JP2004051830A - Curable composition - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a curable composition which can ensure good workability without largely increasing the viscosity, can be filled without largely deteriorating the mechanical physical properties, and contains a cross-linkable functional group-containing vinylic polymer. <P>SOLUTION: This curable composition comprises a vinylic polymer having at least one cross-linkable silyl group and silica having an average particle diameter of 1 to 500μm. The mol. wt. distribution of the vinylic polymer is preferably <1.8. The vinylic polymer is preferably a polymer produced by mainly polymerizing a monomer selected from the group consisting of (meth)acrylic monomers, acrylonitrile-based monomers, aromatic vinyl-based monomers, fluorine-containing vinylic monomers and silicon-containing vinylic monomers. <P>COPYRIGHT: (C)2004,JPO

Description

アルコキシアミン化合物を開始剤として用いる場合、それが上図で示されているような水酸基等の官能基を有するものを用いると、末端に官能基を有する重合体が得られる。これを本発明の方法に利用すると、末端に官能基を有する重合体が得られる。
【００４３】
上記のニトロキシド化合物などのラジカル捕捉剤を用いる重合で用いられるモノマー、溶媒、重合温度等の重合条件は、限定されないが、次に説明する原子移動ラジカル重合について用いるものと同様で構わない。
原子移動ラジカル重合
次に、本発明のリビングラジカル重合としてより好ましい原子移動ラジカル重合法について説明する。
【００４４】
この原子移動ラジカル重合では、有機ハロゲン化物、特に反応性の高い炭素−ハロゲン結合を有する有機ハロゲン化物（例えば、α位にハロゲンを有するカルボニル化合物や、ベンジル位にハロゲンを有する化合物）、あるいはハロゲン化スルホニル化合物等が開始剤として用いられる。
具体的に例示するならば、
Ｃ_６Ｈ_５−ＣＨ_２Ｘ、Ｃ_６Ｈ_５−Ｃ（Ｈ）（Ｘ）ＣＨ_３、Ｃ_６Ｈ_５−Ｃ（Ｘ）（ＣＨ_３）_２（ただし、上の化学式中、Ｃ_６Ｈ_５はフェニル基、Ｘは塩素、臭素、またはヨウ素）
Ｒ^１−Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ^２、Ｒ^１−Ｃ（ＣＨ_３）（Ｘ）−ＣＯ_２Ｒ^２、Ｒ^１−Ｃ（Ｈ）（Ｘ）−Ｃ（Ｏ）Ｒ^２、Ｒ^１−Ｃ（ＣＨ_３）（Ｘ）−Ｃ（Ｏ）Ｒ^２、
（式中、Ｒ^１、Ｒ^２は水素原子または炭素数１〜２０のアルキル基、アリール基、またはアラルキル基、Ｘは塩素、臭素、またはヨウ素）
Ｒ^１−Ｃ_６Ｈ_４−ＳＯ_２Ｘ
（式中、Ｒ^１は水素原子または炭素数１〜２０のアルキル基、アリール基、またはアラルキル基、Ｘは塩素、臭素、またはヨウ素）
等が挙げられる。
【００４５】
原子移動ラジカル重合の開始剤として、重合を開始する官能基以外の官能基を有する有機ハロゲン化物又はハロゲン化スルホニル化合物を用いることもできる。このような場合、一方の主鎖末端に官能基を、他方の主鎖末端に原子移動ラジカル重合の生長末端構造を有するビニル系重合体が製造される。このような官能基としては、アルケニル基、架橋性シリル基、ヒドロキシル基、エポキシ基、アミノ基、アミド基等が挙げられる。
【００４６】
アルケニル基を有する有機ハロゲン化物としては限定されず、例えば、一般式（１）に示す構造を有するものが例示される。
Ｒ^４Ｒ^５Ｃ（Ｘ）−Ｒ^６−Ｒ^７−Ｃ（Ｒ^３）＝ＣＨ_２　（１）
（式中、Ｒ^３は水素、またはメチル基、Ｒ^４、Ｒ^５は水素、または、炭素数１〜２０の１価のアルキル基、アリール基、またはアラルキル基、または他端において相互に連結したもの、Ｒ^６は、−Ｃ（Ｏ）Ｏ−（エステル基）、−Ｃ（Ｏ）−（ケト基）、またはｏ−，ｍ−，ｐ−フェニレン基、Ｒ^７は直接結合、または炭素数１〜２０の２価の有機基で１個以上のエーテル結合を含んでいても良い、Ｘは塩素、臭素、またはヨウ素）
置換基Ｒ^４、Ｒ^５の具体例としては、水素、メチル基、エチル基、ｎ−プロピル基、イソプロピル基、ブチル基、ペンチル基、ヘキシル基等が挙げられる。Ｒ^４とＲ^５は他端において連結して環状骨格を形成していてもよい。
【００４７】
一般式（１）で示される、アルケニル基を有する有機ハロゲン化物の具体例としては、
ＸＣＨ_２Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＣＨ＝ＣＨ_２、Ｈ_３ＣＣ（Ｈ）（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＣＨ＝ＣＨ_２、（Ｈ_３Ｃ）_２Ｃ（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＣＨ＝ＣＨ_２、ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＣＨ＝ＣＨ_２、
【００４８】
【化２】

（上記の各式において、Ｘは塩素、臭素、またはヨウ素、ｎは０〜２０の整数）
ＸＣＨ_２Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＯ（ＣＨ_２）_ｍＣＨ＝ＣＨ_２、Ｈ_３ＣＣ（Ｈ）（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＯ（ＣＨ_２）_ｍＣＨ＝ＣＨ_２、（Ｈ_３Ｃ）_２Ｃ（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＯ（ＣＨ_２）_ｍＣＨ＝ＣＨ_２、ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＯ（ＣＨ_２）_ｍＣＨ＝ＣＨ_２、
【００４９】
【化３】

（上記の各式において、Ｘは塩素、臭素、またはヨウ素、ｎは１〜２０の整数、ｍは０〜２０の整数）
ｏ，ｍ，ｐ−ＸＣＨ_２−Ｃ_６Ｈ_４−（ＣＨ_２）_ｎ−ＣＨ＝ＣＨ_２、ｏ，ｍ，ｐ−ＣＨ_３Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−（ＣＨ_２）_ｎ−ＣＨ＝ＣＨ_２、ｏ，ｍ，ｐ−ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−（ＣＨ_２）_ｎ−ＣＨ＝ＣＨ_２、
（上記の各式において、Ｘは塩素、臭素、またはヨウ素、ｎは０〜２０の整数）
ｏ，ｍ，ｐ−ＸＣＨ_２−Ｃ_６Ｈ_４−（ＣＨ_２）_ｎ−Ｏ−（ＣＨ_２）_ｍ−ＣＨ＝ＣＨ_２、ｏ，ｍ，ｐ−ＣＨ_３Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−（ＣＨ_２）_ｎ−Ｏ−（ＣＨ_２）_ｍ−ＣＨ＝ＣＨ_２、ｏ，ｍ，ｐ−ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−（ＣＨ_２）_ｎ−Ｏ−（ＣＨ_２）_ｍＣＨ＝ＣＨ_２、
（上記の各式において、Ｘは塩素、臭素、またはヨウ素、ｎは１〜２０の整数、ｍは０〜２０の整数）
ｏ，ｍ，ｐ−ＸＣＨ_２−Ｃ_６Ｈ_４−Ｏ−（ＣＨ_２）_ｎ−ＣＨ＝ＣＨ_２、ｏ，ｍ，ｐ−ＣＨ_３Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−Ｏ−（ＣＨ_２）_ｎ−ＣＨ＝ＣＨ_２、ｏ，ｍ，ｐ−ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−Ｏ−（ＣＨ_２）_ｎ−ＣＨ＝ＣＨ_２、
（上記の各式において、Ｘは塩素、臭素、またはヨウ素、ｎは０〜２０の整数）
ｏ，ｍ，ｐ−ＸＣＨ_２−Ｃ_６Ｈ_４−Ｏ−（ＣＨ_２）_ｎ−Ｏ−（ＣＨ_２）_ｍ−ＣＨ＝ＣＨ_２、ｏ，ｍ，ｐ−ＣＨ_３Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−Ｏ−（ＣＨ_２）_ｎ−Ｏ−（ＣＨ_２）_ｍ−ＣＨ＝ＣＨ_２、ｏ，ｍ，ｐ−ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−Ｏ−（ＣＨ_２）_ｎ−Ｏ−（ＣＨ_２）_ｍ−ＣＨ＝ＣＨ_２、
（上記の各式において、Ｘは塩素、臭素、またはヨウ素、ｎは１〜２０の整数、ｍは０〜２０の整数）
アルケニル基を有する有機ハロゲン化物としてはさらに一般式（２）で示される化合物が挙げられる。
Ｈ_２Ｃ＝Ｃ（Ｒ^３）−Ｒ^７−Ｃ（Ｒ^４）（Ｘ）−Ｒ^８−Ｒ^５　（２）
（式中、Ｒ^３、Ｒ^４、Ｒ^５、Ｒ^７、Ｘは上記に同じ、Ｒ^８は、直接結合、−Ｃ（Ｏ）Ｏ−（エステル基）、−Ｃ（Ｏ）−（ケト基）、または、ｏ−，ｍ−，ｐ−フェニレン基を表す）
Ｒ^７は直接結合、または炭素数１〜２０の２価の有機基（１個以上のエーテル結合を含んでいても良い）であるが、直接結合である場合は、ハロゲンの結合している炭素にビニル基が結合しており、ハロゲン化アリル化物である。この場合は、隣接ビニル基によって炭素−ハロゲン結合が活性化されているので、Ｒ^８としてＣ（Ｏ）Ｏ基やフェニレン基等を有する必要は必ずしもなく、直接結合であってもよい。Ｒ^７が直接結合でない場合は、炭素−ハロゲン結合を活性化するために、Ｒ^８としてはＣ（Ｏ）Ｏ基、Ｃ（Ｏ）基、フェニレン基が好ましい。
【００５０】
一般式（２）の化合物を具体的に例示するならば、
ＣＨ_２＝ＣＨＣＨ_２Ｘ、ＣＨ_２＝Ｃ（ＣＨ_３）ＣＨ_２Ｘ、ＣＨ_２＝ＣＨＣ（Ｈ）（Ｘ）ＣＨ_３、ＣＨ_２＝Ｃ（ＣＨ_３）Ｃ（Ｈ）（Ｘ）ＣＨ_３、ＣＨ_２＝ＣＨＣ（Ｘ）（ＣＨ_３）_２、ＣＨ_２＝ＣＨＣ（Ｈ）（Ｘ）Ｃ_２Ｈ_５、ＣＨ_２＝ＣＨＣ（Ｈ）（Ｘ）ＣＨ（ＣＨ_３）_２、ＣＨ_２＝ＣＨＣ（Ｈ）（Ｘ）Ｃ_６Ｈ_５、ＣＨ_２＝ＣＨＣ（Ｈ）（Ｘ）ＣＨ_２Ｃ_６Ｈ_５、ＣＨ_２＝ＣＨＣＨ_２Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ、ＣＨ_２＝ＣＨ（ＣＨ_２）_２Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ、ＣＨ_２＝ＣＨ（ＣＨ_２）_３Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ、ＣＨ_２＝ＣＨ（ＣＨ_２）_８Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ、ＣＨ_２＝ＣＨＣＨ_２Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_５、ＣＨ_２＝ＣＨ（ＣＨ_２）_２Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_５、ＣＨ_２＝ＣＨ（ＣＨ_２）_３Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_５、
（上記の各式において、Ｘは塩素、臭素、またはヨウ素、Ｒは炭素数１〜２０のアルキル基、アリール基、アラルキル基）
等を挙げることができる。
【００５１】
アルケニル基を有するハロゲン化スルホニル化合物の具体例を挙げるならば、ｏ−，ｍ−，ｐ−ＣＨ_２＝ＣＨ−（ＣＨ_２）_ｎ−Ｃ_６Ｈ_４−ＳＯ_２Ｘ、ｏ−，ｍ−，ｐ−ＣＨ_２＝ＣＨ−（ＣＨ_２）_ｎ−Ｏ−Ｃ_６Ｈ_４−ＳＯ_２Ｘ、
（上記の各式において、Ｘは塩素、臭素、またはヨウ素、ｎは０〜２０の整数）
等である。
【００５２】
上記架橋性シリル基を有する有機ハロゲン化物としては特に限定されず、例えば一般式（３）に示す構造を有するものが例示される。
Ｒ^４Ｒ^５Ｃ（Ｘ）−Ｒ^６−Ｒ^７−Ｃ（Ｈ）（Ｒ^３）ＣＨ_２−［Ｓｉ（Ｒ^９）_２−ｂ（Ｙ）_ｂＯ］_ｍ−Ｓｉ（Ｒ^１０）_３−ａ（Ｙ）_ａ　（３）
（式中、Ｒ^３、Ｒ^４、Ｒ^５、Ｒ^６、Ｒ^７、Ｘは上記に同じ、Ｒ^９、Ｒ^１０は、いずれも炭素数１〜２０のアルキル基、アリール基、アラルキル基、または（Ｒ’）_３ＳｉＯ−（Ｒ’は炭素数１〜２０の１価の炭化水素基であって、３個のＲ’は同一であってもよく、異なっていてもよい）で示されるトリオルガノシロキシ基を示し、Ｒ^９またはＲ^１０が２個以上存在するとき、それらは同一であってもよく、異なっていてもよい。Ｙは水酸基または加水分解性基を示し、Ｙが２個以上存在するときそれらは同一であってもよく、異なっていてもよい。ａは０，１，２，または３を、また、ｂは０，１，または２を示す。ｍは０〜１９の整数である。ただし、ａ＋ｍｂ≧１であることを満足するものとする）
一般式（３）の化合物を具体的に例示するならば、
ＸＣＨ_２Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＳｉ（ＯＣＨ_３）_３、ＣＨ_３Ｃ（Ｈ）（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＳｉ（ＯＣＨ_３）_３、（ＣＨ_３）_２Ｃ（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＳｉ（ＯＣＨ_３）_３、ＸＣＨ_２Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＳｉ（ＣＨ_３）（ＯＣＨ_３）_２、ＣＨ_３Ｃ（Ｈ）（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＳｉ（ＣＨ_３）（ＯＣＨ_３）_２、（ＣＨ_３）_２Ｃ（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＳｉ（ＣＨ_３）（ＯＣＨ_３）_２、
（上記の各式において、Ｘは塩素、臭素、ヨウ素、ｎは０〜２０の整数、）
ＸＣＨ_２Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＯ（ＣＨ_２）_ｍＳｉ（ＯＣＨ_３）_３、Ｈ_３ＣＣ（Ｈ）（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＯ（ＣＨ_２）_ｍＳｉ（ＯＣＨ_３）_３、（Ｈ_３Ｃ）_２Ｃ（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＯ（ＣＨ_２）_ｍＳｉ（ＯＣＨ_３）_３、ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＯ（ＣＨ_２）_ｍＳｉ（ＯＣＨ_３）_３、ＸＣＨ_２Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＯ（ＣＨ_２）_ｍＳｉ（ＣＨ_３）（ＯＣＨ_３）_２、Ｈ_３ＣＣ（Ｈ）（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＯ（ＣＨ_２）_ｍ−Ｓｉ（ＣＨ_３）（ＯＣＨ_３）_２、（Ｈ_３Ｃ）_２Ｃ（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＯ（ＣＨ_２）_ｍ−Ｓｉ（ＣＨ_３）（ＯＣＨ_３）_２、ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）Ｃ（Ｏ）Ｏ（ＣＨ_２）_ｎＯ（ＣＨ_２）_ｍ−Ｓｉ（ＣＨ_３）（ＯＣＨ_３）_２、
（上記の各式において、Ｘは塩素、臭素、ヨウ素、ｎは１〜２０の整数、ｍは０〜２０の整数）
ｏ，ｍ，ｐ−ＸＣＨ_２−Ｃ_６Ｈ_４−（ＣＨ_２）_２Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＣＨ_３Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−（ＣＨ_２）_２Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−（ＣＨ_２）_２Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＸＣＨ_２−Ｃ_６Ｈ_４−（ＣＨ_２）_３Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＣＨ_３Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−（ＣＨ_２）_３Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−（ＣＨ_２）_３Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＸＣＨ_２−Ｃ_６Ｈ_４−（ＣＨ_２）_２−Ｏ−（ＣＨ_２）_３Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＣＨ_３Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−（ＣＨ_２）_２−Ｏ−（ＣＨ_２）_３Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−（ＣＨ_２）_２−Ｏ−（ＣＨ_２）_３Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＸＣＨ_２−Ｃ_６Ｈ_４−Ｏ−（ＣＨ_２）_３Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＣＨ_３Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−Ｏ−（ＣＨ_２）_３Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−Ｏ−（ＣＨ_２）_３−Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＸＣＨ_２−Ｃ_６Ｈ_４−Ｏ−（ＣＨ_２）_２−Ｏ−（ＣＨ_２）_３−Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＣＨ_３Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−Ｏ−（ＣＨ_２）_２−Ｏ−（ＣＨ_２）_３Ｓｉ（ＯＣＨ_３）_３、ｏ，ｍ，ｐ−ＣＨ_３ＣＨ_２Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_４−Ｏ−（ＣＨ_２）_２−Ｏ−（ＣＨ_２）_３Ｓｉ（ＯＣＨ_３）_３、
（上記の各式において、Ｘは塩素、臭素、またはヨウ素）
等が挙げられる。
【００５３】
上記架橋性シリル基を有する有機ハロゲン化物としてはさらに、一般式（４）で示される構造を有するものが例示される。
（Ｒ^１０）_３−ａ（Ｙ）_ａＳｉ−［ＯＳｉ（Ｒ^９）_２−ｂ（Ｙ）_ｂ］_ｍ−ＣＨ_２−Ｃ（Ｈ）（Ｒ^３）−Ｒ^７−Ｃ（Ｒ^４）（Ｘ）−Ｒ^８−Ｒ^５　（４）
（式中、Ｒ^３、Ｒ^４、Ｒ^５、Ｒ^７、Ｒ^８、Ｒ^９、Ｒ^１０、ａ、ｂ、ｍ、Ｘ、Ｙは上記に同じ）
このような化合物を具体的に例示するならば、
（ＣＨ_３Ｏ）_３ＳｉＣＨ_２ＣＨ_２Ｃ（Ｈ）（Ｘ）Ｃ_６Ｈ_５、（ＣＨ_３Ｏ）_２（ＣＨ_３）ＳｉＣＨ_２ＣＨ_２Ｃ（Ｈ）（Ｘ）Ｃ_６Ｈ_５、（ＣＨ_３Ｏ）_３Ｓｉ（ＣＨ_２）_２Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ、（ＣＨ_３Ｏ）_２（ＣＨ_３）Ｓｉ（ＣＨ_２）_２Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ、（ＣＨ_３Ｏ）_３Ｓｉ（ＣＨ_２）_３Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ、（ＣＨ_３Ｏ）_２（ＣＨ_３）Ｓｉ（ＣＨ_２）_３Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ、（ＣＨ_３Ｏ）_３Ｓｉ（ＣＨ_２）_４Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ、（ＣＨ_３Ｏ）_２（ＣＨ_３）Ｓｉ（ＣＨ_２）_４Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ、（ＣＨ_３Ｏ）_３Ｓｉ（ＣＨ_２）_９Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ、（ＣＨ_３Ｏ）_２（ＣＨ_３）Ｓｉ（ＣＨ_２）_９Ｃ（Ｈ）（Ｘ）−ＣＯ_２Ｒ、（ＣＨ_３Ｏ）_３Ｓｉ（ＣＨ_２）_３Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_５、（ＣＨ_３Ｏ）_２（ＣＨ_３）Ｓｉ（ＣＨ_２）_３Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_５、（ＣＨ_３Ｏ）_３Ｓｉ（ＣＨ_２）_４Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_５、（ＣＨ_３Ｏ）_２（ＣＨ_３）Ｓｉ（ＣＨ_２）_４Ｃ（Ｈ）（Ｘ）−Ｃ_６Ｈ_５、
（上記の各式において、Ｘは塩素、臭素、またはヨウ素、Ｒは炭素数１〜２０のアルキル基、アリール基、アラルキル基）
等が挙げられる。
【００５４】
上記ヒドロキシル基を持つ有機ハロゲン化物、またはハロゲン化スルホニル化合物としては特に限定されず、下記のようなものが例示される。
ＨＯ−（ＣＨ_２）_ｎ−ＯＣ（Ｏ）Ｃ（Ｈ）（Ｒ）（Ｘ）
（式中、Ｘは塩素、臭素、またはヨウ素、Ｒは水素原子または炭素数１〜２０のアルキル基、アリール基、アラルキル基、ｎは１〜２０の整数）
上記アミノ基を持つ有機ハロゲン化物、またはハロゲン化スルホニル化合物としては特に限定されず、下記のようなものが例示される。
Ｈ_２Ｎ−（ＣＨ_２）_ｎ−ＯＣ（Ｏ）Ｃ（Ｈ）（Ｒ）（Ｘ）
（式中、Ｘは塩素、臭素、またはヨウ素、Ｒは水素原子または炭素数１〜２０のアルキル基、アリール基、アラルキル基、ｎは１〜２０の整数）
上記エポキシ基を持つ有機ハロゲン化物、またはハロゲン化スルホニル化合物としては特に限定されず、下記のようなものが例示される。
【００５５】
【化４】

（式中、Ｘは塩素、臭素、またはヨウ素、Ｒは水素原子または炭素数１〜２０のアルキル基、アリール基、アラルキル基、ｎは１〜２０の整数）
生長末端構造を１分子内に２つ以上有する重合体を得るためには、２つ以上の開始点を持つ有機ハロゲン化物、またはハロゲン化スルホニル化合物を開始剤として用いるのが好ましい。具体的に例示するならば、
【００５６】
【化５】

【００５７】
【化６】

等が挙げられる。
【００５８】
この重合において用いられるビニル系モノマーとしては特に制約はなく、既に例示したものをすべて好適に用いることができる。
【００５９】
重合触媒として用いられる遷移金属錯体としては特に限定されないが、好ましくは周期律表第７族、８族、９族、１０族、または１１族元素を中心金属とする金属錯体である。更に好ましいものとして、０価の銅、１価の銅、２価のルテニウム、２価の鉄又は２価のニッケルの錯体が挙げられる。なかでも、銅の錯体が好ましい。１価の銅化合物を具体的に例示するならば、塩化第一銅、臭化第一銅、ヨウ化第一銅、シアン化第一銅、酸化第一銅、過塩素酸第一銅等である。銅化合物を用いる場合、触媒活性を高めるために２，２′−ビピリジル及びその誘導体、１，１０−フェナントロリン及びその誘導体、テトラメチルエチレンジアミン、ペンタメチルジエチレントリアミン、ヘキサメチルトリス（２−アミノエチル）アミン等のポリアミン等の配位子が添加される。好ましい配位子は、含窒素化合物であり、より好ましい配位子は、キレート型含窒素化合物であり、さらに好ましい配位子は、Ｎ，Ｎ，Ｎ’，Ｎ”，Ｎ”−ペンタメチルジエチレントリアミンである。また、２価の塩化ルテニウムのトリストリフェニルホスフィン錯体（ＲｕＣｌ_２（ＰＰｈ_３）_３）も触媒として好適である。ルテニウム化合物を触媒として用いる場合は、活性化剤としてアルミニウムアルコキシド類が添加される。更に、２価の鉄のビストリフェニルホスフィン錯体（ＦｅＣｌ_２（ＰＰｈ_３）_２）、２価のニッケルのビストリフェニルホスフィン錯体（ＮｉＣｌ_２（ＰＰｈ_３）_２）、及び、２価のニッケルのビストリブチルホスフィン錯体（ＮｉＢｒ_２（ＰＢｕ_３）_２）も、触媒として好適である。
【００６０】
重合は無溶剤または各種の溶剤中で行なうことができる。溶剤の種類としては、ベンゼン、トルエン等の炭化水素系溶媒、ジエチルエーテル、テトラヒドロフラン等のエーテル系溶媒、塩化メチレン、クロロホルム等のハロゲン化炭化水素系溶媒、アセトン、メチルエチルケトン、メチルイソブチルケトン等のケトン系溶媒、メタノール、エタノール、プロパノール、イソプロパノール、ｎ−ブチルアルコール、ｔｅｒｔ−ブチルアルコール等のアルコール系溶媒、アセトニトリル、プロピオニトリル、ベンゾニトリル等のニトリル系溶媒、酢酸エチル、酢酸ブチル等のエステル系溶媒、エチレンカーボネート、プロピレンカーボネート等のカーボネート系溶媒等が挙げられ、単独または２種以上を混合して用いることができる。
【００６１】
また、限定はされないが、重合は０℃〜２００℃の範囲で行うことができ、好ましくは５０〜１５０℃である。
【００６２】
本発明の原子移動ラジカル重合には、いわゆるリバース原子移動ラジカル重合も含まれる。リバース原子移動ラジカル重合とは、通常の原子移動ラジカル重合触媒がラジカルを発生させた時の高酸化状態、例えば、Ｃｕ（Ｉ）を触媒として用いた時のＣｕ（ＩＩ’）に対し、過酸化物等の一般的なラジカル開始剤を作用させ、その結果として原子移動ラジカル重合と同様の平衡状態を生み出す方法である（Ｍａｃｒｏｍｏｌｅｃｕｌｅｓ　１９９９，３２，２８７２参照）。
＜官能基＞
架橋性官能基の数
ビニル系重合体（Ｉ）の架橋性官能基の数は、特に限定されないが、組成物の硬化性、及び硬化物の物性の観点から、平均して１個以上有することが好ましく、より好ましくは１．１個以上４．０以下、さらに好ましくは１．２個以上３．５個以下である。
架橋性官能基の位置
本発明の硬化性組成物を硬化させてなる硬化物にゴム的な性質が特に要求される場合には、ゴム弾性に大きな影響を与える架橋点間分子量が大きくとれるため、架橋性官能基の少なくとも１個は分子鎖の末端にあることが好ましい。より好ましくは、全ての架橋性官能基を分子鎖末端に有するものである。
【００６３】
上記架橋性官能基を分子末端に少なくとも１個有するビニル系重合体、中でも（メタ）アクリル系重合体を製造する方法は、特公平３−１４０６８号公報、特公平４−５５４４４号公報、特開平６−２１１９２２号公報等に開示されている。しかしながらこれらの方法は上記「連鎖移動剤法」を用いたフリーラジカル重合法であるので、得られる重合体は、架橋性官能基を比較的高い割合で分子鎖末端に有する一方で、Ｍｗ／Ｍｎで表される分子量分布の値が一般に２以上と大きく、粘度が高くなるという問題を有している。従って、分子量分布が狭く、粘度の低いビニル系重合体であって、高い割合で分子鎖末端に架橋性官能基を有するビニル系重合体を得るためには、上記「リビングラジカル重合法」を用いることが好ましい。
【００６４】
以下にこれらの官能基について説明する。
架橋性シリル基
本発明の架橋性シリル基としては、一般式（５）；
−［Ｓｉ（Ｒ^９）_２−ｂ（Ｙ）_ｂＯ］_ｍ−Ｓｉ（Ｒ^１０）_３−ａ（Ｙ）_ａ　（５）
｛式中、Ｒ^９、Ｒ^１０は、いずれも炭素数１〜２０のアルキル基、炭素数６〜２０のアリール基、炭素数７〜２０のアラルキル基、または（Ｒ’）_３ＳｉＯ−（Ｒ’は炭素数１〜２０の１価の炭化水素基であって、３個のＲ’は同一であってもよく、異なっていてもよい）で示されるトリオルガノシロキシ基を示し、Ｒ^９またはＲ^１０が２個以上存在するとき、それらは同一であってもよく、異なっていてもよい。Ｙは水酸基または加水分解性基を示し、Ｙが２個以上存在するときそれらは同一であってもよく、異なっていてもよい。ａは０，１，２，または３を、また、ｂは０，１，または２を示す。ｍは０〜１９の整数である。ただし、ａ＋ｍｂ≧１であることを満足するものとする。｝
で表される基があげられる。
【００６５】
加水分解性基としては、たとえば、水素原子、アルコキシ基、アシルオキシ基、ケトキシメート基、アミノ基、アミド基、アミノオキシ基、メルカプト基、アルケニルオキシ基などの一般に使用されている基があげられる。これらのうちでは、アルコキシ基、アミド基、アミノオキシ基が好ましいが、加水分解性がマイルドで取り扱い易いという点から、アルコキシ基がとくに好ましい。アルコキシ基の中では炭素数の少ないものの方が反応性が高く、メトキシ基＞エトキシ基＞プロポキシ基…の順に反応性が低くなり、目的や用途に応じて選択できる。
【００６６】
加水分解性基や水酸基は、１個のケイ素原子に１〜３個の範囲で結合することができ、（ａ＋Σｂ）は１〜５個の範囲が好ましい。加水分解性基や水酸基が架橋性シリル基中に２個以上結合する場合には、それらは同じであってもよいし、異なってもよい。架橋性シリル基を形成するケイ素原子は１個以上であるが、シロキサン結合などにより連結されたケイ素原子の場合には、２０個以下であることが好ましい。とくに、一般式（６）；
−Ｓｉ（Ｒ^１０）_３−ａ（Ｙ）_ａ　（６）
（式中、Ｒ^１０、Ｙ、ａは前記と同じ。）で表される架橋性シリル基が、入手が容易であるので好ましい。
【００６７】
なお、特に限定はされないが、硬化性を考慮するとａは２個以上が好ましい。
【００６８】
このような架橋性シリル基を有するビニル系重合体は珪素原子１つあたり２つの加水分解性基が結合してなる加水分解性珪素基を有する重合体が用いられることが多いが、接着剤の用途等や低温で使用する場合等、特に非常に速い硬化速度を必要とする場合、その硬化速度は充分ではなく、また硬化後の柔軟性を出したい場合には、架橋密度を低下させる必要があり、そのため架橋密度が充分でないためにべたつき（表面タック）があることもあった。その際には、ａが３個のもの（例えばトリメトキシ官能基）であるのが好ましい。
【００６９】
また、ａが３個のもの（例えばトリメトキシ官能基）は２個のもの（例えばジメトキシ官能基）よりも硬化性が速いが、貯蔵安定性や力学物性（伸び等）に関しては２個のものの方が優れている場合がある。硬化性と物性バランスをとるために、２個のもの（例えばジメトキシ官能基）と３個のもの（例えばトリメトキシ官能基）を併用してもよい。
【００７０】
例えば、Ｙが同一の場合、ａが多いほどＹの反応性が高くなるため、Ｙとａを種々選択することにより硬化性や硬化物の機械物性等を制御することが可能であり、目的や用途に応じて選択できる。
アルケニル基
本発明におけるアルケニル基は、限定はされないが、一般式（７）で表されるものであることが好ましい。
Ｈ_２Ｃ＝Ｃ（Ｒ^１１）−　（７）
（式中、Ｒ^１１は水素原子あるいは炭素数１〜２０の炭化水素基である）
一般式（７）において、Ｒ^１１は水素原子あるいは炭素数１〜２０の炭化水素基であり、具体的には以下のような基が例示される。
−（ＣＨ_２）_ｎ−ＣＨ_３、−ＣＨ（ＣＨ_３）−（ＣＨ_２）_ｎ−ＣＨ_３、−ＣＨ（ＣＨ_２ＣＨ_３）−（ＣＨ_２）_ｎ−ＣＨ_３、−ＣＨ（ＣＨ_２ＣＨ_３）_２、−Ｃ（ＣＨ_３）_２−（ＣＨ_２）_ｎ−ＣＨ_３、−Ｃ（ＣＨ_３）（ＣＨ_２ＣＨ_３）−（ＣＨ_２）_ｎ−ＣＨ_３、−Ｃ_６Ｈ_５、−Ｃ_６Ｈ_５（ＣＨ_３）、−Ｃ_６Ｈ_５（ＣＨ_３）_２、−（ＣＨ_２）_ｎ−Ｃ_６Ｈ_５、−（ＣＨ_２）_ｎ−Ｃ_６Ｈ_５（ＣＨ_３）、−（ＣＨ_２）_ｎ−Ｃ_６Ｈ_５（ＣＨ_３）_２
（ｎは０以上の整数で、各基の合計炭素数は２０以下）
これらの内では、水素原子が好ましい。
【００７１】
さらに、限定はされないが、重合体（Ｉ）のアルケニル基が、その炭素−炭素二重結合と共役するカルボニル基、アルケニル基、芳香族環により活性化されていないことが好ましい。
【００７２】
アルケニル基と重合体の主鎖の結合形式は、特に限定されないが、炭素−炭素結合、エステル結合、エーテル結合、カーボネート結合、アミド結合、ウレタン結合等を介して結合されていることが好ましい。
アミノ基
本発明におけるアミノ基としては、限定はされないが、
−ＮＲ^１２ _２
（Ｒ^１２は水素または炭素数１〜２０の１価の有機基であり、２個のＲ^１２は互いに同一でもよく異なっていてもよく、また、他端において相互に連結し、環状構造を形成していてもよい。）
が挙げられるが、
−（ＮＲ^１２ _３）^＋Ｘ⁻
（Ｒ^１２は上記と同じ。Ｘ⁻は対アニオン。）
に示されるアンモニウム塩であっても何ら問題はない。
【００７３】
上記式中、Ｒ^１２は水素または炭素数１〜２０の１価の有機基であり、例えば、水素、炭素数１〜２０のアルキル基、炭素数６〜２０のアリール基、炭素数７〜２０のアラルキル基等が挙げられる。２個のＲ^１２は互いに同一でもよく、異なっていてもよい。また、他端において相互に連結し、環状構造を形成していてもよい。
重合性の炭素−炭素二重結合を有する基
重合性の炭素−炭素二重結合を有する基は、好ましくは、一般式（８）；
−ＯＣ（Ｏ）Ｃ（Ｒ^１３）＝ＣＨ_２　（８）
（式中、Ｒ^１３は水素、または、炭素数１〜２０の一価の有機基を表す。）
で表される基であり、更に好ましくは、Ｒ^１３が、水素、または、メチル基である基である。
【００７４】
一般式（８）において、Ｒ^１３の具体例としては特に限定されず、例えば、−Ｈ、−ＣＨ_３、−ＣＨ_２ＣＨ_３、−（ＣＨ_２）_ｎＣＨ_３（ｎは２〜１９の整数を表す）、−Ｃ_６Ｈ_５、−ＣＨ_２ＯＨ、−ＣＮ
等が挙げられるが、好ましくは−Ｈ、−ＣＨ_３である。
架橋性官能基の導入法
以下に、本発明のビニル系重合体（Ｉ）への架橋性官能基の導入法について説明するが、これに限定されるものではない。
【００７５】
まず、末端官能基変換により架橋性シリル基、アルケニル基、水酸基を導入する方法について記述する。これらの官能基はお互いに前駆体となりうるので、架橋性シリル基から溯る順序で記述していく。
【００７６】
架橋性シリル基を少なくとも１個有するビニル系重合体の合成方法としては、
（Ａ）アルケニル基を少なくとも１個有するビニル系重合体に架橋性シリル基を有するヒドロシラン化合物を、ヒドロシリル化触媒存在下に付加させる方法
（Ｂ）水酸基を少なくとも１個有するビニル系重合体に一分子中に架橋性シリル基とイソシアネート基を有する化合物のような、水酸基と反応し得る基を有する化合物を反応させる方法
（Ｃ）ラジカル重合によりビニル系重合体を合成する際に、１分子中に重合性のアルケニル基と架橋性シリル基を併せ持つ化合物を反応させる方法
（Ｄ）ラジカル重合によりビニル系重合体を合成する際に、架橋性シリル基を有する連鎖移動剤を用いる方法
（Ｅ）反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体に１分子中に架橋性シリル基と安定なカルバニオンを有する化合物を反応させる方法；などが挙げられる。
【００７７】
（Ａ）の方法で用いるアルケニル基を少なくとも１個有するビニル系重合体は種々の方法で得られる。以下に合成方法を例示するが、これらに限定されるわけではない。
【００７８】
（Ａ−ａ）ラジカル重合によりビニル系重合体を合成する際に、例えば下記の一般式（９）に挙げられるような一分子中に重合性のアルケニル基と重合性の低いアルケニル基を併せ持つ化合物を第２のモノマーとして反応させる方法。
Ｈ_２Ｃ＝Ｃ（Ｒ^１４）−Ｒ^１５−Ｒ^１６−Ｃ（Ｒ^１７）＝ＣＨ_２　（９）
（式中、Ｒ^１４は水素またはメチル基を示し、Ｒ^１５は−Ｃ（Ｏ）Ｏ−、またはｏ−，ｍ−，ｐ−フェニレン基を示し、Ｒ^１６は直接結合、または炭素数１〜２０の２価の有機基を示し、１個以上のエーテル結合を含んでいてもよい。Ｒ^１７は水素、または炭素数１〜２０のアルキル基、炭素数６〜２０のアリール基または炭素数７〜２０のアラルキル基を示す）
なお、一分子中に重合性のアルケニル基と重合性の低いアルケニル基を併せ持つ化合物を反応させる時期に制限はないが、特にリビングラジカル重合で、ゴム的な性質を期待する場合には重合反応の終期あるいは所定のモノマーの反応終了後に、第２のモノマーとして反応させるのが好ましい。
【００７９】
（Ａ−ｂ）リビングラジカル重合によりビニル系重合体を合成する際に、重合反応の終期あるいは所定のモノマーの反応終了後に、例えば１，５−ヘキサジエン、１，７−オクタジエン、１，９−デカジエンなどのような重合性の低いアルケニル基を少なくとも２個有する化合物を反応させる方法。
【００８０】
（Ａ−ｃ）反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体に、例えばアリルトリブチル錫、アリルトリオクチル錫などの有機錫のようなアルケニル基を有する各種の有機金属化合物を反応させてハロゲンを置換する方法。
【００８１】
（Ａ−ｄ）反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体に、一般式（１０）に挙げられるようなアルケニル基を有する安定化カルバニオンを反応させてハロゲンを置換する方法。
Ｍ^＋Ｃ⁻（Ｒ^１８）（Ｒ^１９）−Ｒ^２０−Ｃ（Ｒ^１７）＝ＣＨ_２　（１０）
（式中、Ｒ^１７は上記に同じ、Ｒ^１８、Ｒ^１９はともにカルバニオンＣ⁻を安定化する電子吸引基であるか、または一方が前記電子吸引基で他方が水素または炭素数１〜１０のアルキル基、またはフェニル基を示す。Ｒ^２０は直接結合、または炭素数１〜１０の２価の有機基を示し、１個以上のエーテル結合を含んでいてもよい。Ｍ^＋はアルカリ金属イオン、または４級アンモニウムイオンを示す）
Ｒ^１８、Ｒ^１９の電子吸引基としては、−ＣＯ_２Ｒ、−Ｃ（Ｏ）Ｒおよび−ＣＮの構造を有するものが特に好ましい。
【００８２】
（Ａ−ｅ）反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体に、例えば亜鉛のような金属単体あるいは有機金属化合物を作用させてエノレートアニオンを調製し、しかる後にハロゲンやアセチル基のような脱離基を有するアルケニル基含有化合物、アルケニル基を有するカルボニル化合物、アルケニル基を有するイソシアネート化合物、アルケニル基を有する酸ハロゲン化物等の、アルケニル基を有する求電子化合物と反応させる方法。
【００８３】
（Ａ−ｆ）反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体に、例えば一般式（１１）あるいは（１２）に示されるようなアルケニル基を有するオキシアニオンあるいはカルボキシレートアニオンを反応させてハロゲンを置換する方法。
Ｈ_２Ｃ＝Ｃ（Ｒ^１７）−Ｒ^２１−Ｏ⁻Ｍ^＋　（１１）
（式中、Ｒ^１７、Ｍ^＋は上記に同じ。Ｒ^２１は炭素数１〜２０の２価の有機基で１個以上のエーテル結合を含んでいてもよい）
Ｈ_２Ｃ＝Ｃ（Ｒ^１７）−Ｒ^２２−Ｃ（Ｏ）Ｏ⁻Ｍ^＋　（１２）
（式中、Ｒ^１７、Ｍ^＋は上記に同じ。Ｒ^２２は直接結合、または炭素数１〜２０の２価の有機基で１個以上のエーテル結合を含んでいてもよい）
などが挙げられる。
【００８４】
上述の反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体の合成法は、前述のような有機ハロゲン化物等を開始剤とし、遷移金属錯体を触媒とする原子移動ラジカル重合法が挙げられるがこれらに限定されるわけではない。
【００８５】
またアルケニル基を少なくとも１個有するビニル系重合体は、水酸基を少なくとも１個有するビニル系重合体から得ることも可能であり、以下に例示する方法が利用できるがこれらに限定されるわけではない。水酸基を少なくとも１個有するビニル系重合体の水酸基に、
（Ａ−ｇ）ナトリウムメトキシドのような塩基を作用させ、塩化アリルのようなアルケニル基含有ハロゲン化物と反応させる方法。
【００８６】
（Ａ−ｈ）アリルイソシアネート等のアルケニル基含有イソシアネート化合物を反応させる方法。
【００８７】
（Ａ−ｉ）（メタ）アクリル酸クロリドのようなアルケニル基含有酸ハロゲン化物をピリジン等の塩基存在下に反応させる方法。
【００８８】
（Ａ−ｊ）アクリル酸等のアルケニル基含有カルボン酸を酸触媒の存在下に反応させる方法；等が挙げられる。
【００８９】
本発明では（Ａ−ａ）（Ａ−ｂ）のようなアルケニル基を導入する方法にハロゲンが直接関与しない場合には、リビングラジカル重合法を用いてビニル系重合体を合成することが好ましい。制御がより容易である点から（Ａ−ｂ）の方法がさらに好ましい。
【００９０】
反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体のハロゲンを変換することによりアルケニル基を導入する場合は、反応性の高い炭素−ハロゲン結合を少なくとも１個有する有機ハロゲン化物、またはハロゲン化スルホニル化合物を開始剤、遷移金属錯体を触媒としてビニル系モノマーをラジカル重合すること（原子移動ラジカル重合法）により得る、末端に反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体を用いるのが好ましい。制御がより容易である点から（Ａ−ｆ）の方法がさらに好ましい。
【００９１】
また、架橋性シリル基を有するヒドロシラン化合物としては特に制限はないが、代表的なものを示すと、一般式（１３）で示される化合物が例示される。
Ｈ−［Ｓｉ（Ｒ^９）_２−ｂ（Ｙ）_ｂＯ］_ｍ−Ｓｉ（Ｒ^１０）_３−ａ（Ｙ）_ａ　（１３）
｛式中、Ｒ^９、Ｒ^１０は、いずれも炭素数１〜２０のアルキル基、炭素数６〜２０のアリール基、炭素数７〜２０のアラルキル基、または（Ｒ’）_３ＳｉＯ−（Ｒ’は炭素数１〜２０の１価の炭化水素基であって、３個のＲ’は同一であってもよく、異なっていてもよい）で示されるトリオルガノシロキシ基を示し、Ｒ^９またはＲ^１０が２個以上存在するとき、それらは同一であってもよく、異なっていてもよい。Ｙは水酸基または加水分解性基を示し、Ｙが２個以上存在するときそれらは同一であってもよく、異なっていてもよい。ａは０，１，２，または３を、また、ｂは０，１，または２を示す。ｍは０〜１９の整数である。ただし、ａ＋ｍｂ≧１であることを満足するものとする。｝
これらヒドロシラン化合物の中でも、特に一般式（１４）
Ｈ−Ｓｉ（Ｒ^１０）_３−ａ（Ｙ）_ａ　（１４）
（式中、Ｒ^１０、Ｙ、ａは前記に同じ）
で示される架橋性基を有する化合物が入手容易な点から好ましい。
【００９２】
上記の架橋性シリル基を有するヒドロシラン化合物をアルケニル基に付加させる際には、遷移金属触媒が通常用いられる。遷移金属触媒としては、例えば、白金単体、アルミナ、シリカ、カーボンブラック等の担体に白金固体を分散させたもの、塩化白金酸、塩化白金酸とアルコール、アルデヒド、ケトン等との錯体、白金−オレフィン錯体、白金（０）−ジビニルテトラメチルジシロキサン錯体が挙げられる。白金化合物以外の触媒の例としては、ＲｈＣｌ（ＰＰｈ_３）_３，ＲｈＣｌ_３，ＲｕＣｌ_３，ＩｒＣｌ_３，ＦｅＣｌ_３，ＡｌＣｌ_３，ＰｄＣｌ_２・Ｈ_２Ｏ，ＮｉＣｌ_２，ＴｉＣｌ_４等が挙げられる。
【００９３】
（Ｂ）および（Ａ−ｇ）〜（Ａ−ｊ）の方法で用いる水酸基を少なくとも１個有するビニル系重合体の製造方法は以下のような方法が例示されるが、これらの方法に限定されるものではない。
【００９４】
（Ｂ−ａ）ラジカル重合によりビニル系重合体を合成する際に、例えば下記の一般式（１５）に挙げられるような一分子中に重合性のアルケニル基と水酸基を併せ持つ化合物を第２のモノマーとして反応させる方法。
Ｈ_２Ｃ＝Ｃ（Ｒ^１４）−Ｒ^１５−Ｒ^１６−ＯＨ　（１５）
（式中、Ｒ^１４、Ｒ^１５、Ｒ^１６は上記に同じ）
なお、一分子中に重合性のアルケニル基と水酸基を併せ持つ化合物を反応させる時期に制限はないが、特にリビングラジカル重合で、ゴム的な性質を期待する場合には重合反応の終期あるいは所定のモノマーの反応終了後に、第２のモノマーとして反応させるのが好ましい。
【００９５】
（Ｂ−ｂ）リビングラジカル重合によりビニル系重合体を合成する際に、重合反応の終期あるいは所定のモノマーの反応終了後に、例えば１０−ウンデセノール、５−ヘキセノール、アリルアルコールのようなアルケニルアルコールを反応させる方法。
【００９６】
（Ｂ−ｃ）例えば特開平５−２６２８０８に示される水酸基含有ポリスルフィドのような水酸基含有連鎖移動剤を多量に用いてビニル系モノマーをラジカル重合させる方法。
【００９７】
（Ｂ−ｄ）例えば特開平６−２３９９１２、特開平８−２８３３１０に示されるような過酸化水素あるいは水酸基含有開始剤を用いてビニル系モノマーをラジカル重合させる方法。
【００９８】
（Ｂ−ｅ）例えば特開平６−１１６３１２に示されるようなアルコール類を過剰に用いてビニル系モノマーをラジカル重合させる方法。
【００９９】
（Ｂ−ｆ）例えば特開平４−１３２７０６などに示されるような方法で、反応性の高い炭素−ハロゲン結合を少なくとも１個に有するビニル系重合体のハロゲンを加水分解あるいは水酸基含有化合物と反応させることにより、末端に水酸基を導入する方法。
【０１００】
（Ｂ−ｇ）反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体に、一般式（１６）に挙げられるような水酸基を有する安定化カルバニオンを反応させてハロゲンを置換する方法。
Ｍ^＋Ｃ⁻（Ｒ^１８）（Ｒ^１９）−Ｒ^２０−ＯＨ　（１６）
（式中、Ｒ^１８、Ｒ^１９、Ｒ^２０、は上記に同じ）
Ｒ^１８、Ｒ^１９の電子吸引基としては、−ＣＯ_２Ｒ、−Ｃ（Ｏ）Ｒおよび−ＣＮの構造を有するものが特に好ましい。
【０１０１】
（Ｂ−ｈ）反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体に、例えば亜鉛のような金属単体あるいは有機金属化合物を作用させてエノレートアニオンを調製し、しかる後にアルデヒド類、又はケトン類を反応させる方法。
【０１０２】
（Ｂ−ｉ）反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体に、例えば一般式（１７）あるいは（１８）に示されるような水酸基を有するオキシアニオンあるいはカルボキシレートアニオンを反応させてハロゲンを置換する方法。
ＨＯ−Ｒ^２１−Ｏ⁻Ｍ^＋　（１７）
（式中、Ｒ^２１およびＭ^＋は前記に同じ）
ＨＯ−Ｒ^２２−Ｃ（Ｏ）Ｏ⁻Ｍ^＋　（１８）
（式中、Ｒ^２２およびＭ^＋は前記に同じ）
（Ｂ−ｊ）リビングラジカル重合によりビニル系重合体を合成する際に、重合反応の終期あるいは所定のモノマーの反応終了後に、第２のモノマーとして、一分子中に重合性の低いアルケニル基および水酸基を有する化合物を反応させる方法。
【０１０３】
このような化合物としては特に限定されないが、一般式（１９）に示される化合物等が挙げられる。
Ｈ_２Ｃ＝Ｃ（Ｒ^１４）−Ｒ^２１−ＯＨ　（１９）
（式中、Ｒ^１４およびＲ^２１は上述したものと同様である。）
上記一般式（１９）に示される化合物としては特に限定されないが、入手が容易であるということから、１０−ウンデセノール、５−ヘキセノール、アリルアルコールのようなアルケニルアルコールが好ましい。
等が挙げられる。
【０１０４】
本発明では（Ｂ−ａ）〜（Ｂ−ｅ）及び（Ｂ−ｊ）のような水酸基を導入する方法にハロゲンが直接関与しない場合には、リビングラジカル重合法を用いてビニル系重合体を合成することが好ましい。制御がより容易である点から（Ｂ−ｂ）の方法がさらに好ましい。
【０１０５】
反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体のハロゲンを変換することにより水酸基を導入する場合は、有機ハロゲン化物、またはハロゲン化スルホニル化合物を開始剤、遷移金属錯体を触媒としてビニル系モノマーをラジカル重合すること（原子移動ラジカル重合法）により得る、末端に反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体を用いるのが好ましい。制御がより容易である点から（Ｂ−ｉ）の方法がさらに好ましい。
【０１０６】
また、一分子中に架橋性シリル基とイソシアネート基のような水酸基と反応し得る基を有する化合物としては、例えばγ−イソシアナートプロピルトリメトキシシラン、γ−イソシアナートプロピルメチルジメトキシシラン、γ−イソシアナートプロピルトリエトキシシラン等が挙げられ、必要により一般に知られているウレタン化反応の触媒を使用できる。
【０１０７】
（Ｃ）の方法で用いる一分子中に重合性のアルケニル基と架橋性シリル基を併せ持つ化合物としては、例えばトリメトキシシリルプロピル（メタ）アクリレート、メチルジメトキシシリルプロピル（メタ）アクリレートなどのような、下記一般式（２０）で示すものが挙げられる。
Ｈ_２Ｃ＝Ｃ（Ｒ^１４）−Ｒ^１５−Ｒ^２３−［Ｓｉ（Ｒ^９）_２−ｂ（Ｙ）_ｂＯ］_ｍ−Ｓｉ（Ｒ^１０）_３−ａ（Ｙ）_ａ　（２０）
（式中、Ｒ^９、Ｒ^１０、Ｒ^１４、Ｒ^１５、Ｙ、ａ、ｂ、ｍは上記に同じ。Ｒ^２３は、直接結合、または炭素数１〜２０の２価の有機基で１個以上のエーテル結合を含んでいてもよい。）
一分子中に重合性のアルケニル基と架橋性シリル基を併せ持つ化合物を反応させる時期に特に制限はないが、特にリビングラジカル重合で、ゴム的な性質を期待する場合には重合反応の終期あるいは所定のモノマーの反応終了後に、第２のモノマーとして反応させるのが好ましい。
【０１０８】
（Ｄ）の連鎖移動剤法で用いられる、架橋性シリル基を有する連鎖移動剤としては例えば特公平３−１４０６８、特公平４−５５４４４に示される、架橋性シリル基を有するメルカプタン、架橋性シリル基を有するヒドロシランなどが挙げられる。
【０１０９】
（Ｅ）の方法で用いられる、上述の反応性の高い炭素−ハロゲン結合を少なくとも１個有するビニル系重合体の合成法は、前述のような有機ハロゲン化物等を開始剤とし、遷移金属錯体を触媒とする原子移動ラジカル重合法が挙げられるがこれらに限定されるわけではない。一分子中に架橋性シリル基と安定化カルバニオンを併せ持つ化合物としては一般式（２１）で示すものが挙げられる。
Ｍ^＋Ｃ⁻（Ｒ^１８）（Ｒ^１９）−Ｒ^２４−Ｃ（Ｈ）（Ｒ^２５）−ＣＨ_２−［Ｓｉ（Ｒ^９）_２−ｂ（Ｙ）_ｂＯ］_ｍ−Ｓｉ（Ｒ^１０）_３−ａ（Ｙ）_ａ　（２１）
（式中、Ｒ^９、Ｒ^１０、Ｒ^１８、Ｒ^１９、Ｙ、ａ、ｂ、ｍ、は前記に同じ。Ｒ^２４は直接結合、または炭素数１〜１０の２価の有機基で１個以上のエーテル結合を含んでいてもよい、Ｒ^２５は水素、または炭素数１〜１０のアルキル基、炭素数６〜１０のアリール基または炭素数７〜１０のアラルキル基を示す。）
Ｒ^１８、Ｒ^１９の電子吸引基としては、−ＣＯ_２Ｒ、−Ｃ（Ｏ）Ｒおよび−ＣＮの構造を有するものが特に好ましい。
エポキシ基
本発明において反応性官能基を末端に有するビニル系重合体は、限定はされないが、以下の工程：
（１）ビニル系モノマーをリビングラジカル重合法により重合することによってビニル系重合体を製造し；
（２）続いて反応性官能基とエチレン性不飽和基を併せ持つ化合物を反応させる；
ことにより製造される。
【０１１０】
また、原子移動ラジカル重合において、重合終期にアリルアルコールを反応させ、その後、水酸基とハロゲン基でエポキシ環化させる方法も挙げられる。
アミノ基
アミノ基を少なくとも１つ主鎖末端に有するビニル系重合体を製造する方法としては、以下の工程が挙げられる。
（１）ハロゲン基を少なくとも１つ主鎖末端に有するビニル系重合体を製造し、（２）末端ハロゲンを、アミノ基含有化合物を用いてアミノ基を有する置換基に変換する。
【０１１１】
アミノ基を有する置換基としては、特に限定されないが、一般式（２２）に示される基が例示される。
−Ｏ−Ｒ^２６−ＮＲ^１２ _２　（２２）
（式中、Ｒ^２６は、１個以上のエーテル結合又はエステル結合を含んでいてもよい炭素数１〜２０の２価の有機基を表す。Ｒ^１２は水素または炭素数１〜２０の１価の有機基であり、２個のＲ^１２は互いに同一でもよく異なっていてもよく、また、他端において相互に連結し、環状構造を形成していてもよい。）
上記一般式（２２）において、Ｒ^２６は１個以上のエーテル結合又はエステル結合を含んでいてもよい炭素数１〜２０の２価の有機基であり、例えば炭素数１〜２０のアルキレン基、炭素数６〜２０のアリーレン基、炭素数７〜２０のアラルキレン基などが挙げられるが、
−Ｃ_６Ｈ_４−Ｒ^２７−
（式中、Ｃ_６Ｈ_４はフェニレン基、Ｒ^２７は、直接結合または１個以上のエーテル結合又はエステル結合を含んでいてもよい炭素数１〜１４の２価の有機基を表す。）
または、
−Ｃ（Ｏ）−Ｒ^２８−
（式中、Ｒ^２８は、直接結合または１個以上のエーテル結合又はエステル結合を含んでいてもよい炭素数１〜１９の２価の有機基を表す。）
が好ましい。
【０１１２】
ビニル系重合体の末端ハロゲンを変換することにより、重合体末端にアミノ基を導入することができる。置換方法としては特に限定されないが、反応を制御しやすいという点からアミノ基含有化合物を求核剤とする求核置換反応が好ましい。このような求核剤として例えば、一般式（２３）に示される水酸基とアミノ基を併せ持つ化合物が挙げられる。
ＨＯ−Ｒ^２６−ＮＲ^１２ _２　（２３）
（式中、Ｒ^２６は、１個以上のエーテル結合又はエステル結合を含んでいてもよい炭素数１〜２０の２価の有機基を表す。Ｒ^１２は水素または炭素数１〜２０の１価の有機基であり、２個のＲ^１２は互いに同一でもよく異なっていてもよく、また、他端において相互に連結し、環状構造を形成していてもよい。）
上記一般式（２３）において、Ｒ^２６は１個以上のエーテル結合又はエステル結合を含んでいてもよい炭素数１〜２０の２価の有機基であり、例えば炭素数１〜２０のアルキレン基、炭素数６〜２０のアリーレン基、炭素数７〜２０のアラルキレン基などが挙げられる。これらの水酸基とアミノ基を併せ持つ化合物の中で、Ｒ^２６が、
−Ｃ_６Ｈ_４−Ｒ^２７−
（式中、Ｃ_６Ｈ_４はフェニレン基、Ｒ^２７は、直接結合または１個以上のエーテル結合又はエステル結合を含んでいてもよい炭素数１〜１４の２価の有機基を表す）で表されるアミノフェノール類；
−Ｃ（Ｏ）−Ｒ^２８−
（式中、Ｒ^２８は、直接結合または１個以上のエーテル結合又はエステル結合を含んでいてもよい炭素数１〜１９の２価の有機基を表す）で表されるアミノ酸類；が好ましい。
【０１１３】
具体的な化合物として、例えばエタノールアミン；ｏ，ｍ，ｐ−アミノフェノール；ｏ，ｍ，ｐ−ＮＨ_２−Ｃ_６Ｈ_４−ＣＯ_２Ｈ；グリシン、アラニン、アミノブタン酸等が挙げられる。
【０１１４】
アミノ基とオキシアニオンを併せ持つ化合物を求核剤として用いることもできる。このような化合物としては特に限定されないが、例えば、一般式（２４）に示される化合物が挙げられる。
Ｍ^＋Ｏ⁻−Ｒ^２６−ＮＲ^１２ _２　（２４）
（式中、Ｒ^２６は、１個以上のエーテル結合又はエステル結合を含んでいてもよい炭素数１〜２０の２価の有機基を表す。Ｒ^１２は水素または炭素数１〜２０の１価の有機基であり、２個のＲ^１２は互いに同一でもよく異なっていてもよく、また、他端において相互に連結し、環状構造を形成していてもよい。Ｍ^＋はアルカリ金属イオンまたは４級アンモニウムイオンを表す。）
上記一般式（２４）において、Ｍ^＋は、オキシアニオンの対カチオンであり、アルカリ金属イオン又は４級アンモニウムイオンを表す。上記アルカリ金属イオンとしては、リチウムイオン、ナトリウムイオン、カリウムイオン等が挙げられ、好ましくは、ナトリウムイオン又はカリウムイオンである。上記４級アンモニウムイオンとしては、テトラメチルアンモニウムイオン、テトラエチルアンモニウムイオン、トリメチルベンジルアンモニウムイオン、トリメチルドデシルアンモニウムイオン、テトラブチルアンモニウムイオン、ジメチルピペリジニウムイオン等が挙げられる。
【０１１５】
上記のアミノ基とオキシアニオンを併せ持つ化合物のうち、置換反応のコントロールがし易い、入手が容易であるという点から、一般式（２５）に示すアミノフェノール類の塩、または一般式（２６）に示すアミノ酸類の塩が好ましい。
Ｍ^＋Ｏ⁻−Ｃ_６Ｈ_４−Ｒ^２７−ＮＲ^１２ _２　（２５）
Ｍ^＋Ｏ⁻−Ｃ（Ｏ）−Ｒ^２８−ＮＲ^１２ _２　（２６）
（式中、Ｃ_６Ｈ_４はフェニレン基、Ｒ^２７は、直接結合または１個以上のエーテル結合又はエステル結合を含んでいてもよい炭素数１〜１４の２価の有機基、Ｒ^２８は、直接結合または１個以上のエーテル結合又はエステル結合を含んでいてもよい炭素数１〜１９の２価の有機基を表す。Ｒ^１２は水素または炭素数１〜２０の１価の有機基であり、２個のＲ^１２は互いに同一でもよく異なっていてもよく、また、他端において相互に連結し、環状構造を形成していてもよい。Ｍ^＋は上記と同じ。）
一般式（２４）〜（２６）に示されるオキシアニオンを有する化合物は、一般式（２３）に示される化合物を塩基性化合物と作用させることにより容易に得られる。
【０１１６】
塩基性化合物としては各種のものを使用できる。例示すると、ナトリウムメトキシド、カリウムメトキシド、リチウムメトキシド、ナトリウムエトキシド、カリウムエトキシド、リチウムエトキシド、ナトリウム−ｔｅｒｔ−ブトキシド、カリウム−ｔｅｒｔ−ブトキシド、炭酸ナトリウム、炭酸カリウム、炭酸リチウム、炭酸水素ナトリウム、水酸化ナトリウム、水酸化カリウム、水素化ナトリウム、水素化カリウム、メチルリチウム、エチルリチウム、ｎ−ブチルリチウム、ｔｅｒｔ−ブチルリチウム、リチウムジイソプロピルアミド、リチウムヘキサメチルジシラジド等が挙げられる。上記塩基の使用量は、特に制限はないが、上記前駆体に対して、０．５〜５当量、好ましくは０．８〜１．２当量である。
【０１１７】
上記前駆体と上記塩基を反応させる際に用いられる溶媒としては、例えば、ベンゼン、トルエン等の炭化水素系溶媒；ジエチルエーテル、テトラヒドロフラン等のエーテル系溶媒；塩化メチレン、クロロホルム等のハロゲン化炭化水素系溶媒；アセトン、メチルエチルケトン、メチルイソブチルケトン等のケトン系溶媒；メタノール、エタノール、プロパノール、イソプロパノール、ｎ−ブチルアルコール、ｔｅｒｔ−ブチルアルコール等のアルコール系溶媒；アセトニトリル、プロピオニトリル、ベンゾニトリル等のニトリル系溶媒；酢酸エチル、酢酸ブチル等のエステル系溶媒；エチレンカーボネート、プロピレンカーボネート等のカーボネート系溶媒；ジメチルホルムアミド、ジメチルアセトアミド等のアミド系溶媒；ジメチルスルホキシド等のスルホキシド系溶媒等が挙げられる。これらは、単独又は２種以上を混合して用いることができる。
【０１１８】
Ｍ^＋が４級アンモニウムイオンであるオキシアニオンを有する化合物は、Ｍ^＋がアルカリ金属イオンであるものを調製し、これに４級アンモニウムハライドを作用させることによって得られる。上記４級アンモニウムハライドとしては、テトラメチルアンモニウムハライド、テトラエチルアンモニウムハライド、トリメチルベンジルアンモニウムハライド、トリメチルドデシルアンモニウムハライド、テトラブチルアンモニウムハライド等が例示される。
【０１１９】
重合体末端ハロゲンの置換反応に用いられる溶媒は各種のものが使用されてよい。例えば、ベンゼン、トルエン等の炭化水素系溶媒；ジエチルエーテル、テトラヒドロフラン等のエーテル系溶媒；塩化メチレン、クロロホルム等のハロゲン化炭化水素系溶媒；アセトン、メチルエチルケトン、メチルイソブチルケトン等のケトン系溶媒；メタノール、エタノール、プロパノール、イソプロパノール、ｎ−ブチルアルコール、ｔｅｒｔ−ブチルアルコール等のアルコール系溶媒；アセトニトリル、プロピオニトリル、ベンゾニトリル等のニトリル系溶媒；酢酸エチル、酢酸ブチル等のエステル系溶媒；エチレンカーボネート、プロピレンカーボネート等のカーボネート系溶媒；ジメチルホルムアミド、ジメチルアセトアミド等のアミド系溶媒；ジメチルスルホキシド等のスルホキシド系溶媒等が挙げられる。これらは、単独又は２種以上を混合して用いることができる。
【０１２０】
反応温度は０〜１５０℃で行うことができる。また、アミノ基含有化合物の使用量は、特に制限されないが、重合体末端ハロゲンに対して、１〜５当量であり、好ましくは１〜１．２当量である。
【０１２１】
求核置換反応を加速するために、反応混合物中に塩基性化合物を添加してもよい。このような塩基性化合物としては既に例示したもののほかに、トリメチルアミン、トリエチルアミン、トリブチルアミン等のアルキルアミン；テトラメチルエチレンジアミン、ペンタメチルジエチレントリアミン等のポリアミン；ピリジン、ピコリン等のピリジン系化合物等が挙げられる。
【０１２２】
求核置換反応に用いられるアミノ基含有化合物のアミノ基が、求核置換反応に影響を及ぼす場合には、適当な置換基により保護することが好ましい。このような置換基としては、ベンジルオキシカルボニル基、ｔｅｒｔ−ブトキシカルボニル基、９−フルオレニルメトキシカルボニル基等が例示される。
【０１２３】
また、アジドアニオンによりビニル系重合体のハロゲン末端を置換した後、ＬＡＨ等により還元する方法が挙げられる。
重合性の炭素−炭素二重結合を有する基
本発明の重合体（Ｉ）に重合性の炭素−炭素二重結合を有する基を導入する方法としては、限定はされないが、以下のような方法が挙げられる。
▲１▼ビニル系重合体のハロゲン基を、ラジカル重合性の炭素−炭素二重結合を有する化合物で置換することにより製造する方法。具体例としては、一般式（２７）で表される構造を有するビニル系重合体と、一般式（２８）で示される化合物との反応による方法。
−ＣＲ^２９Ｒ^３０Ｘ　（２７）
（式中、Ｒ^２９、Ｒ^３０は、ビニル系モノマーのエチレン性不飽和基に結合した基。Ｘは、塩素、臭素、又は、ヨウ素を表す。）
Ｍ^＋−ＯＣ（Ｏ）Ｃ（Ｒ^１３）＝ＣＨ_２　（２８）
（式中、Ｒ^１３は水素、または、炭素数１〜２０の有機基を表す。Ｍ^＋はアルカリ金属、または４級アンモニウムイオンを表す。）
▲２▼水酸基を有するビニル系重合体と、一般式（２９）で示される化合物との反応による方法。
ＸＣ（Ｏ）Ｃ（Ｒ^１３）＝ＣＨ_２　（２９）
（式中、Ｒ^１３は水素、または、炭素数１〜２０の有機基を表す。Ｘは塩素、臭素、または水酸基を表す。）
▲３▼水酸基を有するビニル系重合体に、ジイソシアネート化合物を反応させ、残存イソシアネート基と一般式（３０）で示される化合物との反応による方法。
ＨＯ−Ｒ^３１−ＯＣ（Ｏ）Ｃ（Ｒ^１３）＝ＣＨ_２　（３０）
（式中、Ｒ^１３は水素、または、炭素数１〜２０の有機基を表す。Ｒ^３１は炭素数２〜２０の２価の有機基を表す。）
以下にこれらの各方法について詳細に説明する。
【０１２４】
上記▲１▼の方法について説明する。
▲１▼一般式（２７）で表される末端構造を有するビニル系重合体と、一般式（２８）で示される化合物との反応による方法。
−ＣＲ^２９Ｒ^３０Ｘ　（２７）
（式中、Ｒ^２９、Ｒ^３０は、ビニル系モノマーのエチレン性不飽和基に結合した基。Ｘは、塩素、臭素、又は、ヨウ素を表す。）
Ｍ^＋−ＯＣ（Ｏ）Ｃ（Ｒ^１３）＝ＣＨ_２　（２８）
（式中、Ｒ^１３は水素、または、炭素数１〜２０の有機基を表す。Ｍ^＋はアルカリ金属、または４級アンモニウムイオンを表す。）
一般式（２７）で表される末端構造を有するビニル系重合体は、上述した有機ハロゲン化物、またはハロゲン化スルホニル化合物を開始剤、遷移金属錯体を触媒としてビニル系モノマーを重合する方法、あるいは、ハロゲン化合物を連鎖移動剤としてビニル系モノマーを重合する方法により製造されるが、好ましくは前者である。
【０１２５】
一般式（２８）で表される化合物としては特に限定されないが、Ｒ^１３の具体例としては、例えば、−Ｈ、−ＣＨ_３、−ＣＨ_２ＣＨ_３、−（ＣＨ_２）_ｎＣＨ_３（ｎは２〜１９の整数を表す）、−Ｃ_６Ｈ_５、−ＣＨ_２ＯＨ、−ＣＮ、
等が挙げられ、好ましくは−Ｈ、−ＣＨ_３である。Ｍ^＋はオキシアニオンの対カチオンであり、Ｍ^＋の種類としてはアルカリ金属イオン、具体的にはリチウムイオン、ナトリウムイオン、カリウムイオン、および４級アンモニウムイオンが挙げられる。４級アンモニウムイオンとしてはテトラメチルアンモニウムイオン、テトラエチルアンモニウムイオン、テトラベンジルアンモニウムイオン、トリメチルドデシルアンモニウムイオン、テトラブチルアンモニウムイオンおよびジメチルピペリジニウムイオン等が挙げられ、好ましくはナトリウムイオン、カリウムイオンである。一般式（２８）のオキシアニオンの使用量は、一般式（２７）のハロゲン基に対して、好ましくは１〜５当量、更に好ましくは１．０〜１．２当量である。この反応を実施する溶媒としては特に限定はされないが、求核置換反応であるため極性溶媒が好ましく、例えば、テトラヒドロフラン、ジオキサン、ジエチルエーテル、アセトン、ジメチルスルホキシド、ジメチルホルムアミド、ジメチルアセトアミド、ヘキサメチルホスホリックトリアミド、アセトニトリル、等が用いられる。反応を行う温度は限定されないが、一般に０〜１５０℃で、重合性の末端基を保持するために好ましくは室温〜１００℃で行う。
【０１２６】
上記▲２▼の方法について説明する。
▲２▼水酸基を有するビニル系重合体と、一般式（２９）で示される化合物との反応による方法。
ＸＣ（Ｏ）Ｃ（Ｒ^１３）＝ＣＨ_２　（２９）
（式中、Ｒ^１３は水素、または、炭素数１〜２０の有機基を表す。Ｘは塩素、臭素、または水酸基を表す。）
一般式（２９）で表される化合物としては特に限定されないが、Ｒ^１３の具体例としては、例えば、−Ｈ、−ＣＨ_３、−ＣＨ_２ＣＨ_３、−（ＣＨ_２）_ｎＣＨ_３（ｎは２〜１９の整数を表す）、−Ｃ_６Ｈ_５、−ＣＨ_２ＯＨ、−ＣＮ、
等が挙げられ、好ましくは−Ｈ、−ＣＨ_３である。
【０１２７】
水酸基を、好ましくは末端に、有するビニル系重合体は、上述した有機ハロゲン化物、またはハロゲン化スルホニル化合物を開始剤、遷移金属錯体を触媒としてビニル系モノマーを重合する方法、あるいは、水酸基を持つ化合物を連鎖移動剤としてビニル系モノマーを重合する方法により製造されるが、好ましくは前者である。これらの方法により水酸基を有するビニル系重合体を製造する方法は限定されないが、以下のような方法が例示される。
【０１２８】
（ａ）リビングラジカル重合によりビニル系重合体を合成する際に、下記一般式（３１）等で表される一分子中に重合性のアルケニル基および水酸基を併せ持つ化合物を第２のモノマーとして反応させる方法。
Ｈ_２Ｃ＝Ｃ（Ｒ^３２）−Ｒ^３３−Ｒ^３４−ＯＨ　（３１）
（式中、Ｒ^３２は炭素数１〜２０の有機基で水素またはメチル基が好ましく、互いに同一であっても異なっていてもよい。Ｒ^３３は−Ｃ（Ｏ）Ｏ−（エステル基）、またはｏ−，ｍ−もしくはｐ−フェニレン基を表す。Ｒ^３４は直接結合、または１個以上のエーテル結合を有していてもよい炭素数１〜２０の２価の有機基を表す。Ｒ^３３がエステル基のものは（メタ）アクリレート系化合物、Ｒ^３３がフェニレン基のものはスチレン系の化合物である。）
なお、一分子中に重合性のアルケニル基および水酸基を併せ持つ化合物を反応させる時期に制限はないが、特にゴム的な性質を期待する場合には重合反応の終期あるいは所定のモノマーの反応終了後に、第２のモノマーとして反応させるのが好ましい。
【０１２９】
（ｂ）リビングラジカル重合によりビニル系重合体を合成する際に、重合反応の終期あるいは所定のモノマーの反応終了後に、第２のモノマーとして、一分子中に重合性の低いアルケニル基および水酸基を有する化合物を反応させる方法。
【０１３０】
このような化合物としては特に限定されないが、一般式（３２）に示される化合物等が挙げられる。
Ｈ_２Ｃ＝Ｃ（Ｒ^３２）−Ｒ^３５−ＯＨ　（３２）
（式中、Ｒ^３２は上述したものと同様である。Ｒ^３５は１個以上のエーテル結合を含んでいてもよい炭素数１〜２０の２価の有機基を表す。）
上記一般式（３２）に示される化合物としては特に限定されないが、入手が容易であるということから、１０−ウンデセノール、５−ヘキセノール、アリルアルコールのようなアルケニルアルコールが好ましい。
【０１３１】
（ｃ）特開平４−１３２７０６号公報などに開示されるような方法で、原子移動ラジカル重合により得られる一般式（２７）で表されるような炭素−ハロゲン結合を少なくとも１個に有するビニル系重合体のハロゲンを、加水分解あるいは水酸基含有化合物と反応させることにより、末端に水酸基を導入する方法。
【０１３２】
（ｄ）原子移動ラジカル重合により得られる一般式（２７）で表されるような炭素−ハロゲン結合を少なくとも１個有するビニル系重合体に、一般式（３３）に挙げられるような水酸基を有する安定化カルバニオンを反応させてハロゲンを置換する方法。
Ｍ^＋Ｃ⁻（Ｒ^３６）（Ｒ^３７）−Ｒ^３５−ＯＨ　（３３）
（式中、Ｒ^３５は上述したものと同様である。Ｒ^３６およびＲ^３７はともにカルバニオンＣ⁻を安定化する電子吸引基、または一方が上記電子吸引基で他方が水素または炭素数１〜１０のアルキル基もしくはフェニル基を表す。Ｒ^３６およびＲ^３７の電子吸引基としては、−ＣＯ_２Ｒ（エステル基）、−Ｃ（Ｏ）Ｒ（ケト基）、−ＣＯＮ（Ｒ_２）（アミド基）、−ＣＯＳＲ（チオエステル基）、−ＣＮ（ニトリル基）、−ＮＯ_２（ニトロ基）等が挙げられる。置換基Ｒは炭素数１〜２０のアルキル基、炭素数６〜２０のアリール基または炭素数７〜２０のアラルキル基であり、好ましくは炭素数１〜１０のアルキル基もしくはフェニル基である。Ｒ^３６およびＲ^３７としては、−ＣＯ_２Ｒ、−Ｃ（Ｏ）Ｒおよび−ＣＮが特に好ましい。）（ｅ）原子移動ラジカル重合により得られる一般式（２７）で表される炭素−ハロゲン結合を少なくとも１個有するビニル系重合体に、例えば亜鉛のような金属単体あるいは有機金属化合物を作用させてエノレートアニオンを調製し、しかる後にアルデヒド類、又はケトン類を反応させる方法。
【０１３３】
（ｆ）重合体末端のハロゲン、好ましくは一般式（２７）で表されるハロゲンを少なくとも１個有するビニル系重合体に、下記一般式（３４）等で表される水酸基含有オキシアニオン又は下記一般式（３５）等で表される水酸基含有カルボキシレートアニオンを反応させて、上記ハロゲンを水酸基含有置換基に置換する方法。
ＨＯ−Ｒ^３５−Ｏ⁻Ｍ^＋　（３４）
（式中、Ｒ^３５およびＭ^＋は上述したものと同様である。）
ＨＯ−Ｒ^３５−Ｃ（Ｏ）Ｏ⁻Ｍ^＋　（３５）
（式中、Ｒ^３５およびＭ^＋は上述したものと同様である。）
本発明では（ａ）〜（ｂ）のような水酸基を導入する方法にハロゲンが直接関与しない場合、制御がより容易である点から（ｂ）の方法がさらに好ましい。
【０１３４】
また（ｃ）〜（ｆ）のような炭素−ハロゲン結合を少なくとも１個有するビニル系重合体のハロゲンを変換することにより水酸基を導入する場合は、制御がより容易である点から（ｆ）の方法がさらに好ましい。
【０１３５】
上記▲３▼の方法について説明する。
▲３▼水酸基を有するビニル系重合体に、ジイソシアネート化合物を反応させ、残存イソシアネート基と一般式（３６）で示される化合物との反応による方法。
ＨＯ−Ｒ^３１−ＯＣ（Ｏ）Ｃ（Ｒ^１３）＝ＣＨ_２　（３６）
（式中、Ｒ^１３は水素、または、炭素数１〜２０の有機基を表す。Ｒ^３１は炭素数２〜２０の２価の有機基を表す。）
一般式（３６）で表される化合物としては特に限定されないが、Ｒ^１３の具体例としては、例えば、−Ｈ、−ＣＨ_３、−ＣＨ_２ＣＨ_３、−（ＣＨ_２）_ｎＣＨ_３（ｎは２〜１９の整数を表す）、−Ｃ_６Ｈ_５、−ＣＨ_２ＯＨ、−ＣＮ、
等が挙げられ、好ましくは−Ｈ、−ＣＨ_３である。具体的な化合物としては、メタクリル酸２−ヒドロキシプロピルが挙げられる。
【０１３６】
末端に水酸基を有するビニル系重合体は、上記の通り。
【０１３７】
ジイソシアネート化合物は、特に限定されないが、従来公知のものをいずれも使用することができ、例えば、トルイレンジイソシアネート、４，４’−ジフェニルメタンジイソシアネート、ヘキサメチレンジイソシアネート、キシリレンジイソシアネート、メタキシリレンジイソシアネート、１，５−ナフタレンジイソシアネート、水素化ジフェニルメタンジイソシアネート、水素化トルイレンジイソシアネート、水素化キシリレンジイソシアネート、イソホロンジイソシアネート等のイソシアネート化合物；等を挙げることができる。これらは、単独で使用しうるほか、２種以上を併用することもできる。またブロックイソシアネートを使用しても構わない。
【０１３８】
よりすぐれた耐候性を生かすためには、例えば、ヘキサメチレンジイソシアネート、水素化ジフェニルメタンジイソシアネート等の芳香環を有しないジイソシアネート化合物を用いるのが好ましい。
＜＜平均粒径１μｍ以上５００μｍ以下のシリカ（ＩＩ）について＞＞
本発明の、平均粒径１μｍ以上５００μｍ以下のシリカ（ＩＩ）とは、篩い分け法により測定される平均粒径が１μｍ以上５００μｍ以下のシリカをいう。篩い分け法とは、具体的には、粉体を各種の目開きの篩（マイクロシーブ等）で分級し、測定に供した粉体の全重量の５０重量％が通過した篩の目開きに相当する値（重量平均粒径）で定義されるものである。なお、あまりに粒径の細かいものはこの篩い分け方によって判別できない場合があり、その際には顕微鏡法を用いて測定する。
【０１３９】
一般的にシリカは、合成シリカと天然物シリカに分けられる。合成シリカは更に製法上から、高温気相反応によりシリカの析出を行なう乾式法シリカ（更に燃焼法とアーク法に大別される）と、珪酸ソーダ水溶液の酸、又はアルカリ金属塩による中和、分解反応によりシリカの析出を行なう湿式法シリカ（更に沈降法とゲル法に大別される）、高温により完全熔融させアモルファス化する熔融シリカ等に分類される。一方、天然物シリカとしては、結晶性シリカ、無水ケイ酸、含水ケイ酸などが挙げられる。
【０１４０】
本発明の硬化性組成物において、平均粒径１μｍ以上５００μｍ以下のシリカ（ＩＩ）は、平均粒径１μｍ以上であれば特に限定はされないが、あまりに粒径が大き過ぎると作業性や機械物性、耐久性等に悪影響を及ぼすため５００μｍ以下であることが好ましい。平均粒径１μｍ以上５００μｍ以下のシリカ（ＩＩ）としては以下に例示するような湿式法シリカ、結晶性シリカ、熔融シリカ、結晶性シリカ、微粉末シリカ等が挙げられる。
【０１４１】
湿式法シリカとしては例えば、沈降法で製造されたトクシールＵ、ＵＲ、ＧＵ、ＵＳＡ、ＵＳＧ等のトクシールシリーズ（トクヤマ製）、ニップシールＳＳシリーズに代表されるニップシールＳＳ−１０、ＳＳ−２０や、ニップシールＬＰ、ニップシールＮＳ−Ｐ、ニップシールＶＮ３、ニップシールＥＲ、ニップシールＮＳ−Ｔ、ニップシールＮＳ−Ｋ、ニップシールＮＡ、ニップシールＬ３００、ニップシールＮ３００Ａ、ニップシールＫ３００、ニップシールＧ３００等のニップシールシリーズ（日本シリカ製）等が例示される。また、ゲル法デ製造されたサイリシア３１０、サイリシア２５０Ｎ、サイリシア４３０、サイリシア７７０、サイリシア４７０等のサイリシアシリーズ（富士シリシア製）やニップゲルシリーズ（日本シリカ製）等が例示される。
【０１４２】
結晶性シリカとしては例えば、クリスタライトＣＭＣ−１２、クリスタライト５Ｘ、クリスタライトＡ−２等のクリスタライトシリーズ、ＩＭＳＩＬ　Ａ−２５、ＩＭＳＩＬ　Ａ−１５、ＩＭＳＩＬ　Ａ−８、ＩＭＳＩＬ　Ａ−１０等のＩＭＳＩＬシリーズ（何れも龍森製）が挙げられる。
【０１４３】
溶融シリカとしては例えば、ヒューズレックスＥ−１、ヒューズレックスＥ−２、ヒューズレックスＺＡ−３０、ヒューズレックスＲＤ−８、ヒューズレックスＲＤ−１２０、ヒューズレックスＭＣＦ−２００、ヒューズレックスＹ−６０等のヒューズレックスシリーズ（龍森製）などが例示される。
【０１４４】
乾式法シリカとしては燃焼法で製造されたアエロジルシリーズ（日本アエロジル製）等があるが、この方法で製造されたシリカは配合時の剪断により容易に一次粒子近くにまで分散してしまい、少量でかなりの補強効果、増粘効果が見られるため、本発明のシリカ（ＩＩ）には不向きである。
【０１４５】
本発明におけるシリカは特に限定されず、上述のいずれの種類を用いても構わない。水分が多く含まれると硬化反応時に副反応が起こる可能性があるため、乾式法シリカを使うのが好ましい場合がある。同様の理由で表面処理を施し疎水化したシリカを使うのが好ましい場合もある。その表面処理方法としては、オルガノシランやオルガノシラザン、ジオルガノポリシロキサン等の有機ケイ素化合物で予め疎水処理する方法が好ましい。
＜平均粒径１μｍ以上５００μｍ以下のシリカ（ＩＩ）の使用量＞
平均粒径１μｍ以上５００μｍ以下のシリカ（ＩＩ）の使用量としては、特に限定されないがビニル系重合体（Ｉ）１００重量部に対し、０．１重量部以上３００重量部以下が好ましく、０．５重量部以上１００重量部以下がより好ましく、１重量部以上８０重量部以下が更に好ましい。配合量が０．１重量部未満の場合には、硬化物の破断強度等の機械物性の改善効果が充分でないことがあり、３００重量部を越えると該硬化性組成物の作業性が低下したりその硬化物の物性が低下したりすることがある。また、本発明の平均粒径１μｍ以上５００μｍ以下のシリカは単独で使用しても良いし、２種以上併用しても構わない。
＜＜硬化性組成物＞＞
本発明の硬化性組成物においては、硬化触媒や硬化剤が必要になるものがある。また、目的とする物性に応じて、各種の配合剤を添加しても構わない。
＜硬化触媒・硬化剤＞
架橋性シリル基の場合
架橋性シリル基を有する重合体は、従来公知の各種縮合触媒の存在下、あるいは非存在下にシロキサン結合を形成することにより架橋、硬化する。硬化物の性状としては、重合体の分子量と主鎖骨格に応じて、ゴム状のものから樹脂状のものまで幅広く作成することができる。
【０１４６】
このような縮合触媒としては、例えば、ジブチル錫ジラウレート、ジブチル錫ジアセテート、ジブチル錫ジエチルヘキサノレート、ジブチル錫ジオクテート、ジブチル錫ジメチルマレート、ジブチル錫ジエチルマレート、ジブチル錫ジブチルマレート、ジブチル錫ジイソオクチルマレート、ジブチル錫ジトリデシルマレート、ジブチル錫ジベンジルマレート、ジブチル錫マレエート、ジオクチル錫ジアセテート、ジオクチル錫ジステアレート、ジオクチル錫ジラウレート、ジオクチル錫ジエチルマレート、ジオクチル錫ジイソオクチルマレート等の４価のスズ化合物類；オクチル酸錫、ナフテン酸錫、ステアリン酸錫等の２価のスズ化合物類；モノブチル錫トリスオクトエートやモノブチル錫トリイソプロポキシド等のモノブチル錫化合物やモノオクチル錫化合物等のモノアルキル錫類；テトラブチルチタネート、テトラプロピルチタネート等のチタン酸エステル類；アルミニウムトリスアセチルアセトナート、アルミニウムトリスエチルアセトアセテート、ジイソプロポキシアルミニウムエチルアセトアセテート等の有機アルミニウム化合物類；カルボン酸ビスマス、カルボン酸鉄、カルボン酸チタニウム、カルボン酸鉛、カルボン酸バナジウム、カルボン酸ジルコニウム、カルボン酸カルシウム、カルボン酸カリウム、カルボン酸バリウム、カルボン酸マンガン、カルボン酸セリウム、カルボン酸ニッケル、カルボン酸コバルト、カルボン酸亜鉛、カルボン酸アルミニウム等のカルボン酸（２−エチルヘキサン酸、ネオデカン酸、バーサチック酸、オレイン酸、ナフテン酸等）金属塩、あるいはこれらと後述のラウリルアミン等のアミン系化合物との反応物および混合物；ジルコニウムテトラアセチルアセトナート、チタンテトラアセチルアセトナート等のキレート化合物類；メチルアミン、エチルアミン、プロピルアミン、イソプロピルアミン、ブチルアミン、アミルアミン、ヘキシルアミン、オクチルアミン、２−エチルヘキシルアミン、ノニルアミン、デシルアミン、ラウリルアミン、ペンタデシルアミン、セチルアミン、ステアリルアミン、シクロヘキシルアミン等の脂肪族第一アミン類；ジメチルアミン、ジエチルアミン、ジプロピルアミン、ジイソプロピルアミン、ジブチルアミン、ジアミルアミン、ジオクチルアミン、ジ（２−エチルヘキシル）アミン、ジデシルアミン、ジラウリルアミン、ジセチルアミン、ジステアリルアミン、メチルステアリルアミン、エチルステアリルアミン、ブチルステアリルアミン等の脂肪族第二アミン類；トリアミルアミン、トリヘキシルアミン、トリオクチルアミン等の脂肪族第三アミン類；トリアリルアミン、オレイルアミン、などの脂肪族不飽和アミン類；ラウリルアニリン、ステアリルアニリン、トリフェニルアミン等の芳香族アミン類；および、その他のアミン類として、モノエタノールアミン、ジエタノールアミン、トリエタノールアミン、ジエチレントリアミン、トリエチレンテトラミン、オレイルアミン、シクロヘキシルアミン、ベンジルアミン、ジエチルアミノプロピルアミン、キシリレンジアミン、エチレンジアミン、ヘキサメチレンジアミン、トリエチレンジアミン、グアニジン、ジフェニルグアニジン、２，４，６−トリス（ジメチルアミノメチル）フェノール、モルホリン、Ｎ−メチルモルホリン、２−エチル−４−メチルイミダゾール、１，８−ジアザビシクロ（５，４，０）ウンデセン−７（ＤＢＵ）等のアミン系化合物、あるいはこれらのアミン系化合物のカルボン酸等との塩；ラウリルアミンとオクチル酸錫の反応物あるいは混合物のようなアミン系化合物と有機錫化合物との反応物および混合物；過剰のポリアミンと多塩基酸とから得られる低分子量ポリアミド樹脂；過剰のポリアミンとエポキシ化合物との反応生成物；γ−アミノプロピルトリメトキシシラン、γ−アミノプロピルトリエトキシシラン、γ−アミノプロピルトリイソプロポキシシラン、γ−アミノプロピルメチルジメトキシシラン、γ−アミノプロピルメチルジエトキシシラン、Ｎ−（β−アミノエチル）アミノプロピルトリメトキシシラン、Ｎ−（β−アミノエチル）アミノプロピルメチルジメトキシシラン、Ｎ−（β−アミノエチル）アミノプロピルトリエトキシシラン、Ｎ−（β−アミノエチル）アミノプロピルメチルジエトキシシラン、Ｎ−（β−アミノエチル）アミノプロピルトリイソプロポキシシラン、γ−ウレイドプロピルトリメトキシシラン、Ｎ−フェニル−γ−アミノプロピルトリメトキシシラン、Ｎ−ベンジル−γ−アミノプロピルトリメトキシシラン、Ｎ−ビニルベンジル−γ−アミノプロピルトリエトキシシラン等を挙げることができる。また、これらを変性した誘導体である、アミノ変性シリルポリマー、シリル化アミノポリマー、不飽和アミノシラン錯体、フェニルアミノ長鎖アルキルシラン、アミノシリル化シリコーン等のアミノ基を有するシランカップリング剤；等のシラノール縮合触媒、さらには他の酸性触媒、塩基性触媒等の公知のシラノール縮合触媒等が例示できる。
【０１４７】
これらの触媒は、単独で使用してもよく、２種以上併用してもよい。この縮合触媒の配合量は、架橋性シリル基を少なくとも１個有するビニル系重合体１００部（重量部、以下同じ）に対して０．１〜２０部程度が好ましく、１〜１０部が更に好ましい。シラノール縮合触媒の配合量がこの範囲を下回ると硬化速度が遅くなることがあり、また硬化反応が十分に進行し難くなる場合がある。一方、シラノール縮合触媒の配合量がこの範囲を上回ると硬化時に局部的な発熱や発泡が生じ、良好な硬化物が得られ難くなるほか、ポットライフが短くなり過ぎ、作業性の点からも好ましくない。なお、特に限定はされないが、硬化性を制御するために錫系硬化触媒を用いるのが好ましい。
【０１４８】
また、本発明の硬化性組成物においては、縮合触媒の活性をより高めるために、アミン系化合物と同様に、上記のアミノ基を有するシランカップリング剤を助触媒として使用することも可能である。このアミノ基含有シランカップリング剤は、加水分解性基が結合したケイ素原子を含む基（以下加水分解性ケイ素基という）及びアミノ基を有する化合物であり、この加水分解性基として既に例示した基を挙げることができるが、メトキシ基、エトキシ基等が加水分解速度の点から好ましい。加水分解性基の個数は、２個以上、特に３個以上が好ましい。
【０１４９】
これらのアミン化合物の配合量は、ビニル系重合体（Ｉ）の有機重合体１００重量部に対して０．０１〜５０重量部程度が好ましく、更に０．１〜２０重量部がより好ましい。アミン化合物の配合量が０．０１重量部未満であると硬化速度が遅くなる場合があり、また硬化反応が充分に進行し難くなる場合がある。一方、アミン化合物の配合量が３０重量部を越えると、ポットライフが短くなり過ぎる場合があり、作業性の点から好ましくない。
【０１５０】
これらのアミン化合物は、１種類のみで使用しても良いし、２種類以上混合使用しても良い。
【０１５１】
更に、下記一般式（３７）
Ｒ^４９ _ａＳｉ（ＯＲ^５０）_４−ａ　（３７）
（式中、Ｒ^４９およびＲ^５０は、それぞれ独立に、炭素数１〜２０の置換あるいは非置換の炭化水素基である。さらに、ａは０、１、２、３のいずれかである。）で示されるアミノ基やシラノール基をもたないケイ素化合物を助触媒として添加しても構わない。
【０１５２】
前記ケイ素化合物としては、限定はされないが、フェニルトリメトキシシラン、フェニルメチルジメトキシシラン、フェニルジメチルメトキシシラン、ジフェニルジメトキシシラン、ジフェニルジエトキシシラン、トリフェニルメトキシシラン等の一般式（３７）中のＲ^４９が、炭素数６〜２０のアリール基であるものが、組成物の硬化反応を加速する効果が大きいために好ましい。特に、ジフェニルジメトキシシランやジフェニルジエトキシシランは、低コストであり、入手が容易であるために最も好ましい。
【０１５３】
このケイ素化合物の配合量は、ビニル系重合体１００部に対して０．０１〜２０部程度が好ましく、０．１〜１０部が更に好ましい。ケイ素化合物の配合量がこの範囲を下回ると硬化反応を加速する効果が小さくなる場合がある。一方、ケイ素化合物の配合量がこの範囲を上回ると、硬化物の硬度や引張強度が低下することがある。
【０１５４】
なお、硬化触媒・硬化剤の種類や添加量は、本発明の一般式（１）や（６）で表されるビニル系重合体のＹの種類やａの数によって選択することが可能であり、目的や用途に応じて本発明の硬化性や機械物性等を制御することが可能である。Ｙがアルコキシ基である場合、炭素数の少ない方が反応性が高く、またａが多い方が反応性が高いため少量で充分硬化させることが可能である。
アルケニル基の場合
アルケニル基を用いて架橋させる場合は、限定はされないが、ヒドロシリル基含有化合物を硬化剤とし、ヒドロシリル化触媒を用いてヒドロシリル化反応により架橋させることが好ましい。
【０１５５】
ヒドロシリル基含有化合物としては、アルケニル基を有する重合体と架橋により硬化できるヒドロシリル基含有化合物であれば特に制限はなく、各種のものを用いることができる。例えば、一般式（３８）または（３９）で表される鎖状ポリシロキサン；
Ｒ^５１ _３ＳｉＯ−［Ｓｉ（Ｒ^５１）_２Ｏ］_ａ−［Ｓｉ（Ｈ）（Ｒ^５２）Ｏ］_ｂ−［Ｓｉ（Ｒ^５２）（Ｒ^５３）Ｏ］_ｃ−ＳｉＲ^５１ _３　　（３８）
ＨＲ^５１ _２ＳｉＯ−［Ｓｉ（Ｒ^５１）_２Ｏ］_ａ−［Ｓｉ（Ｈ）（Ｒ^５２）Ｏ］_ｂ−［Ｓｉ（Ｒ^５２）（Ｒ^５３）Ｏ］_ｃ−ＳｉＲ^５１ _２Ｈ　　（３９）
（式中、Ｒ^５１およびＲ^５２は炭素数１〜６のアルキル基、または、フェニル基、Ｒ^５３は炭素数１〜１０のアルキル基またはアラルキル基を示す。ａは０≦ａ≦１００、ｂは２≦ｂ≦１００、ｃは０≦ｃ≦１００を満たす整数を示す。）
一般式（４０）で表される環状シロキサン；
【０１５６】
【化７】

（式中、Ｒ^５４およびＲ^５５は炭素数１〜６のアルキル基、または、フェニル基、Ｒ^５６は炭素数１〜１０のアルキル基またはアラルキル基を示す。ｄは０≦ｄ≦８、ｅは２≦ｅ≦１０、ｆは０≦ｆ≦８の整数を表し、かつ３≦ｄ＋ｅ＋ｆ≦１０を満たす。）
等の化合物を用いることができる。
【０１５７】
これらは単独で用いても２種以上を混合して用いてもかまわない。これらのシロキサンの中でも（メタ）アクリル系重合体との相溶性の観点から、フェニル基を有する下記一般式（４１）、（４２）で表される鎖状シロキサンや、一般式（４３）、（４４）で表される環状シロキサンが好ましい。
（ＣＨ_３）_３ＳｉＯ−［Ｓｉ（Ｈ）（ＣＨ_３）Ｏ］_ｇ−［Ｓｉ（Ｃ_６Ｈ_５）_２Ｏ］_ｈ−Ｓｉ（ＣＨ_３）_３　（４１）
（ＣＨ_３）_３ＳｉＯ−［Ｓｉ（Ｈ）（ＣＨ_３）Ｏ］_ｇ−［Ｓｉ（ＣＨ_３）｛ＣＨ_２Ｃ（Ｈ）（Ｒ^５７）Ｃ_６Ｈ_５｝Ｏ］_ｈ−Ｓｉ（ＣＨ_３）_３　（４２）
（式中、Ｒ^５７は水素またはメチル基を示す。ｇは２≦ｇ≦１００、ｈは０≦ｈ≦１００の整数を示す。Ｃ_６Ｈ_５はフェニル基を示す。）
【０１５８】
【化８】

（式中、Ｒ^５７は水素、またはメチル基を示す。ｉは２≦ｉ≦１０、ｊは０≦ｊ≦８、かつ３≦ｉ＋ｊ≦１０を満たす整数を示す。Ｃ_６Ｈ_５はフェニル基を示す。）ヒドロシリル基含有化合物としてはさらに、分子中に２個以上のアルケニル基を有する低分子化合物に対し、一般式（３８）から（４４）に表されるヒドロシリル基含有化合物を、反応後にも一部のヒドロシリル基が残るようにして付加反応させて得られる化合物を用いることもできる。分子中に２個以上のアルケニル基を有する化合物としては、各種のものを用いることができる。例示するならば、１，４−ペンタジエン、１，５−ヘキサジエン、１，６−ヘプタジエン、１，７−オクタジエン、１，８−ノナジエン、１，９−デカジエン等の炭化水素系化合物、Ｏ，Ｏ’−ジアリルビスフェノールＡ、３，３’−ジアリルビスフェノールＡ等のエーテル系化合物、ジアリルフタレート、ジアリルイソフタレート、トリアリルトリメリテート、テトラアリルピロメリテート等のエステル系化合物、ジエチレングリコールジアリルカーボネート等のカーボネート系化合物が挙げられる。
【０１５９】
上記一般式（３８）から（４４）に示した過剰量のヒドロシリル基含有化合物に対し、ヒドロシリル化触媒の存在下、上に挙げたアルケニル基含有化合物をゆっくり滴下することにより該化合物を得ることができる。このような化合物のうち、原料の入手容易性、過剰に用いたシロキサンの除去のしやすさ、さらにはビニル系重合体（Ｉ）への相溶性を考慮して、下記のものが好ましい。
【０１６０】
【化９】

重合体と硬化剤は任意の割合で混合することができるが、硬化性の面から、アルケニル基とヒドロシリル基のモル比が５〜０．２の範囲にあることが好ましく、さらに、２．５〜０．４であることが特に好ましい。モル比が５以上になると硬化が不十分でべとつきのある強度の小さい硬化物しか得られず、また、０．２より小さいと、硬化後も硬化物中に活性なヒドロシリル基が大量に残るので、クラック、ボイドが発生し、均一で強度のある硬化物が得られない。
【０１６１】
重合体と硬化剤との硬化反応は、２成分を混合して加熱することにより進行するが、反応をより迅速に進めるために、ヒドロシリル化触媒を添加することができる。このようなヒドロシリル化触媒としては特に限定されず、例えば、有機過酸化物やアゾ化合物等のラジカル開始剤、および遷移金属触媒が挙げられる。
【０１６２】
ラジカル開始剤としては特に限定されず、例えば、ジ−ｔ−ブチルペルオキシド、２，５−ジメチル−２，５−ジ（ｔ−ブチルペルオキシ）ヘキサン、２，５−ジメチル−２，５−ジ（ｔ−ブチルペルオキシ）−３−ヘキシン、ジクミルペルオキシド、ｔ−ブチルクミルペルオキシド、α，α’−ビス（ｔ−ブチルペルオキシ）イソプロピルベンゼンのようなジアルキルペルオキシド、ベンゾイルペルオキシド、ｐ−クロロベンゾイルペルオキシド、ｍ−クロロベンゾイルペルオキシド、２，４−ジクロロベンゾイルペルオキシド、ラウロイルペルオキシドのようなジアシルペルオキシド、過安息香酸−ｔ−ブチルのような過酸エステル、過ジ炭酸ジイソプロピル、過ジ炭酸ジ−２−エチルヘキシルのようなペルオキシジカーボネート、１，１−ジ（ｔ−ブチルペルオキシ）シクロヘキサン、１，１−ジ（ｔ−ブチルペルオキシ）−３，３，５−トリメチルシクロヘキサンのようなペルオキシケタール等を挙げることができる。
【０１６３】
また、遷移金属触媒としても特に限定されず、例えば、白金単体、アルミナ、シリカ、カーボンブラック等の担体に白金固体を分散させたもの、塩化白金酸、塩化白金酸とアルコール、アルデヒド、ケトン等との錯体、白金−オレフィン錯体、白金（０）−ジビニルテトラメチルジシロキサン錯体が挙げられる。白金化合物以外の触媒の例としては、ＲｈＣｌ（ＰＰｈ_３）_３，ＲｈＣｌ_３，ＲｕＣｌ_３，ＩｒＣｌ_３，ＦｅＣｌ_３，ＡｌＣｌ_３，ＰｄＣｌ_２・Ｈ_２Ｏ，ＮｉＣｌ_２，ＴｉＣｌ_４等が挙げられる。これらの触媒は単独で用いてもよく、２種類以上を併用してもかまわない。触媒量としては特に制限はないが、ビニル系重合体（Ｉ）のアルケニル基１ｍｏｌに対し、１０^−１〜１０^−８ｍｏｌの範囲で用いるのが良く、好ましくは１０^−３〜１０^−６ｍｏｌの範囲で用いるのがよい。１０^−８ｍｏｌより少ないと硬化が十分に進行しない。またヒドロシリル化触媒は高価であるので１０^−１ｍｏｌ以上用いないのが好ましい。
【０１６４】
硬化温度については特に制限はないが、一般に０℃〜２００℃、好ましくは３０℃〜１５０℃、さらに好ましくは８０℃〜１５０℃で硬化させるのがよい。
水酸基の場合
本発明の水酸基を有する重合体は、水酸基と反応し得る官能基を２個以上有する化合物を硬化剤として用いることにより、均一に硬化する。硬化剤の具体例としては、例えば、１分子中に２個以上のイソシアネート基を有する多価イソシアネート化合物、メチロール化メラミンおよびそのアルキルエーテル化物または低縮合化物等のアミノプラスト樹脂、多官能カルボン酸およびそのハロゲン化物等が挙げられる。これらの硬化剤を使用して硬化物を作成する際には、それぞれ適当な硬化触媒を使用することができる。
アミノ基の場合
本発明のアミノ基を有する重合体は、アミノ基と反応し得る官能基を２個以上有する化合物を硬化剤として用いることにより、均一に硬化する。硬化剤の具体例としては、例えば、１分子中に２個以上のイソシアネート基を有する多価イソシアネート化合物、メチロール化メラミンおよびそのアルキルエーテル化物または低縮合化物等のアミノプラスト樹脂、多官能カルボン酸およびそのハロゲン化物等が挙げられる。これらの硬化剤を使用して硬化物を作成する際には、それぞれ適当な硬化触媒を使用することができる。
エポキシ基の場合
本発明のエポキシ基を有する重合体の硬化剤としては特に限定されないが、例えば、脂肪族アミン類、脂環族アミン類、芳香族アミン類；酸無水物；ポリアミド；イミダゾール類；アミンイミド；ユリア；メラミンとその誘導体；ポリアミンの塩；フェノール樹脂；ポリメルカプタン、ポリスルフィド；芳香族ジアゾニウム塩、ジアリルヨードニウム塩、トリアリルスルホニウム塩、トリアリルセレニウム塩等の光・紫外線硬化剤等が用いられる。
重合性の炭素−炭素二重結合の場合
重合性の炭素−炭素二重結合を有する重合体は、その重合性の炭素−炭素二重結合の重合反応により架橋させることができる。
【０１６５】
架橋の方法としては、活性エネルギー線で硬化するもの、あるいは、熱で硬化するものが挙げられる。活性エネルギー線硬化性組成物においては、光重合開始剤が光ラジカル開始剤、あるいは、光アニオン開始剤であることが好ましい。熱硬化性組成物においては、熱重合開始剤が、アゾ系開始剤、過酸化物、過硫酸物、及びレドックス開始剤からなる群より選択されるものであるが好ましい。
【０１６６】
以下に詳細にこれらの架橋反応について説明する。
【０１６７】
重合性の炭素−炭素二重結合を有する重合体を架橋させる場合には、その目的に応じて、重合性のモノマー及び／又はオリゴマーや各種添加剤を併用しても構わない。重合性のモノマー及び／又はオリゴマーとしては、ラジカル重合性の基を持つモノマー及び／又はオリゴマー、あるいはアニオン重合性の基を持つモノマー及び／又はオリゴマーが好ましい。ラジカル重合性の基としては、（メタ）アクリル基等のアクリル官能性基、スチレン基、アクリロニトリル基、ビニルエステル基、Ｎ−ビニルピロリドン基、アクリルアミド基、共役ジエン基、ビニルケトン基、塩化ビニル基等が挙げられる。なかでも、本発明の重合体と類似する（メタ）アクリル基を持つものが好ましい。アニオン重合性の基としては、（メタ）アクリル基、スチレン基、アクリロニトリル基、Ｎ−ビニルピロリドン基、アクリルアミド基、共役ジエン基、ビニルケトン基、等が挙げられる。なかでも、アクリル官能性基を持つものが好ましい。
【０１６８】
上記のモノマーの具体例としては、（メタ）アクリレート系モノマー、環状アクリレート、Ｎ−ビニルピロリドン、スチレン系モノマー、アクリロニトリル、Ｎ−ビニルピロリドン、アクリルアミド系モノマー、共役ジエン系モノマー、ビニルケトン系モノマーなどが挙げられる。（メタ）アクリレート系モノマーとしては、（メタ）アクリル酸ｎ−ブチル、（メタ）アクリル酸２−エチルヘキシル、（メタ）アクリル酸イソオクチル、（メタ）アクリル酸イソノニルや下式の化合物などを挙げることができる。
【０１６９】
【化１０】

【０１７０】
【化１１】

【０１７１】
【化１２】

【０１７２】
【化１３】

【０１７３】
【化１４】

スチレン系モノマーとしてはスチレン、α−メチルスチレン等が、アクリルアミド系モノマーとしてはアクリルアミド、Ｎ，Ｎ−ジメチルアクリルアミド等が、共役ジエン系モノマーとしてはブタジエン、イソプレン等が、ビニルケトン系モノマーとしてはメチルビニルケトン等が挙げられる。
【０１７４】
多官能モノマーとしては、ネオペンチルグリコールポリプロポキシジアクリレート、トリメチロールプロパンポリエトキシトリアクリレート、ビスフェノールＦポリエトキシジアクリレート、ビスフェノールＡポリエトキシジアクリレート、ジペンタエリスリトールポリヘキサノリドヘキサクリレート、トリス（ヒドロキシエチル）イソシアヌレートポリヘキサノリドトリアクリレート、トリシクロデカンジメチロールジアクリレート２−（２−アクリロイルオキシ−１，１−ジメチル）−５−エチル−５−アクリロイルオキシメチル−１，３−ジオキサン、テトラブロモビスフェノールＡジエトキシジアクリレート、４，４−ジメルカプトジフェニルサルファイドジメタクリレート、ポリテトラエチレングリコールジアクリレート、１，９−ノナンジオールジアクリレート、ジトリメチロールプロパンテトラアクリレート等が挙げられる。
【０１７５】
オリゴマーとしては、ビスフェノールＡ型エポキシアクリレート樹脂、フェノールノボラック型エポキシアクリレート樹脂、クレゾールノボラック型エポキシアクリレート樹脂等のエポキシアクリレート系樹脂、ＣＯＯＨ基変性エポキシアクリレート系樹脂、ポリオール（ポリテトラメチレングリコール、エチレングリコールとアジピン酸のポリエステルジオール、ε−カプロラクトン変性ポリエステルジオール、ポリプロピレングリコール、ポリエチレングリコール、ポリカーボネートジオール、水酸基末端水添ポリイソプレン、水酸基末端ポリブタジエン、水酸基末端ポリイソブチレン等）と有機イソシアネート（トリレンジイソシアネート、イソホロンジイソシアネート、ジフェニルメタンジイソシアネート、ヘキサメチレンジイソシアネート、キシリレンジイソシアネート等）から得られたウレタン樹脂を水酸基含有（メタ）アクリレート｛ヒドロキシエチル（メタ）アクリレート、ヒドロキシプロピル（メタ）アクリレート、ヒドロキシブチル（メタ）アクリレート、ペンタエリスリトールトリアクリレート等｝を反応させて得られたウレタンアクリレート系樹脂、上記ポリオールにエステル結合を介して（メタ）アクリル基を導入した樹脂、ポリエステルアクリレート系樹脂等が挙げられる。
【０１７６】
これらのモノマー及びオリゴマーは、用いられる開始剤及び硬化条件により選択される。
【０１７７】
また、アクリル官能性基を有するモノマー及び／又はオリゴマーの数平均分子量は、２０００以下であることが好ましく、１０００以下であることが、相溶性が良好であるという理由からさらに好ましい。
【０１７８】
重合性の炭素−炭素二重結合を有する重合体の架橋の方法としては、ＵＶや電子線などの活性エネルギー線によることが好ましい。
【０１７９】
活性エネルギー線により架橋させる場合には、光重合開始剤を含有することが好ましい。
【０１８０】
本発明に用いられる光重合開始剤としては特に制限はないが、光ラジカル開始剤と光アニオン開始剤が好ましく、特に光ラジカル開始剤が好ましい。例えば、アセトフェノン、プロピオフェノン、ベンゾフェノン、キサントール、フルオレノン、ベンズアルデヒド、アンスラキノン、トリフェニルアミン、カルバゾール、３−メチルアセトフェノン、４−メチルアセトフェノン、３−ペンチルアセトフェノン、４−メトキシアセトフェン、３−ブロモアセトフェノン、４−アリルアセトフェノン、ｐ−ジアセチルベンゼン、３−メトキシベンゾフェノン、４−メチルベンゾフェノン、４−クロロベンゾフェノン、４，４‘−ジメトキシベンゾフェノン、４−クロロ−４’−ベンジルベンゾフェノン、３−クロロキサントーン、３，９−ジクロロキサントーン、３−クロロ−８−ノニルキサントーン、ベンゾイル、ベンゾインメチルエーテル、ベンゾインブチルエーテル、ビス（４−ジメチルアミノフェニル）ケトン、ベンジルメトキシケタール、２−クロロチオキサントーン等が挙げられる。これらの開始剤は単独でも、他の化合物と組み合わせても良い。具体的には、ジエタノールメチルアミン、ジメチルエタノールアミン、トリエタノールアミンなどのアミンとの組み合わせ、更にこれにジフェニルヨードニウムクロリドなどのヨードニウム塩と組み合わせたもの、メチレンブルーなどの色素及びアミンと組み合わせたものが挙げられる。
【０１８１】
また、近赤外光重合開始剤として、近赤外光吸収性陽イオン染料を使用しても構わない。近赤外光吸収性陽イオン染料としては、６５０〜１５００ｎｍの領域の光エネルギーで励起する、例えば特開平３−１１１４０２号、特開平５−１９４６１９号公報等に開示されている近赤外光吸収性陽イオン染料−ボレート陰イオン錯体などを用いるのが好ましく、ホウ素系増感剤を併用することがさらに好ましい。
【０１８２】
光重合開始剤の添加量は系をわずかに光官能化するだけでよいので、特に制限はないが、この組成物の重合体１００部に対して、０．００１〜１０重量部が好ましい。
【０１８３】
本発明の活性エネルギー線硬化性組成物を硬化させる方法は特に限定されないが、その光重合開始剤開始剤の性質に応じて、高圧水銀灯、低圧水銀灯、電子線照射装置、ハロゲンランプ、発光ダイオード、半導体レーザー等による光及び電子線の照射が挙げられる。
【０１８４】
また、重合性の炭素−炭素二重結合を有する重合体の架橋の方法としては、熱によることが好ましい。
【０１８５】
活性エネルギー線により架橋させる場合には、熱重合開始剤を含有することが好ましい。
【０１８６】
本発明に用いられる熱重合開始剤としては特に制限はないが、アゾ系開始剤、過酸化物、過硫酸酸、及びレドックス開始剤が含まれる。
【０１８７】
適切なアゾ系開始剤としては、限定されるわけではないが、２，２′−アゾビス（４−メトキシ−２，４−ジメチルバレロニトリル）（ＶＡＺＯ　３３）、２，２′−アゾビス（２−アミジノプロパン）二塩酸塩（ＶＡＺＯ　５０）、２，２′−アゾビス（２，４−ジメチルバレロニトリル）（ＶＡＺＯ　５２）、２，２′−アゾビス（イソブチロニトリル）（ＶＡＺＯ　６４）、２，２′−アゾビス−２−メチルブチロニトリル（ＶＡＺＯ　６７）、１，１−アゾビス（１−シクロヘキサンカルボニトリル）（ＶＡＺＯ　８８）（全てＤｕＰｏｎｔ　Ｃｈｅｍｉｃａｌから入手可能）、２，２′−アゾビス（２−シクロプロピルプロピオニトリル）、及び２，２′−アゾビス（メチルイソブチレ−ト）（Ｖ−６０１）（和光純薬より入手可能）等が挙げられる。
【０１８８】
適切な過酸化物開始剤としては、限定されるわけではないが、過酸化ベンゾイル、過酸化アセチル、過酸化ラウロイル、過酸化デカノイル、ジセチルパーオキシジカーボネート、ジ（４−ｔ−ブチルシクロヘキシル）パーオキシジカーボネート（Ｐｅｒｋａｄｏｘ　１６Ｓ）（Ａｋｚｏ　Ｎｏｂｅｌから入手可能）、ジ（２−エチルヘキシル）パーオキシジカーボネート、ｔ−ブチルパーオキシピバレート（Ｌｕｐｅｒｓｏｌ　１１）（Ｅｌｆ　Ａｔｏｃｈｅｍから入手可能）、ｔ−ブチルパーオキシ−２−エチルヘキサノエート（Ｔｒｉｇｏｎｏｘ　２１−Ｃ５０）（Ａｋｚｏ　Ｎｏｂｅｌから入手可能）、及び過酸化ジクミル等が挙げられる。
【０１８９】
適切な過硫酸塩開始剤としては、限定されるわけではないが、過硫酸カリウム、過硫酸ナトリウム、及び過硫酸アンモニウムが挙げられる。
【０１９０】
適切なレドックス（酸化還元）開始剤としては、限定されるわけではないが、上記過硫酸塩開始剤のメタ亜硫酸水素ナトリウム及び亜硫酸水素ナトリウムのような還元剤との組み合わせ；有機過酸化物と第３級アミンに基づく系、例えば過酸化ベンゾイルとジメチルアニリンに基づく系；並びに有機ヒドロパーオキシドと遷移金属に基づく系、例えばクメンヒドロパーオキシドとコバルトナフテートに基づく系等が挙げられる。
【０１９１】
他の開始剤としては、限定されるわけではないが、テトラフェニル１，１，２，２−エタンジオールのようなピナコール等が挙げられる。
【０１９２】
好ましい熱ラジカル開始剤としては、アゾ系開始剤及び過酸化物系開始剤からなる群から選ばれる。更に好ましいものは、２，２′−アゾビス（メチルイソブチレ−ト）、ｔ−ブチルパーオキシピバレート、及びジ（４−ｔ−ブチルシクロヘキシル）パーオキシジカーボネート、並びにこれらの混合物である。
【０１９３】
本発明に用いられる熱開始剤は触媒的に有効な量で存在し、このような量は、限定はされないが、典型的には、本発明の少なくとも一つの末端にアクリル官能性基を有する重合体及び他に添加されるモノマー及びオリゴマー混合物の合計量を１００重量部とした場合に約０．０１〜５重量部、より好ましくは約０．０２５〜２重量部である。開始剤の混合物が使用される場合には、開始剤の混合物の合計量は、あたかもただ１種の開始剤が使用されるかのような量である。
【０１９４】
本発明の熱硬化性組成物を硬化させる方法は特に限定されないが、その温度は、使用する熱開始剤、重合体（Ｉ）及び添加される化合物等の種類により異なるが、通常５０℃〜２５０℃の範囲内が好ましく、７０℃〜２００℃の範囲内がより好ましい。硬化時間は、使用する重合開始剤、単量体、溶媒、反応温度等により異なるが、通常１分〜１０時間の範囲内である。
＜接着性付与剤＞
本発明の組成物には、シランカップリング剤や、シランカップリング剤以外の接着性付与剤を添加することができる。接着付与剤を添加すると、外力により目地幅等が変動することによって、シーリング材がサイディングボード等の被着体から剥離する危険性をより低減することができる。また、場合によっては接着性向上の為に用いるプライマーの使用の必要性がなくなり、施工作業の簡略化が期待される。シランカップリング剤の具体例としてはアミノ基や、メルカプト基、エポキシ基、カルボキシル基、ビニル基、イソシアネート基、イソシアヌレート、ハロゲン等の官能基をもったシランカップリング剤が例示でき、その具体例としては、γ−イソシアネートプロピルトリメトキシシラン、γ−イソシアネートプロピルトリエトキシシラン、γ−イソシアネートプロピルメチルジエトキシシラン、γ−イソシアネートプロピルメチルジメトキシシラン等のイソシアネート基含有シラン類；γ−アミノプロピルトリメトキシシラン、γ−アミノプロピルトリエトキシシラン、γ−アミノプロピルトリイソプロポキシシラン、γ−アミノプロピルメチルジメトキシシラン、γ−アミノプロピルメチルジエトキシシラン、γ−（２−アミノエチル）アミノプロピルトリメトキシシラン、γ−（２−アミノエチル）アミノプロピルメチルジメトキシシラン、γ−（２−アミノエチル）アミノプロピルトリエトキシシラン、γ−（２−アミノエチル）アミノプロピルメチルジエトキシシラン、γ−（２−アミノエチル）アミノプロピルトリイソプロポキシシラン、γ−ウレイドプロピルトリメトキシシラン、Ｎ−フェニル−γ−アミノプロピルトリメトキシシラン、Ｎ−ベンジル−γ−アミノプロピルトリメトキシシラン、Ｎ−ビニルベンジル−γ−アミノプロピルトリエトキシシラン等のアミノ基含有シラン類；γ−メルカプトプロピルトリメトキシシラン、γ−メルカプトプロピルトリエトキシシラン、γ−メルカプトプロピルメチルジメトキシシラン、γ−メルカプトプロピルメチルジエトキシシラン等のメルカプト基含有シラン類；γ−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシプロピルトリエトキシシラン、γ−グリシドキシプロピルメチルジメトキシシラン、β−（３，４−エポキシシクロヘキシル）エチルトリメトキシシラン、β−（３，４−エポキシシクロヘキシル）エチルトリエトキシシラン等のエポキシ基含有シラン類；β−カルボキシエチルトリエトキシシラン、β−カルボキシエチルフェニルビス（２−メトキシエトキシ）シラン、Ｎ−β−（カルボキシメチル）アミノエチル−γ−アミノプロピルトリメトキシシラン等のカルボキシシラン類；ビニルトリメトキシシラン、ビニルトリエトキシシラン、γ−メタクリロイルオキシプロピルメチルジメトキシシラン、γ−アクロイルオキシプロピルメチルトリエトキシシラン等のビニル型不飽和基含有シラン類；γ−クロロプロピルトリメトキシシラン等のハロゲン含有シラン類；トリス（トリメトキシシリル）イソシアヌレート等のイソシアヌレートシラン類等を挙げることができる。また、これらを変性した誘導体である、アミノ変性シリルポリマー、シリル化アミノポリマー、不飽和アミノシラン錯体、フェニルアミノ長鎖アルキルシラン、アミノシリル化シリコーン、ブロックイソシアネートシラン、シリル化ポリエステル等もシランカップリング剤として用いることができる。
【０１９５】
本発明に用いるシランカップリング剤は、通常、架橋性シリル基含有ビニル系重合体１００部に対し、０．１〜２０部の範囲で使用される。特に、０．５〜１０部の範囲で使用するのが好ましい。本発明の硬化性組成物に添加されるシランカップリング剤の効果は、各種被着体、すなわち、ガラス、アルミニウム、ステンレス、亜鉛、銅、モルタルなどの無機基材や、塩ビ、アクリル、ポリエステル、ポリエチレン、ポリプロピレン、ポリカーボネートなどの有機基材に用いた場合、ノンプライマー条件またはプライマー処理条件下で、著しい接着性改善効果を示す。ノンプライマー条件下で使用した場合には、各種被着体に対する接着性を改善する効果が特に顕著である。
【０１９６】
シランカップリング剤以外の具体例としては、特に限定されないが、例えば、エポキシ樹脂、フェノール樹脂、硫黄、アルキルチタネート類、芳香族ポリイソシアネート等が挙げられる。
【０１９７】
上記接着性付与剤は１種類のみで使用しても良いし、２種類以上混合使用しても良い。これら接着性付与剤は添加することにより被着体に対する接着性を改善することができる。特に限定はされないが、接着性、特にオイルパンなどの金属被着面に対する接着性を向上させるために、上記接着性付与剤の中でもシランカップリング剤を０．１〜２０重量部、併用することが好ましい。
【０１９８】
接着性付与剤の種類や添加量は、本発明の一般式（１）や（６）で表されるビニル系重合体のＹの種類やａの数によって選択することが可能であり、目的や用途に応じて本発明の硬化性や機械物性等を制御することが可能である。特に硬化性や伸びに影響するためその選択には注意が必要である。
＜可塑剤＞
本発明の硬化性組成物には、各種可塑剤を必要に応じて用いても良い。可塑剤を後述する充填材と併用して使用すると硬化物の伸びを大きくできたり、多量の充填材を混合できたりするためより有利となるが、必ずしも添加しなければならないものではない。可塑剤としては特に限定されないが、物性の調整、性状の調節等の目的により、例えば、ジブチルフタレート、ジヘプチルフタレート、ジ（２−エチルヘキシル）フタレート、ブチルベンジルフタレート等のフタル酸エステル類；ジオクチルアジペート、ジオクチルセバケート、ジブチルセバケート、コハク酸イソデシル等の非芳香族二塩基酸エステル類；オレイン酸ブチル、アセチルリシリノール酸メチル等の脂肪族エステル類；ジエチレングリコールジベンゾエート、トリエチレングリコールジベンゾエート、ペンタエリスリトールエステル等のポリアルキレングリコールのエステル類；トリクレジルホスフェート、トリブチルホスフェート等のリン酸エステル類；トリメリット酸エステル類；ポリスチレンやポリ−α−メチルスチレン等のポリスチレン類；ポリブタジエン、ポリブテン、ポリイソブチレン、ブタジエン−アクリロニトリル、ポリクロロプレン；塩素化パラフィン類；アルキルジフェニル、部分水添ターフェニル、等の炭化水素系油；プロセスオイル類；ポリエチレングリコール、ポリプロピレングリコール、ポリテトラメチレングリコール等のポリエーテルポリオールとこれらポリエーテルポリオールの水酸基をエステル基、エーテル基などに変換した誘導体等のポリエーテル類；エポキシ化大豆油、エポキシステアリン酸ベンジル等のエポキシ可塑剤類；セバシン酸、アジピン酸、アゼライン酸、フタル酸等の２塩基酸とエチレングリコール、ジエチレングリコール、トリエチレングリコール、プロピレングリコール、ジプロピレングリコール等の２価アルコールから得られるポリエステル系可塑剤類；アクリル系可塑剤を始めとするビニル系モノマーを種々の方法で重合して得られるビニル系重合体類等が挙げられる。
【０１９９】
なかでも数平均分子量５００〜１５０００の重合体である高分子可塑剤は、添加することにより、該硬化性組成物の粘度やスランプ性および該組成物を硬化して得られる硬化物の引張り強度、伸びなどの機械特性が調整できるとともに、重合体成分を分子中に含まない可塑剤である低分子可塑剤を使用した場合に比較して、初期の物性を長期にわたり維持し、該硬化物にアルキッド塗料を塗布した場合の乾燥性（塗装性ともいう）を改良できる。なお、限定はされないがこの高分子可塑剤は、官能基を有しても有しなくても構わない。
【０２００】
上記で高分子可塑剤の数平均分子量は、５００〜１５０００と記載したが、好ましくは８００〜１００００であり、より好ましくは１０００〜８０００である。分子量が低すぎると熱や降雨により可塑剤が経時的に流出し、初期の物性を長期にわたり維持できず、また、アルキッド塗装性が改善できないことがある。また、分子量が高すぎると粘度が高くなり、作業性が悪くなる。
【０２０１】
これらの高分子可塑剤のうちで、ビニル系重合体と相溶するものが好ましい。中でも相溶性および耐候性、耐熱性の点からビニル系重合体が好ましい。ビニル系重合体の中でも（メタ）アクリル系重合体が好ましく、アクリル系重合体がさらに好ましい。このアクリル系重合体の合成法は、従来からの溶液重合で得られるものや、無溶剤型アクリルポリマー等を挙げることができる。後者のアクリル系可塑剤は溶剤や連鎖移動剤を使用せず高温連続重合法（ＵＳＰ４４１４３７０、特開昭５９−６２０７、特公平５−５８００５、特開平１−３１３５２２、ＵＳＰ５０１０１６６）にて作製されるため本発明の目的にはより好ましい。その例としては特に限定されないが東亞合成品ＵＰシリーズ等が挙げられる（工業材料１９９９年１０月号参照）。勿論、他の合成法としてリビングラジカル重合法をも挙げることができる。この方法によれば、その重合体の分子量分布が狭く、低粘度化が可能なことから好ましく、更には原子移動ラジカル重合法がより好ましいが、これに限定されるものではない。
【０２０２】
高分子可塑剤の分子量分布は特に限定されないが、狭いことが好ましく、１．８未満が好ましい。１．７以下がより好ましく、１．６以下がなお好ましく、１．５以下がさらに好ましく、１．４以下が特に好ましく、１．３以下が最も好ましい。
【０２０３】
上記高分子可塑剤を含む可塑剤は、単独で使用してもよく、２種以上を併用してもよいが、必ずしも必要とするものではない。また必要によっては高分子可塑剤を用い、物性に悪影響を与えない範囲で低分子可塑剤を更に併用しても良い。
【０２０４】
なおこれら可塑剤は、重合体製造時に配合することも可能である。
【０２０５】
可塑剤を用いる場合の使用量は、限定されないが、ビニル系重合体１００重量部に対して５〜１５０重量部、好ましくは１０〜１２０重量部、さらに好ましくは２０〜１００重量部である。５重量部未満では可塑剤としての効果が発現しなくなり、１５０重量部を越えると硬化物の機械強度が不足する。
＜充填材＞
本発明の硬化性組成物には、本発明の平均粒径１μｍ以上５００μｍ以下のシリカ（ＩＩ）の効果を妨げない程度に、各種充填材を必要に応じて用いても良い。充填材としては、特に限定されないが、木粉、パルプ、木綿チップ、アスベスト、ガラス繊維、炭素繊維、マイカ、クルミ殻粉、もみ殻粉、グラファイト、ケイソウ土、白土、シリカ（ヒュームドシリカ、沈降性シリカ、結晶性シリカ、溶融シリカ、ドロマイト、無水ケイ酸、含水ケイ酸等）、カーボンブラックのような補強性充填材；重質炭酸カルシウム、膠質炭酸カルシウム、炭酸マグネシウム、ケイソウ土、焼成クレー、クレー、タルク、酸化チタン、ベントナイト、有機ベントナイト、酸化第二鉄、べんがら、アルミニウム微粉末、フリント粉末、酸化亜鉛、活性亜鉛華、亜鉛末、炭酸亜鉛およびシラスバルーンなどのような充填材；石綿、ガラス繊維およびガラスフィラメント、炭素繊維、ケブラー繊維、ポリエチレンファイバー等のような繊維状充填材等が挙げられる。
【０２０６】
これら充填材のうちでは沈降性シリカ、ヒュームドシリカ、結晶性シリカ、溶融シリカ、ドロマイト、カーボンブラック、炭酸カルシウム、酸化チタン、タルクなどが好ましい。
【０２０７】
特に、これら充填材で強度の高い硬化物を得たい場合には、主にヒュームドシリカ、沈降性シリカ、無水ケイ酸、含水ケイ酸、カーボンブラック、表面処理微細炭酸カルシウム、結晶性シリカ、溶融シリカ、焼成クレー、クレーおよび活性亜鉛華などから選ばれる充填材を添加できる。なかでも、比表面積（ＢＥＴ吸着法による）が５０ｍ^２／ｇ以上、通常５０〜４００ｍ^２／ｇ、好ましくは１００〜３００ｍ^２／ｇ程度の超微粉末状のシリカが好ましい。またその表面が、オルガノシランやオルガノシラザン、ジオルガノポリシロキサン等の有機ケイ素化合物で予め疎水処理されたシリカが更に好ましい。
【０２０８】
補強性の高いシリカ系充填材のより具体的な例としては、特に限定されないが、燃焼法シリカ（ヒュームドシリカ）の１つである日本アエロジル社のアエロジルや、沈降法シリカの１つである日本シリカ社工業のＮｉｐｓｉｌ等が挙げられる。特にヒュームドシリカについては、一次粒子の平均粒径５ｎｍ以上５０ｎｍ以下のヒュームドシリカを用いると、補強効果が特に大きいのでより好ましい。
【０２０９】
また、低強度で伸びが大である硬化物を得たい場合には、主に酸化チタン、炭酸カルシウム、タルク、酸化第二鉄、酸化亜鉛およびシラスバルーンなどから選ばれる充填材を添加できる。なお、一般的に、炭酸カルシウムは、比表面積が小さいと、硬化物の破断強度、破断伸び、接着性と耐候接着性の改善効果が充分でないことがある。比表面積の値が大きいほど、硬化物の破断強度、破断伸び、接着性と耐候接着性の改善効果はより大きくなる。
【０２１０】
更に、炭酸カルシウムは、表面処理剤を用いて表面処理を施してある方がより好ましい。表面処理炭酸カルシウムを用いた場合、表面処理していない炭酸カルシウムを用いた場合に比較して、本発明の組成物の作業性を改善し、該硬化性組成物の接着性と耐候接着性の改善効果がより向上すると考えられる。前記の表面処理剤としては脂肪酸、脂肪酸石鹸、脂肪酸エステル等の有機物や各種界面活性剤、および、シランカップリング剤やチタネートカップリング剤等の各種カップリング剤が用いられている。具体例としては、以下に限定されるものではないが、カプロン酸、カプリル酸、ペラルゴン酸、カプリン酸、ウンデカン酸、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、ベヘン酸、オレイン酸等の脂肪酸と、それら脂肪酸のナトリウム、カリウム等の塩、そして、それら脂肪酸のアルキルエステルが挙げられる。界面活性剤の具体例としては、ポリオキシエチレンアルキルエーテル硫酸エステルや長鎖アルコール硫酸エステル等と、それらのナトリウム塩、カリウム塩等の硫酸エステル型陰イオン界面活性剤、またアルキルベンゼンスルホン酸、アルキルナフタレンスルホン酸、パラフィンスルホン酸、α−オレフィンスルホン酸、アルキルスルホコハク酸等と、それらのナトリウム塩、カリウム塩等のスルホン酸型陰イオン界面活性剤等が挙げられる。この表面処理剤の処理量は、炭酸カルシウムに対して、０．１〜２０重量％の範囲で処理するのが好ましく、１〜５重量％の範囲で処理するのがより好ましい。処理量が０．１重量％未満の場合には、作業性、接着性と耐候接着性の改善効果が充分でないことがあり、２０重量％を越えると、該硬化性組成物の貯蔵安定性が低下することがある。
【０２１１】
特に限定はされないが、炭酸カルシウムを用いる場合、配合物のチクソ性や硬化物の破断強度、破断伸び、接着性と耐候接着性等の改善効果を特に期待する場合には膠質炭酸カルシウムを用いるのが好ましい。
【０２１２】
一方、重質炭酸カルシウムは配合物の低粘度化や増量、コストダウン等を目的として添加することがあるが、この重質炭酸カルシウムを用いる場合は必要に応じて下記のようなものを使用することができる。
【０２１３】
重質炭酸カルシウムとは、天然のチョーク（白亜）、大理石、石灰石などを機械的に粉砕・加工したものである。粉砕方法については乾式法と湿式法があるが、湿式粉砕品は本発明の硬化性組成物の貯蔵安定性を悪化させることが多いために好ましくないことが多い。重質炭酸カルシウムは、分級により、様々な平均粒子径を有する製品となる。特に限定されないが、硬化物の破断強度、破断伸び、接着性と耐候接着性の改善効果を期待する場合には、比表面積の値が１．５ｍ^２／ｇ以上５０ｍ^２／ｇ以下のものが好ましく、２ｍ^２／ｇ以上５０ｍ^２／ｇ以下が更に好ましく、２．４ｍ^２／ｇ以上５０ｍ^２／ｇ以下がより好ましく、３ｍ^２／ｇ以上５０ｍ^２／ｇ以下が特に好ましい。比表面積が１．５ｍ^２／ｇ未満の場合には、その改善効果が充分でないことがある。もちろん、単に粘度を低下させる場合や増量のみを目的とする場合などはこの限りではない。
【０２１４】
なお、比表面積の値とは、測定方法としてＪＩＳ　Ｋ　５１０１に準じて行なった空気透過法（粉体充填層に対する空気の透過性から比表面積を求める方法。）による測定値をいう。測定機器としては、島津製作所製の比表面積測定器ＳＳ−１００型を用いるのが好ましい。
【０２１５】
これらの充填材は目的や必要に応じて単独で併用してもよく、２種以上を併用してもよい。特に限定はされないが、例えば、必要に応じて比表面積の値が１．５ｍ^２／ｇ以上の重質炭酸カルシウムと膠質炭酸カルシウムを組み合わせると、配合物の粘度の上昇を程々に抑え、硬化物の破断強度、破断伸び、接着性と耐候接着性の改善効果が大いに期待できる。
【０２１６】
充填材を用いる場合の添加量は、ビニル系重合体１００重量部に対して、充填材を５〜１０００重量部の範囲で使用するのが好ましく、２０〜５００重量部の範囲で使用するのがより好ましく、４０〜３００重量部の範囲で使用するのが特に好ましい。配合量が５重量部未満の場合には、硬化物の破断強度、破断伸び、接着性と耐候接着性の改善効果が充分でないことがあり、１０００重量部を越えると該硬化性組成物の作業性が低下することがある。充填材は単独で使用しても良いし、２種以上併用しても良い。
＜微小中空粒子＞
また、更に、物性の大きな低下を起こすことなく軽量化、低コスト化を図ることを目的として、微小中空粒子をこれら補強性充填材に併用しても良い。
【０２１７】
このような微少中空粒子（以下バルーンという）は、特に限定はされないが、「機能性フィラーの最新技術」（ＣＭＣ）に記載されているように、直径が１ｍｍ以下、好ましくは５００μｍ以下、更に好ましくは２００μｍ以下の無機質あるいは有機質の材料で構成された中空体が挙げられる。特に、真比重が１．０ｇ／ｃｍ^３以下である微少中空体を用いることが好ましく、更には０．５ｇ／ｃｍ^３以下である微少中空体を用いることが好ましい。
【０２１８】
前記無機系バルーンとして、珪酸系バルーンと非珪酸系バルーンとが例示でき、珪酸系バルーンには、シラスバルーン、パーライト、ガラスバルーン、シリカバルーン、フライアッシュバルーン等が、非珪酸系バルーンには、アルミナバルーン、ジルコニアバルーン、カーボンバルーン等が例示できる。これらの無機系バルーンの具体例として、シラスバルーンとしてイヂチ化成製のウインライト、三機工業製のサンキライト、ガラスバルーンとして日本板硝子製のカルーン、住友スリーエム製のセルスターＺ−２８、ＥＭＥＲＳＯＮ＆ＣＵＭＩＮＧ製のＭＩＣＲＯ　ＢＡＬＬＯＯＮ、ＰＩＴＴＳＢＵＲＧＥ　ＣＯＲＮＩＮＧ製のＣＥＬＡＭＩＣ　ＧＬＡＳＳＭＯＤＵＬＥＳ、３Ｍ製のＧＬＡＳＳ　ＢＵＢＢＬＥＳ、シリカバルーンとして旭硝子製のＱ−ＣＥＬ、太平洋セメント製のＥ−ＳＰＨＥＲＥＳ、フライアッシュバルーンとして、ＰＦＡＭＡＲＫＥＴＩＮＧ製のＣＥＲＯＳＰＨＥＲＥＳ、ＦＩＬＬＩＴＥ　Ｕ．Ｓ．Ａ製のＦＩＬＬＩＴＥ、アルミナバルーンとして昭和電工製のＢＷ、ジルコニアバルーンとしてＺＩＲＣＯＡ製のＨＯＬＬＯＷ　ＺＩＲＣＯＮＩＵＭ　ＳＰＨＥＥＳ、カーボンバルーンとして呉羽化学製クレカスフェア、ＧＥＮＥＲＡＬ　ＴＥＣＨＮＯＬＯＧＩＥＳ製カーボスフェアが市販されている。
【０２１９】
前記有機系バルーンとして、熱硬化性樹脂のバルーンと熱可塑性樹脂のバルーンが例示でき、熱硬化性のバルーンにはフェノールバルーン、エポキシバルーン、尿素バルーンが、熱可塑性バルーンにはサランバルーン、ポリスチレンバルーン、ポリメタクリレートバルーン、ポリビニルアルコールバルーン、スチレン−アクリル系バルーンが例示できる。また、架橋した熱可塑性樹脂のバルーンも使用できる。ここでいうバルーンは、発泡後のバルーンでも良く、発泡剤を含むものを配合後に発泡させてバルーンとしても良い。
【０２２０】
これらの有機系バルーンの具体例として、フェノールバルーンとしてユニオンカーバイド製のＵＣＡＲ及びＰＨＥＮＯＬＩＣ　ＭＩＣＲＯＢＡＬＬＯＯＮＳ、エポキシバルーンとしてＥＭＥＲＳＯＮ＆ＣＵＭＩＮＧ製のＥＣＣＯＳＰＨＥＲＥＳ、尿素バルーンとしてＥＭＥＲＳＯＮ＆ＣＵＭＩＮＧ製のＥＣＣＯＳＰＨＥＲＥＳ　ＶＦ−Ｏ、サランバルーンとしてＤＯＷ　ＣＨＥＭＩＣＡＬ製のＳＡＲＡＮ　ＭＩＣＲＯＳＰＨＥＲＥＳ、日本フィラメント製のエクスパンセル、松本油脂製薬製のマツモトマイクロスフェア、ポリスチレンバルーンとしてＡＲＣＯＰＯＬＹＭＥＲＳ製のＤＹＬＩＴＥ　ＥＸＰＡＮＤＡＢＬＥ　ＰＯＬＹＳＴＹＲＥＮＥ、ＢＡＳＦ　ＷＹＡＮＤＯＴＥ製の　ＥＸＰＡＮＤＡＢＬＥ　ＰＯＬＹＳＴＹＲＥＮＥ　ＢＥＡＤＳ、架橋型スチレン−アクリル酸バルーンには日本合成ゴム製のＳＸ８６３（Ｐ）が、市販されている。
【０２２１】
上記バルーンは単独で使用しても良く、２種類以上混合して用いても良い。さらに、これらバルーンの表面を脂肪酸、脂肪酸エステル、ロジン、ロジン酸リグニン、シランカップリング剤、チタンカップリング剤、アルミカップリング剤、ポリプロピレングリコール等で分散性および配合物の作業性を改良するために処理したものも使用することができる。これらの、バルーンは配合物を硬化させた場合の物性のうち、柔軟性および伸び・強度を損なうことなく、軽量化させコストダウンするために使用される。
【０２２２】
バルーンの含有量は、特に限定されないがビニル系重合体１００重量部に対して、好ましくは０．１〜５０部、更に好ましくは０．１〜３０部の範囲で使用できる。この量が０．１部未満では軽量化の効果が小さく５０部以上ではこの配合物を硬化させた場合の機械特性のうち、引張強度の低下が認められることがある。またバルーンの比重が０．１以上の場合は３〜５０部、更に好ましくは５〜３０部が好ましい。
＜物性調整剤＞
本発明の硬化性組成物には、必要に応じて生成する硬化物の引張特性を調整する物性調整剤を添加しても良い。
【０２２３】
物性調整剤としては特に限定されないが、例えば、メチルトリメトキシシラン、ジメチルジメトキシシラン、トリメチルメトキシシラン、ｎ−プロピルトリメトキシシラン等のアルキルアルコキシシラン類；ジメチルジイソプロペノキシシラン、メチルトリイソプロペノキシシラン、γ−グリシドキシプロピルメチルジイソプロペノキシシラン等のアルキルイソプロペノキシシラン、γ−グリシドキシプロピルメチルジメトキシシラン、γ−グリシドキシプロピルトリメトキシシラン、ビニルトリメトキシシラン、ビニルジメチルメトキシシラン、γ−アミノプロピルトリメトキシシラン、Ｎ−（β−アミノエチル）アミノプロピルメチルジメトキシシラン、γ−メルカプトプロピルトリメトキシシラン、γ−メルカプトプロピルメチルジメトキシシラン等の官能基を有するアルコキシシラン類；シリコーンワニス類；ポリシロキサン類等が挙げられる。前記物性調整剤を用いることにより、本発明の組成物を硬化させた時の硬度を上げたり、硬度を下げ、伸びを出したりし得る。上記物性調整剤は単独で用いてもよく、２種以上併用してもよい。
＜シラノール含有化合物＞
本発明の硬化性組成物には、硬化物の物性を変える等の必要に応じてシラノール含有化合物を添加しても良い。シラノール含有化合物とは、分子内に１個のシラノール基を有する化合物、及び／又は、水分と反応することにより分子内に１個のシラノール基を有する化合物を生成し得る化合物のことをいう。これらは一方のみを用いてもよいし、両化合物を同時に用いてもよい。
【０２２４】
シラノール含有化合物の一つである分子内に１個のシラノール基を有する化合物は、特に限定されず、下記に示した化合物、
（ＣＨ_３）_３ＳｉＯＨ、（ＣＨ_３ＣＨ_２）_３ＳｉＯＨ、（ＣＨ_３ＣＨ_２ＣＨ_２）_３ＳｉＯＨ、（ｎ−Ｂｕ）_３ＳｉＯＨ、（ｓｅｃ−Ｂｕ）_３ＳｉＯＨ、（ｔ−Ｂｕ）_３ＳｉＯＨ、（ｔ−Ｂｕ）Ｓｉ（ＣＨ_３）_２ＯＨ、（Ｃ_５Ｈ_１１）_３ＳｉＯＨ、（Ｃ_６Ｈ_１３）_３ＳｉＯＨ、（Ｃ_６Ｈ_５）_３ＳｉＯＨ、（Ｃ_６Ｈ_５）_２Ｓｉ（ＣＨ_３）ＯＨ、（Ｃ_６Ｈ_５）Ｓｉ（ＣＨ_３）_２ＯＨ、（Ｃ_６Ｈ_５）_２Ｓｉ（Ｃ_２Ｈ_５）ＯＨ、Ｃ_６Ｈ_５Ｓｉ（Ｃ_２Ｈ_５）_２ＯＨ、Ｃ_６Ｈ_５ＣＨ_２Ｓｉ（Ｃ_２Ｈ_５）_２ＯＨ、Ｃ_１０Ｈ_７Ｓｉ（ＣＨ_３）_２ＯＨ
（ただし、上記式中Ｃ_６Ｈ_５はフェニル基を、Ｃ_１０Ｈ_７はナフチル基を示す。）
等のような（Ｒ”）_３ＳｉＯＨ（ただし式中Ｒ”は同一または異種の置換もしくは非置換のアルキル基またはアリール基）で表わすことができる化合物、
【０２２５】
【化１５】

等のようなシラノール基を含有する環状ポリシロキサン化合物、
【０２２６】
【化１６】

等のようなシラノール基を含有する鎖状ポリシロキサン化合物、
【０２２７】
【化１７】

等のような主鎖が珪素、炭素からなるポリマー末端にシラノール基が結合した化合物、
【０２２８】
【化１８】

等のようなポリシラン主鎖末端にシラノール基が結合した化合物、
【０２２９】
【化１９】

等のような主鎖が珪素、炭素、酸素からなるポリマー末端にシラノール基が結合した化合物等が例示できる。このうち下記一般式（４５）で表される化合物が好ましい。
（Ｒ^５８）_３ＳｉＯＨ　（４５）
（式中、Ｒ^５８は炭素数１〜２０の１価の炭化水素基を示す。複数のＲ^５８は同一であってもよく又は異なっていてもよい。）
Ｒ^２７は、メチル基、エチル基、ビニル基、ｔ−ブチル基、フェニル基が好ましく、さらにメチル基が好ましい。
【０２３０】
中でも、入手が容易であり、効果の点から分子量の小さい（ＣＨ_３）_３ＳｉＯＨ等が好ましい。
【０２３１】
上記、分子内に１個のシラノール基を有する化合物は、ビニル系重合体の架橋性シリル基あるいは架橋により生成したシロキサン結合と反応することにより、架橋点の数を減少させ、硬化物に柔軟性を与えているものと推定される。
また本発明の成分の１つである、水分と反応することにより分子内に１個のシラノール基を有する化合物を生成し得る化合物は、特に限定されないが、水分と反応して生成する分子内に１個のシラノール基を有する化合物（加水分解生成物）が、上記一般式（４５）で表される化合物が好ましい。例えば、特に限定されるわけではないが、後述するような一般式（４６）で表される化合物以外に下記の化合物を挙げることができる。
【０２３２】
Ｎ，Ｏ−ビス（トリメチルシリル）アセトアミド、Ｎ−（トリメチルシリル）アセトアミド、ビス（トリメチルシリル）トリフルオロアセトアミド、Ｎ−メチル−Ｎ−トリメチルシリルトリフルオロアセトアミド、ビストリメチルシリル尿素、Ｎ−（ｔ−ブチルジメチルシリル）Ｎ−メチルトリフルオロアセトアミド、（Ｎ，Ｎ−ジメチルアミノ）トリメチルシラン、（Ｎ，Ｎ−ジエチルアミノ）トリメチルシラン、ヘキサメチルジシラザン、１，１，３，３−テトラメチルジシラザン、Ｎ−（トリメチルシリル）イミダゾール、トリメチルシリルトリフルオロメタンスルフォネート、トリメチルシリルフェノキシド、ｎ−オクタノールのトリメチルシリル化物、２―エチルヘキサノールのトリメチルシリル化物、グリセリンのトリス（トリメチルシリル）化物、トリメチロールプロパンのトリス（トリメチルシリル）化物、ペンタエリスリトールのトリス（トリメチルシリル）化物、ペンタエリスリトールのテトラ（トリメチルシリル）化物、（ＣＨ_３）_３ＳｉＮＨＳｉ（ＣＨ_３）_３、（ＣＨ_３）_３ＳｉＮＳｉ（ＣＨ_３）_２、
【０２３３】
【化２０】

等が好適に使用できるが加水分解生成物の含有シラノール基の量からは（ＣＨ_３）_３ＳｉＮＨＳｉ（ＣＨ_３）_３が特に好ましい。
【０２３４】
さらには本発明の成分の１つである、水分と反応することにより分子内に１個のシラノール基を有する化合物を生成し得る化合物は、特に限定されないが、上記化合物以外に下記一般式（４６）で表される化合物が好ましい。
（（Ｒ^５８）_３ＳｉＯ）_ｎＲ^５９　（４６）
（式中、Ｒ^５８は上述したものと同様である。ｎは正数を、Ｒ^５９は活性水素含有化合物から一部あるいは全ての活性水素を除いた基を示す。）
Ｒ^５８は、メチル基、エチル基、ビニル基、ｔ−ブチル基、フェニル基が好ましく、さらにメチル基が好ましい。
（Ｒ^５８）_３Ｓｉ基は、３個のＲ^５８が全てメチル基であるトリメチルシリル基が特に好ましい。また、ｎは１〜５が好ましい。
【０２３５】
上記Ｒ^５９の由来となる活性水素含有化合物としては特に限定されないが、例えば、メタノール、エタノール、ｎ−ブタノール、ｉ−ブタノール、ｔ−ブタノール、ｎ−オクタノール、２−エチルヘキサノール、ベンジルアルコール、エチレングリコール、ジエチレングリコール、ポリエチレングリコール、プロピレングリコール、ジプロピレングリコール、ポリプロピレングリコール、プロパンジオール、テトラメチレングリコール、ポリテトラメチレングリコール、グリセリン、トリメチロールプロパン、ペンタエリスリトール等のアルコール類；フェノール、クレゾール、ビスフェノールＡ、ヒドロキノン等のフェノール類；ギ酸、酢酸、プロピオン酸、ラウリン酸、パルミチン酸、ステアリン酸、ベヘン酸、アクリル酸、メタクリル酸、オレイン酸、リノール酸、リノレン酸、ソルビン酸、シュウ酸、マロン酸、コハク酸、アジピン酸、マレイン酸、安息香酸、フタル酸、テレフタル酸、トリメリット酸等のカルボン酸類；アンモニア；メチルアミン、ジメチルアミン、エチルアミン、ジエチルアミン、ｎ−ブチルアミン、イミダゾール等のアミン類；アセトアミド、ベンズアミド等の酸アミド類、尿素、Ｎ，Ｎ’−ジフェニル尿素等の尿素類；アセトン、アセチルアセトン、２，４−ヘプタジオン等のケトン類等が挙げられる。
【０２３６】
上記一般式（４６）で表される水分と反応することにより分子内に１個のシラノール基を有する化合物を生成し得る化合物は、例えば上述の活性水素含有化合物等に、トリメチルシリルクロリドやジメチル（ｔ−ブチル）クロリド等のようなシリル化剤とも呼ばれる（Ｒ^５８）_３Ｓｉ基とともにハロゲン基等の活性水素と反応し得る基を有する化合物を反応させることにより得ることができるが、これらに限定されるものではない（ただし、Ｒ^５８は上述したものと同様である。）。
【０２３７】
上記一般式（４６）で表される化合物を具体的に例示すると、アリロキシトリメチルシラン、Ｎ，Ｏ−ビス（トリメチルシリル）アセトアミド、Ｎ−（トリメチルシリル）アセトアミド、ビス（トリメチルシリル）トリフルオロアセトアミド、Ｎ−メチル−Ｎ−トリメチルシリルトリフルオロアセトアミド、ビストリメチルシリル尿素、Ｎ−（ｔ−ブチルジメチルシリル）Ｎ−メチルトリフルオロアセトアミド、（Ｎ，Ｎ−ジメチルアミノ）トリメチルシラン、（Ｎ，Ｎ−ジエチルアミノ）トリメチルシラン、ヘキサメチルジシラザン、１，１，３，３−テトラメチルジシラザン、Ｎ−（トリメチルシリル）イミダゾール、トリメチルシリルトリフルオロメタンスルフォネート、トリメチルシリルフェノキシド、ｎ−オクタノールのトリメチルシリル化物、２―エチルヘキサノールのトリメチルシリル化物、グリセリンのトリス（トリメチルシリル）化物、トリメチロールプロパンのトリス（トリメチルシリル）化物、ペンタエリスリトールのトリス（トリメチルシリル）化物、ペンタエリスリトールのテトラ（トリメチルシリル）化物、等が挙げられるが、これらに限定されない。これらは単独で用いてもよく、２種以上を併用してもよい。
【０２３８】
また、一般式（（（Ｒ^６０）_３ＳｉＯ）（Ｒ^６１Ｏ）_ｓ）_ｔＺで表わすことができるような化合物、ＣＨ_３Ｏ（ＣＨ_２ＣＨ（ＣＨ_３）Ｏ）_５Ｓｉ（ＣＨ_３）_３、ＣＨ_２＝ＣＨＣＨ_２（ＣＨ_２ＣＨ（ＣＨ_３）Ｏ）_５Ｓｉ（ＣＨ_３）_３、（ＣＨ_３）_３ＳｉＯ（ＣＨ_２ＣＨ（ＣＨ_３）Ｏ）_５Ｓｉ（ＣＨ_３）_３、（ＣＨ_３）_３ＳｉＯ（ＣＨ_２ＣＨ（ＣＨ_３）Ｏ）_７Ｓｉ（ＣＨ_３）_３
（式中、Ｒ^６０は同一または異種の置換もしくは非置換の１価の炭化水素基または水素原子、Ｒ^６１は炭素数１〜８の２価の炭化水素基、ｓ、ｔは正の整数で、ｓは１〜６、ｓ×ｔは５以上、Ｚは１〜６価の有機基）
等も好適に使用できる。これらは単独で用いてもよく、２種以上を併用してもよい。
【０２３９】
水分と反応することにより分子内に１個のシラノール基を有する化合物を生成し得る化合物の中では、貯蔵安定性、耐候性等に悪影響を及ぼさない点で、加水分解後に生成する活性水素含有化合物はフェノール類、酸アミド類及びアルコール類が好ましく、活性水素含有化合物が水酸基であるフェノール類およびアルコール類が更に好ましい。
【０２４０】
上記の化合物の中では、Ｎ，Ｏ−ビス（トリメチルシリル）アセトアミド、Ｎ−（トリメチルシリル）アセトアミド、トリメチルシリルフェノキシド、ｎ−オクタノールのトリメチルシリル化物、２―エチルヘキサノールのトリメチルシリル化物、グリセリンのトリス（トリメチルシリル）化物、トリメチロールプロパンのトリス（トリメチルシリル）化物、ペンタエリスリトールのトリス（トリメチルシリル）化物、ペンタエリスリトールのテトラ（トリメチルシリル）化物等が好ましい。
【０２４１】
この水分と反応することにより分子内に１個のシラノール基を有する化合物を生成し得る化合物は、貯蔵時、硬化時あるいは硬化後に水分と反応することにより、分子内に１個のシラノール基を有する化合物を生成する。この様にして生成した分子内に１個のシラノール基を有する化合物は、上述のようにビニル系重合体の架橋性シリル基あるいは架橋により生成したシロキサン結合と反応することにより、架橋点の数を減少させ、硬化物に柔軟性を与えているものと推定される。
【０２４２】
シラノール含有化合物の添加量は、硬化物の期待物性に応じて適宜調整可能である。シラノール含有化合物は、ビニル系重合体１００重量部に対して０．１〜５０重量部、好ましくは０．３〜２０重量部、さらに好ましくは０．５〜１０重量部添加できる。０．１重量部未満では添加効果が現れず、５０重量部を越えると架橋が不十分になり、硬化物の強度やゲル分率が低下しすぎる。
【０２４３】
また、シラノール含有化合物をビニル系重合体に添加する時期は特に限定されず、ビニル系重合体の製造時に添加してもよく、硬化性組成物の作製時に添加してもよい。
＜チクソ性付与剤（垂れ防止剤）＞
本発明の硬化性組成物には、必要に応じて垂れを防止し、作業性を良くするためにチクソ性付与剤（垂れ防止剤）を添加しても良い。
【０２４４】
また、垂れ防止剤としては特に限定されないが、例えば、ポリアミドワックス類、水添ヒマシ油誘導体類；ステアリン酸カルシウム、ステアリン酸アルミニウム、ステアリン酸バリウム等の金属石鹸類等が挙げられる。これらチクソ性付与剤（垂れ防止剤）は単独で用いてもよく、２種以上併用してもよい。
＜光硬化性物質＞
本発明の硬化性組成物には、必要に応じて光硬化性物質を添加しても良い。光硬化性物質とは、光の作用によって短時間に、分子構造が化学変化をおこし、硬化などの物性的変化を生ずるものである。この光硬化性物質を添加することにより、硬化性組成物を硬化させた際の硬化物表面の粘着性（残留タックともいう）を低減できる。この光硬化性物質は、光をあてることにより硬化し得る物質であるが、代表的な光硬化性物質は、例えば室内の日の当たる位置（窓付近）に１日間、室温で静置することにより硬化させることができる物質である。この種の化合物には、有機単量体、オリゴマー、樹脂あるいはそれらを含む組成物など多くのものが知られており、その種類は特に限定されないが、例えば、不飽和アクリル系化合物、ポリケイ皮酸ビニル類あるいはアジド化樹脂等が挙げられる。
【０２４５】
不飽和アクリル系化合物は、下記一般式（４７）で表される不飽和基を有する単量体、オリゴマーあるいはこれらの混合物である。
ＣＨ_２＝ＣＨＲ^６２ＣＯ（Ｏ）−　（４７）
式中、Ｒ^６２は水素、炭素数１〜１０のアルキル基、炭素数６〜１０のアリール基または炭素数７〜１０のアラルキル基を示す。
【０２４６】
不飽和アクリル系化合物としては、具体的には、エチレングリコール、グリセリン、トリメチロールプロパン、ペンタエリスリトール、ネオペンチルアルコール等の低分子量アルコール類の（メタ）アクリル酸エステル類；ビスフェノールＡ、イソシアヌル酸等の酸あるいは上記低分子量アルコール等をエチレンオキシドやプロピレンオキシドで変性したアルコール類の（メタ）アクリル酸エステル類；主鎖がポリエーテルで末端に水酸基を有するポリエーテルポリオール、主鎖がポリエーテルであるポリオール中でビニル系モノマーをラジカル重合することにより得られるポリマーポリオール、主鎖がポリエステルで末端に水酸基を有するポリエステルポリオール、主鎖がビニル系あるいは（メタ）アクリル系重合体であり、主鎖中に水酸基を有するポリオール等の（メタ）アクリル酸エステル類；ビスフェノールＡ型やノボラック型等のエポキシ樹脂と（メタ）アクリル酸を反応させることにより得られるエポキシアクリレート系オリゴマー類；ポリオール、ポリイソシアネートおよび水酸基含有（メタ）アクリレート等を反応させることにより得られる分子鎖中にウレタン結合および（メタ）アクリル基を有するウレタンアクリレート系オリゴマー等が挙げられる。
【０２４７】
ポリケイ皮酸ビニル類とは、シンナモイル基を感光基とする感光性樹脂であり、ポリビニルアルコールをケイ皮酸でエステル化したものの他、多くのポリケイ皮酸ビニル系誘導体が挙げられる。
【０２４８】
アジド化樹脂は、アジド基を感光基とする感光性樹脂として知られており、通常はアジド化合物を感光剤として加えたゴム感光液のほか「感光性樹脂」（昭和４７年３月１７日出版、印刷学会出版部発行、９３頁〜、１０６頁から、１１７頁〜）に詳細な例示があり、これらを単独又は混合し、必要に応じて増感剤を加えて使用することができる。
【０２４９】
上記の光硬化性物質の中では、取り扱い易いという理由で不飽和アクリル系化合物が好ましい。
【０２５０】
光硬化性物質は、ビニル系重合体１００重量部に対して０．０１〜２０重量部添加するのが好ましい。０．０１重量部未満では効果が小さく、また２０重量部を越えると物性への悪影響が出ることがある。なお、ケトン類、ニトロ化合物などの増感剤やアミン類等の促進剤を添加すると、効果が高められる場合がある。＜空気酸化硬化性物質＞
本発明の硬化性組成物には、必要に応じて空気酸化硬化性物質を添加しても良い。空気酸化硬化性物質とは、空気中の酸素により架橋硬化できる不飽和基を有する化合物である。この空気酸化硬化性物質を添加することにより、硬化性組成物を硬化させた際の硬化物表面の粘着性（残留タックともいう）を低減できる。本発明における空気酸化硬化性物質は、空気と接触させることにより硬化し得る物質であり、より具体的には、空気中の酸素と反応して硬化する性質を有するものである。代表的な空気酸化硬化性物質は、例えば空気中で室内に１日間静置することにより硬化させることができる。
【０２５１】
空気酸化硬化性物質としては、例えば、桐油、アマニ油等の乾性油；これら乾性油を変性して得られる各種アルキッド樹脂；乾性油により変性されたアクリル系重合体、エポキシ系樹脂、シリコーン樹脂；１，２−ポリブタジエン、１，４−ポリブタジエンを、Ｃ５〜Ｃ８ジエンの重合体や共重合体、更には該重合体や共重合体の各種変性物（マレイン化変性物、ボイル油変性物など）などが具体例として挙げられる。これらのうちでは桐油、ジエン系重合体のうちの液状物（液状ジエン系重合体）やその変性物が特に好ましい。
【０２５２】
上記液状ジエン系重合体の具体例としては、ブタジエン、クロロプレン、イソプレン、１，３−ペンタジエン等のジエン系化合物を重合又は共重合させて得られる液状重合体や、これらジエン系化合物と共重合性を有するアクリロニトリル、スチレンなどの単量体とをジエン系化合物が主体となるように共重合させて得られるＮＢＲ，ＳＢＲ等の重合体や更にはそれらの各種変性物（マレイン化変性物、ボイル油変性物など）などが挙げられる。これらは単独で用いてもよく、２種以上を併用してもよい。これら液状ジエン系化合物のうちでは液状ポリブタジエンが好ましい。
【０２５３】
空気酸化硬化性物質は、単独で用いてもよく、２種以上を併用してもよい。また空気酸化硬化性物質と同時に酸化硬化反応を促進する触媒や金属ドライヤーを併用すると効果を高められる場合がある。これらの触媒や金属ドライヤーとしては、ナフテン酸コバルト、ナフテン酸鉛、ナフテン酸ジルコニウム、オクチル酸コバルト、オクチル酸ジルコニウム等の金属塩やアミン化合物等が例示される。
【０２５４】
空気酸化硬化性物質は、ビニル系重合体１００重量部に対して０．０１〜２０重量部添加するのが好ましい。０．０１重量部未満では効果が小さく、また２０重量部を越えると物性への悪影響が出ることがある。
＜酸化防止剤＞
本発明の硬化性組成物には、必要に応じて酸化防止剤を添加しても良い。酸化防止剤は各種のものが知られており、例えば大成社発行の「酸化防止剤ハンドブック」、シーエムシー化学発行の「高分子材料の劣化と安定化」（２３５〜２４２）等に記載された種々のものが挙げられるが、これらに限定されるわけではない。
【０２５５】
例えば、ＭＡＲＫ　ＰＥＰ−３６、ＭＡＲＫ　ＡＯ−２３等のチオエーテル系（以上いずれもアデカア−ガス化学製）、Ｉｒｇａｆｏｓ３８、Ｉｒｇａｆｏｓ１６８、ＩｒｇａｆｏｓＰ−ＥＰＱ（以上いずれも日本チバガイギー製）等のようなリン系酸化防止剤等が挙げられる。なかでも、以下に示したようなヒンダードフェノール系化合物が好ましい。
【０２５６】
ヒンダードフェノール系化合物としては、具体的には以下のものが例示できる。
２，６−ジ−ｔｅｒｔ−ブチル−４−メチルフェノール、２，６−ジ−ｔｅｒｔ−ブチル−４−エチルフェノール、モノ（又はジ又はトリ）（αメチルベンジル）フェノール、２，２’−メチレンビス（４エチル−６−ｔｅｒｔ−ブチルフェノール）、２，２’−メチレンビス（４メチル−６−ｔｅｒｔ−ブチルフェノール）、４，４’−ブチリデンビス（３−メチル−６−ｔｅｒｔ−ブチルフェノール）、４，４’−チオビス（３−メチル−６−ｔｅｒｔ−ブチルフェノール）、２，５−ジ−ｔｅｒｔ−ブチルハイドロキノン、２，５−ジ−ｔｅｒｔ−アミルハイドロキノン、トリエチレングリコール−ビス−［３−（３−ｔ−ブチル−５−メチル−４ヒドロキシフェニル）プロピオネート］、１，６−ヘキサンジオール−ビス［３−（３，５−ジ−ｔ−ブチル−４−ヒドロキシフェニル）プロピオネート］、２，４−ビス−（ｎ−オクチルチオ）−６−（４−ヒドロキシ−３，５−ジ−ｔ−ブチルアニリノ）−１，３，５−トリアジン、ペンタエリスリチル−テトラキス［３−（３，５−ジ−ｔ−ブチル−４−ヒドロキシフェニル）プロピオネート］、２，２−チオ−ジエチレンビス［３−（３，５−ジ−ｔ−ブチル−４−ヒドロキシフェニル）プロピオネート］、オクタデシル−３−（３，５−ジ−ｔ−ブチル−４−ヒドロキシフェニル）プロピオネート、Ｎ，Ｎ’−ヘキサメチレンビス（３，５−ジ−ｔ−ブチル−４−ヒドロキシ−ヒドロシンナマミド）、３，５−ジ−ｔ−ブチル−４−ヒドロキシ−ベンジルフォスフォネート−ジエチルエステル、１，３，５−トリメチル−２，４，６−トリス（３，５−ジ−ｔ−ブチル−４−ヒドロキシベンジル）ベンゼン、ビス（３，５−ジ−ｔ−ブチル−４−ヒドロキシベンジルホスホン酸エチル）カルシウム、トリス−（３，５−ジ−ｔ−ブチル−４−ヒドロキシベンジル）イソシアヌレート、２，４−２，４−ビス［（オクチルチオ）メチル］ｏ−クレゾール、Ｎ，Ｎ’−ビス［３−（３，５−ジ−ｔ−ブチル−４−ヒドロキシフェニル）プロピオニル］ヒドラジン、トリス（２，４−ジ−ｔ−ブチルフェニル）フォスファイト、２−（５−メチル−２−ヒドロキシフェニル）ベンゾトリアゾール、２−［２−ヒドロキシ−３，５−ビス（α，α−ジメチルベンジル）フェニル］−２Ｈ−ベンゾトリアゾール、２−（３，５−ジ−ｔ−ブチル−２−ヒドロキシフェニル）ベンゾトリアゾール、２−（３−ｔ−ブチル−５−メチル−２−ヒドロキシフェニル）−５−クロロベンゾトリアゾール、２−（３，５−ジ−ｔ−ブチル−２−ヒドロキシフェニル）−５−クロロベンゾトリアゾール、２−（３，５−ジ−ｔ−アミル−２−ヒドロキシフェニル）ベンゾトリアゾール、２−（２’−ヒドロキシ−５’−ｔ−オクチルフェニル）−ベンゾトリアゾール、メチル−３−［３−ｔ−ブチル−５−（２Ｈ−ベンゾトリアゾール−２−イル）−４−ヒドロキシフェニル］プロピオネート−ポリエチレングリコール（分子量約３００）との縮合物、ヒドロキシフェニルベンゾトリアゾール誘導体、２−（３，５−ジ−ｔ−ブチル−４−ヒドロキシベンジル）−２−ｎ−ブチルマロン酸ビス（１，２，２，６，６−ペンタメチル−４−ピペリジル）、２，４−ジ−ｔ−ブチルフェニル−３，５−ジ−ｔ−ブチル−４−ヒドロキシベンゾエート等が挙げられる。
【０２５７】
商品名で言えば、ノクラック２００、ノクラックＭ−１７、ノクラックＳＰ、ノクラックＳＰ−Ｎ、ノクラックＮＳ−５、ノクラックＮＳ−６、ノクラックＮＳ−３０、ノクラック３００、ノクラックＮＳ−７、ノクラックＤＡＨ（以上いずれも大内新興化学工業製）、ＭＡＲＫ　ＡＯ−３０、ＭＡＲＫ　ＡＯ−４０、ＭＡＲＫ　ＡＯ−５０、ＭＡＲＫ　ＡＯ−６０、ＭＡＲＫ　ＡＯ−６１６、ＭＡＲＫ　ＡＯ−６３５、ＭＡＲＫ　ＡＯ−６５８、ＭＡＲＫ　ＡＯ−８０、ＭＡＲＫ　ＡＯ−１５、ＭＡＲＫ　ＡＯ−１８、ＭＡＲＫ　３２８、ＭＡＲＫ　ＡＯ−３７（以上いずれもアデカアーガス化学製）、ＩＲＧＡＮＯＸ−２４５、ＩＲＧＡＮＯＸ−２５９、ＩＲＧＡＮＯＸ−５６５、ＩＲＧＡＮＯＸ−１０１０、ＩＲＧＡＮＯＸ−１０２４、ＩＲＧＡＮＯＸ−１０３５、ＩＲＧＡＮＯＸ−１０７６、ＩＲＧＡＮＯＸ−１０８１、ＩＲＧＡＮＯＸ−１０９８、ＩＲＧＡＮＯＸ−１２２２、ＩＲＧＡＮＯＸ−１３３０、ＩＲＧＡＮＯＸ−１４２５ＷＬ（以上いずれも日本チバガイギー製）、ＳｕｍｉｌｉｚｅｒＧＭ、ＳｕｍｉｌｉｚｅｒＧＡ−８０（以上いずれも住友化学製）等が例示できるがこれらに限定されるものではない。
【０２５８】
酸化防止剤は後述する光安定剤と併用してもよく、併用することによりその効果を更に発揮し、特に耐熱性が向上することがあるため特に好ましい。予め酸化防止剤と光安定剤を混合してあるチヌビンＣ３５３、チヌビンＢ７５（以上いずれも日本チバガイギー製）などを使用しても良い。
【０２５９】
酸化防止剤の使用量は、ビニル系重合体１００重量部に対して０．１〜１０重量部の範囲であることが好ましい。０．１重量部未満では耐候性を改善の効果が少なく、５重量部超では効果に大差がなく経済的に不利である。
＜光安定剤＞
本発明の硬化性組成物には、必要に応じて光安定剤を添加しても良い。光安定剤は各種のものが知られており、例えば大成社発行の「酸化防止剤ハンドブック」、シーエムシー化学発行の「高分子材料の劣化と安定化」（２３５〜２４２）等に記載された種々のものが挙げられるが、これらに限定されるわけではない。
【０２６０】
特に限定はされないが、光安定剤の中でも、紫外線吸収剤が好ましく、具体的には、チヌビンＰ、チヌビン２３４、チヌビン３２０、チヌビン３２６、チヌビン３２７、チヌビン３２９、チヌビン２１３（以上いずれも日本チバガイギー製）等のようなベンゾトリアゾール系化合物やチヌビン１５７７等のようなトリアジン系、ＣＨＩＭＡＳＳＯＲＢ８１等のようなベンゾフェノン系、チヌビン１２０（日本チバガイギー製）等のようなベンゾエート系化合物等が例示できる。
【０２６１】
また、ヒンダードアミン系化合物も好ましく、そのような化合物を以下に記載する。
コハク酸ジメチル−１−（２−ヒドロキシエチル）−４−ヒドロキシ−２，２，６，６−テトラメチルピペリジン重縮合物、ポリ［｛６−（１，１，３，３−テトラメチルブチル）アミノ−１，３，５−トリアジン−２，４−ジイル｝｛（２，２，６，６−テトラメチル−４−ピペリジル）イミノ｝］、Ｎ，Ｎ’−ビス（３アミノプロピル）エチレンジアミン−２，４−ビス［Ｎ−ブチル−Ｎ−（１，２，２，６，６−ペンタメチル−４−ピペリジル）アミノ］−６−クロロ−１，３，５−トリアジン縮合物、ビス（２，２，６，６−テトラメチル−４−ピペリジル）セバケート、コハク酸−ビス（２，２，６，６−テトラメチル−４−ピペリディニル）エステル等が挙げられる。
【０２６２】
商品名で言えば、チヌビン６２２ＬＤ、チヌビン１４４、ＣＨＩＭＡＳＳＯＲＢ９４４ＬＤ、ＣＨＩＭＡＳＳＯＲＢ１１９ＦＬ、Ｉｒｇａｆｏｓ１６８、（以上いずれも日本チバガイギー製）、ＭＡＲＫ　ＬＡ−５２、ＭＡＲＫ　ＬＡ−５７、ＭＡＲＫ　ＬＡ−６２、ＭＡＲＫ　ＬＡ−６７、ＭＡＲＫ　ＬＡ−６３、ＭＡＲＫ　ＬＡ−６８、ＭＡＲＫ　ＬＡ−８２、ＭＡＲＫ　ＬＡ−８７、（以上いずれもアデカア−ガス化学製）、サノールＬＳ−７７０、サノールＬＳ−７６５、サノールＬＳ−２９２、サノールＬＳ−２６２６、サノールＬＳ−１１１４、サノールＬＳ−７４４、サノールＬＳ−４４０（以上いずれも三共製）などが例示できるがこれらに限定されるものではない。
【０２６３】
更には紫外線吸収剤とヒンダードアミン系化合物の組合せはより効果を発揮することがあるため、特に限定はされないが併用しても良く、併用することが好ましいことがある。
【０２６４】
光安定剤は前述した酸化防止剤と併用してもよく、併用することによりその効果を更に発揮し、特に耐候性が向上することがあるため特に好ましい。予め光安定剤と酸化防止剤を混合してあるチヌビンＣ３５３、チヌビンＢ７５（以上いずれも日本チバガイギー製）などを使用しても良い。
【０２６５】
光安定剤の使用量は、ビニル系重合体１００重量部に対して０．１〜１０重量部の範囲であることが好ましい。０．１重量部未満では耐候性を改善の効果が少なく、５重量部超では効果に大差がなく経済的に不利である。
その他の添加剤
本発明の硬化性組成物には、硬化性組成物又は硬化物の諸物性の調整を目的として、必要に応じて各種添加剤を添加してもよい。このような添加物の例としては、たとえば、難燃剤、硬化性調整剤、老化防止剤、ラジカル禁止剤、紫外線吸収剤、金属不活性化剤、オゾン劣化防止剤、リン系過酸化物分解剤、滑剤、顔料、発泡剤、光硬化性樹脂などがあげられる。これらの各種添加剤は単独で用いてもよく、２種類以上を併用してもよい。
【０２６６】
このような添加物の具体例は、たとえば、特公平４−６９６５９号、特公平７−１０８９２８号、特開昭６３−２５４１４９号、特開昭６４−２２９０４号の各明細書などに記載されている。
【０２６７】
本発明の硬化性組成物は、すべての配合成分を予め配合密封保存し、施工後空気中の湿気により硬化する１成分型として調製しても良く、硬化剤として別途硬化触媒、充填材、可塑剤、水等の成分を配合しておき、該配合材と重合体組成物を使用前に混合する２成分型として調整しても良い。２成分型にすると、２成分の混合時に着色剤を添加することができ、例えば、サイディングボードの色に合わせたシーリング材を提供する際に、限られた在庫で豊富な色揃えをすることが可能となるなど、市場から要望されている多色化対応が容易となり、低層建物用等により好ましい。着色剤は、例えば顔料と可塑剤、場合によっては充填材を混合しペースト化したものを用いると作業し易い。また、更に２成分の混合時に遅延剤を添加することにより硬化速度を作業現場にて微調整することができる。
＜＜硬化物＞＞
＜用途＞
本発明の硬化性組成物は、限定はされないが、建築用弾性シーリング材シーラントや複層ガラス用シーリング材等におけるシーリング材、太陽電池裏面封止材などの電気・電子部品材料、電線・ケーブル用絶縁被覆材などの電気絶縁材料、粘着剤、接着剤、弾性接着剤、塗料、粉体塗料、コーティング材、発泡体、缶蓋等のシール材、電気電子用ポッティング剤、フィルム、ガスケット、注型材料、各種成形材料、人工大理石、および、網入りガラスや合わせガラス端面（切断部）の防錆・防水用封止材、自動車部品、電機部品、各種機械部品などにおいて使用される液状シール剤、等の様々な用途に利用可能である。
【０２６８】
【実施例】
以下に、本発明の具体的な実施例を比較例と併せて説明するが、本発明は、下記実施例に限定されるものではない。
【０２６９】
下記実施例および比較例中「部」および「％」は、それぞれ「重量部」および「重量％」を表す。また、本実施例において「トリアミン」とは、ペンタメチルジエチレントリアミンをいう。
【０２７０】
下記実施例中、「数平均分子量」および「分子量分布（重量平均分子量と数平均分子量の比）」は、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）を用いた標準ポリスチレン換算法により算出した。ただし、ＧＰＣカラムとしてポリスチレン架橋ゲルを充填したもの（ｓｈｏｄｅｘ　ＧＰＣ　Ｋ−８０４；昭和電工製）、ＧＰＣ溶媒としてクロロホルムを用いた。
（製造例１）
攪拌機、ジャケット付きの２５０Ｌ反応機にＣｕＢｒ（１．１１ｋｇ）を仕込み、反応容器内を窒素置換した。アセトニトリル（５．０ｋｇ）を加え、ジャケットに温水を通水し７０℃で１５分間攪拌した。これにアクリル酸ブチル（６．６ｋｇ）、アクリル酸エチル（９．５ｋｇ）、アクリル酸メトキシエチル（７．８ｋｇ）及び２，５−ジブロモアジピン酸ジエチル（３．０９ｋｇ）とアセトニトリル（５．０ｋｇ）の混合物を加え、さらに７０℃で３０分程度撹拌した。これにペンタメチルジエチレントリアミン（以下トリアミンという）を加え、反応を開始した。反応途中トリアミンを適宜添加し、内温７０から８０℃程度で重合を行った。重合工程で使用したトリアミン総量は４５ｇであった。反応開始から４時間後に８０℃で減圧下、加熱攪拌することにより未反応のモノマー、アセトニトリルを脱揮した。濃縮物にアセトニトリル（２９．９ｋｇ）、１，７−オクタジエン（２８．４ｋｇ）、トリアミン（４４６ｇ）を添加して６時間撹拌を続けた。混合物を８０℃で減圧下、加熱攪拌することによりアセトニトリル、未反応の１，７−オクタジエンを脱揮させ、濃縮した。濃縮物にトルエン（１２０ｋｇ）を加え、重合体を溶解させた。重合体混合物中の固体銅をバグフィルター（ＨＡＹＷＡＲＤ製、公称濾布孔径１μｍ）によりろ過した。ろ液にキョーワード５００ＳＨ（協和化学製：共重合体１００重量部に対して２重量部）、キョーワード７００ＳＬ協和化学製：共重合体１００重量部に対して２重量部）を添加し、酸素窒素混合ガス雰囲気下（酸素濃度６％）で１２０℃、２時間加熱攪拌した。混合物中の不溶分をろ別した。ろ液を濃縮し、共重合体を得た。共重合体を１８０℃で１２時間加熱脱揮（減圧度１０ｔｏｒｒ以下）することにより共重合体中からＢｒ基を脱離させた。
【０２７１】
共重合体にトルエン（共重合体１００重量部に対して１００重量部）、キョーワード５００ＳＨ（協和化学製：共重合体１００重量部に対して２重量部）、キョーワード７００ＳＬ協和化学製：重合体１００重量部に対して２重量部）、ヒンダードフェノール系酸化防止剤（Ｉｒｇａｎｏｘ１０１０；チバスペシャリティケミカルズ０．０５部）を添加し、酸素窒素混合ガス雰囲気下（酸素濃度６％）で１３０℃、４時間加熱攪拌した。混合物中の不溶分をろ別した。ろ液を濃縮し、アルケニル基末端共重合体｛アルケニル末端ポリ（アクリル酸ブチル、アクリル酸エチル、アクリル酸メトキシエチル）の共重合体［Ｐ１］を得た。
【０２７２】
共重合体［Ｐ１］の数平均分子量は１８０００、分子量分布は１．１であった。共重合体１分子当たりに導入された平均のアルケニル基の数を^１Ｈ　ＮＭＲ分析により求めたところ、１．９個であった。
【０２７３】
攪拌機、ジャケット付きの１４０Ｌ反応機耐圧反応容器に共重合体［Ｐ１］（７６ｋｇ）、ジメトキシメチルヒドロシラン（１．９ｋｇ）、オルトぎ酸メチル（０．９４ｋｇ）、および０価白金の１，１，３，３−テトラメチル−１，３−ジビニルジシロキサン錯体のキシレン溶液（共重合体１ｋｇに対して白金として１０ｍｇ）を仕込んだ。混合物を窒素雰囲気下、１００℃で２時間加熱攪拌した。混合物の揮発分を減圧留去することにより、シリル基末端ビニル系共重合体（共重合体［Ｐ２］）を得た。得られた共重合体の数平均分子量はＧＰＣ測定（ポリスチレン換算）により１９０００、分子量分布は１．２であった。重合体１分子当たりに導入された平均のシリル基の数を^１Ｈ　ＮＭＲ分析により求めたところ、１．８個であった。
（実施例１）
製造例１で得られた共重合体［Ｐ１］１００部に平均粒径１μｍ以上のシリカとしてＩＭＳＩＬ　Ａ−２５（平均粒径３．５μｍ、龍森製）を１０部、他のシリカとしてアエロジルＲ９７４（一次粒子の平均径１２ｎｍのヒュームドシリカ：日本アエロジル製）１０部を配合し、更に３本ペイントロールを用いて充分混合した後、この硬化性組成物の粘度をＥ型粘度計（測定温度５０℃）で測定した。更にその後、共重合体［Ｐ１］に対して鎖状シロキサン（分子中に平均５個のヒドロシリル基と平均５個のα−メチルスチレン基を含有する：Ｓｉ−Ｈ基量　３．７０ｍｍｏｌ／ｇ）を、鎖状シロキサンのＳｉＨ基が、共重合体［Ｐ１］のアルケニル基の１．８当量分となる量を添加し、０価白金の１，１，３，３−テトラメチル−１，３−ジビニルジシロキサン錯体のキシレン溶液（１．３２×１０^−５ｍｍｏｌ／μｌ）を、白金換算で共重合体［Ｐ１］のアルケニル基の５×１０^−４モル当量添加し、更に均一に混合した。このようにして得られた硬化性組成物を５０℃の真空オーブン内にて充分脱泡した後、約２ｍｍ厚のシート状に塗工したものを１５０℃にて１００分硬化させた後、機械物性を測定した。試験片は（２（１／３）号形）ダンベル形に打抜いた。それぞれ結果を表１に示した。
（実施例２）
製造例１で得られた共重合体［Ｐ２］１００部に平均粒径１μｍ以上のシリカとしてＩＭＳＩＬ　Ａ−２５（平均粒径３．５μｍ、龍森製）を１０部、他のシリカとしてアエロジルＲＹ２００（一次粒子の平均径１２ｎｍのヒュームドシリカ：日本アエロジル製）１０部、可塑剤（アクリル系、ＵＰ−１０２０：東亞合成製）２０部、を配合し、更に３本ペイントロールを用いて充分混合した後、この硬化性組成物の粘度をＥ型粘度計（測定温度２３℃）で測定した。更にその後、共重合体１００部に対して硬化触媒（ジブチル錫ジアセトナート：４価錫）が１部となるように添加し、充分撹拌混合して脱泡した後、約２ｍｍ厚のシート状に塗工し、２３℃、５５％Ｒ．Ｈ．にて３日間硬化養生させた後、機械物性を測定した。試験片は（２（１／３）号形）ダンベル形に打抜いた。それぞれ結果を表２に示した。
（実施例３）
実施例２で添加した平均粒径１μｍ以上のシリカであるＩＭＳＩＬ　Ａ−２５の代わりにＩＭＳＩＬ　Ａ−１５（平均粒径３．３μｍ、龍森製）を１０部添加した以外は実施例２と同様にして、硬化性組成物の粘度を測定し、更に同様に硬化触媒を添加して硬化させた硬化物の機械物性を測定した。各結果を表２に示した。
（実施例４）
実施例２で添加した平均粒径１μｍ以上のシリカであるＩＭＳＩＬ　Ａ−２５の代わりにＩＭＳＩＬ　Ａ−８（平均粒径２．２μｍ、龍森製）を１０部添加した以外は実施例２と同様にして、硬化性組成物の粘度を測定し、更に同様に硬化触媒を添加して硬化させた硬化物の機械物性を測定した。各結果を表２に示した。
（比較例１）
実施例１で添加した平均粒径１μｍ以上のシリカを添加しなかった以外は実施例１と同様にして、硬化性組成物の粘度を測定し、更に同様に鎖状シロキサン、白金溶液を添加して硬化させた硬化物の機械物性を測定した。結果を表１に示した。
（比較例２）
実施例１で添加した平均粒径１μｍ以上のシリカの代わりにアエロジルＲ９７４（一次粒子の平均径１２ｎｍのヒュームドシリカ：日本アエロジル製）を同量の１０部添加した以外は実施例１と同様にして、硬化性組成物の粘度を測定し、更に同様に鎖状シロキサン、白金溶液を添加して硬化させた硬化物の機械物性を測定した（結局、ここではアエロジルＲ９４７を合計２０部配合した）。結果を表１に示した。
【０２７４】
【表１】

（比較例３）
実施例２で添加した平均粒径１μｍ以上のシリカを添加しなかった以外は実施例２と同様にして、硬化性組成物の粘度を測定し、更に同様に硬化触媒を添加して硬化させた硬化物の機械物性を測定した。結果を表２に示した。
（比較例４）
実施例２で添加した平均粒径１μｍ以上のシリカの代わりにアエロジルＲＹ２００（一次粒子の平均径１２ｎｍのヒュームドシリカ：日本アエロジル製）を同量の１０部添加した以外は実施例２と同様にして、硬化性組成物の粘度を測定した（結局、ここではアエロジルＲＹ２００を合計２０部配合した）。ＢＳ型粘度計では測定できないほど粘度が高かった。結果を表２に示した。
【０２７５】
【表２】

架橋性官能基を少なくとも１個有するビニル系重合体と平均粒径１μｍ以上のシリカを用いた硬化性組成物は、何れも良好な粘度と機械物性を示した。
【０２７６】
【発明の効果】
本発明は、架橋性シリル基を少なくとも１個有するビニル系重合体、及び、平均粒径１μｍ以上５００μｍ以下のシリカからなる硬化性組成物からなり、その硬化性組成物の粘度をそれ程増大させずに作業性を確保しながら、機械物性もそれほど低下させずに、組成物をシリカ等により増量させた硬化性組成物を提供できる。更に、この増量剤を配合することにより、良好なビニル系重合体の耐油性を更に向上させることや、従来のヒュームドシリカ系充填剤のみを使用する場合よりも配合コストを安価にすることも可能となる。[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a curable composition containing a vinyl polymer (I) having at least one crosslinkable silyl group and silica (II) having an average particle size of 1 μm or more and 500 μm or less.
[0002]
[Prior art]
Among the polymers obtained by ionic polymerization or polycondensation, vinyl polymers obtained by radical polymerization and having a functional group, particularly a functional group at a terminal, have not been practically used yet. Among vinyl polymers, (meth) acrylic polymers have properties such as high weather resistance and transparency, which cannot be obtained with polyether polymers, hydrocarbon polymers, or polyester polymers. Those having an alkenyl group or a crosslinkable silyl group in the side chain are used for highly weather-resistant paints and the like. On the other hand, it is not easy to control the polymerization of the acrylic polymer due to its side reaction, and it is very difficult to introduce a functional group into the terminal.
[0003]
If a vinyl polymer having an alkenyl group at a molecular chain terminal can be obtained by a simple method, a cured product having excellent cured properties can be obtained as compared with a product having a crosslinkable group in a side chain. Therefore, many researchers have studied the production method, but it is not easy to produce them industrially. For example, JP-A-1-247403 and JP-A-5-255415 disclose a method of synthesizing a (meth) acrylic polymer having an alkenyl group at a terminal using an alkenyl group-containing disulfide as a chain transfer agent. .
[0004]
JP-A-5-262808 discloses that a vinyl polymer having a hydroxyl group at both terminals is synthesized using a disulfide having a hydroxyl group, and an alkenyl group is added to the terminal using the reactivity of the hydroxyl group. A method for synthesizing a (meth) acrylic polymer is disclosed.
[0005]
JP-A-5-212922 discloses that a vinyl polymer having a hydroxyl group at both ends is synthesized using a polysulfide having a hydroxyl group, and a silyl group is added to the terminal by utilizing the reactivity of the hydroxyl group. A method for synthesizing a (meth) acrylic polymer is disclosed.
[0006]
In these methods, it is difficult to reliably introduce functional groups at both ends, and a cured product having satisfactory properties cannot be obtained. In order to surely introduce a functional group into both terminals, a large amount of a chain transfer agent must be used, which is a problem in the production process. Further, in these methods, since ordinary radical polymerization is used, it is difficult to control the molecular weight and molecular weight distribution (ratio of weight average molecular weight to number average molecular weight) of the obtained polymer.
[0007]
In contrast to such conventional techniques, the inventors have made numerous inventions on vinyl polymers having various crosslinkable functional groups at their terminals, their production methods, curable compositions, and applications. (JP-A-11-080249, JP-A-11-080250, JP-A-11-005815, JP-A-11-116617, JP-A-11-116606, JP-A-11-080571, JP-A-11-080570, JP-A-11-130931, See JP-A-11-100433, JP-A-11-116763, JP-A-9-272714 and JP-A-9-272715.
[0008]
For example, a silicon-containing group having a hydroxyl group or a hydrolyzable group bonded to a silicon atom and capable of crosslinking by forming a siloxane bond even at room temperature by moisture or the like (hereinafter, also referred to as a “crosslinkable silyl group”). The cured product obtained from the vinyl polymer having the composition or the composition thereof is excellent in heat resistance or weather resistance, and is not particularly limited, but a sealing material in a building elastic sealing material sealant, a double glass sealing material, and the like. Electric and electronic parts materials such as sealing materials for battery backsides, electrical insulating materials such as insulating coatings for electric wires and cables, adhesives, adhesives, elastic adhesives, paints, powder paints, coating materials, foams, can lids Sealing materials, electric and electronic potting agents, films, gaskets, casting materials, various molding materials, artificial marble, glass with mesh and laminated glass The end face rust-waterproof sealing material (cut portion), automotive parts and electrical parts, various machine parts liquid sealing agent used in such, are available in a variety of applications of the seal, etc. and the like.
[0009]
The curable composition having this polymer used for such various applications is used by mixing with a filler for the purpose of reinforcing (improving the strength) of the cured product obtained by curing the composition and reducing the cost. May be However, depending on the type of the filler, problems may occur such that the cost cannot be reduced or the mechanical properties such as the tensile properties of the cured product do not improve to the extent expected even if added. .
[0010]
For example, liquid gaskets and the like used around automobile engines are required to have sealing properties even under severe conditions such as exposure to a heated high-temperature atmosphere or exposure to a high-temperature engine oil. In some cases, a large amount of silica having a small particle size such as fumed silica is blended in the product. However, when used in combination with such a filler, mechanical properties such as breaking strength and elongation can be improved, but the viscosity of the curable composition increases and the workability decreases, and sometimes work becomes difficult. Sometimes it was difficult. In order to solve this problem, a large amount of low-viscosity plasticizers and solvents are added, and if the workability is to be ensured, good oil resistance cannot be exhibited, and the performance of the cured product decreases. There were also things that I did.
[0011]
[Problems to be solved by the invention]
An object of the present invention is to provide a curable composition having a vinyl polymer having a crosslinkable functional group, which ensures workability without increasing the viscosity of the curable composition so much, and which can increase the mechanical properties without significantly decreasing the mechanical properties. It is to provide a composition. Furthermore, by blending this extender, it is possible to further improve the oil resistance of a good vinyl polymer and to lower the blending cost compared to the case where only the conventional fumed silica filler is used. It becomes possible.
[0012]
[Means for Solving the Problems]
The present inventors have conducted intensive studies to solve such problems, and as a result, a vinyl polymer having at least one crosslinkable silyl group and silica having an average particle diameter of 1 μm or more and 500 μm or less as main components. The present inventors have found that the above problems can be solved by using a curable composition, and have completed the present invention.
[0013]
That is, the present invention relates to a curable composition containing a vinyl polymer (I) having at least one crosslinkable silyl group and silica (II) having an average particle size of 1 μm or more and 500 μm or less.
[0014]
The vinyl polymer (I) is not particularly limited, but the ratio of the weight average molecular weight (Mw) to the number average molecular weight (Mn) (Mw / Mn) measured by gel permeation chromatography is less than 1.8. Preferably it is.
[0015]
Further, the main chain of the vinyl polymer (I) is not particularly limited, but may be a group consisting of (meth) acrylic monomers, acrylonitrile monomers, aromatic vinyl monomers, fluorine-containing vinyl monomers, and silicon-containing vinyl monomers. It is preferably produced by mainly polymerizing a monomer selected from the group consisting of (meth) acrylic monomers, more preferably acrylic monomers, and more preferably acrylic ester monomers, for general building applications. In view of the above, from the viewpoint that physical properties such as low viscosity of the blend, low modulus of the cured product, high elongation, weather resistance, heat resistance and the like are required, it is most preferable to produce by polymerization using a butyl acrylate monomer. On the other hand, for applications such as around an engine of an automobile or a machine that requires oil resistance, heat resistance, high strength, etc., it is preferable to produce by polymerization using an ethyl acrylate-based monomer. It is more preferable that the copolymer is produced by copolymerizing an ethyl acrylate-based monomer mainly with a 2-methoxyethyl acrylate-based monomer or a butyl acrylate-based monomer from the viewpoint of properties and the like. The ratio of monomers to be copolymerized can be changed in consideration of physical properties such as oil resistance and low-temperature characteristics.
[0016]
The main chain of the vinyl polymer (I) is not particularly limited, but is preferably produced by living radical polymerization, more preferably atom transfer radical polymerization. Furthermore, the atom transfer radical polymerization is not limited, but a catalyst selected from transition metal complexes having a central metal of Group 7, 8, 9, 10, or 11 of the periodic table as a catalyst. Are preferable, and a complex selected from the group consisting of copper, nickel, ruthenium, and iron complexes is more preferable, and a copper complex is particularly preferable.
[0017]
The position of the crosslinkable silyl group of the vinyl polymer (I) is not limited, but is preferably at the terminal. In addition, a similar functional group may be provided inside the main chain, but it is preferable that the crosslinked cured product has a functional group only at the terminal when rubber elasticity is required.
[0018]
The number of crosslinkable functional groups in the vinyl polymer (I) is not particularly limited, but it is preferable that the number of crosslinkable functional groups is one or more on average, and more preferably 1. The number is 1 or more and 4.0 or less, more preferably 1.2 or more and 3.5 or less.
[0019]
BEST MODE FOR CARRYING OUT THE INVENTION
The present invention relates to curable compositions. More specifically, the following two components:
The present invention relates to a curable composition containing a vinyl polymer (I) having at least one crosslinkable functional group and silica (II) having an average particle size of 1 μm or more and 500 μm or less.
Hereinafter, the curable composition of the present invention will be described in detail.
<< About vinyl polymer >>
<Main chain>
The inventors of the present invention have made numerous inventions on a vinyl polymer having various crosslinkable functional groups at the polymer terminal, a production method thereof, a curable composition, and a use thereof (JP-A-11-080249). JP-A-11-080250, JP-A-11-005815, JP-A-11-116617, JP-A-11-116606, JP-A-11-080571, JP-A-11-080570, JP-A-11-130931, and JP-A-11-100433. See Japanese Unexamined Patent Publication No. Hei 11-11663, JP-A-9-272714 and JP-A-9-272715). The vinyl polymer (I) of the present invention is not particularly limited, but all the polymers disclosed in the above exemplified invention can be suitably used.
[0020]
The vinyl monomer constituting the main chain of the vinyl polymer of the present invention is not particularly limited, and various types can be used. For example, (meth) acrylic acid, methyl (meth) acrylate, ethyl (meth) acrylate, n-propyl (meth) acrylate, isopropyl (meth) acrylate, n- (meth) acrylate Butyl, isobutyl (meth) acrylate, tert-butyl (meth) acrylate, n-pentyl (meth) acrylate, n-hexyl (meth) acrylate, cyclohexyl (meth) acrylate, (meth) acryl Acid n-heptyl, n-octyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, nonyl (meth) acrylate, decyl (meth) acrylate, dodecyl (meth) acrylate, (meth) Phenyl acrylate, tolyl (meth) acrylate, benzyl (meth) acrylate, 2-methoxyethyl (meth) acrylate, 3-methoxybutyl (meth) acrylate, 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, stearyl (meth) acrylate, glycidyl (meth) acrylate, (meth) acryl 2-aminoethyl acid, γ- (methacryloyloxypropyl) trimethoxysilane, an ethylene oxide adduct of (meth) acrylic acid, trifluoromethylmethyl (meth) acrylate, 2-trifluoromethylethyl (meth) acrylate, Perfluoroethylmethyl (meth) acrylate, 2-perfluoroethylethyl (meth) acrylate, perfluoroethylperfluorobutylmethyl (meth) acrylate, 2-perfluoroethyl-2-perfluoro (meth) acrylate Butylethyl, (meth) acrylic acid perflu Oroethyl, perfluoromethyl (meth) acrylate, diperfluoromethylmethyl (meth) acrylate, 2,2-diperfluoromethylethyl (meth) acrylate, perfluoromethyl perfluoroethylmethyl (meth) acrylate, 2-perfluoromethyl-2-perfluoroethylethyl (meth) acrylate, 2-perfluorohexylmethyl (meth) acrylate, 2-perfluorohexylethyl (meth) acrylate, 2-per (meth) acrylate (Meth) acrylic monomers such as fluorodecylmethyl, 2-perfluorodecylethyl (meth) acrylate, 2-perfluorohexadecylmethyl (meth) acrylate, 2-perfluorohexadecylethyl (meth) acrylate; Styrene, vinyltoluene, α-methylstyrene, Aromatic vinyl monomers such as styrene, styrene sulfonic acid and salts thereof; fluorine-containing vinyl monomers such as perfluoroethylene, perfluoropropylene and vinylidene fluoride; silicon-containing vinyl monomers such as vinyltrimethoxysilane and vinyltriethoxysilane Monomers: maleic anhydride, maleic acid, monoalkyl and dialkyl esters of maleic acid; fumaric acid, monoalkyl and dialkyl esters of fumaric acid; maleimide, methylmaleimide, ethylmaleimide, propylmaleimide, butylmaleimide, hexylmaleimide, octyl Maleimide-based monomers such as maleimide, dodecylmaleimide, stearylmaleimide, phenylmaleimide, cyclohexylmaleimide; acrylonitrile, methacrylonitrile Acrylonitrile monomers such as acrylamide, methacrylamide and the like; vinyl monomers containing amide groups such as acrylamide and methacrylamide; vinyl esters such as vinyl acetate, vinyl propionate, vinyl pivalate, vinyl benzoate and vinyl cinnamate; alkenes such as ethylene and propylene Conjugated dienes such as butadiene and isoprene; and vinyl chloride, vinylidene chloride, allyl chloride, allyl alcohol and the like. These may be used alone or a plurality of them may be copolymerized.
[0021]
The main chain of the vinyl polymer mainly polymerizes at least one monomer selected from the group consisting of (meth) acrylic monomers, acrylonitrile monomers, aromatic vinyl monomers, fluorine-containing vinyl monomers and silicon-containing vinyl monomers. It is preferable that it is manufactured by the following method. Here, “mainly” means that at least 50 mol%, preferably at least 70%, of the monomer units constituting the vinyl polymer are the above-mentioned monomers.
[0022]
Among them, styrene-based monomers and (meth) acrylic acid-based monomers are preferred in view of the physical properties of the product. More preferred are acrylate monomers and methacrylate monomers, and particularly preferred are acrylate monomers. In applications such as general building applications, butyl acrylate monomers are more preferred from the viewpoint that physical properties such as low viscosity of the blend, low modulus of the cured product, high elongation, weather resistance and heat resistance are required. On the other hand, in applications requiring oil resistance and the like, such as automotive applications, a copolymer mainly containing ethyl acrylate is more preferable. This polymer mainly composed of ethyl acrylate has excellent oil resistance, but tends to be slightly inferior in low-temperature characteristics (cold resistance). In order to improve the low-temperature characteristics, a part of ethyl acrylate is converted to butyl acrylate. It is also possible to replace it. However, as the ratio of butyl acrylate is increased, its good oil resistance is impaired. Therefore, for applications requiring oil resistance, the ratio is preferably set to 40% or less, and more preferably to 30% or less. More preferably, It is also preferable to use 2-methoxyethyl acrylate or 2-ethoxyethyl acrylate in which oxygen has been introduced into the alkyl group in the side chain in order to improve low-temperature characteristics without impairing oil resistance. However, since the heat resistance tends to be inferior due to the introduction of an alkoxy group having an ether bond in the side chain, when heat resistance is required, the ratio is preferably set to 40% or less. It is possible to obtain a suitable polymer by considering the required properties such as oil resistance, heat resistance, and low-temperature properties and changing the ratio according to various uses and required purposes. For example, without limitation, examples of excellent physical properties such as oil resistance, heat resistance, and low-temperature properties include ethyl acrylate / butyl acrylate / 2-methoxyethyl acrylate (weight ratio of 40 to 50/20 to 30/30 to 20).
[0023]
In the present invention, these preferable monomers may be copolymerized with other monomers, or may be further subjected to block copolymerization. In such a case, it is preferable that these preferable monomers are contained in a weight ratio of 40%. In the above expression format, for example, (meth) acrylic acid means acrylic acid and / or methacrylic acid.
[0024]
The molecular weight distribution of the vinyl polymer of the present invention, that is, the ratio (Mw / Mn) between the weight average molecular weight (Mw) and the number average molecular weight (Mn) measured by gel permeation chromatography is not particularly limited, but is preferable. Is less than 1.8, more preferably 1.7 or less, still more preferably 1.6 or less, still more preferably 1.5 or less, particularly preferably 1.4 or less, and most preferably. Is 1.3 or less. In the GPC measurement in the present invention, usually, chloroform is used as a mobile phase, the measurement is performed using a polystyrene gel column, and the number average molecular weight and the like can be obtained in terms of polystyrene.
[0025]
The number average molecular weight of the vinyl polymer in the present invention is not particularly limited, but is preferably in the range of 500 to 1,000,000, more preferably 1,000 to 100,000, as measured by gel permeation chromatography. , 5,000-50,000.
<Main chain synthesis method>
The method for synthesizing the vinyl polymer in the present invention is not limited, but controlled radical polymerization is preferred, living radical polymerization is more preferred, and atom transfer radical polymerization is particularly preferred. These will be described below.
Controlled radical polymerization
The radical polymerization method is a `` general radical polymerization method '' in which a monomer having a specific functional group and a vinyl monomer are simply copolymerized using an azo compound, a peroxide, or the like as a polymerization initiator, and a terminal. Can be classified into a "controlled radical polymerization method" in which a specific functional group can be introduced at a controlled position.
[0026]
The `` general radical polymerization method '' is a simple method, but in this method, a monomer having a specific functional group is stochastically introduced into the polymer, so that a polymer having a high functionalization rate is obtained. In such a case, it is necessary to use a considerably large amount of the monomer, and conversely, if the monomer is used in a small amount, there is a problem that the proportion of the polymer into which the specific functional group is not introduced becomes large. In addition, since it is free radical polymerization, there is a problem that only a polymer having a wide molecular weight distribution and a high viscosity can be obtained.
[0027]
The “controlled radical polymerization method” further includes a “chain transfer agent method” in which a vinyl polymer having a functional group at a terminal is obtained by performing polymerization using a chain transfer agent having a specific functional group. It can be classified as a “living radical polymerization method” in which a polymer having a molecular weight substantially as designed can be obtained by growing the terminal without causing a termination reaction or the like.
[0028]
The “chain transfer agent method” can obtain a polymer having a high functionalization rate, but requires a considerably large amount of a chain transfer agent having a specific functional group with respect to the initiator, and includes a treatment. There is an economic problem. Further, similarly to the above-mentioned "general radical polymerization method", there is also a problem that since it is free radical polymerization, only a polymer having a wide molecular weight distribution and a high viscosity can be obtained.
[0029]
Unlike these polymerization methods, the “living radical polymerization method” has a high polymerization rate and is susceptible to a termination reaction due to coupling between radicals. It is difficult to obtain a polymer having a narrow molecular weight distribution (Mw / Mn is about 1.1 to 1.5), and the molecular weight can be freely controlled by the charging ratio of the monomer and the initiator.
[0030]
Therefore, the `` living radical polymerization method '' has a narrow molecular weight distribution and can obtain a polymer having a low viscosity, and can introduce a monomer having a specific functional group into almost any position of the polymer, It is more preferable as a method for producing the vinyl polymer having the above specific functional group.
[0031]
In the narrow sense, living polymerization refers to polymerization in which the terminal always has activity and the molecular chain grows, but in general, the polymerization in which the terminal is inactivated and the one in which the terminal is activated are activated. Pseudo-living polymerization that grows in an equilibrium state is also included. The definition in the present invention is also the latter.
[0032]
“Living radical polymerization” has been actively studied in recent years by various groups. Examples thereof include those using a cobalt porphyrin complex as shown in, for example, Journal of American Chemical Society (J. Am. Chem. Soc.), 1994, 116, 7943, Macromolecules “Atom transfer radical polymerization” using a radical scavenger such as a nitroxide compound as shown in (Macromolecules), Vol. 27, p. 7228, 1994, and using an organic halide or the like as an initiator and a transition metal complex as a catalyst ( Atom @ Transfer @ Radical @ Polymerization: ATRP).
[0033]
Among the "living radical polymerization methods", the "atom transfer radical polymerization method" in which a vinyl monomer is polymerized using an organic halide or a sulfonyl halide compound as an initiator and a transition metal complex as a catalyst is the above-mentioned "living radical polymerization method". In addition to the features described above, the production of vinyl polymers having specific functional groups is possible because of having a halogen or the like at the terminal that is relatively advantageous for the functional group conversion reaction and having a high degree of freedom in designing initiators and catalysts. The method is more preferable. As the atom transfer radical polymerization method, for example, Matyjaszewski et al., Journal of American Chemical Society (J. Am. Chem. Soc.) 1995, 117, 5614, Macromolecules 1995, 28, 7901, Science 1996, 272, 866, WO96 / 30421, WO97 / 18247, WO98 / 01480, WO98 / 40415, or Sawamoto et al., Macromolecules (Macromolecules) 1995, Vol. 28, p. 1721, JP-A-9-208616, JP-A-8-41117, and the like.
[0034]
In the present invention, although any of these living radical polymerization methods is not particularly limited, an atom transfer radical polymerization method is preferable.
[0035]
In the following, living radical polymerization will be described in detail, but before that, one of the controlled radical polymerizations that can be used for the production of a vinyl polymer described later, polymerization using a chain transfer agent will be described. I do. The radical polymerization using a chain transfer agent (telomer) is not particularly limited, but the following two methods are exemplified as a method for obtaining a vinyl polymer having a terminal structure suitable for the present invention.
[0036]
JP-A-4-132706 discloses a method for obtaining a halogen-terminated polymer by using a halogenated hydrocarbon as a chain transfer agent, and JP-A-61-271306 and JP-A-2594402. This is a method for obtaining a hydroxyl group-terminated polymer using a hydroxyl group-containing mercaptan or a hydroxyl group-containing polysulfide as a chain transfer agent as disclosed in Japanese Patent Application Laid-Open No. 54-47782.
[0037]
Hereinafter, living radical polymerization will be described.
[0038]
First, a method using a radical scavenger such as a nitroxide compound will be described. In this polymerization, a stable nitroxy free radical (= NO) is generally used as a radical capping agent. Examples of such compounds include, but are not limited to, 2,2,6,6-substituted-1-piperidinyloxy radical and 2,2,5,5-substituted-1-pyrrolidinyloxy radical. Nitroxy free radicals from cyclic hydroxyamines are preferred. As the substituent, an alkyl group having 4 or less carbon atoms such as a methyl group and an ethyl group is suitable. Specific nitroxy free radical compounds include, but are not limited to, 2,2,6,6-tetramethyl-1-piperidinyloxy radical (TEMPO), 2,2,6,6-tetraethyl-1- Piperidinyloxy radical, 2,2,6,6-tetramethyl-4-oxo-1-piperidinyloxy radical, 2,2,5,5-tetramethyl-1-pyrrolidinyloxy radical, 1,3,3-tetramethyl-2-isoindolinyloxy radical, N, N-di-t-butylamineoxy radical and the like. Instead of the nitroxy free radical, a stable free radical such as galvinoxyl free radical may be used.
[0039]
The radical capping agent is used in combination with a radical generator. It is considered that the reaction product of the radical capping agent and the radical generator serves as a polymerization initiator, and the polymerization of the addition-polymerizable monomer proceeds. The combination ratio of the two is not particularly limited, but 0.1 to 10 mol of the radical initiator is appropriate for 1 mol of the radical capping agent.
[0040]
As the radical generator, various compounds can be used, but a peroxide capable of generating a radical under polymerization temperature conditions is preferable. Examples of the peroxide include, but are not limited to, diacyl peroxides such as benzoyl peroxide and lauroyl peroxide; dialkyl peroxides such as dicumyl peroxide and di-t-butyl peroxide; diisopropyl peroxydicarbonate; There are peroxycarbonates such as (4-t-butylcyclohexyl) peroxydicarbonate and alkyl peresters such as t-butylperoxyoctoate and t-butylperoxybenzoate. Particularly, benzoyl peroxide is preferred. Further, a radical generator such as a radical-generating azo compound such as azobisisobutyronitrile may be used instead of the peroxide.
[0041]
Macromolecules @ 1995, 28, p. As reported in 2993, instead of using a radical capping agent and a radical generator together, an alkoxyamine compound as shown in the following figure may be used as an initiator.
[0042]
Embedded image

When an alkoxyamine compound is used as an initiator, if it has a functional group such as a hydroxyl group as shown in the above figure, a polymer having a functional group at the terminal can be obtained. When this is used in the method of the present invention, a polymer having a functional group at a terminal can be obtained.
[0043]
The polymerization conditions such as a monomer, a solvent, and a polymerization temperature used in the polymerization using the radical scavenger such as the nitroxide compound are not limited, but may be the same as those used for the atom transfer radical polymerization described below.
Atom transfer radical polymerization
Next, a more preferred atom transfer radical polymerization method as the living radical polymerization of the present invention will be described.
[0044]
In this atom transfer radical polymerization, an organic halide, particularly an organic halide having a highly reactive carbon-halogen bond (for example, a carbonyl compound having a halogen at the α-position or a compound having a halogen at the benzyl position) or a halogenated compound A sulfonyl compound or the like is used as an initiator.
To give a concrete example,
C₆H₅-CH₂X, C₆H₅-C (H) (X) CH₃, C₆H₅-C (X) (CH₃)₂(However, in the above chemical formula, C₆H₅Is a phenyl group, X is chlorine, bromine, or iodine)
R¹-C (H) (X) -CO₂R², R¹-C (CH₃) (X) -CO₂R², R¹-C (H) (X) -C (O) R², R¹-C (CH₃) (X) -C (O) R²,
(Where R¹, R²Is a hydrogen atom or an alkyl, aryl, or aralkyl group having 1 to 20 carbon atoms, and X is chlorine, bromine, or iodine.
R¹-C₆H₄-SO₂X
(Where R¹Is a hydrogen atom or an alkyl, aryl, or aralkyl group having 1 to 20 carbon atoms, and X is chlorine, bromine, or iodine.
And the like.
[0045]
As an initiator of the atom transfer radical polymerization, an organic halide or a sulfonyl halide compound having a functional group other than the functional group that initiates the polymerization can also be used. In such a case, a vinyl polymer having a functional group at one main chain terminal and a growing terminal structure of atom transfer radical polymerization at the other main chain terminal is produced. Examples of such a functional group include an alkenyl group, a crosslinkable silyl group, a hydroxyl group, an epoxy group, an amino group, and an amide group.
[0046]
The organic halide having an alkenyl group is not limited, and examples thereof include those having a structure represented by the general formula (1).
R⁴R⁵C (X) -R⁶-R⁷-C (R³) = CH₂(1)
(Where R³Is hydrogen or a methyl group, R⁴, R⁵Is hydrogen, or a monovalent alkyl group, aryl group, or aralkyl group having 1 to 20 carbon atoms, or those mutually linked at the other end;⁶Is -C (O) O- (ester group), -C (O)-(keto group), or o-, m-, p-phenylene group, R⁷Is a direct bond, or a divalent organic group having 1 to 20 carbon atoms and may contain one or more ether bonds. X is chlorine, bromine, or iodine.
Substituent R⁴, R⁵Specific examples include hydrogen, methyl, ethyl, n-propyl, isopropyl, butyl, pentyl, hexyl and the like. R⁴And R⁵May be linked at the other end to form a cyclic skeleton.
[0047]
Specific examples of the organic halide having an alkenyl group represented by the general formula (1) include:
XCH₂C (O) O (CH₂)_nCH = CH₂, H₃CC (H) (X) C (O) O (CH₂)_nCH = CH₂, (H₃C)₂C (X) C (O) O (CH₂)_nCH = CH₂, CH₃CH₂C (H) (X) C (O) O (CH₂)_nCH = CH₂,
[0048]
Embedded image

(In each of the above formulas, X is chlorine, bromine, or iodine, and n is an integer of 0 to 20.)
XCH₂C (O) O (CH₂)_nO (CH₂)_mCH = CH₂, H₃CC (H) (X) C (O) O (CH₂)_nO (CH₂)_mCH = CH₂, (H₃C)₂C (X) C (O) O (CH₂)_nO (CH₂)_mCH = CH₂, CH₃CH₂C (H) (X) C (O) O (CH₂)_nO (CH₂)_mCH = CH₂,
[0049]
Embedded image

(In each of the above formulas, X is chlorine, bromine, or iodine, n is an integer of 1 to 20, and m is an integer of 0 to 20.)
o, m, p-XCH₂-C₆H₄− (CH₂)_n-CH = CH₂, O, m, p-CH₃C (H) (X) -C₆H₄− (CH₂)_n-CH = CH₂, O, m, p-CH₃CH₂C (H) (X) -C₆H₄− (CH₂)_n-CH = CH₂,
(In each of the above formulas, X is chlorine, bromine, or iodine, and n is an integer of 0 to 20.)
o, m, p-XCH₂-C₆H₄− (CH₂)_n-O- (CH₂)_m-CH = CH₂, O, m, p-CH₃C (H) (X) -C₆H₄− (CH₂)_n-O- (CH₂)_m-CH = CH₂, O, m, p-CH₃CH₂C (H) (X) -C₆H₄− (CH₂)_n-O- (CH₂)_mCH = CH₂,
(In each of the above formulas, X is chlorine, bromine, or iodine, n is an integer of 1 to 20, and m is an integer of 0 to 20.)
o, m, p-XCH₂-C₆H₄-O- (CH₂)_n-CH = CH₂, O, m, p-CH₃C (H) (X) -C₆H₄-O- (CH₂)_n-CH = CH₂, O, m, p-CH₃CH₂C (H) (X) -C₆H₄-O- (CH₂)_n-CH = CH₂,
(In each of the above formulas, X is chlorine, bromine, or iodine, and n is an integer of 0 to 20.)
o, m, p-XCH₂-C₆H₄-O- (CH₂)_n-O- (CH₂)_m-CH = CH₂, O, m, p-CH₃C (H) (X) -C₆H₄-O- (CH₂)_n-O- (CH₂)_m-CH = CH₂, O, m, p-CH₃CH₂C (H) (X) -C₆H₄-O- (CH₂)_n-O- (CH₂)_m-CH = CH₂,
(In each of the above formulas, X is chlorine, bromine, or iodine, n is an integer of 1 to 20, and m is an integer of 0 to 20.)
Examples of the organic halide having an alkenyl group further include a compound represented by the general formula (2).
H₂C = C (R³) -R⁷-C (R⁴) (X) -R⁸-R⁵(2)
(Where R³, R⁴, R⁵, R⁷, X is the same as above, R⁸Represents a direct bond, -C (O) O- (ester group), -C (O)-(keto group), or o-, m-, p-phenylene group)
R⁷Is a direct bond, or a divalent organic group having 1 to 20 carbon atoms (which may contain one or more ether bonds). The group is attached and is a halogenated allylic compound. In this case, since the carbon-halogen bond is activated by the adjacent vinyl group, R⁸Need not necessarily have a C (O) O group, a phenylene group, etc., and may be a direct bond. R⁷Is not a direct bond, to activate the carbon-halogen bond, R⁸Are preferably a C (O) O group, a C (O) group and a phenylene group.
[0050]
If the compound of the general formula (2) is specifically exemplified,
CH₂= CHCH₂X, CH₂= C (CH₃) CH₂X, CH₂= CHC (H) (X) CH₃, CH₂= C (CH₃) C (H) (X) CH₃, CH₂= CHC (X) (CH₃)₂, CH₂= CHC (H) (X) C₂H₅, CH₂= CHC (H) (X) CH (CH₃)₂, CH₂= CHC (H) (X) C₆H₅, CH₂= CHC (H) (X) CH₂C₆H₅, CH₂= CHCH₂C (H) (X) -CO₂R, CH₂= CH (CH₂)₂C (H) (X) -CO₂R, CH₂= CH (CH₂)₃C (H) (X) -CO₂R, CH₂= CH (CH₂)₈C (H) (X) -CO₂R, CH₂= CHCH₂C (H) (X) -C₆H₅, CH₂= CH (CH₂)₂C (H) (X) -C₆H₅, CH₂= CH (CH₂)₃C (H) (X) -C₆H₅,
(In each of the above formulas, X is chlorine, bromine, or iodine, and R is an alkyl group, an aryl group, or an aralkyl group having 1 to 20 carbon atoms.)
And the like.
[0051]
Specific examples of the sulfonyl halide compound having an alkenyl group include o-, m-, p-CH₂= CH- (CH₂)_n-C₆H₄-SO₂X, o-, m-, p-CH₂= CH- (CH₂)_n-OC₆H₄-SO₂X,
(In each of the above formulas, X is chlorine, bromine, or iodine, and n is an integer of 0 to 20.)
And so on.
[0052]
The organic halide having a crosslinkable silyl group is not particularly limited, and examples thereof include those having a structure represented by the general formula (3).
R⁴R⁵C (X) -R⁶-R⁷-C (H) (R³) CH₂− [Si (R⁹)_2-b(Y)_bO]_m-Si (R¹⁰)_3-a(Y)_a(3)
(Where R³, R⁴, R⁵, R⁶, R⁷, X is the same as above, R⁹, R¹⁰Is an alkyl group having 1 to 20 carbon atoms, an aryl group, an aralkyl group, or (R ′)₃A triorganosiloxy group represented by SiO- (R 'is a monovalent hydrocarbon group having 1 to 20 carbon atoms, and three R's may be the same or different); , R⁹Or R¹⁰When two or more are present, they may be the same or different. Y represents a hydroxyl group or a hydrolyzable group, and when two or more Ys are present, they may be the same or different. a represents 0, 1, 2, or 3, and b represents 0, 1, or 2. m is an integer of 0-19. However, it is assumed that a + mb ≧ 1 is satisfied.)
If the compound of the general formula (3) is specifically exemplified,
XCH₂C (O) O (CH₂)_nSi (OCH₃)₃, CH₃C (H) (X) C (O) O (CH₂)_nSi (OCH₃)₃, (CH₃)₂C (X) C (O) O (CH₂)_nSi (OCH₃)₃, XCH₂C (O) O (CH₂)_nSi (CH₃) (OCH₃)₂, CH₃C (H) (X) C (O) O (CH₂)_nSi (CH₃) (OCH₃)₂, (CH₃)₂C (X) C (O) O (CH₂)_nSi (CH₃) (OCH₃)₂,
(In each of the above formulas, X is chlorine, bromine, iodine, n is an integer of 0 to 20,
XCH₂C (O) O (CH₂)_nO (CH₂)_mSi (OCH₃)₃, H₃CC (H) (X) C (O) O (CH₂)_nO (CH₂)_mSi (OCH₃)₃, (H₃C)₂C (X) C (O) O (CH₂)_nO (CH₂)_mSi (OCH₃)₃, CH₃CH₂C (H) (X) C (O) O (CH₂)_nO (CH₂)_mSi (OCH₃)₃, XCH₂C (O) O (CH₂)_nO (CH₂)_mSi (CH₃) (OCH₃)₂, H₃CC (H) (X) C (O) O (CH₂)_nO (CH₂)_m-Si (CH₃) (OCH₃)₂, (H₃C)₂C (X) C (O) O (CH₂)_nO (CH₂)_m-Si (CH₃) (OCH₃)₂, CH₃CH₂C (H) (X) C (O) O (CH₂)_nO (CH₂)_m-Si (CH₃) (OCH₃)₂,
(In each of the above formulas, X is chlorine, bromine, iodine, n is an integer of 1 to 20, and m is an integer of 0 to 20.)
o, m, p-XCH₂-C₆H₄− (CH₂)₂Si (OCH₃)₃, O, m, p-CH₃C (H) (X) -C₆H₄− (CH₂)₂Si (OCH₃)₃, O, m, p-CH₃CH₂C (H) (X) -C₆H₄− (CH₂)₂Si (OCH₃)₃, O, m, p-XCH₂-C₆H₄− (CH₂)₃Si (OCH₃)₃, O, m, p-CH₃C (H) (X) -C₆H₄− (CH₂)₃Si (OCH₃)₃, O, m, p-CH₃CH₂C (H) (X) -C₆H₄− (CH₂)₃Si (OCH₃)₃, O, m, p-XCH₂-C₆H₄− (CH₂)₂-O- (CH₂)₃Si (OCH₃)₃, O, m, p-CH₃C (H) (X) -C₆H₄− (CH₂)₂-O- (CH₂)₃Si (OCH₃)₃, O, m, p-CH₃CH₂C (H) (X) -C₆H₄− (CH₂)₂-O- (CH₂)₃Si (OCH₃)₃, O, m, p-XCH₂-C₆H₄-O- (CH₂)₃Si (OCH₃)₃, O, m, p-CH₃C (H) (X) -C₆H₄-O- (CH₂)₃Si (OCH₃)₃, O, m, p-CH₃CH₂C (H) (X) -C₆H₄-O- (CH₂)₃-Si (OCH₃)₃, O, m, p-XCH₂-C₆H₄-O- (CH₂)₂-O- (CH₂)₃-Si (OCH₃)₃, O, m, p-CH₃C (H) (X) -C₆H₄-O- (CH₂)₂-O- (CH₂)₃Si (OCH₃)₃, O, m, p-CH₃CH₂C (H) (X) -C₆H₄-O- (CH₂)₂-O- (CH₂)₃Si (OCH₃)₃,
(In each of the above formulas, X is chlorine, bromine, or iodine.)
And the like.
[0053]
Examples of the organic halide having a crosslinkable silyl group further include those having a structure represented by the general formula (4).
(R¹⁰)_3-a(Y)_aSi- [OSi (R⁹)_2-b(Y)_b]_m-CH₂-C (H) (R³) -R⁷-C (R⁴) (X) -R⁸-R⁵(4)
(Where R³, R⁴, R⁵, R⁷, R⁸, R⁹, R¹⁰, A, b, m, X and Y are the same as above)
If these compounds are specifically exemplified,
(CH₃O)₃SiCH₂CH₂C (H) (X) C₆H₅, (CH₃O)₂(CH₃) SiCH₂CH₂C (H) (X) C₆H₅, (CH₃O)₃Si (CH₂)₂C (H) (X) -CO₂R, (CH₃O)₂(CH₃) Si (CH₂)₂C (H) (X) -CO₂R, (CH₃O)₃Si (CH₂)₃C (H) (X) -CO₂R, (CH₃O)₂(CH₃) Si (CH₂)₃C (H) (X) -CO₂R, (CH₃O)₃Si (CH₂)₄C (H) (X) -CO₂R, (CH₃O)₂(CH₃) Si (CH₂)₄C (H) (X) -CO₂R, (CH₃O)₃Si (CH₂)₉C (H) (X) -CO₂R, (CH₃O)₂(CH₃) Si (CH₂)₉C (H) (X) -CO₂R, (CH₃O)₃Si (CH₂)₃C (H) (X) -C₆H₅, (CH₃O)₂(CH₃) Si (CH₂)₃C (H) (X) -C₆H₅, (CH₃O)₃Si (CH₂)₄C (H) (X) -C₆H₅, (CH₃O)₂(CH₃) Si (CH₂)₄C (H) (X) -C₆H₅,
(In each of the above formulas, X is chlorine, bromine, or iodine, and R is an alkyl group, an aryl group, or an aralkyl group having 1 to 20 carbon atoms.)
And the like.
[0054]
The organic halide having a hydroxyl group or the sulfonyl halide compound is not particularly limited, and examples thereof include the following.
HO- (CH₂)_n-OC (O) C (H) (R) (X)
(Wherein, X is chlorine, bromine, or iodine, R is a hydrogen atom or an alkyl group, an aryl group, an aralkyl group having 1 to 20 carbon atoms, and n is an integer of 1 to 20)
The organic halide having an amino group or the sulfonyl halide compound is not particularly limited, and examples thereof include the following.
H₂N- (CH₂)_n-OC (O) C (H) (R) (X)
(Wherein, X is chlorine, bromine, or iodine, R is a hydrogen atom or an alkyl group, an aryl group, an aralkyl group having 1 to 20 carbon atoms, and n is an integer of 1 to 20)
The organic halide having an epoxy group or the sulfonyl halide compound is not particularly limited, and examples thereof include the following.
[0055]
Embedded image

(Wherein, X is chlorine, bromine, or iodine, R is a hydrogen atom or an alkyl group, an aryl group, an aralkyl group having 1 to 20 carbon atoms, and n is an integer of 1 to 20)
In order to obtain a polymer having two or more growing terminal structures in one molecule, it is preferable to use an organic halide or a sulfonyl halide compound having two or more starting points as an initiator. To give a concrete example,
[0056]
Embedded image

[0057]
Embedded image

And the like.
[0058]
The vinyl monomer used in this polymerization is not particularly limited, and any of the above-mentioned examples can be suitably used.
[0059]
The transition metal complex used as the polymerization catalyst is not particularly limited, but is preferably a metal complex containing a Group 7, 8, 9, 9, or 11 element of the periodic table as a central metal. More preferred are complexes of zero-valent copper, monovalent copper, divalent ruthenium, divalent iron, and divalent nickel. Among them, a copper complex is preferable. Specific examples of monovalent copper compounds include cuprous chloride, cuprous bromide, cuprous iodide, cuprous cyanide, cuprous oxide, cuprous perchlorate, and the like. is there. When a copper compound is used, 2,2'-bipyridyl and its derivatives, 1,10-phenanthroline and its derivatives, tetramethylethylenediamine, pentamethyldiethylenetriamine, hexamethyltris (2-aminoethyl) amine and the like for enhancing the catalytic activity A ligand such as polyamine is added. Preferred ligands are nitrogen-containing compounds, more preferred ligands are chelating-type nitrogen-containing compounds, and further preferred ligands are N, N, N ', N ", N" -pentamethyldiethylenetriamine. It is. Also, tristriphenylphosphine complex of divalent ruthenium chloride (RuCl₂(PPh₃)₃) Are also suitable as catalysts. When a ruthenium compound is used as a catalyst, aluminum alkoxides are added as an activator. Further, bistriphenylphosphine complex of divalent iron (FeCl₂(PPh₃)₂), Bistriphenylphosphine complex of divalent nickel (NiCl₂(PPh₃)₂) And bistributylphosphine complex of divalent nickel (NiBr₂(PBu₃)₂) Are also suitable as catalysts.
[0060]
The polymerization can be carried out without solvent or in various solvents. Examples of the solvent include hydrocarbon solvents such as benzene and toluene, ether solvents such as diethyl ether and tetrahydrofuran, halogenated hydrocarbon solvents such as methylene chloride and chloroform, and ketone solvents such as acetone, methyl ethyl ketone and methyl isobutyl ketone. Solvents, alcohol solvents such as methanol, ethanol, propanol, isopropanol, n-butyl alcohol and tert-butyl alcohol; nitrile solvents such as acetonitrile, propionitrile and benzonitrile; ester solvents such as ethyl acetate and butyl acetate; Examples thereof include carbonate-based solvents such as ethylene carbonate and propylene carbonate, and these can be used alone or in combination of two or more.
[0061]
Further, although not limited, the polymerization can be carried out in the range of 0 ° C to 200 ° C, preferably 50 to 150 ° C.
[0062]
The atom transfer radical polymerization of the present invention includes so-called reverse atom transfer radical polymerization. Reverse atom transfer radical polymerization refers to a state in which a normal atom transfer radical polymerization catalyst is in a highly oxidized state when radicals are generated, for example, Cu (II ′) when Cu (I) is used as a catalyst, This is a method in which a general radical initiator such as a product is allowed to act, and as a result, an equilibrium state similar to that of atom transfer radical polymerization is produced (see Macromolecules @ 1999, 32, 2872).
<Functional group>
Number of crosslinkable functional groups
The number of the crosslinkable functional groups of the vinyl polymer (I) is not particularly limited, but from the viewpoint of the curability of the composition and the physical properties of the cured product, the number is preferably one or more on average, more preferably. It is 1.1 or more and 4.0 or less, more preferably 1.2 or more and 3.5 or less.
Location of crosslinkable functional group
When rubber properties are particularly required for the cured product obtained by curing the curable composition of the present invention, the molecular weight between crosslink points that greatly affects rubber elasticity can be increased, so that at least the crosslinkable functional group One is preferably at the end of the molecular chain. More preferably, it has all crosslinkable functional groups at the molecular chain terminals.
[0063]
A method for producing a vinyl polymer having at least one crosslinkable functional group at a molecular terminal, in particular, a (meth) acrylic polymer is disclosed in Japanese Patent Publication Nos. 3-14068 and 4-55444, It is disclosed in, for example, JP-A-6-212922. However, since these methods are free radical polymerization methods using the above “chain transfer agent method”, the resulting polymer has a relatively high ratio of crosslinkable functional groups at the molecular chain terminals, while Mw / Mn Has a problem that the value of the molecular weight distribution represented by is generally as large as 2 or more, and the viscosity becomes high. Therefore, in order to obtain a vinyl polymer having a narrow molecular weight distribution and a low viscosity, and having a high proportion of a crosslinkable functional group at a molecular chain end, the above-mentioned “living radical polymerization method” is used. Is preferred.
[0064]
Hereinafter, these functional groups will be described.
Crosslinkable silyl group
As the crosslinkable silyl group of the present invention, general formula (5):
− [Si (R⁹)_2-b(Y)_bO]_m-Si (R¹⁰)_3-a(Y)_a(5)
中 where R⁹, R¹⁰Is an alkyl group having 1 to 20 carbon atoms, an aryl group having 6 to 20 carbon atoms, an aralkyl group having 7 to 20 carbon atoms, or (R ′)₃A triorganosiloxy group represented by SiO- (R 'is a monovalent hydrocarbon group having 1 to 20 carbon atoms, and three R's may be the same or different); , R⁹Or R¹⁰When two or more are present, they may be the same or different. Y represents a hydroxyl group or a hydrolyzable group, and when two or more Ys are present, they may be the same or different. a represents 0, 1, 2, or 3, and b represents 0, 1, or 2. m is an integer of 0-19. However, it is assumed that a + mb ≧ 1 is satisfied. ｝
And the group represented by
[0065]
Examples of the hydrolyzable group include groups generally used such as a hydrogen atom, an alkoxy group, an acyloxy group, a ketoximate group, an amino group, an amide group, an aminooxy group, a mercapto group, and an alkenyloxy group. Among these, an alkoxy group, an amide group and an aminooxy group are preferred, but an alkoxy group is particularly preferred because of its mild hydrolyzability and easy handling. Among the alkoxy groups, those having a smaller number of carbon atoms have higher reactivity, the reactivity becomes lower in the order of methoxy group> ethoxy group> propoxy group, and can be selected according to the purpose and application.
[0066]
A hydrolyzable group or a hydroxyl group can be bonded to one silicon atom in a range of 1 to 3, and (a + Δb) is preferably in a range of 1 to 5. When two or more hydrolyzable groups or hydroxyl groups are bonded to the crosslinkable silyl group, they may be the same or different. The number of silicon atoms forming a crosslinkable silyl group is one or more. In the case of silicon atoms linked by a siloxane bond or the like, the number is preferably 20 or less. In particular, general formula (6);
-Si (R¹⁰)_3-a(Y)_a(6)
(Where R¹⁰, Y and a are the same as above. The crosslinkable silyl group represented by ()) is preferable because it is easily available.
[0067]
Although not particularly limited, a is preferably 2 or more in consideration of curability.
[0068]
As such a vinyl polymer having a crosslinkable silyl group, a polymer having a hydrolyzable silicon group in which two hydrolyzable groups are bonded to one silicon atom is often used. In cases where a very fast curing speed is required, such as when the application is used or at a low temperature, the curing speed is not sufficient, and when it is desired to provide flexibility after curing, it is necessary to lower the crosslinking density. In some cases, the cross-linking density was not sufficient and stickiness (surface tack) sometimes occurred. In that case, it is preferable that a is three (for example, a trimethoxy functional group).
[0069]
Further, those having three a (for example, a trimethoxy functional group) have a higher curing property than those having two (for example, a dimethoxy functional group), but those having two a for storage stability and mechanical properties (elongation and the like). May be better. Two (for example, dimethoxy functional groups) and three (for example, trimethoxy functional groups) may be used in combination in order to balance curability and physical properties.
[0070]
For example, when Y is the same, the reactivity of Y increases as the number of a increases, so that curability and mechanical properties of a cured product can be controlled by variously selecting Y and a. Can be selected according to the application.
Alkenyl group
The alkenyl group in the present invention is not limited, but is preferably one represented by the general formula (7).
H₂C = C (R¹¹)-(7)
(Where R¹¹Is a hydrogen atom or a hydrocarbon group having 1 to 20 carbon atoms)
In the general formula (7), R¹¹Is a hydrogen atom or a hydrocarbon group having 1 to 20 carbon atoms, and specific examples include the following groups.
− (CH₂)_n-CH₃, -CH (CH₃)-(CH₂)_n-CH₃, -CH (CH₂CH₃)-(CH₂)_n-CH₃, -CH (CH₂CH₃)₂, -C (CH₃)₂− (CH₂)_n-CH₃, -C (CH₃) (CH₂CH₃)-(CH₂)_n-CH₃, -C₆H₅, -C₆H₅(CH₃), -C₆H₅(CH₃)₂,-(CH₂)_n-C₆H₅,-(CH₂)_n-C₆H₅(CH₃),-(CH₂)_n-C₆H₅(CH₃)₂
(N is an integer of 0 or more, and the total carbon number of each group is 20 or less)
Of these, a hydrogen atom is preferred.
[0071]
Further, although not limited, it is preferable that the alkenyl group of the polymer (I) is not activated by a carbonyl group, an alkenyl group, or an aromatic ring conjugated to the carbon-carbon double bond.
[0072]
The form of bonding between the alkenyl group and the main chain of the polymer is not particularly limited, but is preferably bonded via a carbon-carbon bond, an ester bond, an ether bond, a carbonate bond, an amide bond, a urethane bond, or the like.
Amino group
The amino group in the present invention is not limited,
-NR¹² ₂
(R¹²Is hydrogen or a monovalent organic group having 1 to 20 carbon atoms, and two R¹²May be the same or different from each other, and may be connected to each other at the other end to form a cyclic structure. )
But
− (NR¹² ₃)⁺X⁻
(R¹²Is the same as above. X⁻Is a counter anion. )
There is no problem even with the ammonium salts shown in the above.
[0073]
In the above formula, R¹²Is hydrogen or a monovalent organic group having 1 to 20 carbon atoms, and examples thereof include hydrogen, an alkyl group having 1 to 20 carbon atoms, an aryl group having 6 to 20 carbon atoms, and an aralkyl group having 7 to 20 carbon atoms. Can be Two R¹²May be the same or different. Further, they may be connected to each other at the other end to form an annular structure.
Group having a polymerizable carbon-carbon double bond
The group having a polymerizable carbon-carbon double bond is preferably a group represented by the general formula (8):
-OC (O) C (R¹³) = CH₂(8)
(Where R¹³Represents hydrogen or a monovalent organic group having 1 to 20 carbon atoms. )
And more preferably a group represented by R¹³Is hydrogen or a group that is a methyl group.
[0074]
In the general formula (8), R¹³Is not particularly limited, for example, -H, -CH₃, -CH₂CH₃,-(CH₂)_nCH₃(N represents an integer of 2 to 19), -C₆H₅, -CH₂OH, -CN
And the like, preferably -H, -CH₃It is.
Introduction method of crosslinkable functional group
Hereinafter, a method for introducing a crosslinkable functional group into the vinyl polymer (I) of the present invention will be described, but the method is not limited thereto.
[0075]
First, a method for introducing a crosslinkable silyl group, alkenyl group, and hydroxyl group by terminal functional group conversion will be described. Since these functional groups can be precursors to each other, they are described in the order starting from the crosslinkable silyl group.
[0076]
As a method for synthesizing a vinyl polymer having at least one crosslinkable silyl group,
(A) Method of adding a hydrosilane compound having a crosslinkable silyl group to a vinyl polymer having at least one alkenyl group in the presence of a hydrosilylation catalyst
(B) A method of reacting a vinyl polymer having at least one hydroxyl group with a compound having a group capable of reacting with a hydroxyl group, such as a compound having a crosslinkable silyl group and an isocyanate group in one molecule.
(C) A method of reacting a compound having both a polymerizable alkenyl group and a crosslinkable silyl group in one molecule when synthesizing a vinyl polymer by radical polymerization.
(D) Method of using a chain transfer agent having a crosslinkable silyl group when synthesizing a vinyl polymer by radical polymerization
(E) a method in which a compound having a crosslinkable silyl group and a stable carbanion in one molecule is reacted with a vinyl polymer having at least one highly reactive carbon-halogen bond.
[0077]
The vinyl polymer having at least one alkenyl group used in the method (A) can be obtained by various methods. The synthesis method is exemplified below, but is not limited thereto.
[0078]
(Aa) When synthesizing a vinyl polymer by radical polymerization, a compound having both a polymerizable alkenyl group and a low polymerizable alkenyl group in one molecule as shown in the following general formula (9), for example. As a second monomer.
H₂C = C (R¹⁴) -R^Fifteen-R¹⁶-C (R¹⁷) = CH₂(9)
(Where R¹⁴Represents hydrogen or a methyl group;^FifteenRepresents -C (O) O- or an o-, m-, p-phenylene group;¹⁶Represents a direct bond or a divalent organic group having 1 to 20 carbon atoms, and may contain one or more ether bonds. R¹⁷Represents hydrogen, an alkyl group having 1 to 20 carbon atoms, an aryl group having 6 to 20 carbon atoms, or an aralkyl group having 7 to 20 carbon atoms)
There is no restriction on the timing of reacting a compound having both a polymerizable alkenyl group and a low polymerizable alkenyl group in one molecule. It is preferable to react as the second monomer at the end or after completion of the reaction of the predetermined monomer.
[0079]
(Ab) When a vinyl polymer is synthesized by living radical polymerization, at the end of the polymerization reaction or after the reaction of a predetermined monomer, for example, 1,5-hexadiene, 1,7-octadiene, 1,9-decadiene A method of reacting a compound having at least two alkenyl groups having low polymerizability, such as
[0080]
(Ac) Various organic metal compounds having an alkenyl group such as organic tin such as allyltributyltin and allyltrioctyltin are added to a vinyl polymer having at least one highly reactive carbon-halogen bond. A method of substituting halogen by reacting.
[0081]
(Ad) A method in which a vinyl-based polymer having at least one highly reactive carbon-halogen bond is reacted with a stabilized carbanion having an alkenyl group as shown in the general formula (10) to substitute halogen. .
M⁺C⁻(R¹⁸) (R¹⁹) -R²⁰-C (R¹⁷) = CH₂(10)
(Where R¹⁷Is the same as above, R¹⁸, R¹⁹Are both Carbanion C⁻Or one of them represents hydrogen or an alkyl group having 1 to 10 carbon atoms or a phenyl group. R²⁰Represents a direct bond or a divalent organic group having 1 to 10 carbon atoms, and may contain one or more ether bonds. M⁺Represents an alkali metal ion or a quaternary ammonium ion)
R¹⁸, R¹⁹As an electron withdrawing group of₂Those having the structures of R, -C (O) R and -CN are particularly preferred.
[0082]
(A-e) An enolate anion is prepared by reacting a vinyl polymer having at least one highly reactive carbon-halogen bond with a simple metal such as zinc or an organometallic compound. Method for reacting with an alkenyl group-containing electrophilic compound such as an alkenyl group-containing compound having a leaving group such as an acetyl group, an alkenyl group-containing carbonyl compound, an alkenyl group-containing isocyanate compound, and an alkenyl group-containing acid halide. .
[0083]
(Af) An oxyanion or carboxylate anion having an alkenyl group represented by the general formula (11) or (12) is added to a vinyl polymer having at least one highly reactive carbon-halogen bond. A method of substituting halogen by reacting.
H₂C = C (R¹⁷) -R²¹-O⁻M⁺(11)
(Where R¹⁷, M⁺Is the same as above. R²¹Is a divalent organic group having 1 to 20 carbon atoms and may contain one or more ether bonds.)
H₂C = C (R¹⁷) -R²²-C (O) O⁻M⁺(12)
(Where R¹⁷, M⁺Is the same as above. R²²Is a direct bond or a divalent organic group having 1 to 20 carbon atoms and may contain one or more ether bonds.)
And the like.
[0084]
The above-mentioned method for synthesizing a vinyl polymer having at least one highly reactive carbon-halogen bond includes the above-described atom transfer radical polymerization method using an organic halide or the like as an initiator and a transition metal complex as a catalyst. But are not limited to these.
[0085]
Further, the vinyl polymer having at least one alkenyl group can be obtained from a vinyl polymer having at least one hydroxyl group, and the method exemplified below can be used, but is not limited thereto. A hydroxyl group of a vinyl polymer having at least one hydroxyl group,
(Ag) A method of reacting with a base such as sodium methoxide and reacting with an alkenyl group-containing halide such as allyl chloride.
[0086]
(Ah) A method of reacting an alkenyl group-containing isocyanate compound such as allyl isocyanate.
[0087]
(Ai) A method of reacting an alkenyl group-containing acid halide such as (meth) acrylic acid chloride in the presence of a base such as pyridine.
[0088]
(Aj) a method of reacting an alkenyl group-containing carboxylic acid such as acrylic acid in the presence of an acid catalyst;
[0089]
In the present invention, when a halogen is not directly involved in the method for introducing an alkenyl group such as (Aa) and (Ab), it is preferable to synthesize a vinyl polymer using a living radical polymerization method. The method (Ab) is more preferable because the control is easier.
[0090]
When an alkenyl group is introduced by converting a halogen of a vinyl polymer having at least one highly reactive carbon-halogen bond, an organic halide having at least one highly reactive carbon-halogen bond, or A vinyl polymer having at least one highly reactive carbon-halogen bond at a terminal obtained by radical polymerization of a vinyl monomer (atom transfer radical polymerization) using a sulfonyl halide compound as an initiator and a transition metal complex as a catalyst. It is preferred to use coalescence. The method (Af) is more preferable because the control is easier.
[0091]
The hydrosilane compound having a crosslinkable silyl group is not particularly limited, but a representative one is exemplified by a compound represented by the general formula (13).
H- [Si (R⁹)_2-b(Y)_bO]_m-Si (R¹⁰)_3-a(Y)_a(13)
中 where R⁹, R¹⁰Is an alkyl group having 1 to 20 carbon atoms, an aryl group having 6 to 20 carbon atoms, an aralkyl group having 7 to 20 carbon atoms, or (R ′)₃A triorganosiloxy group represented by SiO- (R 'is a monovalent hydrocarbon group having 1 to 20 carbon atoms, and three R's may be the same or different); , R⁹Or R¹⁰When two or more are present, they may be the same or different. Y represents a hydroxyl group or a hydrolyzable group, and when two or more Ys are present, they may be the same or different. a represents 0, 1, 2, or 3, and b represents 0, 1, or 2. m is an integer of 0-19. However, it is assumed that a + mb ≧ 1 is satisfied. ｝
Among these hydrosilane compounds, in particular, the general formula (14)
H-Si (R¹⁰)_3-a(Y)_a(14)
(Where R¹⁰, Y and a are the same as above.)
The compound having a crosslinkable group represented by is preferred from the viewpoint of easy availability.
[0092]
When adding the above-mentioned hydrosilane compound having a crosslinkable silyl group to an alkenyl group, a transition metal catalyst is usually used. Examples of the transition metal catalyst include, for example, platinum alone, alumina, silica, a dispersion of platinum solids in a carrier such as carbon black, chloroplatinic acid, a complex of chloroplatinic acid with alcohol, aldehyde, ketone, etc., platinum-olefin Complexes, and platinum (0) -divinyltetramethyldisiloxane complex. Examples of catalysts other than platinum compounds include RhCl (PPh₃)₃, RhCl₃, RuCl₃, IrCl₃, FeCl₃, AlCl₃, PdCl₂・ H₂O, NiCl₂, TiCl₄And the like.
[0093]
Examples of the method for producing a vinyl polymer having at least one hydroxyl group used in the methods (B) and (Ag) to (Aj) include the following methods, but are not limited to these methods. Not something.
[0094]
(Ba) When synthesizing a vinyl polymer by radical polymerization, for example, a compound having both a polymerizable alkenyl group and a hydroxyl group in one molecule as shown in the following general formula (15) is used as a second monomer As a reaction.
H₂C = C (R¹⁴) -R^Fifteen-R¹⁶-OH (15)
(Where R¹⁴, R^Fifteen, R¹⁶Is the same as above)
There is no restriction on the timing of reacting a compound having both a polymerizable alkenyl group and a hydroxyl group in one molecule, but especially in the case of living radical polymerization, where rubber-like properties are expected, the end of the polymerization reaction or a predetermined monomer After completion of the above reaction, the reaction is preferably carried out as a second monomer.
[0095]
(Bb) When a vinyl polymer is synthesized by living radical polymerization, an alkenyl alcohol such as 10-undecenol, 5-hexenol, or allyl alcohol is reacted at the end of the polymerization reaction or after the reaction of a predetermined monomer is completed. How to let.
[0096]
(Bc) A method of radically polymerizing a vinyl monomer using a large amount of a hydroxyl group-containing chain transfer agent such as a hydroxyl group-containing polysulfide disclosed in JP-A-5-262808.
[0097]
(Bd) A method of radically polymerizing a vinyl monomer using hydrogen peroxide or a hydroxyl group-containing initiator as described in, for example, JP-A-6-239912 and JP-A-8-283310.
[0098]
(Be) A method of radically polymerizing a vinyl monomer by using an excess of alcohols as described in, for example, JP-A-6-11612.
[0099]
(Bf) Hydrolyzing or reacting a halogen of a vinyl polymer having at least one highly reactive carbon-halogen bond with a hydroxyl group-containing compound by a method described in, for example, JP-A-4-132706. By introducing a hydroxyl group into the terminal.
[0100]
(Bg) A method of reacting a vinyl-based polymer having at least one highly reactive carbon-halogen bond with a stabilized carbanion having a hydroxyl group as shown in the general formula (16) to replace halogen.
M⁺C⁻(R¹⁸) (R¹⁹) -R²⁰-OH (16)
(Where R¹⁸, R¹⁹, R²⁰, Is the same as above)
R¹⁸, R¹⁹As an electron withdrawing group of₂Those having the structures of R, -C (O) R and -CN are particularly preferred.
[0101]
(Bh) An enolate anion is prepared by reacting a vinyl polymer having at least one highly reactive carbon-halogen bond with, for example, a simple metal such as zinc or an organometallic compound. Or a method of reacting ketones.
[0102]
(Bi) Reaction of a vinyl polymer having at least one highly reactive carbon-halogen bond with, for example, an oxyanion or a carboxylate anion having a hydroxyl group represented by the general formula (17) or (18) To replace the halogen.
HO-R²¹-O⁻M⁺(17)
(Where R²¹And M⁺Is the same as above)
HO-R²²-C (O) O⁻M⁺(18)
(Where R²²And M⁺Is the same as above)
(Bj) When synthesizing a vinyl polymer by living radical polymerization, at the end of the polymerization reaction or after the reaction of a predetermined monomer, as a second monomer, an alkenyl group and a hydroxyl group having low polymerizability in one molecule are used. Reacting a compound having the formula:
[0103]
Such a compound is not particularly limited, and examples thereof include a compound represented by the general formula (19).
H₂C = C (R¹⁴) -R²¹-OH (19)
(Where R¹⁴And R²¹Is the same as described above. )
The compound represented by the general formula (19) is not particularly limited, but alkenyl alcohols such as 10-undecenol, 5-hexenol, and allyl alcohol are preferable because they are easily available.
And the like.
[0104]
In the present invention, when a halogen is not directly involved in a method for introducing a hydroxyl group such as (Ba) to (Be) and (Bj), a vinyl polymer is produced using a living radical polymerization method. It is preferred to synthesize. The method (Bb) is more preferable because the control is easier.
[0105]
When a hydroxyl group is introduced by converting a halogen of a vinyl polymer having at least one highly reactive carbon-halogen bond, an organic halide or a sulfonyl halide compound is used as an initiator, and a transition metal complex is used as a catalyst. It is preferable to use a vinyl polymer having at least one highly reactive carbon-halogen bond at a terminal obtained by radical polymerization of a vinyl monomer (atom transfer radical polymerization method). The method (B-i) is more preferable because the control is easier.
[0106]
Compounds having a group capable of reacting with a hydroxyl group such as a crosslinkable silyl group and an isocyanate group in one molecule include, for example, γ-isocyanatopropyltrimethoxysilane, γ-isocyanatopropylmethyldimethoxysilane, γ-isocyanate Natopropyltriethoxysilane and the like can be mentioned, and if necessary, a generally known catalyst for a urethanization reaction can be used.
[0107]
Examples of the compound having a polymerizable alkenyl group and a crosslinkable silyl group in one molecule used in the method (C) include, for example, trimethoxysilylpropyl (meth) acrylate, methyldimethoxysilylpropyl (meth) acrylate, and the like. What is shown by the following general formula (20) is mentioned.
H₂C = C (R¹⁴) -R^Fifteen-R²³− [Si (R⁹)_2-b(Y)_bO]_m-Si (R¹⁰)_3-a(Y)_a(20)
(Where R⁹, R¹⁰, R¹⁴, R^Fifteen, Y, a, b, and m are the same as above. R²³May have a direct bond or one or more ether bonds with a divalent organic group having 1 to 20 carbon atoms. )
There is no particular limitation on the timing of reacting a compound having both a polymerizable alkenyl group and a crosslinkable silyl group in one molecule. After the completion of the reaction of the monomer (2), it is preferable to make it react as a second monomer.
[0108]
Examples of the chain transfer agent having a crosslinkable silyl group used in the chain transfer agent method (D) include mercaptans having a crosslinkable silyl group and crosslinkable silyl shown in JP-B-3-14068 and JP-B-4-55444. Hydrosilane having a group is exemplified.
[0109]
In the method for synthesizing the vinyl polymer having at least one highly reactive carbon-halogen bond used in the method (E), the above-mentioned organic halide or the like is used as an initiator, and a transition metal complex is used. Examples include, but are not limited to, atom transfer radical polymerization using a catalyst. As a compound having both a crosslinkable silyl group and a stabilized carbanion in one molecule, a compound represented by the general formula (21) can be given.
M⁺C⁻(R¹⁸) (R¹⁹) -R²⁴-C (H) (R²⁵) -CH₂− [Si (R⁹)_2-b(Y)_bO]_m-Si (R¹⁰)_3-a(Y)_a(21)
(Where R⁹, R¹⁰, R¹⁸, R¹⁹, Y, a, b, m are the same as above. R²⁴Is a direct bond or a divalent organic group having 1 to 10 carbon atoms, which may contain one or more ether bonds.²⁵Represents hydrogen, an alkyl group having 1 to 10 carbon atoms, an aryl group having 6 to 10 carbon atoms, or an aralkyl group having 7 to 10 carbon atoms. )
R¹⁸, R¹⁹As an electron withdrawing group of₂Those having the structures of R, -C (O) R and -CN are particularly preferred.
Epoxy group
In the present invention, the vinyl polymer having a reactive functional group at the terminal is not limited, but includes the following steps:
(1) A vinyl polymer is produced by polymerizing a vinyl monomer by a living radical polymerization method;
(2) Subsequently, a compound having both a reactive functional group and an ethylenically unsaturated group is reacted;
It is manufactured by
[0110]
In addition, in the atom transfer radical polymerization, a method of reacting allyl alcohol at the end of the polymerization, and then performing an epoxy cyclization with a hydroxyl group and a halogen group may also be used.
Amino group
A method for producing a vinyl polymer having at least one amino group at the terminal of the main chain includes the following steps.
(1) A vinyl polymer having at least one halogen group at the terminal of the main chain is produced, and (2) a terminal halogen is converted into a substituent having an amino group using an amino group-containing compound.
[0111]
Although it does not specifically limit as a substituent which has an amino group, The group shown by General formula (22) is illustrated.
-OR²⁶-NR¹² ₂(22)
(Where R²⁶Represents a divalent organic group having 1 to 20 carbon atoms which may contain one or more ether bonds or ester bonds. R¹²Is hydrogen or a monovalent organic group having 1 to 20 carbon atoms, and two R¹²May be the same or different from each other, and may be connected to each other at the other end to form a cyclic structure. )
In the general formula (22), R²⁶Is a divalent organic group having 1 to 20 carbon atoms which may contain one or more ether bonds or ester bonds, such as an alkylene group having 1 to 20 carbon atoms, an arylene group having 6 to 20 carbon atoms, Examples include aralkylene groups having the number of 7 to 20,
-C₆H₄-R²⁷−
(Where C₆H₄Is a phenylene group, R²⁷Represents a divalent organic group having 1 to 14 carbon atoms which may have a direct bond or one or more ether bonds or ester bonds. )
Or
-C (O) -R²⁸−
(Where R²⁸Represents a divalent organic group having 1 to 19 carbon atoms which may have a direct bond or one or more ether bonds or ester bonds. )
Is preferred.
[0112]
By converting the terminal halogen of the vinyl polymer, an amino group can be introduced into the terminal of the polymer. Although the substitution method is not particularly limited, a nucleophilic substitution reaction using an amino group-containing compound as a nucleophile is preferable in that the reaction is easily controlled. Examples of such a nucleophilic agent include a compound having both a hydroxyl group and an amino group represented by the general formula (23).
HO-R²⁶-NR¹² ₂(23)
(Where R²⁶Represents a divalent organic group having 1 to 20 carbon atoms which may contain one or more ether bonds or ester bonds. R¹²Is hydrogen or a monovalent organic group having 1 to 20 carbon atoms, and two R¹²May be the same or different from each other, and may be connected to each other at the other end to form a cyclic structure. )
In the above general formula (23), R²⁶Is a divalent organic group having 1 to 20 carbon atoms which may contain one or more ether bonds or ester bonds, such as an alkylene group having 1 to 20 carbon atoms, an arylene group having 6 to 20 carbon atoms, And aralkylene groups of the formulas 7 to 20; Among these compounds having both a hydroxyl group and an amino group, R²⁶But,
-C₆H₄-R²⁷−
(Where C₆H₄Is a phenylene group, R²⁷Represents a divalent organic group having 1 to 14 carbon atoms which may have a direct bond or one or more ether bonds or ester bonds);
-C (O) -R²⁸−
(Where R²⁸Represents a divalent organic group having 1 to 19 carbon atoms which may contain a direct bond or one or more ether bonds or ester bonds).
[0113]
Specific compounds include, for example, ethanolamine; o, m, p-aminophenol; o, m, p-NH₂-C₆H₄-CO₂H: glycine, alanine, aminobutanoic acid and the like.
[0114]
A compound having both an amino group and an oxyanion can be used as the nucleophile. Such a compound is not particularly limited, and examples thereof include a compound represented by the general formula (24).
M⁺O⁻-R²⁶-NR¹² ₂(24)
(Where R²⁶Represents a divalent organic group having 1 to 20 carbon atoms which may contain one or more ether bonds or ester bonds. R¹²Is hydrogen or a monovalent organic group having 1 to 20 carbon atoms, and two R¹²May be the same or different from each other, and may be connected to each other at the other end to form a cyclic structure. M⁺Represents an alkali metal ion or a quaternary ammonium ion. )
In the general formula (24), M⁺Is a counter cation of an oxyanion and represents an alkali metal ion or a quaternary ammonium ion. Examples of the alkali metal ion include a lithium ion, a sodium ion, and a potassium ion, and are preferably a sodium ion or a potassium ion. Examples of the quaternary ammonium ion include a tetramethylammonium ion, a tetraethylammonium ion, a trimethylbenzylammonium ion, a trimethyldodecylammonium ion, a tetrabutylammonium ion, and a dimethylpiperidinium ion.
[0115]
Among the above compounds having both an amino group and an oxyanion, the salts of aminophenols represented by the general formula (25) or the general formula (26) The salts of the amino acids shown are preferred.
M⁺O⁻-C₆H₄-R²⁷-NR¹² ₂(25)
M⁺O⁻-C (O) -R²⁸-NR¹² ₂(26)
(Where C₆H₄Is a phenylene group, R²⁷Is a divalent organic group having 1 to 14 carbon atoms which may contain a direct bond or one or more ether bonds or ester bonds, R²⁸Represents a divalent organic group having 1 to 19 carbon atoms which may have a direct bond or one or more ether bonds or ester bonds. R¹²Is hydrogen or a monovalent organic group having 1 to 20 carbon atoms, and two R¹²May be the same or different from each other, and may be connected to each other at the other end to form a cyclic structure. M⁺Is the same as above. )
The compound having an oxyanion represented by any one of formulas (24) to (26) can be easily obtained by reacting the compound represented by formula (23) with a basic compound.
[0116]
Various compounds can be used as the basic compound. For example, sodium methoxide, potassium methoxide, lithium methoxide, sodium ethoxide, potassium ethoxide, lithium ethoxide, sodium tert-butoxide, potassium tert-butoxide, sodium carbonate, potassium carbonate, lithium carbonate, hydrogen hydrogen carbonate Examples thereof include sodium, sodium hydroxide, potassium hydroxide, sodium hydride, potassium hydride, methyl lithium, ethyl lithium, n-butyl lithium, tert-butyl lithium, lithium diisopropylamide, and lithium hexamethyldisilazide. The amount of the base used is not particularly limited, but is 0.5 to 5 equivalents, preferably 0.8 to 1.2 equivalents, based on the precursor.
[0117]
Examples of the solvent used for reacting the precursor with the base include: hydrocarbon solvents such as benzene and toluene; ether solvents such as diethyl ether and tetrahydrofuran; halogenated hydrocarbon solvents such as methylene chloride and chloroform. Solvents; ketone solvents such as acetone, methyl ethyl ketone and methyl isobutyl ketone; alcohol solvents such as methanol, ethanol, propanol, isopropanol, n-butyl alcohol and tert-butyl alcohol; nitrile solvents such as acetonitrile, propionitrile and benzonitrile Solvents; Ester solvents such as ethyl acetate and butyl acetate; carbonate solvents such as ethylene carbonate and propylene carbonate; amide solvents such as dimethylformamide and dimethylacetamide; dimethyl sulfo Sulfoxide solvents such as Sid the like. These can be used alone or in combination of two or more.
[0118]
M⁺A compound having an oxyanion wherein is a quaternary ammonium ion⁺Is obtained by preparing a compound of which is an alkali metal ion and reacting it with a quaternary ammonium halide. Examples of the quaternary ammonium halide include tetramethylammonium halide, tetraethylammonium halide, trimethylbenzylammonium halide, trimethyldodecylammonium halide, and tetrabutylammonium halide.
[0119]
Various solvents may be used for the substitution reaction of the terminal halogen of the polymer. For example, hydrocarbon solvents such as benzene and toluene; ether solvents such as diethyl ether and tetrahydrofuran; halogenated hydrocarbon solvents such as methylene chloride and chloroform; ketone solvents such as acetone, methyl ethyl ketone and methyl isobutyl ketone; Alcohol solvents such as ethanol, propanol, isopropanol, n-butyl alcohol and tert-butyl alcohol; nitrile solvents such as acetonitrile, propionitrile and benzonitrile; ester solvents such as ethyl acetate and butyl acetate; ethylene carbonate, propylene Carbonate solvents such as carbonate; amide solvents such as dimethylformamide and dimethylacetamide; and sulfoxide solvents such as dimethylsulfoxide. These can be used alone or in combination of two or more.
[0120]
The reaction temperature can be from 0 to 150 ° C. The amount of the amino group-containing compound used is not particularly limited, but is 1 to 5 equivalents, preferably 1 to 1.2 equivalents, based on the terminal halogen of the polymer.
[0121]
To accelerate the nucleophilic substitution reaction, a basic compound may be added to the reaction mixture. Examples of such basic compounds include, in addition to those already exemplified, alkylamines such as trimethylamine, triethylamine and tributylamine; polyamines such as tetramethylethylenediamine and pentamethyldiethylenetriamine; and pyridine compounds such as pyridine and picoline.
[0122]
When the amino group of the amino group-containing compound used in the nucleophilic substitution reaction affects the nucleophilic substitution reaction, it is preferable to protect the amino group-containing compound with an appropriate substituent. Examples of such a substituent include a benzyloxycarbonyl group, a tert-butoxycarbonyl group, and a 9-fluorenylmethoxycarbonyl group.
[0123]
Further, there is a method of substituting a halogen terminal of a vinyl polymer with an azide anion and then reducing the terminal with LAH or the like.
Group having a polymerizable carbon-carbon double bond
The method for introducing a group having a polymerizable carbon-carbon double bond into the polymer (I) of the present invention is not limited, but includes the following methods.
{Circle around (1)} A method in which a halogen group of a vinyl polymer is replaced with a radical polymerizable compound having a carbon-carbon double bond. As a specific example, a method in which a vinyl polymer having a structure represented by the general formula (27) is reacted with a compound represented by the general formula (28).
-CR²⁹R³⁰X (27)
(Where R²⁹, R³⁰Is a group bonded to an ethylenically unsaturated group of a vinyl monomer. X represents chlorine, bromine, or iodine. )
M⁺-OC (O) C (R¹³) = CH₂(28)
(Where R¹³Represents hydrogen or an organic group having 1 to 20 carbon atoms. M⁺Represents an alkali metal or quaternary ammonium ion. )
{Circle around (2)} A method comprising reacting a vinyl polymer having a hydroxyl group with a compound represented by the general formula (29).
XC (O) C (R¹³) = CH₂(29)
(Where R¹³Represents hydrogen or an organic group having 1 to 20 carbon atoms. X represents chlorine, bromine, or a hydroxyl group. )
{Circle around (3)} A method in which a diisocyanate compound is reacted with a vinyl polymer having a hydroxyl group, and the remaining isocyanate group is reacted with the compound represented by formula (30).
HO-R³¹-OC (O) C (R¹³) = CH₂(30)
(Where R¹³Represents hydrogen or an organic group having 1 to 20 carbon atoms. R³¹Represents a divalent organic group having 2 to 20 carbon atoms. )
Hereinafter, each of these methods will be described in detail.
[0124]
The method (1) will be described.
{Circle around (1)} A method comprising reacting a vinyl polymer having a terminal structure represented by the general formula (27) with a compound represented by the general formula (28).
-CR²⁹R³⁰X (27)
(Where R²⁹, R³⁰Is a group bonded to an ethylenically unsaturated group of a vinyl monomer. X represents chlorine, bromine, or iodine. )
M⁺-OC (O) C (R¹³) = CH₂(28)
(Where R¹³Represents hydrogen or an organic group having 1 to 20 carbon atoms. M⁺Represents an alkali metal or quaternary ammonium ion. )
The vinyl polymer having a terminal structure represented by the general formula (27) is obtained by polymerizing a vinyl monomer using the above-mentioned organic halide or a sulfonyl halide compound as an initiator and a transition metal complex as a catalyst, or It is produced by a method of polymerizing a vinyl monomer using a halogen compound as a chain transfer agent, but the former is preferred.
[0125]
The compound represented by the general formula (28) is not particularly limited.¹³As specific examples of, for example, -H, -CH₃, -CH₂CH₃,-(CH₂)_nCH₃(N represents an integer of 2 to 19), -C₆H₅, -CH₂OH, -CN,
And the like, preferably -H, -CH₃It is. M⁺Is a counter cation of the oxyanion, and M⁺Examples of the type include alkali metal ions, specifically, lithium ions, sodium ions, potassium ions, and quaternary ammonium ions. Examples of the quaternary ammonium ion include a tetramethylammonium ion, a tetraethylammonium ion, a tetrabenzylammonium ion, a trimethyldodecylammonium ion, a tetrabutylammonium ion, a dimethylpiperidinium ion and the like, and preferably a sodium ion and a potassium ion. The use amount of the oxyanion of the general formula (28) is preferably 1 to 5 equivalents, more preferably 1.0 to 1.2 equivalents, to the halogen group of the general formula (27). The solvent for carrying out this reaction is not particularly limited, but a polar solvent is preferable because it is a nucleophilic substitution reaction.For example, tetrahydrofuran, dioxane, diethyl ether, acetone, dimethyl sulfoxide, dimethylformamide, dimethylacetamide, hexamethylphosphonic Triamide, acetonitrile, and the like are used. The temperature at which the reaction is carried out is not limited, but is generally from 0 to 150 ° C, preferably from room temperature to 100 ° C in order to retain the polymerizable terminal group.
[0126]
The method (2) will be described.
{Circle around (2)} A method comprising reacting a vinyl polymer having a hydroxyl group with a compound represented by the general formula (29).
XC (O) C (R¹³) = CH₂(29)
(Where R¹³Represents hydrogen or an organic group having 1 to 20 carbon atoms. X represents chlorine, bromine, or a hydroxyl group. )
The compound represented by the general formula (29) is not particularly limited.¹³As specific examples of, for example, -H, -CH₃, -CH₂CH₃,-(CH₂)_nCH₃(N represents an integer of 2 to 19), -C₆H₅, -CH₂OH, -CN,
And the like, preferably -H, -CH₃It is.
[0127]
A vinyl polymer having a hydroxyl group, preferably at the terminal, is a method of polymerizing a vinyl monomer using the above-mentioned organic halide or a sulfonyl halide compound as an initiator, a transition metal complex as a catalyst, or a compound having a hydroxyl group. Is used as a chain transfer agent to polymerize a vinyl monomer, but the former is preferred. The method for producing a vinyl polymer having a hydroxyl group by these methods is not limited, but the following methods are exemplified.
[0128]
(A) When a vinyl polymer is synthesized by living radical polymerization, a compound represented by the following general formula (31) or the like having both a polymerizable alkenyl group and a hydroxyl group in one molecule is reacted as a second monomer. Method.
H₂C = C (R³²) -R³³-R³⁴-OH (31)
(Where R³²Is an organic group having 1 to 20 carbon atoms, preferably hydrogen or methyl group, which may be the same or different. R³³Represents -C (O) O- (ester group) or an o-, m- or p-phenylene group. R³⁴Represents a direct bond or a divalent organic group having 1 to 20 carbon atoms which may have one or more ether bonds. R³³Is an ester group, a (meth) acrylate compound, R³³However, those having a phenylene group are styrene compounds. )
In addition, there is no limitation on the timing of reacting a compound having both a polymerizable alkenyl group and a hydroxyl group in one molecule, but in particular, when rubbery properties are expected, at the end of the polymerization reaction or after the reaction of a predetermined monomer, It is preferred to react as a second monomer.
[0129]
(B) When synthesizing a vinyl polymer by living radical polymerization, at the end of the polymerization reaction or after completion of the reaction of a predetermined monomer, the second monomer has a low polymerizable alkenyl group and a hydroxyl group in one molecule. A method of reacting a compound.
[0130]
Such a compound is not particularly limited, and examples thereof include a compound represented by the general formula (32).
H₂C = C (R³²) -R³⁵-OH (32)
(Where R³²Is the same as described above. R³⁵Represents a divalent organic group having 1 to 20 carbon atoms which may contain one or more ether bonds. )
The compound represented by the general formula (32) is not particularly limited, but alkenyl alcohols such as 10-undecenol, 5-hexenol, and allyl alcohol are preferable because they are easily available.
[0131]
(C) A vinyl resin having at least one carbon-halogen bond represented by the general formula (27) obtained by atom transfer radical polymerization by a method as disclosed in JP-A-4-132706 and the like. A method of introducing a hydroxyl group into a terminal by hydrolyzing or reacting a halogen of a polymer with a hydroxyl group-containing compound.
[0132]
(D) A vinyl polymer having at least one carbon-halogen bond represented by the general formula (27) obtained by atom transfer radical polymerization and having a hydroxyl group represented by the general formula (33) A method of reacting a halogenated carbanion to replace a halogen.
M⁺C⁻(R³⁶) (R³⁷) -R³⁵-OH (33)
(Where R³⁵Is the same as described above. R³⁶And R³⁷Are both Carbanion C⁻Represents one of the above-mentioned electron-withdrawing groups and the other represents hydrogen or an alkyl group having 1 to 10 carbon atoms or a phenyl group. R³⁶And R³⁷As an electron withdrawing group of₂R (ester group), -C (O) R (keto group), -CON (R₂) (Amide group), -COSR (thioester group), -CN (nitrile group), -NO₂(Nitro group) and the like. The substituent R is an alkyl group having 1 to 20 carbon atoms, an aryl group having 6 to 20 carbon atoms or an aralkyl group having 7 to 20 carbon atoms, preferably an alkyl group having 1 to 10 carbon atoms or a phenyl group. R³⁶And R³⁷As -CO₂R, -C (O) R and -CN are particularly preferred. (E) A simple metal or an organometallic compound such as zinc is allowed to act on a vinyl polymer having at least one carbon-halogen bond represented by the general formula (27) obtained by atom transfer radical polymerization. A method in which an enolate anion is prepared and then reacted with an aldehyde or a ketone.
[0133]
(F) A vinyl-containing polymer having at least one halogen at the terminal of the polymer, preferably at least one halogen represented by the general formula (27), and a hydroxyl group-containing oxyanion represented by the following general formula (34) or A method in which a hydroxyl group-containing carboxylate anion represented by Formula (35) or the like is reacted to replace the halogen with a hydroxyl group-containing substituent.
HO-R³⁵-O⁻M⁺(34)
(Where R³⁵And M⁺Is the same as described above. )
HO-R³⁵-C (O) O⁻M⁺(35)
(Where R³⁵And M⁺Is the same as described above. )
In the present invention, when a halogen is not directly involved in the method for introducing a hydroxyl group as in (a) and (b), the method (b) is more preferable because control is easier.
[0134]
When a hydroxyl group is introduced by converting a halogen of a vinyl polymer having at least one carbon-halogen bond as in (c) to (f), the control of (f) The method is more preferred.
[0135]
The method (3) will be described.
(3) A method in which a diisocyanate compound is reacted with a vinyl polymer having a hydroxyl group, and the remaining isocyanate group is reacted with the compound represented by the general formula (36).
HO-R³¹-OC (O) C (R¹³) = CH₂(36)
(Where R¹³Represents hydrogen or an organic group having 1 to 20 carbon atoms. R³¹Represents a divalent organic group having 2 to 20 carbon atoms. )
The compound represented by the general formula (36) is not particularly limited.¹³As specific examples of, for example, -H, -CH₃, -CH₂CH₃,-(CH₂)_nCH₃(N represents an integer of 2 to 19), -C₆H₅, -CH₂OH, -CN,
And the like, preferably -H, -CH₃It is. Specific compounds include 2-hydroxypropyl methacrylate.
[0136]
The vinyl polymer having a hydroxyl group at the terminal is as described above.
[0137]
The diisocyanate compound is not particularly limited, and any conventionally known diisocyanate compounds can be used. Isocyanate compounds such as 1,5-naphthalenediisocyanate, hydrogenated diphenylmethane diisocyanate, hydrogenated toluylene diisocyanate, hydrogenated xylylene diisocyanate, and isophorone diisocyanate. These can be used alone or in combination of two or more. Further, a blocked isocyanate may be used.
[0138]
In order to make better use of weather resistance, it is preferable to use a diisocyanate compound having no aromatic ring, such as hexamethylene diisocyanate and hydrogenated diphenylmethane diisocyanate.
<<< Silica (II) having an average particle diameter of 1 μm or more and 500 μm or less >>>
The silica (II) having an average particle diameter of 1 μm or more and 500 μm or less in the present invention refers to silica having an average particle diameter of 1 μm or more and 500 μm or less as measured by a sieving method. Specifically, the sieving method is to classify powder with a sieve having various openings (micro sieves or the like), and to sieve the sieve through which 50% by weight of the total weight of the powder used for measurement has passed. It is defined by the corresponding value (weight average particle size). In addition, there are cases where the particles having an excessively small particle size cannot be distinguished by this sieving method, and in that case, the measurement is performed using a microscopic method.
[0139]
Generally, silica is divided into synthetic silica and natural silica. Synthetic silica is further produced from a dry process silica (which is further roughly classified into a combustion process and an arc process) in which silica is precipitated by a high-temperature gas phase reaction, and neutralization of an aqueous sodium silicate solution with an acid or an alkali metal salt. The silica is classified into wet silica (which is further classified into a precipitation method and a gel method) in which silica is precipitated by a decomposition reaction, and fused silica which is completely melted and becomes amorphous at a high temperature. On the other hand, examples of natural silica include crystalline silica, silicic anhydride, and hydrous silicic acid.
[0140]
In the curable composition of the present invention, silica (II) having an average particle diameter of 1 μm or more and 500 μm or less is not particularly limited as long as the average particle diameter is 1 μm or more. It is preferable that the thickness be 500 μm or less, since it adversely affects durability and the like. Examples of the silica (II) having an average particle size of 1 μm or more and 500 μm or less include wet-process silica, crystalline silica, fused silica, crystalline silica, and fine powder silica as exemplified below.
[0141]
Examples of the wet-process silica include nip seals SS-10 and SS-20 typified by the Tokusil series (manufactured by Tokuyama) such as Tokusil U, UR, GU, USA, and USG manufactured by the sedimentation method, and the nip seal SS series. Nip seal series (made by Nippon silica) such as Nip seal LP, Nip seal NS-P, Nip seal VN3, Nip seal ER, Nip seal NS-T, Nip seal NS-K, Nip seal NA, Nip seal L300, Nip seal N300A, Nip seal K300, Nip seal G300, etc. Is exemplified. In addition, a thyricia series (manufactured by Fuji Silysia), a nip gel series (manufactured by Nippon Silica), and the like such as thyricia 310, thyricia 250N, thyricia 430, thyricia 770, and thyricia 470 manufactured by gel method are exemplified.
[0142]
Examples of the crystalline silica include crystallite series such as Crystallite CMC-12, Crystallite 5X, and Crystallite A-2, and IMSIL such as IMSIL の A-25, IMSIL A-15, IMSIL 、 A-8, and IMSIL A-10. Series (both made by Tatsumori).
[0143]
As the fused silica, for example, fuses such as Hughe Rex E-1, Hughe Rex E-2, Hughe Rex ZA-30, Hughe Rex RD-8, Hughe Rex RD-120, Hughe Rex MCF-200, Hughe Rex Y-60, etc. Rex series (made by Tatsumori) and the like are exemplified.
[0144]
The dry process silica includes the Aerosil series (produced by Nippon Aerosil) manufactured by the combustion method. However, the silica manufactured by this method easily disperses to near the primary particles due to shearing during compounding. Since a considerable reinforcing effect and a thickening effect are observed, the silica (II) of the present invention is not suitable.
[0145]
The silica in the present invention is not particularly limited, and any of the types described above may be used. If a large amount of water is contained, a side reaction may occur during the curing reaction, and thus it may be preferable to use dry silica. For the same reason, it may be preferable to use silica which has been subjected to a surface treatment and made hydrophobic. As the surface treatment method, a method in which hydrophobic treatment is performed in advance with an organosilicon compound such as organosilane, organosilazane, or diorganopolysiloxane is preferable.
<Use amount of silica (II) having an average particle diameter of 1 μm or more and 500 μm or less>
The amount of silica (II) having an average particle diameter of 1 μm or more and 500 μm or less is not particularly limited, but is preferably 0.1 to 300 parts by weight, and more preferably 0.1 to 300 parts by weight, per 100 parts by weight of the vinyl polymer (I). 5 parts by weight or more and 100 parts by weight or less are more preferable, and 1 part by weight or more and 80 parts by weight or less are further preferable. If the amount is less than 0.1 part by weight, the effect of improving mechanical properties such as the breaking strength of the cured product may not be sufficient, and if it exceeds 300 parts by weight, the workability of the curable composition may be reduced. Or the physical properties of the cured product may be reduced. The silica of the present invention having an average particle diameter of 1 μm or more and 500 μm or less may be used alone or in combination of two or more kinds.
<< Curable composition >>
Some curable compositions of the present invention require a curing catalyst or a curing agent. Further, various compounding agents may be added according to the desired physical properties.
<Curing catalyst / curing agent>
For crosslinkable silyl groups
The polymer having a crosslinkable silyl group is crosslinked and cured by forming a siloxane bond in the presence or absence of various conventionally known condensation catalysts. As the properties of the cured product, a wide range from rubbery to resinous can be prepared according to the molecular weight of the polymer and the main chain skeleton.
[0146]
Examples of such a condensation catalyst include dibutyltin dilaurate, dibutyltin diacetate, dibutyltin diethylhexanolate, dibutyltin dioctate, dibutyltin dimethylmalate, dibutyltin diethylmalate, dibutyltin dibutylmalate, and dibutyltin dibutyltin. Isooctyl malate, dibutyl tin ditridecyl malate, dibutyl tin dibenzyl malate, dibutyl tin maleate, dioctyl tin diacetate, dioctyl tin distearate, dioctyl tin dilaurate, dioctyl tin diethyl malate, dioctyl tin diisooctyl malate, etc. Divalent tin compounds such as tin octylate, tin naphthenate and tin stearate; monobutyltin compounds such as monobutyltin trisoctoate and monobutyltin triisopropoxide; Monoalkyltins such as nooctyltin compounds; titanates such as tetrabutyl titanate and tetrapropyltitanate; organic aluminum compounds such as aluminum trisacetylacetonate, aluminum trisethylacetoacetate, diisopropoxyaluminum ethylacetoacetate; Bismuth carboxylate, iron carboxylate, titanium carboxylate, lead carboxylate, vanadium carboxylate, zirconium carboxylate, calcium carboxylate, potassium carboxylate, barium carboxylate, manganese carboxylate, cerium carboxylate, nickel carboxylate, carboxylic acid Carboxylic acids such as cobalt, zinc carboxylate, aluminum carboxylate (2-ethylhexanoic acid, neodecanoic acid, versatic acid, oleic acid, naphthenic acid, etc.) Genus salts or reactants and mixtures thereof with amine compounds such as laurylamine described below; chelate compounds such as zirconium tetraacetylacetonate and titanium tetraacetylacetonate; methylamine, ethylamine, propylamine, isopropylamine; Aliphatic primary amines such as butylamine, amylamine, hexylamine, octylamine, 2-ethylhexylamine, nonylamine, decylamine, laurylamine, pentadecylamine, cetylamine, stearylamine, cyclohexylamine; dimethylamine, diethylamine, dipropylamine , Diisopropylamine, dibutylamine, diamylamine, dioctylamine, di (2-ethylhexyl) amine, didecylamine, dilaurylamine, dicetylua Aliphatic secondary amines such as amine, distearylamine, methylstearylamine, ethylstearylamine, butylstearylamine; aliphatic tertiary amines such as triamylamine, trihexylamine, trioctylamine; triallylamine, oleylamine , Etc .; aliphatic amines such as lauryl aniline, stearyl aniline, and triphenylamine; and other amines such as monoethanolamine, diethanolamine, triethanolamine, diethylenetriamine, triethylenetetramine, Oleylamine, cyclohexylamine, benzylamine, diethylaminopropylamine, xylylenediamine, ethylenediamine, hexamethylenediamine, triethylenediamine, guanidine, diphene Luguanidine, 2,4,6-tris (dimethylaminomethyl) phenol, morpholine, N-methylmorpholine, 2-ethyl-4-methylimidazole, 1,8-diazabicyclo (5,4,0) undecene-7 (DBU) And the like, or salts of these amine compounds with carboxylic acids and the like; reactants and mixtures of amine compounds and organotin compounds such as reactants or mixtures of laurylamine and tin octylate; Low molecular weight polyamide resin obtained from polyamine and polybasic acid; reaction product of excess polyamine and epoxy compound; γ-aminopropyltrimethoxysilane, γ-aminopropyltriethoxysilane, γ-aminopropyltriisopropoxysilane , Γ-aminopropylmethyldimethoxysilane, γ-aminopro N- (β-aminoethyl) aminopropyltrimethoxysilane, N- (β-aminoethyl) aminopropylmethyldimethoxysilane, N- (β-aminoethyl) aminopropyltriethoxysilane, N- (Β-aminoethyl) aminopropylmethyldiethoxysilane, N- (β-aminoethyl) aminopropyltriisopropoxysilane, γ-ureidopropyltrimethoxysilane, N-phenyl-γ-aminopropyltrimethoxysilane, N- Benzyl-γ-aminopropyltrimethoxysilane, N-vinylbenzyl-γ-aminopropyltriethoxysilane and the like can be mentioned. Silanol condensation of amino-modified silyl polymers, silylated amino polymers, unsaturated amino silane complexes, phenylamino long-chain alkyl silanes, silane coupling agents having amino groups such as amino silylated silicones, and derivatives thereof which are modified derivatives thereof. Examples of the catalyst include known silanol condensation catalysts such as other acidic catalysts and basic catalysts.
[0147]
These catalysts may be used alone or in combination of two or more. The amount of the condensation catalyst is preferably about 0.1 to 20 parts, more preferably 1 to 10 parts based on 100 parts (parts by weight, the same applies hereinafter) of the vinyl polymer having at least one crosslinkable silyl group. . If the amount of the silanol condensation catalyst falls below this range, the curing rate may be slow, and the curing reaction may not be sufficiently advanced. On the other hand, if the amount of the silanol condensation catalyst exceeds this range, local heat generation or foaming occurs during curing, and it becomes difficult to obtain a good cured product, and the pot life becomes too short, which is preferable from the viewpoint of workability. Absent. Although not particularly limited, it is preferable to use a tin-based curing catalyst to control the curability.
[0148]
In the curable composition of the present invention, in order to further enhance the activity of the condensation catalyst, it is possible to use the above-mentioned silane coupling agent having an amino group as a cocatalyst, similarly to the amine compound. . The amino group-containing silane coupling agent is a compound having a group containing a silicon atom to which a hydrolyzable group is bonded (hereinafter referred to as a hydrolyzable silicon group) and an amino group. Although a methoxy group, an ethoxy group and the like are preferable from the viewpoint of the hydrolysis rate. The number of hydrolyzable groups is preferably 2 or more, particularly preferably 3 or more.
[0149]
The amount of the amine compound is preferably about 0.01 to 50 parts by weight, more preferably 0.1 to 20 parts by weight, based on 100 parts by weight of the organic polymer of the vinyl polymer (I). If the compounding amount of the amine compound is less than 0.01 part by weight, the curing speed may be slow, and the curing reaction may not be sufficiently advanced. On the other hand, if the amount of the amine compound exceeds 30 parts by weight, the pot life may be too short, which is not preferable from the viewpoint of workability.
[0150]
These amine compounds may be used alone or in combination of two or more.
[0151]
Further, the following general formula (37)
R⁴⁹ _aSi (OR⁵⁰)_4-a(37)
(Where R⁴⁹And R⁵⁰Is each independently a substituted or unsubstituted hydrocarbon group having 1 to 20 carbon atoms. A is 0, 1, 2, or 3. ), A silicon compound having no amino group or silanol group may be added as a co-catalyst.
[0152]
Examples of the silicon compound include, but are not limited to, R in the general formula (37) such as phenyltrimethoxysilane, phenylmethyldimethoxysilane, phenyldimethylmethoxysilane, diphenyldimethoxysilane, diphenyldiethoxysilane, and triphenylmethoxysilane.⁴⁹Is preferably an aryl group having 6 to 20 carbon atoms because the effect of accelerating the curing reaction of the composition is large. In particular, diphenyldimethoxysilane and diphenyldiethoxysilane are most preferable because they are low in cost and easily available.
[0153]
The amount of the silicon compound is preferably about 0.01 to 20 parts, more preferably 0.1 to 10 parts, per 100 parts of the vinyl polymer. If the amount of the silicon compound falls below this range, the effect of accelerating the curing reaction may be reduced. On the other hand, if the amount of the silicon compound exceeds this range, the hardness and tensile strength of the cured product may decrease.
[0154]
The type and amount of the curing catalyst / curing agent can be selected depending on the type of Y and the number of a in the vinyl polymer represented by the general formulas (1) and (6) of the present invention. The curability and mechanical properties of the present invention can be controlled according to the purpose and application. When Y is an alkoxy group, the smaller the number of carbon atoms, the higher the reactivity, and the larger the number of a, the higher the reactivity.
For alkenyl groups
When the crosslinking is carried out using an alkenyl group, the crosslinking is preferably carried out by a hydrosilylation reaction using a hydrosilylation catalyst using a hydrosilyl group-containing compound as a curing agent.
[0155]
The hydrosilyl group-containing compound is not particularly limited as long as it can be cured by crosslinking with a polymer having an alkenyl group, and various compounds can be used. For example, a linear polysiloxane represented by the general formula (38) or (39);
R⁵¹ ₃SiO- [Si (R⁵¹)₂O]_a-[Si (H) (R⁵²) O]_b− [Si (R⁵²) (R⁵³) O]_c-SiR⁵¹ ₃(38)
HR⁵¹ ₂SiO- [Si (R⁵¹)₂O]_a-[Si (H) (R⁵²) O]_b− [Si (R⁵²) (R⁵³) O]_c-SiR⁵¹ ₂H (39)
(Where R⁵¹And R⁵²Is an alkyl group having 1 to 6 carbon atoms or a phenyl group, R⁵³Represents an alkyl group having 1 to 10 carbon atoms or an aralkyl group. a represents an integer satisfying 0 ≦ a ≦ 100, b represents an integer satisfying 2 ≦ b ≦ 100, and c represents an integer satisfying 0 ≦ c ≦ 100. )
A cyclic siloxane represented by the general formula (40);
[0156]
Embedded image

(Where R⁵⁴And R⁵⁵Is an alkyl group having 1 to 6 carbon atoms or a phenyl group, R⁵⁶Represents an alkyl group having 1 to 10 carbon atoms or an aralkyl group. d represents an integer of 0 ≦ d ≦ 8, e represents an integer of 2 ≦ e ≦ 10, f represents an integer of 0 ≦ f ≦ 8, and satisfies 3 ≦ d + e + f ≦ 10. )
And the like.
[0157]
These may be used alone or in combination of two or more. Among these siloxanes, from the viewpoint of compatibility with the (meth) acrylic polymer, chain siloxanes having a phenyl group represented by the following general formulas (41) and (42), and the general formulas (43) and (43) The cyclic siloxane represented by 44) is preferred.
(CH₃)₃SiO- [Si (H) (CH₃) O]_g− [Si (C₆H₅)₂O]_h-Si (CH₃)₃(41)
(CH₃)₃SiO- [Si (H) (CH₃) O]_g-[Si (CH₃) ｛CH₂C (H) (R⁵⁷) C₆H₅｝ O]_h-Si (CH₃)₃(42)
(Where R⁵⁷Represents hydrogen or a methyl group. g represents an integer of 2 ≦ g ≦ 100, and h represents an integer of 0 ≦ h ≦ 100. C₆H₅Represents a phenyl group. )
[0158]
Embedded image

(Where R⁵⁷Represents hydrogen or a methyl group. i is an integer satisfying 2 ≦ i ≦ 10, j is an integer satisfying 0 ≦ j ≦ 8, and 3 ≦ i + j ≦ 10. C₆H₅Represents a phenyl group. ) As the hydrosilyl group-containing compound, a low molecular weight compound having two or more alkenyl groups in the molecule may further include a hydrosilyl group-containing compound represented by any of general formulas (38) to (44) even after the reaction. A compound obtained by performing an addition reaction so that the hydrosilyl group remains may also be used. Various compounds can be used as the compound having two or more alkenyl groups in the molecule. For example, hydrocarbon compounds such as 1,4-pentadiene, 1,5-hexadiene, 1,6-heptadiene, 1,7-octadiene, 1,8-nonadiene and 1,9-decadiene, O, O Ether compounds such as' -diallylbisphenol A and 3,3'-diallylbisphenol A, ester compounds such as diallyl phthalate, diallyl isophthalate, triallyl trimellitate and tetraallyl pyromellitate, carbonates such as diethylene glycol diallyl carbonate System compounds.
[0159]
The above alkenyl group-containing compound can be obtained by slowly dropping the above-mentioned alkenyl group-containing compound in the presence of a hydrosilylation catalyst to an excess amount of the hydrosilyl group-containing compound represented by the general formulas (38) to (44). it can. Among these compounds, the following compounds are preferable in consideration of the availability of raw materials, the ease of removing excess siloxane, and the compatibility with the vinyl polymer (I).
[0160]
Embedded image

The polymer and the curing agent can be mixed at an arbitrary ratio, but from the viewpoint of curability, the molar ratio of the alkenyl group to the hydrosilyl group is preferably in the range of 5 to 0.2, and more preferably 2.5 to 0.2. It is particularly preferred that the value be 0.4. When the molar ratio is 5 or more, only a cured product with insufficient strength and stickiness is obtained, and when it is less than 0.2, a large amount of active hydrosilyl groups remains in the cured product even after curing. , Cracks and voids occur, and a uniform and strong cured product cannot be obtained.
[0161]
The curing reaction between the polymer and the curing agent proceeds by mixing and heating the two components, but a hydrosilylation catalyst can be added to accelerate the reaction more quickly. Such a hydrosilylation catalyst is not particularly limited, and examples thereof include a radical initiator such as an organic peroxide and an azo compound, and a transition metal catalyst.
[0162]
The radical initiator is not particularly limited, and for example, di-t-butyl peroxide, 2,5-dimethyl-2,5-di (t-butylperoxy) hexane, 2,5-dimethyl-2,5-di ( t-butylperoxy) -3-hexyne, dicumyl peroxide, t-butylcumyl peroxide, dialkyl peroxides such as α, α′-bis (t-butylperoxy) isopropylbenzene, benzoyl peroxide, p-chlorobenzoyl peroxide, m-chlorobenzoyl peroxide, 2,4-dichlorobenzoyl peroxide, diacyl peroxides such as lauroyl peroxide, peresters such as t-butyl perbenzoate, diisopropyl percarbonate, di-2-ethylhexyl percarbonate. Such as peroxydicarbonate, 1,1 And peroxyketals such as -di (t-butylperoxy) cyclohexane and 1,1-di (t-butylperoxy) -3,3,5-trimethylcyclohexane.
[0163]
Further, the transition metal catalyst is not particularly limited, for example, platinum alone, alumina, silica, a dispersion of platinum solids on a carrier such as carbon black, chloroplatinic acid, chloroplatinic acid and alcohol, aldehyde, ketone and the like , A platinum-olefin complex, and a platinum (0) -divinyltetramethyldisiloxane complex. Examples of catalysts other than platinum compounds include RhCl (PPh₃)₃, RhCl₃, RuCl₃, IrCl₃, FeCl₃, AlCl₃, PdCl₂・ H₂O, NiCl₂, TiCl₄And the like. These catalysts may be used alone or in combination of two or more. The amount of the catalyst is not particularly limited, but may be 10 to 1 mol of the alkenyl group of the vinyl polymer (I).^-1-10^-8mol in the range of 10 mol, preferably 10 mol.^-3-10^-6It is good to use in the range of mol. 10^-8If it is less than 10 mol, curing will not proceed sufficiently. Also, since hydrosilylation catalysts are expensive,^-1It is preferable not to use more than mol.
[0164]
Although the curing temperature is not particularly limited, it is generally preferable to cure at 0 ° C to 200 ° C, preferably 30 ° C to 150 ° C, and more preferably 80 ° C to 150 ° C.
For hydroxyl group
The polymer having a hydroxyl group of the present invention is uniformly cured by using a compound having two or more functional groups capable of reacting with a hydroxyl group as a curing agent. Specific examples of the curing agent include, for example, a polyvalent isocyanate compound having two or more isocyanate groups in one molecule, an aminoplast resin such as a methylolated melamine and an alkyl etherified product or a low condensed product thereof, a polyfunctional carboxylic acid and And halides thereof. When preparing a cured product using these curing agents, an appropriate curing catalyst can be used.
In the case of amino group
The polymer having an amino group of the present invention is uniformly cured by using a compound having two or more functional groups capable of reacting with the amino group as a curing agent. Specific examples of the curing agent include, for example, a polyvalent isocyanate compound having two or more isocyanate groups in one molecule, an aminoplast resin such as a methylolated melamine and an alkyl etherified product or a low condensed product thereof, a polyfunctional carboxylic acid and And halides thereof. When preparing a cured product using these curing agents, an appropriate curing catalyst can be used.
For epoxy group
The curing agent for the polymer having an epoxy group of the present invention is not particularly limited. For example, aliphatic amines, alicyclic amines, aromatic amines; acid anhydrides; polyamides; imidazoles; amine imides; Melamine and its derivatives; salts of polyamines; phenolic resins; polymercaptans, polysulfides; and light / ultraviolet curing agents such as aromatic diazonium salts, diallyliodonium salts, triallylsulfonium salts, triallylselenium salts and the like.
In the case of a polymerizable carbon-carbon double bond
A polymer having a polymerizable carbon-carbon double bond can be crosslinked by a polymerization reaction of the polymerizable carbon-carbon double bond.
[0165]
Examples of the method of crosslinking include a method of curing with active energy rays and a method of curing with heat. In the active energy ray-curable composition, the photopolymerization initiator is preferably a photoradical initiator or a photoanion initiator. In the thermosetting composition, the thermal polymerization initiator is preferably selected from the group consisting of an azo initiator, a peroxide, a persulfate, and a redox initiator.
[0166]
Hereinafter, these crosslinking reactions will be described in detail.
[0167]
When a polymer having a polymerizable carbon-carbon double bond is crosslinked, a polymerizable monomer and / or oligomer and various additives may be used in combination depending on the purpose. As the polymerizable monomer and / or oligomer, a monomer and / or oligomer having a radical polymerizable group or a monomer and / or oligomer having an anion polymerizable group is preferable. Examples of the radical polymerizable group include an acrylic functional group such as a (meth) acryl group, a styrene group, an acrylonitrile group, a vinyl ester group, an N-vinylpyrrolidone group, an acrylamide group, a conjugated diene group, a vinyl ketone group, and a vinyl chloride group. Is mentioned. Among them, those having a (meth) acryl group similar to the polymer of the present invention are preferable. Examples of the anionic polymerizable group include a (meth) acryl group, a styrene group, an acrylonitrile group, an N-vinylpyrrolidone group, an acrylamide group, a conjugated diene group, and a vinyl ketone group. Among them, those having an acrylic functional group are preferred.
[0168]
Specific examples of the above monomers include (meth) acrylate monomers, cyclic acrylates, N-vinylpyrrolidone, styrene monomers, acrylonitrile, N-vinylpyrrolidone, acrylamide monomers, conjugated diene monomers, vinyl ketone monomers and the like. Can be Examples of the (meth) acrylate-based monomer include n-butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, isooctyl (meth) acrylate, isononyl (meth) acrylate, and compounds of the following formulas. it can.
[0169]
Embedded image

[0170]
Embedded image

[0171]
Embedded image

[0172]
Embedded image

[0173]
Embedded image

Styrene-based monomers include styrene, α-methylstyrene, etc., acrylamide-based monomers include acrylamide, N, N-dimethylacrylamide, etc., conjugated diene-based monomers include butadiene and isoprene, and vinylketone-based monomers include methylvinylketone. And the like.
[0174]
Examples of polyfunctional monomers include neopentyl glycol polypropoxy diacrylate, trimethylolpropane polyethoxy triacrylate, bisphenol F polyethoxy diacrylate, bisphenol A polyethoxy diacrylate, dipentaerythritol polyhexanolide hexaacrylate, tris (hydroxy Ethyl) isocyanurate polyhexanolide triacrylate, tricyclodecane dimethylol diacrylate 2- (2-acryloyloxy-1,1-dimethyl) -5-ethyl-5-acryloyloxymethyl-1,3-dioxane, tetra Bromobisphenol A diethoxy diacrylate, 4,4-dimercaptodiphenyl sulfide dimethacrylate, polytetraethylene glycol diacrylate, 1,9 Nonanediol diacrylate, and ditrimethylolpropane tetraacrylate.
[0175]
Examples of the oligomer include an epoxy acrylate resin such as a bisphenol A type epoxy acrylate resin, a phenol novolak type epoxy acrylate resin, a cresol novolak type epoxy acrylate resin, a COOH group-modified epoxy acrylate resin, a polyol (polytetramethylene glycol, ethylene glycol and adipine). Acid polyester diol, ε-caprolactone modified polyester diol, polypropylene glycol, polyethylene glycol, polycarbonate diol, hydroxyl-terminated hydrogenated polyisoprene, hydroxyl-terminated polybutadiene, hydroxyl-terminated polyisobutylene, etc.) and organic isocyanates (tolylene diisocyanate, isophorone diisocyanate, diphenylmethane) Diisocyanate, hexamethylene diisocyanate (Meth) acrylates such as hydroxyethyl (meth) acrylate, hydroxypropyl (meth) acrylate, hydroxybutyl (meth) acrylate, pentaerythritol triacrylate, etc. Examples thereof include a urethane acrylate resin obtained by the above, a resin in which a (meth) acryl group is introduced into the above polyol via an ester bond, and a polyester acrylate resin.
[0176]
These monomers and oligomers are selected according to the initiator and curing conditions used.
[0177]
Further, the number average molecular weight of the monomer and / or oligomer having an acrylic functional group is preferably 2,000 or less, and more preferably 1,000 or less, because the compatibility is good.
[0178]
As a method for crosslinking a polymer having a polymerizable carbon-carbon double bond, it is preferable to use an active energy ray such as UV or an electron beam.
[0179]
In the case of crosslinking by active energy rays, it is preferable to contain a photopolymerization initiator.
[0180]
The photopolymerization initiator used in the present invention is not particularly limited, but a photoradical initiator and a photoanion initiator are preferable, and a photoradical initiator is particularly preferable. For example, acetophenone, propiophenone, benzophenone, xanthol, fluorenone, benzaldehyde, anthraquinone, triphenylamine, carbazole, 3-methylacetophenone, 4-methylacetophenone, 3-pentylacetophenone, 4-methoxyacetophenone, 3-bromoacetophenone , 4-allylacetophenone, p-diacetylbenzene, 3-methoxybenzophenone, 4-methylbenzophenone, 4-chlorobenzophenone, 4,4'-dimethoxybenzophenone, 4-chloro-4'-benzylbenzophenone, 3-chloroxantone, 3,9-dichloroxanthone, 3-chloro-8-nonylxanthone, benzoyl, benzoin methyl ether, benzoin butyl ether, bis (4-dimethyl Minofeniru) ketone, benzyl methoxy ketal, 2-chlorothioxanthone tone, and the like. These initiators may be used alone or in combination with other compounds. Specific examples include a combination with an amine such as diethanolmethylamine, dimethylethanolamine, and triethanolamine, further combined with an iodonium salt such as diphenyliodonium chloride, and a combination with a dye and an amine such as methylene blue. Can be
[0181]
Further, as a near-infrared light polymerization initiator, a near-infrared light absorbing cationic dye may be used. As the near-infrared light-absorbing cationic dye, for example, a near-infrared light-absorbing cationic dye which is excited by light energy in a range of 650 to 1500 nm, which is disclosed in JP-A-3-111402, JP-A-5-194619, etc. It is preferable to use a cationic cation dye-borate anion complex, and it is more preferable to use a boron sensitizer in combination.
[0182]
The amount of the photopolymerization initiator to be added is not particularly limited since it is only necessary to slightly functionalize the system, but is preferably 0.001 to 10 parts by weight based on 100 parts of the polymer of the composition.
[0183]
The method of curing the active energy ray-curable composition of the present invention is not particularly limited, but depending on the properties of the photopolymerization initiator, a high-pressure mercury lamp, a low-pressure mercury lamp, an electron beam irradiation device, a halogen lamp, a light-emitting diode, Irradiation of light and an electron beam by a semiconductor laser or the like can be given.
[0184]
As a method for crosslinking a polymer having a polymerizable carbon-carbon double bond, heat is preferably used.
[0185]
When crosslinking by active energy rays, it is preferable to contain a thermal polymerization initiator.
[0186]
The thermal polymerization initiator used in the present invention is not particularly limited, but includes an azo initiator, a peroxide, a persulfate, and a redox initiator.
[0187]
Suitable azo initiators include, but are not limited to, 2,2'-azobis (4-methoxy-2,4-dimethylvaleronitrile) (VAZO @ 33), 2,2'-azobis (2- Amidinopropane) dihydrochloride (VAZO @ 50), 2,2'-azobis (2,4-dimethylvaleronitrile) (VAZO @ 52), 2,2'-azobis (isobutyronitrile) (VAZO @ 64), 2, 2′-azobis-2-methylbutyronitrile (VAZOＺ67), 1,1-azobis (1-cyclohexanecarbonitrile) (VAZO 88) (all available from DuPont Chemical), 2,2′-azobis (2- Cyclopropylpropionitrile) and 2,2'-azobis (methylisobutyrate) (V-601) (available from Wako Pure Chemical Industries, Ltd.) ), And the like.
[0188]
Suitable peroxide initiators include, but are not limited to, benzoyl peroxide, acetyl peroxide, lauroyl peroxide, decanoyl peroxide, dicetyl peroxydicarbonate, di (4-t-butylcyclohexyl) Peroxydicarbonate (Perkadox @ 16S) (available from Akzo Nobel), di (2-ethylhexyl) peroxydicarbonate, t-butylperoxypivalate (Luppersol @ 11) (available from Elf Atochem), t-butylper Oxy-2-ethylhexanoate (Trigonox 21-C50) (available from Akzo Nobel), and dicumyl peroxide.
[0189]
Suitable persulfate initiators include, but are not limited to, potassium persulfate, sodium persulfate, and ammonium persulfate.
[0190]
Suitable redox (redox) initiators include, but are not limited to, combinations of the above persulfate initiators with reducing agents such as sodium metabisulfite and sodium bisulfite; Examples include systems based on tertiary amines, such as systems based on benzoyl peroxide and dimethylaniline; and systems based on organic hydroperoxides and transition metals, such as systems based on cumene hydroperoxide and cobalt naphthate.
[0191]
Other initiators include, but are not limited to, pinacols such as tetraphenyl 1,1,2,2-ethanediol.
[0192]
Preferred thermal radical initiators are selected from the group consisting of azo initiators and peroxide initiators. Even more preferred are 2,2'-azobis (methylisobutyrate), t-butylperoxypivalate, and di (4-t-butylcyclohexyl) peroxydicarbonate, and mixtures thereof.
[0193]
The thermal initiator used in the present invention is present in a catalytically effective amount, and such an amount is not limited, but typically includes a poly (acrylic) functional group having at least one terminal acrylic functional group. It is about 0.01 to 5 parts by weight, more preferably about 0.025 to 2 parts by weight, based on 100 parts by weight of the total amount of the monomer and oligomer mixture added and combined. If a mixture of initiators is used, the total amount of the mixture of initiators is as if only one initiator was used.
[0194]
The method for curing the thermosetting composition of the present invention is not particularly limited, and the temperature varies depending on the type of the thermal initiator, the polymer (I), the compound to be added, and the like. C. is preferable, and more preferably 70C to 200C. The curing time varies depending on the used polymerization initiator, monomer, solvent, reaction temperature and the like, but is usually in the range of 1 minute to 10 hours.
<Adhesiveness imparting agent>
A silane coupling agent or an adhesion-imparting agent other than the silane coupling agent can be added to the composition of the present invention. When the adhesion imparting agent is added, the joint width or the like fluctuates due to an external force, so that the risk of the sealing material peeling off from the adherend such as a siding board can be further reduced. In some cases, the necessity of using a primer used for improving the adhesiveness is eliminated, and simplification of the construction work is expected. Specific examples of silane coupling agents include silane coupling agents having functional groups such as amino groups, mercapto groups, epoxy groups, carboxyl groups, vinyl groups, isocyanate groups, isocyanurates, and halogens, and specific examples thereof. Isocyanate group-containing silanes such as γ-isocyanatopropyltrimethoxysilane, γ-isocyanatopropyltriethoxysilane, γ-isocyanatopropylmethyldiethoxysilane, γ-isocyanatopropylmethyldimethoxysilane; and γ-aminopropyltrimethoxysilane Γ-aminopropyltriethoxysilane, γ-aminopropyltriisopropoxysilane, γ-aminopropylmethyldimethoxysilane, γ-aminopropylmethyldiethoxysilane, γ- (2-aminoethyl) amino Propyl trimethoxysilane, γ- (2-aminoethyl) aminopropylmethyldimethoxysilane, γ- (2-aminoethyl) aminopropyltriethoxysilane, γ- (2-aminoethyl) aminopropylmethyldiethoxysilane, γ -(2-aminoethyl) aminopropyltriisopropoxysilane, γ-ureidopropyltrimethoxysilane, N-phenyl-γ-aminopropyltrimethoxysilane, N-benzyl-γ-aminopropyltrimethoxysilane, N-vinylbenzyl Amino-containing silanes such as -γ-aminopropyltriethoxysilane; γ-mercaptopropyltrimethoxysilane, γ-mercaptopropyltriethoxysilane, γ-mercaptopropylmethyldimethoxysilane, γ-mercaptopropylmethyldiethoxysilane, etc. Mercapto group-containing silanes; γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropyltriethoxysilane, γ-glycidoxypropylmethyldimethoxysilane, β- (3,4-epoxycyclohexyl) ethyltrimethoxy Epoxy group-containing silanes such as silane and β- (3,4-epoxycyclohexyl) ethyltriethoxysilane; β-carboxyethyltriethoxysilane, β-carboxyethylphenylbis (2-methoxyethoxy) silane, N-β- Carboxysilanes such as (carboxymethyl) aminoethyl-γ-aminopropyltrimethoxysilane; vinyltrimethoxysilane, vinyltriethoxysilane, γ-methacryloyloxypropylmethyldimethoxysilane, γ-acroyloxypropylmethyltriet Silanes containing a vinyl-type unsaturated group such as xysilane; silanes containing a halogen such as γ-chloropropyltrimethoxysilane; and isocyanurate silanes such as tris (trimethoxysilyl) isocyanurate. Amino-modified silyl polymers, silylated amino polymers, unsaturated amino silane complexes, phenylamino long-chain alkyl silanes, amino silylated silicones, blocked isocyanate silanes, silylated polyesters, and the like, which are derivatives of these modified compounds, are also used as silane coupling agents. Can be used.
[0195]
The silane coupling agent used in the present invention is usually used in an amount of 0.1 to 20 parts based on 100 parts of the crosslinkable silyl group-containing vinyl polymer. In particular, it is preferable to use in the range of 0.5 to 10 parts. The effect of the silane coupling agent to be added to the curable composition of the present invention is various adherends, that is, glass, aluminum, stainless steel, zinc, copper, an inorganic base such as mortar, PVC, acrylic, polyester, When used for organic substrates such as polyethylene, polypropylene, and polycarbonate, they exhibit a remarkable effect of improving adhesion under non-primer conditions or primer treatment conditions. When used under non-primer conditions, the effect of improving the adhesion to various adherends is particularly significant.
[0196]
Specific examples other than the silane coupling agent are not particularly limited, and include, for example, epoxy resins, phenol resins, sulfur, alkyl titanates, aromatic polyisocyanates, and the like.
[0197]
The above-mentioned adhesiveness-imparting agent may be used alone or in combination of two or more. The addition of these adhesion-imparting agents can improve the adhesion to the adherend. Although not particularly limited, 0.1 to 20 parts by weight of a silane coupling agent among the above-mentioned adhesiveness-imparting agents is used in combination, in order to improve the adhesiveness, particularly to the metal-coated surface such as an oil pan. Is preferred.
[0198]
The type and amount of the adhesion-imparting agent can be selected according to the type of Y and the number of a in the vinyl polymer represented by the general formulas (1) and (6) of the present invention. The curability, mechanical properties, and the like of the present invention can be controlled depending on the application. Care must be taken in the selection, especially since it affects the curability and elongation.
<Plasticizer>
Various plasticizers may be used in the curable composition of the present invention as needed. When a plasticizer is used in combination with a filler described later, the elongation of the cured product can be increased, and a large amount of the filler can be mixed, which is more advantageous, but it is not always necessary to add the plasticizer. The plasticizer is not particularly limited. For example, phthalic acid esters such as dibutyl phthalate, diheptyl phthalate, di (2-ethylhexyl) phthalate, and butyl benzyl phthalate; for the purpose of adjusting physical properties, adjusting properties, and the like; dioctyl adipate , Dioctyl sebacate, dibutyl sebacate, non-aromatic dibasic acid esters such as isodecyl succinate; aliphatic esters such as butyl oleate and methyl acetyl ricinoleate; diethylene glycol dibenzoate, triethylene glycol dibenzoate, pentane Esters of polyalkylene glycol such as erythritol ester; phosphates such as tricresyl phosphate and tributyl phosphate; trimellitate; polystyrene and poly-α-methylstyrene Polybutadiene, polybutene, polyisobutylene, butadiene-acrylonitrile, polychloroprene; chlorinated paraffins; hydrocarbon-based oils such as alkyldiphenyl, partially hydrogenated terphenyl, etc .; process oils; polyethylene glycol, polypropylene glycol, poly Polyether polyols such as tetramethylene glycol and derivatives thereof in which hydroxyl groups of these polyether polyols are converted to ester groups, ether groups, etc .; epoxy plasticizers such as epoxidized soybean oil and benzyl epoxystearate; sebacic acid , Adipic acid, azelaic acid, phthalic acid and other dibasic acids and ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, etc. Polyester plasticizers obtained from coal; vinyl polymers obtained by polymerizing vinyl monomers such as acrylic plasticizers by various methods; and the like.
[0199]
Among them, a polymer plasticizer, which is a polymer having a number average molecular weight of 500 to 15,000, is added, and the viscosity and slump property of the curable composition and the tensile strength of the cured product obtained by curing the composition, The mechanical properties such as elongation can be adjusted, and the initial physical properties are maintained for a long time as compared with the case where a low molecular weight plasticizer which is a plasticizer containing no polymer component in the molecule is used, and the alkyd Drying properties (also referred to as paintability) when a paint is applied can be improved. Although not limited, the polymer plasticizer may or may not have a functional group.
[0200]
Although the number average molecular weight of the high molecular weight plasticizer is described as 500 to 15000, it is preferably 800 to 10000, and more preferably 1000 to 8000. If the molecular weight is too low, the plasticizer flows out over time due to heat or rainfall, so that the initial physical properties cannot be maintained for a long time, and the alkyd coating property may not be improved. On the other hand, if the molecular weight is too high, the viscosity increases, and the workability deteriorates.
[0201]
Among these polymer plasticizers, those compatible with the vinyl polymer are preferable. Among them, vinyl polymers are preferred from the viewpoint of compatibility, weather resistance and heat resistance. Among the vinyl polymers, a (meth) acrylic polymer is preferable, and an acrylic polymer is more preferable. Examples of the method for synthesizing the acrylic polymer include those obtained by conventional solution polymerization, and solventless acrylic polymers. The latter acrylic plasticizer is produced by a high-temperature continuous polymerization method (US Pat. No. 4,414,370, JP-A-59-6207, Japanese Patent Publication No. 5-58005, JP-A-1-313522, US Pat. No. 5,010,166) without using a solvent or a chain transfer agent. More preferred for the purposes of the present invention. Examples thereof include, but are not particularly limited to, Toagosei product UP series and the like (see Industrial Materials, October 1999). Of course, a living radical polymerization method can also be mentioned as another synthesis method. This method is preferable because the molecular weight distribution of the polymer is narrow and the viscosity can be reduced. Further, the atom transfer radical polymerization method is more preferable, but not limited thereto.
[0202]
The molecular weight distribution of the polymer plasticizer is not particularly limited, but is preferably narrow, and is preferably less than 1.8. It is more preferably 1.7 or less, still more preferably 1.6 or less, further preferably 1.5 or less, particularly preferably 1.4 or less, and most preferably 1.3 or less.
[0203]
The plasticizers including the above-mentioned polymer plasticizers may be used alone or in combination of two or more, but are not necessarily required. If necessary, a high-molecular plasticizer may be used, and a low-molecular plasticizer may be further used in a range that does not adversely affect the physical properties.
[0204]
In addition, these plasticizers can be blended at the time of polymer production.
[0205]
The amount of the plasticizer used is not limited, but is 5 to 150 parts by weight, preferably 10 to 120 parts by weight, and more preferably 20 to 100 parts by weight based on 100 parts by weight of the vinyl polymer. If it is less than 5 parts by weight, the effect as a plasticizer will not be exhibited, and if it exceeds 150 parts by weight, the cured product will have insufficient mechanical strength.
<Filling material>
In the curable composition of the present invention, various fillers may be used as necessary to such an extent that the effect of the silica (II) having an average particle diameter of 1 μm or more and 500 μm or less of the present invention is not hindered. Examples of the filler include, but are not particularly limited to, wood powder, pulp, cotton chips, asbestos, glass fiber, carbon fiber, mica, walnut shell powder, rice hull powder, graphite, diatomaceous earth, clay, silica (fumed silica, sediment Silica, crystalline silica, fused silica, dolomite, silicic anhydride, hydrous silicic acid, etc.), reinforcing fillers such as carbon black; heavy calcium carbonate, colloidal calcium carbonate, magnesium carbonate, diatomaceous earth, calcined clay, Fillers such as clay, talc, titanium oxide, bentonite, organic bentonite, ferric oxide, red iron oxide, aluminum fine powder, flint powder, zinc oxide, activated zinc white, zinc dust, zinc carbonate, shirasu balloon and the like; asbestos, Glass fiber and glass filament, carbon fiber, Kevlar fiber, polyethylene fiber Include fibrous fillers such as is.
[0206]
Among these fillers, precipitated silica, fumed silica, crystalline silica, fused silica, dolomite, carbon black, calcium carbonate, titanium oxide, talc and the like are preferable.
[0207]
In particular, when it is desired to obtain a high-strength cured product with these fillers, mainly fumed silica, precipitated silica, silicic anhydride, hydrous silicic acid, carbon black, surface-treated fine calcium carbonate, crystalline silica, fused silica A filler selected from silica, calcined clay, clay and activated zinc white can be added. Above all, the specific surface area (by BET adsorption method) is 50m²/ G or more, usually 50 to 400 m²/ G, preferably 100-300 m²/ G of ultrafine powdered silica is preferred. Further, silica whose surface is subjected to hydrophobic treatment in advance with an organosilicon compound such as organosilane, organosilazane, or diorganopolysiloxane is more preferable.
[0208]
More specific examples of the silica-based filler having a high reinforcing property include, but are not particularly limited to, Aerosil manufactured by Nippon Aerosil Co., Ltd., which is one of the fumed silicas, and one of the precipitated silicas. Nipsil manufactured by Nippon Silica Co., Ltd., and the like. In particular, with regard to fumed silica, it is more preferable to use fumed silica having an average primary particle size of 5 nm or more and 50 nm or less, since the reinforcing effect is particularly large.
[0209]
When it is desired to obtain a cured product having low strength and large elongation, a filler selected mainly from titanium oxide, calcium carbonate, talc, ferric oxide, zinc oxide, shirasu balloon and the like can be added. In general, if the specific surface area of calcium carbonate is small, the effect of improving the breaking strength, breaking elongation, adhesion and weather resistance of the cured product may not be sufficient. As the value of the specific surface area is larger, the effect of improving the breaking strength, breaking elongation, adhesion and weather resistance of the cured product becomes larger.
[0210]
Further, it is more preferable that the calcium carbonate has been subjected to a surface treatment using a surface treatment agent. When the surface-treated calcium carbonate is used, the workability of the composition of the present invention is improved as compared with the case where calcium carbonate without the surface treatment is used, and the adhesiveness and weather resistance of the curable composition are improved. It is considered that the improvement effect is further improved. As the surface treatment agent, organic substances such as fatty acids, fatty acid soaps and fatty acid esters and various surfactants, and various coupling agents such as silane coupling agents and titanate coupling agents are used. Specific examples include, but are not limited to, fatty acids such as caproic acid, caprylic acid, pelargonic acid, capric acid, undecanoic acid, lauric acid, myristic acid, palmitic acid, stearic acid, behenic acid, and oleic acid. And salts of the fatty acids such as sodium and potassium, and alkyl esters of the fatty acids. Specific examples of the surfactant include polyoxyethylene alkyl ether sulfates and long-chain alcohol sulfates, and sulfate-type anionic surfactants such as sodium salts and potassium salts thereof, and alkylbenzenesulfonic acids and alkylnaphthalenes. Sulfonic acid, paraffin sulfonic acid, α-olefin sulfonic acid, alkyl sulfosuccinic acid and the like, and sulfonic acid type anionic surfactants such as a sodium salt and a potassium salt thereof and the like are included. The amount of the surface treatment agent to be treated is preferably in the range of 0.1 to 20% by weight, more preferably in the range of 1 to 5% by weight, based on calcium carbonate. If the treatment amount is less than 0.1% by weight, the effect of improving workability, adhesion and weather resistance may not be sufficient, and if it exceeds 20% by weight, the storage stability of the curable composition may be insufficient. May drop.
[0211]
Although not particularly limited, when calcium carbonate is used, the colloidal calcium carbonate is used when the thixotropy of the compound and the breaking strength of the cured product, the breaking elongation, and the effect of improving the adhesion and weather resistance are particularly expected. Is preferred.
[0212]
On the other hand, heavy calcium carbonate may be added for the purpose of lowering the viscosity and increasing the amount of the compound, reducing costs, and the like.If this heavy calcium carbonate is used, use the following as necessary. be able to.
[0213]
Heavy calcium carbonate is obtained by mechanically pulverizing and processing natural chalk (chalk), marble, limestone and the like. The pulverization method includes a dry method and a wet method, but a wet-pulverized product is often not preferable because the storage stability of the curable composition of the present invention often deteriorates. Heavy calcium carbonate becomes a product having various average particle diameters by classification. Although not particularly limited, when the effect of improving the breaking strength, breaking elongation, adhesion and weather resistance of the cured product is expected, the value of the specific surface area is 1.5 m.²/ G or more 50m²/ G or less, preferably 2 m²/ G or more 50m²/ G or less, more preferably 2.4 m²/ G or more 50m²/ G or less, more preferably 3 m²/ G or more 50m²/ G or less is particularly preferred. 1.5m specific surface area²If it is less than / g, the improvement effect may not be sufficient. Of course, this is not the case when the viscosity is simply reduced or when the purpose is only to increase the amount.
[0214]
Here, the value of the specific surface area refers to a value measured by an air permeation method (a method of determining a specific surface area from the permeability of air to a powder-packed layer) according to JIS K 5101 as a measurement method. It is preferable to use a specific surface area measuring device SS-100 manufactured by Shimadzu Corporation as a measuring instrument.
[0215]
These fillers may be used alone or in combination of two or more as required. Although not particularly limited, for example, the value of the specific surface area is 1.5 m if necessary.²/ G or more of calcium carbonate and colloidal calcium carbonate, the increase in the viscosity of the compound is moderately suppressed, and the effects of improving the breaking strength, breaking elongation, adhesion and weather resistance of the cured product can be greatly expected.
[0216]
When the filler is used, the amount of the filler is preferably 5 to 1000 parts by weight, and more preferably 20 to 500 parts by weight, based on 100 parts by weight of the vinyl polymer. More preferably, it is particularly preferably used in the range of 40 to 300 parts by weight. If the amount is less than 5 parts by weight, the effect of improving the breaking strength, elongation at break, adhesion and weather resistance of the cured product may not be sufficient. May be reduced. The filler may be used alone or in combination of two or more.
<Micro hollow particles>
Further, for the purpose of weight reduction and cost reduction without causing significant deterioration in physical properties, fine hollow particles may be used in combination with these reinforcing fillers.
[0219]
Such fine hollow particles (hereinafter, referred to as balloons) are not particularly limited, but have a diameter of 1 mm or less, preferably 500 μm or less, and more preferably, as described in “The Latest Technology of Functional Fillers” (CMC). Is a hollow body made of an inorganic or organic material of 200 μm or less. In particular, the true specific gravity is 1.0 g / cm³It is preferable to use the following minute hollow body, and more preferably 0.5 g / cm³It is preferable to use the following minute hollow body.
[0218]
Examples of the inorganic balloons include silicate balloons and non-silicate balloons, and silicate balloons include shirasu balloons, perlite, glass balloons, silica balloons, fly ash balloons, and the like, and non-silicate balloons include alumina. Balloons, zirconia balloons, carbon balloons and the like can be exemplified. Specific examples of these inorganic balloons include WINLIGHT manufactured by Ichi Kasei as a Shirasu balloon, Sankilite manufactured by Sanki Kogyo, Caloon manufactured by Nippon Sheet Glass, Cellstar Z-28 manufactured by Sumitomo 3M, and MICRO manufactured by EMERSON & CUMING. BALLOON, CELAMIC GLASSOMODULES manufactured by PITTSBURGER CORNING, GLASS BUBBLES manufactured by 3M, Q-CEL manufactured by Asahi Glass as a silica balloon, E-SPHERES manufactured by Taiheiyo Cement, CEROSPHERES manufactured by PFAMARKETING as a fly ash balloon. S. A FILLITE manufactured by A, BW manufactured by Showa Denko as an alumina balloon, HOLLOW ZIRCONIUM SPHEES manufactured by ZIRCOA as a zirconia balloon, Kurekasphere manufactured by Kureha Chemical and Carbosphere manufactured by GENERAL TECHNOLOGIES are manufactured as a carbon balloon.
[0219]
Examples of the organic balloon include a thermosetting resin balloon and a thermoplastic resin balloon.The thermosetting balloon includes a phenol balloon, an epoxy balloon, and a urea balloon.The thermoplastic balloon includes a Saran balloon and a polystyrene balloon. Examples include a polymethacrylate balloon, a polyvinyl alcohol balloon, and a styrene-acrylic balloon. Also, a balloon of a crosslinked thermoplastic resin can be used. The balloon here may be a balloon after foaming, or a balloon containing a foaming agent and then foamed after blending.
[0220]
Specific examples of these organic balloons include UCAR and PHENOLIC MICROBALLLOONS manufactured by Union Carbide as phenol balloons, ECCOSPHERES manufactured by EMERSON & CUMING as epoxy balloons, EMERSON & CUMING manufactured by EMERSON & CUMING ECCOSPHERES VF-O manufactured by Saran Balloons, and MICROSEHERM manufactured by Saran Balloon. Expancel manufactured by Nippon Filament, Matsumoto Microspheres manufactured by Matsumoto Yushi Seiyaku, and DYLITE EXPANDABLE POLYSTYRENE manufactured by ARCOPOLYMERS as polystyrene balloons, and EXPANDABLE POLYSTYRENE BEA manufactured by BASF WYANDOTE. S, crosslinked styrene - SX863 is acrylic acid balloon made by Japan Synthetic Rubber (P) are commercially available.
[0221]
The balloons may be used alone or in combination of two or more. Further, the surface of these balloons is fatty acid, fatty acid ester, rosin, rosin lignin, silane coupling agent, titanium coupling agent, aluminum coupling agent, polypropylene glycol, etc. to improve dispersibility and workability of the compound. Processed ones can also be used. These balloons are used to reduce the weight and cost without impairing the flexibility, elongation and strength of the physical properties when the composition is cured.
[0222]
Although the content of the balloon is not particularly limited, it can be preferably used in the range of 0.1 to 50 parts, more preferably 0.1 to 30 parts, based on 100 parts by weight of the vinyl polymer. When the amount is less than 0.1 part, the effect of weight reduction is small, and when the amount is 50 parts or more, a decrease in tensile strength among mechanical properties when the composition is cured may be observed. When the specific gravity of the balloon is 0.1 or more, it is preferably 3 to 50 parts, more preferably 5 to 30 parts.
<Physical property modifier>
The curable composition of the present invention may optionally contain a physical property modifier for adjusting the tensile properties of the resulting cured product.
[0223]
The physical property adjuster is not particularly limited, and for example, alkyl alkoxysilanes such as methyltrimethoxysilane, dimethyldimethoxysilane, trimethylmethoxysilane, n-propyltrimethoxysilane; dimethyldiisopropenoxysilane, methyltriisopropenoxy Silane, alkylisopropenoxysilane such as γ-glycidoxypropylmethyldiisopropenoxysilane, γ-glycidoxypropylmethyldimethoxysilane, γ-glycidoxypropyltrimethoxysilane, vinyltrimethoxysilane, vinyldimethylmethoxy Silane, γ-aminopropyltrimethoxysilane, N- (β-aminoethyl) aminopropylmethyldimethoxysilane, γ-mercaptopropyltrimethoxysilane, γ-mercaptopropylmethyldimethoxy Alkoxysilanes having a functional group such as a silane; silicone varnishes; polysiloxanes and the like. By using the physical property modifier, the hardness of the composition of the present invention when it is cured can be increased, or the hardness can be decreased, and elongation can be obtained. The physical property modifiers may be used alone or in combination of two or more.
<Silanol-containing compound>
A silanol-containing compound may be added to the curable composition of the present invention as necessary, such as changing the physical properties of the cured product. The silanol-containing compound means a compound having one silanol group in a molecule and / or a compound capable of producing a compound having one silanol group in a molecule by reacting with water. One of these may be used, or both compounds may be used simultaneously.
[0224]
The compound having one silanol group in the molecule, which is one of the silanol-containing compounds, is not particularly limited, and the compounds shown below,
(CH₃)₃SiOH, (CH₃CH₂)₃SiOH, (CH₃CH₂CH₂)₃SiOH, (n-Bu)₃SiOH, (sec-Bu)₃SiOH, (t-Bu)₃SiOH, (t-Bu) Si (CH₃)₂OH, (C₅H₁₁)₃SiOH, (C₆H₁₃)₃SiOH, (C₆H₅)₃SiOH, (C₆H₅)₂Si (CH₃) OH, (C₆H₅) Si (CH₃)₂OH, (C₆H₅)₂Si (C₂H₅) OH, C₆H₅Si (C₂H₅)₂OH, C₆H₅CH₂Si (C₂H₅)₂OH, C₁₀H₇Si (CH₃)₂OH
(However, C in the above formula₆H₅Represents a phenyl group, C₁₀H₇Represents a naphthyl group. )
Like (R ")₃A compound which can be represented by SiOH (wherein R ″ is the same or different and is a substituted or unsubstituted alkyl or aryl group),
[0225]
Embedded image

A cyclic polysiloxane compound containing a silanol group such as
[0226]
Embedded image

A chain polysiloxane compound containing a silanol group such as
[0227]
Embedded image

Compounds in which a silanol group is bonded to a polymer terminal having a main chain of silicon or carbon, such as
[0228]
Embedded image

Compounds in which silanol groups are bonded to polysilane main chain terminals, such as
[0229]
Embedded image

Compounds in which a silanol group is bonded to the terminal of a polymer having a main chain composed of silicon, carbon, and oxygen, etc., can be exemplified. Among them, a compound represented by the following general formula (45) is preferable.
(R⁵⁸)₃SiOH (45)
(Where R⁵⁸Represents a monovalent hydrocarbon group having 1 to 20 carbon atoms. Multiple R⁵⁸May be the same or different. )
R²⁷Is preferably a methyl group, an ethyl group, a vinyl group, a t-butyl group, and a phenyl group, and more preferably a methyl group.
[0230]
Above all, it is easily available and has a small molecular weight (CH₃)₃SiOH and the like are preferred.
[0231]
The compound having one silanol group in the molecule reacts with a crosslinkable silyl group of a vinyl polymer or a siloxane bond formed by crosslinking, thereby reducing the number of crosslinking points and providing a cured product with flexibility. It is estimated that
The compound that can form a compound having one silanol group in the molecule by reacting with water, which is one of the components of the present invention, is not particularly limited. The compound having one silanol group (hydrolysis product) is preferably a compound represented by the above general formula (45). For example, although not particularly limited, the following compounds can be mentioned in addition to the compound represented by the general formula (46) as described below.
[0232]
N, O-bis (trimethylsilyl) acetamide, N- (trimethylsilyl) acetamide, bis (trimethylsilyl) trifluoroacetamide, N-methyl-N-trimethylsilyltrifluoroacetamide, bistrimethylsilylurea, N- (t-butyldimethylsilyl) N -Methyltrifluoroacetamide, (N, N-dimethylamino) trimethylsilane, (N, N-diethylamino) trimethylsilane, hexamethyldisilazane, 1,1,3,3-tetramethyldisilazane, N- (trimethylsilyl) Imidazole, trimethylsilyl trifluoromethanesulfonate, trimethylsilylphenoxide, trimethylsilyl n-octanol, trimethylsilyl 2-ethylhexanol, tris (glycerol tris) Chirushiriru) iodide, tris (trimethylsilyl) ated trimethylolpropane, tris (trimethylsilyl) ated pentaerythritol, pentaerythritol tetra (trimethylsilyl) ated product, (CH₃)₃SiNHSi (CH₃)₃, (CH₃)₃SiNSi (CH₃)₂,
[0233]
Embedded image

Can be preferably used, but from the amount of silanol groups contained in the hydrolysis product, (CH₃)₃SiNHSi (CH₃)₃Is particularly preferred.
[0234]
Further, a compound which is one of the components of the present invention and which can form a compound having one silanol group in the molecule by reacting with water is not particularly limited, but other than the above compound, other than the above compound, the following general formula (46) ) Is preferred.
((R⁵⁸)₃SiO)_nR⁵⁹(46)
(Where R⁵⁸Is the same as described above. n is a positive number, R⁵⁹Represents a group obtained by removing some or all active hydrogens from an active hydrogen-containing compound. )
R⁵⁸Is preferably a methyl group, an ethyl group, a vinyl group, a t-butyl group, and a phenyl group, and more preferably a methyl group.
(R⁵⁸)₃The Si group has three R⁵⁸Is particularly preferably a trimethylsilyl group wherein all are methyl groups. Further, n is preferably 1 to 5.
[0235]
R above⁵⁹The active hydrogen-containing compound from which is derived is not particularly limited, for example, methanol, ethanol, n-butanol, i-butanol, t-butanol, n-octanol, 2-ethylhexanol, benzyl alcohol, ethylene glycol, diethylene glycol, Alcohols such as polyethylene glycol, propylene glycol, dipropylene glycol, polypropylene glycol, propanediol, tetramethylene glycol, polytetramethylene glycol, glycerin, trimethylolpropane, and pentaerythritol; phenols such as phenol, cresol, bisphenol A, and hydroquinone Formic, acetic, propionic, lauric, palmitic, stearic, behenic, acrylic, methacrylic, oleic Carboxylic acids such as acid, linoleic acid, linolenic acid, sorbic acid, oxalic acid, malonic acid, succinic acid, adipic acid, maleic acid, benzoic acid, phthalic acid, terephthalic acid and trimellitic acid; ammonia; methylamine, dimethylamine Amines such as ethylamine, diethylamine, n-butylamine and imidazole; acid amides such as acetamide and benzamide; ureas such as urea and N, N'-diphenylurea; ketones such as acetone, acetylacetone and 2,4-heptadione. And the like.
[0236]
Compounds that can produce a compound having one silanol group in the molecule by reacting with water represented by the general formula (46) include, for example, trimethylsilyl chloride and dimethyl (t (Butyl) chloride and the like.⁵⁸)₃It can be obtained by reacting a compound having a group capable of reacting with active hydrogen such as a halogen group together with a Si group, but is not limited thereto.⁵⁸Is the same as described above. ).
[0237]
Specific examples of the compound represented by the general formula (46) include allyloxytrimethylsilane, N, O-bis (trimethylsilyl) acetamide, N- (trimethylsilyl) acetamide, bis (trimethylsilyl) trifluoroacetamide, N- Methyl-N-trimethylsilyltrifluoroacetamide, bistrimethylsilylurea, N- (t-butyldimethylsilyl) N-methyltrifluoroacetamide, (N, N-dimethylamino) trimethylsilane, (N, N-diethylamino) trimethylsilane, Hexamethyldisilazane, 1,1,3,3-tetramethyldisilazane, N- (trimethylsilyl) imidazole, trimethylsilyl trifluoromethanesulfonate, trimethylsilylphenoxide, trimethyl of n-octanol Silylation products, triethylsilyl products of 2-ethylhexanol, tris (trimethylsilyl) products of glycerin, tris (trimethylsilyl) products of trimethylolpropane, tris (trimethylsilyl) products of pentaerythritol, tetra (trimethylsilyl) products of pentaerythritol, etc. But not limited to these. These may be used alone or in combination of two or more.
[0238]
In addition, the general formula (((R⁶⁰)₃SiO) (R⁶¹O)_s)_tA compound which can be represented by Z, CH₃O (CH₂CH (CH₃) O)₅Si (CH₃)₃, CH₂= CHCH₂(CH₂CH (CH₃) O)₅Si (CH₃)₃, (CH₃)₃SiO (CH₂CH (CH₃) O)₅Si (CH₃)₃, (CH₃)₃SiO (CH₂CH (CH₃) O)₇Si (CH₃)₃
(Where R⁶⁰Is the same or different, substituted or unsubstituted monovalent hydrocarbon group or hydrogen atom, R⁶¹Is a divalent hydrocarbon group having 1 to 8 carbon atoms, s and t are positive integers, s is 1 to 6, s × t is 5 or more, and Z is a 1 to 6 valent organic group.
Etc. can also be suitably used. These may be used alone or in combination of two or more.
[0239]
Among the compounds that can produce a compound having one silanol group in the molecule by reacting with moisture, the active hydrogen-containing compounds produced after hydrolysis, because they do not adversely affect storage stability, weather resistance, etc. Are preferably phenols, acid amides and alcohols, and more preferably phenols and alcohols in which the active hydrogen-containing compound is a hydroxyl group.
[0240]
Among the above compounds, N, O-bis (trimethylsilyl) acetamide, N- (trimethylsilyl) acetamide, trimethylsilylphenoxide, trimethylsilyl compound of n-octanol, trimethylsilyl compound of 2-ethylhexanol, tris (trimethylsilyl) compound of glycerin, Preference is given to trimethylolpropane tris (trimethylsilyl) compound, pentaerythritol tris (trimethylsilyl) compound, pentaerythritol tetra (trimethylsilyl) compound and the like.
[0241]
A compound capable of producing a compound having one silanol group in the molecule by reacting with water has one silanol group in the molecule by reacting with water during storage, curing, or after curing. Produce compound. The compound having one silanol group in the molecule formed as described above reacts with the crosslinkable silyl group of the vinyl polymer or the siloxane bond formed by crosslinking as described above, thereby reducing the number of crosslinking points. It is presumed that the cured product was reduced to give flexibility.
[0242]
The amount of the silanol-containing compound added can be appropriately adjusted according to the expected physical properties of the cured product. The silanol-containing compound can be added in an amount of 0.1 to 50 parts by weight, preferably 0.3 to 20 parts by weight, more preferably 0.5 to 10 parts by weight, based on 100 parts by weight of the vinyl polymer. If the amount is less than 0.1 part by weight, the effect of addition will not be exhibited, and if it exceeds 50 parts by weight, crosslinking will be insufficient, and the strength and gel fraction of the cured product will be too low.
[0243]
The time at which the silanol-containing compound is added to the vinyl polymer is not particularly limited, and may be added during the production of the vinyl polymer or may be added during the preparation of the curable composition.
<Thixotropic agent (anti-sagging agent)>
A thixotropic agent (anti-sagging agent) may be added to the curable composition of the present invention, if necessary, to prevent sagging and improve workability.
[0244]
The anti-sagging agent is not particularly limited, and examples thereof include polyamide waxes, hydrogenated castor oil derivatives; and metal soaps such as calcium stearate, aluminum stearate, and barium stearate. These thixotropic agents (anti-sagging agents) may be used alone or in combination of two or more.
<Photocurable substance>
A photocurable substance may be added to the curable composition of the present invention as needed. A photocurable substance is a substance in which the molecular structure undergoes a chemical change in a short time by the action of light, and causes a physical change such as curing. By adding this photocurable substance, the tackiness (also referred to as residual tack) of the cured product surface when the curable composition is cured can be reduced. This photocurable substance is a substance that can be cured by irradiating light, and a typical photocurable substance is, for example, to be left standing at room temperature for one day in a sunshine position (near a window) in a room. It is a substance that can be cured by Many types of compounds of this kind are known, such as organic monomers, oligomers, resins and compositions containing them, and the type is not particularly limited. For example, unsaturated acrylic compounds, polycinnamic acids Examples include vinyls and azide resins.
[0245]
The unsaturated acrylic compound is a monomer, an oligomer or a mixture thereof having an unsaturated group represented by the following general formula (47).
CH₂= CHR⁶²CO (O)-(47)
Where R⁶²Represents hydrogen, an alkyl group having 1 to 10 carbon atoms, an aryl group having 6 to 10 carbon atoms, or an aralkyl group having 7 to 10 carbon atoms.
[0246]
Specific examples of the unsaturated acrylic compound include (meth) acrylic acid esters of low molecular weight alcohols such as ethylene glycol, glycerin, trimethylolpropane, pentaerythritol and neopentyl alcohol; bisphenol A, isocyanuric acid and the like. (Meth) acrylic acid esters of acids or alcohols obtained by modifying the above low molecular weight alcohols with ethylene oxide or propylene oxide; polyether polyols having a main chain of polyether and having a hydroxyl group at a terminal, and polyols having a main chain of polyether. A polymer polyol obtained by radical polymerization of a vinyl monomer with a polyester, a polyester polyol having a main chain of a polyester and having a hydroxyl group at a terminal, a vinyl or (meth) acrylic polymer having a main chain having a hydroxyl group in the main chain (Meth) acrylic acid esters such as polyols having epoxy resin; epoxy acrylate oligomers obtained by reacting (meth) acrylic acid with epoxy resin such as bisphenol A type or novolak type; polyol, polyisocyanate and hydroxyl group-containing ( A urethane acrylate oligomer having a urethane bond and a (meth) acrylic group in a molecular chain obtained by reacting a (meth) acrylate or the like may be used.
[0247]
Polyvinyl cinnamate is a photosensitive resin having a cinnamoyl group as a photosensitive group, and includes many polyvinyl alcohol cinnamate derivatives in addition to those obtained by esterifying polyvinyl alcohol with cinnamic acid.
[0248]
Azide resin is known as a photosensitive resin having an azide group as a photosensitive group, and is usually a photosensitive resin in addition to a rubber photosensitive solution containing an azide compound as a photosensitive agent (published on March 17, 1972. Pp. 93-106 and 117-) published by The Printing Society of Japan, and these can be used alone or in combination, and if necessary, a sensitizer may be added.
[0249]
Among the above photocurable substances, unsaturated acrylic compounds are preferred because they are easy to handle.
[0250]
The photocurable substance is preferably added in an amount of 0.01 to 20 parts by weight based on 100 parts by weight of the vinyl polymer. If the amount is less than 0.01 part by weight, the effect is small, and if it exceeds 20 parts by weight, physical properties may be adversely affected. The effect may be enhanced by adding a sensitizer such as a ketone or a nitro compound or an accelerator such as an amine. <Air oxidation curable substance>
An air oxidation curable substance may be added to the curable composition of the present invention as needed. An air oxidation-curable substance is a compound having an unsaturated group that can be cross-linked and cured by oxygen in the air. By adding this air oxidation curable substance, it is possible to reduce the tackiness (also referred to as residual tack) of the cured product surface when the curable composition is cured. The air oxidation curable substance in the present invention is a substance which can be cured by contact with air, and more specifically, has a property of reacting with oxygen in the air to cure. A typical air oxidatively curable material can be cured, for example, by standing in air indoors for one day.
[0251]
Examples of the air oxidation curable substance include drying oils such as tung oil and linseed oil; various alkyd resins obtained by modifying these drying oils; acrylic polymers, epoxy resins, and silicone resins modified with the drying oil; 1,2-polybutadiene and 1,4-polybutadiene are converted into C5-C8 diene polymers and copolymers, and various modified products of the polymers and copolymers (maleated modified products, boiled oil modified products, etc.) And the like are specific examples. Of these, tung oil and liquid materials (liquid diene polymers) and modified products thereof among diene polymers are particularly preferred.
[0252]
Specific examples of the liquid diene-based polymer include butadiene, chloroprene, isoprene, a liquid polymer obtained by polymerizing or copolymerizing a diene-based compound such as 1,3-pentadiene, and copolymerizable with these diene-based compounds. Such as NBR and SBR obtained by copolymerizing a monomer such as acrylonitrile and styrene having a diene compound as the main component, and various modified products thereof (maleated modified product, boiled oil) And the like). These may be used alone or in combination of two or more. Among these liquid diene compounds, liquid polybutadiene is preferred.
[0253]
The air oxidation curable substance may be used alone or in combination of two or more. In some cases, the effect can be enhanced by using a catalyst or a metal dryer that promotes the oxidation curing reaction together with the air oxidation-curable substance. Examples of these catalysts and metal dryers include metal salts and amine compounds such as cobalt naphthenate, lead naphthenate, zirconium naphthenate, cobalt octylate, and zirconium octylate.
[0254]
It is preferable to add 0.01 to 20 parts by weight of the air oxidation curable substance to 100 parts by weight of the vinyl polymer. If the amount is less than 0.01 part by weight, the effect is small, and if it exceeds 20 parts by weight, physical properties may be adversely affected.
<Antioxidant>
An antioxidant may be added to the curable composition of the present invention as needed. Various antioxidants are known, and are described in, for example, "Antioxidant Handbook" issued by Taisei Corporation and "Deterioration and Stabilization of Polymer Materials" (235-242) issued by CMC Chemical. Although various things are mentioned, it is not necessarily limited to these.
[0255]
For example, phosphorus-based antioxidants such as thioethers such as MARK @ PEP-36 and MARK @ AO-23 (all of which are manufactured by Adeka-Gas Chemical), Irgafos38, Irgafos168, IrgafosP-EPQ (all of which are manufactured by Nippon Ciba Geigy). And the like. Among them, hindered phenol compounds as shown below are preferred.
[0256]
Specific examples of the hindered phenol compound include the following.
2,6-di-tert-butyl-4-methylphenol, 2,6-di-tert-butyl-4-ethylphenol, mono (or di or tri) (α-methylbenzyl) phenol, 2,2′-methylenebis (4ethyl-6-tert-butylphenol), 2,2′-methylenebis (4methyl-6-tert-butylphenol), 4,4′-butylidenebis (3-methyl-6-tert-butylphenol), 4,4 ′ -Thiobis (3-methyl-6-tert-butylphenol), 2,5-di-tert-butylhydroquinone, 2,5-di-tert-amylhydroquinone, triethylene glycol-bis- [3- (3-t- Butyl-5-methyl-4hydroxyphenyl) propionate], 1,6-hexanediol-bis [3- (3 5-di-tert-butyl-4-hydroxyphenyl) propionate], 2,4-bis- (n-octylthio) -6- (4-hydroxy-3,5-di-tert-butylanilino) -1,3,3 5-triazine, pentaerythrityl-tetrakis [3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate], 2,2-thio-diethylenebis [3- (3,5-di-t -Butyl-4-hydroxyphenyl) propionate], octadecyl-3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate, N, N'-hexamethylenebis (3,5-di-t- Butyl-4-hydroxy-hydrocinnamamide), 3,5-di-tert-butyl-4-hydroxy-benzylphosphonate-diethyl ester, 1,3,5-trimethyl -2,4,6-tris (3,5-di-t-butyl-4-hydroxybenzyl) benzene, calcium bis (3,5-di-t-butyl-4-hydroxybenzylphosphonate) calcium, tris- (3,5-di-t-butyl-4-hydroxybenzyl) isocyanurate, 2,4-2,4-bis [(octylthio) methyl] o-cresol, N, N′-bis [3- (3 5-di-t-butyl-4-hydroxyphenyl) propionyl] hydrazine, tris (2,4-di-t-butylphenyl) phosphite, 2- (5-methyl-2-hydroxyphenyl) benzotriazole, 2- [2-hydroxy-3,5-bis (α, α-dimethylbenzyl) phenyl] -2H-benzotriazole, 2- (3,5-di-t-butyl-2-hydroxyphenyl) Benzotriazole, 2- (3-t-butyl-5-methyl-2-hydroxyphenyl) -5-chlorobenzotriazole, 2- (3,5-di-t-butyl-2-hydroxyphenyl) -5-chloro Benzotriazole, 2- (3,5-di-t-amyl-2-hydroxyphenyl) benzotriazole, 2- (2′-hydroxy-5′-t-octylphenyl) -benzotriazole, methyl-3- [3 -T-butyl-5- (2H-benzotriazol-2-yl) -4-hydroxyphenyl] propionate-condensate with polyethylene glycol (molecular weight about 300), hydroxyphenylbenzotriazole derivative, 2- (3,5- Bis (1,2,2,6,6-pentame di-t-butyl-4-hydroxybenzyl) -2-n-butylmalonate -4-piperidyl), 2,4-di -t- butyl-3,5-di -t- butyl-4-hydroxybenzoate, and the like.
[0257]
Speaking of trade names, Nocrack 200, Nocrack M-17, Nocrack SP, Nocrack SP-N, Nocrack NS-5, Nocrack NS-6, Nocrack NS-30, Nocrack 300, Nocrack NS-7, Nocrack DAH (all above) MARK AO-30, MARK AO-40, MARK AO-50, MARK AO-60, MARK AO-616, MARK AO-635, MARK AO-658, MARK AO-80, MARK AO-15, MARK AO-18, MARK 328, MARK AO-37 (all manufactured by Adeka Argus Chemical), IRGANOX-245, IRGANOX-259, IRGANOX-565, IRGANOX-1010, IRGANOX-1024 IRGANOX-1035, IRGANOX-1076, IRGANOX-1081, IRGANOX-1098, IRGANOX-1222, IRGANOX-1330, IRGANOX-1425WL (all manufactured by Ciba Geigy Japan), SumilizerGM, SumilizerGA-80 (all manufactured by Sumitomo Chemical) However, the present invention is not limited thereto.
[0258]
The antioxidant may be used in combination with a light stabilizer described later, and when used in combination, the effect is further exhibited, and heat resistance is particularly improved, which is particularly preferable. Tinuvin C353 and Tinuvin B75 (all of which are manufactured by Nippon Ciba Geigy) in which an antioxidant and a light stabilizer are mixed in advance may be used.
[0259]
The amount of the antioxidant used is preferably in the range of 0.1 to 10 parts by weight based on 100 parts by weight of the vinyl polymer. If it is less than 0.1 part by weight, the effect of improving the weather resistance is small, and if it is more than 5 parts by weight, there is no great difference in the effect and it is economically disadvantageous.
<Light stabilizer>
A light stabilizer may be added to the curable composition of the present invention as needed. Various types of light stabilizers are known, and are described in, for example, "Antioxidant Handbook" issued by Taisei Corporation and "Deterioration and Stabilization of Polymer Materials" (235 to 242) published by CMC Chemical. Although various things are mentioned, it is not necessarily limited to these.
[0260]
Although not particularly limited, among the light stabilizers, an ultraviolet absorber is preferable, and specifically, tinuvin P, tinuvin 234, tinuvin 320, tinuvin 326, tinuvin 327, tinuvin 329, and tinuvin 213 (all manufactured by Nippon Ciba Geigy Co., Ltd.) ), Benzophenone compounds such as CHIMASSORB81, and benzoate compounds such as Tinuvin 120 (manufactured by Nippon Ciba Geigy).
[0261]
Also, hindered amine compounds are preferred, and such compounds are described below.
Dimethyl succinate-1- (2-hydroxyethyl) -4-hydroxy-2,2,6,6-tetramethylpiperidine polycondensate, poly [{6- (1,1,3,3-tetramethylbutyl)] Amino-1,3,5-triazine-2,4-diyl {(2,2,6,6-tetramethyl-4-piperidyl) imino}], N, N'-bis (3aminopropyl) ethylenediamine- 2,4-bis [N-butyl-N- (1,2,2,6,6-pentamethyl-4-piperidyl) amino] -6-chloro-1,3,5-triazine condensate, bis (2 2,6,6-tetramethyl-4-piperidyl) sebacate, succinic acid-bis (2,2,6,6-tetramethyl-4-piperidinyl) ester and the like.
[0262]
Speaking of trade names, Tinuvin 622LD, Tinuvin 144, CHIMASSORB 944LD, CHIMASSORB 119FL, Irgafos 168 (all manufactured by Nippon Ciba Geigy), MARK LA-52, MARK LA-57, MARK LA-62, MARK LA-67. 63, MARK LA-68, MARK LA-82, MARK LA-87 (all manufactured by Adeka Gas Co., Ltd.), SANOL LS-770, SANOL LS-765, SANOL LS-292, SANOL LS-2626, SANOL LS -1114, SANOL LS-744, SANOL LS-440 (all manufactured by Sankyo) and the like, but are not limited thereto.
[0263]
Further, a combination of an ultraviolet absorber and a hindered amine compound may exert more effects. Therefore, the combination is not particularly limited, but may be used in combination, and the combination is sometimes preferred.
[0264]
The light stabilizer may be used in combination with the above-mentioned antioxidant, and when used together, the effect is further exhibited, and particularly, the weather resistance is sometimes improved, so that it is particularly preferable. Tinuvin C353 and Tinuvin B75 (all of which are manufactured by Nippon Ciba Geigy) in which a light stabilizer and an antioxidant are mixed in advance may be used.
[0265]
The amount of the light stabilizer used is preferably in the range of 0.1 to 10 parts by weight based on 100 parts by weight of the vinyl polymer. If it is less than 0.1 part by weight, the effect of improving the weather resistance is small, and if it is more than 5 parts by weight, there is no great difference in the effect and it is economically disadvantageous.
Other additives
Various additives may be added to the curable composition of the present invention as needed for the purpose of adjusting various physical properties of the curable composition or the cured product. Examples of such additives include, for example, flame retardants, curability regulators, antioxidants, radical inhibitors, ultraviolet absorbers, metal deactivators, ozone deterioration inhibitors, phosphorus peroxide decomposers , A lubricant, a pigment, a foaming agent, a photocurable resin and the like. These various additives may be used alone or in combination of two or more.
[0266]
Specific examples of such additives are described, for example, in the specifications of JP-B-4-69659, JP-B-7-108928, JP-A-63-254149 and JP-A-64-22904. I have.
[0267]
The curable composition of the present invention may be prepared as a one-component type in which all the components are pre-mixed, sealed and stored, and cured by the moisture in the air after application. A component such as an agent and water may be blended, and the blended material and the polymer composition may be adjusted as a two-component type to be mixed before use. When the two-component type is used, a coloring agent can be added at the time of mixing the two components. For example, when providing a sealing material that matches the color of the siding board, a wide variety of colors can be provided with limited stock. For example, it becomes possible to easily cope with multi-color demands from the market, and it is more preferable for low-rise buildings and the like. As the colorant, for example, a pigment and a plasticizer, and in some cases, a filler obtained by mixing and pasting a filler are used to facilitate the operation. Further, by adding a retarder at the time of mixing the two components, the curing speed can be finely adjusted at the work site.
<< Cured product >>
<Application>
The curable composition of the present invention includes, but is not limited to, sealing materials for building elastic sealing materials, sealants for double glazing, etc., electric and electronic component materials such as solar cell back surface sealing materials, and wires and cables. Electrical insulating materials such as insulating coating materials, adhesives, adhesives, elastic adhesives, paints, powder coatings, coating materials, foams, sealing materials such as can lids, potting agents for electric and electronic devices, films, gaskets, casting Materials, various molding materials, artificial marble, sealing materials for rust prevention and waterproofing of the end face (cut part) of netted glass and laminated glass, liquid sealants used in automobile parts, electric parts, various machine parts, etc. It can be used for various applications such as.
[0268]
【Example】
Hereinafter, specific examples of the present invention will be described together with comparative examples, but the present invention is not limited to the following examples.
[0269]
In the following Examples and Comparative Examples, “parts” and “%” represent “parts by weight” and “% by weight”, respectively. In this example, “triamine” refers to pentamethyldiethylenetriamine.
[0270]
In the following examples, "number average molecular weight" and "molecular weight distribution (ratio of weight average molecular weight to number average molecular weight)" were calculated by a standard polystyrene conversion method using gel permeation chromatography (GPC). However, a GPC column filled with a crosslinked polystyrene gel (shodex @ GPC @ K-804; manufactured by Showa Denko) was used, and chloroform was used as a GPC solvent.
(Production Example 1)
CuBr (1.11 kg) was charged into a 250 L reactor equipped with a stirrer and a jacket, and the inside of the reaction vessel was purged with nitrogen. Acetonitrile (5.0 kg) was added, warm water was passed through the jacket, and the mixture was stirred at 70 ° C. for 15 minutes. To this, butyl acrylate (6.6 kg), ethyl acrylate (9.5 kg), methoxyethyl acrylate (7.8 kg), diethyl 2,5-dibromoadipate (3.09 kg) and acetonitrile (5.0 kg) Was added, and the mixture was further stirred at 70 ° C. for about 30 minutes. To this was added pentamethyldiethylenetriamine (hereinafter referred to as triamine) to start the reaction. Triamine was appropriately added during the reaction, and polymerization was carried out at an internal temperature of about 70 to 80 ° C. The total amount of triamine used in the polymerization step was 45 g. Four hours after the start of the reaction, unreacted monomer and acetonitrile were devolatilized by heating and stirring at 80 ° C. under reduced pressure. Acetonitrile (29.9 kg), 1,7-octadiene (28.4 kg) and triamine (446 g) were added to the concentrate, and stirring was continued for 6 hours. The mixture was heated and stirred at 80 ° C. under reduced pressure to devolatilize acetonitrile and unreacted 1,7-octadiene, and concentrated. Toluene (120 kg) was added to the concentrate to dissolve the polymer. The solid copper in the polymer mixture was filtered with a bag filter (manufactured by HAYWARD, nominal filter cloth pore diameter 1 μm). To the filtrate were added Kyoward 500SH (2 parts by weight per 100 parts by weight of copolymer) and Kyoward 700SL made by Kyowa Chemical: 2 parts by weight per 100 parts by weight of copolymer. The mixture was heated and stirred for 2 hours at 120 ° C. in a nitrogen mixed gas atmosphere (oxygen concentration: 6%). The insolubles in the mixture were filtered off. The filtrate was concentrated to obtain a copolymer. The copolymer was subjected to heat devolatilization (reduced pressure of 10 torr or less) at 180 ° C. for 12 hours to thereby remove Br groups from the copolymer.
[0271]
Toluene (100 parts by weight per 100 parts by weight of copolymer), Kyoward 500SH (2 parts by weight per 100 parts by weight of copolymer), Kyoward 700SL by Kyowa Chemical: heavy Hindered phenolic antioxidant (Irganox 1010; Ciba Specialty Chemicals 0.05 part) was added at 130 ° C. in an oxygen-nitrogen mixed gas atmosphere (oxygen concentration 6%). The mixture was heated and stirred for 4 hours. The insolubles in the mixture were filtered off. The filtrate was concentrated to obtain a copolymer [P1] of alkenyl-terminated copolymer 共 alkenyl-terminated poly (butyl acrylate, ethyl acrylate, methoxyethyl acrylate).
[0272]
The number average molecular weight of the copolymer [P1] was 18,000, and the molecular weight distribution was 1.1. The average number of alkenyl groups introduced per molecule of the copolymer is¹It was 1.9 as determined by 1 H NMR analysis.
[0273]
Copolymer [P1] (76 kg), dimethoxymethylhydrosilane (1.9 kg), methyl orthoformate (0.94 kg), and 1,1, 0-valent platinum were placed in a 140 L reactor pressure-resistant reaction vessel equipped with a stirrer and jacket. A xylene solution of 3,3-tetramethyl-1,3-divinyldisiloxane complex (10 mg of platinum per 1 kg of the copolymer) was charged. The mixture was heated and stirred at 100 ° C. for 2 hours under a nitrogen atmosphere. The volatile components of the mixture were distilled off under reduced pressure to obtain a silyl group-terminated vinyl copolymer (copolymer [P2]). The number average molecular weight of the obtained copolymer was 19000 by GPC measurement (in terms of polystyrene), and the molecular weight distribution was 1.2. The average number of silyl groups introduced per molecule of polymer is¹As a result of 1 H NMR analysis, the number was 1.8.
(Example 1)
In 100 parts of the copolymer [P1] obtained in Production Example 1, 10 parts of IMSIL # A-25 (average particle diameter of 3.5 μm, manufactured by Tatsumori) as silica having an average particle diameter of 1 μm or more, and Aerosil R974 as another silica. 10 parts of fumed silica having an average primary particle diameter of 12 nm (manufactured by Nippon Aerosil Co., Ltd.) were further mixed using a three-paint roll, and the viscosity of the curable composition was measured using an E-type viscometer (measurement temperature). 50 ° C.). Then, a chain siloxane (containing an average of 5 hydrosilyl groups and an average of 5 α-methylstyrene groups in the molecule: the amount of Si—H groups 3.70 mmol / g) is added to the copolymer [P1]. Is added in an amount such that the SiH group of the linear siloxane becomes 1.8 equivalents of the alkenyl group of the copolymer [P1], and 1,1,3,3-tetramethyl-1,3 of zero-valent platinum is added. Xylene solution of divinyldisiloxane complex (1.32 × 10^-5mmol / μl) is calculated as 5 × 10 5 alkenyl groups of the copolymer [P1] in terms of platinum.^-4Molar equivalents were added and mixed evenly. After sufficiently defoaming the curable composition thus obtained in a vacuum oven at 50 ° C, a sheet having a thickness of about 2 mm was applied and cured at 150 ° C for 100 minutes. Physical properties were measured. The test piece was punched into a (2 (1/3) number) dumbbell shape. The results are shown in Table 1.
(Example 2)
In 100 parts of the copolymer [P2] obtained in Production Example 1, 10 parts of IMSIL # A-25 (average particle diameter of 3.5 μm, manufactured by Tatsumori) as silica having an average particle diameter of 1 μm or more, and Aerosil RY200 as another silica. 10 parts of fumed silica having an average primary particle diameter of 12 nm: manufactured by Nippon Aerosil Co., Ltd. and 20 parts of a plasticizer (acrylic, UP-1020: manufactured by Toagosei Co., Ltd.) are further mixed thoroughly using three paint rolls. After that, the viscosity of this curable composition was measured with an E-type viscometer (measuring temperature 23 ° C.). Thereafter, a curing catalyst (dibutyltin diacetate: tetravalent tin) was added to 100 parts of the copolymer so that the amount became 1 part, and the mixture was sufficiently stirred and mixed to remove bubbles, and then coated in a sheet having a thickness of about 2 mm. 23 ° C, 55% R. H. After curing and curing for 3 days, the mechanical properties were measured. The test piece was punched into a (2 (1/3) number) dumbbell shape. The results are shown in Table 2.
(Example 3)
Same as Example 2 except that 10 parts of IMSIL # A-15 (average particle size: 3.3 [mu] m, manufactured by Tatsumori) was added instead of IMSIL # A-25 which is silica having an average particle diameter of 1 [mu] m or more added in Example 2. Then, the viscosity of the curable composition was measured, and the mechanical properties of a cured product cured by adding a curing catalyst were measured in the same manner. Table 2 shows the results.
(Example 4)
Same as Example 2 except that 10 parts of IMSIL A-8 (average particle size: 2.2 μm, manufactured by Tatsumori) was added instead of IMSIL A-25 which is silica having an average particle size of 1 μm or more added in Example 2. Then, the viscosity of the curable composition was measured, and the mechanical properties of a cured product cured by adding a curing catalyst were measured in the same manner. Table 2 shows the results.
(Comparative Example 1)
The viscosity of the curable composition was measured in the same manner as in Example 1 except that the silica having an average particle diameter of 1 μm or more added in Example 1 was not added. The mechanical properties of the cured product were measured. The results are shown in Table 1.
(Comparative Example 2)
In the same manner as in Example 1 except that the same amount of 10 parts of Aerosil R974 (fumed silica having an average primary particle diameter of 12 nm: manufactured by Nippon Aerosil) was added instead of the silica having an average particle diameter of 1 μm or more added in Example 1, Then, the viscosity of the curable composition was measured, and the mechanical properties of a cured product cured by adding a chain siloxane and a platinum solution were also measured in the same manner (after all, here, a total of 20 parts of Aerosil R947 was blended). . The results are shown in Table 1.
[0274]
[Table 1]

(Comparative Example 3)
The viscosity of the curable composition was measured in the same manner as in Example 2 except that the silica having an average particle diameter of 1 μm or more added in Example 2 was not added, and a curing catalyst was added and cured in the same manner. The mechanical properties of the cured product were measured. The results are shown in Table 2.
(Comparative Example 4)
In the same manner as in Example 2 except that 10 parts of the same amount of Aerosil RY200 (fumed silica having an average primary particle diameter of 12 nm: manufactured by Nippon Aerosil) was added instead of the silica having an average particle diameter of 1 μm or more added in Example 2, Then, the viscosity of the curable composition was measured (after all, here, a total of 20 parts of Aerosil RY200 was blended). The viscosity was so high that it could not be measured with a BS viscometer. The results are shown in Table 2.
[0275]
[Table 2]

Each of the curable compositions using a vinyl polymer having at least one crosslinkable functional group and silica having an average particle size of 1 μm or more exhibited good viscosity and mechanical properties.
[0276]
【The invention's effect】
The present invention comprises a vinyl polymer having at least one crosslinkable silyl group, and a curable composition composed of silica having an average particle diameter of 1 μm or more and 500 μm or less, without increasing the viscosity of the curable composition so much. It is possible to provide a curable composition in which the composition is increased with silica or the like without significantly deteriorating mechanical properties while ensuring workability. Furthermore, by blending this extender, it is possible to further improve the oil resistance of a good vinyl polymer and to lower the blending cost compared to the case where only the conventional fumed silica filler is used. It becomes possible.

Claims (19)

The following two components:
(A) a vinyl polymer (I) having at least one crosslinkable functional group, and
(B) silica (II) having an average particle size of 1 μm or more and 500 μm or less,
A curable composition containing: The curable composition according to claim 1, further comprising fumed silica having an average primary particle size of 5 nm or more and 50 nm or less. The curable composition according to claim 1, further comprising a vinyl polymer (I) having a molecular weight distribution of less than 1.8. The main chain is produced by mainly polymerizing a monomer selected from the group consisting of (meth) acrylic monomers, acrylonitrile monomers, aromatic vinyl monomers, fluorine-containing vinyl monomers and silicon-containing vinyl monomers. The curable composition according to any one of claims 1 to 3, further comprising a vinyl polymer (I). The curable composition according to any one of claims 1 to 4, wherein the main chain contains a vinyl polymer (I) that is a (meth) acrylic polymer. The curable composition according to any one of claims 1 to 4, wherein the main chain contains a vinyl polymer (I) that is an acrylic polymer. The curable composition according to claim 6, wherein the main chain contains a vinyl polymer (I) that is an acrylic ester polymer. The curable composition according to any one of claims 1 to 7, wherein the crosslinkable functional group contains a vinyl polymer (I) at a main chain terminal. The curable composition according to any one of claims 1 to 8, wherein the crosslinkable functional group contains a vinyl polymer (I) that is a crosslinkable silyl group. The curable composition according to any one of claims 1 to 8, wherein the crosslinkable functional group contains a vinyl polymer (I) that is an alkenyl group. The curable composition according to any one of claims 1 to 8, wherein the crosslinkable functional group contains a vinyl polymer (I) that is a hydroxyl group. The curable composition according to any one of claims 1 to 7, wherein the crosslinkable functional group contains a vinyl polymer (I) that is an amino group. The curing according to any one of claims 1 to 8, wherein the crosslinkable functional group contains a vinyl polymer (I) which is a group having a polymerizable carbon-carbon double bond. Composition. The curable composition according to any one of claims 1 to 8, wherein the crosslinkable functional group contains a vinyl polymer (I) that is an epoxy group. The curing according to any one of claims 1 to 14, wherein the main chain of the vinyl polymer (I) contains a vinyl polymer produced by a living radical polymerization method. Composition. The curable composition according to claim 15, wherein the living radical polymerization contains a vinyl polymer that is an atom transfer radical polymerization. The atom transfer radical polymerization contains a vinyl polymer catalyzed by a complex selected from transition metal complexes having a central metal of Group 7, 8, 9, 10 or 11 of the Periodic Table. The curable composition according to claim 16, characterized in that: 18. The curable composition according to claim 17, wherein the metal complex used as a catalyst contains a vinyl polymer that is a complex selected from the group consisting of copper, nickel, ruthenium, and iron complexes. 19. The curable composition according to claim 18, wherein the metal complex used as a catalyst contains a vinyl polymer that is a copper complex.