JP2000248238A - Adhesive sheet - Google Patents

Adhesive sheet

Info

Publication number
JP2000248238A
JP2000248238A JP11055829A JP5582999A JP2000248238A JP 2000248238 A JP2000248238 A JP 2000248238A JP 11055829 A JP11055829 A JP 11055829A JP 5582999 A JP5582999 A JP 5582999A JP 2000248238 A JP2000248238 A JP 2000248238A
Authority
JP
Japan
Prior art keywords
sheet
synthetic resin
colored coating
sensitive adhesive
resin sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP11055829A
Other languages
Japanese (ja)
Inventor
Toshiyuki Miyake
敏之 三宅
Kenji Asada
健次 麻田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sekisui Chemical Co Ltd
Original Assignee
Sekisui Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sekisui Chemical Co Ltd filed Critical Sekisui Chemical Co Ltd
Priority to JP11055829A priority Critical patent/JP2000248238A/en
Publication of JP2000248238A publication Critical patent/JP2000248238A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To obtain an adhesive sheet for decorative use, easy for small lot production, good in groundwork masking effect and adhesion, hard to be stuck with dust, and good in cuttability by using each specific acrylic urethane-based resin and urethane-based resin, or the like. SOLUTION: This adhesive sheet is obtained by laminating one side of a synthetic resin sheet with (A) 100 pts.wt. of an acrylic urethane-based resin 30-80 deg.C in glass transition temperature, (B) 4-30 pts.wt. of a urethane-based resin -50 to -5 deg.C in glass transition temperature and (C) a colored coating film layer comprising 0.5-50 pts.wt. of a pigment, and laminating the other side with a tack agent layer, wherein it is preferable that the component A is a reaction product from an acrylic polyol and a polyisocyanate compound in such a ratio that the functional group ratio of the formula satisfy 20-40, and the above synthetic resin sheet is white, and the above colored coating film layer is transparent.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【発明の属する技術分野】本発明は、装飾用途に好適な
粘着シートに関する。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pressure-sensitive adhesive sheet suitable for decorative applications.

【0002】[0002]

【従来の技術】従来から、着色された合成樹脂シート
(特に塩化ビニル系樹脂からなるシート)の一面に粘着
剤層が積層されている粘着シートが、装飾用途に様々な
分野で使用されている。
2. Description of the Related Art Conventionally, pressure-sensitive adhesive sheets in which a pressure-sensitive adhesive layer is laminated on one surface of a colored synthetic resin sheet (particularly a sheet made of a vinyl chloride resin) have been used in various fields for decorative applications. .

【0003】通常、着色された塩化ビニル系樹脂シート
は、塩化ビニル系樹脂、顔料、可塑剤、熱安定剤などの
混合物を加熱混練してシート状に成形するカレンダー法
もしくは押出法や、上記混合物を有機溶剤に分散させた
分散溶液(オルガノゾルと呼ばれる)を離型処理された
工程紙上に塗布乾燥し、加熱融着してシート状に成形す
るゾルキャスティング法などにより製造されている。
[0003] Usually, a colored vinyl chloride resin sheet is prepared by calendering or extruding a mixture of a vinyl chloride resin, a pigment, a plasticizer, a heat stabilizer and the like by heating and kneading the mixture into a sheet, or the above-mentioned mixture. Is produced by a sol casting method or the like in which a dispersion solution (referred to as an organosol) in which is dispersed in an organic solvent is applied onto a process paper subjected to a release treatment, dried and heated and fused to form a sheet.

【0004】最近では、看板などの被着体の材質や色も
様々であり、これに貼付される装飾用粘着シートの色も
多品種準備しておく必要が出てきているが、上述したよ
うな塩化ビニル系樹脂に顔料を混合しシート状に成形す
る方法では、1色当たりの製造量が非常に大きくなり経
済的でないといった問題点があり、小ロット化への対応
が望まれている。
Recently, materials and colors of adherends such as signboards are various, and it is necessary to prepare a variety of colors for decorative adhesive sheets to be attached thereto. The method of mixing a vinyl chloride resin with a pigment and forming the same into a sheet shape has a problem that the production amount per color is extremely large and it is not economical, and it is desired to cope with a small lot.

【0005】これに対して、最近では下地として単色の
塩化ビニル系樹脂シートを上述のいずれかの方法で予め
作り、この表面に様々な色の着色塗膜層を形成すること
により小ロット化及び多品種化を可能にし、多色に対応
しようという動きが見られる。
On the other hand, recently, a single-color vinyl chloride resin sheet is prepared in advance as a base by any of the above-described methods, and a colored coating layer of various colors is formed on the surface to reduce the lot size, thereby reducing the number of lots. There is a movement to make it possible to increase the variety of products and to support multiple colors.

【0006】[0006]

【発明が解決しようとする課題】しかしながら、通常の
塗膜層は合成樹脂シートとの密着性を十分なものとする
ために柔軟なものであることが必要だが、この目的で樹
脂成分のガラス転移温度を低くすると塗膜層にタック感
が現れ、塵や埃が付着し易く、取り扱い性が低下すると
いった問題点があった。
However, the ordinary coating layer needs to be flexible in order to have sufficient adhesion to the synthetic resin sheet, but for this purpose the glass transition of the resin component is required. When the temperature is lowered, there is a problem that a tackiness appears in the coating layer, dust and dirt are easily attached, and the handling property is reduced.

【0007】本発明は、上記問題点に鑑みてなされたも
のであり、その目的は粘着シートの製造に対して小ロッ
ト化が容易であり、被着体である下地の隠蔽性が良好で
あり、更に塗膜層と合成樹脂シートとの密着性が良好で
あり、塗料層にタック感がないため塵や埃が付着し難
く、引裂強度が高いためにカット性が良好である装飾用
途に好適な粘着シートを提供することにある。
SUMMARY OF THE INVENTION The present invention has been made in view of the above problems, and an object of the present invention is to make it easy to reduce the lot for the production of an adhesive sheet and to provide a good concealing property for a substrate as an adherend. In addition, the adhesiveness between the coating layer and the synthetic resin sheet is good, there is no tackiness in the paint layer, and it is difficult for dust and dirt to adhere, and the tear strength is high, so it is suitable for decorative applications with good cutability. To provide a flexible adhesive sheet.

【0008】[0008]

【課題を解決するための手段】本発明の粘着シートは、
合成樹脂シートの一面に、ガラス転移温度が30〜80
℃であるアクリルウレタン系樹脂100重量部、ガラス
転移温度が−50〜−5℃であるウレタン系樹脂5〜3
0重量部及び顔料0.5〜50重量部からなる着色塗膜
層が積層され、もう一面に粘着剤層が積層されているこ
とを特徴とするものである。
Means for Solving the Problems The pressure-sensitive adhesive sheet of the present invention comprises:
A glass transition temperature of 30 to 80 on one surface of the synthetic resin sheet
100 parts by weight of an acrylic urethane resin having a glass transition temperature of -50 to -5 ° C.
A colored coating layer comprising 0 parts by weight and 0.5 to 50 parts by weight of a pigment is laminated, and an adhesive layer is laminated on the other side.

【0009】合成樹脂シート 本発明で使用される合成樹脂シートを構成する合成樹脂
としては、例えば、塩化ビニル系樹脂;低密度ポリエチ
レン、中密度ポリエチレン、高密度ポリエチレン、直鎖
状低密度ポリエチレンなどのポリエチレン;ポリプロピ
レン;エチレン−酢酸ビニル共重合体、エチレン−エチ
ルアクリレート共重合体、エチレン−α−オレフィン共
重合体などのエチレン系共重合体などが挙げられ、ま
た、これらの合成樹脂にスチレン系樹脂などのエラスト
マーを混合したものも挙げられるが、可塑剤などの添加
により柔軟性の付与が容易であるという理由から塩化ビ
ニル系樹脂が好適である。
Synthetic Resin Sheet The synthetic resin constituting the synthetic resin sheet used in the present invention includes, for example, vinyl chloride resin; low-density polyethylene, medium-density polyethylene, high-density polyethylene, linear low-density polyethylene and the like. Polyethylene; polypropylene; ethylene-based copolymers such as ethylene-vinyl acetate copolymer, ethylene-ethyl acrylate copolymer, and ethylene-α-olefin copolymer; and styrene-based resins as synthetic resins. Examples thereof include those obtained by mixing an elastomer such as a vinyl chloride resin, but a vinyl chloride resin is preferable because it is easy to impart flexibility by adding a plasticizer or the like.

【0010】また、上記合成樹脂シートは、異なる合成
樹脂を複数種均一混合した混合樹脂からなるシートでも
よいし、異なる合成樹脂からなるシートを複数積層した
積層シートでもよい。
The synthetic resin sheet may be a sheet made of a mixed resin obtained by uniformly mixing a plurality of different synthetic resins, or may be a laminated sheet formed by stacking a plurality of sheets made of different synthetic resins.

【0011】以下に、合成樹脂として、主に塩化ビニル
系樹脂を使用した場合について中心に説明する。合成樹
脂には、シートへの成形性やシート物性などを損わない
範囲において他の添加物が添加されてもよく、例えば、
可塑剤、顔料、紫外線吸収剤、熱安定剤などが挙げられ
る。
The following mainly describes the case where a vinyl chloride resin is mainly used as the synthetic resin. Other additives may be added to the synthetic resin within a range that does not impair the formability of the sheet or the sheet properties, for example,
Plasticizers, pigments, ultraviolet absorbers, heat stabilizers and the like can be mentioned.

【0012】上記可塑剤は、合成樹脂シートに柔軟性を
付与する目的で添加されるものであり、例えば、フタル
酸ジオクチル、フタル酸ジイソノニル、フタル酸オクチ
ルデシル、フタル酸ジイソデシルなどのフタル酸系可塑
剤、アジピン酸ジ−2−エチルヘキシル、アジピン酸ジ
イソノニル、アジピン酸ジイソデシルなどのアジピン酸
系可塑剤、アゼライン酸ジ−2−エチルヘキシル、セバ
シン酸ジ−2−エチルヘキシル、リン酸トリクレジル、
リン酸トリキシリル、リン酸トリブチル、リン酸トリ−
2−エチルヘキシル、リン酸オクチルジフェニル、塩素
化パラフィン、塩素化脂肪酸エステル、エポキシ化大豆
油などが挙げられる。
The plasticizer is added for the purpose of imparting flexibility to the synthetic resin sheet. For example, phthalic acid-based plasticizers such as dioctyl phthalate, diisononyl phthalate, octyldecyl phthalate and diisodecyl phthalate are used. Adipic acid plasticizers such as di-2-ethylhexyl adipate, diisononyl adipate, diisodecyl adipate, di-2-ethylhexyl azelate, di-2-ethylhexyl sebacate, tricresyl phosphate,
Trixylyl phosphate, tributyl phosphate, tri-phosphate
2-ethylhexyl, octyldiphenyl phosphate, chlorinated paraffin, chlorinated fatty acid esters, epoxidized soybean oil, and the like.

【0013】可塑剤の添加量は、少なくなると十分な可
塑化効果が得られず、三次元曲面等への貼付性の低い粘
着シートになり、多くなると粘着剤中に移行し、粘着物
性が経時で変化することがあるため、上記合成樹脂10
0重量部に対して10〜200重量部が好ましく、より
好ましくは20〜100重量部である。
When the amount of the plasticizer is too small, a sufficient plasticizing effect cannot be obtained, resulting in an adhesive sheet having a low sticking property to a three-dimensional curved surface or the like. In the synthetic resin 10
The amount is preferably from 10 to 200 parts by weight, more preferably from 20 to 100 parts by weight, based on 0 parts by weight.

【0014】上記顔料としては、例えば、アゾ系、フタ
ロシアニン系、スレン系、染料レーキ系、キナクリドン
系、ジオキサジン系などの有機顔料、酸化チタンなどの
酸化物系、クロム酸モリブデン酸系、硫化物・セレン化
物系、フェロシアン化物系、炭酸カルシウムなどの無機
顔料などが挙げられるが、被着体の色を隠蔽し、後述す
る着色塗膜層の彩度を向上させるという点で白色顔料が
好適であり、該白色顔料の中でも特に酸化チタンが好適
である。
Examples of the pigment include organic pigments such as azo, phthalocyanine, sulene, dye lake, quinacridone, and dioxazine; oxides such as titanium oxide; molybdate chromate; Selenide-based, ferrocyanide-based, inorganic pigments such as calcium carbonate and the like are mentioned, but a white pigment is preferable in that it conceals the color of the adherend and improves the saturation of the colored coating layer described later. Of these white pigments, titanium oxide is particularly preferred.

【0015】また、上記合成樹脂シートを白色に着色し
ておくことにより、その表面に積層される着色塗膜層の
色が映え、着色塗膜層の色を変更することにより粘着シ
ートの色調を適宜変更することができる。つまり、1種
類の白色の合成樹脂シートを大量生産しておき、この合
成樹脂シートの一面(装飾面)に様々な着色塗膜層を積
層することにより小ロット化を可能にでき、少量多品種
に対応できるという効果もある。
Further, by coloring the synthetic resin sheet white, the color of the colored coating layer laminated on the surface of the synthetic resin sheet shines, and the color tone of the adhesive sheet is changed by changing the color of the colored coating layer. It can be changed as appropriate. In other words, one type of white synthetic resin sheet is mass-produced, and various colored coating layers are laminated on one surface (decorative surface) of the synthetic resin sheet, so that a small lot can be realized. There is also an effect that it can respond to.

【0016】酸化チタンとしては、下地隠蔽性と高彩度
化が良好であるという点でルチル型結晶からなり、かつ
平均粒径0.01〜1μmのものが好適である。また、
合成樹脂中での分散性を向上させる目的で酸化チタン粒
子の表面が、例えばアルミニウム、シリカ、有機物など
で処理されていてもよい。
Titanium oxide is preferably a rutile type crystal having an average particle size of 0.01 to 1 μm in terms of good base concealing property and high chroma. Also,
For the purpose of improving the dispersibility in the synthetic resin, the surface of the titanium oxide particles may be treated with, for example, aluminum, silica, an organic substance, or the like.

【0017】酸化チタンの添加量は、少なくなると隠蔽
性が低下し被着体の色を透過するため、着色塗膜層の色
がくすんだりして彩度が十分に得られにくくなり、多く
なると合成樹脂シートの引裂強度が低下し、取り扱いに
くくなるため、合成樹脂100重量部に対して5〜40
重量部が好ましく、より好ましくは8〜35重量部であ
り、特に好ましくは10〜30重量部である。
When the addition amount of titanium oxide is small, the concealing property is reduced and the color of the adherend is transmitted, so that the color of the colored coating layer becomes dull and it becomes difficult to obtain sufficient saturation, and when the addition amount is large, the addition amount is increased. Since the tear strength of the synthetic resin sheet is reduced and it becomes difficult to handle, 5 to 40 parts by weight of the synthetic resin 100 parts by weight.
Part by weight is preferred, more preferably 8 to 35 parts by weight, and particularly preferably 10 to 30 parts by weight.

【0018】上記紫外線吸収剤としては、例えば、サリ
チル酸エステル系紫外線吸収剤、ベンゾフェノン系紫外
線吸収剤、ベンゾトリアゾール系紫外線吸収剤、シアノ
アクリレート系紫外線吸収剤などが挙げられる。上記熱
安定剤としては、例えば、金属石鹸系熱安定剤、有機ス
ズ系熱安定剤、鉛系熱安定剤、アンチモン系熱安定剤、
非金属熱安定剤などが挙げられる。また、その他の充填
剤も添加可能であり、例えば、タルク(塩基性ケイ酸マ
グネシウム)、カオリン(ケイ酸アルミニウム)、シリ
カなどが挙げられる。
Examples of the ultraviolet absorber include salicylate-based ultraviolet absorbers, benzophenone-based ultraviolet absorbers, benzotriazole-based ultraviolet absorbers, and cyanoacrylate-based ultraviolet absorbers. As the heat stabilizer, for example, metal soap-based heat stabilizer, organotin-based heat stabilizer, lead-based heat stabilizer, antimony-based heat stabilizer,
Non-metallic heat stabilizers and the like can be mentioned. Further, other fillers can be added, and examples thereof include talc (basic magnesium silicate), kaolin (aluminum silicate), and silica.

【0019】合成樹脂シートの製造方法としては、例え
ば、塩化ビニル系樹脂シートの場合は樹脂組成物を加熱
混練してシート状に成形するカレンダー法もしくは樹脂
組成物を有機溶剤に分散させた分散溶液を離型処理され
た工程紙上に塗布乾燥し、加熱融着してシート状に成形
するゾルキャスティング法などが挙げられ、オレフィン
系樹脂シートの場合は押出成形法などが挙げられる。ま
た、塩化ビニル系樹脂シートの場合は、シート自体に成
形時の応力が残りにくいという点でゾルキャスティング
法が好適である。
As a method for producing the synthetic resin sheet, for example, in the case of a vinyl chloride resin sheet, a calendering method in which the resin composition is heated and kneaded to form a sheet, or a dispersion solution in which the resin composition is dispersed in an organic solvent. Is applied and dried on a process paper subjected to a release treatment, and then heated and fused to form a sheet. For example, in the case of an olefin resin sheet, an extrusion molding method is used. In the case of a vinyl chloride resin sheet, the sol-casting method is preferred in that stress during molding hardly remains in the sheet itself.

【0020】上記ゾルキャスティング法に使用される有
機溶剤としては、例えば、エチルアルコール、イソプロ
ピルアルコール、ベンゼン、トルエン、キシレン、アセ
トン、メチルエチルケトン、メチルイソブチルケトン、
ジイソブチルケトン、メチルアミルケトン、テトラヒド
ロフラン、シクロヘキサノンなどが挙げられるが、これ
らに限定されるものではない。
Examples of the organic solvent used in the sol casting method include ethyl alcohol, isopropyl alcohol, benzene, toluene, xylene, acetone, methyl ethyl ketone, methyl isobutyl ketone,
Examples include, but are not limited to, diisobutyl ketone, methyl amyl ketone, tetrahydrofuran, cyclohexanone, and the like.

【0021】上記分散溶液の濃度は、低いと乾燥後に合
成樹脂シート中に溶剤が残り、粘着剤層とのアンカー性
が低下することがあり、高いと粘度が高くなり成形性が
低下し、表面荒れなどの外観不良が発生することがある
ため、30〜100%が好ましく、より好ましくは40
〜70%である。
If the concentration of the above-mentioned dispersion solution is low, the solvent remains in the synthetic resin sheet after drying, and the anchoring property with the pressure-sensitive adhesive layer may decrease. Since appearance defects such as roughness may occur, the content is preferably 30 to 100%, more preferably 40 to 100%.
~ 70%.

【0022】上記合成樹脂シートの厚さは、薄くなると
コシがなくなり貼付作業性が低下することがあり、厚く
なるとシートの剛性が高くなり、コルゲート板などの三
次元曲面への追従性が得られにくくなるため、30〜1
50μmが好ましく、より好ましくは40〜100μm
である。
When the thickness of the synthetic resin sheet is reduced, the stiffness is reduced and the workability of the bonding may be reduced. When the thickness is increased, the rigidity of the sheet is increased and the followability to a three-dimensional curved surface such as a corrugated plate is obtained. 30-1
50 μm is preferred, and more preferably 40 to 100 μm
It is.

【0023】また、上記合成樹脂シート表面には、合成
樹脂シートと後述する着色塗膜層もしくは粘着剤層との
アンカー性を向上させる目的で表面処理を行ってもよ
く、例えば、コロナ放電処理、下塗り剤の塗布などが挙
げられる。
The surface of the synthetic resin sheet may be subjected to a surface treatment for the purpose of improving the anchoring property between the synthetic resin sheet and a colored coating layer or a pressure-sensitive adhesive layer described later, for example, a corona discharge treatment, Application of an undercoat agent and the like can be mentioned.

【0024】着色塗膜層 本発明で使用される着色塗膜層は、(1)ガラス転移温
度が30〜80℃であるアクリルウレタン系樹脂100
重量部、(2)ガラス転移温度が−50〜−5℃である
ウレタン系樹脂5〜30重量部及び(3)顔料0.5〜
50重量部からなる。
Colored Coating Layer The colored coating layer used in the present invention comprises (1) an acrylic urethane resin 100 having a glass transition temperature of 30 to 80 ° C.
Parts by weight, (2) 5 to 30 parts by weight of a urethane resin having a glass transition temperature of -50 to -5 ° C, and (3) pigment 0.5 to
Consists of 50 parts by weight.

【0025】(1)アクリルウレタン系樹脂 上記アクリルウレタン系樹脂は、分子内に多数の水酸基
を有するアクリルポリオールをポリイソシアネート化合
物で網目状に架橋させて得られるものであり、通常は、
上記アクリルポリオールを含有する溶液とポリイソシア
ネート化合物を含有する溶液を混合してポットライフの
制限内で使用され、硬化後にアクリルウレタン系樹脂と
なる。
(1) Acrylic urethane-based resin The acrylic urethane-based resin is obtained by cross-linking an acrylic polyol having a large number of hydroxyl groups in a molecule thereof with a polyisocyanate compound.
The solution containing the acrylic polyol and the solution containing the polyisocyanate compound are mixed and used within the limit of pot life, and after curing, it becomes an acrylic urethane-based resin.

【0026】更に具体的に言うと、上記着色塗膜層は、
アクリルポリオール、顔料及び有機溶剤からなる主材塗
料の溶液に、上記アクリルポリオールを網目状に架橋可
能な上記ポリイソシアネート化合物及び有機溶剤からな
る硬化剤の溶液を添加し、十分に混合した後、塗布乾燥
することにより形成される。
More specifically, the colored coating layer comprises:
Acrylic polyol, a solution of a curing agent consisting of a polyisocyanate compound and an organic solvent capable of cross-linking the acrylic polyol into a network, to a solution of a main coating material consisting of a pigment and an organic solvent, and after sufficient mixing, coating It is formed by drying.

【0027】上記アクリルポリオールは、アクリル系ポ
リマーからなる主鎖に多数の水酸基が側鎖として化合し
たものであり、着色塗膜層の柔軟性を向上させる効果が
あり、通常はアクリル系モノマーと水酸基含有ビニルモ
ノマーとを共重合することや、分子内に水酸基を有する
水酸基含有アクリル系モノマーを1種以上(共)重合す
ることにより得られる。
The acrylic polyol is obtained by combining a large number of hydroxyl groups as side chains in the main chain of an acrylic polymer and has the effect of improving the flexibility of the colored coating layer. It can be obtained by copolymerizing with a vinyl monomer containing a polymer or by (co) polymerizing one or more kinds of hydroxyl group-containing acrylic monomers having a hydroxyl group in a molecule.

【0028】有機溶剤は、アクリルポリオール、後述す
る顔料及びポリイソシアネート化合物などの構成成分を
均一に混合し易くすると同時に、粘度調整して塗膜層の
厚さを調整し易くする目的で添加されるものであるが、
ポリイソシアネート化合物中のイソシアネート基と反応
可能な活性水素を有するものは原則として使用できな
い。
The organic solvent is added for the purpose of facilitating uniform mixing of components such as an acrylic polyol, a pigment and a polyisocyanate compound to be described later, and also facilitating the adjustment of viscosity to easily adjust the thickness of the coating layer. Although
Those having active hydrogen capable of reacting with isocyanate groups in the polyisocyanate compound cannot be used in principle.

【0029】使用可能な有機溶剤としては、例えば、ベ
ンゼン、トルエン、キシレン、アセトン、メチルエチル
ケトン、メチルイソブチルケトン、ジイソブチルケト
ン、メチルアミルケトン、テトラヒドロフラン、シクロ
ヘキサノンなどが挙げられるが、これらに限定されるも
のではない。
Examples of usable organic solvents include benzene, toluene, xylene, acetone, methyl ethyl ketone, methyl isobutyl ketone, diisobutyl ketone, methyl amyl ketone, tetrahydrofuran, cyclohexanone and the like. Absent.

【0030】上記構成成分を均一に混合した後での有機
溶剤の全添加量は、少ないと塗料溶液の粘度が高くな
り、塗工時にスジが発生することがあり、多いと十分に
乾燥できないことがあるため、アクリルポリオール及び
ポリイソシアネート化合物の合計量100重量部に対し
て、20〜100重量部が好ましく、より好ましくは3
0〜70重量部である。
If the total amount of the organic solvent added after uniformly mixing the above-mentioned constituents is small, the viscosity of the coating solution becomes high, and streaks may be generated during coating. Therefore, the amount is preferably 20 to 100 parts by weight, more preferably 3 to 100 parts by weight based on the total amount of the acrylic polyol and the polyisocyanate compound.
0 to 70 parts by weight.

【0031】上記ポリイソシアネート化合物は、分子内
に2個以上のイソシアネート基を有するものであれば特
に限定されるものではなく、例えば、トリレンジイソシ
アネート(TDI)、ジフェニルメタンジイソシアネー
ト(MDI)、1,5−ナフタレンジイソシアネート
(NDI)、トリジンジイソシアネート(TODI)、
ヘキサメチレンジイソシアネート(HDI)、イソホロ
ンジイソシアネート(IPDI)、p−フェニレンジイ
ソシアネート、トランスシクロヘキサン1,4−ジイソ
シアネート、キシリレンジイソシアネート(XDI)、
水添キシリレンジイソシアネート、リジンジイソシアネ
ート(LDI)、テトラメチルキシレンジイソシアネー
ト(TMXDI)、トリフェニルメタントリイソシアネ
ート、トリス(イソシアネートフェニル)チオホスフェ
ート、リジンエステルトリイソシアネート、ウンデカン
トリイソシアネートなどのポリイソシアネート類、及び
これらのトリメチロールプロパンのアダクト型、ビュレ
ット型、イソシアヌレート型などが挙げられるが、特に
限定されるものではない。
The polyisocyanate compound is not particularly limited as long as it has two or more isocyanate groups in the molecule. For example, tolylene diisocyanate (TDI), diphenylmethane diisocyanate (MDI), 1,5 -Naphthalene diisocyanate (NDI), tolidine diisocyanate (TODI),
Hexamethylene diisocyanate (HDI), isophorone diisocyanate (IPDI), p-phenylene diisocyanate, transcyclohexane 1,4-diisocyanate, xylylene diisocyanate (XDI),
Polyisocyanates such as hydrogenated xylylene diisocyanate, lysine diisocyanate (LDI), tetramethyl xylene diisocyanate (TMXDI), triphenylmethane triisocyanate, tris (isocyanate phenyl) thiophosphate, lysine ester triisocyanate, undecane triisocyanate, and the like Adduct type, buret type, isocyanurate type and the like of trimethylolpropane, but are not particularly limited thereto.

【0032】アクリルウレタン系樹脂を構成しているア
クリルポリオールに由来する水酸基と、ポリイソシアネ
ート化合物に由来するイソシアネート基の濃度の比率
は、低くなっても高くなっても、引裂強度に影響を与え
ることから、アクリルポリオールとポリイソシアネート
化合物は、下式
The ratio of the concentration of the hydroxyl group derived from the acrylic polyol constituting the acrylic urethane resin to the concentration of the isocyanate group derived from the polyisocyanate compound may affect the tear strength even if the ratio is low or high. From the formula, acrylic polyol and polyisocyanate compound

【0033】[0033]

【化2】 Embedded image

【0034】で表される官能基比率が20〜40を満た
すように混合されなければならない。また、好ましくは
25〜35である。
Must be mixed so that the functional group ratio represented by the formula satisfies 20 to 40. Moreover, it is preferably 25 to 35.

【0035】上記アクリルウレタン系樹脂を構成するこ
とができる塗料の市販品としては、例えば、「プラニッ
トU#700」、「プラニットU#750」、「プラニ
ットU#755」、「プラニットU#760」、「プラ
ニットU#780」、「プラニットU#901」、「プ
ラニットU#902」(以上、全て大日本塗料社製)、
「ソフレックス80」(関西ペイント社製)、「NAX
マイティラックG−II」、「NAX ベスタ」、「N
AX スペリオ」(以上、全て日本ペイント社製)など
が挙げられる。
Commercially available paints which can constitute the above-mentioned acrylic urethane resin include, for example, "Planit U # 700", "Planit U # 750", "Planit U # 755", "Planit U # 760". , "Planit U # 780", "Planit U # 901", "Planit U # 902" (all manufactured by Dainippon Paint Co., Ltd.),
"Soflex 80" (manufactured by Kansai Paint Co., Ltd.), "NAX
Mighty Lac G-II, NAX Vesta, N
AX Superior "(all manufactured by Nippon Paint Co., Ltd.).

【0036】上記アクリルウレタン系樹脂のガラス転移
温度は、低くなると粘着シートとしての引裂強度が高く
なりカット性が低下したり、着色塗膜層表面にタック感
が発現しブロッキングが発生することがあり、また高く
なると粘着シート全体の剛性が高くなり合成樹脂シート
との密着性が低下したり、曲面への接着性が低下するこ
とがあるため、30〜80℃に限定され、好ましくは4
0〜60℃である。
When the glass transition temperature of the acrylic urethane-based resin is low, the tear strength of the pressure-sensitive adhesive sheet is increased, so that the cuttability is reduced. When the temperature is increased, the rigidity of the entire pressure-sensitive adhesive sheet is increased, and the adhesiveness to the synthetic resin sheet may be reduced or the adhesiveness to a curved surface may be reduced.
0-60 ° C.

【0037】前述の主材塗料の溶液と硬化剤の溶液を混
合する方法は、特に限定されるものではないが、ポリイ
ソシアネート化合物が空気中の水分で失活することがあ
るため、機械的に高速でミキシングすることが好まし
い。
The method of mixing the solution of the main coating material and the solution of the curing agent is not particularly limited. However, since the polyisocyanate compound may be deactivated by the moisture in the air, it may be mechanically mixed. Mixing at high speed is preferred.

【0038】(2)ウレタン系樹脂 上記ウレタン系樹脂は、上記アクリルウレタン系樹脂と
の相溶性が良好であり、かつ着色塗膜層全体のガラス転
移温度を低下させ、柔軟性を付加することにより、耐衝
撃性を向上させ、かつ前述の合成樹脂シートに積層した
後の密着性を向上させる目的で添加されるものであり、
そのガラス転移温度は低くなると着色塗膜層表面にタッ
ク感が発現し埃等が付着しやすくなり、高くなると合成
樹脂シートとの密着性が低下することがあるため、−5
0〜−5℃に限定され、好ましくは−30〜−10℃で
ある。
(2) Urethane Resin The urethane resin has good compatibility with the acrylic urethane resin, lowers the glass transition temperature of the entire colored coating layer, and adds flexibility. It is added for the purpose of improving impact resistance, and improving adhesion after lamination on the above-mentioned synthetic resin sheet,
If the glass transition temperature is low, a tacky feeling appears on the surface of the colored coating film layer, and dust and the like tend to adhere, and if the glass transition temperature is high, the adhesion to the synthetic resin sheet may be reduced.
The temperature is limited to 0 to -5C, preferably -30 to -10C.

【0039】ウレタン系樹脂の添加量は、少なくなると
着色塗膜層の柔軟性が低下し、合成樹脂シートとの密着
性が低下することがあり、多くなると着色塗膜層表面に
タック感が発現することがあるため、アクリルウレタン
系樹脂100重量部に対して5〜30重量部が好まし
く、より好ましくは7〜25重量部である。
When the amount of the urethane resin is small, the flexibility of the colored coating layer is reduced and the adhesion to the synthetic resin sheet may be reduced. When the added amount is large, a tacky feeling appears on the surface of the colored coating layer. Therefore, the amount is preferably 5 to 30 parts by weight, more preferably 7 to 25 parts by weight, based on 100 parts by weight of the acrylic urethane resin.

【0040】(3)顔料 上記顔料としては、通常、合成樹脂の着色に使用される
顔料が略全て使用可能であり、例えば、アゾ系、フタロ
シアニン系、スレン系、染料レーキ系、キナクリドン
系、ジオキサジン系などの有機顔料、酸化物系、クロム
酸モリブデン酸系、硫化物・セレン化物系、フェロシア
ン化物系などの無機顔料などが挙げられ、所望の色調を
得る目的で混合されて用いられてもよい。
(3) Pigment As the pigment, generally all pigments used for coloring a synthetic resin can be used. For example, azo, phthalocyanine, sulene, dye lake, quinacridone, dioxazine Organic pigments, such as organic pigments, oxide pigments, molybdate chromate pigments, sulfides / selenide pigments, and inorganic pigments such as ferrocyanide pigments, and may be used in combination for the purpose of obtaining a desired color tone. Good.

【0041】顔料の添加量は、少なくなると十分な装飾
性が得られにくくなり、多くなると着色塗膜層の皮膜強
度が低下することがあるため、上記アクリルウレタン系
樹脂100重量部に対して、0.5〜50重量部に限定
され、好ましくは1〜40重量部である。
When the amount of the pigment is too small, it is difficult to obtain a sufficient decorative property, and when the amount is too large, the film strength of the colored coating film layer may be reduced. It is limited to 0.5 to 50 parts by weight, preferably 1 to 40 parts by weight.

【0042】また、顔料の添加量を制御することによ
り、着色塗膜層を着色透明にすることができる。これに
より彩度をより向上させることができる。着色透明にす
る際の顔料の添加量は、各顔料で異なるために一概に決
定できないが、例えば、キナクリドンレッドを使用した
場合は、アクリルウレタン系樹脂100重量部に対して
5〜15重量部程度が好ましく、シアニンブルーを使用
した場合は、0.5〜2重量部程度が好ましい。
Further, by controlling the amount of the pigment to be added, the colored coating layer can be colored and transparent. Thereby, the saturation can be further improved. The amount of the pigment to be colored and transparent cannot be determined unconditionally because it differs for each pigment, but, for example, when quinacridone red is used, about 5 to 15 parts by weight based on 100 parts by weight of the acrylic urethane resin. When cyanine blue is used, the amount is preferably about 0.5 to 2 parts by weight.

【0043】上記合成樹脂シートへの着色塗膜層の積層
方法は、特に限定されるものではなく、各種塗工方法が
可能であるが、例えば、バーコーター、リバースコータ
ー、スプレーガンコーター、ナイフコーター、ロータリ
ースクリーン、スクリーン印刷、グラビアコーター、キ
スコーターなどの方法が挙げられる。特に、塗料溶液の
タンクからコーター部までの配管の容量が少ないために
準備すべき塗料溶液が少なくてすみ、コーター部の洗浄
が容易であるために、色変えが容易であるという点で、
リバースコーター及びスプレーガンコーターが好適であ
る。
The method of laminating the colored coating layer on the synthetic resin sheet is not particularly limited, and various coating methods are possible. Examples thereof include a bar coater, a reverse coater, a spray gun coater, and a knife coater. , Rotary screen, screen printing, gravure coater, kiss coater and the like. In particular, since the volume of the pipe from the coating solution tank to the coater portion is small, only a small amount of coating solution needs to be prepared, and since the coater portion is easy to clean, the color change is easy.
Reverse coaters and spray gun coaters are preferred.

【0044】また、着色塗膜層の厚さは、薄くなると耐
候性が低下することがあり、厚くなると乾燥性が低下
し、残留溶剤により表面にタック感が発現しブロッキン
グが発生することがあるため、5〜100μmに限定さ
れ、好ましくは10〜70μm、より好ましくは12〜
50μmである。
When the thickness of the colored coating layer is reduced, the weather resistance may be reduced, and when the thickness is increased, the drying property may be reduced. Therefore, it is limited to 5 to 100 μm, preferably 10 to 70 μm, more preferably 12 to
50 μm.

【0045】また、上記着色塗膜層の耐候性を高めるこ
とにより、合成樹脂シートの耐候性を向上させることが
できる。具体的な方法としては、例えば、紫外線吸収
剤、ヒンダードアミン系光安定剤などを着色塗膜層に添
加する方法が挙げられる。上記紫外線吸収剤としては、
前述の紫外線吸収剤が全て挙げられる。
Further, by increasing the weather resistance of the colored coating film layer, the weather resistance of the synthetic resin sheet can be improved. As a specific method, for example, a method of adding an ultraviolet absorber, a hindered amine-based light stabilizer, or the like to the colored coating film layer is exemplified. As the above ultraviolet absorber,
All of the aforementioned ultraviolet absorbers are included.

【0046】また、上記ヒンダードアミン系光安定剤と
しては、例えば、 ・2,2,4,4−テトラメチルピペリジル−4−ベン
ゾエート、 ・ビス(2,2,6,6−テトラメチル−4−ピペリジ
ル)セバケート、 ・トリス(2,2,6,6−テトラメチル−4−ピペリ
ジル)ホスファイト、 ・1,3,8−トリアザ−7,7,9,9−テトラメチ
ル−3−n−オクチルスピロ[4,5]デカン−2,4
−ジオン、 ・1,2,3,4−テトラ(4−カルボニルオキシ−
2,2,6,6−テトラメチルピペリジル)−ブタン ・1,3,8−トリアザ−7,7,9,9−テトラメチ
ル−2,4−ジオキソ−スピロ[4,5]デカン ・トリ(4−アセトキシ−2,2,6,6−テトラメチ
ルピペリジル)アミン ・4−アセトキシ−2,2,6,6−テトラメチルピペ
リジル ・4−ステアロイルオキシ−2,2,6,6−テトラメ
チルピペリジル ・4−ベンジルオキシ−2,2,6,6−テトラメチル
ピペリジル ・4−フェニルカルバモイルオキシ−2,2,6,6−
テトラメチルピペリジルなどが挙げられる。
Examples of the hindered amine light stabilizer include: 2,2,4,4-tetramethylpiperidyl-4-benzoate, and bis (2,2,6,6-tetramethyl-4-piperidyl) ) Sebacate, tris (2,2,6,6-tetramethyl-4-piperidyl) phosphite, 1,3,8-triaza-7,7,9,9-tetramethyl-3-n-octylspiro [4,5] decane-2,4
-Dione, 1,2,3,4-tetra (4-carbonyloxy-
2,2,6,6-tetramethylpiperidyl) -butane 1,3,8-triaza-7,7,9,9-tetramethyl-2,4-dioxo-spiro [4,5] decane tri ( 4-acetoxy-2,2,6,6-tetramethylpiperidyl) amine 4-acetoxy-2,2,6,6-tetramethylpiperidyl 4-stearoyloxy-2,2,6,6-tetramethylpiperidyl・ 4-benzyloxy-2,2,6,6-tetramethylpiperidyl ・ 4-phenylcarbamoyloxy-2,2,6,6-
Tetramethylpiperidyl and the like.

【0047】粘着剤層 上記合成樹脂シートの内、着色塗膜層が積層されていな
い面には粘着剤層が積層される。粘着剤層に使用される
粘着剤としては特に限定されるものではないが、屋外で
の耐候性が良好であり、多くの被着体に対して良好な接
着性を示すという点でアクリル系粘着剤が好ましい。
Pressure-sensitive adhesive layer A pressure-sensitive adhesive layer is laminated on the surface of the synthetic resin sheet on which the colored coating layer is not laminated. The pressure-sensitive adhesive used for the pressure-sensitive adhesive layer is not particularly limited, but is an acrylic pressure-sensitive adhesive in that it has good weather resistance outdoors and exhibits good adhesion to many adherends. Agents are preferred.

【0048】粘着剤には、その物性を低下させない範囲
で、通常使用される他の添加物が添加されてもよく、例
えば、粘着付与樹脂、増量剤、紫外線吸収剤、酸化防止
剤、顔料などが挙げられる。
To the pressure-sensitive adhesive, other additives that are usually used may be added as long as the physical properties are not deteriorated. For example, tackifier resins, extenders, ultraviolet absorbers, antioxidants, pigments, etc. Is mentioned.

【0049】合成樹脂シートへの粘着剤層の積層方法
は、粘着剤溶液を直接塗布乾燥してもよいし、離型紙に
粘着剤溶液を塗布乾燥した後、転写により積層してもよ
い。
The method of laminating the pressure-sensitive adhesive layer on the synthetic resin sheet may be such that the pressure-sensitive adhesive solution is directly applied and dried, or the pressure-sensitive adhesive solution is coated and dried on release paper and then laminated by transfer.

【0050】尚、粘着剤層の厚さは、十分な粘着力を発
揮するものであれば特に限定されるものではなく、10
〜50μmが好ましい。粘着剤層に積層される離型紙と
しては、通常使用されている公知の離型紙が全て使用で
きる。
The thickness of the pressure-sensitive adhesive layer is not particularly limited as long as it exhibits a sufficient adhesive strength.
~ 50 μm is preferred. As the release paper laminated on the pressure-sensitive adhesive layer, all known release papers which are usually used can be used.

【0051】本発明の粘着シートは上記構成を有するも
のである。この粘着シートを具体的に装飾用途に使用す
る方法は特に限定されないが、例えば、装飾すべき被着
体全面に貼付する方法や、コンピューター制御されたカ
ッティングマシーンにより所望の図形や文字にカットさ
れた後、不要部分をカス取りし、アプリケーション粘着
テープを用いて被着体に転着する方法などが挙げられ
る。
The pressure-sensitive adhesive sheet of the present invention has the above constitution. The method of using this pressure-sensitive adhesive sheet specifically for decorative purposes is not particularly limited. Thereafter, a method of removing unnecessary portions and transferring the unnecessary portions to an adherend using an application adhesive tape may be used.

【0052】(作用)本発明は、主成分としてガラス転
移温度が30〜80℃のアクリルウレタン系樹脂を使用
しているために着色塗膜層の乾燥性が良好なものとなっ
ている。また、上記アクリルウレタン系樹脂に対してガ
ラス転移温度が−50〜−5℃のウレタン系樹脂を特定
量添加することにより乾燥性を低下させることなく、合
成樹脂シートへの密着性を向上させたものとなってい
る。更に、合成樹脂シートの他面に粘着剤層を積層する
ことにより、装飾すべき被着体への貼付作業性に優れた
ものとなる。
(Function) In the present invention, since the acrylic urethane resin having a glass transition temperature of 30 to 80 ° C. is used as a main component, the drying property of the colored coating film layer is good. Further, by adding a specific amount of a urethane-based resin having a glass transition temperature of -50 to -5 ° C to the acrylic urethane-based resin, the adhesion to the synthetic resin sheet was improved without lowering the drying property. It has become something. Furthermore, by laminating the pressure-sensitive adhesive layer on the other surface of the synthetic resin sheet, the workability of sticking to the adherend to be decorated is improved.

【0053】また、請求項2の発明では、アクリルウレ
タン系樹脂を構成しているアクリルポリオールに由来す
る水酸基とポリイソシアネート化合物に由来するイソシ
アネート基の比率を特定範囲に限定することにより、粘
着シートの引裂強度が良好なものとなっている。
In the second aspect of the present invention, the ratio of the hydroxyl group derived from the acrylic polyol constituting the acrylic urethane resin to the isocyanate group derived from the polyisocyanate compound is limited to a specific range. The tear strength is good.

【0054】更に、請求項3の発明では、合成樹脂シー
トに酸化チタン等の白色顔料を含有させることにより白
色シートとすることで、予め1種類の白色の合成樹脂シ
ートを大量生産しておき、この合成樹脂シートの一面
(装飾面)に様々な着色塗膜層をその都度積層すること
により小ロット化が可能となり、少量多品種に対応でき
る。また、白色シートにより被着体の下地色がしっかり
と隠蔽され、着色塗膜層の色が高彩度となり、装飾性の
良好なものとなる。
Further, according to the third aspect of the present invention, the white sheet is obtained by adding a white pigment such as titanium oxide to the synthetic resin sheet, so that one kind of white synthetic resin sheet is mass-produced in advance, By laminating various colored coating layers on one surface (decorative surface) of the synthetic resin sheet each time, it is possible to reduce the number of lots, and it is possible to cope with small lots and many kinds. In addition, the base sheet of the adherend is firmly hidden by the white sheet, the color of the colored coating layer becomes high in color, and the decorative property is good.

【0055】[0055]

【発明の実施の形態】以下に、本発明の実施の形態につ
いて説明する。 (実施例1)塩化ビニル系樹脂シートの作製 塩化ビニル系樹脂(鐘淵化学社製、商品名「PSH−1
0」)100重量部、ポリエステル系可塑剤(旭電化社
製、品番「P−300」)30重量部、金属石鹸系熱安
定剤(旭電化社製、商品名「MARK−SC34」)5
重量部及び酸化チタン(大日精化社製、品番「VT00
5」)45重量部を、有機溶剤(三菱化学社製、商品名
「ソルベッソ」)100重量部に混合分散することによ
り塩化ビニル系樹脂の分散溶液を得た。次いで、一面が
離型処理されている工程紙上に上記塩化ビニル系樹脂の
分散溶液を塗布乾燥し、加熱溶融することにより塩化ビ
ニル系樹脂シートを得た。
Embodiments of the present invention will be described below. (Example 1) Production of vinyl chloride resin sheet Vinyl chloride resin (manufactured by Kanegafuchi Chemical Co., Ltd., trade name "PSH-1")
0 ") 100 parts by weight, 30 parts by weight of a polyester plasticizer (manufactured by Asahi Denka Co., Ltd., product number" P-300 "), 5 metal soap heat stabilizers (manufactured by Asahi Denka Co., trade name" MARK-SC34 ") 5
Parts by weight and titanium oxide (manufactured by Dainichi Seika Co., Ltd., product number "VT00"
5)) 45 parts by weight were mixed and dispersed in 100 parts by weight of an organic solvent (manufactured by Mitsubishi Chemical Corporation, trade name "Solvesso") to obtain a dispersion solution of a vinyl chloride resin. Next, a dispersion solution of the vinyl chloride resin was applied on a process paper having one surface subjected to a release treatment, dried and heated and melted to obtain a vinyl chloride resin sheet.

【0056】次に、表1に従って固形分換算で、アクリ
ルポリオール及び有機溶剤からなる塗料溶液(大日本塗
料社製、商品名「プラニットU#700」、水酸基価=
70)100重量部、青色顔料20重量部、ポリイソシ
アネート化合物(日本ポリウレタン社製、商品名「コロ
ネート2094」、イソシアネート基の比率=16.5
重量%)6.5重量部及びウレタン系樹脂(住友バイエ
ルウレタン社製、商品名「デスモラック4125」、T
g=−10℃)15重量部を均一に混合することにより
塗料溶液を調整した。尚、この時の官能基比率は261
1であった。次いで、上記塩化ビニル系樹脂シートの一
面にリバースコーターを用いて塗布し、乾燥することに
より着色塗膜層を形成した。
Next, according to Table 1, a coating solution composed of an acrylic polyol and an organic solvent (trade name “Planit U # 700”, manufactured by Dainippon Paint Co., Ltd., hydroxyl value =
70) 100 parts by weight, 20 parts by weight of blue pigment, polyisocyanate compound (manufactured by Nippon Polyurethane Co., trade name "Coronate 2094", ratio of isocyanate group = 16.5)
6.5% by weight) and a urethane-based resin (manufactured by Sumitomo Bayer Urethane Co., trade name "Desmolak 4125", T
g = −10 ° C.) A coating solution was prepared by uniformly mixing 15 parts by weight. The functional group ratio at this time was 261.
It was one. Next, a color coating layer was formed on one surface of the vinyl chloride resin sheet by using a reverse coater and drying.

【0057】更に、固形分換算で、アクリル系粘着剤
(東洋インキ社製、商品名「BPS4341」)100
重量部及び架橋剤(東洋インキ社製、商品名「BHS8
515」)2重量部からなる粘着剤溶液を調製し、上記
塩化ビニル系樹脂シートの内、着色塗膜層が形成されて
いない面に乾燥後の厚さが30μmとなるように塗布乾
燥し、粘着剤層積層面に離型紙(リンテック社製、品番
「S80MZ」)を積層して、粘着シートを得た。
Further, in terms of solid content, an acrylic pressure-sensitive adhesive (trade name “BPS4341”, manufactured by Toyo Ink Co., Ltd.) is 100
Parts by weight and a crosslinking agent (trade name “BHS8, manufactured by Toyo Ink Co., Ltd.”
515 ") A pressure-sensitive adhesive solution consisting of 2 parts by weight is prepared, and is coated and dried on the surface of the vinyl chloride resin sheet on which the colored coating layer is not formed so that the thickness after drying is 30 μm. Release paper (manufactured by Lintec Co., Ltd., product number "S80MZ") was laminated on the surface of the pressure-sensitive adhesive layer to obtain a pressure-sensitive adhesive sheet.

【0058】(実施例2〜5及び比較例1〜4)表1の
配合組成に従って、着色塗膜層を形成したこと以外は実
施例1と同様にして粘着シートを得た。
(Examples 2 to 5 and Comparative Examples 1 to 4) An adhesive sheet was obtained in the same manner as in Example 1 except that a colored coating layer was formed in accordance with the composition shown in Table 1.

【0059】(評価方法)上記で得られた塩化ビニル系
樹脂シート及びそれを用いた粘着テープについて、塩
化ビニル系樹脂シートと着色塗膜層との密着性、着色
塗膜層が積層されている塩化ビニル系樹脂シートのエル
メンドルフ引裂強度、着色塗膜層表面のタック感、
装飾面の彩度をそれぞれ以下の方法により評価し、その
結果を表1に示した。
(Evaluation Method) With respect to the vinyl chloride resin sheet obtained above and the adhesive tape using the same, the adhesion between the vinyl chloride resin sheet and the colored coating layer, and the colored coating layer are laminated. Elmendorf tear strength of vinyl chloride resin sheet, tackiness of colored coating layer surface,
The chroma of the decorative surface was evaluated by the following methods, and the results are shown in Table 1.

【0060】塩化ビニル系樹脂シートと着色塗膜層と
の密着性 作製した粘着シートをアルミニウム板に貼付し、着色塗
膜層の面から1mm間隔で縦横方向にそれぞれ11本づ
つのハーフカットの切れ込みを入れ、着色塗膜層表面を
100個の正方形(1mm×1mm)に分割した。次い
で、着色塗膜層にセロハンテープを貼付した後剥離し、
剥離した着色塗膜層の数を測定した。
Adhesion between Vinyl Chloride Resin Sheet and Colored Coating Layer The prepared pressure-sensitive adhesive sheet was affixed to an aluminum plate, and 11 half-cuts each in the vertical and horizontal directions at 1 mm intervals from the surface of the colored coating layer. And the surface of the colored coating layer was divided into 100 squares (1 mm × 1 mm). Then, after applying a cellophane tape to the colored coating layer, peeled off,
The number of peeled colored coating layers was measured.

【0061】塩化ビニル系樹脂シートのエルメンドル
フ引裂強度 着色塗膜層が積層されている塩化ビニル系樹脂シート
を、63mm×76mmの長方形にカットし、16枚重
ねてエルメンドルフ引裂強度試験機を用いて引裂強度を
測定した。
Elmendorf Tear Strength of Vinyl Chloride Resin Sheet A vinyl chloride resin sheet having a colored coating layer laminated thereon is cut into a rectangle of 63 mm × 76 mm, and 16 sheets are laminated and torn using an Elmendorf tear strength tester. The strength was measured.

【0062】着色塗膜層表面のタック感 着色塗膜層の乾燥後のタック感を実際に触り、以下の評
価基準に従って評価した。 (評価基準) 3・・・全くタック感なし 2・・・ややタック感あり 1・・・タック感あり
Tackiness of Colored Coating Layer Surface The tackiness of the colored coating layer after drying was actually touched and evaluated according to the following evaluation criteria. (Evaluation criteria) 3 ... No tackiness at all 2 ... Slight tackiness 1 ... Tackiness

【0063】装飾面の彩度 装飾面である着色塗膜層の彩度(C値)を測色機(ミノ
ルタ社製、「CM3−3W」)を用いて測定した。
Chroma of Decorative Surface The chroma (C value) of the colored coating layer as a decorative surface was measured using a colorimeter (“CM3-3W” manufactured by Minolta Co.).

【0064】[0064]

【表1】 [Table 1]

【0065】[0065]

【発明の効果】請求項1記載の発明は、上記構成を有す
ることにより、着色塗膜層の乾燥性が良好で、合成樹脂
シートへの密着性を向上させたものとなっており、更に
装飾すべき被着体への貼付作業性に優れたものとなって
いる。
According to the first aspect of the present invention, by having the above-mentioned structure, the colored coating layer has good drying properties and improved adhesion to the synthetic resin sheet. It is excellent in the workability of sticking to the adherend to be performed.

【0066】請求項2の発明では、アクリルウレタン系
樹脂を構成しているアクリルポリオールに由来する水酸
基とポリイソシアネート化合物に由来するイソシアネー
ト基の比率を限定することにより、粘着シートの引裂強
度が更に良好なものとなっている。
In the invention of claim 2, the tear strength of the pressure-sensitive adhesive sheet is further improved by limiting the ratio of the hydroxyl group derived from the acrylic polyol constituting the acrylic urethane resin to the isocyanate group derived from the polyisocyanate compound. It has become something.

【0067】請求項3の発明では、合成樹脂シートが酸
化チタン等を含有させることにより白色シートとするこ
とにより、1種類の白色の合成樹脂シートを大量生産し
ておき、この合成樹脂シートの一面(装飾面)に様々な
着色塗膜層を積層することにより小ロット化を可能にで
き、少量多品種に対応できる。また、白色シートにより
被着体の下地色がしっかりと隠蔽され、着色塗膜層の色
が高彩度となり、装飾性の良好なものとなる。
According to the third aspect of the present invention, the synthetic resin sheet is made into a white sheet by containing titanium oxide or the like, so that one kind of white synthetic resin sheet is mass-produced, and one surface of the synthetic resin sheet is produced. By laminating various colored coating layers on the (decorative surface), it is possible to reduce the number of lots, and it is possible to cope with many kinds in small quantities. In addition, the base sheet of the adherend is firmly hidden by the white sheet, the color of the colored coating layer becomes high in color, and the decorative property is good.

Claims (3)

【特許請求の範囲】[Claims] 【請求項1】 合成樹脂シートの一面に、ガラス転移温
度が30〜80℃であるアクリルウレタン系樹脂100
重量部、ガラス転移温度が−50〜−5℃であるウレタ
ン系樹脂5〜30重量部及び顔料0.5〜50重量部か
らなる着色塗膜層が積層され、もう一面に粘着剤層が積
層されていることを特徴とする粘着シート。
1. An acrylic urethane resin 100 having a glass transition temperature of 30 to 80 ° C. on one surface of a synthetic resin sheet.
5 to 30 parts by weight of a urethane-based resin having a glass transition temperature of -50 to -5 ° C and 0.5 to 50 parts by weight of a pigment, and a pressure-sensitive adhesive layer on the other side. A pressure-sensitive adhesive sheet characterized by being made.
【請求項2】 アクリルウレタン系樹脂が、アクリルポ
リオールとポリイソシアネート化合物からなる反応物で
あり、かつ両者が下式 【化1】 で表される官能基比率が20〜40を満たすように混合
されてなることを特徴とする請求項1記載の粘着シー
ト。
2. The acrylic urethane-based resin is a reactant comprising an acrylic polyol and a polyisocyanate compound, and both are represented by the following formula: The pressure-sensitive adhesive sheet according to claim 1, wherein the pressure-sensitive adhesive sheet is mixed so that the functional group ratio represented by satisfies 20 to 40.
【請求項3】 合成樹脂シートが白色であり、かつ着色
塗膜層が着色透明であることを特徴とする請求項1又は
2に記載の粘着シート。
3. The pressure-sensitive adhesive sheet according to claim 1, wherein the synthetic resin sheet is white and the colored coating layer is colored and transparent.
JP11055829A 1999-03-03 1999-03-03 Adhesive sheet Pending JP2000248238A (en)