JP2000191970A - Emulsion ink for stencil printing - Google Patents
Emulsion ink for stencil printingInfo
- Publication number
- JP2000191970A JP2000191970A JP36659898A JP36659898A JP2000191970A JP 2000191970 A JP2000191970 A JP 2000191970A JP 36659898 A JP36659898 A JP 36659898A JP 36659898 A JP36659898 A JP 36659898A JP 2000191970 A JP2000191970 A JP 2000191970A
- Authority
- JP
- Japan
- Prior art keywords
- oil
- dye
- water
- ink
- phase
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は孔版印刷用エマルシ
ョンインキに関し、さらに詳しくは、印刷物の色彩が鮮
明で、滲みや裏抜けが少ないとともに、印刷機を長期間
使用しなかった後の印刷でも良好な画像をトラブル無く
得られる孔版印刷用エマルションインキに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an emulsion ink for stencil printing, and more particularly, to a printed material having a clear color, less bleeding or strike-through, and good printing even after the printing press has not been used for a long time. Stencil printing emulsion ink which can obtain a good image without any trouble.
【0002】[0002]
【従来の技術】孔版印刷は、孔版原紙を用いて製版し、
これにより形成された穿孔部にインキを通過させ、紙な
どの被印刷体に印刷を行うものである。輪転式孔版印刷
機は、大量の印刷物を低コストで印刷できる上に、製版
・印刷の自動化が進み操作も簡便になったため、幅広い
分野で利用されている。かかる孔版印刷機では、従来か
ら、孔版印刷用インキとして、一般に、油中水(W/O)
型エマルションインキが使用されており、着色剤として
顔料が使用されている(特開昭61-255967号公報、特開
昭64-14284号公報、特開平4-132777号公報、特開平7-18
8598号公報、特開平10-81846号公報等参照)。2. Description of the Related Art In stencil printing, stencil printing is performed using stencil paper.
The ink is allowed to pass through the perforated portion formed by this, and printing is performed on a printing medium such as paper. Rotary stencil printing machines are used in a wide range of fields because they can print a large amount of printed matter at low cost, and the stencil making and printing are automated and the operation is simplified. In such a stencil printing machine, conventionally, water-in-oil (W / O) has generally been used as a stencil printing ink.
A type emulsion ink is used, and a pigment is used as a colorant (JP-A-61-255967, JP-A-64-14284, JP-A-4-132777, JP-A-7-18
8598, JP-A-10-81846, etc.).
【0003】しかし、顔料は、カラーインキの着色剤と
しては鮮明さに劣り、色の再現範囲が狭いことが知られ
ている。そこで、着色剤として染料を使用することが提
案されている(特開平5-117565号公報、特開平6-9912号
公報参照)。However, pigments are known to be inferior in sharpness as colorants for color inks and have a narrow color reproduction range. Therefore, it has been proposed to use a dye as a coloring agent (see JP-A-5-117565 and JP-A-6-9912).
【0004】[0004]
【発明が解決しようとする課題】しかしながら、染料は
インキ成分とともに紙繊維に沿って浸透しやすいため、
印刷画像の滲みや裏抜けが発生し易いという問題があっ
た。特に、油溶性染料は、インキ中の不揮発性溶剤とと
もに浸透するため、滲みや裏抜けを発生し易かった。However, since the dye easily penetrates along the paper fiber together with the ink component,
There is a problem that bleeding or strike-through of a printed image easily occurs. In particular, the oil-soluble dye penetrates together with the non-volatile solvent in the ink, so that bleeding or strike-through easily occurred.
【0005】さらに、着色剤が染料からなるエマルショ
ンインキを使用した場合、孔版印刷機を長期間使用せず
に放置しておくと、印刷機の版胴内部に残されたインキ
は、エマルション内の水分が蒸発することにより、油相
(連続相)に対する水相(分散相)の比率が減少し、粘
度が大幅に低下してしまう。このようにインキが軟化す
る結果、印刷機からインキが漏れ出してメンテナンス作
業を煩雑にしたり、過剰のインキが印刷用紙に転移し
て、細字つぶれや乾燥性劣化の問題を引き起こすことが
あった。Further, when an emulsion ink comprising a dye as a coloring agent is used, if the stencil printing machine is not used for a long period of time, the ink remaining inside the printing drum of the printing machine will cause the ink remaining in the emulsion. As the water evaporates, the ratio of the aqueous phase (dispersed phase) to the oil phase (continuous phase) is reduced, and the viscosity is greatly reduced. As a result of the softening of the ink, the ink leaks out of the printing machine to complicate the maintenance work, or excessive ink may be transferred to the printing paper, causing problems such as crushing of fine characters and deterioration of dryness.
【0006】本発明の目的は、上記の従来技術の問題を
解決し、色彩が鮮やかで、滲みや裏抜けが少なく、印刷
機内に放置してもトラブルを起こさず、良好な画像の得
られる孔版印刷用エマルションインキを提供することに
ある。SUMMARY OF THE INVENTION It is an object of the present invention to solve the above-mentioned problems of the prior art, and to provide a stencil having a vivid color, little bleeding or strike-through, no trouble when left in a printing machine, and a good image can be obtained. An object of the present invention is to provide an emulsion ink for printing.
【0007】[0007]
【課題を解決するための手段】本発明者は、着色剤とし
て染料を含有する油中水(W/O)型エマルションインキ
に、さらに体質顔料を含ませることにより、上記問題を
解決できることを見出し本発明を完成するに至った。Means for Solving the Problems The present inventor has found that the above problem can be solved by further adding an extender pigment to a water-in-oil (W / O) emulsion ink containing a dye as a colorant. The present invention has been completed.
【0008】印刷後の油中水(W/O)型エマルションイ
ンキの乾燥は、印刷用紙への浸透と蒸発によって起き
る。油中水(W/O)型エマルションインキの印刷用紙へ
の浸透は、印刷用紙の繊維間の空隙へのエマルションの
浸透現象と、エマルションが油相成分と水相成分に分離
し、まず油相成分、続いて水相成分が印刷用紙の繊維に
沿って浸透する現象とによって起こると考えられてい
る。本発明の油中水(W/O)型エマルションインキは、
印刷後に、体質顔料が印刷用紙の表面積を上げるかのよ
うな効果をもたらす。その結果、インキ中の成分は、紙
繊維に添って浸透していくだけでなく、体質顔料表面に
も吸着する。すなわち、油溶性染料の場合は、エマルシ
ョンの油相成分とともに印刷用紙の繊維に沿って浸透す
ることが防止され、水溶性染料の場合は、水相成分とと
もに印刷用紙の繊維に沿って浸透することが防止され、
画像の裏抜けや滲みを減少させると考えられる。[0008] Drying of a water-in-oil (W / O) emulsion ink after printing is caused by permeation and evaporation of printing paper. The penetration of water-in-oil (W / O) emulsion ink into printing paper is based on the phenomenon of emulsion penetration into the voids between fibers of the printing paper and the separation of the emulsion into an oil phase component and an aqueous phase component. It is believed that the component, and subsequently the aqueous phase component, penetrates along the fibers of the printing paper. The water-in-oil (W / O) emulsion ink of the present invention is
After printing, the extender pigment has the effect of increasing the surface area of the printing paper. As a result, the components in the ink not only permeate along with the paper fibers, but also adsorb on the surface of the extender pigment. That is, in the case of an oil-soluble dye, it is prevented from penetrating along the fibers of the printing paper together with the oil phase component of the emulsion, and in the case of a water-soluble dye, it is permeated along the fibers of the printing paper together with the aqueous phase component. Is prevented,
It is considered to reduce strikethrough and bleeding of the image.
【0009】さらに、本発明の油中水(W/O)型エマル
ションインキは、孔版印刷機を長期間使用せずにいてエ
マルション内の水分が蒸発し、油相(連続相)に対する
水相(分散相)の比率が減少しても、インキの軟化を防
止できる。この理由は、水分の蒸発とともにインキ全体
の体積も減少するが、それにともない体質顔料のインキ
に占める比率が高まり、その結果、体質顔料が分散質と
して機能してインキに降伏値をもたせるためと考えられ
る。Further, the water-in-oil (W / O) emulsion ink of the present invention can be obtained by evaporating water in the emulsion without using the stencil printing machine for a long period of time, so that the water phase (continuous phase) is converted to the water phase (continuous phase). Even if the ratio of (dispersed phase) decreases, the softening of the ink can be prevented. The reason for this is that although the volume of the entire ink decreases as the water evaporates, the proportion of the extender in the ink increases with that, and as a result, the extender functions as a dispersoid and gives the ink a yield value. Can be
【0010】[0010]
【発明の実施の形態】以下、本発明をさらに詳しく説明
する。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in more detail.
【0011】本発明の油中水(W/O)型エマルションイ
ンキは、着色剤として染料を含有する。染料としては、
油溶性染料及び水溶性染料の何れも用いることができ、
また、両者を併用することもできる。油溶性染料は油相
中に添加するに好都合であり、水溶性染料は水相中に添
加するに好都合である。油溶性染料としては、例えば、
アゾ系、アントラキノン系、アジン系等の油溶性染料が
用いられる。水溶性染料としては、例えば、塩基性染
料、酸性染料、直接染料、可溶性バット染料、酸性媒染
染料、媒染染料、反応染料、バット染料、硫化染料等の
うち、水溶性の染料および還元等により水溶性にされた
染料が用いられる。これらの染料の添加量は、エマルシ
ョンインキの総量に対して、0.1〜20重量%が好まし
く、0.5〜10重量%の範囲がより好ましい。The water-in-oil (W / O) emulsion ink of the present invention contains a dye as a coloring agent. As a dye,
Any of an oil-soluble dye and a water-soluble dye can be used,
Moreover, both can be used together. Oil-soluble dyes are convenient to add to the oil phase, and water-soluble dyes are convenient to add to the aqueous phase. As oil-soluble dyes, for example,
Azo-based, anthraquinone-based and azine-based oil-soluble dyes are used. Examples of the water-soluble dye include, for example, a basic dye, an acid dye, a direct dye, a soluble vat dye, an acid mordant dye, a mordant dye, a reactive dye, a vat dye, and a sulfur dye. Activated dyes are used. The addition amount of these dyes is preferably 0.1 to 20% by weight, more preferably 0.5 to 10% by weight, based on the total amount of the emulsion ink.
【0012】本発明においては、所望の色彩を出すため
に、必要であれば、着色剤として染料に加えて顔料を用
いてもよい。ただし、染料は、着色剤全量の30重量%以
上を占めることが好ましい。染料の比率が低すぎると、
鮮明な色彩を得ることが難しくなる。顔料は、油相およ
び/または水相中に含ませることができる。顔料として
は、各種色調の公知のものが用いられる。例えば、アゾ
系、フタロシアニン系、染料系、縮合多環系、ニトロ
系、ニトロソ系等の有機顔料(ブリリアントカーミン6
B、レーキレッドC、ウォッチングレッド、ジスアゾイエ
ロー、ハンザイエロー、フタロシアニンブルー、フタロ
シアニングリーン、およびアルカリブルー、アニリンブ
ラック等)の他、コバルト、鉄、クロム、銅、亜鉛、
鉛、チタン、バナジウム、マンガン、ニッケル等の金属
類、金属酸化物および硫化物、並びに、ファーネスカー
ボンブラック、ランプブラック、チャンネルブラック等
のカーボンブラック類、黄土、群青、紺青等の無機顔料
が用いられる。In the present invention, in order to obtain a desired color, a pigment may be used as a coloring agent in addition to the dye, if necessary. However, the dye preferably accounts for 30% by weight or more of the total amount of the colorant. If the ratio of the dye is too low,
It is difficult to obtain clear colors. The pigment can be included in the oil phase and / or the aqueous phase. As the pigment, known pigments having various colors are used. For example, organic pigments such as azo-based, phthalocyanine-based, dye-based, condensed polycyclic, nitro-based, and nitroso-based organic pigments (Brilliant Carmine 6)
B, lake red C, watching red, disazo yellow, hansa yellow, phthalocyanine blue, phthalocyanine green, and alkali blue, aniline black, etc.), cobalt, iron, chromium, copper, zinc,
Metals such as lead, titanium, vanadium, manganese and nickel, metal oxides and sulfides, and carbon blacks such as furnace carbon black, lamp black and channel black, and inorganic pigments such as loess, ultramarine blue and navy blue are used. .
【0013】本発明の油中水(W/O)型エマルションイ
ンキは、油相および/または水相中に体質顔料が含まれ
る。染料を体質顔料の表面に吸着しやすくするために、
体質顔料は染料と同一相に含ませることが好ましい。体
質顔料としては、インキに含まれても不溶であり、無色
な微粒子が用いられる。例えば、白土、タルク、クレ
ー、珪藻土、炭酸カルシウム、炭酸バリウム、硫酸バリ
ウム、アルミナホワイト、シリカ、カオリン、マイカ、
水酸化アルミニウム等の無機微粒子のほか、ポリアクリ
ル酸エステル、ポリウレタン、ポリエステル、ポリエチ
レン、ポリプロピレン、ポリ塩化ビニル、ポリ塩化ビニ
リデン、ポリスチレン、ポリシロキサン、フェノール樹
脂、エポキシ樹脂、ベンゾグアナミン樹脂等の有機微粒
子またはこれらの共重合体からなる微粒子等が用いられ
る。[0013] The water-in-oil (W / O) emulsion ink of the present invention contains an extender pigment in an oil phase and / or an aqueous phase. In order to make the dye easily adsorb to the surface of the extender,
The extender pigment is preferably contained in the same phase as the dye. As the extender pigment, colorless fine particles which are insoluble even in the ink and are insoluble are used. For example, clay, talc, clay, diatomaceous earth, calcium carbonate, barium carbonate, barium sulfate, alumina white, silica, kaolin, mica,
In addition to inorganic fine particles such as aluminum hydroxide, organic fine particles such as polyacrylate, polyurethane, polyester, polyethylene, polypropylene, polyvinyl chloride, polyvinylidene chloride, polystyrene, polysiloxane, phenol resin, epoxy resin, benzoguanamine resin, and the like. Fine particles made of a copolymer of the above are used.
【0014】本発明の体質顔料の平均粒径は、10μm以
下であることが好ましい。粒径が大きすぎると、孔版印
刷原紙の穿孔部から通過できなかったり、油中水(W/
O)型エマルションを崩壊することがある。体質顔料の
添加量は、エマルションインキの総量に対して、1〜20
重量%が好ましく、3〜10重量%の範囲がより好まし
い。体質顔料の添加量が少なすぎると、印刷画像の滲み
・裏抜け、長期放置後の印刷機からのインキ漏れ出しや
印刷用紙への過剰のインキ転移を防止する効果が小さく
なる。体質顔料の添加量が多すぎると、孔版印刷に不適
合な、すなわち、孔版印刷原紙の穿孔部を通過しにくい
インキとなりやすい。The extender pigment of the present invention preferably has an average particle size of 10 μm or less. If the particle size is too large, it will not be able to pass through the perforated part of the stencil sheet,
O) Emulsions may collapse. The amount of extender added is 1 to 20 with respect to the total amount of the emulsion ink.
% By weight, more preferably in the range of 3 to 10% by weight. If the amount of the extender is too small, the effect of preventing bleeding or strike-through of a printed image, leakage of ink from a printing machine after being left for a long period of time, or excessive transfer of ink to printing paper is reduced. If the amount of the extender pigment is too large, the ink tends to be unsuitable for stencil printing, that is, difficult to pass through the perforated portion of the stencil printing paper.
【0015】本発明の油中水(W/O)型エマルションイ
ンキは、通常、15〜50重量%の油相に85〜50重量%の水
相を徐々に添加して乳化させることにより製造される。
油溶性染料を用いる場合は、油相は15〜40重量%、水相
は85〜60重量%であることが好ましい。この範囲より油
相の比率が高いと、油溶性染料が油相成分とともに紙繊
維に浸透しやすくなり、インキの滲みが大きくなる。ま
た、水溶性染料を用いる場合は、油相は25〜50重量%、
水相は75〜50重量%であることが好ましい。この範囲よ
り油相の比率が低いと、油相成分の紙繊維への浸透が早
く終わり、水相成分の紙繊維への浸透が早まってしま
い、インキの滲みが大きくなる。The water-in-oil (W / O) emulsion ink of the present invention is usually produced by gradually adding 85 to 50% by weight of an aqueous phase to 15 to 50% by weight of an oil phase and emulsifying the oil phase. You.
When an oil-soluble dye is used, the oil phase is preferably 15 to 40% by weight, and the aqueous phase is preferably 85 to 60% by weight. When the ratio of the oil phase is higher than this range, the oil-soluble dye and the oil phase component easily penetrate into the paper fiber, and the bleeding of the ink increases. When using a water-soluble dye, the oil phase is 25 to 50% by weight,
Preferably, the aqueous phase is 75-50% by weight. If the ratio of the oil phase is lower than this range, the penetration of the oil phase component into the paper fiber ends early, and the penetration of the water phase component into the paper fiber is accelerated, and the bleeding of the ink increases.
【0016】本発明における油相は、基本的に、油成
分、乳化剤から構成されるが、水相中に水溶性染料を含
ませない場合は油相中に油溶性染料を含ませなくてはな
らない。また、体質顔料は、油相か水相の少なくともい
ずれか一方に含ませなくてはならない。さらに、必要に
応じて、油相中に顔料を含ませることができる。油相粘
度は、油相中に顔料や体質顔料を含むかどうかで大きく
異なるが、例えばこれらを含まない場合では、通常15〜
2000mPa・s程度、より一般的には60〜600mPa・s程度であ
る。The oil phase in the present invention is basically composed of an oil component and an emulsifier. When the water phase does not contain a water-soluble dye, the oil phase must contain an oil-soluble dye. No. The extender must be contained in at least one of the oil phase and the aqueous phase. Further, if necessary, a pigment can be contained in the oil phase. The oil phase viscosity varies greatly depending on whether a pigment or extender is contained in the oil phase.
It is about 2000 mPa · s, more usually about 60 to 600 mPa · s.
【0017】油成分としては、各種工業用溶剤、モータ
ー油、ギヤー油、軽油、灯油、スピンドル油、マシン
油、流動パラフィン等の鉱物油、オリーブ油、ナタネ
油、アマニ油、ヒマシ油、サラダ油、大豆油等の植物油
のほか、合成油等も用いられる。油成分は、放置後の印
刷開始時の印刷性能をさらに高める等の目的のため、揮
発性の異なる油を複数混合して用いることが好ましい。The oil component includes various industrial solvents, motor oil, gear oil, light oil, kerosene, spindle oil, machine oil, mineral oil such as liquid paraffin, olive oil, rapeseed oil, linseed oil, castor oil, salad oil, In addition to vegetable oils such as bean oil, synthetic oils and the like are also used. The oil component is preferably used by mixing a plurality of oils having different volatility for the purpose of further improving the printing performance at the start of printing after standing.
【0018】乳化剤は、油中水(W/O)型エマルション
を構成するために用いられ、アニオン界面活性剤、カチ
オン界面活性剤、両面界面活性剤、非イオン界面活性剤
のいずれでもよい。このうち、非イオン界面活性剤が好
ましく用いられ、例えば、ソルビタンモノラウレート、
ソルビタンモノパルミテート、ソルビタンモノオレエー
ト、ソルビタンセスキオレート、ソルビタンモノステア
レート等のソルビタン脂肪酸エステル、グリセリルモノ
ステアレート、ヘキサグリセリルテトラオレエート、デ
カグリセリルデカオレエート、ヘキサグリセリルペンタ
オレエート等の(ポリ)グリセリン脂肪酸エステル、ポ
リオキシエチレンソルビタン脂肪酸エステル、ポリオキ
シエチレングリセリン脂肪酸エステル、ポリオキシエチ
レンソルビット脂肪酸エステル、プロピレングリコール
脂肪酸エステル、(ポリ)エチレングリコール脂肪酸エ
ステル、ポリオキシエチレンアルキルエーテル、ポリオ
キシエチレンポリオキシプロピレンアルキルエーテル、
ポリオキシエチレンアルキルフェニルエーテル、ポリオ
キシエチレン(硬化)ヒマシ油、等が用いられる。乳化
剤は、単一の種類のみでなく、二種類以上を組み合わせ
て用いることもできる。The emulsifier is used to form a water-in-oil (W / O) emulsion, and may be any of an anionic surfactant, a cationic surfactant, a double-sided surfactant, and a nonionic surfactant. Of these, nonionic surfactants are preferably used, for example, sorbitan monolaurate,
Sorbitan monopalmitate, sorbitan monooleate, sorbitan sesquiolate, sorbitan fatty acid esters such as sorbitan monostearate, glyceryl monostearate, hexaglyceryl tetraoleate, decaglyceryl decaoleate, hexaglyceryl pentaoleate, etc. ) Glycerin fatty acid ester, polyoxyethylene sorbitan fatty acid ester, polyoxyethylene glycerin fatty acid ester, polyoxyethylene sorbite fatty acid ester, propylene glycol fatty acid ester, (poly) ethylene glycol fatty acid ester, polyoxyethylene alkyl ether, polyoxyethylene polyoxy Propylene alkyl ether,
Polyoxyethylene alkylphenyl ether, polyoxyethylene (hardened) castor oil, and the like are used. Emulsifiers can be used not only in a single type but also in combination of two or more types.
【0019】なお、油相中には、エマルションの安定性
を向上させるため、または、インキの粘度付与剤等とし
て、樹脂を含ませることができる。油相中に顔料や体質
顔料が含まれている場合は、顔料や体質顔料の分散性や
紙への定着性を上げるため、樹脂を含ませることが好ま
しい。例えば、ロジン、ギルソナイト、ロジンエステ
ル、マレイン酸樹脂、ロジン変性フェノール樹脂、アル
キド樹脂、石油樹脂、アクリル樹脂、アミノ樹脂、ウレ
タン樹脂、セルロース樹脂、天然ゴム誘導体樹脂等が用
いられる。さらに、油相中には、必要に応じて、ゲル化
剤、酸化防止剤、顔料や体質顔料の分散剤等を含ませる
ことができる。The oil phase may contain a resin for improving the stability of the emulsion or as a viscosity imparting agent for the ink. When a pigment or extender is contained in the oil phase, it is preferable to include a resin in order to increase the dispersibility of the pigment or extender and the fixability to paper. For example, rosin, Gilsonite, rosin ester, maleic acid resin, rosin-modified phenol resin, alkyd resin, petroleum resin, acrylic resin, amino resin, urethane resin, cellulose resin, natural rubber derivative resin and the like are used. Further, the oil phase may contain a gelling agent, an antioxidant, a dispersant for a pigment or an extender, or the like, if necessary.
【0020】本発明における水相は、主に水から構成さ
れるが、油相中に油溶性染料を含まない場合は水相中に
水溶性染料を含ませなくてはならない。また、体質顔料
は、油相か水相の少なくともいずれか一方に含ませなく
てはならない。さらに、必要に応じて、水相中に顔料を
含ませることができる。The aqueous phase in the present invention is mainly composed of water. When the oil phase does not contain an oil-soluble dye, the water phase must contain a water-soluble dye. The extender must be contained in at least one of the oil phase and the aqueous phase. Further, if necessary, a pigment can be contained in the aqueous phase.
【0021】水相には、必要に応じて水中油(O/W)型
樹脂エマルションおよび/または水溶性樹脂を含ませる
ことができる。なお、顔料や体質顔料を水相に添加する
場合、水中油(O/W)型樹脂エマルションや水溶性樹脂
を水相に含ませることにより、顔料や体質顔料の濡れ性
や分散性と、用紙等の被印刷体への顔料や体質顔料の固
着性とを向上させることができる。The aqueous phase may contain an oil-in-water (O / W) type resin emulsion and / or a water-soluble resin, if necessary. When a pigment or extender is added to the aqueous phase, an oil-in-water (O / W) type resin emulsion or a water-soluble resin is included in the aqueous phase, so that the wettability and dispersibility of the pigment or extender can be improved. And the fixability of the pigment or extender to the printing medium.
【0022】水中油(O/W)型樹脂エマルションとして
は、例えば、ポリ酢酸ビニル、エチレン−酢酸ビニル共
重合体、酢酸ビニル−アクリル酸エステル共重合体、ポ
リメタクリル酸エステル、ポリスチレン、スチレン−ア
クリル酸エステル共重合体、スチレン−ブタジエン共重
合体、塩化ビニリデン−アクリル酸エステル共重合体、
ポリ塩化ビニル、塩化ビニル−酢酸ビニル共重合体、ポ
リウレタン等の樹脂エマルションが用いられる。Examples of the oil-in-water (O / W) resin emulsion include polyvinyl acetate, ethylene-vinyl acetate copolymer, vinyl acetate-acrylate copolymer, polymethacrylate, polystyrene, and styrene-acryl. Acid ester copolymer, styrene-butadiene copolymer, vinylidene chloride-acrylate copolymer,
Resin emulsions such as polyvinyl chloride, vinyl chloride-vinyl acetate copolymer, and polyurethane are used.
【0023】また、水溶性樹脂としては、例えば、ポリ
ビニルアルコール、メチルセルロース、カルボキシメチ
ルセルロース、ヒドロキシエチルセルロース、ポリビニ
ルピロリドン、ポリエチレン−ポリビニルアルコール共
重合体、ポリエチレンオキサイド、ポリビニルエーテ
ル、ポリアクリルアミド、アラビアゴム、澱粉、水溶性
ウレタン等が用いられる。Examples of the water-soluble resin include polyvinyl alcohol, methyl cellulose, carboxymethyl cellulose, hydroxyethyl cellulose, polyvinyl pyrrolidone, polyethylene-polyvinyl alcohol copolymer, polyethylene oxide, polyvinyl ether, polyacrylamide, gum arabic, starch, water-soluble resin. Urethane or the like is used.
【0024】さらに、水相中には、水に対する顔料や体
質顔料の濡れ性や分散性を改良するため、アニオン界面
活性剤、カチオン界面活性剤、両性界面活性剤、非イオ
ン界面活性剤、または、高分子系、シリコーン系、フッ
素系の界面活性剤、更には、特開平8-34944号公報に記
載のような第三アミン化合物若しくは特開平10-1634号
に記載のような酸無水物含有水溶性ポリマーを含ませる
ことができる。これらの分散剤のうち、第三アミン化合
物および酸無水物含有水溶性ポリマーが特に好ましい。
これらの添加量は、各々が持つ顔料や体質顔料の分散能
力等によって適宜決定される。Further, in the aqueous phase, an anionic surfactant, a cationic surfactant, an amphoteric surfactant, a nonionic surfactant, or , Polymer-based, silicone-based, fluorine-based surfactants, and further, containing a tertiary amine compound as described in JP-A-8-34944 or an acid anhydride as described in JP-A-10-1634 A water-soluble polymer can be included. Among these dispersants, tertiary amine compounds and acid anhydride-containing water-soluble polymers are particularly preferred.
The amounts of these additives are appropriately determined depending on the dispersing ability of the pigments and extenders which each has.
【0025】水相中には、さらに、湿潤剤、水蒸発抑制
剤、凍結防止剤を含ませることができ、好ましくは水溶
性有機溶媒が用いられる。例えば、エチレングリコー
ル、プロピレングリコール、ジエチレングリコール、ポ
リエチレングリコール、グリセリン等の多価アルコール
類、エチレングリコールモノエチルエーテル、トリエチ
レングリコールモノエチルエーテル等の多価アルコール
のアルキルエーテル類、その他にトリエタノールアミン
等も用いられる。The aqueous phase may further contain a wetting agent, a water evaporation inhibitor and an antifreezing agent, and preferably a water-soluble organic solvent is used. For example, polyhydric alcohols such as ethylene glycol, propylene glycol, diethylene glycol, polyethylene glycol, and glycerin; alkyl ethers of polyhydric alcohols such as ethylene glycol monoethyl ether and triethylene glycol monoethyl ether; and triethanolamine and the like. Used.
【0026】さらに、水相中には、電解質やpH調整剤を
含ませることができる。例えば、硫酸ナトリウム、硫酸
マグネシウム、リン酸水素カリウム、クエン酸ナトリウ
ム、酒石酸カリウム、ホウ酸ナトリウム、トリエタノー
ルアミン等が用いられる。Further, the aqueous phase can contain an electrolyte and a pH adjuster. For example, sodium sulfate, magnesium sulfate, potassium hydrogen phosphate, sodium citrate, potassium tartrate, sodium borate, triethanolamine and the like are used.
【0027】なお、水相は、さらに、必要に応じて防腐
剤、防黴剤、酸化防止剤等の水溶性添加物を含んでもよ
い。The aqueous phase may further contain a water-soluble additive such as a preservative, a fungicide and an antioxidant, if necessary.
【0028】[0028]
【実施例】以下、本発明を実施例により詳しく説明する
が、本発明はこれらに限定されるものではない。なお、
例中の部は重量部を意味する。実施例および比較例にお
いては、表に示す配合により、それぞれ下記の方法で油
中水(W/O)型エマルションインキを作製した。なお、
表に示した体質顔料の平均粒径は、体質顔料を分散後
に、遠心沈降式粒度分布計(堀場製作所製CAPA-700)で
測定した値である。The present invention will be described in more detail with reference to the following Examples, which should not be construed as limiting the invention thereto. In addition,
Parts in the examples mean parts by weight. In Examples and Comparative Examples, water-in-oil (W / O) emulsion inks were prepared according to the formulations shown in the tables by the following methods. In addition,
The average particle size of the extender pigment shown in the table is a value measured by a centrifugal sedimentation type particle size distribution analyzer (CAPA-700 manufactured by Horiba, Ltd.) after dispersing the extender pigment.
【0029】実施例1、2 まず、体質顔料、アルキド樹脂、モーター油、ポリグリ
セリン脂肪酸エステル、ポリオキシエチレン硬化ひまし
油を混合し、三本ロールで充分に分散した。この体質顔
料分散液に油溶性染料、石油系溶剤を混合・攪拌して染
料を溶解させ、油相を調製した。この油相中にグリセリ
ンとイオン交換水の混合溶液を徐々に滴下しながら攪拌
機で乳化を行い、孔版印刷用エマルションインキを得
た。Examples 1 and 2 First, an extender, an alkyd resin, a motor oil, a polyglycerin fatty acid ester, and a polyoxyethylene hardened castor oil were mixed and thoroughly dispersed with a three-roll mill. An oil-soluble dye and a petroleum-based solvent were mixed and stirred into the extender dispersion to dissolve the dye, thereby preparing an oil phase. The mixture was emulsified with a stirrer while a mixed solution of glycerin and ion-exchanged water was gradually dropped into the oil phase to obtain a stencil printing emulsion ink.
【0030】実施例3 まず、体質顔料、アルキド樹脂(5.5部)、モーター油
(4.0部)、ポリグリセリン脂肪酸エステル(0.5部)、
ポリオキシエチレン硬化ひまし油(0.5部)を混合し、
三本ロールで充分に分散した。次に、顔料、アルキド樹
脂(2.5部)、モーター油(2.0部)、ポリグリセリン脂
肪酸エステル(0.5部)、ポリオキシエチレン硬化ひま
し油(0.5部)を混合し、三本ロールで充分に分散し
た。この体質顔料分散液と顔料分散液に、油溶性染料、
石油系溶剤を混合・攪拌して染料を溶解させ、油相を調
製した。この油相中にグリセリンとイオン交換水の混合
溶液を徐々に滴下しながら攪拌機で乳化を行い、孔版印
刷用エマルションインキを得た。Example 3 First, extender, alkyd resin (5.5 parts), motor oil (4.0 parts), polyglycerin fatty acid ester (0.5 parts),
Mix polyoxyethylene hardened castor oil (0.5 parts)
The mixture was sufficiently dispersed with three rolls. Next, the pigment, alkyd resin (2.5 parts), motor oil (2.0 parts), polyglycerin fatty acid ester (0.5 parts), and polyoxyethylene hardened castor oil (0.5 parts) were mixed and sufficiently dispersed with a three-roll mill. In this extender pigment dispersion and the pigment dispersion, an oil-soluble dye,
The dye was dissolved by mixing and stirring a petroleum solvent to prepare an oil phase. While a mixed solution of glycerin and ion-exchanged water was gradually dropped into the oil phase, emulsification was performed with a stirrer to obtain an emulsion ink for stencil printing.
【0031】実施例4、5 まず、アルキド樹脂、モーター油、石油系溶剤、ポリグ
リセリン脂肪酸エステル、ポリオキシエチレン硬化ひま
し油を混合して、油相を調製した。次に、体質顔料、ポ
リビニルピロリドン、グリセリン、イオン交換水を混合
し、ボールミルで充分に分散した。この体質顔料分散液
に、水溶性染料を混合・攪拌して染料を溶解させ、水相
を調製した。この水相を油相中に徐々に滴下しながら攪
拌機で乳化を行い、孔版印刷用エマルションインキを得
た。Examples 4 and 5 First, an alkyd resin, a motor oil, a petroleum solvent, a polyglycerin fatty acid ester, and a polyoxyethylene hardened castor oil were mixed to prepare an oil phase. Next, the extender, polyvinylpyrrolidone, glycerin, and ion-exchanged water were mixed and sufficiently dispersed by a ball mill. A water-soluble dye was mixed and stirred with this extender pigment dispersion to dissolve the dye, thereby preparing an aqueous phase. The aqueous phase was gradually dropped into the oil phase and emulsified by a stirrer to obtain a stencil printing emulsion ink.
【0032】実施例6 まず、油溶性染料、アルキド樹脂、モーター油、石油系
溶剤、ポリグリセリン脂肪酸エステル、ポリオキシエチ
レン硬化ひまし油を混合・攪拌して染料を溶解させ、油
相を調製した。次に、体質顔料、ポリビニルピロリド
ン、グリセリン、イオン交換水を混合し、ボールミルで
充分に分散して、水相を調製した。この水相を油相中に
徐々に滴下しながら攪拌機で乳化を行い、孔版印刷用エ
マルションインキを得た。Example 6 First, an oil-soluble dye, an alkyd resin, a motor oil, a petroleum solvent, a polyglycerin fatty acid ester, and a polyoxyethylene hardened castor oil were mixed and stirred to dissolve the dye, thereby preparing an oil phase. Next, an extender, polyvinylpyrrolidone, glycerin, and ion-exchanged water were mixed and sufficiently dispersed by a ball mill to prepare an aqueous phase. The aqueous phase was gradually dropped into the oil phase and emulsified by a stirrer to obtain a stencil printing emulsion ink.
【0033】実施例7 まず、体質顔料、アルキド樹脂、モーター油、ポリグリ
セリン脂肪酸エステル、ポリオキシエチレン硬化ひまし
油を混合し、三本ロールで充分に分散した。この体質顔
料分散液に石油系溶剤を混合・攪拌して、油相を調製し
た。次に、水溶性染料、グリセリン、イオン交換水を混
合・攪拌して染料を溶解させ、水相を調製した。この水
相を油相中に徐々に滴下しながら攪拌機で乳化を行い、
孔版印刷用エマルションインキを得た。Example 7 First, an extender, an alkyd resin, a motor oil, a polyglycerin fatty acid ester, and a polyoxyethylene hardened castor oil were mixed and thoroughly dispersed with a three-roll mill. An oil phase was prepared by mixing and stirring a petroleum-based solvent with the extender dispersion. Next, a water-soluble dye, glycerin, and ion-exchanged water were mixed and stirred to dissolve the dye, thereby preparing an aqueous phase. While gradually dropping this aqueous phase into the oil phase, emulsification is performed with a stirrer,
An emulsion ink for stencil printing was obtained.
【0034】比較例1 まず、油溶性染料、アルキド樹脂、モーター油、石油系
溶剤、ポリグリセリン脂肪酸エステル、ポリオキシエチ
レン硬化ひまし油を混合・攪拌して染料を溶解させ、油
相を調製した。この油相中にグリセリンとイオン交換水
の混合溶液を徐々に滴下しながら攪拌機で乳化を行い、
孔版印刷用エマルションインキを得た。Comparative Example 1 First, an oil-soluble dye, an alkyd resin, a motor oil, a petroleum solvent, a polyglycerin fatty acid ester, and a polyoxyethylene hardened castor oil were mixed and stirred to dissolve the dye, thereby preparing an oil phase. While gradually dropping a mixed solution of glycerin and ion-exchanged water into the oil phase, emulsification was performed with a stirrer,
An emulsion ink for stencil printing was obtained.
【0035】比較例2 まず、アルキド樹脂、モーター油、石油系溶剤、ポリグ
リセリン脂肪酸エステル、ポリオキシエチレン硬化ひま
し油を混合して、油相を調製した。次に、水溶性染料、
グリセリン、イオン交換水を混合・攪拌して染料を溶解
させ、水相を調製した。この水相を油相中に徐々に滴下
しながら攪拌機で乳化を行い、孔版印刷用エマルション
インキを得た。Comparative Example 2 First, an alkyd resin, a motor oil, a petroleum solvent, a polyglycerin fatty acid ester, and a polyoxyethylene hardened castor oil were mixed to prepare an oil phase. Next, a water-soluble dye,
Glycerin and ion-exchanged water were mixed and stirred to dissolve the dye, thereby preparing an aqueous phase. The aqueous phase was gradually dropped into the oil phase and emulsified by a stirrer to obtain a stencil printing emulsion ink.
【0036】[0036]
【表1】 [Table 1]
【0037】実施例1〜7および比較例1、2でそれぞ
れ作製した孔版印刷用エマルションインキを用いて、孔
版印刷機(リソグラフ(登録商標)GR375、理想科学工業
株式会社製)により孔版印刷を行い、得られた印刷物の
滲みと裏抜けを目視により評価した。実施例1〜7、特
に実施例1〜5では、滲みや裏抜けの少ない画像が得ら
れたのに対し、比較例1および2では、滲みや裏抜けの
多い画像であった。Using the stencil emulsion inks prepared in Examples 1 to 7 and Comparative Examples 1 and 2, stencil printing was performed by a stencil printing machine (Risograph® GR375, manufactured by Riso Kagaku Corporation). The bleeding and strikethrough of the obtained printed matter were visually evaluated. In Examples 1 to 7, and particularly in Examples 1 to 5, images with little bleeding or strike-through were obtained, whereas in Comparative Examples 1 and 2, images with much bleeding or strike-through were obtained.
【0038】また、印刷機を一ヶ月間使用せずに放置し
た後、孔版印刷を行い、印刷機の状態と得られた印刷物
の画像性を評価した。実施例1〜7では、印刷機にトラ
ブルもなく良好な印刷物を得ることができた。比較例1
および2では、印刷機の版胴端部からインキが漏れ出て
いて清掃する必要があった上、得られた印刷物は細字が
つぶれていて判読困難なものであった。After the printing machine was left unused for one month, stencil printing was performed, and the condition of the printing machine and the image quality of the obtained printed matter were evaluated. In Examples 1 to 7, good prints could be obtained without any trouble in the printing press. Comparative Example 1
In Nos. 2 and 3, the ink leaked from the cylinder end of the printing press, necessitating cleaning, and the resulting printed matter was hardly legible because the fine print was broken.
【0039】[0039]
【発明の効果】本発明のW/O型エマルションインキは、
染料とともに体質顔料を含んでいるため、色彩が鮮明
で、インキの滲みや裏抜けが少ない画像を形成し、ま
た、印刷機を長期間使用しなかった後でも、版胴からの
インキ漏れ等のトラブルが少なく、良好な品質の画像を
得ることができる。The W / O emulsion ink of the present invention is
Since it contains extender pigments together with dyes, it produces clear images with less ink bleeding and strikethrough, and ink leakage from the plate cylinder even after the printer has not been used for a long time. Good quality images can be obtained with less trouble.
Claims (5)
エマルションインキにおいて、さらに、体質顔料を含む
ことを特徴とする孔版印刷用エマルションインキ。1. A stencil printing emulsion ink comprising a water-in-oil (W / O) emulsion ink containing a dye as a colorant, and further comprising an extender pigment.
あることを特徴とする請求項1に記載の孔版印刷用エマ
ルションインキ。2. The emulsion ink for stencil printing according to claim 1, wherein the dye is at least 30% by weight based on the total amount of the colorant.
とする請求項1又は2に記載の孔版印刷用エマルション
インキ。3. The emulsion ink for stencil printing according to claim 1, wherein the dye is an oil-soluble dye.
とする請求項1又は2に記載の孔版印刷用エマルション
インキ。4. The emulsion ink for stencil printing according to claim 1, wherein the dye is a water-soluble dye.
ョンの同一相に含有されている請求項1に記載の孔版印
刷用エマルションインキ。5. The emulsion ink for stencil printing according to claim 1, wherein the dye and the extender are contained in the same phase of the emulsion.