FR3017128A1 - EASY CLEANING GLAZING COMPRISING AN EXTERNAL LAYER BASED ON TIN OXIDE AND ZINC - Google Patents

Abstract

The invention relates to a glazing unit comprising a glass substrate coated on at least a portion of its surface with an oxide layer, said layer being single or the last layer of a stack of layers of dielectric materials, wherein said layer is an oxide of tin and zinc.

Description

The invention relates to a glazing unit incorporating a glass substrate comprising on at least a portion of its surface a moisture-resistant and easy-to-use coating. clean. Without being limited thereto, the invention applies in particular to the field of interior furnishings, more particularly when the substrate is intended to be arranged in a moist environment, such as a bathroom, the substrate forming for example the wall of a shower enclosure or a bath screen, or a mirror. It is known that a moist environment induces corrosion of the glass substrates until the visible appearance of white traces, and that in parallel these substrates get dirty quickly due to deposits of dirt, including limestone or soap. In order not to hinder the visualization and for reasons of aesthetics and ease of cleaning, these glass substrates are, in a known manner, coated for the most part with hydrophobic layers of the silicone or fluorinated molecule type. We can notably mention the glass marketed under the name Aquacontrol® of the company SAINT-GOBAIN. In known manner, a hydrophobic coating allows the water deposited thereon to pearl in the form of drops. When the drops are large enough, they flow naturally by gravity on the vertical surface and do not leave traces of limestone when drying. In the field of so-called hydrophobic glazings or coatings, it is generally possible to evaluate the interactions between the glazing unit and the water: the contact angle θ, which makes it possible to evaluate the more or less hydrophobic nature of a placed surface in horizontal position and the sliding volume which more directly evaluates the propensity of a drop to slide along the wall of the glazing in inclined or vertical position, taking into account in particular the surface state of the latter (in particular roughness and chemical homogeneity of said surface). By contact angle is meant the angle formed by the surface of the substrate and the tangent to the drop at the meeting point between the air, the drop and the substrate. Organic coatings made of silicone or comprising fluorinated molecules exhibit the best hydrophobicity performance in the sense previously described. However, the hardness of such hydrophobic layers is by nature very low (organic compounds), while the adhesion between these layers and the glass substrate is often quite bad (particularly for silicones). As a result, they begin to degrade rapidly (a few weeks to a few months), leaving portions of the surface hydrophilic while others remain hydrophobic. This chemical inhomogeneity tends to disadvantage the overall flow of drops of water along the glass wall. In addition, in the presence of water, the surface of the glass which is no longer protected deteriorates (corrodes) progressively due to the loss of the cations, especially of the alkaline type, initially present in the glass material. Under the effect of this corrosion, the glass surface sees its roughness increase, which also affects the evacuation of water drops. Moreover, if outside the evacuation of drops of water on a hydrophobic glazing is favored by the presence of a flow of air such as wind (especially on automotive windows), indoors it is not the case. Therefore, small drops of water whose weight is not large enough will not flow, forming what is called "steam", and will leave traces of limestone drying.

Also, although a hydrophobic coating used in the bathroom is significant to easily remove dirt, it is highly recommended to wipe the glass with a squeegee to make it clean and dry after spraying. water and formation of drops detaching with difficulty alone. If the residual limestone can then be cleaned by products commercially sold as anti-lime scale, they nevertheless attack the hydrophobic coating which thus deteriorates even more rapidly over time. Thus, when the use of cleaning products leads to the aggression of the hydrophobic coating, or even removes it, the glass which has no barrier layer corrodes very quickly over time, causing an increase in the roughness of its surface. . The glass surface is subsequently more and more difficult to clean because of the incrustation of limestone in the roughened surface. Finally, the hydrophobic coatings are not toughenable, which forces them to be deposited after the step of tempering the glazing, which aims to make the latter 20 impact-resistant, and therefore after the cutting of the glass panels to the final dimensions. This obviously causes an additional cost, and most often implies that the deposit is made in glass transformers while they are not necessarily equipped for it. In summary, the conventional hydrophobic coatings described above have limited effectiveness on deposition of dirt on the glass surface, have a relatively limited life span, ranging from a few months to a few years, and ultimately imply protection against corrosion. limited in time. It is furthermore necessary to deposit them separately on a previously dipped glass substrate.

In the end, such a hydrophobic coating is impractical for tempered glass substrates, such as those used in bathrooms, for which the drops of water are not always wiped after each projection, and which are intended to be frequently cleaned with aggressive products.

Other glazing solutions for bathrooms are currently available. In particular, DLC carbon-like layers (Diamond Like Carbon) have been advanced in the applications W02013184607A2 or W02013003186A1 from Guardian Industries. Such a glazing to be dipped with a DLC layer has recently been marketed in Europe under the trade name Showerguard®. It is indicated that this layer makes it easier to clean the glass and to make it resistant to limescale. The hydrophobic layer DLC has an initial contact angle θ of 70 ° and is indicated as being heatable in the sense previously indicated, that is to say that it is no longer necessary to deposit this layer after the quenching step of its glass support. The first disadvantage of this DLC layer is related to quenching, which is made possible only by the addition of three layers over the DLC layer for its protection: a dense layer sensitive to acid attack, a dense barrier layer with oxygen and a scratch resistant polymer layer. The plastic layer is removed manually just before the quenching step, and requires specific cutting tools. The two dense layers are removed after quenching with a vinegar cleaning, which also requires specific tools. Obtaining the final monolayer product via an initial four-layer product thus ultimately proves to be a complex and expensive process. Another disadvantage of the layer is its yellow color, due to the absorption by the DLC layer of a portion of the visible radiation.

The invention therefore aims to provide a glazing which, during its transformation, its life and its use, does not have the aforementioned drawbacks, in particular the appearance of corrosion, the coloring of the glazing, the accumulation limestone on its surface and the use of specific tools for processing, and which is easily cleaned. The invention also proposes to provide a glazing whose manufacture is simple and inexpensive, incorporating a coating that can undergo the step of quenching its glass support without damage or significant degradation of its properties. More specifically, the invention relates to a glazing unit comprising a glass substrate coated on at least a portion of its surface with an oxide layer, said layer being single or the last layer of a stack of layers of dielectric materials, characterized in that said layer is a zinc oxide and tin. For the purposes of the present invention, zinc oxide and tin oxide means that the oxide essentially comprises cations of zinc and tin atoms, without excluding other cations, in particular other metal atoms. such that Al, Ga, In, B, Y, La, Ge, Si, P, As, Sb, Bi, Ce, Ti, Zr, Nb and Ta can be present in a very minor amount compared to the sum of zinc and tin atoms, for example in an amount less than 10% of said sum, or even less than 5% of said sum. The insertion of such cations may in particular be intended to promote the deposition of the oxide layers on the substrate by magnetron techniques, as indicated in the application WO 00/24686.

According to one characteristic, the tin oxide and zinc oxide layer is deposited by magnetic field assisted sputtering (magnetron) and therefore has a high density, in particular greater than 90% of the theoretical density of the bulk material.

According to another characteristic, zinc oxide and tin has a Sn / Zn molar ratio of between 30/70 and 70/30. Preferably, said Sn / Zn molar ratio is between 35/65 and 60/40 and very preferably said Sn / Zn molar ratio is between 40/60 and 50/50. According to the invention, the tin oxide and zinc oxide layer has a thickness of between 5 and 100 nm. Preferably, the layer has a thickness of between 10 and 50 nm. Very preferably, the layer has a thickness of less than 30 nm, or even less than 25 nm or even less than 20 nm.

Preferably, said layer of tin oxide and zinc is unique and deposited directly on the glass substrate. Thus, the layer according to the invention has several roles, it is easy to clean ("easy-to-clean" function according to the terms used in the field) and anti-corrosion (function of preventing corrosion of the substrate), without need to associate any other layer with it. The layer is also hydrophobic. In addition, the invention also relates to a glazing as previously described and having undergone a quenching to make it mechanically resistant. The invention also relates to the use of glazing as described above arranged in a humid environment in which drops of water are intended to form on the glazing. The glazing according to the invention can be in particular a bathroom glazing, in particular a glazing of a shower cabin or a bath screen, or a mirror. The invention also relates to a method for obtaining a glazing unit as previously described. Said method makes it possible to obtain a tempered and / or curved glazing unit, comprising a glass substrate coated on at least a part of its surface with an oxide layer comprising tin and zinc, said layer being single or the last layer of a stack of layers of dielectric materials. Said method comprises the steps of depositing the layer stack or said layer on said substrate by a vacuum deposition technique such as magnetic field assisted sputtering and performing the quenching and / or bending heat treatment. the substrate thus coated with the oxide layer comprising tin and zinc or the stack comprising the same.

The inventors have unexpectedly demonstrated the hydrophobic character of the zinc oxide and tin oxide layer (also referred to as SnxZnyO in the remainder of the description) during its use while the latter is initially hydrophilic. Although this can not be considered as a well-established fact, the inventors believe that the impurities deposited on the initially hydrophilic SnxZny0 layer give it, after a short time of use, a property that is hydrophobic on the contrary, with contact angles of order of 60-70 °. Such a property makes it possible, unexpectedly, to envisage the use of such a layer, very advantageously, as a covering (or last layer of a coating) of a shower enclosure or more generally for any other use in which a glass , subject to splashing water, must quickly evacuate it. The invention is now described with the aid of the following examples, which are only illustrative and in no way limit the scope of the invention. The glazings described in these examples incorporate a glass substrate comprising a single layer of coating, called the "easy-to-clean" layer, at least on a surface part, part intended to be exposed to a humid environment, such as in a room de-bain, and more particularly intended to receive splashes of water.

No other layer is deposited above or below the "easy-to-clean" layer. The substrate is made of soda-lime glass, of a thickness for example of 2 mm, and marketed under the reference PLANILUX® by the applicant company. Conventionally, the oxide layer comprising tin and zinc is deposited on the glass substrate in a magnetic field assisted magnetron sputtering chamber (magnetron). More specifically, two targets, one SnOx and the other ZnO constitute cathodes and are co-sprayed by an argon gas plasma and oxygen in the chamber according to conventional techniques well known in the field of thin film deposition. The different molar ratios of Sn and Zn elements in the final oxide layer as reported in Table 1 which follows are obtained by adjusting the respective powers applied to each of the two targets of zinc and tin. For each of the embodiments, a layer 80 nm thick of zinc oxide and tin SnxZny0 is deposited. The glass substrate thus coated is then quenched.

In a first step, glazings according to the invention are made and their performances are measured, for the different respective contents of zinc and tin. The coloring of the different glazings thus obtained is firstly measured according to the international representation and standard CIE L * a * b *. Specifically, the b * value is measured, a large positive value indicating a marked undesirable yellow color. The measurements are made with a UV-visible spectrometer in transmission and in reflection on the layer side. The different measured values are reported in Table 1 which follows. The windows are then immersed for 8 hours in vinegar (maintenance product commonly used for the shower enclosure) to measure their resistance to corrosion. The difference in thickness of the layer between its initial value and its final value is indicated in Table 1 which follows.

Ratio molar Measured value Measured value Sn / Zn thickness variation in the b * T (in de b * R (in (nm) after test transmission layer) reflection) vinegar. 18/82 -2 7 15 28/72 -2 6 7 40/60 -2 7 3 46/54 -2 7 2 55/45 -3 10 2 67/33 -3 15 2 75/25 -4 20 1 Table The results reported in Table 1 above show that high levels of zinc in the oxide lead to low corrosion resistance.

Conversely, high levels of tin result in good chemical resistance of the layer but also in a marked yellow color of the glazing provided with its layer, in reflection. The results reported in the preceding table show that the best compromise is thus reached for molar ratio values of between 30/70 and 70/30, in particular between 35/65 and 60/40, and in particular between 40/60 and 70/30. / 60 and 50/50. In a second series of examples, it also verifies the hardenability of the layer and in particular its properties after the heat treatment of the glass substrate, particularly with respect to the other layers used today and described above for the shower cabinet glazings. Specifically, a 10 nm thick layer of mixed zinc and tin oxide is deposited by magnetron sputtering techniques onto a 8mm thick Diamant® glass substrate from an alloy target. Metal SnZn whose atomic ratio is 45/55 (or a mass ratio 60/40), in an argon and oxygen plasma, introduced into the chamber in a volume ratio of the order of 1.8 .

The glazing provided with the layer according to the invention is heated at 700 ° C. for 3 minutes followed by quenching.

This glazing thus obtained according to the invention is compared with a first reference glazing, having a conventional hydrophobic coating based on fluorinated silanes, in this case a glass marketed under the trademark Aquacontrol® by the applicant company, obtained thanks to functionalization. by scouring a previously dipped glass substrate.

The glazing obtained according to the invention is also compared to a second reference glazing, comprising a hydrophobic coating based on DLC, in this case a toughened glass sold under the trade name Showerguard® by Guardian Industries.

Finally, the performances of the three previous glazings are compared with those of the bare glass substrate. The tests carried out on the various glazings to compare the performances reported in Table 2 are described below: The value of the light absorption is obtained with a UV-Visible spectrometer by measuring the transmission and the reflection of the sample side layer. The water contact angle θ is measured with a drop of 2 μL deposited with a syringe on the horizontal surface of the substrate and with the aid of a suitable camera. The sliding limit volume is defined as the limit value below which the drops no longer flow on the surface of a vertically held substrate, their weight no longer sufficient to drag them down. If the contact angle θ provides information on the hydrophobic nature of the layer, the sliding limit volume is more representative of the desired performance of the glazing during its use, especially as a shower wall.

These two values are obtained after exposure of the samples in the open air for 2 days, in order to simulate the actual conditions of use where the glazings are not cleaned before use. The High Humidity (HH) test consists in placing the samples in a chamber heated to 50 ° C and in which there is a constant relative humidity of 95% for 75 days, then measuring the blur appeared, the blur being defined as the ratio between the diffuse transmission and the total transmission. This blur is the result of the roughening of the substrate under the action of corrosion. This accelerated aging test appears very representative of the actual conditions of use, over a long period of time, of the glazing in a hot and humid atmosphere such as a bathroom. The measurement of the coefficient of friction aims to assess the ease with which a squeegee can be used on the surface of the glazing to clean its surface. The coefficient of friction reported in Table 2 is measured by means of a device comprising a squeegee 25 cm in length, disposed on the surface of the glazing on the side covered by the coating. On the squeegee is arranged a load of one kilogram. The force required for the squeegee to be moved at a speed of 4 m / m in can be measured with a dynamometer in Newtons.

The results obtained for the various tests and the various glazings studied are summarized in Table 2 which follows: Layer None Aquacontrol® Showerguard® Sn ,, Zny0 (bare glass) (invention) Absorption 5.1 5.1 6.6 5, 1 0 30 ° 105 ° 70 ° 60 ° Sliding Drag 15 IAL 27 IAL 19 IAL Coefficient of friction 0.55 N 0.50 N 0.75 N 0.60 N Blur after 10% 0 2.4% 1% HH test Table 2 The measurements made by the applicant company show that the glazing according to the invention differs from bare glass in having a high resistance to corrosion, by an ability to make the drops of water flow, as indicated by its very low sliding volume, close to that of the reference organic hydrophobic layer. Such a property makes it possible to limit the amount of water to be wiped on the glazing, but also to effectively limit the quantity of drops of water remaining after each spraying on the surface of the wall and thus the appearance of traces of limestone. The measurements made by the applicant company on the reference product comprising a DLC layer show that this layer confers on the coated glazing a coloration due to a visible absorption. In addition, the DLC layer according to the prior art has a hydrolytic resistance (as measured by the HH test) lower than that of the coating according to the present invention. Also, the DLC layer according to the prior art has a lower ability to flow water drops and greater difficulty in removing these drops with a squeegee, as evidenced by the greater slip volume and the coefficient of higher friction.

The layer according to the invention has properties quite similar to those of the hydrophobic comparative layer. It can also advantageously be deposited on a glass substrate to be quenched or quenched.

The present invention thus finally makes it possible to obtain glazing whose properties in use are close to those of glazings comprising organic hydrophobic layers, with the additional advantages that the glass substrate can be quenched after deposition of said zinc oxide layer. and tin by conventional vacuum techniques, and that the properties, including corrosion resistance, will last several years.

Claims (12)

REVENDICATIONS1. Glazing comprising a glass substrate coated on at least a portion of its surface with an oxide layer, said layer being single or the last layer of a stack of layers of dielectric materials, characterized in that said layer is an oxide of tin and zinc. 2. Glazing according to claim 1, wherein the zinc oxide and tin has a Sn / Zn molar ratio between 70/30 and 30/70. 3. Glazing according to claim 1, wherein the zinc oxide and tin has a Sn / Zn molar ratio of between 60/40 and 35/65. 4. Glazing according to claim 1, wherein the zinc oxide and tin has a Sn / Zn molar ratio of between 50/50 and 40/60. 5. Glazing according to one of the preceding claims wherein said layer is unique. 6. Glazing according to one of the preceding claims wherein the zinc oxide layer and tin has a thickness between 5 and 100 nm. 7. Glazing according to one of the preceding claims wherein the zinc oxide layer and tin has a thickness of 10 and 50 nm. 8. Glazing according to one of the preceding claims wherein said layer of tin oxide and zinc is unique and deposited directly on the glass substrate. 9. Glazing according to one of the preceding claims wherein the substrate is soaked and / or curved. 10. Glazing according to one of the preceding claims, wherein the layer is deposited by magnetic field assisted sputtering (magnetron) and preferably has a density greater than 90% of the density of the bulk material. 11. Bathroom glazing, in particular for shower enclosure or bath screen or mirror according to one of the preceding claims. 12. A method of manufacturing a tempered and / or curved glazing comprising a glass substrate coated on at least a portion of its surface with an oxide layer comprising tin and zinc, said layer being unique or the last layer of a stack of layers of dielectric materials, said method comprising the steps of depositing the layer stack or said layer on said substrate by a vacuum deposition technique such as magnetic field assisted sputtering and to be carried out the quenching and / or bending heat treatment on the substrate thus coated with the oxide layer comprising tin and zinc or the stack comprising the latter.