JP2002265970A - グリース組成物およびそのグリース組成物で潤滑した転がり軸受 - Google Patents
グリース組成物およびそのグリース組成物で潤滑した転がり軸受Info
- Publication number
- JP2002265970A JP2002265970A JP2001071692A JP2001071692A JP2002265970A JP 2002265970 A JP2002265970 A JP 2002265970A JP 2001071692 A JP2001071692 A JP 2001071692A JP 2001071692 A JP2001071692 A JP 2001071692A JP 2002265970 A JP2002265970 A JP 2002265970A
- Authority
- JP
- Japan
- Prior art keywords
- grease composition
- rolling bearing
- urea compound
- thickener
- grease
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【課題】 玉軸受の音響性能と耐フレッチング性を同時
に向上させることができるグリース組成物と、このグリ
ース組成物で潤滑した転がり軸受を提供する。 【解決手段】 基油と増ちょう剤を主成分とするグリー
ス組成物において、増ちょう剤としてウレア化合物とリ
チウム石鹸との混合物を配合する。増ちょう剤中のウレ
ア化合物の含有率は20〜80重量%とするのがよく、
ウレア化合物としては、アルキル基又はシクロヘキシル
基を末端基とするジウレア化合物、特に、ジイソシアネ
ート成分が4,4′−ジフェニルメタンジイソシアネー
トであるジウレア化合物が好適に使用される。このグリ
ース組成物で潤滑した転がり軸受は、リチウム石鹸とウ
レア化合物との相乗作用で音響性能が大幅に向上し、且
つ、ウレア化合物の作用で耐フレッチング性も同時に向
上する。
に向上させることができるグリース組成物と、このグリ
ース組成物で潤滑した転がり軸受を提供する。 【解決手段】 基油と増ちょう剤を主成分とするグリー
ス組成物において、増ちょう剤としてウレア化合物とリ
チウム石鹸との混合物を配合する。増ちょう剤中のウレ
ア化合物の含有率は20〜80重量%とするのがよく、
ウレア化合物としては、アルキル基又はシクロヘキシル
基を末端基とするジウレア化合物、特に、ジイソシアネ
ート成分が4,4′−ジフェニルメタンジイソシアネー
トであるジウレア化合物が好適に使用される。このグリ
ース組成物で潤滑した転がり軸受は、リチウム石鹸とウ
レア化合物との相乗作用で音響性能が大幅に向上し、且
つ、ウレア化合物の作用で耐フレッチング性も同時に向
上する。
Description
【0001】
【発明の属する技術分野】本発明は、情報機器類のスピ
ンドルモータの転がり軸受に封入されて使用されるグリ
ース組成物に関する。
ンドルモータの転がり軸受に封入されて使用されるグリ
ース組成物に関する。
【0002】
【従来の技術】従来より、コンピュータのハードディス
クドライブ(HDD)等の記録装置におけるスピンドル
モータの玉軸受などの転がり軸受には、エステルを基油
とし、リチウム石鹸を増ちょう剤とするグリース組成物
を封入したものが多い。
クドライブ(HDD)等の記録装置におけるスピンドル
モータの玉軸受などの転がり軸受には、エステルを基油
とし、リチウム石鹸を増ちょう剤とするグリース組成物
を封入したものが多い。
【0003】このようなグリース組成物の代表例として
は、ペンタエリスリトールとセバシン酸ジ−2−エチル
ヘキシルを基油とし、ステアリン酸リチウムと12−ヒ
ドロキシステアリン酸リチウムを増ちょう剤としたグリ
ース組成物が挙げられる。このグリース組成物は、転が
り軸受の耐フレッチング性の向上には寄与しないが、転
がり軸受の振動値を低減させ、音響寿命を向上させると
いう長所を有するものである。
は、ペンタエリスリトールとセバシン酸ジ−2−エチル
ヘキシルを基油とし、ステアリン酸リチウムと12−ヒ
ドロキシステアリン酸リチウムを増ちょう剤としたグリ
ース組成物が挙げられる。このグリース組成物は、転が
り軸受の耐フレッチング性の向上には寄与しないが、転
がり軸受の振動値を低減させ、音響寿命を向上させると
いう長所を有するものである。
【0004】
【発明が解決しようとする課題】しかしながら、近年の
記録密度の増大に伴う転がり軸受の高精度化や回転数増
加によって高い音響性能が要求されるようになったた
め、上記のグリース組成物の音響性能では不充分となっ
てきた。
記録密度の増大に伴う転がり軸受の高精度化や回転数増
加によって高い音響性能が要求されるようになったた
め、上記のグリース組成物の音響性能では不充分となっ
てきた。
【0005】また、最近では、磁気ヘッドのローディン
グ機構がCSS方式(コンタクト・スタート・ストップ
方式)からランプロードアンロード方式に移行しつつあ
る。このため、HDD輸送時等に外部振動が加わるとH
DDモータが微小振動し、転がり軸受転送面にフレッチ
ングが発生するため、騒音が大きくなることがある。こ
の解決のため、転がり軸受に耐フレッチング性の要求が
強くなり、上記のグリース組成物では対応が困難になっ
てきた。
グ機構がCSS方式(コンタクト・スタート・ストップ
方式)からランプロードアンロード方式に移行しつつあ
る。このため、HDD輸送時等に外部振動が加わるとH
DDモータが微小振動し、転がり軸受転送面にフレッチ
ングが発生するため、騒音が大きくなることがある。こ
の解決のため、転がり軸受に耐フレッチング性の要求が
強くなり、上記のグリース組成物では対応が困難になっ
てきた。
【0006】本発明は上記の問題に対処すべくなされた
もので、その目的とするところは、転がり軸受の音響性
能と耐フレッチング性を同時に向上させることができる
グリース組成物と、このグリース組成物で潤滑した転が
り軸受を提供することにある。
もので、その目的とするところは、転がり軸受の音響性
能と耐フレッチング性を同時に向上させることができる
グリース組成物と、このグリース組成物で潤滑した転が
り軸受を提供することにある。
【0007】
【課題を解決するための手段】上記の目的を達成するた
め、本発明に係るグリース組成物は、基油と増ちょう剤
を主成分とするグリース組成物において、増ちょう剤が
ウレア化合物とリチウム石鹸との混合物より成ることを
特徴とするものである。
め、本発明に係るグリース組成物は、基油と増ちょう剤
を主成分とするグリース組成物において、増ちょう剤が
ウレア化合物とリチウム石鹸との混合物より成ることを
特徴とするものである。
【0008】このグリース組成物のように、増ちょう剤
としてウレア化合物とリチウム石鹸との混合物を配合す
ると、リチウム石鹸がウレア化合物と相乗的に作用して
転がり軸受の音響性能の向上に大きく寄与し、リチウム
石鹸のみの増ちょう剤を配合する場合に比べて、音響性
能が大幅に高められる。しかも、ウレア化合物が転がり
軸受の耐フレッチング性の向上に大きく寄与するため、
耐フレッチング性も同時に高められる。この事実は、後
述する実施例と比較例のデータによって裏付けられる。
としてウレア化合物とリチウム石鹸との混合物を配合す
ると、リチウム石鹸がウレア化合物と相乗的に作用して
転がり軸受の音響性能の向上に大きく寄与し、リチウム
石鹸のみの増ちょう剤を配合する場合に比べて、音響性
能が大幅に高められる。しかも、ウレア化合物が転がり
軸受の耐フレッチング性の向上に大きく寄与するため、
耐フレッチング性も同時に高められる。この事実は、後
述する実施例と比較例のデータによって裏付けられる。
【0009】そして、本発明の転がり軸受は、上記のグ
リース組成物で潤滑したことを特徴とするものであり、
上記グリース組成物の作用によって優れた音響性能と耐
フレッチング性を有する。
リース組成物で潤滑したことを特徴とするものであり、
上記グリース組成物の作用によって優れた音響性能と耐
フレッチング性を有する。
【0010】
【発明の実施の形態】以下、本発明に係るグリース組成
物の具体的な実施形態を詳述する。
物の具体的な実施形態を詳述する。
【0011】本発明のグリース組成物において、増ちょ
う剤として配合するウレア化合物とリチウム石鹸との混
合物は、ウレア化合物が20〜80重量%含有されてい
るものが好ましい。このような増ちょう剤を配合する
と、既述したようにリチウム石鹸がウレア化合物と相乗
的に作用して転がり軸受の音響性能の向上に大きく寄与
し、且つ、ウレア化合物が転がり軸受の耐フレッチング
性の向上に大きく寄与するため、音響性能と耐フレッチ
ング性を同時に高めることができるグリース組成物が得
られる。
う剤として配合するウレア化合物とリチウム石鹸との混
合物は、ウレア化合物が20〜80重量%含有されてい
るものが好ましい。このような増ちょう剤を配合する
と、既述したようにリチウム石鹸がウレア化合物と相乗
的に作用して転がり軸受の音響性能の向上に大きく寄与
し、且つ、ウレア化合物が転がり軸受の耐フレッチング
性の向上に大きく寄与するため、音響性能と耐フレッチ
ング性を同時に高めることができるグリース組成物が得
られる。
【0012】増ちょう剤中のウレア化合物の含有率が2
0%よりも少ない場合は、リチウム石鹸のみの増ちょう
剤に近くなり、転がり軸受の耐フレッチング性を向上さ
せることが困難になる。一方、80重量%よりも多い場
合は、ウレア化合物のみの増ちょう剤に近くなり、転が
り軸受の耐フレッチング性を向上させることはできて
も、音響性能の低下を招くことになる。従って、いずれ
の場合も、本発明の目的を満足に達成することが難しく
なる。
0%よりも少ない場合は、リチウム石鹸のみの増ちょう
剤に近くなり、転がり軸受の耐フレッチング性を向上さ
せることが困難になる。一方、80重量%よりも多い場
合は、ウレア化合物のみの増ちょう剤に近くなり、転が
り軸受の耐フレッチング性を向上させることはできて
も、音響性能の低下を招くことになる。従って、いずれ
の場合も、本発明の目的を満足に達成することが難しく
なる。
【0013】ウレア化合物としては、アルキル基又はシ
クロヘキシル基を末端基とするジウレア化合物、即ち、
末端基がアルキル基である脂肪族ジウレア、末端基がシ
クロヘキシル基である脂環族ジウレア、或は、これらの
混合物である脂肪族/脂環族ジウレアが使用され、特
に、下記の[化1]に示すように、ジイソシアネート成
分が4,4′−ジフェニルメタンジイソシアネートであ
るジウレアは好ましく使用される。なお、ジイソシアネ
ート成分が、2,4′−トルイレンジイソシアネートや
フェニレンジイソシアネート等であるジウレアも使用可
能である。
クロヘキシル基を末端基とするジウレア化合物、即ち、
末端基がアルキル基である脂肪族ジウレア、末端基がシ
クロヘキシル基である脂環族ジウレア、或は、これらの
混合物である脂肪族/脂環族ジウレアが使用され、特
に、下記の[化1]に示すように、ジイソシアネート成
分が4,4′−ジフェニルメタンジイソシアネートであ
るジウレアは好ましく使用される。なお、ジイソシアネ
ート成分が、2,4′−トルイレンジイソシアネートや
フェニレンジイソシアネート等であるジウレアも使用可
能である。
【0014】
【化1】
【0015】また、リチウム石鹸としては、ステアリン
酸リチウムを必須成分とし、これに12−ヒドロキシス
テアリン酸リチウムを0〜50重量%含んだものが好ま
しく使用される。ステアリン酸リチウムは、単独でウレ
ア化合物と混合しても良好な音響性能を付与できるが、
12−ヒドロキシステアリン酸リチウムは、単独でウレ
ア化合物と混合すると音響性能を向上させることが難し
くなるので、上記のようにステアリン酸リチウムと併用
することが好ましい。その場合は、12−ヒドロキシス
テアリン酸リチウムの配合量を、上記のようにステアリ
ン酸リチウムと同量もしくはそれ以下にすることが好ま
しく、50重量%より多く配合すると、音響性能の向上
が不充分になる。
酸リチウムを必須成分とし、これに12−ヒドロキシス
テアリン酸リチウムを0〜50重量%含んだものが好ま
しく使用される。ステアリン酸リチウムは、単独でウレ
ア化合物と混合しても良好な音響性能を付与できるが、
12−ヒドロキシステアリン酸リチウムは、単独でウレ
ア化合物と混合すると音響性能を向上させることが難し
くなるので、上記のようにステアリン酸リチウムと併用
することが好ましい。その場合は、12−ヒドロキシス
テアリン酸リチウムの配合量を、上記のようにステアリ
ン酸リチウムと同量もしくはそれ以下にすることが好ま
しく、50重量%より多く配合すると、音響性能の向上
が不充分になる。
【0016】一方、本発明のグリース組成物に配合する
基油としては、脂肪族二塩基酸エステル及びポリオール
エステルのいずれか一方又は双方のエステルと、ポリ−
α−オレフィンとからなる混合油を使用することが好ま
しい。基油としてエステルのみを使用してもよいが、耐
熱性に優れるポリ−α−オレフィンを混合すると、基油
の寿命が延び、耐フレッチング性や音響性能も一層向上
する利点がある。基油中のポリ−α−オレフィンの混合
量は、20〜90重量%程度とするのが好ましい。
基油としては、脂肪族二塩基酸エステル及びポリオール
エステルのいずれか一方又は双方のエステルと、ポリ−
α−オレフィンとからなる混合油を使用することが好ま
しい。基油としてエステルのみを使用してもよいが、耐
熱性に優れるポリ−α−オレフィンを混合すると、基油
の寿命が延び、耐フレッチング性や音響性能も一層向上
する利点がある。基油中のポリ−α−オレフィンの混合
量は、20〜90重量%程度とするのが好ましい。
【0017】脂肪族二塩基酸エステルとしては、セバシ
ン酸ジ−2−エチルヘキシル、アゼライン酸ジ−2−エ
チルヘキシル、ドデカン二酸ジ−2−エチルヘキシルな
どが好ましく使用され、ポリオールエステルとしては、
ペンタエリスリトールエステル、トリメチロールプロパ
ンなどが好ましく使用される。また、ポリ−α−オレフ
ィンとしては、デセン−1(C10α−オレフィン)オリ
ゴマー水添物などが好ましく使用される。これらのエス
テルやポリ−α−オレフィンの動粘度は、低トルク特性
を付与するために、10〜40mm2 /s(40℃)程
度とすることが好ましい。
ン酸ジ−2−エチルヘキシル、アゼライン酸ジ−2−エ
チルヘキシル、ドデカン二酸ジ−2−エチルヘキシルな
どが好ましく使用され、ポリオールエステルとしては、
ペンタエリスリトールエステル、トリメチロールプロパ
ンなどが好ましく使用される。また、ポリ−α−オレフ
ィンとしては、デセン−1(C10α−オレフィン)オリ
ゴマー水添物などが好ましく使用される。これらのエス
テルやポリ−α−オレフィンの動粘度は、低トルク特性
を付与するために、10〜40mm2 /s(40℃)程
度とすることが好ましい。
【0018】本発明のグリース組成物においては、基油
の含有率を80〜90重量%とし、増ちょう剤の含有率
を20〜10重量%として、組成物全体の混和ちょう度
が250〜300の範囲となるようにすることが好まし
い。この程度の混和ちょう度を有するグリース組成物を
玉軸受に封入すると、低トルクの玉軸受の得ることがで
きる。
の含有率を80〜90重量%とし、増ちょう剤の含有率
を20〜10重量%として、組成物全体の混和ちょう度
が250〜300の範囲となるようにすることが好まし
い。この程度の混和ちょう度を有するグリース組成物を
玉軸受に封入すると、低トルクの玉軸受の得ることがで
きる。
【0019】なお、本発明のグリース組成物において
は、酸化防止剤、防錆剤その他の添加剤が適宜配合され
ることは言うまでもない。
は、酸化防止剤、防錆剤その他の添加剤が適宜配合され
ることは言うまでもない。
【0020】一方、本発明の転がり軸受は、上述したグ
リース組成物を封入して潤滑したものであり、転がり軸
受そのものとしては、公知の種々の構造の転がり軸受が
全て採用可能である。このような本発明の転がり軸受
は、潤滑したグリース組成物の作用によって優れた音響
性能と耐フレッチング性を発揮する。
リース組成物を封入して潤滑したものであり、転がり軸
受そのものとしては、公知の種々の構造の転がり軸受が
全て採用可能である。このような本発明の転がり軸受
は、潤滑したグリース組成物の作用によって優れた音響
性能と耐フレッチング性を発揮する。
【0021】次に、本発明の更に具体的な実施例を説明
する。
する。
【0022】[実施例1〜5]下記の表1に示す増ちょ
う剤と基油と添加剤とを、表1の実施例1〜5に示す割
合でそれぞれ混合、攪拌して、実施例1〜5のグリース
組成物をそれぞれ調製した。そして、各グリース組成物
について混和ちょう度を測定したところ、表1に示す通
りであった。
う剤と基油と添加剤とを、表1の実施例1〜5に示す割
合でそれぞれ混合、攪拌して、実施例1〜5のグリース
組成物をそれぞれ調製した。そして、各グリース組成物
について混和ちょう度を測定したところ、表1に示す通
りであった。
【0023】次いで、各グリース組成物について、以下
の試験条件を採用して耐フレッチング性試験を行った。
その結果を表1に示す。尚、表1の耐フレッチング試験
の欄において、◎は耐フレッチング摩耗の防止効果が大
きいことを、○は耐フレッチング摩耗の防止効果がある
ことを、×は耐フレッチング摩耗の防止効果が劣ること
を表す。
の試験条件を採用して耐フレッチング性試験を行った。
その結果を表1に示す。尚、表1の耐フレッチング試験
の欄において、◎は耐フレッチング摩耗の防止効果が大
きいことを、○は耐フレッチング摩耗の防止効果がある
ことを、×は耐フレッチング摩耗の防止効果が劣ること
を表す。
【0024】(耐フレッチング性の試験条件) 使用した玉軸受: 深溝玉軸受(内径5mm、外径13
mm、幅4mm) 外輪揺動角 : 1〜5° 揺動周波数 : 5〜50Hz 揺動回数 : 10000回 アキシャル荷重: 14.7N 温度 : 25℃
mm、幅4mm) 外輪揺動角 : 1〜5° 揺動周波数 : 5〜50Hz 揺動回数 : 10000回 アキシャル荷重: 14.7N 温度 : 25℃
【0025】更に、実施例1〜5の各グリース組成物に
ついて、以下の試験条件を採用して玉軸受の音響寿命試
験を行った。その結果を表1に併せて示す。尚、表1の
音響寿命試験の欄において、◎は玉軸受の音響上昇が殆
どないことを、○は玉軸受の音響上昇が少しあること
を、×は玉軸受の音響上昇が大きいことを表す。
ついて、以下の試験条件を採用して玉軸受の音響寿命試
験を行った。その結果を表1に併せて示す。尚、表1の
音響寿命試験の欄において、◎は玉軸受の音響上昇が殆
どないことを、○は玉軸受の音響上昇が少しあること
を、×は玉軸受の音響上昇が大きいことを表す。
【0026】(音響寿命の試験条件) 使用した玉軸受: 深溝玉軸受(内径5mm、外径13
mm、幅4mm) 外輪回転数 : 5400rpm 時間 : 1000h 予圧 : 14.7N 周囲温度 : 70℃
mm、幅4mm) 外輪回転数 : 5400rpm 時間 : 1000h 予圧 : 14.7N 周囲温度 : 70℃
【0027】[比較例1〜3]下記の表1に示す増ちょ
う剤と基油と添加剤とを、表1の比較例1〜3に示す割
合でそれぞれ混合、攪拌して、比較例1〜3のグリース
組成物をそれぞれ調製した。そして、各グリース組成物
について、混和ちょう度を測定すると共に、上記実施例
1〜5と同じ試験条件を採用して耐フレッチング性試験
と音響寿命試験を行った。その結果を表1に併記する。
う剤と基油と添加剤とを、表1の比較例1〜3に示す割
合でそれぞれ混合、攪拌して、比較例1〜3のグリース
組成物をそれぞれ調製した。そして、各グリース組成物
について、混和ちょう度を測定すると共に、上記実施例
1〜5と同じ試験条件を採用して耐フレッチング性試験
と音響寿命試験を行った。その結果を表1に併記する。
【0028】
【表1】
【0029】この表1を見ると、増ちょう剤としてリチ
ウム石鹸のみを含有し、脂肪族/脂環族ジウレアを含有
していない比較例1,3のグリース組成物は、音響寿命
は良いけれども耐フレッチング性に劣っており、また、
増ちょう剤として脂肪族/脂環族ジウレアのみを含有
し、リチウム石鹸を含有していない比較例2のグリース
組成物は、耐フレッチング性には優れるけれども音響寿
命に劣っている。これに対し、増ちょう剤として脂肪族
/脂環族ジウレアとリチウム石鹸との混合物を使用した
実施例1〜5のグリース組成物は、耐フレッチング性も
音響寿命も優秀又は良好であり、本発明の目的を達成し
ていることが判る。そして、これら実施例1〜5のグリ
ース組成物はいずれも、増ちょう剤中のジウレアの含有
率が20〜80重量%の範囲にあり、このことから、ジ
ウレアの含有率を20〜80重量%にすれば、確実に耐
フレッチング性と音響性能を高める得ることが判る。
ウム石鹸のみを含有し、脂肪族/脂環族ジウレアを含有
していない比較例1,3のグリース組成物は、音響寿命
は良いけれども耐フレッチング性に劣っており、また、
増ちょう剤として脂肪族/脂環族ジウレアのみを含有
し、リチウム石鹸を含有していない比較例2のグリース
組成物は、耐フレッチング性には優れるけれども音響寿
命に劣っている。これに対し、増ちょう剤として脂肪族
/脂環族ジウレアとリチウム石鹸との混合物を使用した
実施例1〜5のグリース組成物は、耐フレッチング性も
音響寿命も優秀又は良好であり、本発明の目的を達成し
ていることが判る。そして、これら実施例1〜5のグリ
ース組成物はいずれも、増ちょう剤中のジウレアの含有
率が20〜80重量%の範囲にあり、このことから、ジ
ウレアの含有率を20〜80重量%にすれば、確実に耐
フレッチング性と音響性能を高める得ることが判る。
【0030】また、実施例2と実施例4を対比すれば、
ペンタエリスリトールエステルなどのポリオールエステ
ルは、セバシン酸ジ−2−エチルヘキシルなどの脂肪族
二塩基酸エステルよりも有効であることが判る。更に、
実施例1と実施例3を対比すれば、増ちょう剤中にジウ
レアを80重量%と多量に含有する実施例1のグリース
組成物は耐フレッチング性の方が優れているのに対し、
増ちょう剤中にリチウム石鹸を80重量%と多量に含有
する実施例3のグリース組成物は音響寿命の方が優れて
おり、このことから、ジウレアは耐フレッチング性の向
上に、リチウム石鹸は音響性能の向上に有効に作用する
ことが判る。
ペンタエリスリトールエステルなどのポリオールエステ
ルは、セバシン酸ジ−2−エチルヘキシルなどの脂肪族
二塩基酸エステルよりも有効であることが判る。更に、
実施例1と実施例3を対比すれば、増ちょう剤中にジウ
レアを80重量%と多量に含有する実施例1のグリース
組成物は耐フレッチング性の方が優れているのに対し、
増ちょう剤中にリチウム石鹸を80重量%と多量に含有
する実施例3のグリース組成物は音響寿命の方が優れて
おり、このことから、ジウレアは耐フレッチング性の向
上に、リチウム石鹸は音響性能の向上に有効に作用する
ことが判る。
【0031】
【発明の効果】以上の説明から明らかなように、本発明
のグリース組成物は、転がり軸受の音響性能と耐フレッ
チング性を同時に向上させることができるといった顕著
な効果を奏し、高い音響性能と耐フレッチング性が要求
される情報機器類のスピンドルモータの転がり軸受等に
好適に使用し得るものである。そして、このグリース組
成物で潤滑した本発明の転がり軸受は、グリース組成物
の作用によって優れた音響性能と耐フレッチング性を発
揮するといった効果を奏する。
のグリース組成物は、転がり軸受の音響性能と耐フレッ
チング性を同時に向上させることができるといった顕著
な効果を奏し、高い音響性能と耐フレッチング性が要求
される情報機器類のスピンドルモータの転がり軸受等に
好適に使用し得るものである。そして、このグリース組
成物で潤滑した本発明の転がり軸受は、グリース組成物
の作用によって優れた音響性能と耐フレッチング性を発
揮するといった効果を奏する。
フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) C10M 117/02 C10M 117/02 117/04 117/04 F16C 33/66 F16C 33/66 Z // C10N 10:02 C10N 10:02 30:00 30:00 Z 40:02 40:02 50:10 50:10 (72)発明者 伊藤 奈歩 大阪府大阪市中央区南船場三丁目5番8号 光洋精工株式会社内 (72)発明者 谷口 陽三 大阪府大阪市中央区南船場三丁目5番8号 光洋精工株式会社内 Fターム(参考) 3J101 AA01 EA63 FA01 FA35 GA53 4H104 BA07A BB17B BB19B BB33A BB34A BE13B CA05A FA01 LA20 PA01 QA18
Claims (8)
- 【請求項1】基油と増ちょう剤を主成分とするグリース
組成物において、増ちょう剤がウレア化合物とリチウム
石鹸との混合物より成ることを特徴とするグリース組成
物。 - 【請求項2】増ちょう剤中のウレア化合物の含有率が2
0〜80重量%である請求項1に記載のグリース組成
物。 - 【請求項3】ウレア化合物が、アルキル基又はシクロヘ
キシル基を末端基とするジウレア化合物である請求項1
又は請求項2に記載のグリース組成物。 - 【請求項4】ジウレア化合物のジイソシアネート成分が
4,4′−ジフェニルメタンジイソシアネートである請
求項3に記載のグリース組成物。 - 【請求項5】リチウム石鹸が、ステアリン酸リチウムを
必須成分とし、これに12−ヒドロキシステアリン酸リ
チウムを0〜50重量%含んだものである請求項1ない
し請求項4のいずれかに記載のグリース組成物。 - 【請求項6】基油が、脂肪族二塩基酸エステル及びポリ
オールエステルのいずれか一方又は双方のエステルと、
ポリ−α−オレフィンとからなるものである請求項1な
いし請求5のいずれかに記載のグリース組成物。 - 【請求項7】情報機器類のスピンドルモータの転がり軸
受に封入されて使用される請求項1ないし請求項5のい
ずれかに記載のグリース組成物。 - 【請求項8】請求項1ないし請求項7のいずれかに記載
のグリース組成物で潤滑したことを特徴とする転がり軸
受。