IE911686A1 - Composite clay materials for removal of SOx from gas streams - Google Patents

Abstract

A method for preparing and using compositions including a smectite clay and a base or base precursor which reacts with S0x in a hot flue gas is described. The 5 base or base precursor is preferably the dispersed phase in the bulk phase of the clay. The compositions are heated to form the base which reacts with S0x in the flue gas.

Description

This invention relates to alkali and alkali earth oxides or carbonates supported on clays where the host clay belongs to the smectite group, and to a method of preparing them. More particularly, it relates to the method of developing improved composite materials for use in SOX, (sulfur dioxide and sulfur trioxide), removal from flue gas. (2) Prior Art The first example of flue gas scrubbing for sulfur dioxide control occurred in London, England, in 1933 However, the application of this technology to coal-fired utility boilers in the United States did not begin until the 1970's. The first large-scale application of flue gas scrubbing using lime or limestone was installed in 1964, in the Soviet Union. This facility was followed by an installation at a large sulfuric acid plant in Japan in 1966. In 1970, the Clean Air Act Amendments were adopted.

This legislation provided for enforcement, by the United States Environmental Protection Agency (EPA), of SOX emissions limits for power plants constructed or modified after August 17, 1971. This Act spurred extensive flue gas desulfurization (FGD) research. As of January 1984, calcium-based, wet, throwaway systems (including lime, limestone, and alkaline-ash systems) accounted for 84 percent of existing and planned FGD capacity. The Clean Air Act was amended in 1977 to require further control of SOX emissions. Increasing federal regulations and the high cost to construct and operate existing wet FGD units have -2encouraged continued research on new or modified flue gas cleanup processes.

Controlling the emissions of S0x from power plants is a world-wide problem due to its relationship to acid rain. Therefore, research into its control is a global effort. Example of a recent patent using calcium based systems to reduce S0x emissions is Thompson and Nuzio, U.S. Patent No. 4,731,233. In most cases a commercial source of limestone or lime is used due to cost effectiveness and available quantities.

There are a number of ways to control S0x emissions in existing power plants or features that can be included in construction of new power plants. These approaches can be classified according to the position in the combustion system at which pollutant control technology is applied. Precombustion control involves removal of sulfur, nitrogen and ash compounds from the fuel before it is burned. In most cases this involves application of coal-cleaning technology. Combustion control includes staged combustion, boiler limestone injection, and fluidized-bed combustion with limestone addition. Post-combustion control involves removal of pollutants after they have been formed but before they are released into the atmosphere. This would include in-duct dry sorbent injection, induct spray drying and combined electrostatic precipitator (ESP)/fabric filter sorbent injection (Jozewicz, W., Chang, J. C. S. , Sedman, C. B. and Brna, T. G., React. Solids, 6 243 (1988)).

Flue gas treatment systems can be classified as either wet or dry based on the moisture content of the treated flue gas and the spent sorbent. Wet systems completely saturate the flue gas with water vapor. The flue gas is contacted with a liquid or slurry stream. Dry systems contact the flue gas with a dry or wet sorbent but never include enough water for complete saturation of the flue gas. Dry systems result in a dry product or spent -3sorbent material, while wet systems result in either a slurry or a sludge.

Although calcium based systems are the major source of S0x control they are not without problems.

Agglomeration of particles can be a serious problem that results in a less than optimal conversion to CaSOx, (CaSC>3 and CaS04). The activity of the calcium species decreases as its particle size increases. Also CaSOx occupies more volume than CaO, the common active species. Therefore, an increase in volume occurs as the reaction proceeds, which causes a loss in the original porous character of the CaO. This results in a blockage of SOX and O2 to the active CaO centers (Gullett, Β. K. and Blom, J. A., React. Solids, _3 337 (1987): Gullett, Β. K., Blom, J. A. and Cunningham, R.

T., React. Solids, 2 263 (1988); Chang, Ε. Y. and Thodes, G., AIChE J., 30. 450 (1984); Thibault, J. D., Steward, F.

R. and Ruthven, D. M., Can. J. Chem. Eng., 60 796 (1982)).

Prior art in this field has used limestone, lime or hydrated lime as a precursor for the active CaO species or has used Ca(OH)2 as the active species. Generally, the active species has been used as a bulk phase and not as a dispersed species (Chang, J. C. S. and Kaplan, N., Envir. Prog., 2 267 (1984); Gullett, Β. K., Blom, J. A. and Cunningham, R. T., React. Solids, 6_ 263 (1988); Chang, E. y. and Thodes, G., AIChE J., 30 450 (1984); Fuller, E. L. and Yoos, T. R., Langmuir, 2 753 (1987)). Recent work has concentrated on the addition of fly ash to Ca(OH)2 to enhance its activity in SOX control (Jozewicz, W. and Rochelle, G. T., Envir. Prog. 5 219 (1986); Jozewicz, W. , Chang, J. C. S. , Sedman, C. B. and Brna, T. G., JAPCA, 38. 1027 (1988); Jozewicz, W. , Jorgensen, C., Chang, J. C. S., Sedman, C. B. and Brna, T. G., JAPCA, 38 796 (1988); Jozewicz, W., Chang, J. C. S., Sedman, C. B. and Brna, T.

G., React. Solids, 6 243 (1988); Jozewicz, W., Chang, J. C. s., Sedman, C. B. and Brna, T. G., EPA/600/D-87/095, (NTIS PB87-175857/AS); Jozewicz, W., Chang, J. C. S., Sedman, C. B. and Brna, T. G., EPA/600/D-87/135, (NTIS PB87-182663 ) . -4The fly ash is a siliceous material and the formation of various calcium silicates can occur. Several diatomaceous earths, montmorillonite clays, and kaolins have also been identified as containing reactive silica (Jozewicz, W., Chang, J. C. S., Sedman, C. B. and Brna, T. G., React. Solids, 6 243 ( 1988) ) .

It is therefore an object of the present invention to provide a method for preparing improved sorbent compositions including a smectite clay as the bulk phase and with a relatively smaller amount of a basic compound as the active phase. Further, it is an object of the present invention to provide improved compositions which are more active over time, thus more effective in SOX removal. Further still, it is an object of the present invention to provide compositions which are relatively economical to prepare and use. These and other objects will become increasingly apparent from the following description and the drawings.

IN THE DRAWINGS Figure 1 is a graph showing a Cu K alpha XRPD pattern of the A:Z, A=l, Z=1, CaCC>3:Na-montmorillonite composite designated Sample 1.

Figure 2 is a graph showing a TGA profile of Sample 1.

Figure 3 is a graph showing the initial SO2 uptake of Samples 1, 3 and precipitated CaCOj.

Figure 4 is a graph showing a Cu K alpha XRPD pattern for Sample 17, 1.5:1, Ca(CH3CO2)2:Na-montmorilloni te .

Figure 5 is a graph showing the temperature dependence of SO2 uptake for the 1:1 ratio of CaC03:Na-Montmorillonite composite, for Samples 1, 22, 23 and 24.

GENERAL DESCRIPTION The present invention relates to a method for preparing a composite material useful for removing SOX from a gas stream which comprises: providing a suspension of a -5smectite clay in water; providing a basic compound selected from the group consisting of alkali metal and alkaline earth metal salts and bases in the suspension with the clay; and drying the suspension to provide the composite material, wherein when the composite material is heated, preferably to at least about 500°C, the S0x is removed from the gas by the basic compound.

Further, the present invention relates to a method of preparing a composite material, capable of removing S0x from a gas stream comprising the steps: providing a suspension of a smectite clay in water; introducing a quantity of a basic compound selected from the group consisting of a base and a base precursor into the clay suspension; and drying the suspension in air, wherein when the composite material is heated, preferably to at least about 500°C, the SOX is removed from the gas.

Further still, the present invention relates to a method for preparing a composite material capable of removing S0x from a gas stream comprising the steps of; providing a suspension containing a smectite clay in water; dissolving an amount of sodium carbonate in the suspension of the clay; adding a soluble alkaline earth metal salt in stoichiometric amount for reaction with the sodium carbonate to form an alkaline earth metal carbonate precipitate in the suspension with the clay; washing the composite; and drying the suspension to provide the composite material, wherein when the composite material is heated, preferably to at least about 500°C.

Finally the present invention relates to a composition for use in removing SOX from a gas stream when the composite material is heated, preferably to at least about 500°C, which comprises in admixture: a basic compound selected from the group consisting of alkali metal and alkaline earth metal salts and bases; and a smectite clay, wherein the basic compound is provided in an aqueous suspension with the clay and then dried to form the composition . -6The present invention provides a method for production of composite materials consisting of alkali or alkali earth metal/smectite clay composites, of varying alkali or alkali earth metal/clay ratios than has heretofore been known in the prior art, specifically by causing the precipitation of CaCC>3 or Ca(0H)2 from salts onto and into the clay particle while the clay is in suspension and by the impregnation of sodium or calcium species into the clay particle by the addition of an aqueous solution of alkali or alkali earth species to a suspension of clay to produce these ratios. The resulting materials are used to remove SOX from flue gas.

In accordance with one method of the invention, a 0.5 to 1.5 weight percent aqueous suspension of clay was initially prepared. An aqueous solution of Na2CC>3 was added dropwise to the clay suspension while it was stirred. This was followed by a similar addition of CaCl2-2H2O. The addition of the calcium species caused the precipitation of CaCC>3. The amount of Na2CC>3 and CaCl2*2H2O can be varied to provide the desired weight ratio of CaCO3 to clay. The product was washed with deionized distilled water, either by centrifugation/decantation or by dialysis, to remove the excess chloride and sodium ions before drying at room temperature or in an oven at 100 °C. The wash was checked with a silver nitrate solution for precipitation of silver chloride. A negative test for silver chloride indicated that the chloride had been removed. Washing the preparation was preferred, because reactivity with S0x was diminished if no attempt was made to remove the chloride.

The adverse effect of chloride on SOX removal has also been verified by another study which evaluated the effects of magnesium and chloride ions on the performance of 1imestone-regenerated dual alkali processes under closed-loop operating conditions (Chang, J. C. S., Kaplan, N. and Brna. T. G. in Fossil Fuels Utilization: Environmental Concerns (Eds. R. Markuszewski, B.

Blaustein) Chap. 15). Limestone reactivity decreased with -7the increase of chloride ion concentration. The effect was especially pronounced after a concentration of 80,000 ppm was reached.

X-ray powder diffraction (XRPD) indicates that the clay retains its original layered structure with a basal spacing of approximately every 10 Crystalline CaCC>3 is also present in the XRPD pattern.

The precipitation of Ca(0H)2 was carried out using a similar method. A 50 wt.% solution of NaOH containing the desired amount of OH“ was added to water.

The solution was added dropwise to the clay suspension while stirring. An aqueous solution of CaCl2’2H2O was added in a similar manner after addition of the NaOH solution . in situ precipitation resulted in smaller CaCO3 particle size than can be attained through a physical mixture of CaCO3 and the clay.

An oxidation catalyst was also added to some of the composite preparations. Iron was added in the form of FeCl3’6H2O or Fe(NO3)3·9H2O. Fe2O3 was formed upon thermal decomposition of the salts; and catalyzed the oxidation of SO2 to SO3. SO3 reacts with calcium oxide at lower temperatures than SO2 resulting in a wider temperature window for the removal of SOX from the gas stream. Various transition metals can be used as oxidation catalysts.

Prior to exposure to SO2 the product was heated to 900°C in air. Thermal gravimetric analysis (TGA) indicated the loss of H2O and CO2 based upon mass measurements of the sample. The thermal treatment caused the decomposition of CaCC>3 to CaO. It also caused a severe drop in the clay intensity present in the pattern with only a low intensity remaining at 9.4 £ for the CaC03/Na-montmorillonite composite .

A second method of preparing a highly dispersed alkali or alkali earth metal species was the impregnation of a water soluble sodium or calcium compound onto the clay As previously described, the desired amount of dissolved -8alkali metal or alkali earth metal carbonate species was added to the clay suspension while the suspension was stirred. Calcium formate, calcium acetate and sodium bicarbonate have been used as example preparations, but 5 other soluble alkali metal and alkaline earth metal salts may be used. Washing was not necessary in these latter preparations that were chloride free. The suspension was air dried on a glass plate at room temperature.

An XRPD pattern of calcium formate and 10 Na-montmorillonite in a 1:1 weight ratio contained crystalline calcium formate peaks and d(QQD spacing typical of the clay (10.9 &) . A small peak also occurred at a d-spacing of 22.7 indicating that some intercalation of the formate species occurred. In 15 contrast, the XRPD pattern for a calcium acetate/Na-montmorillonite composite prepared using the impregnation method did not exhibit crystalline calcium acetate. Instead, a major reflection occurred at a d-spacing of 24.0 j(, indicating that most of the calcium 20 acetate species formed a nanocomposite with the clay by intercalation into the interlayer of the clay host forming a new composition of matter. (T. J. Pinnavaia in Chemical Physics of Intercalation, Ed. by A. P. Legrand and S. Flandrois, NATO ASI Series, Series B: Physics Vol. 172, pp 233-252, (1987)).

The products resulting from this invention constitute a calcium/clay composite in the case of precipitated CaCOg from the previously mentioned salts or impregnation of Ca(CHOO)2, Ca(CH3CO2)2 or NaHCO3 . A 30 sodium/clay composite is formed in the case of impregnated NaHCO3. A more intermediate interaction between the clay and the calcium acetate occurred during the impregnation method, as evidenced by a change in the clay XRPD pattern, resulting in a regularly intercalated clay non-composite.

Although CaCC>3, NaHCOg, Ca(CHO2)2, and Ca(CH3CO2)2 are suitable bases or base precursors for SOX removal in the temperature range 100-900°C by composite -9formation with smectite clay, certain calcium salts such as calcium hydroxide (quicklime), Ca(OH)2, is not a suitable reagent for this purpose because the salt is too unstable on the clay support at high temperatures, presumably due to chemical reaction with the clay support, and its ability to remove S0x from a gas stream is lost.

The particle size of the smectite clay is preferably less than about 2 microns. A particle size between about 0.1 and 2 microns is preferred. a weight ratio of about 1 to 3 and 5 to 1 for salt to clay is preferred. Any weight ratio which produces effective SOX removal from flue gas can be used, preferably where the bulk phase is the clay.

The composite material can be dried by various means including spray drying, tray drying and the like.

The solids can be removed from solution by centrifuging with intermediate washing steps with water.

SPECIFIC DESCRIPTION Example 1 Na-montmorillonite from Crook County, Wyoming USA was selected as the representative member of the smectite family of 2:1 layer lattice silicates. A 1.4 weight percent, wt.%, of clay was dispersed in deionized distilled water. An upper limit of 2 micron particle size was achieved by sedimentation in water and application of Stokes’ law of settling under gravity. The procedure was followed twice. Sedimentation also removed quartz and other insoluble impurities that may have been present in the clay. After purification the clay was air dried on a glass plate or stored in an aqueous suspension.

A desired weight ratio, A:Z, of CaCC>3 :Na-montmorillonite was achieved by preparing a 1.4 wt.% solution of Na-montmorillonite in deionized distilled water. A total weight of 20 grams of solution was used.

In the example of A=Z=1, 0.28 grams of CaCC»3 or 2.8 x 10-3 mole was desired. Therefore, 2.8 x 10-3 mole of Na2CC>3 was dissolved in deionized distilled water with a total -10solution weight of 20 grams. The Na2CC>3 solution was slowly added to the Na-montmorillonite suspension while stirring. A similar solution of CaC^'t^O was added to the solution after addition of the Na2CC>3 solution was complete.

The sodium salt is added first to discourage cation exchange of the calcium with the sodium in the montmorillonite.

After preparation the product was washed and centrifuged repeatedly with deionized distilled water to remove excess chloride and sodium ions. The wash was tested with a solution of silver nitrate to determine the absence of chloride ions. The product was dried on a glass plate at ambient temperature. An XRPD pattern of the product is shown in Figure 1. The reflection at 5.8° (15.1 &) is the major Na-montmorillonite peak and the peak at 29.5° (3.0 is the major peak of CaCO3.

A sample prepared as described above was evaluated and was shown to be active for SO2 removal from a gas mixture. The sample was heated to 900°C at a rate of °C/min and maintained at 900°C for 30 minutes prior to the introduction of 5000 ppm SO2 for 1 hour in flowing air.

The uptake of SO2 is illustrated in Figure 2. The sample removed an 88% CaCC>3 conversion, with 19% conversion occurring within the first minute. The conversion is based upon the following reaction: CaO + SO2 + O2 -2^Q>CaSO4.

Examples 2 and 3 Examples 2 and 3 provided products, designated samples 2 and 3, respectively, that were prepared utilizing the procedures of Example 1, with the weights of Na2CC>3 and CaCl2’2H2O varied to yield respective values of A=3, Z=1; A=0.33, Z=1. Samples of 2 and 3 were tested for SO2 uptake following the procedure cited in Example 1. Sample 2 exhibited a total CaCC>3 conversion of 100% with 14% of the conversion occurring during the first minute of the reaction. Sample 3 gave a total CaCC>3 conversion of 100%, with conversion after 1 minute of 36%. Figure 3 -11illustrates the differences in initial SO2 uptake by Samples 1, 3 and CaC03 caused by varying the CaCC>3 :Na-montmori 1 loni te weight ratio.

Examples 4 to 6 A series of 1:1 CaC03 : smec ti te clay composites in accordance with the method of Example 1, were prepared using other members of the smectite family in place of purified montmorillonite, Bentone EW P&G GST-865 (Sample 4); nontronite (Sample 5); fluorohectorite (Sample 6).

These composite preparations were tested for SO2 reactivity according to the method described in Example 1. After 1 hour of reaction, the Bentone preparation gave a total conversion of 98%, the nontronite sample gave a total conversion of 78% and the fluorohectorite sample gave a total conversion of 90%.

Examples 7 to 9 A series of A:Z Na-montmorillonite samples in accordance with the invention were prepared utilizing the procedures of Example 1, but the washing procedure was eliminated and the drying temperature was varied. Samples 7 and 8 had A=l, Z=1 and A=0.33, Z=l, respectively, and were dried at room temperature. Sample 9 had A=l, Z=1 and was dried at 100°C in air. Samples 7 to 9 had total conversions of 52, 59 and 42%, respectively, as determined by the test conditions cited in Example 1. The chloride ion interferes with the conversion.

Example 10 An iron-containing CaCC>3: Na-montmorillonite composite, designated Sample 10, with A=Z=1 was prepared by a co-precipitation method using FeCl3*6H2O as the iron source. The addition of Na2CC>3 was carried out in accordance with the method described in Example 1, except that FeCl3-6H2O was added to the CaCl2*2H2O solution to yield a composite containing an Fe content of 1.5 wt.%. -12The sample exhibited a total CaCC>3 conversion of 42.5% after 1 hour reaction with S02 under the conditions described in Example 1.

Example 11 An iron containing CaCOg:Na-montmori11 onite sample, designated Sample 11, with A=Z=1 was prepared using Fe (NO3 ) 3 · 9H2O as the source. A CaCC>3 : Na-mon tmori lloni te composite with A=1, Z=1 was prepared according to the procedure described in Example 1. A 0.5 wt.% quantity of Fe(NO3)3·9H2O was dissolved in deionized distilled water and was added to the CaCC^/Na-montmorillonite suspension. The product was air dried on a glass plate at room temperature. The sample showed a total CaCC>3 conversion of 88% after 1 hour reaction with SO2 under the conditions described in Example 1.

Examples 12 and 13 A 1:1 by weight composite of Ca(OH)2 and Na-montmorillonite, designated Sample 12, was prepared by using NaOH, CaCl2'2H2O and Na-montmorillonite as starting materials. An amount of a 50 weight percent NaOH solution appropriate for the stoichiometric reaction with CaCl2-2H2O was added to a stirred 50 gram of a 0.5 wt.% suspension of Na-montmorilIonite. After the addition of the NaOH, to the clay, an equivalent amount of a solution of CaCl2-2H2O was added to the solution to produce the 1:1 Ca(OH)2:Na-montmorillonite composite. The product was washed with deionized distilled water as described in Example 1. A second sample, designated Sample 13, was prepared to afford a 3:1 Ca(OH)2:Na-montmorilionite (Sample 13). The total conversions after 1 hour reaction with SO2 at 900°C using the test conditions cited in Example 1 were 5 and 1%, respectively, for Samples 12 and 13. In these examples, Ca(OH>2 loses its ability to react with SOX under these reaction conditions when supported on smectite clay. -13Presumably the Ca(0H)2 reacts with the clay, forming a calcium silicate that is inert to S0x .

Examples 14 and 15 An amount of calcium formate, Ca(HC00)2z was dissolved in a minimum amount of deionized distilled water. The solution was slowly added with constant stirring to a 1.4 wt.% slurry of Na-montmorillonite. The amount of Ca(HC00)2 added to the clay slurry was varied to yield composite with a Ca(HCOO)2:Na-montmorillonite ratio of 1:1, designated Sample 14, and 3:1 designated Sample 15. The products were air dried at room temperature on a glass plate. Sample 14 gave a total conversion based on Ca(HCOO)2 of 60% after 1 hour reaction time with SO2 and a conversion of 24% after the first minute under the conditions described in Example 1. The conversions for Sample 15 were 94% and 14% after 1 hour and 1 minute reaction time, respectively.

Examples 16 to 19 A series of calcium acetate: Na-montmorillonite composite samples in accordance with the invention, were prepared utilizing the procedures of Examples 14 and 15 for the preparation of clay calcium formate composite. The amount of Ca(H3CCOO)2·XH2O used was varied to yield composite with Ca(CH3CO2)2:Na-montmorillonite weight ratio of 1:1, designated Sample 16; 1.5:1 designated Sample 17; 0.33:1, designated Sample 18; 5.0:1, designated Sample 19.

An XRPD pattern of the product from Sample 17 is shown in Figure 4. The pattern does not exhibit any crystalline Ca(H3CCOO)2 species but it does exhibit an increase in d-spacing for the clay structure, indicating intercalation of the acetate species. The conversions for Samples 16 to 19 after 1 hour reaction time with SO2 were 52, 36, 15 and 78%, under the conditions cited in Example 1. -14Example 20 A sample of NaHCC>3 supported on Na-montmorillonite was prepared by dissolving the bicarbonate salt in a minimum amount of deionized distilled water and adding the solution slowly to a clay suspension with constant stirring, and allowing the mixture to air dry on a glass plate. The NaHCO3:clay ratio was 1:2. The sample designated Sample 20, gave a total conversion based on NaHCC>3 of 31% after 1 hour reaction with SO2 under the test conditions cited in Example 1.

Example 21 A quantity of sample 20 from Example 20 was tested for S02 reactivity at 500°C. The sample was heated to 500°C at a ramp rate of 5°C/min until a temperature of 500°C was reached. The sample was maintained at 500°C for minutes. An air stream containing 5000 ppm of SO2 then was allowed to flow over the sample for 1 hour, total flow rate of 200 cc/min while the sample was at 500°C. The sample was maintained at 500°C for an additional 30 minutes without weight loss. The total conversion after 1 hour reaction with SO2 based on NaHCC>3 content was 46%.

Example 22 A quantity of Sample 1 was tested for S02 uptake at 500°C under the conditions cited in Example 21. The percent conversion for the sample was 0%. The temperature is too low for effective conversion of the CaCC>3.

Example 23 A quantity of sample 1 was tested for SO2 uptake at 700°C by ramping the temperature at 5°C/min until a temperature of 700°C was obtained. A temperature of 700°C was maintained for 30 minutes prior to the introduction of SO2 in air at a concentration of 5000 ppm. The sample was maintained at 700°C for an additional 30 minutes after the SO2 without weight loss. The percent conversion based on -15CaCC>3 was 11% which indicated that the higher temperature was better.

Example 24 A quantity of sample 1 was tested for S02 uptake at 800°C by ramping the temperature at 5°C/min until a temperature of 800°C was obtained. A temperature of 800°C was maintained for 30 minutes prior to the introduction of SO2 in air at a concentration of 500 ppm. The sample was maintained without weight loss at 800°C for an additional minutes after the SO2 had stopped. The percent conversion based on CaCC>3 was 75%. The temperature dependence of S02 uptake for CaCC>3/Na-montmorillonite, 1:1 wt.% for samples from Examples 1, 22, 23 and 24 is shown in Figure 5.

Examples 25 and 26 Two of the preparations were tested for SO2 reactivity under the conditions cited in Example 1 with additional moisture present in the gas stream. A quantity of sample 1 was run at a partial pressure of 0.22 H2O present in the gas stream and yielded a total conversion of 111%, part of which may be due to moisture uptake by the sample. A second sample from Sample 18 was tested at a partial pressure of 0.064 H2O and yielded a total conversion of 64%.

Examples 27 to 29 Samples 1, 10 and 11 were tested for SO2 reactivity at 700°C. The samples were ramped to 900°C as cited in Example 1 and then ramped to 700°C at 5°C/min.

The sample was maintained at 700°C for 30 minutes before 5000 ppm of SO2 was admitted to the gas stream for 1 hour.

Samples 1, 10 and 11 had total conversions of 61, 38 and 54%, respectively, under these conditions. -16Example 30 Hectorite from San Bernardino County, California USA, was purified utilizing the procedures of Example 1. A 1:1 CaC03:hectorite clay composite was prepared in accordance with the method of Example 1. Excess chloride ions were removed by dialysis. The composite preparation was tested for SO2 reactivity according to the method described in Example 1. After 1 hour of reaction, the composite gave a total conversion of 85% with 24% of the reaction occurring within the first minute.

Results of Examples Table 1 lists the values for SO2 uptake after 1 minute and after 1 hour for all of the Examples 1 to 29. Unless otherwise specified, the samples were ramped at °C/min until a temperature of 900 °C was reached. The temperature was maintained at 900°C for 30 minutes prior to admittance of 5000 ppm of SO2 into the gas stream for 1 hour. The sample was maintained at 900°C for an additional 30 minutes after admission of SO2 had ceased to test the thermal stability of the products.

Table 1 Activity for SO2 Removal Using Base/Clay Composites S.# Rxn. % Conversion a Base/Clay Ratio Temp. °C 1 min. 60 min. Comments 1 CaC03/Na-mont 1:1 900 19 88 2 3:1 900 14 100 3 0.33:1 900 36 100 7 1:1 900 13 52 8 0.33:1 900 15 59 unwashed 309b 1:1 900 6 42 unwashed 10 1:1 900 5 43 FeCl3 doped 11 1:1 900 13 88 Fe (NO3)3 doped -1712 Ca(0H)2/ 13 Na-mont 1:1 3:1 900 900 c c 5 1 14 Ca(FOR)/ 5 Na-mont 1:1 900 24 60 15 3:1 900 14 94 16 Ca(ACE)/ Na-mont 1:1 900 25 52 17 1.5:1 900 4 36 10 18 0.33:1 900 8 15 19 5:1 900 26 78 20 NaHCC>3/ Na-mont 1:2 900 11 33 21 1:2 500 16 46 15 1:2 100 active active 22 CaCC>3/Na-mont 1:1 500 c c 23 1:1 700 4 11 24 1:1 800 12 75 25 1:1 800 34 111 PH20 0.22 26 1:1 800 17 64 PH20 0.064 27 1:1 700 7 61 preheat 900°C 28 1:1 700 12 38 preheat 900°C 29 1:1 700 9 54 preheat 900°C 30 CaCO3/Na+- hectorite 1:1 900 24 85 4 CaCC>3/Bentone 1:1 -18- 900 14 98 5 CaCC>3/Nontron 1:1 900 26 78 6 CaC03/ Fluorhect 1:1 900 11 90 CaCO3 precipitated 900 9 82 aCaO + S02 + 02 -900°c> CaSC>4 bdried at 100°C. cno significant uptake.

The present invention has been particularly set forth in terms of specific embodiments thereof, it will be understood in view of the instant disclosure, that numerous variations upon the invention are now enabling to those skilled in the art, which variations yet reside within the scope of the instant teaching. Accordingly, the present invention is limited only by the hereinafter appended claims .

Claims (1)

1. WE CLAIM: -ΙΑ method for preparing a composite material useful for S0 x removal from a gas stream which comprises: (a) providing a suspension of a smectite clay in water; 2. 5 (b) providing a basic compound selected from the group consisting of alkali metal and alkaline earth metal salts and bases in the suspension with the clay; and (c) drying the suspension to provide the composite material, wherein when the composite material is 3. 10 heated, the SO X is removed from the gas by the basic compound. -2The method of Claim 1 wherein the weight ratio of salt to clay is between about 1:3 and 5:1. -3A method for preparing a composite material capable of removing SO X from a gas stream comprising the steps of: (a) providing a suspension containing a 5 smectite clay in water; (b) dissolving an amount of sodium carbonate in the suspension of the clay; (c) adding a soluble alkaline earth metal salt in stoichiometric amount for reaction with the sodium 10 carbonate to form an alkaline earth metal carbonate precipitate in the suspension with the clay; and (d) drying the suspension to provide the composite material, wherein when the composite material is heated, the SO X is removed from the gas. -20-4A method in accordance with Claim 3, wherein the alkaline earth metal carbonate and clay are recovered from the water for drying by centrifuging. -5A method in accordance with Claim 4 wherein the alkaline earth metal carbonate and clay recovered by centrifuging is washed and air dried. -6A method in accordance with Claim 4 wherein the alkaline earth metal carbonate and clay recovered by centrifuging is air dried at a temperature up to about 100°C. -7A method in accordance with Claim 3 wherein the alkaline earth metal carbonate and clay are mixed with an iron salt selected from the group consisting of ferric chloride and ferric nitrate. -8A method in accordance with Claim 3 wherein the smectite clay is selected from the group consisting of montmorillonite, fluorohectorite, bentonite, nontronite, hectorite, saponite, and beidellite. -9A method in accordance with Claim 3 wherein the alkaline earth metal is selected from the group consisting of magnesium and calcium. -21-10A method of preparing a composite material, capable of removing SO X from a gas stream comprising the s teps: (a) providing a suspension of a smectite clay 5 in water; (b) introducing a quantity of a basic compound selected from the group consisting of a base and a base precursor into the clay suspension; and (c) drying the suspension in air, wherein when 10 the composite material is heated, the S0 x is removed from the gas. -11A method in accordance with Claim 10, wherein said base precursor is selected from the group consisting of NaHC03, Na 2 CC>3, calcium acetate and calcium formate. -12The method of Claim 10 wherein the weight ratio of basic compound to clay is between about 1:3 and 5:1. -13A method for removing SO X from a gas mixture which comprises: (a) providing a dried mixture of a basic compound selected from the group consisting of an alkali 5 metal and alkaline earth metal salts and bases dispersed in a smectite clay; and (b) heating the mixture in the presence of a gas containing S0 x to remove the SO X . -14The method of Claim 13 wherein the mixture contains an iron salt for oxidizing SO 2 to SO3. -22-15A composition for use in removing S0 x from a gas stream when the composite material is heated which comprises in admixture: (a) a basic compound selected from the group 5 consisting of alkali metal and alkaline earth metal salts and bases; and (b) a smectite clay, wherein the basic compound is provided in an aqueous suspension with the clay and then dried to form the composition. -16The composition of Claim 15 wherein the admixture includes an iron salt for oxidizing SO2 to SO3 when the composition is heated. -17The composition of Claim 15 wherein the clay has a particle size of less than about 2 microns. -18The composition of Claim 14 wherein the clay is sedimented in water to provide the clay with the 2 micron particle size. -2319. A method for preparing a composite material substantially as hereinbefore described with reference to the Examples and drawings . 20. A composite material whenever prepared by a method as claimed in any of claims 1 to 11 or 19. 21. A method of removing SOx from a gas mixture substantially as hereinbefore described with reference to the Examples and drawings . 22. A composition substantially as hereinbefore described with reference to the Examples and drawings.