JP2000096443A - Textile fabric and its production - Google Patents
Textile fabric and its productionInfo
- Publication number
- JP2000096443A JP2000096443A JP10271053A JP27105398A JP2000096443A JP 2000096443 A JP2000096443 A JP 2000096443A JP 10271053 A JP10271053 A JP 10271053A JP 27105398 A JP27105398 A JP 27105398A JP 2000096443 A JP2000096443 A JP 2000096443A
- Authority
- JP
- Japan
- Prior art keywords
- binder
- fiber cloth
- textile fabric
- microcapsules
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明はハッカ油および/ま
たはl−メントールを添加することにより清涼感を与え
る繊維布帛に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fiber fabric which gives a refreshing feeling by adding mint oil and / or l-menthol.
【0002】[0002]
【従来の技術】ポリエステルやナイロン等の合成繊維は
優れた物理的および化学的特性を有しているため広く利
用されているが、その反面吸湿性が低く着用時に蒸れや
すい。また、帯電しやすいという欠点があり、改善が望
まれている。2. Description of the Related Art Synthetic fibers such as polyester and nylon are widely used because of their excellent physical and chemical properties, but they have low hygroscopicity and easily stuffy when worn. In addition, there is a disadvantage that it is easily charged, and improvement is desired.
【0003】このため特公昭60−34979号公報で
示されるように、合成繊維にアクリル酸やメタクリル酸
をグラフト重合させたり、特公昭58−46589号公
報に示されるように、ラジカル重合可能な親水性モノマ
ーをポリエステル繊維上で重合させる方法が提案されて
いる。For this reason, as disclosed in Japanese Patent Publication No. Sho 60-34979, acrylic acid or methacrylic acid is graft-polymerized onto synthetic fibers. A method has been proposed in which a hydrophilic monomer is polymerized on a polyester fiber.
【0004】しかし、これらの方法には性能や耐久性が
不十分であったり、風合いが硬くなったりする欠点があ
った。[0004] However, these methods have the drawbacks that the performance and durability are insufficient and the hand becomes hard.
【0005】また、マイクロカプセルを繊維に付与する
方法としては、香料を含むマイクロカプセルとアラビア
ゴム系糊剤を織物に浸漬付与する方法が特開昭49−1
9197号公報に、香料入りカルボキシルメチルセルロ
ース系マイクロカプセルをプリントする方法が特公昭5
3−47440号公報に、香料をポリアミド樹脂および
シリカゲルに吸着させ、ビニル系バインダーで繊維に付
与する方法が特開昭53−52561号公報に、香料入
りマイクロカプセルをアクリル系樹脂でタオル地に捺染
する方法が特開昭58−4886号公報に記載されてい
る。As a method of applying microcapsules to fibers, a method of immersing microcapsules containing a fragrance and a gum arabic paste in a woven fabric is disclosed in JP-A-49-1.
No. 9197 discloses a method for printing carboxymethylcellulose-based microcapsules containing a fragrance.
JP-A-3-47440 discloses a method in which a fragrance is adsorbed on a polyamide resin and silica gel, and a method of applying the fragrance to fibers with a vinyl binder is described in JP-A-53-52561. The method is described in JP-A-58-4886.
【0006】しかしながら、これらのマイクロカプセル
を付与する従来技術によってストッキングを加工すれ
ば、編み目が詰まる、風合いが硬化する、ストレッチ性
が低下するなどの問題があった。[0006] However, if the stocking is processed by the conventional technique of providing these microcapsules, there are problems such as clogging of stitches, hardening of texture, and deterioration of stretchability.
【0007】また、香料を含むマイクロカプセルをシリ
コーン系バインダーと共にストッキングに付与する方法
が特開平1−201501号公報に、香料入りホルマリ
ン系マイクロカプセルとシリコーン系バインダーを用い
る方法が特開平1−292183号公報に記載されてい
るが、香料入りカプセルの吸尽性のばらつきや着用時の
滑り易さが問題となる。Japanese Patent Application Laid-Open No. 1-250101 discloses a method of applying microcapsules containing a fragrance to a stocking together with a silicone-based binder, and Japanese Patent Application Laid-Open No. 1-292183 discloses a method of using a formalin-based microcapsule containing a fragrance and a silicone-based binder. As described in the official gazette, there are problems in the exhaustion of the scented capsule and the slipperiness when worn.
【0008】これらの欠点を解決すべく、耐久性のある
吸放湿性、制電性を有し、しかも柔軟な風合いを有する
繊維材料を得る方法として、ビニルカルボン酸および/
またはビニルスルホン酸モノマーを含む処理液を繊維材
料表面で重合させる方法が特開平8−209540号公
報で提案されている。この方法により、耐久性のある吸
湿性と制電性が得られるが、吸湿性だけでは清涼感が得
られなかった。[0008] In order to solve these drawbacks, vinyl carboxylic acid and / or vinyl carboxylic acid have been used as a method for obtaining a durable fiber material having moisture absorption / desorption properties, antistatic properties and a soft texture.
Alternatively, a method of polymerizing a treatment liquid containing a vinyl sulfonic acid monomer on the surface of a fiber material has been proposed in Japanese Patent Application Laid-Open No. 8-209540. According to this method, durable hygroscopicity and antistatic property were obtained, but a refreshing sensation was not obtained only with hygroscopicity.
【0009】[0009]
【発明が解決しようとする課題】本発明は、かかる従来
の背景に鑑み、十分な耐久性のある清涼感を有し、かつ
柔軟な風合いの繊維布帛を提供せんとするものである。SUMMARY OF THE INVENTION In view of the above background, an object of the present invention is to provide a fiber fabric having a sufficiently durable refreshing feeling and a soft texture.
【0010】[0010]
【課題を解決するための手段】本発明は十分な耐久性の
ある清涼感と柔軟な風合いを得るために、有機系樹脂を
壁材としたハッカ油および/またはl(エル)−メント
ールを内包したマイクロカプセルを繊維布帛にバインダ
ーにより接合されている繊維布帛を特徴とする。SUMMARY OF THE INVENTION The present invention includes mint oil and / or l-menthol containing an organic resin as a wall material in order to obtain a sufficiently durable cool feeling and a soft texture. The present invention is characterized by a fiber fabric in which the microcapsules thus formed are joined to the fiber fabric by a binder.
【0011】さらに、本発明は、有機系樹脂を壁材とし
ハッカ油および/またはl−メントールを内包したマイ
クロカプセルをビニルカルボン酸および/またはビニル
スルホン酸モノマー(以下、「モノマーA」という。)
と、一般式〔1〕および/または一般式〔2〕で示され
るジビニルモノマー(以下、「モノマーB」という。)
とを含む処理液が繊維材料の表面上に付与され重合され
てなることを特徴とする繊維布帛を特徴とする。Further, in the present invention, microcapsules containing an organic resin as a wall material and containing mint oil and / or 1-menthol are used as vinyl carboxylic acid and / or vinyl sulfonic acid monomers (hereinafter, referred to as "monomer A").
And a divinyl monomer represented by the general formula [1] and / or the general formula [2] (hereinafter, referred to as “monomer B”).
And fibrous fabric characterized in that a treatment liquid containing the above is applied onto the surface of the fiber material and polymerized.
【0012】[0012]
【化3】 Embedded image
【化4】 さらに、本発明は、有機系樹脂を壁材としハッカ油およ
び/またはl−メントールを内包したマイクロカプセル
をアクリル樹脂および/またはウレタン樹脂を主体にし
たバインダーで接合されている繊維布帛を特徴とする。Embedded image Furthermore, the present invention is characterized by a fiber fabric in which microcapsules containing an organic resin as a wall material and containing mint oil and / or l-menthol are bonded with a binder mainly composed of an acrylic resin and / or a urethane resin. .
【0013】[0013]
【発明の実施の形態】本発明でいうハッカ油およびl−
メントールとは、日本種のハッカおよび洋種のハッカを
水蒸気蒸留すると、留出する精油をハッカ油といい、さ
らにハッカ油を精製したものをl−メントールという。BEST MODE FOR CARRYING OUT THE INVENTION Mentha oil and l-
The menthol is obtained by steam distillation of Japanese mint and Western mint. The essential oil distilled out is called mint oil, and the refined mint oil is called 1-menthol.
【0014】本発明に用いるマイクロカプセルの壁材と
しては、有機系マイクロカプセルが好ましく、例えばポ
リスチレン、エチルセルロース、ポリアミド、ポリアク
リル酸、メラミン、シリコーン系樹脂などが挙げられ
る。As the wall material of the microcapsules used in the present invention, organic microcapsules are preferable, and examples thereof include polystyrene, ethyl cellulose, polyamide, polyacrylic acid, melamine, and silicone resins.
【0015】有機系マイクロカプセルの粒径は被膜強
度、凝集、製品品位の観点から、0.1〜20μの粒径
を有する微多孔質の無機粒子、または粒径0.1〜20
μの中空微多孔を有するメラミン系樹脂、アクリル系樹
脂などからなる有機系粒子が挙げられる。中でも、メラ
ミン樹脂系粒子のものは被膜強力、耐薬品、接着性、透
明性の点において優れており好ましい壁材である。The particle size of the organic microcapsules is selected from microporous inorganic particles having a particle size of 0.1 to 20 μm or particle sizes of 0.1 to 20 from the viewpoint of film strength, aggregation and product quality.
Organic particles composed of a melamine-based resin, an acrylic-based resin, or the like having a hollow microporosity of μ are included. Among them, melamine resin-based particles are preferable wall materials because they are excellent in film strength, chemical resistance, adhesiveness, and transparency.
【0016】本発明に用いうる繊維としては、合成繊維
ではポリエチレンテレフタレートやポリブチレンテレフ
タレートなどのポリエステル系繊維、ポリエステルに第
3成分を共重合した共重合ポリエステル系繊維、ナイロ
ン6やナイロン66等のポリアミド系繊維、ポリアミド
に第3成分を共重合した共重合ポリアミド系繊維、ポリ
アクリロニトリルを主成分とするアクリル系繊維、ポリ
塩化ビニル系繊維、セルロース系繊維、たんぱく質系繊
維などが挙げられこれらを混紡混繊した混用素材も含ま
れる。また、繊維布帛の形態としては、織編物、不織布
などのいかなる形態であってもよい。The fibers usable in the present invention include polyester fibers such as polyethylene terephthalate and polybutylene terephthalate as synthetic fibers, copolyester fibers obtained by copolymerizing a third component with polyester, and polyamides such as nylon 6 and nylon 66. Fibers, copolymerized polyamide fibers obtained by copolymerizing a third component with polyamide, acrylic fibers containing polyacrylonitrile as a main component, polyvinyl chloride fibers, cellulosic fibers, protein fibers, and the like. Includes delicate mixed materials. Further, the form of the fiber cloth may be any form such as a woven or knitted fabric or a nonwoven fabric.
【0017】請求項3について下記に詳しく説明する。Claim 3 will be described in detail below.
【0018】本発明で用いるバインダーとしては、溶液
の安定性、作業性、耐洗濯性、製品の風合い、の機能を
すべて同時に満足させることが重要である。It is important that the binder used in the present invention satisfies all the functions of solution stability, workability, washing resistance and texture of the product at the same time.
【0019】本発明に用いるモノマーAとしてはビニル
カルボン酸および/またはビニルスルホン酸が選ばれ
る。ビニルカルボン酸の具体例としては、アクリル酸、
メタクリル酸、マレイン酸、等が挙げられる。ビニルス
ルホン酸の具体例としては、2−アクリルアミド−2−
メチルプロパンスルホン酸(以下、「AMPS」とい
う。)、2−アリルオキシ−2−ヒドロキシプロンスル
ホン酸、スチレンスルホン酸ナトリウムなどが挙げられ
る。本発明では、これらのモノマー2種類以上用いるこ
とも何ら差し支えない。特に重合効率と吸湿性の面か
ら、アクリル酸、メタクリル酸、AMPS、スチレンス
ルホン酸ナトリウムが好ましい。As the monomer A used in the present invention, vinyl carboxylic acid and / or vinyl sulfonic acid are selected. Specific examples of vinyl carboxylic acid include acrylic acid,
Examples include methacrylic acid and maleic acid. Specific examples of vinyl sulfonic acid include 2-acrylamide-2-
Examples include methylpropanesulfonic acid (hereinafter, referred to as “AMPS”), 2-allyloxy-2-hydroxypronsulfonic acid, and sodium styrenesulfonate. In the present invention, two or more of these monomers may be used at all. In particular, acrylic acid, methacrylic acid, AMPS, and sodium styrenesulfonate are preferred from the viewpoint of polymerization efficiency and hygroscopicity.
【0020】本発明に用いるモノマーBの一種は下記一
般式〔1〕で表され、N=9〜23であるものである。One kind of the monomer B used in the present invention is represented by the following general formula [1], wherein N = 9 to 23.
【0021】[0021]
【化5】 nが9より小さくても23より大きくても十分な耐久性
が得られない。制電性の面から、n=14〜23の範囲
であることがモノマーBとして好ましい。Embedded image If n is smaller than 9 or larger than 23, sufficient durability cannot be obtained. From the viewpoint of antistatic properties, the monomer B is preferably in the range of n = 14 to 23.
【0022】またモノマーBの他の種は、下記一般式
〔2〕で表され、M+N=10〜30であるものであ
る。Another type of the monomer B is represented by the following general formula [2], wherein M + N = 10 to 30.
【0023】[0023]
【化6】 モノマーBとして、一般式〔1〕、〔2〕のモノマーを
それぞれ単独でも用いることができ、また一般式〔1〕
および一般式〔2〕のものを併用してもよく、更に一般
式〔1〕、〔2〕で表されるものに含まれる2種以上の
ものを用いても何ら差し支えない。また、Xについては
安全の面からはX=CH3 を用いることが好ましい。Embedded image As the monomer B, the monomers of the general formulas [1] and [2] can be used alone, and the monomers of the general formula [1]
And the general formula [2] may be used in combination, and two or more of the general formulas [1] and [2] may be used. As for X, it is preferable to use X = CH 3 from the viewpoint of safety.
【0024】本発明に用いる重合開始剤としては、通常
のラジカル開始剤を使用できる。例えば、過硫酸アンモ
ニウム、過硫酸カリウム、過酸化水素など無機塩基など
無機系重合開始剤や2.2’−アゾビス(2−アミディ
ノプロパン)ジハイドロクロライド、2.2’−アゾビ
ス(N,N−ジメチレンイソブチラミディン)ジハイド
ロクロライド、2−(カルバモイラゾ)イソブチロニト
リルなどの有機系重合開始剤が挙げられる。また、過酸
化ベンゾイル、アゾビスイソブチロニトリルなどの水不
溶性重合開始剤をアニオン、ノニオン等の界面活性剤で
乳化させても用いてもよい。As the polymerization initiator used in the present invention, a usual radical initiator can be used. For example, inorganic polymerization initiators such as inorganic bases such as ammonium persulfate, potassium persulfate, and hydrogen peroxide, and 2.2′-azobis (2-amidinopropane) dihydrochloride, 2.2′-azobis (N, N- Organic polymerization initiators such as dimethyleneisobutyramidin) dihydrochloride and 2- (carbamoylazo) isobutyronitrile. Further, a water-insoluble polymerization initiator such as benzoyl peroxide or azobisisobutyronitrile may be used after being emulsified with a surfactant such as an anion or nonion.
【0025】処理液を繊維材料に付与する方法として
は、通常用いられる手段が適応可能である。例えば、パ
ディング法、スプレー法、キスロールコータ、スリット
コータなどが挙げられる。As a method of applying the treatment liquid to the fiber material, a commonly used means can be applied. For example, a padding method, a spray method, a kiss roll coater, a slit coater and the like can be mentioned.
【0026】本発明において、モノマーAとモノマーB
を重合させる方法としては、ラジカル重合に用いられる
あらゆる手段が適応可能である。例えば、乾熱処理、ス
チーム処理、浸漬法、コールドバッチ法、マイクロ波処
理、紫外線処理などが挙げられる。マイクロ波処理と
は、2450MHzまたは920MHzの波長の高周波
を被加熱物に当てることで発熱させるものである。これ
らの処理手段は、単独で適応してもよいし、加熱効率を
高めるために、例えば、スチーム処理または乾熱処理時
にマイクロ波処理または紫外線処理を併用するなどして
もよい。なお、空気中の酸素が存在すると重合が進みに
くくなるので、乾熱処理、マイクロ波処理、紫外線処理
の場合は、不活性ガス雰囲気下で処理することが好まし
く、コールバッチ法の場合にも、シールド剤で密封する
ことが好ましい。In the present invention, monomer A and monomer B
Any method used for radical polymerization can be applied as a method for polymerizing. For example, dry heat treatment, steam treatment, immersion method, cold batch method, microwave treatment, ultraviolet treatment and the like can be mentioned. The microwave treatment is to generate heat by applying a high-frequency wave having a wavelength of 2450 MHz or 920 MHz to an object to be heated. These treatment means may be applied alone, or may be combined with microwave treatment or ultraviolet treatment at the time of steam treatment or dry heat treatment, for example, in order to increase the heating efficiency. In the case of dry heat treatment, microwave treatment, and ultraviolet treatment, it is preferable that the treatment be performed in an inert gas atmosphere. It is preferable to seal with an agent.
【0027】これらの重合法の中では、スチーム処理が
重合効率および処理の安定性の観点から好適である。ス
チーム処理は、常圧スチーム、加熱スチーム、高圧スチ
ームのいずれでもよいがコスト面からは、常圧スチーム
または加熱スチームが好ましい。スチーム処理温度は、
80〜180℃さらには100〜160℃が好ましい。
スチーム処理時間は1〜10分程度でよい。Among these polymerization methods, steam treatment is preferred from the viewpoints of polymerization efficiency and treatment stability. The steam treatment may be any of normal pressure steam, heating steam, and high pressure steam, but from the viewpoint of cost, normal pressure steam or heating steam is preferable. The steam processing temperature is
80-180 ° C, more preferably 100-160 ° C.
The steam processing time may be about 1 to 10 minutes.
【0028】なお、本発明において、繊維材料に処理液
を付与した後、モノマーAとモノマーBを重合させる前
に、風乾あるいは乾燥機などで予備乾燥することも好ま
しく行われる。In the present invention, after the treatment liquid is applied to the fiber material, before the monomer A and the monomer B are polymerized, the fiber material is preferably preliminarily dried by air drying or a drier.
【0029】本発明の処理液による重合物の付着量は、
吸湿性能を優れたものにし、一方、風合いの粗硬化を防
ぐ観点から、繊維材料に対して1〜20重量%とするこ
とが好ましい。The amount of polymer adhered by the treatment liquid of the present invention is as follows:
From the viewpoint of improving the moisture absorption performance and preventing rough hardening of the texture, the content is preferably 1 to 20% by weight based on the fiber material.
【0030】次に請求項4について詳しく説明する。Next, claim 4 will be described in detail.
【0031】本発明に用いるバインダーとしては、アク
リル樹脂またはウレタン樹脂を主体とするものからなっ
ているものである。かかるアクリル樹脂またはウレタン
樹脂を主体に用いることにより、マイクロカプセルを保
持し耐久性のある加工を達成することができる。ここで
主体とは、バインダーの固形分比で4割以上を占めるこ
とを意味する。かかる主体とするアクリル樹脂またはウ
レタン樹脂以外のバインダーとしてはシリコーン樹脂、
メラミン樹脂、ポリエステル樹脂、ポリアミド樹脂およ
び酢酸ビニール樹脂から選ばれた少なくとも1種を使用
することができる。The binder used in the present invention is a binder mainly composed of an acrylic resin or a urethane resin. By mainly using such an acrylic resin or a urethane resin, it is possible to hold the microcapsules and achieve durable processing. Here, “mainly” means that the binder occupies 40% or more of the solid content ratio. As a binder other than the acrylic resin or urethane resin as the main component, a silicone resin,
At least one selected from melamine resin, polyester resin, polyamide resin and vinyl acetate resin can be used.
【0032】本発明の繊維布帛の製造方法としては、ハ
ッカ油および/またはl−メントール内包のマイクロカ
プセルとpH調整剤とバインダーからなる処理剤に繊維
布帛を浸漬し、好ましくは50〜100℃の温度で浴中
処理し、繊維布帛にマイクロカプセルとバインダーの任
意の量をある一定の浴比に入れ、50〜100℃まで加
熱し、pH調整剤の温度によるpH変化を利用して繊維
布帛に付着させる方法が好ましく適用できる。この浴中
処理により繊維の1本1本にマイクロカプセルとバイン
ダーが概略均一に被膜化することにより、マイクロカプ
セル保持性がよくなり、かつ、風合いの良いものを提供
することができるのである。As a method for producing the fiber cloth of the present invention, the fiber cloth is immersed in a treating agent comprising mint oil and / or microcapsules containing 1-menthol, a pH adjuster and a binder, preferably at 50 to 100 ° C. Treated in a bath at a temperature, put an arbitrary amount of microcapsules and a binder in the fiber cloth at a certain bath ratio, heat to 50 to 100 ° C, and use the pH change due to the temperature of the pH adjuster to produce a fiber cloth. The method of attaching is preferably applicable. The microcapsules and the binder are coated almost uniformly on each of the fibers by the treatment in the bath, so that the microcapsules can be maintained well and a good texture can be provided.
【0033】本発明の繊維布帛は、ドレスシャツ、イン
ナー、レッグニット類に使用されることを特徴とする。
よって、l−メントールおよび/またはハッカ油のマイ
クロカプセルが付着した繊維布帛が肌に直接触れていた
方が清涼感が効率よく得られ、コートやセーター等のア
ウターに本発明を利用しても肌に直接触れていないので
本発明の特徴の清涼感が得られなくなってしまい好まし
くない。The fiber fabric of the present invention is characterized in that it is used for dress shirts, innerwear and leg knits.
Therefore, when the fibrous fabric to which l-menthol and / or mint oil microcapsules are attached is in direct contact with the skin, a refreshing feeling can be obtained more efficiently. Is not directly touched, so that the refreshing feeling of the present invention cannot be obtained, which is not preferable.
【0034】[0034]
【実施例】以下、実施例および比較例を用いて本発明を
さらに具体的に説明する。The present invention will be described more specifically below with reference to examples and comparative examples.
【0035】なお、実施例中に記載した各種性能は以下
のようにして評価した。The various performances described in the examples were evaluated as follows.
【0036】[洗濯]自動反転渦巻き式電気洗濯機(東
芝(株)製;VH−1150と同性能のもの)に、45
cm×45cmの試験布を500gと40±2℃の0.
2%弱アルカリ性合成洗剤(JIS K−3371弱ア
ルカリ性・第1種)液25lとを入れ、強条件で25分
洗濯した。次いで、遠心脱水機で30秒間脱水後、常温
水をオーバーフローさせながら10分間すすぎを行っ
た。その後、再度、30秒間脱水し、同条件で10分間
すすいだ前記方法を洗濯5回とする。これを4回繰り返
し洗濯20回と表示した。[Washing] An automatic reversing spiral electric washing machine (manufactured by Toshiba Corporation; having the same performance as that of VH-1150) was used.
500 g of a test cloth of 45 cm × 45 cm and 0.4 g of 40 ± 2 ° C.
25 l of a 2% weakly alkaline synthetic detergent (JIS K-3371 weakly alkaline type 1) solution was added, and washing was performed under strong conditions for 25 minutes. Next, after dehydration for 30 seconds by a centrifugal dehydrator, rinsing was performed for 10 minutes while overflowing normal-temperature water. After that, dehydration is performed again for 30 seconds, and the above method of rinsing for 10 minutes under the same conditions is repeated five times. This was repeated four times and indicated as washing 20 times.
【0037】[樹脂付着量] 樹脂付着量(%)={(A−B)/B}×100 ここで、A:加工後の生地重量 B:加工前の生地重量 ここで、生地重量とは20℃×65%RH雰囲気下に2
4時間放置したときの重量をいう。[Resin Adhesion Amount] Resin adhesion amount (%) = {(AB) / B} × 100 where A: fabric weight after processing B: fabric weight before processing 2 at 20 ° C x 65% RH
The weight when left for 4 hours.
【0038】[吸湿性(ΔMR)] ΔMR(%)=MR2 −MR1 ここで、MR1 とは絶乾状態から20℃×65%RH雰
囲気下に24時間放置したときの吸湿率(%)をいい、
洋服ダンスの中に入っている状態、すなわち着用前の環
境に相当する。また、MR2 とは絶乾状態から30℃×
90%RH雰囲気下に24時間放置したときの吸湿率
(%)をいい、運動状態における衣服内の環境に相当す
る。[Hygroscopicity (ΔMR)] ΔMR (%) = MR 2 −MR 1 Here, MR 1 is a moisture absorption rate (%) when allowed to stand in a 20 ° C. × 65% RH atmosphere from an absolutely dry state for 24 hours. ),
This corresponds to the state of being in the clothes dance, that is, the environment before wearing. Also, MR 2 is 30 ° C x
Moisture absorption (%) when left in a 90% RH atmosphere for 24 hours, and corresponds to the environment in clothes under exercise conditions.
【0039】ΔMRは、MR2 からMR1 の値を差し引
いた値で表せるものであり、衣服を着用してから運動し
たときに、衣服内のムレをどれだけ吸収するかに相当
し、ΔMR値が高いほど快適であるといえる。一般にポ
リエステルのΔMRは0%、ナイロンで2%、木綿で4
%、ウールで、6%といわれる。[0039] ΔMR are those represented by the value obtained by subtracting the value of the MR 1 from MR 2, when the movement from wearing the clothes, equivalent to or absorb much of the stuffiness of the clothes, ΔMR value The higher the is, the more comfortable it is. Generally, ΔMR of polyester is 0%, 2% for nylon and 4% for cotton.
%, Wool, 6%.
【0040】[清涼感]加工したものと未加工のものを
モニターに着用してもらい、どちらが涼しく感じたか官
能的な評価方法でアンケートをとった。今回の場合、1
0人に着用してもらい、「涼しい」と感じた人が9人以
上の場合は○、7〜8人の場合は○〜△、5〜6人の場
合は△、3〜4人の場合は△〜×、2人以下の場合は×
とした。[Cooling feeling] The processed and unprocessed ones were worn on a monitor, and a questionnaire was taken by a sensory evaluation method to determine which one felt cooler. In this case, 1
0 people wear it and feel “cool” if 9 or more people are ○, 7-8 people ○-△, 5-6 people △, 3-4 people △ ~ × × 2 or less
And
【0041】[摩擦帯電圧]試験片と綿布を20℃×3
0%RHの雰囲気中に24時間放置後、京大化研式ロー
タリースタティックテスタを用い、20℃×30%RH
の雰囲気中で両者を摩擦させ、帯電圧を測定した。(J
IS L 1094の規定による) [供試生地]実施例の供試生地には、ポリエステル10
0%織物(番手40×40、密度128×83本/イン
チ)と、ナイロン6加工糸とポリウレタン弾性糸からな
るストッキングを用いた。[Friction charging voltage] A test piece and a cotton cloth were placed at 20 ° C. × 3.
After leaving in an atmosphere of 0% RH for 24 hours, using a rotary static tester of Kyoto University Kaken type, 20 ° C. × 30% RH
The two were rubbed in the same atmosphere, and the charged voltage was measured. (J
[Specimen under test] Polyester 10 was used as the sample under test in the examples.
A stocking composed of a 0% woven fabric (count 40 × 40, density 128 × 83 / inch) and nylon 6 processed yarn and polyurethane elastic yarn was used.
【0042】[風合い]生地を掴んだときの感触を、非
常に柔らかい、柔らかい、やや硬い、硬い、非常に硬い
の5段階で評価した。[Feel] The feeling when the fabric was grasped was evaluated on a five-point scale: very soft, soft, slightly hard, hard, and very hard.
【0043】実施例1 供試生地のポリエステル100%織物を下記組成の処理
液に浸漬後、ピックアップ率80%に設定したマングル
で絞り、乾燥機で120℃、2分間乾燥させた。マイク
ロカプセルは壁材がメラミンのものを使用した。Example 1 A 100% polyester fabric of a test fabric was immersed in a treatment solution having the following composition, squeezed with a mangle set at a pickup ratio of 80%, and dried at 120 ° C. for 2 minutes with a drier. The microcapsules used had a wall material of melamine.
【0044】 マイクロカプセル化したl−メントール(固形分40%) 10g/l AMPS 20g/l 一般式[1]においてX:−CH3、n=23のモノマー 40g/l N−メチロールアクリルアミド 7g/l 過硫酸アンモニウム 2g/l 乾燥後、直ちに、105℃の加熱スチーマーで5分間処
理し、湯水洗、乾燥した。次いで、乾燥機で170℃、
1分間セットし、評価を行った。結果は表1に示す。Microencapsulated 1-menthol (solid content: 40%) 10 g / l AMPS 20 g / l In the general formula [1], X: —CH 3, n = 23 monomer 40 g / l N-methylolacrylamide 7 g / l excess Immediately after the ammonium sulfate was dried at 2 g / l, the mixture was treated with a heated steamer at 105 ° C for 5 minutes, washed with hot and cold water, and dried. Then, 170 ° C in a dryer,
It was set for one minute and evaluated. The results are shown in Table 1.
【0045】実施例2供試生地のポリエステル100%
織物を下記組成の処理液に浸漬後、実施例1と同じ処理
を施して試料を作製した。マイクロカプセルは壁材がメ
ラミンのものを使用した。評価結果を表1に示す。Example 2 100% polyester of the test cloth
After immersing the woven fabric in a treatment solution having the following composition, the same treatment as in Example 1 was performed to prepare a sample. The microcapsules used had a wall material of melamine. Table 1 shows the evaluation results.
【0046】 マイクロカプセル化したl−メントール(固形分40%) 10g/l AMPS 20g/l 一般式[2]においてX:−CH3、n=23のモノマー 40g/l N−メチロールアクリルアミド 7g/l 過硫酸アンモニウム 2g/l 実施例3 加工剤を下記配合で秤量した。マイクロカプセルは壁材
がメラミンのものを使用した。Microencapsulated l-menthol (solid content: 40%) 10 g / l AMPS 20 g / l In the general formula [2], X: —CH3, monomer of n = 23 40 g / l N-methylolacrylamide 7 g / l excess Ammonium sulfate 2 g / l Example 3 A processing agent was weighed with the following composition. The microcapsules used had a wall material of melamine.
【0047】 マイクロカプセル化したl−メントール(固形分40%) 6%owf アクリル樹脂(固形分40%) 5%owf シリコーン樹脂(固形分40%) 2%owf pH調整剤 4%owf 秤量した加工剤を浴比1:20のドラム染色機の中に入
れ、ナイロン6加工糸とポリウレタン弾性糸からなるス
トッキングと加工剤をドラム染色機にて昇温2℃/分で
90℃まで加熱し、30分キ−プした後、ストッキング
を取り出し水洗し、120℃で30秒間乾燥、セット
し、評価を行った。結果を表2に示す。Microencapsulated l-menthol (solid content 40%) 6% owf acrylic resin (solid content 40%) 5% owf silicone resin (solid content 40%) 2% owf pH adjuster 4% owf Weighed processing The agent was put into a drum dyeing machine having a bath ratio of 1:20, and the stocking composed of nylon 6 processed yarn and polyurethane elastic yarn and the processing agent were heated to 90 ° C. at a rate of 2 ° C./min by a drum dyeing machine. After the capping, the stockings were taken out, washed with water, dried and set at 120 ° C. for 30 seconds, and evaluated. Table 2 shows the results.
【0048】実施例4 加工剤を下記配合で秤量した。マイクロカプセルは壁材
がメラミンのものを使用した。Example 4 A processing agent was weighed in the following composition. The microcapsules used had a wall material of melamine.
【0049】 マイクロカプセル化したl−メントール 6%owf ウレタン樹脂(固形分40%) 5%owf シリコーン樹脂(固形分40%) 2%owf pH調整剤 4%owf 秤量した加工剤を浴比1:20のドラム染色機の中に入
れ、ナイロン6加工糸とポリウレタン弾性糸からなるス
トッキングと加工剤をドラム染色機にて昇温2℃/分で
90℃まで加熱し、30分キ−プした後、ストッキング
を取り出し水洗し、120℃で30秒間乾燥、セット
し、評価を行った。結果を表2に示す。Microencapsulated l-menthol 6% owf urethane resin (solid content 40%) 5% owf silicone resin (solid content 40%) 2% owf pH adjuster 4% ow After placing in a drum dyeing machine No. 20, the stocking made of nylon 6 processed yarn and polyurethane elastic yarn and the processing agent were heated to 90 ° C. at a rate of 2 ° C./minute by a drum dyeing machine, and kept for 30 minutes. The stockings were taken out, washed with water, dried at 120 ° C. for 30 seconds, set, and evaluated. Table 2 shows the results.
【0050】比較例1 供試生地のポリエステル100%織物を下記組成の処理
液に浸漬後、ピックアップ率80%に設定したマングル
で絞り、乾燥機で120℃、2分間乾燥させた。Comparative Example 1 A 100% polyester fabric of a test fabric was immersed in a treatment solution having the following composition, squeezed with a mangle set at a pickup ratio of 80%, and dried at 120 ° C. for 2 minutes with a drier.
【0051】 AMPS 20g/l 一般式[1]においてX:−CH3、n=23のモノマー 40g/l N−メチロールアクリルアミド 7g/l 過硫酸アンモニウム 2g/l 乾燥後、直ちに、105℃の加熱スチーマーで5分間処
理し、湯水洗、乾燥した。次いで、乾燥機で170℃、
1分間セットし、評価を行った。結果は表1に示す。AMPS 20 g / l In the general formula [1], X: —CH 3, n = 23 monomer 40 g / l N-methylolacrylamide 7 g / l ammonium persulfate 2 g / l The mixture was treated for a minute, washed with hot water, and dried. Then, 170 ° C in a dryer,
It was set for one minute and evaluated. The results are shown in Table 1.
【0052】比較例2 供試生地のポリエステル100%織物を下記組成の処理
液に浸漬後、ピックアップ率80%に設定したマングル
で絞り、乾燥機で120℃、2分間乾燥させた。Comparative Example 2 A 100% polyester fabric of the test fabric was immersed in a treatment solution having the following composition, squeezed with a mangle set at a pickup ratio of 80%, and dried at 120 ° C. for 2 minutes with a drier.
【0053】 AMPS 20g/l 一般式[2]においてX:−CH3、n=23のモノマー 40g/l N−メチロールアクリルアミド 7g/l 過硫酸アンモニウム 2g/l 乾燥後、直ちに、105℃の加熱スチーマーで5分間処
理し、湯水洗、乾燥した。次いで、乾燥機で170℃、
1分間セットし、評価を行った。結果は表1に示す。AMPS 20 g / l In the general formula [2], X: —CH 3, n = 23 monomer 40 g / l N-methylolacrylamide 7 g / l ammonium persulfate 2 g / l The mixture was treated for a minute, washed with hot water, and dried. Then, 170 ° C in a dryer,
It was set for one minute and evaluated. The results are shown in Table 1.
【0054】比較例3 供試生地のポリエステル100%織物を加工を施さず、
そのまま評価に用いた。評価結果を表1に示す。Comparative Example 3 A 100% polyester woven fabric of the test fabric was not processed.
It was used for evaluation as it was. Table 1 shows the evaluation results.
【0055】比較例4 供試生地のナイロン6加工糸とポリウレタン弾性糸から
なるストッキングに加工を施さず、そのまま評価に用い
た。評価結果を表2に示す。Comparative Example 4 A stocking composed of a nylon 6 processed yarn and a polyurethane elastic yarn of a test cloth was not subjected to processing, and was used for evaluation as it was. Table 2 shows the evaluation results.
【0056】[0056]
【表1】 [Table 1]
【表2】 表1、表2から明らかなように、実施例のものは、比較
例のものに比較して、清涼感があり、風合いが柔らかく
耐久性に優れていることがわかる。[Table 2] As is clear from Tables 1 and 2, it can be seen that those of Examples have a refreshing feeling, soft texture and excellent durability as compared with those of Comparative Examples.
【0057】[0057]
【発明の効果】本発明によれば、清涼感の耐久性が非常
に優れ、風合いの柔軟な繊維布帛が得られる。According to the present invention, it is possible to obtain a fiber fabric having very excellent refreshing durability and a soft texture.
───────────────────────────────────────────────────── フロントページの続き Fターム(参考) 4L031 AB01 BA13 BA17 BA31 CA07 CA08 DA00 DA14 DA20 4L033 AB01 AB04 AC02 AC06 AC15 BA21 BA77 BA96 CA18 CA36 CA50 CA59 DA02 ──────────────────────────────────────────────────の Continued on the front page F term (reference) 4L031 AB01 BA13 BA17 BA31 CA07 CA08 DA00 DA14 DA20 4L033 AB01 AB04 AC02 AC06 AC15 BA21 BA77 BA96 CA18 CA36 CA50 CA59 DA02
Claims (6)
またはl−メントールを内包したマイクロカプセルが繊
維布帛にバインダーにより接合されていることを特徴と
する繊維布帛。1. A mint oil containing an organic resin as a wall material and / or
Alternatively, a fiber cloth characterized in that microcapsules containing l-menthol are bonded to the fiber cloth with a binder.
ポリスチレン、エチルセルロース、ポリアミド、ポリア
クリル酸、メラミン、シリコーン系樹脂から選ばれた少
なくとも1種であることを特徴とする請求項1に記載の
繊維布帛。2. The organic resin wall material of the microcapsule,
The fiber cloth according to claim 1, wherein the fiber cloth is at least one selected from polystyrene, ethyl cellulose, polyamide, polyacrylic acid, melamine, and silicone resin.
び/またはビニルスルホン酸モノマーと下記一般式
[1]および/または一般式[2]で示されるジビニル
モノマーであることを特徴とする請求項1または2に記
載の繊維布帛。 【化1】 【化2】 3. The method according to claim 1, wherein the binder is a vinyl carboxylic acid and / or vinyl sulfonic acid monomer and a divinyl monomer represented by the following general formula [1] and / or general formula [2]. 3. The fiber fabric according to 2. Embedded image Embedded image
またはウレタン樹脂を主体とするものからなることを特
徴とする請求項1または2に記載の繊維布帛。4. The method according to claim 1, wherein the binder is an acrylic resin and / or
3. The fiber cloth according to claim 1, wherein the fiber cloth is mainly composed of a urethane resin.
またはl−メントールを内包したマイクロカプセルとバ
インダーからなる処理剤を繊維布帛に付与し、繊維布帛
にマイクロカプセルをバインダーにより結合させること
を特徴とする繊維布帛の製造方法。5. A mint oil and / or an organic resin as a wall material.
Alternatively, a method for producing a fiber cloth, comprising applying a treatment agent comprising a microcapsule containing l-menthol and a binder to the fiber cloth, and binding the microcapsule to the fiber cloth with a binder.
が、ドレスシャツ、インナー、またはレッグニットのい
ずれかに使用されていることを特徴とする繊維布帛製
品。6. A fiber fabric product, wherein the fiber fabric according to any one of claims 1 to 4 is used for a dress shirt, an inner, or a leg knit.