GB2607537A - A nickel-based alloy - Google Patents
A nickel-based alloy Download PDFInfo
- Publication number
- GB2607537A GB2607537A GB2212512.4A GB202212512A GB2607537A GB 2607537 A GB2607537 A GB 2607537A GB 202212512 A GB202212512 A GB 202212512A GB 2607537 A GB2607537 A GB 2607537A
- Authority
- GB
- United Kingdom
- Prior art keywords
- nickel
- less
- weight percent
- alloy
- based alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A nickel-based alloy comprising (by weight): 4.0-5.6 % aluminium, 2.0-12.7 % tungsten, 6-16.7 % chromium, 0.02-0.35 % carbon, 0.001-0.2 % boron, 0-1.0 % titanium, 0-4.0 % niobium, 0-11.9 % tantalum, 0-3.0 % molybdenum, 0-22.0 % cobalt, 0-0.5 % zirconium, 0-3.0 % rhenium, 0-2.0 % ruthenium, 0-3.0 % iridium, 0-0.5 % vanadium, 0-1.0 % palladium, 0-1.0 % platinum, 0-0.5 % silicon, 0-0.1 % yttrium, 0-0.1 % lanthanum, 0-0.1 % cerium, 0-0.003 % sulphur, 0-0.25 % manganese, 0-0.1 % magnesium, 0-4.0 % iron, 0-0.5 % copper and 0-0.5 % hafnium with the balance being nickel and impurities and where 0.3xNb + 0.15xTa ≥ 1.1. Alloy can be in powder or wire form as a raw material to make components by additive layer manufacturing techniques such as powder-bed methods and direct metal deposition methods (powder and wire based).
Description
A Nickel-Based Alloy The present invention relates to a nickel-based superalloy composition designed for application in additive manufacturing (AM) processes, examples of such processes including but not limited to, powder-bed based AM methods (e.g. selective laser melting, electron beam melting), direct metal deposition methods (e.g. powder deposition and wire based methods).
Currently, there has been a tendency to migrate nickel-based superalloys which have been successfully manufactured in cast form or wrought form to the AM process. However, this has proven largely inappropriate because many of the material characteristic required for ease of processing in the AM process are not fulfilled by such alloys leading to substantial difficulties in processing and resulting in materials which do not have the expected structural integrity.
In particular there has been significant challenge to develop high volume fraction of y' alloys for the additive manufacturing process, as these alloys are often classed as 'non-weldable'. Commonly these alloys are processed by investment casting method, examples of common alloys used for the investment casting process are listed in Table 1.
The application of the alloys listed in Table 1 for additive manufacturing methods has been widely studied. It has been shown that although the alloys maybe 'non-weldable' and difficult to process, certain failure mechanisms can be limited For example these alloys are susceptible to strain-age cracking but careful control during the in-process AM conditions (scan strategy, heat input, etc.) and the post-processing conditions (heat treatment window and heating rate) the risks associated with strain-age cracking can be minimised to some degree.
Similarly, strain-age crack resistance can be improved by designing the geometry of the part to reduce the impact of stress-concentrating features such as notches.
Strain-age cracking occurs because of two principal factors: residual strain and y' precipitation. The magnitude of residual stress may simply be reduced by prc-heating the powder bed, which minimises the temperature range for thermal contraction. It is also shown by Illston (Patent No. US 9352421 B2) that residual stress build-up can be minimised through process control, particularly the use of thin powder layers and deliberately overlapping laser scans, hence allowing for improved printability of high-sr superalloys. It is also shown by Etter et al (Patent No. US 9670572 B2) that by ramping up particularly quickly to the post-AM stress-relief heat treatment temperature the risk of strain-age cracking can bc reduced.
Another mechanism which cannot be as easily mitigated by optimisation of processing is hot cracking. hot cracking occurs during the last stages of solidification process with a strong dependence on alloy chemistry.
It is the aim of this invention to develop an alloy of high of)" volume fraction which is particularly resistant to the mechanism of hot cracking by tailoring the alloy chemistry to overcome this unwanted damage mechanism.
In combination with this improved processability the alloy of thc invention preferably has a very high level of oxidation resistance (achieved by having sufficient levels of aluminium to form a protective aluminium-based oxide scale) and also a high level of creep resistance.
Table 1: Nominal composition in wt% of conventional high volume fraction of 7' alloys.
Alloy (wt%) Al Co Cr lVfo Nb Ta Ti W C B Zr Hf 1N738 3.4 8.5 16.0 1.8 0.9 1.8 3.4 2.6 0.11 0.01 0.04 0 CM247 5.5 9.5 8.4 0.5 0.0 3.0 0.7 9.5 0.07 0.015 0.015 1.5 1N713 6.0 0.0 12.5 4.5 2.0 0.0 0.8 0.0 0.12 0.001 0.10 0 1N792 3.2 9.0 12.7 1.8 0.0 3.9 4.2 3.9 0.07 0.016 0.018 0 The prescnt invention provides a nickel-based alloy composition consisting, in weight percent, of: 4.0 to 5.6% aluminium, 0.0 to 1.0% titanium, 0.0 to 4.0% niobium, 0.0 to 11.9% tantalum, 2.0 to 12.7% tungsten, 0.0 to 3.0% molybdenum, 0.0 to 22.0% cobalt, 6.0 to 16.7% chromium, 0.02 to 0.35% carbon, 0.001 to 0.2% boron, 0.00 to 0.5% zirconium, 0.0 to 3.0% rhenium, 0.0 to 2.0% ruthenium, 0.0 to 3.0% iridium, 0.0 to 0.5% vanadium, 0.0 to 1.0% palladium, 0.0 to 1.0% platinum, 0.0 to 0.5% silicon, 0.0 to 0.1% yttrium, 0.0 to 0.1% lanthanum, 0.0 to 0.1% cerium, 00 to 0.003% sulphur, 0.0 to 0.25% manganese, 0.0 to 0.1 magnesium, 0.0 to 4.0% iron, 0.0 to 0.5% copper, 0.0 to 0.5% hafnium, the balance being nickel and incidental impurities, wherein the following equations are satisfied in which WNb, and WTa are the weight percent of niobium and tantalum respectively 1.1 < 0.3 WNb + 0.1 WTa Such a nickel based alloy has superior hot cracking resistance as well as reasonable creep resistance, strength, strain age cracking resistance, microstructural stability as well as acceptable freezing range, density and cost.
In an embodiment the following equation is satisfied in which Wm, and Wra are the weight percent of niobium and tantalum in the alloy respectively 1.2 < 0.3WNb + 0.15WTa preferably 1.4 0.3WNb + 0.15WTa or preferably 1.8 0.3 WNb + 0.15 WTa Such an alloy has further improved hot cracking resistance.
In an embodiment the following equation is satisfied in which WA], WTI WNb and WT11 are the weight percent of aluminium, titanium, niobium and tantalum in the alloy respectively 5.6 WA] + 0.5W11 0.3WNb + 0.15WTa 7.0 preferably 5.6 Wm + 0.5 Wri 0.3 Kb 0.15Wra < 6.5 Such an alloy has improved strain age cracking resistance.
In an embodiment the following equation is satisfied in which Ww and Wm. are the weight percent of tungsten and molybdenum in the alloy respectively Ww + 0.65Wmo > 4.0 preferably Ww + 0.65Wmo > 6.0 more preferably Ww + 0.65Ww, > 8.0 Such an alloy has improved creep resistance.
In an embodiment the nickel-based alloy composition consists of, in weight percent, 8.0% or more chromium, preferably 10.0% or more. Such an alloy has improved oxidation resistance.
In an embodiment the nickel-based alloy composition consists of, in weight percent, 14.7% or less chromium, preferably 13.8% or less. Such an alloy has improved microstructural stability.
In an embodiment the nickel-based alloy composition consists of, in weight percent, 9.8wt% or less tantalum, preferably of 9.2% or less tantalum, more preferably of 7.1% or less tantalum. Such an alloy has reduced density.
In an embodiment the nickel-based alloy composition consists of, in weight percent, 2.0% or less molybdenum, preferably 1.8% or less molybdenum. Such an alloy has improved hot corrosion resistance.
In an embodiment the nickel-based alloy composition consists of, in weight percent, 0.5% or less titanium, preferably 0.1% or less titanium. Such an alloy has better oxidation resistance.
In an embodiment the nickel-based alloy composition consists of, in weight percent, 10.7 or less tungsten, preferably 8.7or less tungsten. Such an alloy has improved microstructural 20 stability.
In an embodiment the nickel-based alloy composition consists of, in weight percent, 3.0% or less niobium. Such an alloy has improved oxidation resistance.
In an embodiment the nickel-based alloy composition consists of, in weight percent, 0.5% or less of one or both of platinum and palladium. Such an alloy has lower cost.
In an embodiment the nickel-based alloy composition consists of, in weight percent, 4.5% or more aluminium. Such an alloy has improved corrosion resistance.
In an embodiment the nickel-based alloy composition consists of, in weight percent, 5.3% or less aluminium, preferably of 5.1% or less aluminium, more preferably of 4.6% or less aluminium. The strain age cracking and resistance are improved in such an alloy in combination with improved hot cracking resistance.
In an embodiment the nickel-based alloy composition consists of, in weight percent, 15.0% or less cobalt. Such an alloy has a lower freezing range.
In an embodiment the nickel-based alloy composition consists of, in weight percent 1.1wt% or more tantalum, preferably of 3.7% or more tantalum, more preferably of 5.8% or more tantalum. Such an alloy allows the amount of niobium to be reduced without reduction in hot cracking resistance, or in combination with higher levels of niobium, improves hot cracking resistance yet further.
In an embodiment the nickel-based alloy composition consists of, in weight percent 2.7wt% or more tungsten, preferably of 2.8% or more tungsten, more preferably of 4.7% or more tungsten, even more preferably of 5,1% or more tungsten, most preferably of 5.2% or more tungsten.
Such an alloy has improved creep resistance.
In an embodiment the following equation is satisfied in which Wra and Ww are the weight percent of tantalum and tungsten in the alloy respectively Ww WTa < 13.9 preferably WW WTa < 11.8 Such an alloy has reduced density.
In an embodiment the following equation is satisfied in which \Wt., Wm. and Ww are the weight percent of chromium, molybdenum and tungsten in the alloy respectively Ww + Mtn. + 1.7WAR, _< 18.7 preferably Ww + Wct + 1.7Wmo <17.8 Such an alloy has improved mierostructural stability.
Figure 1 shows the calculated values for strain age merit index and hot cracking index for a number of commercially used superalloys (including alloys listed in Table 1), limits for creep resistance, stain age cracking and hot cracking are identified, the target area for the invention is shaded; Figure 2 is a contour plot showing the effect of y' forming elements aluminium and niobium plus tantalum (according to the relationship 0.3 Wivb+0.15 Wm) on volume fraction of y' when titanium content is fixed at 0.0 wt% for alloys within the alloy design space, determined from phase equilibrium calculations conducted at 900°C. Delineated on the graph are different limits for strain age index and hot cracking index; Figure 3 is a contour plot showing the effect of y' forming elements aluminium and niobium plus tantalum (according to the relationship 0.3W,vb+0.15Wm) on hot cracking index when titanium content is fixed at 0.0 wt% for alloys within the alloy design space, determined from phase equilibrium calculations conducted at 900 °C; Figure 4 is a contour plot showing the effect of y' volume fraction and creep merit index on creep temperature capability, contours have been normalised to IN713C alloy, the predicted position for alloys listed in Table 1 is shown; Figure 5 is a contour plot showing the effect of elements molybdenum and tungsten on creep merit index, delineated on the graph are limits for stability at different concentrations of chromium; Figure 6 is a contour plot showing the effect of elements molybdenum and tungsten on alloy stability (in terms of Md number) when the chromium content is fixed at 6.0 wt%, delineated on the graph are different levels for creep merit index; Figure 7 is a contour plot showing the effect of elements molybdenum and tungsten on 30 alloy stability (in terms of Md number) when the chromium content is fixed at 8.0 wt%, delineated on the graph are different levels for creep merit index; Figure 8 is a contour plot showing the effect of elements molybdenum and tungsten on alloy stability (in terms of Md number) when the chromium content is fixed at 10.0 wt%, delineated on the graph are different levels for creep merit index; Figure 9 is a contour plot showing the effect of elements molybdenum and tungsten on alloy stability (in terms of Md number) when the chromium content is fixed at 12.0 wt%, delineated on the graph are different levels for creep merit index; Figure 10 is a contour plot showing the effect of elements molybdenum and tungsten 10 on alloy stability (in terms of Md number) when the chromium content is fixed at 14.0 wt%, delineated on the graph are different levels for creep merit index; Figure 11 is a contour plot showing the effect of elements molybdenum and tungsten on alloy stability (in terms of Md number) when the chromium content is fixed at 16.0 wt%, delineated on the graph are different levels for creep merit index; Figure 12 is a contour plot showing the effect of elements tantalum and tungsten on alloy density; Figure 13 is a contour plot showing the effect of strain age cracking index and cobalt on alloy solidification range; and Figure 14 shows micrographs of nickel-based superalloys manufactured using a powder-bed based AM process. Apparent is the effect of hot cracking index (1-1C1) on the susceptibility to cracking during AM processing rationalising the preferred limit for hot cracking index of 1.5 or less of the present invention.
Traditionally, nickel-based superalloys have been designed through empiricism. Thus their chemical compositions have been isolated using time consuming and expensive experimental development, involving small-scale processing of limited quantities of material and subsequent characterisation of their behaviour. The alloy composition adopted is then the one found to display the best, or most desirable, combination of properties. The large number of possible alloying elements indicates that these alloys are not entirely optimised and that improved alloys are likely to exist.
In superalloys, generally additions of chromium (Cr) and aluminium (Al) are added to impart resistance to oxidation/corrosion, cobalt (Co) is added to improve resistance to sulphidisation. For creep resistance, molybdenum (Mo), tungsten (W), cobalt are introduced, because these retard the thermally-activated processes -such as, dislocation climb -which determine the rate of creep deformation. To promote static and cyclic strength, aluminium (Al), tantalum (Ta), niobium (Nb) and titanium (Ti) are introduced as these promote the formation of the precipitate hardening phase gamma-prime (y9. This precipitate phase is coherent with the face-centred cubic (FCC) matrix phase which is referred to as gamma (y).
A modelling-based approach used for the isolation of new grades of nickel-based superalloys is described here, termed the "Alloys-By-Design" (ABD) method. This approach utilises a framework of computational materials models to estimate design relevant properties across a very broad compositional space. In principle, this alloy design tool allows the so-called inverse problem to be solved; identifying optimum alloy compositions that best satisfy a specified set of design constraints.
The first step in the design process is the definition of an elemental list along with the associated upper and lower compositional limits. The compositional limits for each of the elemental additions considered in this invention -referred to as the "alloy design space" -are detailed in Table 2.
Table 2: Alloys design space in wt% searched using the "Alloys-by-Design" method.
Alloy (wt%) Al Co Cr Mo Nb Ta Ti W Min 2.0 0.0 2.0 0.0 0.0 0.0 0.0 0.0 Max 10.0 25.0 18.0 8.0 6.0 14.0 4.0 16.0 The balance is nickel. The levels of carbon, boron and zirconium where fixed at 0.06%, 0.015% and 0.06% respectively.
The second step relies upon thermodynamic calculations used to calculate the phase diagram and thermodynamic properties for a specific alloy composition. Often this is referred to as the CALPHAD method (CALeulation of PHAse Diagrams). These calculations are conducted at the typical service temperature for the new alloy (900°C), providing information about the phase equilibrium (microstructure).
A third stage involves isolating alloy compositions which have the desired microstructural architecture. Tn the case of nickel-based superalloys which require superior resistance to creep deformation, the creep rupture life generally improves as the volume fraction of the precipitate hardening phase 7' is increased, the most beneficial range for volume fraction of 7' lies between 60%-70%. At values above 70% volume fraction of 7' a reduction in creep resistance is observed.
It is also necessary that the 7/7' lattice misfit should conform to a small value, either positive or negative, since coherency is otherwise lost; thus limits are placed on its magnitude.
The lattice misfit 6 is defined as the mismatch between 7 and 7' phases, and is determined according to -2(art -a a,+a (1)
Y
where ar and ay are the lattice parameters of the y and 7' phases.
Rejection of alloy on the basis of unsuitable microstructural architecture is also made from estimates of susceptibility to topologically close-packed (TCP) phases. The present calculations predict the formation of the deleterious TCP phases sigma (a), P and mu (u) using 25 CALPIIAD modelling.
Thus the model isolates all compositions in the design space which are calculated to result in a desired volume fraction of y', which have a lattice misfit y' of less than a predetermined magnitude and have a total volume fraction of TCP phases below a 30 predetermined magnitude.
In the fourth stage, merit indices are estimated for the remaining isolated alloy compositions in the dataset. Examples of these include: creep-merit index (which describes an alloy's creep resistance based solely on mean composition), strength-merit index (which describes an alloy's precipitation yield strength based solely on mean composition), solid-solution merit index (which describes an alloy's solid solution yield strength based solely on mean composition), density and cost.
In the fifth stage, the calculated merit indices are compared with limits for required behaviour, these design constraints are considered to be the boundary conditions to the problem. All compositions which do not fulfil the boundary conditions are excluded. At this stage, the trial dataset will be reduced in size quite markedly.
The final, sixth stage involves analysing the dataset of remaining compositions. This can be done in various ways. One can sort through the database for alloys which exhibit maximal values of the merit indices -the lightest, the most creep resistant, the most oxidation resistant, and the cheapest for example. Or alternatively, one can use the database to determine the relative trade-offs in performance which arise from different combination of properties.
The example seven merit indices are now described.
The first merit index is the creep merit index. The overarching observation is that time-dependent deformation (i.e. creep) of a nickel-based superalloy occurs by dislocation creep with the initial activity being restricted to the y phase. Thus, because the fraction of the y' phase is large, dislocation segments rapidly become pinned at the y/y' interfaces. The rate-controlling step is then the escape of trapped configurations of dislocations from y/y' interfaces, and it is the dependence of this on local chemistry -in this case composition of the 7 phase -which gives rise to a significant influence of alloy composition on creep properties.
A physically-based microstructure model can be invoked for the rate of accumulation of creep strain e when loading is uniaxial and along the 001) crystallographic direction. The equation set is n(ool) = P.,10"Defr (1-cap)(1 / 0p113 1)sinh = Ce001) o-b2 co where R1 is the mobile dislocation density, Op is the volume fraction of the 7' phase, and t-.0 is width of the matrix channels. The terms cr and T are the applied stress and temperature, respectively. The terms b and k are the Burgers vector and Boltzmann constant, respectively. The term JI =1+20p" / 1"Tc(1-Op") is a constraint factor, which accounts for the close proximity of the cuboidal particles in these alloys. Equation 3 describes the dislocation multiplication process which needs an estimate of the multiplication parameter C and the initial dislocation density, The term Rif is the effective diffusivity controlling the climb processes at the particle/matrix interfaces.
Note that in the above, the composition dependence arises from the two terms or, and D. . Thus, provided that the microstructural architecture is assumed constant (microstructural architecture is mostly controlled by heat treatment) so that Op is fixed, any dependence upon chemical composition arises through R. For the purposes of the alloy design modelling described here, it turns out to be unnecessary to implement a full integration of Equations 2 and 3 for each prototype alloy composition. Instead, a first order merit index Afcreep is employed which needs to be maximised, which is given by _Keep =Ix / (4) where x, is the atomic fraction of solute i in the 7 phase and ne is the appropriate interdiffusion coefficient.
The second merit index is for strength merit index. For high nickel-based superaBoys, the vast majority of strength comes from the precipitate phase. Therefore, optimising alloy composition for maximal precipitate strengthening is a critical design consideration. From hardening theory, a merit index for strength, /14 -strength, is proposed. The index considers the maximum possible precipitate strength -determined to be the point where the transition from weakly coupled to strongly coupled dislocation shearing occurs -which can be approximated using, Mstrength = m * YAPB Sup / M. f-A 1 / 2,, (5) Where M is the Taylor factor, yApg is the anti-phase boundary (APB) energy, Op is the volume fraction of the y' phase and b is the Burgers vector. ;From Equation 5 it is apparent that fault energies in the y' phase -for example, the anti-phase boundary APB energy -have a significant influence on the deformation behaviour of nickel-based superalloys. Increasing the APB energy has been found to improve mechanical properties including, tensile strength and resistance to creep deformation. The APB energy was studied for a number of Ni-Al-X systems using density functional theory. From this work the effect of ternary elements on the APB energy of the y' phase was calculated, linear superposition of the effect for each ternary addition was assumed when considering complex multicomponent systems, resulting in the following equation, YAPB = 195 -1.7xcr -1.7xmb 4.6xw 27.1xn, 21.4xN5 15xTi (6) where, :err, xmo, xw, xra, xm, and xT, represent the concentrations, in atomic percent, of 20 chromium, molybdenum, tungsten, tantalum, niobium and titanium in the y' phase, respectively. The composition of the 7' phase is determined from phase equilibrium calculations. ;The third merit index is density. The density, p, was calculated using a simple rule of mixtures and a correctional factor, where, p, is the density for a given element and x, is the atomic fraction of the alloy element. ;p = 1.05 [Ei xipi] (7) The fourth merit index was cost. In order to estimate the cost of each alloy a simple rule of mixtures was applied, where the weight fraction of the alloy element, x,, was multiplied by the current (2016) raw material cost for the alloying element, c,. ;Cost = Zixtc, (8) The estimates assume that processing costs are identical for all alloys, i.e. that the product yield is not affected by composition. ;A fifth merit index is based upon rejection of candidate alloys on the basis of unsuitable microstructural architecture made on the basis of susceptibility to TCP phases. To do this use is made of the d-orbital energy levels of the alloying elements (referred as Md) to determine the total effective Md level according to Md = Ei xiMdi (9) where the z represents the mole fraction of the element i in the alloy. Higher values of Md are indicative of higher probability of TCP formation. ;The sixth merit index is a strain age cracking index. The ability of an alloy to be processed by additive manufacturing is related to the chemical composition. The index is developed from the empirical observations which relate alloy composition to the weldability of nickel-based superalloys in terms of susceptibility to strain age cracking. In this relationship a factor of 0.5 is added to the titanium content to convert this to an "aluminium equivalent" as titanium has approximately twice the density of aluminium, in effect the additive manufacturing process for metallic alloys is a continuous welding process. There has been adaption of previous observations which only relate weldability to aluminium and titanium content. A modification is included to account for the influence of tantalum and niobium, which behave in a similar manner to aluminium and titanium during alloy aging. Similar to titanium a constant is added to convert these elemental additions to an "aluminium equivalent", thus, niobium and tantalum have correctional factors (determined from their density relative to aluminium) of 0.3 and 0.15 respectively. The strain age index is applied via the following equation. ;Mstrain-age -(WAI + 0.5 WTI 0.3WNb C.15 Wra) (10) where Wai, WTI, WNb, and Wra the weight percent of aluminium, titanium, niobium and tantalum in the alloy by weight percent. A lower value of this strain age index indicates a better response to the additive manufacture process. ;A seventh merit index is based on the solidification behaviour of candidate alloys as predicted by the Schell-Gulliver model, in order to rank susceptibility to hot cracking based on composition. In this approach the temperature range of the terminal stage of solidification, between 90% and 99% fraction solid, is taken to represent the region where an alloy is vulnerable to hot cracking, as it is in this phase that liquid feeding is likely to he restricted by bridged networks of solid material. The temperature range of 40% to 90% of solid fraction is considered to be the safe region, since liquid feeding is far less restricted in this stage; the temperature range before 40% fraction solid is not considered to be relevant because liquid is still the predominant phase. ;According to the ranking system used by Clyne and Davis for alloy castings, the hot cracking index is defined as the ratio of the vulnerable temperature range to the safe temperature range, as follows: HC1 -7190-T99 T40 -T90 Lower values of this index correspond to a lower risk of hot cracking. ;The ABD method described above was used to isolate the inventive alloy composition. The design intent for this alloy is to develop a highly creep resistant superalloy -achieved by having a high volume fraction of y' -combined with improved processability by additive manufacturing compared to other high volume y' alloys -achieved by having an improved resistance to strain age cracking and to the mechanism of hot cracking. Alongside these attributes a good resistance to oxidation is achieved by having sufficient levels of aluminium to form a protective aluminium-based oxide scale and other key material properties including microstructural stability and alloy density are optimised. ;The material properties -determined using the ABD method -for the typical compositions, listed in Table 1, are listed in Table 3. The design of the new alloy was considered in relation to die predicted properties listed for these alloys. ;The rationale for the design of the new alloy is now described. ;Table 3: Calculated phase fractions and merit indices made with the "Alloys-by-Design" software. Results for nickel-based superalloys listed in Table I. Strength Md Strain Hot Freezing Cost Creep Merit y/y' Merit Age Cracking Range Index Density Misfit Index Index Index Alloy 7' (m-2s x 10') (Wee) (%) (Mpa) (eV) ("C) $/Kg 1N738 0.45 5.9 8.3 0.16 1517 0.92 5.6 1.82 259 5.54 CM247LC 0.59 8.0 8.6 -0.05 1243 0.92 6.3 4.44 606 10.63 1N713 0.55 5.8 8.0 -0.35 1139 0.93 7.0 2.03 213 2.59 IN792 0.51 6.5 8.5 0.17 1702 0.92 5.9 2.05 269 7.54 Alloys with a high strain-age cracking index are known from welding literature to be difficult to process, and the same trends are generally observed in AM. Reducing the strain-age merit index lowers the propensity to this failure mechanism, however, high-temperature strength (in terms of creep strength and tensile strength) and oxidation resistance (in terms of protective oxide scale formed) are dependent on a relatively high content of y'-forming elements which makes avoiding a high strain-age index difficult. To overcome this strain-age cracking can be managed in other ways. For example, carefully controlling the in-process AM conditions (scan strategy, heat input, etc.) and the post-processing conditions (heat treatment window and heating rate) can limit the risks associated with strain-age cracking. Similarly, the risk of strain-age crack can be reduced by designing the geometry of the components in way which reduces stress-concentrating features that result in localised strain age cracking. See for example US 9352421 B2 and US 9670572 B2. ;Unlike strain age cracking another manufacturing defect which can arise during the additive manufacturing process is hot cracking. Hot cracking may happen during the solidification process. The mechanism of this manufacturing defect is driven by changes in liquid composition during solidification of the alloy. The risk of hot cracking occurring cannot be managed in the same way as strain age cracking. Carefully controlling the in-process AM conditions may help to some degree, however, the use of post processing or design changes will not influence this mechanism for example. The most direct way to improve resistance to hot cracking is by modification of alloy chemistry. Improving the resistance to hot cracking substantially improves the processability of an alloy for additive manufacturing even when a high strain-age cracking index must be tolerated. It is the aim of this invention to isolate alloys which have low values of hot cracking index relative to other alloys and which have a high strain age index in a range in which strain-age cracking can be managed by processing conditions, see Figure 1. ;Figure 2 describes the relationship between the addition of elements aluminium, niobium and tantalum which are predominantly added to form the 7' phase and control the volume fraction of y'. ;The elements which form the y' phase may reduce the ease by which an alloy can be processed by AM due to an increasing strain age merit index (Equation 10). Thus the combination of these elements must be optimised to provide the desired balance between limiting likelihood of strain age cracking during AM processing and volume fraction of 7' (which provides strength in terms of creep resistance and tensile strength.). ;To achieve the preferred strain age cracking index the aluminium, titanium, niobium and tantalum content must satisfy the following constraint f(SAC) = WAt 0.5WT, 0.3WNb 0.1.5Wra where, f(SAC) is a numerical value of 7.0 or less and Wm, Wn, WNb and Wib are the weight percent of aluminium, titanium, niobium and tantalum in the alloy respectively. A value of 7.0 or less is selected to be equivalent or better than alloy IN713C, see Table 3. Values for f(SAC) greater than 7 are less preferable because they limit the processing of the alloy in terms of strain age cracking. It is preferable to lower the strain age merit index, to enable easier processing by AM, so preferably Wm + 0.5Wn + 0.3WNb + 0.15Wra < 6.5. ;The intended application temperature for this new alloy is up to temperatures of 1000 °C in highly oxidising and corrosive environments. Examples of the application areas include hot sections of a gas turbine engine or within the exhaust system of an internal combustion 30 engine. ;To achieve desirable oxidation performance it is desired that the alloy of the invention must form a protective aluminium-based oxide scale (A1203), as such oxides arc stable at and above 1000 °C as opposed to those based on Cr203. Alloys such as 1N738 and 1N792 have a relatively high volume fraction of 7' and very good creep resistance but their relatively low aluminium content -3.4 wt% and 3.2 wt%, respectively -means they are unable to form an aluminium-based protective oxide scale, instead they form a less protective chromium based oxide scale. An aluminium-based oxide scale has better adhesion and thermal stability in comparison to chromium-based protective oxide scales which may encounter chromium volatisation at temperatures close to 1000 °C, resulting in a less protective oxide. To produce an aluminium-based protective oxide scale an aluminium content of at least 4.0 wt% is required, more preferably 4.5 wt% or more as this further improves the formation of the alumina scale providing better oxidation resistance. ;Alloying additions of titanium are known to decrease oxidation performance due to the formation of titanium oxides. This has been found to be significantly deleterious to the oxidation performance. For the alloy of the invention titanium use is limited to 1.0 wt%, preferably 0.5 wt% and most preferably 0.1 wt% due to its negative influence on high temperature oxidation resistance. Titanium also has a relatively high co-efficient for strain age cracking (Equation 10) so it is beneficial to limit titanium to reduce propensity to strain age cracking. ;Alloying additions of niobium are also known to negatively influence oxidation. This is because niobium forms grain boundary carbides which are particularly detrimental for oxidation assisted cracking mechanisms in which damage may accumulate along grain boundaries, such as under low cycle fatigue, creep-fatigue conditions or during high temperature creep. However, additions of niobium are beneficial for improving resistance to hot cracking resistance (discussed later with reference to Figure 3) so its use is limited to 4.0 wt%, more preferably 3.0 wt% or less. ;Additions of chromium will promote the formation a protective alumina oxide scale. ;Chromium in particular is desirable for improving resistance to hot corrosion. Alloys such as 114738 and IN792 have relatively high level of chromium -16.0 wt% and 12.7 wt%, respectively-this is primarily for resistance to hot corrosion, however, the maximum operating temperature is limited as they have poor oxidation kinetics at very high temperatures as they do not form protective aluminium-based oxides. The upper limit of operating temperature for these alloys is also limited as they have a lower resistance to creep relative to IN713C (Figure 4). The alloy of this invention requires a chromium content of 6.0 wt% or greater. A chromium level of 6.0 wt% or greater is desirable in order to achieve a good level of hot corrosion resistance. More preferably the chromium content is 8.0 wt% or greater as this provides hot corrosion resistance equivalent to CM247LC. Even more preferably chromium is present in an amount of 10.0% or greater this increases the corrosion resistance in comparison to alloy CM247LC even further. ;Molybdenum is known to reduce the hot corrosion resistance of nickel superalloys significantly. Therefore, to achieve a good level of corrosion resistance it preferable to limit molybdenum to 3.0 wt% or less. More preferably molybdenum is limited to 2.0 wt% or less. Most preferably molybdenum is limited to 1.8 wt% or less as alloys 1N738 and IN792 are known to have a very good resistance to corrosion. ;Based upon the minimum content for aluminium (4.0 wt%) and the desirability for f(SAC)<7, as well as the preference to limit the alloy to less than 0.1 wt% titanium (e.g 0.0 wt%), it is necessary to limit the sum of the elements tantalum and niobium according to the relationship 0.3 Wivb+0. l5WT, to 3.0 or less. Therefore, the maximum limits of niobium and tantalum should be 9.7 wt% and 20.0 wt% respectively. Preferably for an improved balance of oxidation resistance (aluminium 4.5 wt% or greater) and strain age cracking resistance (f(SAC)<6.5) 0.3W.vb+0.15Wra is limited to 2.5 or less. Therefore the maximum limit of niobium and tantalum should more preferably be 8.1 wt% and 16.6 wt% respectively. Most preferably a balance of resistance to strain age cracking and oxidation resistance is achieved when aluminium is 5.0 wt% and J(SAC)<6.5, therefore it is most preferable to limit 0.3 Wivb+0.15 Wm to 2.0 or less. Therefore the maximum limit of niobium and tantalum should be 6.5 wt% and 13.3 wt% respectively. However as will be explained later, the alloy of the present invention actually requires even lower levels of niobium and tantalum. ;Plotted on Figure 2 are dotted lines depicting different limits for strain age cracking. It is seen that to produce an alloy which has a strain age index of less than 7 it is preferable that the y' volume fraction is limited to 0.63 at an equilibrium temperature of 900 °C. Preferably the volume fraction of 7' volume fraction is limited to 0.56 based on the more preferred value for strain age index Wm + 0.5 WTI + 0.3 WNb 0.15WTa Lc. 6.5. ;The desirable minimum requirement for volume fraction of y' is 0.42, described later in relation to achieving required creep resistance using Figure 4 and Figure 5. To achieve the desired volume fraction of 7' the aluminium, titanium niobium and tantalum content must satisfy the following constraint f (Yr) = WA! "WTI "WNb °.15WTa where, f(y2 is a numerical value which ranges between 5.6 and 7.0 to produce an alloy with the desired y' fraction of between 0.42 and 0.63. Iff(y2 is a numerical value which ranges between 5.6 and 6.5 an alloy with a y' fraction between 0.42 and 0.56 is produced resulting in an alloy with an improved combination of high creep strength and AM processing. Described later in reference to improving alloy creep resistance it is preferred to have a 7' fraction of 0.43 or greater, more preferably 0.45 or greater and most preferably 0.50 or greater, resulting in preferred values off(y') of 5.7 or more, 5.8 or more and 6.1 or more respectively. ;The elements platinum, palladium behave in a similar way to that of tantalum, titanium and niobium i.e. they are y' forming elements which increase anti-phase boundary energy. ;These elements can optionally be added to the alloy in substitution for the elements tantalum, titanium and niobium. The benefits of this may include an improvement in resistance to high temperature corrosion. The "aluminium equivalent", for platinum and palladium require correctional factors (determined from their density relative to aluminium) of 0.125 and 0.225 respectively. However, additions of these elements can be limited due to the high cost of these elemental additions. Therefore, those elements can each be present in an amount of up to 1.0 wt%, preferably they are limited to 0.5 wt% or less and most preferably 0.1 wt% or less as this range provides the best balance of cost and improvement to corrosion resistance. It is preferred that the following equation is satisfied to provide good processing by additive manufacturing Wm + 0.5W1 + 0.3 WNb + 0.15 WTa 0.125Wpt 0.225Wpd 7.0 preferably 0.5Wri 0.3WNb + 0.15 Wra 0.125Wpt 0.225Wpd 6.5 where WPt and Wpd are the weight percent of platinum and palladium in the alloy respectively. ;The propensity for an alloy to form hot cracks is determined in terms of a hot cracking index (Equation 11). This hot cracking mechanism is driven by elements which segregate primarily to the liquid phase during solidification, in the design space studied (Table 2) niobium and tantalum are elements which segregate most heavily to liquid phase, therefore they have the strongest influence on hot cracking. ;Figure 3 shows the hot cracking index as a function of the of elements aluminium, niobium and tantalum as these drive strain age cracking (as described in relation to Figure 1 balancing of strain age cracking and hot cracking is necessary for best AM processability). It is seen that niobium and tantalum strongly affect the hot cracking index. The alloys listed in Table 1 show a high propensity for hot cracking failure during AM, alloy IN738 is the least prone to hot cracking with an index of 1.8. Alloys which process very well in AM and do not exhibit hot cracking, such as alloy 718 and alloy 625 have a hot cracking index of less than 1 0 (Figure 1). For an alloy which is much more resistant to hot cracking an index of less than 1.5 is useful, from Figure 3 it is determined that to achieve the desired hot cracking index the niobium and tantalum content must satisfy the following constraint f (H CI) = 0.3WNb + 0.15Wra where f(HCI) is a numerical value, of which a value of 1.1 or greater achieves a hot cracking index of 1.5 or less. On Figure 2 the line for a hot cracking index 011.5 is superimposed. It is seen that to achieve a hot cracking index of 1.5 or less in combination with a strain age cracking index of 7.0 or less aluminium must be limited to 5.6 wt% or less. More preferably a hot cracking index of 1.5 or less in combination with a strain age index of 6.5 or less is desired so it is preferable to limit to 5.3 wt% aluminium. It is preferred that niobium is limited to 3.0wt% or less for improving alloy resistance to oxidation assisted cracking. When niobium is at its preferred level of 3.0 wt% to achieve a hot cracking index of 1.5 or less in combination with a strain age index of 6.5 or less it is preferred that the alloy contains at least 1.1wt% tantalum to achieve the desired value for hot cracking index. ;For better resistance to hot cracking it is more preferable to have a hot cracking index of 1.0 or less, so a numerical value for f(HC1) of greater than 1.8 is preferred, though a value of 1.2 or greater or 1.4 or greater is also desirable. On Figure 2 thc lines for a hot cracking index of 1.0 and 1.5 are superimposed (HCI=1 and HCI=1.5). It is seen that to achieve a hot cracking index of 1.0 or less in combination with a strain age cracking index of 7.0 or less aluminium is limited to 5.1 wt% or less, more preferably a hot cracking index of 1.0 or less in combination with a strain age index of 6.5 or less is desired so it is preferable to limit to 4.6 wt% aluminium Based upon the maximum niobium content (4.0 wt%) to achieve the preferred numerical value for.f(HCI) of 1.8 or more it is preferred that the tantalum content is at least 3.7 wt%, more preferably niobium is limited to 3.0 wt% or less therefore it is preferred that 10 tantalum content is 5.8 wt% or more. ;Additions of cobalt have the effect of lowering the y' solvus temperature. A lowering * of y' solvus temperature is desirable as it reduces the temperature at which y' precipitation will occur which is advantageous for reducing the rate at which strain-age hardening occurs, as this relies on y' precipitation, A lower y' solvus also improves the ability to perform solution heat-treatment needed to homogenise distribution of elemental species occurring after the AM process and also needed to modify certain microstructural features, for example enlarging grain size and to dissolve coarse y' precipitates which do not provide a great strengthening benefit; by rapidly cooling from solution heat-treatment temperature a fine dispersion of y' particles can be achieved which aid improved mechanical properties.
However, as cobalt content increases, the Scheil solidification temperature range of the alloy is increased (Figure 13). A high freezing range is associated with an increased length of time to solidify, and when the alloy is in a semi-solid condition it can be at risk of solidification cracking, so it is desirable to limit the freezing range. A target freezing range of 300 °C or less is desired, therefore cobalt up to 22.0 wt% is allowable. In order to match the freezing range of IN792, it is desirable that the cobalt content is 15.0 wt% or less.
The relationship between y' volume fraction and creep merit index on creep resistance 30 (in terms of temperature capability at 137MPa, with contours normalised to IN713) is shown in Figure 4, increasing both parameters will increase creep resistance and the sensitivity to each parameter is determined. The position of the alloys listed in Table 3 are shown in Figure 4.
The aim of the invention is to have a creep performance which is equivalent to 1N713C, more preferably an improvement of 25 °C is desired.
For the alloy of this invention it is desired that the creep merit index higher than alloy IN713C. Therefore, for the alloy of this invention a creep merit index of 6.0 x 1015 tn-2s is desired. The elemental additions required to achieve this level of creep merit index are reviewed in following section with reference to Figures 5. the maximum achievable creep merit index is determined from the need to have a minimum of 6.0 wt% chromium in the alloy for corrosion resistance while maintaining a stable microstructure which is essentially free from TCP phases (see Figure 5). A y' volume fraction of 0.42 is desired to have a creep resistance equivalent to 1N713C. More preferably a minimum of 25°C improvement of creep resistance of 1N713C is desired, therefore particularly when the creep merit index is 6.0 x 10-15 m-2s it is preferable to have a y' volume fraction of 0.50, this is equivalent to numerical value of f(1) greater than or equal to 6.1.
Slow diffusing elements which partition to the gamma matrix phase most strongly influence the creep merit index, which is calculated based upon the composition of the gamma-phase at an equilibrium temperature of 900 °C. Tungsten is the slowest diffusing element in the alloy design space listed in Table 2, followed by molybdenum. The influence of the elements tungsten and molybdenum on creep resistance is presented in Figure 5. From Figure 5 it is determined that the change in creep merit index was related to the sum of the elements molybdenum and tungsten according to the formula f (CMI) = Ww + 0.65Wm0 where f(C1All) is a numerical value and Ww and Wm. are the weight percent of tungsten and molybdenum in the alloy respectively. A value of 4.0 or greater is desired as this achieves the desired creep merit index of 6.0 x 10-15 m-2s. Based upon the maximum limit of molybdenum (3.0 wt%) a minimum tungsten content of 2.0 wt% is required. More preferably molybdenum is limited to 2 wt% therefore it is preferred to have a tungsten content of 2.7 wt% or greater.
Most preferably molybdenum is limited to 1.8 wt% therefore it is most preferable to have a minimum of 2.8 wt% or greater. A more desirable level off(CMI) is 6.0 or greater, preferably 8.0 or greater.
For an even better combination of creep resistance and resistance to strain age cracking it is desired to have a 25 °C improvement in temperature capability over IN7I3C combined with a strain age cracking index of 6.5 or less. This limits the maximum y' volume fraction to 0.56, therefore a creep merit index of 6.90 x 10-15 m-2s or greater is required. To achieve a creep merit index of 6.90 x 1045 m-2s or greater the value for J(CM./) must be 6.4 or greater. Based upon the maximum limit of molybdenum (3 wt%) a minimum tungsten content of 4.7 wt% is required. More preferably molybdenum is limited to 2.0 wt% therefore it is preferred to have a tungsten content of 5.1 wt% or greater. Most preferably molybdenum is limited to 1.8 wt% therefore it is most preferable to have a minimum of 5.2 wt% or greater.
The elements rhenium, ruthenium and iridium behave in a similar way to that of tungsten i.e. they are gamma forming elements which improve the creep merit index. These elements can optionally be added to the alloy. Additions of these elements will significantly increase the creep response of the alloy in comparison to tungsten (as they have much slower diffusivity), however this is achieved with substantial increases in cost due to the high cost of the elements. Preferably the addition of rhenium and iridium is limited to less than 3.0 wt% and even more preferably less than 2 0 wt%, most preferably less than 1.5 wt% due to its elemental cost. Ruthenium deleteriously increases hot cracking index (see AM1055 and AM1056) and so it is limited 2.0 wt%, preferably 1.5 wt%.
There is a trade-off between creep resistance (in terms of creep merit index), alloy stability (in terms of Md number) and alloy corrosion resistance (in terms of chromium content), The limit for alloy stability at different levels of chromium content as determined by the equation for j(stability) (described below with reference to figures 6-10) are delineated on Figure 5. It is seen that as chromium is increased for a given microstructural stability the creep merit index reduces. Thus lower levels of chromium are seen to be beneficial for microstructural stability but undesirable for high creep merit index.
Improvements in oxidation and in particular corrosion resistance come from additions of chromium. However, the additions of molybdenum and tungsten for creep resistance as well as chromium for oxidation and corrosion resistance will increase the propensity for the alloy to form unwanted TCP phases. Figures 6-10 show the effect of tungsten and molybdenum additions on phase stability for alloys containing different levels of chromium. A higher stability number results in an alloy which is more prone to TCP phase formation. Limiting or stopping the precipitation of TCP phase formation is beneficial as these phases lead to deterioration in material properties over time. A complex trade-off between mechanical performance, oxidation/corrosion resistance and microstructural stability must be managed.
S
A stability number target (Md) of 0.93 or less (determined at an equilibrium temperature of 900 °C) is desired in order to ensure microstructural stability and avoid TCP formation, see prior art alloys in Table 3. More preferably a stability number target of 0.92 or less is desirable in order to ensure better microstructural stability and avoid TCP formation.
From Figures 6-10 it is determined that for alloys with a volume fraction of y' between 42-63% the additions of the elements molybdenum tungsten and chromium adhere to the following equation f (stability) = Ww + We, + 1.7Wmo where [(stability) is a numerical value. Iff(stability) has a value or 18.7 or less an alloy with a stability number of 0.93 or less is achieved. Based on the equation for f(stability), assuming the minimum amount of tungsten of 2.0 wt%, chromium may be present in an amount of 16.7 wt% or less in order to satisfy the desirable microstructural stability Md of 0.93 or less. Based on the equation forfry/ability) when chromium levels are 6.0 wt% a maximum limit of 12.7 wt% tungsten can be included in the alloy. A preferred chromium content of 8.0 wt% and even more preferably 10 wt% results in tungsten being limited to 10.7 wt % or less and 8.7 wt% or less respectively.
The best balance of creep resistance and corrosion resistance (while maintaining alloy stability) is achieved when tungsten is equal to 4.0 wt% (based upon f(CMI)). Limiting the maximum chromium content of the alloy to 14.7 wt% or less is therefore preferred as this allows 4.0 wt% tungsten and a stability number Md or 0.93 or less. It is preferable to limit the stability number to 0.92. To do this the numerical value for [(stability) should be less 17.8. It is therefore preferable to limit chromium content to 13.8 wt% as this will limit the stability number to 0.92 providing better microstructural stability.
In combination with a high level of mechanical strength -in terms of creep resistance -there is a requirement to limit the density of the alloy. A density target of 8.9g/cm3 is imposed, this is typical of the upper limit of density for commercially used nickel-based superalloys. From the elements within the alloy design space listed in Table 2 the elements tungsten and tantalum have a density which is significantly greater than nickel and have strongest influence on increasing density. Figure 12 shows the effect of elements tantalum and tungsten on alloy density. From Figure 12 it is determined that additions of tungsten and tantalum should adhere to the following equation f (density) = Ww + where f(density) is a numerical value which must be less than 13.9 in order to achieve an alloy with a density of less than 8.9 g/cm3. Given that the minimal required concentration of tungsten (2.0 wt%) it is necessary to limit the tantalum concentration to less than 11.9 wt%. Preferably density is limited to less than 8.8 g/cm3, to achieve this the numerical value for f(density) should be less than 11.8 therefore tantalum should be 9.8 wt% or less. Even more preferably tungsten should be greater than 4.7 wt% or greater, therefore tantalum should be limited to 9.2 wt% and 7.1 wt% to achieve a value off(density) of 13.9 and 11.8 respectively.
Additions of carbon, boron and zirconium arc required in order to provide strength to grain boundaries. This is particularly beneficial for the creep and fatigue properties of the alloy. The carbon concentrations should range from 0.02 wt% to 0.35 wt%. Preferably lower levels of carbon are preferred in order to reduce cracking during the additive manufacturing process, thus a content of less than 0.2 wt% or less than 0.15 wt% is preferred, more preferably less than 0.1 wt%. The boron concentration should range from 0.001 to 0.2 wt%, preferably less than 0.03 wt% as boron separates to the liquid phase during solidification and may lead to liquation cracking during the AM process, more preferably less than 0.02 wt%. The zirconium concentrations should range up to 0.5wt%, preferably from 0.001 wt% to 0.5 wt%, preferably less than 0.01 wt%, more preferably less than 0.006 wt%.
It is beneficial that when the alloy is produced, it is substantially free from incidental impurities. These impurities may include the elements sulphur (S), manganese (Mn) and copper 30 (Cu). The element sulphur should remain 0.003 wt% or less (30 PPM in terms of mass). The presence of sulphur above 0.003 wt%, can lead to embrittlement of the alloy and sulphur also segregates to alloy/oxide interfaces formed during oxidation, preferably sulphur levels are 0.001 wt% or less. Manganese is an incidental impurity which is limited to 0.25 wt%, preferably this limited to 0.1 wt% or less. Copper is an incidental impurity which is preferably limited to 0.5 wt%. Vanadium (V) is an incidental impurity, which negatively influences the oxidation behaviour of the alloy and is which is preferably limited to 0.5 wt%, preferably 0.3 wt% or less and most preferably this limited to 0.1 wt% or less. This segregation may lead to increased spallation of protective oxide scales. If the concentrations of these incidental impurities exceed the specified levels, issues surrounding product yield and deterioration of the material properties of the alloy is expected.
Iron behaves in a similar way to nickel and can be added as a low-cost alternative to nickel. Moreover, tolerance to iron additions improves the ability of the alloy to be manufactured from recycled materials. Therefore, it is preferred that iron is present in an amount of at least 0.1 wt%. However, additions of iron up to 4.0 wt% can be made in order to substantially reduce the cost. Preferably the additions of iron are 2.0 wt% or less in order to reduce the propensity to form the unwanted Laves phase which degrades the mechanical properties of the alloy. Most preferably iron additions are limited to 1.0 wt% as this produces an alloy which has good ability to be recycled with no loss in material performance.
Additions of hafnium (Hf) of up to 0.5 wt%, or more preferably up to 0.2 wt% are beneficial for tying up incidental impurities in the alloy and for providing strength. Hafnium is a strong carbide former it can provide additional grain boundary strengthening.
Additions of the so called 'reactive-elements', yttrium (Y), lanthanum (La) and cerium (Ce) may be beneficial up to levels of 0.1 wt% to improve the adhesion of protective oxide layers, such as A1203. These reactive -elements can 'mop up' tramp elements, for example sulphur, which segregates to the alloy oxide interface weakening the bond between oxide and substrate leading to oxide spallation. Magnesium (Mg) likewise may act to 'mop up' tramp elements, and can have beneficial effects on mechanical properties, so may be added up to 0.1%. Additions of silicon (Si) up to 0.5 wt% may be beneficial, it has been shown that additions of silicon to nickel based superalloys at levels up to 0.5 wt% are beneficial for oxidation properties. In particular silicon segregates to the alloy/oxide interface and improves cohesion of the oxide to the substrate. This reduces spallation of the oxide, hence, improving oxidation resistance.
Based upon the description of the invention presented in this section the broad range for the invention is listed in Table 4. A preferable range is also given in Table 4 as well as a most preferable range.
Table 4: Compositional range in wt% fbr the newly designed alloy Alloy (wt%) Al Co Cr Mo Nb Ta Ti W Min 4.0 0.0 6.0 0.0 0.0 0.0 0.0 2.0 Max 5.6 22.0 16.7 3.0 4.0 11.9 1.0 12.7 Preferable Min 4.0 0.0 8.0 0.0 0.0 3.7 0.0 4.7 Preferable Max 5.1 15.0 143 2.0 3.0 9.8 0.5 10.7 Most Preferable Min 4.5 0.0 10.0 0.0 0.0 5.8 0.0 5.2 Most Preferable Max 4.6 15.0 13.8 1.8 3.0 7.1 0.1 8.7 Examples of the Invention Table 5: Nominal compositions in wt% of the newly designed high volume fraction of y' nickel-based superalloys compared with the alloys listed in Table I. Alloy (wt%) Al Co Cr Mo Nb Ta Ti W C B Zr J(HCI) f(C41) 1N738 3.4 8.5 16.0 1.8 0.9 1.8 3.4 2.6 0.11 0.01 0.04 0.53 3.7 CM247 5.5 9.5 8.4 0.5 0.0 3.0 0.7 9.5 0.07 0.015 0.015 0.45 9.8 1N713 6.0 0.0 12.5 4.5 2.0 0,0 0,8 0.0 0.12 0.001 0.10 0.60 2.9 1N792 3.2 9.0 12,7 1.8 0.0 3.9 4.2 3.9 0.07 0.016 0,018 0.59 5,1 AM1005 4.2 19 9 1.2 3.6 5.8 0.1 7 0.04 0.005 - 1.95 7.8 AM1006 4.7 19 9 1.2 2.9 4.6 0.1 7 0.04 0.005 - 1.56 7.8 AM1007 5,2 19 9 1.2 2.2 3.3 0.1 7 0.04 0.005 1.16 7.8 AM1010 4 19 9 1.2 3 4.6 0.1 7 0.04 0.005 1.59 7.8 AM1011 4.5 19 9 1.2 2.3 3,4 0.1 7 0.04 0.005 1.2 7.8 AM1012 4,5 19 9 I 4.0 7.6 0.1 6.5 0.04 0.005 234 7,15 AM1013 5 19 9 1 3.4 5.8 0.1 6.5 0.04 0.005 1.92 7.15 AM1014 5.5 19 9 1 2.6 3.9 0.1 6.5 0.04 0.005 1.37 7.15 Table 6: Calculated phase fractions and merit indices made with the "Alloys-by-Design" software. Results fhr conventional high volume fraction of y' nickel-based superalloys used listed in Table I and newly designed high volume fraction of y' nickel-based superalloys compared with the alloys listed in Table I. Alloy 7' Creep Density Strength Md Strain Hot Freezing Range Cost Merit (g/el113) Merit (eV) Age Cracking (°C) $/kg Index Index Index Index (res x 10- (MPa) ) 1738 0.45 5.9 8.3 1517 0.92 5.6 1.82 259 5.5 CM247LC 0.59 8.0 8.6 1243 0.92 6.3 4.44 606 10.6 IN713 0.55 5.8 8.0 1139 0.93 7.0 2.03 213 2.5 1N792 0.51 6.4 8.5 1702 0.92 5.9 2.05 269 7.4 AM1005 0.51 7.4 8.9 1675 0.92 6.2 0.72 277 12.3 AM1006 0.51 7.4 8.7 1522 0.92 6.3 1.04 292 10.8 AM1007 0.50 7.4 8.6 1353 0.92 6.4 1.48 304 9.3 AM1010 0.42 7.4 8.9 1471 0.91 5.6 1.01 280 10.8 AM 1011 0.42 7.4 8.7 1317 0.91 5.8 1.43 291 9.4 AM1012 0.60 7.2 8.9 1889 0.93 6.9 0.44 273 14.1 AM1013 0.59 7.2 8.7 1694 0.93 7.0 0.77 292 12.1 AM1014 0.57 7.2 8.5 1467 0.92 6.9 1.29 307 9.9
S
The example alloys in tables 5 and 6 have been designed by varying the quantity f(H0). The T' content has been controlled by varying the quantityESAC). Creep merit index is controlled by the presence of Mo and W. The result is that all eight alloys have superior hot cracking indices than the prior art alloys, along with comparable or greater strength and creep predictions. The alloys AM1005-7 are designed to have the same strain-age cracking index as CM247LC. AM1005 is designed to have the lowest hot cracking risk but is also likely to have the poorest oxidation resistance due to its comparatively low Al content. By contrast, AM1007 is designed to have the best oxidation resistance but the least hot cracking resistance. AM1006 represents a middle ground between the two. The alloys AM1010 and AM1011 are homologous to AM1005-7 but at the lower end of the allowable range of f(S'AC), while AM1012-4 sit at the upper end of the allowable range off(SAC).
Table 7: Nominal compositions in wt% of the newly designed high volume fraction of y' nickel-based superalloys.
Alloy (wt%) Al Co Cr Mo Nb Ta Ti W C B Zr f(11171) ACMI) AM1015 4,7 19 9 1.2 0.2 10 0.1 7 0.04 0.005 1.56 7.8 AM1016 4,7 19 9 1.2 0.7 9 0.1 7 0.04 0.005 1.56 7.8 AM! 017 4.7 19 9 1.2 1.2 8 0.1 7 0.04 0.005 1.56 7.8 AM1018 4.7 19 9 1.2 1.7 7 0.1 7 0.04 0.005 1.56 7.8 AMI019 4.7 19 9 1.2 2.2 6 0.1 7 0.04 0.005 1.56 7.8 AM1020 4.7 19 9 1.2 2.7 5 0.1 7 0.04 0.005 1.56 7.8 AM1021 4.7 19 9 1.2 3.2 4 0.1 7 0.04 0.005 1.56 7.8 AM1022 4.7 19 9 1.2 3.7 3 0.1 7 0.04 0.005 - 1.56 7.8 Table 8: Calculated phase fractions and merit indices made with the "Alloys-by-Design" software of the alloys listed in table 7.
y Creep Merit Index (in-2s x 10- Density Strength Md Strain Hot Schell Cost Merit (eV) Age Cracking Freezing $./kg Index Index Index Range (°C) Alloy 15) (g/un') (MPa) AM1015 0.53 7.4 8.9 1654 0.93 6.3 0.90 334 15.2 AM1016 0.53 7.4 8.9 1630 0.93 6.3 0.83 316 14.4 AM1017 0.52 7.4 8.9 1606 0.93 6.3 0.84 304 13.6 AM1018 0.52 7.4 8.8 1582 0.92 6.3 0.89 300 12.8 AM1019 0.51 7.4 8.8 1557 0.92 6.3 0.96 298 11.9 AM1020 0.51 7.4 8.7 1531 0.92 6.3 1.02 294 11.1 AM1021 0.51 7.4 8.7 1505 0.92 6.3 1.06 288 10.3 AM1022 0.50 7.4 8.7 1479 0.92 6.3 1.10 281 9.53 Tables 7 and 8 show the properties of alloys AM1015 to AM1022, which are variants of alloy AM1006. In these alloys the proportions of Ta and Nb have been varied so as to keep the values of (JiCI) and f(SAC) constant. It is shown that the Ta-rich alloys have a higher strength and creep merit indices and more favourable hot cracking index. However, the Nb-rich alloys have lower density and cost, along with narrower Seheil freezing range.
Table 9: Nominal compositions in wt% of the newly designed high volume fraction of y' nickel-based superalloys.
Alloy (wt%) Al Co Cr Mu Nb 'La.fi W C B Zr f(110) f(C1117) AM1023 4.2 19 9 1.2 3.6 5.8 0.1 7 0.04 0.005 1,95 7.8 AM1024 4.2 17 9 1.2 3.6 5.8 0,1 7 0.04 0.005 1.95 7.8 AM1025 4.2 15 9 1.2 3.6 5.8 0.1 7 0_04 0.005 1.95 7.8 AM1026 4.2 13 9 1,2 3.6 5.8 0.1 7 0.04 0.005 1.95 7,8 AM1027 4,2 11 9 1,2 3,6 5.8 0.1 7 0,04 0.005 1.95 7.8 AM1028 4,2 9 9 1.2 3.6 5.8 0.1 7 0.04 0.005 1.95 7.8 AM1029 4.2 7 9 1.2 3.6 5.8 0.1 7 0.04 0.005 1.95 7.8 AM1030 4.2 5 9 1.2 3.6 5,8 0.1 7 0.04 0.005 1.95 7.8 AM1031 4.2 3 9 1.2 3.6 5.8 0,1 7 0.04 0.005 1,95 7.8 AM1032 4,2 1 9 1.2 3.6 5.8 0.1 7 0.04 0.005 1.95 7.8 Table 10: Calculated phase fractions and merit indices made with the "Alloys-by-Design" software of the alloys listed in table 9.
Alloy 7' Creep Density Strength Md Strain Hot Schell Cost Merit (g/cm3) Merit (eV) Age Cracking Freezing.5/kg Index Index Index Index Range (res x 10- (MPa) (°C) is) AM1023 0.51 7.4 8.9 1675 0.92 6.2 0.72 277 12.3 AM1024 0.51 7.4 8.9 1671 0.92 6.2 0.79 272 11.9 AM1025 0.51 7.4 8.9 1665 0.92 6.2 0.86 266 11.6 AM1026 0.51 7.4 8.9 1657 0.92 6.2 0.94 262 11.3 AM1027 0.51 7.4 8.9 1646 0.92 6.2 1.02 258 11.0 AM1028 0.51 7.4 8.9 1631 0.92 6.2 1.11 254 10.6 AM1029 0.50 7.4 8.9 1613 0.92 6.2 1.20 250 10.3 AM1030 0.50 7.4 8.9 1590 0.92 6.2 1.29 247 9.96 AM1031 0.50 7.4 8.9 1563 0.92 6.2 1.39 245 9.63 AM1032 0.49 7.4 8.9 1533 0.92 6.2 1.48 244 9.30 Tables 9 and 10 show the composition and properties of alloys AM1023 to AM1032. These alloys are variants of AM1005 with cobalt substituted out for nickel. The lower-cobalt alloys may be desirable for cost-limited applications and have narrower freezing ranges. On the other hand, lower-cobalt alloys display lower strength merit indices and higher hot cracking indices, hence making them less desirable for applications limited by strength and/or printability. Higher Co content also acts to marginally supress the formation of 7', which is also beneficial for printability Table 11: Nominal compositions in wt% ofthe newly designed high volume fraction of r' nickel-based superalloys.
Alloy (wt%) Al Co Cr Mo Nb Ta Ti W C B Fe f(I1C1) f(CMI) AM1033 4.7 18 9 1.2 2.9 4.6 0.1 7 0.04 0.005 1.0 1.56 7.8 AM1034 4.7 16 9 1.2 2.9 4.6 0.1 7 0.04 0.005 3.0 1.56 7,8 AM1036 4.7 19 9 1.2 2,9 4.6 0.1 7 0.04 0.005 1.0 1.56 7.8 AM1037 4,7 19 9 1.2 2.9 4.6 0,1 7 0.04 0.005 3,0 1.56 7.8 AM1039 4,7 10 9 1.2 2,9 4,6 0.1 7 0.04 0.005 1.0 1.56 7.8 AM1040 4.7 8 9 1.2 2.9 4.6 0.1 7 0.04 0.005 3.0 1_56 7.8 Table 12: Calculated phase fractions and merit indices made with the "Alloys-by-Design" software of the alloys listed in table 11.
Alloy y' Creep Merit Index (tn-2s x 10- Density Strength Mil Strain Hot Schell Cost 13) (g/cm3) Merit (eV) Age Cracking Freezing $/kg Index Index Index Range (MPa) (°C) AM1033 AM1034 AM1036 AM1037 AM1039 AMI040 9.51 0.50 0.51 0.50 0.52 0.51 7.4 7.4 7.4 7.4 7.4 7.4 8.7 8.7 8.7 8.7 8.7 8.7 1521 1518 1521 1518 1508 1505 0.92 0.92 0.92 0.93 0.92 0.92 6.3 6.3 6.3 6.3 6.3 6.3 1.02 0.99 0.99 0.94 1.31 1.26 295 299 299 315 269 272 10.7 10.3 10.8 10.8 9.33 9.01 Tables 11 and 12 describe alloys AM1033 to AM1041, which contain iron (1-3 wt%, substituted out for cobalt and nickel in various combinations). Iron is mostly benign with regards to mechanical properties, the key reason for its addition being is to reduce cost; this is particularly observed in cases where it is substituted for cobalt.
Table 13: Nominal compositions in wt% of the newly designed high volume fraction of y' nickel-based superalloys.
Alloy (wt%) Al Co Cr Ylo Nb Tn Ti W C B LI' f(IICI) f(011) AN11049 4.7 19 6 1.6 2.9 4.6 0.1 9.32 0.04 0.005 1.56 10.36 Alt/11050 4.7 19 8 1.33 2.9 4.6 0.1 7.77 0.04 0.005 1.56 8.64 AIV11051 4.7 19 10 1.07 2.9 4.6 0.1 6.23 0.04 0.005 1.56 6.92 AM1052 4.7 19 12 0.8 2.9 4.6 0.1 4.68 0.04 0.005 1.56 5.20 AN11053 4.7 19 14 0.54 2.9 4.6 0.1 3.13 0.04 0.005 1.56 3.45 Table 14: Calculated phase fractions and merit indices made with the "Alloys-by-Design" software of the alloys listed in table 13.
Creep Strength Md Strain Hot Schell Cost Merit Merit Age Cracking Freezing Index Density Index Index Index Range Alloy 1! (m-2s x 10- (g/cm3) (MPa) (eV) (°C) $/kg is) AM1049 0.53 8.0 8.9 1529 0.92 6.3 1.30 301 11.1 AM1050 0.51 7.6 8.8 1525 0.92 6.3 1.12 295 10.9 AM1051 0.50 7.0 8.7 1518 0.92 6.3 0.96 289 10.7 AM1052 0.49 6.4 8.6 1509 0.92 6.3 0.82 284 10.6 AM1053 0.48 5.8 8.5 1498 0.92 6.3 0.69 280 10.4 Tables 13 and 14 describe a series of alloys in which Mo and W are substituted for Cr in such a way as to maintain a constant stability merit index. Apart from their greater corrosion resistance, the high-Cr alloys are of low density and are favourable in terms of hot cracking index and freezing range; this may make them more amenable to the AM process. They would bc desirable in applications where high corrosion resistance is needed. Conversely, the low-Cr alloys have greater strength and creep merit indices, making them more useful in highly loaded applications.
Table 15: Nominal compositions in wt% of the newly designed high volume fraction of y' nickel-based superalloys.
Alloy (,1%) Al Co Cr Mo Nb Ta Ti W C II Ru Re f(CMI) AM 1055 4.7 19 9 1.2 2.9 4.6 0.1 6.4 0.04 0.005 1.0 7.13 AM 1056 4.7 19 9 1.2 2.9 4.6 0.1 5.7 0.04 0.005 2.0 6.49 AM 1057 4.7 19 9 1.2 2.9 4.6 0.1 5.9 0.04 0.005 - 1.0 6.69 AM1058 4.7 19 9 1.2 2.9 4.6 0.1 4.8 0.04 0.005 2.0 5.61 AM 1059 4.7 19 9 1.2 2.9 4.6 0.1 3.7 0.04 0.005 3.0 4.52 Table 16: Calculated phase fractions and merit indices made with the "Alloys-by-Design" software of the alloys listed in table 15.
7' Creep Merit Index (m-2s x 10- Density Strength Md Strain Hot Scheil Cost Merit (eV) Age Cracking Freezing $/kg Index Index Index Range (t) Alloy 15) (g/cm3) (MPa) AM1055 0.50 8.3 8.7 1517 0.92 6.3 1.41 368 74.3 AM1056 0.50 9.3 8.7 1512 0.91 6.3 1.50 406 138 AN11057 0,51 8.5 8.7 1520 0.92 6.3 1.01 290 25.2 AM1058 0.50 9.8 8.7 1518 0.92 6.3 0.99 289 39.5 AM1059 0.50 11.1 8.7 1516 0.91 6.3 0.96 288 53.8 Tables 15 and 16 describe alloys with additions of Ru and Re, substituted for W. These alloys all display particularly high creep merit indices, but with significant cost increases over the previously described alloys. This would make them suitable for applications in which strong creep resistance is required in non-cost-limited applications. Care should be taken before applying Ru-bearing alloys as they have high hot cracking indices, due to the impact of Ru on extending the freezing range.
Table 17: Nominal compositions in wt% of the newly designed high volume fraction of 2/ nickel-based superalloys.
Alloy (wt%) Al Co Cr Mo Nb Ta Ti W C B Zr filICI) f(ail) AM1060 4.7 19 9 1.2 2.9 3.6 0.4 7 0.04 0.005 1.41 7.8 AM1061 4.7 19 9 1.2 2.9 2.6 0.7 7 0.04 0.005 1.26 7.8 AM1062 4.7 19 9 1.2 2.9 1.6 1.0 7 0.04 0.005 1.11 7.8 AM1063 4.7 19 9 1.2 2.4 4.6 0.4 7 0.04 0.005 1.41 7.8 AM1064 4.7 19 9 1.2 1.9 4.6 0.7 7 0.04 0.005 1.26 7.8 AM1065 4.7 19 9 1.2 1.4 4.6 1.0 7 0.04 0.005 1.11 7.8 Table 18: Calculated phase fractions and merit indices made with the "Alloys-by-Design" software of the alloys listed in table 17.
y' Creep Merit Index (m-2s x 10- Density Strength Md Strain Hot Scheil Cost Merit (eV) Age Cracking Freezing $/kg Index Index Index Range (°C) Alloy IS (g/cm3) (MPa) ) AM1060 0.51 7.4 8.7 1489 0.92 6.3 1.16 288 9.84 AM1061 0.51 7.4 8.6 1457 0.92 6.3 1.30 283 8.86 AM1061 0.50 7.4 8.5 1425 0.92 6.3 1.45 276 7.88 AM1063 0.51 7.4 8.7 1513 0.92 6.3 1.12 295 10.6 AMI064 0.51 7.4 8.7 1505 0.92 6.3 122 298 10.5 AM1065 0.52 7.4 8.7 1495 0.92 6.3 1.34 302 10.3 Tables 17 and 18 describe a series of derivative alloys of AM1006 in which Nb and Ta have been substituted out for Ti up to the allowable limit. In AM1060-62, which have reduced Ta content, clear reductions in density and cost are observed. However, there are corresponding decreases in strength and printability. The same trends are observed in alloys AM1063-65, which have reduced Nb, but the differences are more marginal.
In comparison to the baseline alloy AIV11005 it is seen that increasing the hot cracking index IICI towards the limit of 1.5 (AM1006 and AM1007) will increase the susceptibility to cracking during AM processing. From Figure 14 it can be seen that an HCI of 1.5 or less results in little or no cracking during AM manufacture but that with an HCI of 1.5 or more (prior art alloys IN738, CM247C and IN713) substantial cracking occurs during AM manufacture. The samples in figure 14 were cubic samples measuring 10 rum x 10 mm x 10 mm which were fabricated using a selective laser melting powder-bed method to assess the ease of processing by additive manufacture of selected nickel-based superalloys. Samples were manufactured under the same conditions from argon gas atomised alloy powder (15-53 pm) processed under argon atmosphere (<0.1% 02). A fixed energy density of 2.2 J/nim2 and a layer thickness of 30 jim was selected to best represent how a machine would operate in a manufacturing situation. Metallographic samples were prepared by sectioning perpendicular to the build direction revealing thc X-Y plane after a final 1 pm diamond polish. Figure 14 shows typical micrographs from an optical microscope after applying histogram-derived thresholding.
Claims (1)
- Claims 1. A nickel-based alloy composition consisting, in weight percent, of: 4.0 to 5.6% aluminium, 0.0 to 1.0% titanium, 0.0 to 4.0% niobium, 0.0 to 11.9% tantalum, 2.0 to 12.7% tungsten, 0.0 to 3.0% molybdenum, 0.0 to 22.0% cobalt, 6.0 to 16.7% chromium, 0.02 to 0.35% carbon, 0.001 to 0.2% boron, 0.00 to 0.5% zirconium, 0.0 to 3.0% rhenium, 0.0 to 2.0% ruthenium, 0.0 to 3.0% iridium, 0.0 to 0.5% vanadium, 0.0 to 1.0% palladium, 0.0 to 1.0% platinum, 0.0 to 0.5% silicon, 0.0 to 0.1% yttrium, 0.0 to 0.1% lanthanum, 0.0 to 0.1% cerium, 0.0 to 0.003% sulphur, 0.0 to 0.25% manganese, 0.0 to 0.1 magnesium, 0.0 to 4.0% iron, 0.0 to 0.5% copper, 0.0 to 0.5% hafnium, the balance being nickel and incidental impurities, wherein the following equations are satisfied in which W10, and Wra are the weight percent of niobium and tantalum respectively 1.1 < 0.3WNb 0.15WTa 2. The nickel-based alloy composition according to claim 1, wherein the following equation is satisfied in which WNb and WTa are the weight percent of niobium and tantalum in the alloy respectively preferably 1.2 < 0.3WNb 0.15WT3 more preferably 1.4 5 0.313/4fb 0.15WTa 1.8 < 0.3WNb 0.15WTa 3. The nickel-based alloy composition according to claim 1 or 2, wherein the following equation is satisfied in which Wm, WT WNb and Wra are the weight percent of aluminium, titanium, niobium and tantalum in the alloy respectively 5.6 Wm 0.5W11 0.3WNb 0.15WTa < 7.0 preferably 5.6 5. Wm 0.5WT; 0.3WNb 0.15WTa < 6.5 4. The nickel-based alloy composition according to claim 1,2 or 3, wherein the alloy comprises a volume fraction of gamma prime phase of 63% or less at 900°C, preferably of 56% or less at 900°C.5. "I he nickel-based alloy composition according to claim I, 2, 3 or 4, wherein the alloy comprises a volume fraction of gamma prime phase of 42% or more at 900°C, preferably of 43% or more at 900°C, more preferably of 45% or more at 900°C, still more preferably of 50% or more at 900°C, still more preferably of 57% or more at 900°C, still more preferably of 57% or more at 900°C, most preferably of 60% or more at 900°C.6. The nickel-based alloy composition according to any of claims 1 to 5, wherein the following equation is satisfied in which Ww and Wmo are the weight percent of tungsten and molybdenum in the alloy respectively Wyt,-+ 0.65 W,40 > 4.0 preferably + 0.65 Wm, > 6.0 more preferably Ww + 0.65Wmo > 8.0 7. The nickel-based alloy composition of any of claims 1-6, consisting of, in weight percent, 8.0% or more chromium, preferably 10.0% or more.8. The nickel-based alloy composition of any of claims 1-7, consisting of, in weight percent, 14.7% or less chromium, preferably 13.8% or less.9. The nickel-based alloy composition of any of claims 1-8 consisting of, in weight percent, 9.8wt% or less tantalum, preferably of 9.2% or less tantalum, more preferably of 7.1% or less 30 tantalum.10. The nickel-based alloy composition of any of claims 1-9 consisting of, in weight percent, 2.0% or less molybdenum, preferably 1.8% or less molybdenum.11. The nickel-based alloy composition of any of claims 1-10 consisting of, in weight percent, 0.5% or less titanium, preferably 0.1% or less titanium.12. The nickel-based alloy composition of any of claims 1-11 consisting of, in weight percent, 0.2 or less hafnium.13. The nickel-based alloy composition of any of claims 1-12 consisting of, in weight percent, 10.7 or less tungsten, preferably 8.7or less tungsten.14. The nickel-based alloy composition of any of claims 1-13, consisting of, in weight percent, 3.0% or less niobium.15. The nickel-based alloy composition of any of claims 1-14, consisting of, in weight percent, 0.5% or less of one or both of platinum and palladium.16. The nickel-based alloy composition of any of claims 1-15, consisting, in weight percent, 4.5% or morc aluminium.17. The nickel-based alloy composition of any of claims 1-16, consisting, in weight percent, 5.3% or less aluminium, preferably of 5.1% or less aluminium, more preferably of 4.6% or less aluminium 18. The nickel-based alloy composition of any of claims 1-17, consisting of, in weight percent, 15.0% or less cobalt.19. The nickel-based alloy composition of any of claims 1-18 consisting of, in weight percent, or less vanadium, preferably of 0.1% or less vanadium.20. The nickel-based alloy composition according to any of claims 1 to 19, consisting of, in weight percent 1.1wt% or more tantalum, preferably of 3.7% or more tantalum, more preferably of 5.8% or more tantalum.21. The nickel-based alloy composition according to any of claims 1 to 20, consisting of, in weight percent 2.7M% or more tungsten, preferably of 2.8% or more tungsten, more preferably of 4,7% or more tungsten, even more preferably of 5.1% or more tungsten, most preferably of 5.2% or more tungsten.S22. The nickel-based alloy composition of any of claims 1-21, wherein the following equation is satisfied in which WNh, WTa, WTI, W21, WPd and WAd are the weight percent of niobium, tantalum, titanium, platinum, palladium and aluminium, respectively WAI ± 0.5 WTI + 0.3 WNb ± 0.15 WTa 0.125Wpt + 0.225Wp1 < 7.0 preferably WA1 ± 0.5 Wri + 0.3 WNb 0.15 Wra 0.125Wpt + 0.225Wpd < 6.5 23. The nickel-based alloy composition of any of claims 1-22, wherein the following equation is satisfied in which WTa and Ww are the weight percent of tantalum and tungsten in the alloy respectively Ww Mira < 13.9 preferably Ww + Wra < 11.8 24. The nickel-based alloy composition of any of claims 1-23, wherein the following equation is satisfied in which Wcr, Wht, and Ww are the weight percent of chromium, molybdenum and tungsten in the alloy respectively Ww Wcr 1.7Wmo < 18.7 preferably Ww + Wc, + 1.7Wmo < 17.8