DE8703556U1 - Composite film for the production of cuboid-shaped evacuated packages - Google Patents

Composite film for the production of cuboid-shaped evacuated packages

Info

Publication number
DE8703556U1
DE8703556U1 DE8703556U DE8703556U DE8703556U1 DE 8703556 U1 DE8703556 U1 DE 8703556U1 DE 8703556 U DE8703556 U DE 8703556U DE 8703556 U DE8703556 U DE 8703556U DE 8703556 U1 DE8703556 U1 DE 8703556U1
Authority
DE
Germany
Prior art keywords
composite film
layer
film according
vinyl alcohol
polyolefin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE8703556U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hoechst AG
Original Assignee
Hoechst AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hoechst AG filed Critical Hoechst AG
Priority to DE8703556U priority Critical patent/DE8703556U1/en
Publication of DE8703556U1 publication Critical patent/DE8703556U1/en
Priority to EP88103029A priority patent/EP0281893B1/en
Priority to DE8888103029T priority patent/DE3862218D1/en
Priority to AT88103029T priority patent/ATE62180T1/en
Expired legal-status Critical Current

Description

WffiäsWffies

• » S * S « ce« ci• » S * S « ce« ci

HOECHST. :AK£1ENGESELLSCHAFT: - Werk KALLEHOECHST. :AK£1ENGESELLSCHAFT: - KALLE plant

87/K 007G WLJ-DC.Ho-rp87/K 007G WLJ-DC.Ho-rp

09. März 198709 March 1987

Verbundfolie zur Herstellung von quaderförmigen evakuierten PackungenComposite film for the production of cuboid-shaped evacuated packages

Die vorliegende Neuerung beschreibt eine Verbundfolie zur Herstellung von im wesentlichen quaderförmigen, evakuierten Schlauchbeutelpackungen aus thermoplastischen Kunststoffen mit einer besonders geringen Sauerstoffdurchläßsigkeit. The present innovation describes a composite film for the production of essentially cuboid-shaped, evacuated tubular bag packages made of thermoplastics with a particularly low oxygen permeability.

Quaderförmige Beutelpackungen mit einer möglichst niedrigen Sauerstoffdurchlässigkeit werden insbesondere benötigt zum Verpacken von empfindlichen, gegen Aromaverlust anfälligen und bei Sauerstoffaufnähme verderblichen Lebensmitteln, insbesondere für gemahlenen Kaffee. Um für diesen speziellen Sinsatzzweck das Verpackungsgut auch über längere Zeitspannen in wirklich einwandfreiem Zustand zu bewahren, werden als Verpackungsmaterial meist |Cuboid-shaped bag packages with the lowest possible oxygen permeability are particularly required for packaging sensitive foods that are susceptible to loss of flavor and perishable when exposed to oxygen, especially ground coffee. In order to keep the packaged goods in perfect condition for this special purpose over longer periods of time, the packaging material used is usually |

Verbünde umfassend Aluminiumfolien eingesetzt. Diese Verbundfolien werden hergestellt unter Verwendung von biaxial gestreckter Polyethylenterephthalatfolie bzw. Polyamidfolie als Trägerfolie. Diese Aluminiumverbundfolien haben jedoch den Nachteil, daß sie teuer und nur durch technisch aufwendige Verfahren herstellbar sind.Composites comprising aluminum foils are used. These composite films are manufactured using biaxially stretched polyethylene terephthalate film or polyamide film as a carrier film. However, these aluminum composite films have the disadvantage that they are expensive and can only be manufactured using technically complex processes.

Durch die Weiterentwicklung neuer Techniken konnten in der Folgezeit Folien aus Kunststoff zum Einsatz gebracht werden, die durch Vakuumaufdampfung entstandene Aluminiumschichten trugen und damit preiswert und einfach herstellbar waren. Die metallisierten Verbundfolien selbst wiesen zwar akzeptable SauerstoffSperreigenschaften auf,The further development of new technologies subsequently made it possible to use plastic films that had aluminum layers created by vacuum deposition, making them inexpensive and easy to manufacture. The metallized composite films themselves had acceptable oxygen barrier properties,

••♦•J ti t
• ··* · ··· · · ••♦•J ti t
··* · ··· · ·

HOECHST:AKT'lEtiSE'S*BL'LSdHA*Fl - Werk KALLEHOECHST : AKT'lEtiSE'S*BL'LSdHA*Fl - Werk KALLE

jedoch stellte sich nachteiligerweise heraus, daß bei der , Verarbeitung der mit den hauchdünnen Schichten aus MetallHowever, it turned out that during the processing of the wafer-thin layers of metal

überzogenen Folien zu Verpackungseinheiten und beim an-, schließenden Evakuieren derselben, insbesondere im Be-coated films to form packaging units and during the subsequent evacuation of the same, especially in the

reich der Kanten und Ecken der Packung. Verdehnungen in einem solchen Ausmaß auftraten, daß die Sauerstoffdurchlässigkeit bedingt durch Beschädigungen der Metallisierung in der Größenordnung einer Zehnerpotenz anstieg und daß daher diese Packungen für den bestimmungsgemäßen Gin- ^O satzzweck nicht mehr als geeignet anzusehen sind.area of the edges and corners of the pack. Expansions occurred to such an extent that the oxygen permeability increased by a factor of ten due to damage to the metallization and that these packs can therefore no longer be considered suitable for their intended use.

Es stellte sich somit die Aufgabe, eine Folie zu schaffen, die geeignet ist, zu quaderförmigen evakuierten Schlauchbeutelpackungen verarbeitet zu werden, und die gleichzeitig die Vorteile der, verglichen mit Aluminiumfolien, technisch unkomplizierten und damit preisgünstigeren Herstellbarkeit besitzt und die zusätzlich aber bei der Verarbeitung und dem Verpackungsvorgang ihre hervorragenden SauerstoffSperreigenschaften beibehält.The task was therefore to create a film that is suitable for processing into cuboid-shaped evacuated tubular bag packages and that at the same time has the advantages of being technically uncomplicated and therefore cheaper to manufacture compared to aluminum foil and that also retains its excellent oxygen barrier properties during processing and packaging.

2020

Gelöst wird diese Aufgabe überraschenderweise durch eine Folie der eingangs genannten Gattung, deren Kennzeichenmerkmale darin zu sehen sind, daß sie wenigstens eine biaxial streckorientierte Schicht aus einem Polymeren enthaltend VinylalkohqVleinheiten und wenigstens eine Schicht aus Polyolefin enthält.This object is surprisingly achieved by a film of the type mentioned at the outset, the characteristic features of which are that it contains at least one biaxially stretch-oriented layer of a polymer containing vinyl alcohol units and at least one layer of polyolefin.

Unter einem Polymeren enthaltend Vinylalkoholeinheiten soll im wesentlichen Polyvinylalkohol oder ein Copolymerisat aus Vinylalkohol und Alfa-Olefineinheiten mit 2 bis 5 C-Atomen, insbesondere aus Ethyleneinheiten, zuA polymer containing vinyl alcohol units is essentially polyvinyl alcohol or a copolymer of vinyl alcohol and alpha-olefin units with 2 to 5 carbon atoms, in particular ethylene units.

HOECHST* AKTrKMGESELL'SCHÄFT - Werk KALLEHOECHST* AKTrKMGESELL'SCHÄFT - KALLE plant

verstehen sein. Insbesondere sollen die copolymerisierten AIfa-Olefineinheiten in einem mengenmäßigen Anteil von
nicht mehr als 40 MoI-S, bevorzugt nicht mehr als
20 Mol-%, vorliegen, bezogen auf die Gesamtmenge an Copolymerisat. In particular, the copolymerized Alfa-olefin units should be present in a proportion of
not more than 40 MoI-S, preferably not more than
20 mol-%, based on the total amount of copolymer.

Das Copolymerisat entsteht durch Copolymerisation von
Olefineinheiten mit Vinylacetat und nachfolgender, praktisch vollständiger Verseifung des copolymerisierten
Vinylacetats derart, daß wenigstens 95 Gew.-% der Acetylgruppen des Copolymerisats durch Verseifung in OH-Gruppen umgewandelt sind.The copolymer is produced by copolymerization of
Olefin units with vinyl acetate and subsequent, practically complete saponification of the copolymerized
Vinyl acetate such that at least 95% by weight of the acetyl groups of the copolymer are converted into OH groups by saponification.

Auch der Polyvinylalkohol entsteht durch PolymerisationPolyvinyl alcohol is also produced by polymerization

von Vinylacetat und nachfolgender Verseifung zu wenigstens 95 %. Die Schicht aus Polyvinylalkohol oder Copolymerisat aus Vinylalkohol und Alfa-Olefin ist neuerungsgemäß biaxial streckorientiert, insbesondere biaxial
streckorientiert und hitzefixiert.of vinyl acetate and subsequent saponification to at least 95 %. The layer of polyvinyl alcohol or copolymer of vinyl alcohol and alpha-olefin is biaxially stretch-oriented, in particular biaxially
stretch oriented and heat set.

Die Schicht aus Polyolefin enthält bevorzugt ein siegelbares Polyolefin, bevorzugt soll das Polyolefin heißsiegelbar sein. Geeignete Polyolefine sind z. B. Polyethylen hoher Dichte und Polyethylen niedriger Dichte, Copolymere aus Ethylen und Propylen, Terpolymere aus Ethylen, Propylen und Butylen oder Mischungen aus diesen. Dabei liegt
der Ethylengehalt der Co- bzw. Terpolymeren insbesondere
im Bereich von 0,1 bis 15 Gew.-%, bezogen auf das Gesamtgewicht der jeweiligen Polymeren, der Butylengehalt liegt im Bereich von 1 bis 25 Gew.-%, ebenfalls bezogen auf dasThe polyolefin layer preferably contains a sealable polyolefin, preferably the polyolefin should be heat-sealable. Suitable polyolefins are, for example, high-density polyethylene and low-density polyethylene, copolymers of ethylene and propylene, terpolymers of ethylene, propylene and butylene or mixtures of these.
the ethylene content of the co- or terpolymers in particular
in the range of 0.1 to 15 wt.%, based on the total weight of the respective polymers, the butylene content is in the range of 1 to 25 wt.%, also based on the

• &ogr; &igr; &igr;·· · - ·•&ogr;&igr;&igr;·· · - ·

HOECRST'AKTIENGESELLSCHAFT - Werk KALLEHOECRST'AKTIENGESELLSCHAFT - KALLE plant

Gesamtgewicht des jeweiligen Polymeren. Die siegelbare Polyolefinschicht kann zur Verbesserung der Kratzfestigkeit und der Laufsicherheit auf schnellaufenden Verpackungsmaschinen übliche Zusätze wie niedermolekulare, verträgliche Harze, Schlupf- und Gleitmittel, Antiblockmittel oder Antistatika enthalten. Andere Zusätze wie Stabilisatoren gegen thermische Alterung oder Antioxydantien können gltichflalls gegebenenfalls vorgesehen sein.
10Total weight of the respective polymer. The sealable polyolefin layer can contain conventional additives such as low molecular weight, compatible resins, slip and lubricants, antiblocking agents or antistatic agents to improve scratch resistance and run safety on high-speed packaging machines. Other additives such as stabilizers against thermal ageing or antioxidants can also be provided if necessary.
10

Die Polyolefinschicht liegt als unorientierte weitgehend amorphe Schicht vor. Die Schichtdicke der Polyolefinschicht liegt im Bereich von 40 bis 100, bevorzugt von bis 80 /um. Die Polyolefinschicht kann durch Schmelzextrusion auf die biaxial orientierte Folie aus Polymeren enthaltend Polyvinylalkoholeinheiten und anschließender Abkühlung, aufgebracht werden, bevorzugt wird jedoch die Polyolefinschicht getrennt von der Schicht aus Polymeren enthaltend Vinylalkoholeinheiten hergestellt und anschließend erst mit Hilfe eines geeigneten Klebers zusammenkaschiert. Geeignete Klebstoffe sind z.B. lösemittelhaltige Kleber oder Zweikomponentenkleber, die üblicherweise in Mengen im Bereich von 0,5 bis 3.0 g/m2 angewandt v/erden. Die Schichtdicke der Schicht aus Polymeren enthaltend Einheiten von Vinylalkohol liegt zwischen 8 und 25 /Um, bevorzugt zwischen 12 und 15 /um.The polyolefin layer is present as an unoriented, largely amorphous layer. The layer thickness of the polyolefin layer is in the range from 40 to 100, preferably from 1 to 80 µm. The polyolefin layer can be applied to the biaxially oriented film made of polymers containing polyvinyl alcohol units by melt extrusion and subsequent cooling, but the polyolefin layer is preferably produced separately from the layer made of polymers containing vinyl alcohol units and then laminated together using a suitable adhesive. Suitable adhesives are, for example, solvent-based adhesives or two-component adhesives, which are usually used in amounts in the range from 0.5 to 3.0 g/m 2 . The layer thickness of the layer made of polymers containing vinyl alcohol units is between 8 and 25 µm, preferably between 12 and 15 µm.

An einer weiteren Ausführungsform der Neuerung kann die Verbundkombination auch noch zusätzliche weitere Schichten aus Polyvinylidenchlorid enthalten. Bevorzugt ist dieIn a further embodiment of the innovation, the composite combination can also contain additional layers of polyvinylidene chloride.

&bull; &igr; · 111 11 1111 r 11 · < · t < < · U&bull;&igr; · 111 11 1111 r 11 · < · t < < · U

11-1(11·» \> 11-1(11·» \>

lMIIlMII

HOECHST :A£flEJ$6ESELL^CHAiFT - Werk KALLEHOECHST : A£flEJ$6ESELL^CHAiFT - KALLE plant

Schicht aus Polymeren enthaltend Einheiten aus Vinylalkohol beidseitig mit Schichten aus Polyvinylidenchlorid überzogen. Diese zusätzlichen Schichten verleihen der neuerungsgemäßen Verbundkombination eine verbesserte Beständigkeit gegen den Einfluß von Feuchtigkeit. £33 Aufbringen der Polyvinylidenchloridüberzüge ist im Stand der Technik bekannt und wird üblicherweise durch Auftrag einer Dispersion des Polymeren in einem geeigneten Dispersionsmedium vorgenommen, insbesondere in wäßrigem Medium oder in einer Mischung von Wasser mit wassermischbaren organischen Lösemitteln.Layer of polymers containing units of vinyl alcohol coated on both sides with layers of polyvinylidene chloride. These additional layers give the new composite combination improved resistance to the influence of moisture. £33 Application of the polyvinylidene chloride coatings is known in the art and is usually carried out by applying a dispersion of the polymer in a suitable dispersion medium, in particular in an aqueous medium or in a mixture of water with water-miscible organic solvents.

In einer weiteren neuerungsgemäß vorgesehenen Ausführungsform kann die Schicht aus Polymeren enthaltend Vinylalkoholeinheiten mit einer Metallisierung versehen sein. Als Metallisierung kommen vor allem durch Vakuumbedampf ung. aufgebrachte dünne Schichten aus Aluminium in Frage, die der Folie ein hochglänzendes Aussehen verleihen. Durch die Metallisierung wird das optische Erscheinungsbild der Folie verbessert, und die aus der Folie hergestellte Verpackung erhält ein das menschliche Geschmacksempfinden angenehm ansprechendes attraktives Aussehen. In a further embodiment provided for in accordance with the innovation, the layer of polymers containing vinyl alcohol units can be provided with a metallization. The metallization can be thin layers of aluminum applied by vacuum vapor deposition, which give the film a high-gloss appearance. The optical appearance of the film is improved by the metallization, and the packaging made from the film has an attractive appearance that is pleasantly appealing to the human taste.

In einer v/eiteren ganz bevorzugten Ausführungsform ist die neuerungsgemäße Verbundkombination mit einer Kombination aus Metallisierung und Beschichtung aus Polyvinylidenchlorid versehen. Dabei kann zunächst die Schicht aus Polymeren enthaltend Vinylalkoholeinheiten ein- oder beidseitig mit Schichten aus Polyvinylidenchlorid überzo-In a further very preferred embodiment, the composite combination according to the invention is provided with a combination of metallization and coating of polyvinylidene chloride. The layer of polymers containing vinyl alcohol units can first be coated on one or both sides with layers of polyvinylidene chloride.

Il lilt It IHi MU illl I Il lilt It IHi MU illl I

i I III · · * &diams; i I III · · * &diams;

Ii &igr; &igr; t · Mi «II >l Ii &igr;&igr; t · Mi «II >l

&igr; &igr; &igr; r &igr; t * Ii &igr;&igr;&igr; r &igr; t * Ii

t I I ItIi * * It I I ItIi * * I

ti I Il 14 * I * «»« Iti I Il 14 * I * «»« I

HOECHST* :AKT!ENGfiSEL-LSCHÄFT: - Werk KALLEHOECHST* : ACTUAL ENGINEERING COMPANY : - KALLE plant

gen und dann metallisiert werden. Die metallisierte Folie wird danach auf der metallisierten Seite mit der Polyolefinschicht zusammenkaschiert. In einer besonders bevorzugten Ausführungsform der Neuerung ist die Verbundfolie J zusätzlich mit einer Bedruckung versehen, die außen auf dem überzug aus Polyvinylidenchlorid leicht aufgebracht werden kann.and then metallized. The metallized film is then laminated to the polyolefin layer on the metallized side. In a particularly preferred embodiment of the innovation, the composite film J is additionally provided with a print which can easily be applied to the outside of the polyvinylidene chloride coating.

Die Neuerung wird anhand der beigefügten Abbildung beispielhaft noch näher erläutert. Die Abbildung zeigt einen Querschnitt durch eine neuerungsgemäße Verbundkombination in seitlicher Ansicht. Im einzelnen sind durch Bezugszifiern hervorgehoben die Polyolefinschicht 1, die Schicht enthalcend Einheiten aus Polyvinylalkohol 2, die auf ihrer Oberflä he beidseitig mit überzügen aus Polyvinylidenchlorid 3/3' versehen ist, sowie eine Metallisierung 4, die zwischen der Polyolefinschicht 1 und der inneren Schicht aus Polyvinylidenchlorid 3' angeordnet ist. Auf der freien Oberfläche der äußeren Schicht aus Polyvinylidenchlorid 3 ist die Bedruckung 5 erkennbar.The innovation is explained in more detail using the attached illustration as an example. The illustration shows a cross-section through a composite combination according to the innovation in a side view. In detail, the polyolefin layer 1, the layer containing units of polyvinyl alcohol 2, which is provided on both sides with coatings of polyvinylidene chloride 3/3', and a metallization 4, which is arranged between the polyolefin layer 1 and the inner layer of polyvinylidene chloride 3', are highlighted by reference numbers.

Überraschenderweise hat sich gezeigt, daß die Sauerstoffdurchläss.igkeit der quaderförmigen Schlauchbeutelpackungen für gemahlenen Kaffee durch den Einsatz der neuerungsgemäßen Folie signifikant herabgesetzt werden konn-Surprisingly, it has been shown that the oxygen permeability of the cuboid-shaped tubular bag packages for ground coffee can be significantly reduced by using the innovative film.

&idigr;
te, verglichen mit Packungen aus metallisierter Folie aus anderen Polymeren. An einer metallisierten Polyesterfolie (Polyethylenterephthalat einer Dicke von 12 /um), die mit einer Polyethylenschicht von 75 /um überzogen war, wurde die Sauerstoffdurchlässigkeit in der Einheit (cm^/m^'d'bar) gemessen. &idgr;
compared with packages made of metallized film made of other polymers. The oxygen permeability in units (cm^2/m^2'd'bar) was measured on a metallized polyester film (polyethylene terephthalate with a thickness of 12 /um) coated with a polyethylene layer of 75 /um.

&bull; · · ■« mi&bull; · · ■« mi

»&bull;&bull;&bull;&bull;I I»&bull;&bull;&bull;&bull;I I

HOECHST. SUTTfENeESBLLSCHAFT:- Werk KALLEHIGHEST SUTTfENeESBLLSCHAFT:- KALLE plant

&mdash; 7 &mdash;—7—

Für die flachliegende Folie ergab die Messung 0/5 bis 0,8, während an der fertig hergestellten Verpackung Werte von 2 bis 6 gemessen wurden.For the flat film, the measurement resulted in values of 0.5 to 0.8, while values of 2 to 6 were measured for the finished packaging.

Demgegenüber wurden an einer neuerungsgemäßen Verbundkombination aus Polyethylen und reinem Polyvinylalkohol mit einem Verseifungsgrad von 99,9% die Sauerstof !.durchlässigkeit an der flachliegenden Folie als <0,01 gemessen, und an einer aus der genannten neuerungsgemäßen Verbundkombination hergestellten Schlauchpackung für gemahlenen Kaffee wurde immer noch eine Sauerstoffdurchlässigkeit von <0,01 bestimmt. Besonders überraschend ist, daß diese geringe Sauerstoffdurchlassigkeit auch bei Luftfeuchtigkeitswerten um 85% rel. Luftfeuchtigkeit aufrechterhalten wird.In contrast, the oxygen permeability of a new composite combination made of polyethylene and pure polyvinyl alcohol with a degree of saponification of 99.9% was measured as <0.01 on the flat film, and an oxygen permeability of <0.01 was still determined on a tube pack for ground coffee made from the new composite combination mentioned. It is particularly surprising that this low oxygen permeability is maintained even at air humidity values of around 85% relative humidity.

Weitere Vorteile der Neuerung sind darin zu sehen, daß die Folie eine Wärmebeständigkeit nach ASTM D 1637 bis 220° aufweist und somit auf allen üblichen Abpackmaschinen problemlos verarbeitbar ist. Die Folie besitzt eine hervorragende Steifigkeit (&Egr;-Modul) und eine sehr hohe üurchstoßfestigkeit, die bei gemahlenem Kaffee besonders wichtig ist. Die neuerungsgemäße Folie weist eine Dichte von 1,32 g/cm3 auf und ist damit im Vergleich zu PoIyesterfolie enthaltenden Verpackungsmaterialien (Dichte: 1,40 g/cm3) leichter. Damit wird eine erhöhte Ergiebigkeit erreicht. Neuerungsgemäfii besonders geeignet ist die Polyvinylalkoholfolie BOVLOn(r) der Firma Nippon Gohsei,-Further advantages of the innovation are that the film has a heat resistance of up to 220° according to ASTM D 1637 and can therefore be processed without any problems on all standard packaging machines. The film has excellent rigidity (ε-modulus) and a very high puncture resistance, which is particularly important for ground coffee. The film according to the innovation has a density of 1.32 g/cm 3 and is therefore lighter than packaging materials containing polyester film (density: 1.40 g/cm 3 ). This results in increased yield. According to the innovation, the polyvinyl alcohol film BOVLOn( r ) from Nippon Gohsei is particularly suitable.

Claims (16)

HOECHST AKTIENGESELLSCHAFT -'Werk KALLE 87/K 007G - 8 - WLJ-DC.Ho-bl 21. Mai 1987 SchutzansprücheHOECHST AKTIENGESELLSCHAFT -'Werk KALLE 87/K 007G - 8 - WLJ-DC.Ho-bl 21 May 1987 Protection claims 1. Verbundfolie zur Herstellung von im wesentlichen quaderförmigen, evakuierten Schlauchbeutelpackungen aus thermoplastischen Kunststoffen mit einer besonders niedrigen Sauerstoffdurchlässigkeit, dadurch gekennzeichnet, daß sie wenigstens eine biaxial streckorientierte Schicht aus einem Polymeren enthaltend Vinylalkoholeinheiten und eine Schicht aus einem Polyolefin enthält. 101. Composite film for the production of essentially cuboid-shaped, evacuated tubular bag packages made of thermoplastics with a particularly low oxygen permeability, characterized in that it contains at least one biaxially stretch-oriented layer made of a polymer containing vinyl alcohol units and a layer made of a polyolefin. 10 2. Verbundfolie nach Anspruch I1. dadurch gekennzeichnet,· daß die Schicht aus Polymeren enthaltend Vinylalkoholeinheiten Polyvinylalkohol oder ein Copolymerisat aus Vinylalkohol und Alfa-Olefinen mit 2 bis 5 C-Atomen enthält. 2. Composite film according to claim 1 1 , characterized in that the layer of polymers containing vinyl alcohol units contains polyvinyl alcohol or a copolymer of vinyl alcohol and alpha-olefins having 2 to 5 carbon atoms. 3. Verbundfolie nach Anspruch 2, dadurch gekennzeichnet, daß als Alfa-Olefin Ethylen eingesetzt wird in einem mengenmäßigen Anteil von höchstens 40 Mol-%, bevorzugt höchstens 20 Mol-%, bezogen auf die Gesamtmenge an Copolymerisat. 3. Composite film according to claim 2, characterized in that ethylene is used as the alpha-olefin in a quantitative proportion of at most 40 mol%, preferably at most 20 mol%, based on the total amount of copolymer. 4. Verbundfolie nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die Schicht aus Polyolefin heißsiegelbar ist.4. Composite film according to one of claims 1 to 3, characterized in that the layer of polyolefin is heat-sealable. \ \ 5. Verbundfolie nach einem der Ansprüche 1 bis 4, da-5. Composite film according to one of claims 1 to 4, ; durch gekennzeichnet, daß die Schicht aus Polyolefin; characterized in that the layer of polyolefin Ethylen, Copolymere aus Ethylen und Propylen, TerpolymereEthylene, copolymers of ethylene and propylene, terpolymers | 30 aus Ethylen, Propylen und Butylen oder Mischungen von diesen enthält,| 30 of ethylene, propylene and butylene or mixtures thereof, HOECHST AKTIENGESELLSCHAFT -"Werk KALLE 87/K 007G - 9 -HOECHST AKTIENGESELLSCHAFT -"KALLE plant 87/K 007G - 9 - 6. Verbundfolie nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß sie durch Kleberkaschierung hergestellt ist.6. Composite film according to one of claims 1 to 5, characterized in that it is produced by adhesive lamination. C C 7. Verbundfolie nach einem der Ansprüche 1 bis 6, da-7. Composite film according to one of claims 1 to 6, I durch gekennzeichnet, daß die Schichtdicke der SchichtI characterized in that the layer thickness of the layer \ aus Polyolefin im Bereich zwischen 40 und 100 /um liegt, \ made of polyolefin in the range between 40 and 100 /um, \ bevorzugt zwischen 50 und 80 /um. \ preferably between 50 and 80 /um. I ioI io \ \ 8. Verbundfolie nach einem der Ansprüche 1 bis 7, da-8. Composite film according to one of claims 1 to 7, I durch gekennzeichnet, dpß die Schichtdicke der SchichtI characterized by, dpß the layer thickness of the layer aus Polymeren enthaltend Vinylalkoholeinheiten im Bereich von 8 bis 25 /um liegt, bevorzugt zwischen 12 und 15 /um.of polymers containing vinyl alcohol units in the range of 8 to 25 /um, preferably between 12 and 15 /um. 1515 I I 9. Verbundfolie nach einem der Ansprüche 1 bis 3, da-9. Composite film according to one of claims 1 to 3, i durch gekennzeichent, daß sie wenigstens eine zusätzlichei marked by that they contain at least one additional ' Schicht aus Polyvinylidenchlorid enthält.' layer of polyvinylidene chloride. I 20 I20 10. Verbundfolie nach Anspruch 9, dadurch geker.nzeich-10. Composite film according to claim 9, characterized in 4 net, daß die Schicht aus Polyvinylidenchlorid unmittelbar 4 net that the layer of polyvinylidene chloride immediately ' mit der Schicht aus Polymeren enthaltend Vinylalkoholeinheiten verbunden ist. ' is bonded to the layer of polymers containing vinyl alcohol units. 25 25 11. Verbundfolie nach Anspruch 9, dadurch gekennzeichnet, daß die Schicht aus Polymeren enthaltend Vinylalkoholeinheiten beidseitig mit Schichten aus Polyvinylidenchlorid überzogen ist. 11. Composite film according to claim 9, characterized in that the layer of polymers containing vinyl alcohol units is coated on both sides with layers of polyvinylidene chloride. 30 30 12. Verbundfolie nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, daß sie eine Metallisierung trägt.12. Composite film according to one of claims 1 to 8, characterized in that it carries a metallization. < · ti< · ti i till« * · *i till« * · * HOECHST AKTIENGESELLSOHÄFT -"Werk KALLEHOECHST AKTIENGESELLSCHAFT -"Werk KALLE 87/K 007G - 10 -87/K 007G - 10 - 13. Verbundfolie nach Anspruch 12, dadurch gekennzeichnet, daß die Metallisierung durch Vakuumaufdampfuhg aufgebrachtes Aluminium ist.13. Composite film according to claim 12, characterized in that the metallization is aluminum applied by vacuum vapor deposition. 14. Verbundfolie nach einem deif Ansprüche 1 bis 8, da·^14. Composite film according to one of claims 1 to 8, durch gekennzeichnet, daß sie mit einer Kombination aus |characterized in that it is provided with a combination of | Metallisierung und einer Schicht aus Polyvinylidenchlorid jMetallization and a layer of polyvinylidene chloride j versehen ist. t?is provided. t? jj 15. Verbundfolie nach Anspruch 14, dadurch gekennzeich- |15. Composite film according to claim 14, characterized in that | net, daß die Metallisierung in direktem Kontakt zu der |net that the metallization is in direct contact with the | Schicht aus Polyolefin steht. jjLayer of polyolefin. jj 16. Verbundfolie nach einem der Ansprüche 1 bis 15, da- * durch gekennzeichnet, daß sie eine Sauerstoffdurchlässig- ] keit von weniger als 0,01 cmVm^*<3 'bar aufweist.16. Composite film according to one of claims 1 to 15, characterized in that it has an oxygen permeability of less than 0.01 cm2 /m2 bar.
DE8703556U 1987-03-10 1987-03-10 Composite film for the production of cuboid-shaped evacuated packages Expired DE8703556U1 (en)