IL107976A - Cemented carbide with binder phase enriched surface zone and method for its manufacture - Google Patents

Description

CEMENTED CARBIDE WITH BINDER PHASE ENRICHED SURFACE ZONE AND METHOD FOR THE MANUFACTURE THEREOF inpgn"? πϋ'Βπ ιυρη imn ΠΤΝΕΠ nw TITNΊνι pmm vmp 1 107,976/2 The present invention relates to coated cemented carbide inserts with a binder phase enriched surface zone and a process for the making of same. More particularly, the present invention relates to coated inserts in which the binder phase enriched surface zone has been modified in such a way that a unique combination of toughness behavior and plastic deformation resistance can be achieved.

The present specification relates to an invention which is a modification of the invention described and claimed in Israel Specification 104,747, filed on February 16, 1993.

In Israel Specification 104,747, there is described and claimed a cemented carbide insert with improved toughness and resistance against plastic deformation, containing WC and cubic phases of carbide and/or carbonitride in a binder phase based on Co and/or Ni with a binder phase enriched surface zone, wherein the total amount of cubic phase expressed as the content of metallic elements that forms cubic carbides is between 6-15 wt.%, the content of cubic phases in the binder phase enriched zone, other than the surface, is essentially zero, and in a zone < 300 μπι thick below the binder phase enriched surface zone, the binder phase content is 0.85-1 times the binder phase content in the inner portion of the insert, with the content of cubic phases essentially constant and equal to the content of cubic phases in the inner portion of the insert.

The present specification is directed to a cemented carbide body containing WC and cubic phases in a binder phase enriched surface zone, wherein the binder phase enriched surface zone has an outer portion essentially free of cubic phase and an essentially constant binder content and an inner portion containing cubic phase and stratified binder phase layers in which the tungsten content is less than the norminal tungsten content of the body as a whole and is no more than 95% of the nominal tungsten content of the cemented carbide at any point within the said inner portion. 1A 107,976/1 Coated cemented carbide inserts with binder phase enriched surface zone are today used to a great extent for machining of steel and stainless materials. Through the binder phase enriched surface zone an extension of the application area is obtained.

Methods of producing binder phase enriched surface zones on cemented carbides containing WC, cubic phase and binder phase are known as gradient sintering and have been known for some time, e.g., through Tobioka (US Patent 4,277,283, Nemeth (US Patent 4,610,931), Taniguchi (US Patent 4,830,283) and Okada (US Patent 5, 106, 674) .

The patents by Tobioka and Nemeth disclose methods to accomplish binder phase enrichment by dissolution of the cubic phase close to the insert surfaces. Their methods require that the cubic phase contains some nitrogen, since dissolution of cubic phase at the sintering temperature requires a partial pressure of nitrogen, nitrogen activity, within the body being sintered exceeding the partial pressure of nitrogen within the sintering atmosphere. The nitrogen can be added through the powder and/or the furnace atmosphere at the beginning of the sintering cycle. The dissolution of cubic phase results in small volumes that will be filled with binder phase giving the desired binder phase enrichment. As a result, a surface zone generally about 25 um thick consisting of essentially WC and binder phase is obtained. Below this zone a zone with an enrichment of cubic phase and a corresponding depletion in binder phase is obtained. As a consequence, this zone is embrittled and cracks grow more easily. A method of elimination of this latter zone is disclosed in Swedish patent application 9200530-5.

Binder phase enriched surface zones can also be accomplished by controlled cooling, e.g. according to the patent by Okada or by controlled decarburization at constant temperature in the solid/liquid region of the binder phase after sintering or in the process of sintering e.g. according to the patent by Taniguchi. The structure in this kind of binder enriched cemented carbide inserts is characterised by an up to 25-35 |im thick surface zone containing stratified layers, 1 - 3 um in thickness, of binder phase mainly parallel to the surface. The thickest and most continuous layers are found close to the surface within the first 15 jam. Furthermore, the interior of the insert is characterized by a certain amount of free carbon.

The ability for certain cemented carbides to form a stratified structure has been known for a long time. The degree of binder phase enrichment in the zone and its depth below the surface depend strongly on the interstitial balance and on the cooling rate through the solidification region, after sinter-ing. The interstitial balance i.e. the ratio between the amount of carbide/nitride forming elements and the amount of carbon and nitrogen, has to be controlled within a narrow composition range for controlled formation of the stratified layers.

Cemented carbides with a binder phase enrichment formed by dissolution of the cubic phase are normally characterised by, in comparison with stratified ones, a rather low toughness behaviour in combination with a very high plastic deformation resistance. The comparably low toughness level and high deformation resistance shown by this type of cemented carbides are largely due to the enrichment of cubic phase and the corresponding binder phase depletion in a zone below the binder phase enriched zone.

Cemented carbides containing stratified binder phase gradients are normally characterised by extremely good toughness be-haviour in combination with somewhat inferior plastic deformation resistance. The toughness behaviour is a result of both the binder phase enrichment and the stratified structure of the binder phase enrichment. The reduced plastic deformation resis- 3 107,976/2 tance is to the dominating part caused by local sliding in the thick binder phase stratified layers closest to the surface due to the very high shear stresses in the cutting zone.

Surprisingly, it has now been found that by combining binder phase enrichment by dissolution of cubic phase with the requirements that result in formation of stratified layers a unique structure is obtained. The structure according to the invention is characterised by, in comparison with the .ones previously known, deeper situated stratified layers and lower and less sharp maximum binder phase enrichment. The possibility of combining dissolution of the cubic phase with formation of stratified layers offers new ways to optimize the properties of tungsten carbide based cemented carbides for cutting tools.

Fig 1 shows in 1200 X the structure of a binder phase enriched surface zone according to the present invention.

Fig 2 shows the distribution of Ti, Co and in the binder phase enriched surface zone according to the present invention.

In fig 1 and 2 A+B refers to the binder phase enriched surface zone, C is an inner zone and S refers to stratified layers of binder phase. 3A 107,976/1 The present specification provides a cemented carbide body containing WC and cubic phases in a binder phase enriched surface zone, wherein the binder phase enriched surface zone has an outer portion essentially free of cubic phase and an essentially constant binder content and an inner portion containing cubic phase and stratified binder phase layers in which the tungsten content is less than the norminal tungsten content of the body as a whole and is no more than 95% of the nominal tungsten content of the cemented carbide at any point within the said inner portion.

In the cemented carbide body of the present invention, said surface zone is <75 μηι, said outer portion is >10 μπ. and said inner portion is >10 μπι thick. In preferred embodiments of the invention, said surface zone is 20-50 μπι, said outer portion is <25 μη , and said inner portion is <30 μιη thick.

In the inner portion of the cemented carbide body of the invention, the binder phase content is above the nominal binder phase content of the body as a whole, and has a maximum of 1.5-4 times the nominal binder phase content. In preferred embodiments, the binder phase content has a maximum of 2-3 times the nominal binder phase content.

The invention also provides a method of manufacturing binder phase enriched cemented carbide, said method comprising sintering a presintered or green cemented carbide body containing nitrogen and carbon in an inert atmosphere of in vaccum for 15 to 180 minutes at between 1380-1520°C, followed by slow cooling at a rate of 20-100°C per hour through the solidification region at a temperature of 1300-1220°C.

Said method also comprises sintering a cemented carbide body subutectic in carbon content in a carburizing atmosphere containing a mixture of CH4/H2 and/or CO2/CO for 30-180 minutes at 1380-1520°C, followed by slow cooling at a rate no greater than 100°C per hour in the same atmosphere or in an inert 4 107,976/2 atmosphere or vacuum. In preferred embodiments of the invention, the cemented carbide body subutectic in carbon content has a porosity of CO4-C08.

The present invention is applicable to cemented carbides with varying amounts of binder phase and cubic phase. The binder phase preferably contains cobalt and dissolved carbide forming elements such as tungsten, titanium, tantalum and niobium. However, there is no reason to believe that an intentional or unintentional addition of nickel or iron should influence the result appreciably, nor will small additions of metals that can form intermetallic phases with the binder phase or any other form of dispersion influence the result appreciably.

The amount of binder phase forming elements can vary between 2 and 10% by weight, preferably between 4 and 8% by weight. The amount of cubic phase forming elements can be varied rather freely. The process works on cemented carbides with varying amount of titanium, tantalum, niobium, vanadium, tungsten and/or molybdenum. The optimum combination of toughness and deformation resistance is achieved with an amount of cubic carbide corresponding to 4 - 15% by weight of the cubic carbide forming elements, titanium, tantalum and niobium etc., preferably 7 - 10% by weight. The amount of added nitrogen, either through the powder or through the sintering process, determine the rate of dissolution of the cubic phase during sintering. The optimum amount of nitrogen depends on the amount of cubic phase and can vary between 0.1 and 3% by weight per % by weight of group IVB and VB elements.

The amount of carbon in the binder phase required to achieve the desired stratified structure according to the present invention coincides with the eutectic composition, i.e. graphite saturation. The optimum amount of carbon is, thus, a function of all other elements and cannot easily be stated. The carbon content can be controlled either by a very accurate blending and sintering procedure or by a carburization treatment in connection with the sintering.

Production of cemented carbides according to the invention is most favourably done by sintering a presintered or compacted body containing nitrogen and, for formation of stratified layers optimum amount of carbon as discussed above, in an inert atmosphere or in vacuum, 15 to 180 min at 1380-1520°C, followed by slow cooling, 20-100°C/h, preferably 40-75°C/h, through the solidification region, 1300-1220°C, preferably 1290-1250°C. An alternative route includes sintering a slightly subeutectic body in a carburizing atmosphere, containing a mixture of CH4/H2 and/or CO2/CO, 30-180 min at 1380 to 1520°C followed by slow cooling according to above in the same atmosphere, preferably in an inert atmosphere or vacuum.

Cemented carbide inserts according to the present invention are preferably coated with in itself known thin wear resistant coatings with CVD- or PVD-technique . Preferably there is deposited an innermost coating of carbide, nitride, carbonitride, oxycarbide, oxynitride or oxycarbonitride preferably of titanium e.g. followed by an oxide, preferably aluminium oxide, top coating. Prior to the deposition the cobalt- and/or graphite layer on top of the cemented carbide surface is removed e.g. by electrolytic etching or blasting.

Example 1 From a powder mixture consisting of 2.2 weight-% TiC, 0.4 weight-% TiCN, 3.6 weight-% TaC, 2.4 weight-.% NbC, 6.5 weight-% Co and rest WC with 0.25 weight-% overstoichiometric carbon content turning inserts CN G 120408 were pressed. The inserts were sintered in H2 up to 450°C for dewaxing, further in vacuum to 1350°C and after that in protective atmosphere of Ar for 1 h at 1450°C. This part is according to standard practice. The cooling was performed with a well controlled temperature decrease of 60°C/h within the temperature interval 1290 to 1240°C in the same protective atmosphere as during the sintering. After that, the cooling continued as normal furnace cooling with maintained protective atmosphere.

The structure in the binder phase enriched surface zone of the inserts was a 15 μιη thick moderately binder phase enriched outer part essentially free of cubic phase, A, in which the stratified binder phase structure was weakly developed. Below this outer part there was a 20 thick zone containing cubic phase and with a strong binder phase enrichment as a stratified binder phase structure, B. The maximum cobalt-content in this part was about 17 weight-%. Further below this part,. B, there was a zone, C, about 150-200 \lm thick with essentially nominal content of cubic phase and binder phase but without graphite. In the inner of the insert, graphite was present up to C08. On the surface there was a thin film of cobalt and graphite. This film was removed by an electrochemical method in connection with the edge rounding treatment. The inserts were coated ac-cording to known CVD-technique with an about 10 coating of TiCN and AI2O3.

Example 2 From a similar powder mixture as in example 1 but with about 0.20 weight-% overstoichiometric carbon content turning inserts CNMG120408 were pressed. The inserts were sintered in H2 up to 450°C for dewaxing and further in vacuum to 1350°C and after that in a carburizing, 1 bar, CH4/H2, atmosphere, for 1 h at 1450°C. Cooling was performed in a protective, inert atmos-phere with a well controlled temperature decrease of 60°C/h within the temperature interval 1290 to 1240°C. After that, the cooling continued as normal furnace cooling with maintained protective atmosphere.

The structure of the inserts was essentially identical to that of the inserts of the preceding example. The inserts were etched, edgerounded and coated according to example 1.

Example 3 Comparative example From a similar powder mixture as in example 1 but with TiC instead of TiCN, inserts were pressed of the same type and sintered according to example 1. The structure in the surface of the inserts was characterized by compared to that of example 1 that zone A was almost missing (<5 μια) i.e. zone B with cubic phase and strong binder phase enrichment extended to the surface and a sharp cobalt-maximum of about 25 weight-%. Zone C had the same structure as in example 1. The inserts were etched, edgerounded and coated according to example 1.

Example 4 From a powder mixture consisting of 2.7 weight-% TiCN, 3.6 weight-% TaC, 2.4 weight-% NbC, 6.5 weight-% Co and rest WC with 0.30 weight-% overstoichiometric carbon content turning inserts CNMG 120408 were pressed. The inserts were sintered in H2 up to 450°C for dewaxing and further in vacuum to 1350°C and after that in protective atmosphere of Ar for 1 h at 1450°C. This part is according to standard practice.

During the cooling a well controlled temperature decrease was performed with 70°C/h within the temperature interval 1295 to 1230°C in the same protective atmosphere as during sintering. After that the cooling continued as normal furnace cooling with maintained protective atmosphere.

The structure in the surface zone of the inserts consisted of a 25 μιη thick moderately binder phase enriched outer part essentially free of cubic phase and essentially free of stratified binder phase structure, A. Below this outer part there was a 15 |im thick zone containing cubic phase and with a moderate binder phase enrichment as a stratified binder phase structure, B. The maximum cobalt-content in this part was about 10 weight-% . Zone C and the interior of the inserts were identical to example 1. The inserts were etched, edgerounded and coated according to example 1.

Example 5 Comparative example From a similar powder mixture as in example 4 inserts were pressed of the same type and sintered according to example 4 but without the controlled cooling step.

The structure in the surface of the insert consisted of outermost a 20-25 \i thick moderately binder phase enriched zone essentially free from cubic phase. No tendency to stratified binder phase was present. Below this superficial zone there was an about 75-100 μπι thick zone depleted of binder phase and enriched in cubic phase. The minimum cobalt-content in this zone was about 5 weight-%. The inner of the inserts exhibited C-porosity, C08. The inserts were etched, edgerounded and coated according to example 4.

Example 6 With the CNMG 120408-inserts of examples 1, 2, 3, 4 and 5 a test consisting of an intermittent turning operation, in an unalloyed steel with the hardness HBllO was performed with the following cutting data: Speed: 80 m/min Feed: 0.30 mm/rev Cutting depth: 2 mm 30 edges of each variant were run until fracture or max 10 min. The average tool life is shown in the table below.

Average tool life, min Example 1 (invention) 10 (no fracture) Example 2 (invention) 10 (no fracture) Example 3 (known technique) 10 (no fracture) Example 4 (invention) 4.5 Example 5 (known technique) 0.5 In order to differentiate, if possible, between examples 1, 2 and 3 the same test was repeated but with cutting fluid. The following results were obtained: Average tool life, min Example 1 (invention) 10 (still no fracture) Example 2 (invention) 10 (still no fracture) Example 3 (known technique) 10 (still no fracture) Example 4 (invention) 1.5 Example 5 (known technique) 0.1 Example 7 The inserts from examples 1, 2, 3, 4 and 5 were tested in a continuous turning operation in a tough-hardened steel with the hardness HB280. The following cutting data were used.

Speed: 250 m/min Feed: 0.25 mm/rev Cutting depth: 2 mm The operation led to a plastic deformation of the cutting edge which could be observed as a flank wear on the clearance face of the insert. The time to a flank wear of 0.4 mm was measured for five edges each with the following results.: Average tool life, min Example 1 (invention) 8.3 Example 2 (invention) 8.0 Example 3 (known technique) 3.5 Example 4 (invention) 18.5 Example 5 (known technique) 20.3 From examples 6 and 7 it is apparent that inserts according to the present invention, Example 4, exhibit a considerably better toughness behaviour than according to known technique without having significantly impaired their deformation resistance. In addition, inserts according to the invention in example 1 and 2 have a clearly better deformation resistance without losing toughness behaviour compared to known technique. It is evident that a large span in cutting properties and thereby application area can be obtained.

Claims (8)

10 107,976/2 WHAT IS CLAIMED IS:

1. A cemented carbide body containing WC and cubic phases in a binder phase enriched surface zone, wherein the binder phase enriched surface zone has an outer portion essentially free of cubic phase and an essentially constant binder content and an inner portion containing cubic phase and stratified binder phase layers in which the tungsten content is less than the norminal tungsten content of the body as a whole and is no more than 95% of the nominal tungsten content of the cemented carbide at any point within the said inner portion.

2. The cemented carbide body of claim 1, wherein said surface zone is <75 μπι, said outer portion is >10 μπι and said inner portion is >10 μηι thick.

3. The cemented carbide body of claim 1, wherein said surface zone is 20-50 μιη, said outer portion is <25 μιη, and said inner portion is <30 μηι thick.

4. The cemented carbide body of claim 1, wherein, in said inner portion, the binder phase content is above the nominal binder phase content of the body as a whole, and has a maximum of 1.5-4 times the nominal binder phase content.

5. The cemented carbide body of claim 4, wherein, in said inner portion, the binder phase content has a maximum of 2-3 times the nominal binder phase content. 1 1 107,976/1

6. A method of manufacturing binder phase enriched cemented carbide according to claim 1, said method comprising sintering a presintered or green cemented carbide body containing nitrogen and carbon in an inert atmosphere of in vaccum for 15 to 180 minutes at between 1380-1520°C, followed by slow cooling at a rate of 20-100°C per hour through the solidification region at a temperature of 1300-1220°C.

7. A method of manufacturing a binder phase enriched cemented carbide according to claim 1, comprising sintering a cemented carbide body subutectic in carbon content in a carburizing atmosphere containing a mixture of CH4/H2 and/or CO2/CO for 30-180 minutes at 1380-1520°C, followed by slow cooling at a rate no greater than 100°C per hour in the same atmosphere or in an inert atmosphere or vacuum.

8. The method of claim 7, wherein said cemented carbide body subutectic in carbon content has a porosity of CO4-CO8. for the Applicant: WOLFF, BREGMAN AND GOLLER