google Patents
Colored composite powder and cosmetic compounded with the same Download PDFInfo
- Publication number
- JP2008024677A JP2008024677A JP2006201658A JP2006201658A JP2008024677A JP 2008024677 A JP2008024677 A JP 2008024677A JP 2006201658 A JP2006201658 A JP 2006201658A JP 2006201658 A JP2006201658 A JP 2006201658A JP 2008024677 A JP2008024677 A JP 2008024677A
- Authority
- JP
- Japan
- Prior art keywords
- composite powder
- colored composite
- metal
- colored
- cosmetic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
本発明は、鮮やかな有色の外観を有する着色複合粉末及びこれを配合した化粧料に関する。 The present invention relates to a colored composite powder having a bright colored appearance and a cosmetic containing the same.
さらに詳しくは、特定粒子径の微粒子金属コロイドを内包した金属酸化物からなる着色複合粉末と、これを、ファンデーション、アイシャドー、口紅、グロス、マスカラ、アイライナー、ネールエナメル、ネールエナメルベースコート、クリーム、乳液等の化粧料に配合して得られる、安定性に優れかつ鮮やかな有色の外観を有する化粧料に関する。 More specifically, a colored composite powder composed of a metal oxide encapsulating a fine particle metal colloid having a specific particle size, and a foundation, eye shadow, lipstick, gloss, mascara, eyeliner, nail enamel, nail enamel base coat, cream, The present invention relates to a cosmetic that is obtained by blending into a cosmetic such as an emulsion and has a stable and vivid colored appearance.
化粧料、特にファンデーション、口紅、ネールエナメル等のメーキャップ化粧料は、メーキャップ効果を付与するために、有機顔料、無機顔料、或は雲母チタン等のパール剤を配合するものが殆どである。 Most cosmetics, especially makeup cosmetics such as foundations, lipsticks, and nail enamels, are blended with organic pigments, inorganic pigments, or pearl agents such as titanium mica in order to impart a makeup effect.
しかし、これら顔料のうち、無機顔料は、安定性に優れるものの彩度は低く、鮮やかな発色を得ることが非常に困難である。逆に、有機顔料は、鮮やかな発色を得られるものの、化粧料に用いられるものは、光を照射されることにより色調が大きく変化してしまい、安定性が非常に悪いものが多い。 However, among these pigments, inorganic pigments are excellent in stability but have low saturation and it is very difficult to obtain vivid colors. Conversely, organic pigments can obtain vivid colors, but those used in cosmetics often have very poor stability because their color tone changes greatly when irradiated with light.
そこで、安定性が高く、彩度の高い色材として微粒子金属コロイドゾルに注目した研究がなされてきた。これらの微粒子金属コロイドはプラズモン発色と呼ばれる原理により、金であれば５５０ｎｍ付近に吸収を持つことから赤色を呈し、銀や水銀であれば４５０ｎｍ以下の低波長側に吸収を持つことから黄色を呈することが知られている。そして、この原理を用いた特許も多数出願されてきた。 Therefore, studies have been made focusing on fine-particle metal colloidal sol as a highly stable and highly saturated colorant. These fine-particle metal colloids exhibit a red color because they have an absorption near 550 nm in the case of gold by the principle called plasmon coloring, and yellow because they have an absorption in the lower wavelength side of 450 nm or less if they are silver or mercury. It is known. Many patents using this principle have been filed.
例えば、特許文献１には、塩化金酸を還元した時に得られる微細な金のコロイド粒子をその生成と同時に担体表面にコーティングした紫色顔料を配合した化粧料が記載されている。
また、特許文献２には、金属酸化物上に金水酸化物を析出させ、金水酸化物を焼成することにより分解して金超微粒子を均一に析出固定させた固定化酸化物を配合した化粧料が記載されている。
さらに、特許文献３には、貴金属コロイドを母材顔料に被覆し、これを焼成した顔料を配合した化粧料が収載されている。
For example, Patent Document 1 describes a cosmetic containing a purple pigment in which fine gold colloidal particles obtained by reducing chloroauric acid are coated on the surface of the carrier at the same time as the generation thereof.
Patent Document 2 discloses a cosmetic containing a fixed oxide in which gold hydroxide is deposited on a metal oxide and decomposed by firing the gold hydroxide to uniformly deposit and fix gold ultrafine particles. Is described.
Furthermore, Patent Document 3 discloses a cosmetic containing a pigment obtained by coating a base material pigment with a noble metal colloid and firing it.
しかしながら、上記の特許文献に記載されているように、金コロイドについてはその鮮やかな赤色〜紫色の発色に着目されて化粧料に利用されたものであり、それ以外の色についての記載はない。特に青色〜緑色に発色する金コロイド複合粒子は示唆されていない。
また、特許文献１及び特許文献３に記載されているように、核を用いてその表面に固定化する製法では、配合する製品によっては表面から微粒子金属が再分離してしまい、安定性に欠ける場合があった。
さらに、特許文献２においては、特許文献１及び特許文献３以外の製法として、金属酸化物と同種の金属塩水溶液及び金化合物水溶液の混液をアルカリに滴下することにより金超微粒子固定化酸化物を得る製法が記載されているが、この製法では還元剤を使用していないため、金コロイドの粒径をコントロールすることが困難であるだけではなく、金属塩水溶液が加水分解する際の急激なｐＨ変化のため、金属酸化物の粒径やその形状をコントロールすることが困難である。
このように、上記特許文献には微粒子金属コロイドと金属酸化物との複合粉末を化粧料に配合することは記載されているが、特定粒子径の金属コロイドを金属酸化物に内包させ、赤色〜紫色以外の色に発色する複合粉末に関する記載はない。
However, as described in the above-mentioned patent document, the colloidal gold is used for cosmetics with attention paid to its bright red to purple color development, and there is no description about other colors. In particular, gold colloid composite particles that develop blue to green color are not suggested.
In addition, as described in Patent Document 1 and Patent Document 3, in the manufacturing method in which the core is immobilized on the surface, the particulate metal is re-separated from the surface depending on the product to be blended, and lacks stability. There was a case.
Furthermore, in Patent Document 2, as a manufacturing method other than Patent Document 1 and Patent Document 3, a mixed solution of a metal salt aqueous solution and a gold compound aqueous solution of the same type as a metal oxide is added dropwise to an alkali to produce an ultrafine gold particle-immobilized oxide. Although a manufacturing method to be obtained is described, since this method does not use a reducing agent, it is not only difficult to control the particle size of the gold colloid, but also a rapid pH when the aqueous metal salt solution is hydrolyzed. Due to the change, it is difficult to control the particle size and shape of the metal oxide.
As described above, in the above-mentioned patent document, it is described that a composite powder of a fine particle metal colloid and a metal oxide is blended in cosmetics. There is no description regarding composite powders that develop colors other than purple.
本発明者らは上述の観点から鋭意研究を重ねた結果、金属酸化物を生成する際に特定の粒子径を持つ金属コロイドゾルが金属酸化物に内包されるように合成すると赤色〜紫色以外の色、特に青色又は緑色に鮮やかに発色する複合粉末が得られ、これを化粧料に配合すると、安定性に優れ、美しい色彩を有する化粧料を製造できることを見出し本発明を完成するに至った。 As a result of intensive research from the above viewpoint, the present inventors have synthesized a metal colloidal sol having a specific particle size so as to be encapsulated in the metal oxide when producing the metal oxide. In particular, a composite powder that vividly develops blue or green color is obtained, and when this is blended into cosmetics, it has been found that cosmetics having excellent stability and beautiful colors can be produced, and the present invention has been completed.
本発明の目的は、特定の微粒子金属コロイド粒子を内包した着色複合粉末を提供し、これを化粧料に配合することにより、安定性を損なうことなく、美しい色彩を有する化粧料を提供することである。 An object of the present invention is to provide a colored composite powder encapsulating specific fine metal colloidal particles, and by blending this into a cosmetic, it provides a cosmetic having a beautiful color without impairing stability. is there.
すなわち、本発明は、平均粒子径１〜６０ｎｍの微粒子金属コロイドを内包した金属酸化物からなることを特徴とする着色複合粉末を提供するものである。 That is, the present invention provides a colored composite powder comprising a metal oxide encapsulating fine metal colloid having an average particle diameter of 1 to 60 nm.
また、本発明は、前記微粒子金属コロイドが金コロイドであり、その内包量が着色複合粉末全量に対して０．１〜１０質量％であることを特徴とする上記の着色複合粉末を提供するものである。 In addition, the present invention provides the above-described colored composite powder, wherein the particulate metal colloid is a gold colloid, and the amount of inclusion is 0.1 to 10% by mass with respect to the total amount of the colored composite powder. It is.
さらに、本発明は、前記金属酸化物が、酸化チタンであることを特徴とする上記の着色複合粉末を提供するものである。 Furthermore, the present invention provides the above-mentioned colored composite powder, wherein the metal oxide is titanium oxide.
また、本発明は、前記着色複合粉末の平均粒子径が０．５〜５μｍであることを特徴とする上記の着色複合粉末を提供するものである。 The present invention also provides the above-described colored composite powder, wherein the colored composite powder has an average particle size of 0.5 to 5 μm.
さらに、本発明は、前記着色複合粉末の色がマンセル色相環で７．５ＰＢ〜２．５Ｇであることを特徴とする上記の着色複合粉末を提供するものである。 Furthermore, the present invention provides the above-described colored composite powder, wherein the colored composite powder has a Munsell hue ring of 7.5 PB to 2.5 G.
また、本発明は、上記の着色複合粉末を、化粧料全量に対して０．１〜５０質量％配合したことを特徴とする化粧料を提供するものである。 Moreover, this invention provides the cosmetics characterized by mix | blending 0.1-50 mass% of said colored composite powder with respect to cosmetics whole quantity.
本発明の着色複合粉末は、化粧料に配合することにより、安定性を損なうことなく鮮やかに発色する。 The colored composite powder of the present invention can be vividly colored without sacrificing stability when blended in cosmetics.
特に、金コロイドを酸化チタンに内包した着色複合粉末は、青色又は緑色に鮮やかに発色し、安定性や使用感にも優れた化粧料を提供できる。
従来、化粧料に配合される青色の無機顔料は群青や紺青等が利用されていたが、安定性に欠ける場合があった。本発明によれば、優れた安定性を有する青色又は緑色顔料を化粧料顔料として提供できることになる。
In particular, a colored composite powder in which colloidal gold is encapsulated in titanium oxide can provide a cosmetic material that is vividly colored in blue or green and has excellent stability and usability.
Conventionally, ultramarine blue and bitumen have been used as blue inorganic pigments to be blended in cosmetics, but there are cases where the stability is lacking. According to the present invention, a blue or green pigment having excellent stability can be provided as a cosmetic pigment.
以下、本発明について詳述する。 Hereinafter, the present invention will be described in detail.
本発明の着色複合粉末は、プラズモン発色を呈する微粒子金属コロイドを内包した金属酸化物である。この微粒子金属コロイドは、一般的な公知な製法、例えば塩化金酸を還元することにより得ることができる。また、分散安定剤で安定化された市販品の微粒子金属コロイドゾルを用いることもできる。好ましい金属コロイドは貴金属コロイドであり、特に金コロイドが好ましい。 The colored composite powder of the present invention is a metal oxide enclosing a fine metal colloid exhibiting plasmon color. The fine particle metal colloid can be obtained by a general known production method, for example, by reducing chloroauric acid. A commercially available fine particle metal colloidal sol stabilized with a dispersion stabilizer can also be used. A preferred metal colloid is a noble metal colloid, and a gold colloid is particularly preferred.
微粒子金属コロイドの平均粒子径は１〜６０ｎｍ、好ましくは５〜３０ｎｍである。粒子径が６０ｎｍを超えると、プラズモン発色効果が失われて特異的な吸収を示さなくなる場合があり、ただの金属色が現れるだけになってしまう。また、１ｎｍ未満のものは製造することが難しかったり、また、安定性が非常に悪くなってその取り扱いが極めて難しくなってしまう。 The average particle diameter of the fine metal colloid is 1 to 60 nm, preferably 5 to 30 nm. If the particle diameter exceeds 60 nm, the plasmon coloring effect may be lost and the specific absorption may not be exhibited, and only a metallic color appears. In addition, it is difficult to produce a material having a thickness of less than 1 nm, and the stability is very poor and the handling thereof is extremely difficult.
微粒子金属コロイドの内包量は、着色複合粉末全量に対して０．１〜１０質量％、好ましくは０．５〜５．０質量％である。０．１質量％未満では色調が薄くなりすぎて鮮やかな外観が得られない。また、１０質量％を超えると、濃度が濃すぎて明度が下がり、やはり鮮やかな外観が得られなくなってしまう。 The amount of the particulate metal colloid is 0.1 to 10% by mass, preferably 0.5 to 5.0% by mass, based on the total amount of the colored composite powder. If it is less than 0.1% by mass, the color tone becomes too thin and a vivid appearance cannot be obtained. On the other hand, if it exceeds 10% by mass, the density is too high and the brightness is lowered, so that a vivid appearance cannot be obtained.
本発明に使用される金属酸化物は、化粧料に用いられる一般的なものを用いることができる。例えば、酸化鉄、黒酸化鉄、黄酸化鉄、酸化チタン、酸化アルミニウム、酸化亜鉛などを用いることができるが、特に酸化チタンが好ましい。 As the metal oxide used in the present invention, a general metal oxide used in cosmetics can be used. For example, iron oxide, black iron oxide, yellow iron oxide, titanium oxide, aluminum oxide, zinc oxide and the like can be used, and titanium oxide is particularly preferable.
本発明の着色複合粉末の製造方法は、微粒子金属コロイドが金属無機酸化物の粒子内に内包される限り限定されないが、金属酸化物の粒子自体を微粒子金属コロイド溶液中にて製造する必要がある。単に金属酸化物の粒子と微粒子金属コロイドとを混合するだけでは、金属酸化物の粒子表面に微粒子金属コロイドが被覆するだけで内包されず、本発明の着色複合粉末は得られない。本発明の着色複合粉末は、微粒子金属コロイドが金属酸化物の粒子内に内包されているので（微粒子金属コロイドが無機酸化物粒子内部に存在している）、微粒子金属コロイドが金属酸化物粒子から容易に分離することがない。これに対して、微粒子金属コロイドがその表面に被覆しただけの金属酸化物粒子の場合は、溶液中にて（特にアルカリ溶液等）、微粒子金属コロイドが溶出したりして分離してしまう。 The method for producing the colored composite powder of the present invention is not limited as long as the fine metal colloid is encapsulated in the metal inorganic oxide particles, but the metal oxide particles themselves must be produced in the fine metal colloid solution. . By simply mixing the metal oxide particles and the fine metal colloids, the metal oxide particles are simply covered with the fine metal colloids and are not encapsulated, and the colored composite powder of the present invention cannot be obtained. In the colored composite powder of the present invention, since the fine metal colloid is encapsulated in the metal oxide particles (the fine metal colloid is present inside the inorganic oxide particles), the fine metal colloid is formed from the metal oxide particles. It does not separate easily. On the other hand, in the case of metal oxide particles in which the surface of the particulate metal colloid is only coated, the particulate metal colloid is eluted or separated in the solution (especially alkaline solution).
具体的な製造方法としては、金属酸化物と同じ種類の金属塩化物又は金属硫酸塩のいずれかの水溶液と塩化金酸水溶液の混合液に還元剤としてエタノール等を加えて、水酸化ナトリウム等のアルカリ性水溶液を徐々に添加して、金属塩化物または金属硫酸塩を加水分解すると同時に塩化金酸を還元して金コロイドを生成させ、得られた粉末を洗浄、乾燥した後、６００℃〜１１００℃で焼成することで得られる。焼成温度により色調を変化させることが可能である。
例えば、平均粒子径１〜６０ｎｍの金微粒子を内包した酸化チタンからなることを特徴とする着色複合粉末を製造するには、四塩化チタンと塩化金酸とエタノールとを水溶液中にて加温しながら攪拌し、水酸化ナトリウムを徐々に添加して四塩化チタンを加水分解すると同時に塩化金酸を還元した後、ろ過、洗浄、乾燥後、７５０℃にて焼成することにより、鮮やかな青色の外観色を有する金コロイド内包酸化チタン粉末が得られる。また、乾燥後の粉末を１０５０℃で焼成することにより鮮やかな緑色の外観色を有する金コロイド内包酸化チタン粉末が得られる。
As a specific manufacturing method, ethanol or the like is added as a reducing agent to a mixed solution of either an aqueous solution of metal chloride or metal sulfate of the same type as the metal oxide and an aqueous chloroauric acid solution, An alkaline aqueous solution is gradually added to hydrolyze the metal chloride or metal sulfate and simultaneously reduce chloroauric acid to form a gold colloid. After washing and drying the obtained powder, 600 ° C to 1100 ° C It is obtained by firing with It is possible to change the color tone depending on the firing temperature.
For example, to produce a colored composite powder comprising titanium oxide containing gold fine particles having an average particle diameter of 1 to 60 nm, titanium tetrachloride, chloroauric acid, and ethanol are heated in an aqueous solution. Stirring, gradually adding sodium hydroxide to hydrolyze titanium tetrachloride and simultaneously reducing chloroauric acid, followed by filtration, washing, drying, and firing at 750 ° C. to give a bright blue appearance A gold colloid-encapsulated titanium oxide powder having a color is obtained. Further, the powder after drying is fired at 1050 ° C. to obtain gold colloid-encapsulated titanium oxide powder having a bright green appearance color.
上記で得られる着色複合粉末において、金コロイドを内包する酸化チタン複合粉末は
は青又は緑に発色し、マンセル色相環で７．５ＰＢ〜２．５Ｇの範囲にあることが特徴である。
In the colored composite powder obtained above, the titanium oxide composite powder encapsulating the gold colloid is colored blue or green and is characterized by having a Munsell hue ring in the range of 7.5 PB to 2.5 G.
上記で得られる着色複合粉末は化粧料配合原料として極めて優れた有色粉末となる。
化粧料への配合量は、化粧料全量に対して０．１〜５０質量％、好ましくは０．５〜２０質量％である。０．１質量％未満では十分な発色効果が得られず、一方、５０質量％を越えると、他の原料を入れる処方幅が非常に狭くなり、粘度、硬度などの製品の物性調整が困難になってしまう。
The colored composite powder obtained above is a colored powder that is extremely excellent as a cosmetic blending raw material.
The compounding quantity to cosmetics is 0.1-50 mass% with respect to cosmetics whole quantity, Preferably it is 0.5-20 mass%. If the amount is less than 0.1% by mass, a sufficient coloring effect cannot be obtained. On the other hand, if the amount exceeds 50% by mass, the prescription width for containing other raw materials becomes very narrow, making it difficult to adjust the physical properties of the product such as viscosity and hardness. turn into.
本発明の着色複合粉末を配合できる化粧料は限定されない。例えば、ファンデーション、アイシャドー、口紅、グロス、マスカラ、アイライナー、ネールエナメル、ネールエナメルベースコート等のメーキャップ化粧料、化粧水、乳液、クリーム等の基礎化粧料、ヘアスプレー、頭髪油などの毛髪化粧料等に、複合粉末を配合して本発明の化粧料が得られる。特に鮮やかな色調を求められるメーキャップ化粧料に好ましい。 Cosmetics that can be blended with the colored composite powder of the present invention are not limited. For example, makeup cosmetics such as foundation, eye shadow, lipstick, gloss, mascara, eyeliner, nail enamel, nail enamel base coat, basic cosmetics such as lotion, milky lotion, cream, hair cosmetics such as hair spray, hair oil Etc., the cosmetic powder of the present invention can be obtained by blending the composite powder. It is particularly preferred for makeup cosmetics that require a vivid color tone.
本発明の化粧料には、本発明の効果を損なわない程度に必要に応じて固体、半固体、液状の油分、水、水溶性高分子、多価アルコール、溶剤、界面活性剤、粉体、樹脂、有機変性粘土鉱物、高分子、紫外線吸収剤、保湿剤、防腐剤、殺菌剤、香料、酸化防止剤、美肌用成分、生理活性成分粉末、顔料、染料、ラメ剤、薬剤、保湿剤、紫外線吸収剤、つや消し剤、充填剤、界面活性剤、金属石鹸等の一般に化粧料に配合される原料を適宜配合して、目的とする化粧料に応じて常法により製造することができる。 The cosmetics of the present invention include solids, semi-solids, liquid oils, water, water-soluble polymers, polyhydric alcohols, solvents, surfactants, powders, as necessary to the extent that the effects of the present invention are not impaired. Resin, organically modified clay mineral, polymer, UV absorber, moisturizer, antiseptic, bactericidal agent, fragrance, antioxidant, skin beautifying component, physiologically active ingredient powder, pigment, dye, lame agent, drug, moisturizer, Raw materials generally blended in cosmetics such as ultraviolet absorbers, matting agents, fillers, surfactants, metal soaps and the like can be blended as appropriate, and can be produced by conventional methods according to the intended cosmetics.
本発明を実施例に基づいてさらに具体的に説明する。本発明は下記の実施例により限定されるものではない。なお、配合量は特に断りのない限り質量％である。 The present invention will be described more specifically based on examples. The present invention is not limited to the following examples. The blending amount is mass% unless otherwise specified.
「実施例１ 微粒子金コロイド内包酸化チタンの製造」
２００ｍｌのイオン交換水中に６０ｇの四塩化チタン溶液（和光純薬工業株式会社製）を添加し、次いで塩化金酸（ナカライテスク株式会社製）０．１６ｇ、エタノール２０ｍＬを入れて加温しながら攪拌し、８３℃付近の一定温度になったら２５％水酸化ナトリウム水溶液を１時間かけて添加した。全量滴下後、更に１時間攪拌し、希塩酸で中和した後、ろ過、洗浄を行い、1０５℃で1時間乾燥させた。次いで７５０℃で１時間焼成を行い、平均粒子径が０．５μm〜１μｍの鮮やかな青色の外観色を持つ０．５質量％金コロイド内包酸化チタン（着色複合粉末Ａ）を得た。
"Example 1 Production of fine particle gold colloid-encapsulated titanium oxide"
60 g of titanium tetrachloride solution (manufactured by Wako Pure Chemical Industries, Ltd.) is added to 200 ml of ion-exchanged water, and then 0.16 g of chloroauric acid (manufactured by Nacalai Tesque) and 20 mL of ethanol are added and stirred while heating. When the temperature reached 83 ° C., a 25% aqueous sodium hydroxide solution was added over 1 hour. After dropping the whole amount, the mixture was further stirred for 1 hour, neutralized with dilute hydrochloric acid, filtered and washed, and dried at 105 ° C. for 1 hour. Subsequently, baking was performed at 750 ° C. for 1 hour to obtain 0.5% by mass of gold colloid-encapsulated titanium oxide (colored composite powder A) having a bright blue appearance color having an average particle diameter of 0.5 μm to 1 μm.
「実施例２ 微粒子金コロイド内包酸化チタンの製造」
２００ｍｌのイオン交換水中に６０ｇの四塩化チタン溶液（和光純薬工業株式会社製）を添加し、次いで塩化金酸（ナカライテスク株式会社製）０．１６ｇ、エタノール２０ｍＬを入れて加温しながら攪拌し、８３℃付近の一定温度になったら２５％水酸化ナトリウム水溶液を１時間かけて添加した。全量滴下後、更に１時間攪拌し、希塩酸で中和した後、ろ過、洗浄を行い、1０５℃で1時間乾燥させた。次いで１０５０℃で１時間焼成を行い、平均粒子径が０．５μm〜１μｍの鮮やかな緑色の外観色を持つ０．５質量％金コロイド内包酸化チタン（着色複合粉末Ｂ）を得た。図１に電子顕微鏡写真を示す。図１の写真から、塊状（球状ではない）の金コロイド内包チタンが得られることが分かる。
"Example 2 Production of fine particle gold colloid-encapsulated titanium oxide"
60 g of titanium tetrachloride solution (manufactured by Wako Pure Chemical Industries, Ltd.) is added to 200 ml of ion-exchanged water, and then 0.16 g of chloroauric acid (manufactured by Nacalai Tesque) and 20 mL of ethanol are added and stirred while heating. When the temperature reached 83 ° C., a 25% aqueous sodium hydroxide solution was added over 1 hour. After dropping the whole amount, the mixture was further stirred for 1 hour, neutralized with dilute hydrochloric acid, filtered and washed, and dried at 105 ° C. for 1 hour. Subsequently, baking was performed at 1050 ° C. for 1 hour to obtain 0.5% by mass of gold colloid-encapsulated titanium oxide (colored composite powder B) having a bright green appearance color with an average particle diameter of 0.5 μm to 1 μm. FIG. 1 shows an electron micrograph. From the photograph of FIG. 1, it can be seen that massive (not spherical) gold colloid-containing titanium is obtained.
実施例１の着色複合粉末Ａ及び実施例２の着色複合粉末Ｂをそれぞれビニール袋に取り、ビニール袋の上から複合粉末の色を分光測色計（ＣＭ−２６００ｄ、ミノルタ製）で測色したところ、マンセル色相環で、着色複合粉末Ａは５．６ＰＢ、着色複合粉末Ｂは９．０Ｇであった。 The colored composite powder A of Example 1 and the colored composite powder B of Example 2 were each taken in a plastic bag, and the color of the composite powder was measured from the top of the plastic bag with a spectrocolorimeter (CM-2600d, manufactured by Minolta). In the Munsell hue ring, the colored composite powder A was 5.6 PB, and the colored composite powder B was 9.0 G.
次に、本発明の化粧料の実施例を挙げる。いずれの化粧料も本発明の着色複合粉末を配合して常法により製造される。 Next, examples of the cosmetic of the present invention will be given. All cosmetics are produced by a conventional method by blending the colored composite powder of the present invention.
「実施例３：マスカラ」
着色複合粉末Ａ（実施例１） 0.5
軽質イソパラフィン 7
ジメチルポリシロキサン 2
デカメチルシクロペンタシロキサン 10
トリメチルシロキシケイ酸 10
メチルポリシロキサンエマルション 適量
１，３−ブチレングリコール 4
ジオレイン酸ポリエチレングリコール 2
ジイソステアリン酸ジグリセリル 2
炭酸水素ナトリウム 0.2
酢酸DL−α−トコフェロール 0.1
パラオキシ安息香酸エステル 適量
デヒドロ酢酸ナトリウム 適量
黒酸化鉄 7
海藻エキス 0.1
ベントナイト 1
ジメチルジステアリルアンモニウムヘクトライト 6
ポリ酢酸ビニルエマルション 30
精製水 残量
上記で得られる本発明のマスカラは、塗布時の仕上がりに優れ、美しい色彩に彩られたメーキャップ効果を有する。
"Example 3: Mascara"
Colored composite powder A (Example 1) 0.5
Light isoparaffin 7
Dimethylpolysiloxane 2
Decamethylcyclopentasiloxane 10
Trimethylsiloxysilicate 10
Methyl polysiloxane emulsion Appropriate amount 1,3-butylene glycol 4
Dioleic acid polyethylene glycol 2
Diglyceryl diisostearate 2
Sodium bicarbonate 0.2
DL-α-tocopherol acetate 0.1
P-Hydroxybenzoate appropriate amount sodium dehydroacetate appropriate amount black iron oxide 7
Seaweed extract 0.1
Bentonite 1
Dimethyl distearyl ammonium hectorite 6
Polyvinyl acetate emulsion 30
Purified water remaining
The mascara of the present invention obtained above is excellent in the finish upon application and has a makeup effect colored in a beautiful color.
「実施例４：口紅」
着色複合粉末Ａ（実施例１） 5
固形パラフィン 11
カルナバロウ 2
トリ−２−エチルヘキサン酸グリセリル 残量
セスキオレイン酸ソルビタン 1
酸化チタン 5
雲母チタン 12
マイカ 17
黒酸化鉄 1
上記で得られる本発明の口紅は、塗布時の仕上がりに優れ、美しい色彩に彩られたメーキャップ効果を有する。
"Example 4: Lipstick"
Colored composite powder A (Example 1) 5
Solid paraffin 11
Carnavalou 2
Glyceryl tri-2-ethylhexanoate Remaining sorbitan sesquioleate 1
Titanium oxide 5
Mica titanium 12
Mica 17
Black iron oxide 1
The lipstick of the present invention obtained above is excellent in finish at the time of application and has a makeup effect colored in a beautiful color.
「実施例５ アイシャドー」
着色複合粉末Ｂ（実施例２） 4
流動パラフィン 3
ジメチルポリシロキサン 3
マイカ 20
タルク 残余
δ−トコフェロール 適量
パラオキシ安息香酸エステル 0.2
色素 4
ケイ酸アルミニウムマグネシウム 1.5
香料 適量
セリサイト 20
セスキイソステアリン酸ソルビタン 2
ミリスチン酸亜鉛 5
上記で得られる本発明のアイシャドーは、塗布時の仕上がりに優れ、美しい色彩に彩られたメーキャップ効果を有する。
"Example 5 eye shadow"
Colored composite powder B (Example 2) 4
Liquid paraffin 3
Dimethylpolysiloxane 3
Mica 20
Talc Residual δ-Tocopherol Appropriate amount Paraoxybenzoate 0.2
Dye 4
Aluminum magnesium silicate 1.5
Fragrance Appropriate amount Sericite 20
Sorbitan sesquiisostearate 2
Zinc myristate 5
The eye shadow of the present invention obtained above is excellent in the finish at the time of application and has a makeup effect colored in a beautiful color.
「実施例６：ネールエナメル」
着色複合粉末Ａ（実施例１） 2
ブタノール 0.5
マカデミアナッツ油 0.1
酢酸エチル 7
酢酸ブチル 残余
ポリオキシエチレンアルキル（１２−１５）エーテルリン酸（２Ｅ．Ｏ．） 0.1
塩化ポリオキシプロピレンメチルジエチルアンモニウム 0.5
酸化チタン被覆合成金雲母 0.1
合成金雲母 0.1
ステアリン酸カルシウム 0.05
クエン酸 0.01
酢酸ＤＬ−α−トコフェロール 0.1
酸化チタン・無水ケイ酸複合被覆マイカ（ブルー） 適量
黒酸化鉄 適量
赤色２０２号 適量
黄色４号 適量
青色４０４号 適量
ポリエチレンテレフタレート・ポリエチレンイソフタレート積層末 0.2
（角八魚鱗箔社製ＮＥＷオーロラフレーク０．１：粒径150μｍ）
トリメリト酸系アルキッド樹脂 12
ジメチルジステアリルアンモニウムベントナイト 0.5
ベンジルジメチルステアリルアンモニウムベントナイト 1
ニトロセルロース 17
安息香酸ショ糖エステル 2
クエン酸アセチルトリブチル 5
上記で得られる本発明のネールエナメルは塗布時の仕上がりに優れ、美しい色彩に彩られたメーキャップ効果を有する。
"Example 6: Nail enamel"
Colored composite powder A (Example 1) 2
Butanol 0.5
Macadamia nut oil 0.1
Ethyl acetate 7
Butyl acetate Residual polyoxyethylene alkyl (12-15) ether phosphoric acid (2EO) 0.1
Polyoxypropylene methyl diethylammonium chloride 0.5
Titanium oxide coated synthetic phlogopite 0.1
Synthetic phlogopite 0.1
Calcium stearate 0.05
Citric acid 0.01
DL-α-tocopherol acetate 0.1
Titanium oxide / silicic acid composite coated mica (blue) Appropriate amount of black iron oxide Appropriate amount of red No. 202 Appropriate amount of yellow No. 4 Appropriate amount of blue No. 404 Appropriate amount Polyethylene terephthalate / polyethylene isophthalate laminated powder 0.2
(NEW Aurora Flakes 0.1: particle size 150 μm, manufactured by Kakuhachi Fish Scale)
Trimellitic acid alkyd resin 12
Dimethyl distearyl ammonium bentonite 0.5
Benzyldimethylstearylammonium bentonite 1
Nitrocellulose 17
Benzoic acid sucrose ester 2
Acetyl tributyl citrate 5
The nail enamel of the present invention obtained above is excellent in the finish upon application and has a makeup effect colored in a beautiful color.
本発明によれば、微粒子金属コロイドを内包した金属酸化物からなる着色複合粉末を、ファンデーション、アイシャドー、口紅、グロス、マスカラ、アイライナー、ネールエナメル、ネールエナメルオーバーコート、ネールエナメルベースコート、クリーム、乳液等の化粧料に配合することにより、安定性に優れかつ鮮やかな有色外観を有する化粧料を提供できる。 According to the present invention, a colored composite powder composed of a metal oxide encapsulating a particulate metal colloid is applied to a foundation, eye shadow, lipstick, gloss, mascara, eyeliner, nail enamel, nail enamel overcoat, nail enamel base coat, cream, By blending into a cosmetic such as an emulsion, a cosmetic having excellent stability and a vivid colored appearance can be provided.
Claims (6)
A cosmetic comprising 0.1 to 50% by mass of the colored composite powder according to claim 1, 2, 3, 4 or 5 based on the total amount of the cosmetic.