GB2090810A - Labels transfers and the like - Google Patents

Description

1

GB 2 090 81 OA

1

SPECIFICATION Tranfers labels and the like

5 This invention realtes to reansfers, labels and the like which may be used, for example, for marking or labelling textile articles, for the production of identification tapes or badges and for patching or repairing garments or 10 other articles. Such products are referred to hereafter and in the appended claims as "marking elements".

Marking elements are known which comprise a substrate of woven cotton fabric or 15 similar flexible material, one face of which carries information to be displayed when the element is attached to a garment or other surface, and the other face of which is coated with a heat activated adhesive film. The ele-20 ment is applied to a garment or the like by placing it in position and applying heat which activates the adhesive and fuses the substrate to the garment. Removal of such marking elements may be effected using suitable sol-25 vents.

Marking elements are also known which comprise film-forming resin compositions and do not require a fabric or similar substrate. However, hitherto the chemical composition 30 of such elements has been such thay they cannot be subsequently removed and this is a substantial disadvantage of marking elements of this kind. Moreover it has been necessary to apply such marking elements face down to 35 the surface on which they are to be applied using a removable backing and hence it has not been possible to add identification markings to such elements by hand before the elements are applied to the surface, since 40 such markings would require to be in reverse or mirror-image. Thus such identification markings have to be applied after the marking element has been heat sealed to the garment and have to be subsequently heat sealed to 45 the marking element itself.

We have now found that it is possible to produce a marking element which does not utilise a fabric substrate, which will securely adhere to textile articles such as clothing and 50 withstand repeated laundering or cleaning operations, and which may be subsequently removed from the article when required. This is achieved by utilising a coherent film if a heat sensitive adhesive composition of a previously 55 used as a backing for fabric labels or transfers.

Thus according to the invention there is provided a marking element consisting of a printed or coated linear thermo-plastic resin 60 film.

The invention also provides a marking element comprising a film of a linear thermoplastic resin which is non-tacky at room temperature, the surface of the element which is 65 exposed in use being printed or coated with a compatible ink composition, whereby the element may be applied in face-up relation to a garment or other support and adhered thereto by application of heat and pressure, the label being subsequently removable by means of a solvent.

Preferably the resin film comprises a linear polyurethane resin. The thickness of the film may be of the order of 2-15 thousandths of an inch and preferably 5-7 thousandths of an inch.

An embodiment of the invention will now be described, by way of example only, with reference to the accompanying drawings in which:

Figure 7 is a diagrammatic cross-section through one form of apparatus for the production of marking elements according to the invention; and

Figure 2 is a cross-section through a marking element.

Referring to Fig. 1, a pre-formed film 5 of a suitable linear thermoplastic polyurethane which is non-tacky at room temperature is transported on a suitable carrier 6 supported on rollers 7 past a coating station 8 at which an overall surface coating 9 of printing ink is applied to the upper surface of the film by a roller 10. The film 5 may be temporarily attached to the carrier 6 by a pressure sensitive adhesive or other suitable means. The coated film then passes to a printing station at which a printed pattern such as an emblem or printed information indicated at 11 is applied to the coated surface by a printing roller 12 and after drying of the coating the film is cut to form individual transfers or marking elements as shown in Fig. 2. The support on which the film is carried during the coating and/or printing operations may also be cut to form a temporary protective sheet as shown in Fig. 2 which may be peeled from the marking element before use. Alternatively the film may be removed from the supporting surface prior to cutting to form individual marking elements.

In an alternative arrangement a pre-formed film of a linear thermoplastic polyurethane which is non-tacky at room temperature and incorporates a white or other pigment is transported on a suitable carrier, to which it may be temporarily attached by a pressure sensitive adhesive or other suitable means, past a printing station at which a printed pattern such as an emblem or printed information is applied directly to the surface of the film and after drying the film is cut to form individual transfers or marking elements.

Printing of the film may be effected using any inks which will withstand laundering or other operations to which the marking element will be subjected when attached to a garment of the like in use and are compatible with the marking element. Vinyl or urethane inks have been found to be particularly suit70

75

80

85

90

95

100

105

110

115

120

125

130

2

GB 2 090 81 OA 2

able for this purpose. However certain commercially available thermoplastic polyurethane films incorporate an "anti-blocking" composition serving to prevent curling or deformation 5 of the film during production and in use. This can inhibit the application of printing to the outer surface of the film and where such a composition is present it must first be removed using suitable solvents or a compatible 10 ink and printing process utilized. It has been found that fatty acid ester blocking agents do not substantially impair printing.

In use of the marking element it is applied to the surface of a garment or other article to 15 which is is to be adhered in a "face-up" orientation, that is with the printed surface upper-most and is then subjected to heat and pressure to activate the adhesive film which softens and bonds the marking element to the 20 surface of the article. The temperature and pressure applied may be varied within wide limits but typically temperatures of the order to 190-230T and preferably 200-220°C and pressures of the order of 20-45lbs/sq. in 25 typically around 35-37lbs/sq. in are employed. The time of application may vary dependent of the temperature, pressure and other factors but is generally in the region of 5-15 seconds and preferably 7-10 seconds. 30 Additional markings may be applied to the element before attachment to the garment if desired and fuse into the element on heating to form indelible markings which, together with the printed markings previously applied, 35 will withstand laundering and cleaning operations to which the garment may be subjected. It has also been found that additional markings may be applied by laundry marking pen shortly after bonding of the marking element 40 to the garment but before the thermoplastic film has re-hardened. Such markings become embedded in the film and after cooling and hardening of the marking element have been found to be indelible in the same manner as 45 markings applied prior to fixing of the marking element to the garment without requiring any further heating.

In cases where the surface of the polyurethane film is provided with an overall ink 50 coating prior to printing, it has been found that some printing inks used to form the coating crack and flake under certain circumstances. In order to improve the adherence of the coating to the surface of the film in such 55 circumstances the coated film may be heated, for example by infra-red or ultra-violet heaters, or by means of heated rollers to seal the surface coating to the film. This prevents cracking or flaking and provides a coherent 60 background surface on which designs or printed information may be subsequently applied.

In an alternative technique the surface of the film may be textured prior to application 65 of an overall coating, texturing being effected by mechanical means or by chemical etching. Alternatively a suitable solvent for etching the surface may be incorporated with the coating ink composition.

70 If it is subsequently desired to remove the marking element this may be effected by application of a suitable solvent, for example using the technique described in our co-pending British Patent application No. 8041585. 75 By virtue of the fact that the marking element comprises a thermoplastic film alone, no fabric support of the kind previously required in the production of such marking elements is necessary, thereby increasing the elasticity 80 and flexibility of the marking element compared with previously proposed elements incorporating fabric supports. Moreover while reference has been made herein to the use of a temporary carrier for the film, such a carrier 85 can be dispensed with in certain circumstances, particularly in the case of pigmented film. Where a carrier is utilized this may be cut to form individual elements as described above or may remain as a roll for cutting by 90 the user. Alternatively the film may be cut to form individual elements leaving the backing intact to act as a continuous carrier for the elements until they are removed for use.

Since the marking element relies on 95 thermo-plasticity to effect adherence to the surface to which it is to be applied in use rather than a chemical bonding action, it is possible to employ a pre-formed film on to which information can be directly printed face 100 up rather than in inverted or mirror-image fashion. Consequently it is also possible to add additional information to the outer surface of the element prior to application to a garment or the like by laundry or other suitable 105 marking pen, following which the element can be adhered by a single operation involving application of heat and pressure without deforming or otherwise interfering with the printed information. This compares favourably 110 with previous transfers comprising film forming resins which have hitherto been of a thermo-setting type relying on chemical bonding to secure the element to a garment or the like. This prevents the use of pre-formed sheet 115 or film and has required that the elements be applied face-down to the garment so that they must initially be printed in reverse or mirror image. Consequently additional markings cannot readily be applied by laundry marking pen 120 until after the element has been adhered to the garment and further heat-sealing is then required. Moreover due to the chemical nature of the bond between the element and the garment it has not hitherto been possible to 125 remove such labels or marking elements after application.

The invention may be used in connection with a wide variety of marking elements including badges, emblems, identification tapes 130 and labels of various kinds, but in addition,

3

GB2090810A 3

elements according to the invention may be used for repairing tears or other damage in garments or fabrics. For this purpose an element having an overall surface coating of an 5 ink medium coloured to correspond to the colour of the article to be repaired is applied over the torn or damaged area and heat sealed into position so as to bridge the tear and form a repair in the nature of a patch 10 which will be largely indistinguishable due to its relatively thin form and the fact that it may be coloured to correspond to the background colour of the article being repaired. Colouring of the patch may be effected by application of 15 an overall surface coating of a coloured ink composition selected to match the garment to be repaired or by incorporation of a pigment or dye of a suitable colour in the polyurethane film.

20 Various modifications may be made without departing from the invention. For example while the preferred thermoplastic film is polyurethane film, other thermoplastic film forming resins having similar properties may be 25 used.

Claims (1)

1. A marking element consisting of a printed or coated thermoplastic resin film. 30 2. A marking element comprising a preformed film of a linear thermoplastic resin which is non-tacky at room temperature, the surface of the element which is exposed in use being printed or coated with a compatible 35 ink composition, whereby the element may be applied in face-up relation to a garment or other support and adhered thereto by application of heat and pressure, the element being subsequently removable by means of a sol-40 vent.

3. A marking element according to claim 1 or 2 wherein the exposed surface of the element is receptive to markings applied thereto by marking pen either before or after heat

45 treatment, to produce indelible markings which will withstand laundering operations.

4. A marking element according to any preceding claim wherein the outer surface of said film is provided with an overall coating of

50 an ink composition prior to printing thereof.

5. A marking element according to any preceding claim wherein said thermoplastic resin film incorporates a non-silicone antiblocking agent.

55 6. A marking element according to claim 5 wherein said anti-blocking agent comprises a fatty acid ester.

7. A marking element according to any preceding claim wherein said thermoplastic

60 resin film comprises a linear polyurethane.

8. A marking element according to any preceding claim wherein said film has a thickness of 2-15 thousandths of an inch.

9. A marking element according to any 65 preceding claim wherein the undersurface of said film is temporarily supported on a carrier sheet.

10. A marking element according to claim 9 wherein said film is temporarily attached to

70 said carrier sheet by a pressure sensitive adhesive.

11. A marking element according to any preceding claim wherein said ink composition is selected from vinyl and urethane inks.

75 12. A marking element according to any preceding claim wherein said printing is applied by a hot foil technique.

13. A marking element according to any preceding claim wherein the element may be

80 removed by application of a solvent.

14. A marking element according to any preceding claim wherein the exposed surface of said film is textured prior to application of said printing or coating thereto.

85 15. A marking element according to claim

14 wherein said surface of the film is chemically etched.

16. A marking element according to claim

15 wherein said ink composition incorporates

90 a solvent for etching said surface of the film.

17. A marking element according to any preceding claim in the form of a badge or emblem.

18. A marking element according to any

95 of claims 1 to 16 in the form of an identification tape or label.

19. A marking element according to any of claims 1 to 16 in the form of a patch for repairing damage to garments or fabrics.

100 20. A marking element according to claim 19 which is coloured to correspond to a garment or fabric to be repaired.

21. A marking element substantially as hereinbefore described.

105 22. A method of attaching a marking element according to any preceding claim to a garment, comprising locating the marking in the desired position on the garment and simultaneously applying heat and pressure

110 there to to soften said thermoplastic film and fuse the element to the garment.

23. A method according to claim 22 wherein a marking is applied to the element by marking pen prior to adherence of the

115 element to the garment.

24. A method according to claim 22 or 23 wherein a marking is applied to the element after application of the element to the garment.

120 25. A method according to claim 24

wherein said marking is applied before resoli-dification of said film.

26. A method according to any of claims 22 to 25 wherein said element is heated to a

125 temperature of 190°C to 230°C for between 5 and 15 seconds.

27. A method according to any of claims 22 to 26 wherein said element is subjected to a pressure of 20-45lbs/sq.in.

130 28. A method of applying a marking ele-

4

GB 2 090 81 OA 4

ment to a garment or fabric substantially as hereinbefore described.

29. A method of producing a marking element comprising providing a pre-formed

5 film of a linear thermoplastic polyurethane resin and directly printing or coating the exposed surface of the film with a compatible ink medium using a suitable printing process.

30. A method according to claim 29

10 wherein the anti-blocking agent comprises a fatty acid ester.

31. A method according to claim 29 or * 30 wherein said printing process comprises a * hot-foil process.

15 32. A method of producing a marking *

element substantially as hereinbefore de- *

scribed.

33. Any novel subject matter or combination including novel subject matter herein dis-

20 closed, whether or not within the scope of or relating to the same invention as any of the preceding claims.

Printed for Her Majesty's Stationery Office by Burgess & Son (Abingdon) Ltd.—1982.

Published at The Patent Office, 25 Southampton Buildings,

London, WC2A 1AY, from which copies may be obtained.