DE4432298A1 - Hygiene products

Info

Publication number: DE4432298A1
Application number: DE19944432298
Authority: DE
Inventors: Eddy Taal; Eckhard Dr Puerkner; Walter Weis
Original assignee: Henkel AG and Co KGaA
Current assignee: Henkel AG and Co KGaA
Priority date: 1994-09-10
Filing date: 1994-09-10
Publication date: 1996-03-14
Also published as: WO1996007385A3; WO1996007385A2

Abstract

Described are articles of hygiene, in particular sanitary napkins and pantiliners, which are characterized by the use of an antislip agent rather than a contact adhesive. This obviates the need to cover the adhesive with silicone paper. The antislip agent is essentially based on an ethylene-vinylacetate copolymer or a styrene copolymer.

Description

Die Erfindung betrifft einen Hygieneartikel und seine Herstellung.The invention relates to a hygiene article and its manufacture.

Unter einem Hygieneartikel soll ein flüssigkeitsabsorbierender Formkörper verstanden werden, der aus einem Kern aus absorbierendem Material und einer Hülle aus flüssigkeitsdurchlässigem Blattmate rial besteht und üblicherweise auf einer Seite noch eine flüssig keitsundurchlässige Schicht enthält. Konkrete Gegenstände sind z. B. Binden zur Inkontinenz und zur Frauenhygiene (Damenbinden oder Slip einlagen). Um einen sicheren Sitz dieses Hygieneartikels zu er zielen, wird er üblicherweise an der Kleidung befestigt, z. B. in einem Slip. Dafür hat der Hygieneartikel eine selbstklebende Schicht aus einem Haftklebstoff. Hierbei handelt es sich um einen permanent klebrigen Klebstoff, der bei leichtem Druck sofort auf allen Substraten haftet. Die mit dem Haftklebstoff hergestellten Klebverbunde können meistens ohne Zerstörung der verklebten Sub strate gelöst werden.Under a hygiene article, a liquid-absorbent Shaped body to be understood, which consists of a core of absorbent Material and a cover made of liquid-permeable leaf mat rial exists and usually still liquid on one side impermeable layer. Specific objects are e.g. B. Bandages for incontinence and feminine hygiene (sanitary napkins or briefs insoles). To ensure a secure fit of this hygiene item aim, it is usually attached to clothing, e.g. B. in a slip. For this, the hygiene article has a self-adhesive Layer of a pressure sensitive adhesive. This is a permanent sticky glue that comes on immediately with light pressure adheres to all substrates. Those made with the pressure sensitive adhesive Adhesive bonds can usually be done without destroying the bonded sub strate to be resolved.

Nachteilig bei der Verwendung von Haftklebstoffen bei Hygienearti keln ist, daß bis zum Gebrauch immer auch eine Schutzschicht not wendig ist, die ein Verkleben mit unerwünschten Substraten verhin dert. Sie besteht aus einer nichthaftenden oder schlechthaftenden Schicht, insbesondere silikonisiertem Papier. Das Papier wird bei Gebrauch weggeworfen. Ein weiterer Nachteil des Haftklebstoffes ist, daß er nicht immer rückstandsfrei von dem Bekleidungsstück entfernt werden kann.Disadvantageous when using pressure sensitive adhesives for hygiene articles keln is that a protective layer is always necessary before use is agile, which prevents sticking with unwanted substrates different. It consists of a non-adhesive or poor adhesive Layer, especially siliconized paper. The paper comes in Discarded use. Another disadvantage of the pressure sensitive adhesive is that he is not always residue-free from the garment can be removed.

Mit diesem Problem der zerstörungsfreien und rückstandsfreien Ent fernung des Hygieneartikels beschäftigt sich die EP 0 211 311. Darin wird ein absorptionsfähiger Formkörper, beispielsweise Da menbinde oder Slipeinlage, mit einem Kern aus absorbierenden Mate rial und einer Hülle aus flüssigkeitsdurchlässigen Blattmaterial beschrieben, wobei auf einer Seite des Formkörpers auf der Ober fläche der Hülle eine mit einer ablösbaren Schutzfolie abgedeckte druckempfindliche selbstklebende Klebstoffschicht vorgesehen ist, die aus einem Haftschmelzkleber aus 20 bis 80% im wesentlichen amorphen olefinischen Polymeren, 20 bis 80% klebrig machenden Har zen und 0 bis 80% Weichmacheröl besteht. Der Haftschmelzkleber ist dadurch gekennzeichnet, daß er aus ataktischen Polymeren besteht und eine Scherfestigkeit von weniger als 1 Minute aufweist.With this problem of non-destructive and residue-free Ent Removal of the hygiene article is concerned with EP 0 211 311. An absorbent molded body, for example Da menbinde or panty liner, with a core of absorbent mate rial and a shell made of liquid-permeable sheet material described, being on one side of the molded body on the upper surface of the cover is covered with a removable protective film pressure-sensitive self-adhesive layer is provided, essentially from a hot melt adhesive from 20 to 80% amorphous olefinic polymers, 20 to 80% tackifying Har zen and 0 to 80% plasticizer oil. The hot melt adhesive is characterized in that it consists of atactic polymers and has a shear strength of less than 1 minute.

Ausgehend von diesem Stand der Technik ergab sich als erfindungsge mäße Aufgabe, Hygieneartikel zur Verfügung zu stellen, die auch ohne einen Haftklebstoff und damit ohne eine Schutzfolie auskommen und dennoch einen sicheren Sitz gewährleisten sowie zerstörungsfrei und rückstandsfrei von dem Bekleidungsstück wieder zu entfernen sind.Based on this prior art emerged as Invention moderate task to provide hygiene articles that also without a pressure sensitive adhesive and thus without a protective film and still ensure a secure fit and non-destructive and remove it from the garment without leaving any residue are.

Die erfindungsgemäße Lösung ist den Patentansprüchen zu entnehmen. Sie besteht im wesentlichen in der Verwendung von Antislipmitteln anstelle von Haftklebstoffen. The solution according to the invention can be found in the patent claims. It consists essentially in the use of anti-slip agents instead of pressure sensitive adhesives.

Antislipmittel sollen bereits bei sehr geringem Druck ein Verrut schen, d. h. eine unbeabsichtigte gleitende Verschiebung zweier Ge genstände zueinander verhindern, jedoch ihre Trennung voneinander ohne weiteres ermöglichen. Das wird in der Regel dadurch erreicht, daß das Antislipmittel Bewegungen in Gleitrichtung großen Wider stand entgegensetzt, Bewegungen senkrecht dazu jedoch keinen oder einen so geringen Widerstand, daß die Oberfläche der getrennten Gegenstände nicht geschädigt wird. Im Idealfall sollte also die Zugscherfestigkeit gemäß DIN 53 283 sehr groß sein und die Zugfe stigkeit senkrecht zur Klebfläche gemäß DIN 53 288 sehr klein. Sie soll so klein sein, daß nichts auf dem Antislipmittel haftet, und man auf die Schutzfolien verzichten kann. Die Scherfestigkeit einer Standardbeschichtung von 60 g/m² erfindungsgemäßem Antislipmittel auf Polyester-Folie gegen Baumwollstoff-Maschenware ist nach 15 Stunden bei 38°C und einem Druck von 0,13 N/cm³ kleiner als 0,6, insbesondere kleiner als 0,3 N/25 mm. Die Klebrigkeit ist ins besondere so gering, daß ein Silikonpapier darauf nicht mehr haf tet. Es fällt aufgrund des eigenen Gewichtes nach unten.Antislip agents are said to slip even at very low pressure little, d. H. an inadvertent sliding shift of two Ge prevent objects from each other, but their separation from one another enable easily. This is usually achieved by that the anti-slip agent large movements in sliding direction opposed, but movements perpendicular to it none or such a low resistance that the surface of the separated Objects are not damaged. Ideally, that should Tensile shear strength according to DIN 53 283 be very large and the tensile strength Very small perpendicular to the adhesive surface according to DIN 53 288. she should be so small that nothing adheres to the anti-slip agent, and you can do without the protective films. The shear strength of a Standard coating of 60 g / m² of anti-slip agent according to the invention on polyester film against cotton knitwear is after 15 hours at 38 ° C and a pressure of 0.13 N / cm³ less than 0.6, in particular less than 0.3 N / 25 mm. The stickiness is ins special so low that a silicone paper no longer has it tet. It falls down due to its own weight.

Ein Antislipmittel enthält neben dem Basispolymeren üblicherweise nachfolgende Komponenten: Harz, Wachs, Weichmacher, Stabilisator, Pigment, Füllstoff usw.In addition to the base polymer, an anti-slip agent usually contains following components: resin, wax, plasticizer, stabilizer, Pigment, filler, etc.

In der stofflichen Zusammensetzung unterscheidet sich also das Anti slipmittel von einem Haftklebstoff weniger in der Art des Basis polymeren als vielmehr darin, daß es keinen Klebrigmacher enthält, sondern eher Trennmittel. Besondere geeignete Trennmittel sind Wachse. Sie haben einen Schmelzpunkt von wenigstens 40°C, sind verhältnismäßig niedrigviskos und ziehen im Gegensatz zu vielen Harzen keine Fäden. Als konkrete Wachse seien genannt: Paraffin wachs mit Schmelzpunkten im Bereich von 45 bis 70°C und Molgewich ten zwischen 225 und 500, mikrokristalline Wachse mit Schmelzpunk ten im Bereich von 60 bis 95°C, synthetische Fischer-Tropsch-Wach se mit Schmelzpunkten im Bereich von 100 bis 115°C und Polyethy len-Wachse mit Schmelzbereichen zwischen 85 und 140°C und Molge wichten im Bereich von 500 bis 3500.The anti differs in the material composition slip agent from a pressure sensitive adhesive less in the type of base polymeric rather than not containing any tackifier, rather release agents. Particularly suitable release agents are Waxes. They have a melting point of at least 40 ° C relatively low viscosity and pull unlike many Resin no threads. Specific waxes are: paraffin wax with melting points in the range of 45 to 70 ° C and Molgewich between 225 and 500, microcrystalline waxes with melting point ten in the range of 60 to 95 ° C, synthetic Fischer-Tropsch-Wach se with melting points in the range of 100 to 115 ° C and polyethylene len waxes with melting ranges between 85 and 140 ° C and molge weight in the range of 500 to 3500.

Klebrigmachende Harze sind entweder überhaupt nicht oder in unter geordneten Mengen in dem Antislipmittel enthalten. An Harzen können enthalten sein, z. B. Kohlenwasserstoffharze, insbesondere Petrole umharze. Sie entstehen durch Polymerisation niedriger ungesättigter Kohlenwasserstoffe mit durchschnittlich 5 C-Atomen pro Molekül (so genannte C₅-Harze mit mittleren Molekulargewichten von ca. 1200 bis 1500). Durch Polymerisation von ungesättigten Kohlenwasserstoffen mit neun Kohlenstoffatomen, z. B. Inden, Methylinden und Styrolde rivaten, erhält man die sogenannten C₉-Harze. Mischpolymerisationen von C₅- und C₉-Kohlenwasserstoffen führen zu beständigen thermo plastischen Harzen mit Erweichungspunkten zwischen 70 und 120°C.Tackifying resins are either not at all or in under orderly amounts contained in the anti-slip agent. Resins can be included, e.g. B. hydrocarbon resins, especially petroleum resin. They are formed by polymerizing lower unsaturated ones Hydrocarbons with an average of 5 carbon atoms per molecule (see above) C₅ resins mentioned with average molecular weights of about 1200 to 1500). By polymerizing unsaturated hydrocarbons with nine carbon atoms, e.g. B. indene, methylindene and styrene rivaten, you get the so-called C₉ resins. Mixed polymerizations of C₅ and C₉ hydrocarbons lead to stable thermo plastic resins with softening points between 70 and 120 ° C.

Basisbildende Polymere sind vor allem Polyolefine und Kautschuke. Polyolefine haben die allgemeine Formel (-CH₂-CR¹R²)_n, wobei R¹ meistens H ist und R² für H und geradkettige oder verzweigte ge sättigte aliphatische bzw. cycloaliphatische oder aromatische Grup pen steht, z. B. Butyl-, Propyl-, Butyl- und Cyclohexyl-. Kommen mehrere Komponenten in einem Molekül vor, so handelt es sich um Copolymere. Bevorzugte Copolymere basieren auf Ethylen und Vinyl acetat. Sie sind zweckmäßigerweise niedrigviskos, d. h. ihr Schmelz index liegt im Bereich von 800 bis 3000 g/10 min nach DIN 53 735. Bevorzugte Basispolymere sind Ethylen/Vinylacetat-Copolymere, ins besondere mit einem Gehalt von ca. 10 bis 40, insbesondere ca. 30 Gew.-% an Vinylacetat, z. B. Escorene Ultra der Fa. Exxon oder das amorphe Copolymere von α-Olefinen Vestoplast der Firma Chem. Werke Hüls AG. Weitere geeignete Antislipmittel werden in der DE 42 30 472 beschrieben. Sie basieren auf einer wäßrigen Dispersion von Poly merisaten, olefinisch ungesättigter Verbindungen wie z. B. Acryl säure und deren C₁-C₈-Alkylester, Butadien, Ethylen, Vinylacetat, Styrol, Acrylnitril und/oder Vinylpyrrolidon, wobei Copolymere von Ethylen und Vinylacetat mit gegebenenfalls weiteren Comonomeren, wie z. B. Acrylsäure oder Vinylpyrrolidon besonders bevorzugt sind.The basic polymers are mainly polyolefins and rubbers. Polyolefins have the general formula (-CH₂-CR¹R²) _n , where R¹ is mostly H and R² is H and straight-chain or branched ge saturated aliphatic or cycloaliphatic or aromatic groups, for. B. butyl, propyl, butyl and cyclohexyl. If there are several components in one molecule, they are copolymers. Preferred copolymers are based on ethylene and vinyl acetate. They are expediently low-viscosity, ie their melt index is in the range from 800 to 3000 g / 10 min according to DIN 53 735. Preferred base polymers are ethylene / vinyl acetate copolymers, in particular with a content of approx. 10 to 40, in particular approx. 30 % By weight of vinyl acetate, e.g. B. Escorene Ultra from Exxon or the amorphous copolymer of α-olefins Vestoplast from Chem. Werke Hüls AG. Other suitable anti-slip agents are described in DE 42 30 472. They are based on an aqueous dispersion of poly merisates, olefinically unsaturated compounds such as. B. acrylic acid and its C₁-C₈ alkyl ester, butadiene, ethylene, vinyl acetate, styrene, acrylonitrile and / or vinyl pyrrolidone, copolymers of ethylene and vinyl acetate with optionally further comonomers, such as. B. acrylic acid or vinyl pyrrolidone are particularly preferred.

Es können auch Polyolefin-Kautschuke eingesetzt werden, also Elasto mere mit Kautschukcharakter auf der Basis von Olefinen, insbeson dere Copolymere aus Ethylen und Propylen (EPDM) bzw. Terpolymere aus Ethylen, Propylen und einem nichtkonjugierten Dien.Polyolefin rubbers, i.e. elasto, can also be used mers with rubber character based on olefins, in particular copolymers of ethylene and propylene (EPDM) or terpolymers from ethylene, propylene and a non-conjugated diene.

Von den Kautschuken eignen sich die synthetischen Kautschuke be sonders gut als Basis für die Antislipmittel. Hiervon sind wiederum die Styrol-Copolymere von besonderer Bedeutung, insbesondere Sty rol/Butadien-Kautschuk und Styrol/Butadien/Styrol-Kautschuk. Ein geeignetes Styrolblockcopolymeres ist z. B. das Cariflex TR-KX 138 S der Fa. Shell oder das Stereon 840 A der Firma Firestone. Geeignete Antislipmittel auf der Basis von Styrol-Copolymerisaten werden in der DE 42 30 473 beschrieben. Dabei handelt es sich um eine wäßrige Dispersion eines Polymerisates aus Styrol und einem Dien, Isopren oder Butadien im Gewichtsverhältnis von 20 : 80 bis 80 : 20. Außer dem kann auch Itaconsäure mitverwendet werden.Of the rubbers, the synthetic rubbers are suitable especially good as a basis for the anti-slip agents. Of these are again the styrene copolymers of particular importance, especially sty rol / butadiene rubber and styrene / butadiene / styrene rubber. On suitable styrene block copolymer is e.g. B. the Cariflex TR-KX 138 S from Shell or the Stereon 840 A from Firestone. Suitable Antislip agents based on styrene copolymers are used in described in DE 42 30 473. It is an aqueous one Dispersion of a polymer from styrene and a diene, isoprene or butadiene in a weight ratio of 20:80 to 80:20 itaconic acid can also be used.

Das Antislipmittel kann weitere Zusätze enthalten wie z. B. Stabi lisatoren, insbesondere Antioxidantien, Pigmente, wie z. B. Titan oxid und Füllstoffe wie z. B. Zinkoxid.The anti-slip agent may contain other additives such as. B. Stabi lisators, especially antioxidants, pigments, such as. B. Titan oxide and fillers such. B. zinc oxide.

Das Antislipmittel enthält die eben angeführten Komponenten in fol genden Konzentrationen:The anti-slip agent contains the components just listed in fol concentrations:

1. 30 to 100, in particular 70 to 100 wt .-% of at least one of the Base polymers,
2. 0 to 60% by weight of at least one resin,
3. 0 to 30, in particular 5 to 25% by weight of at least one Wax,
4. 0 to 30, in particular 1 to 5% by weight of at least one Softener,
5. 0 to 2% by weight of at least one antioxidant,
6. 0 to 2% by weight of at least one pigment and
7. 0 to 15% by weight of at least one filler.

Die Summe der Anteile ergibt 100%. Falls es sich bei dem Antislip mittel um eine Dispersion oder Lösung handelt, so beziehen sich die obigen Anteile auf den Feststoffgehalt.The sum of the shares is 100%. If it is the anti-slip medium is a dispersion or solution, so refer to above proportions on the solids content.

Zweckmäßigerweise besteht die Rezeptur ausThe recipe expediently consists of

30 bis 40 Gew.-% eines Poly-α-olefins,
45 bis 55 Gew.-% eines Kohlenwasserstoffharzes,
15 bis 25 Gew.-% eines Paraffins und
0,1 bis 1,0 Gew.-% eines Antioxidans.30 to 40% by weight of a poly-α-olefin,
45 to 55% by weight of a hydrocarbon resin,
15 to 25% by weight of a paraffin and
0.1 to 1.0% by weight of an antioxidant.

Das Antislipmittel wird auf bekannte Art und Weise durch Mischen der Komponenten hergestellt. Vorzugsweise wird dabei auf die Ver wendung von Wasser und insbesondere von organischen Lösungsmitteln verzichtet.The anti-slip agent is mixed in a known manner of the components. Preferably, the Ver Use of water and especially organic solvents waived.

Dementsprechend wird das Antislipmittel vorzugsweise aus der Schmel ze auf den Hygieneartikel aufgetragen, aber auch der Auftrag aus einer wäßrigen Dispersion bzw. organischen Lösung ist möglich, ins besondere in Form von Pasten (Viskosität von 20 bis 100 Pas bei 20°C nach ASTM D 323673). Hochkonzentrierte wäßrige Dispersionen mit einem Feststoffgehalt von 40 bis 60% werden zweckmäßigerweise mit Infrarotstrahlung bzw. mit Hochfrequenz getrocknet.Accordingly, the anti-slip agent is preferably made from the melt ze applied to the hygiene article, but also the order an aqueous dispersion or organic solution is possible, ins especially in the form of pastes (viscosity from 20 to 100 Pas 20 ° C according to ASTM D 323673). Highly concentrated aqueous dispersions with a solids content of 40 to 60% are expedient dried with infrared radiation or with high frequency.

Auch die Vorrichtungen zum Klebstoffauftrag sind bekannt (siehe z. B. Ullmanns Enclyclopädie der techn. Chemie Band 14, S. 244 bis 246). Konkret seien genannt der Auftrag durch Sprühen, mit Breit schlitzdüsen, mit Rasterwalzen und nach dem Transfer-Verfahren mit Hilfe von Silikonpapier. Zweckmäßigerweise wird aber ein Siebdruck verfahren verwendet. Dabei wird das Antislipmittel mit Hilfe eines Rakels durch ein Kunststoff- oder Metallsieb hindurchgedrückt. Das Sieb ist auf der Unterseite mit einer Beschichtung versehen, bei der schablonenartig die mit Klebstoff zu versehenden Stellen aus gespart sind, so daß der Klebstoff nur an den freien Stellen durch das Sieb gelangen kann. Vorzugsweise wird eine Rotations-Siebdruck maschine verwendet, bei der das Siebmaterial auf Zylindern gespannt ist. Die Rakel streifen an der Innenseite der Zylinder. Wenn das Antislipmittel aus der Schmelze aufgetragen wird, muß die Tempera tur des Siebes genau kontrolliert werden.The devices for applying adhesive are also known (see e.g. B. Ullmanns Enclyclopadie der techn. Chemistry Volume 14, pp. 244 bis 246). The application by spraying with Breit should be mentioned specifically slot nozzles, with anilox rollers and using the transfer process Help of silicone paper. However, screen printing is expedient process used. The anti-slip agent is used with the help of a Squeegee pushed through a plastic or metal sieve. The Sieve is coated on the underside, at the template-like areas to be glued are saved so that the adhesive only through the free areas the sieve can get. Rotary screen printing is preferred machine used in which the screen material is stretched on cylinders is. The squeegees graze on the inside of the cylinders. If that Antislip agent is applied from the melt, the tempera of the sieve can be checked precisely.

Das Antislipmittel kann auf die wasserundurchlässige Schicht, ins besondere auf die Polyethylenfolie aufgetragen werden. Bei einem direkten Auftrag, also nicht beim Transferverfahren mit Silikonpa pier ist besonders zu berücksichtigen, daß die Folie durch die Schmelze des Antislipmittels nicht zerstört wird. Vorzugsweise wird das Antislipmittel jedoch auf die Umhüllung aus einem Nonwoven- Stoff aufgetragen. Er besteht in der Regel aus Fasern von Polyethy len, Polypropylen und/oder Viskose.The anti-slip agent can be applied to the waterproof layer special to be applied to the polyethylene film. At a direct order, i.e. not with the transfer process with silicone pa pier is particularly important to note that the film through the The melt of the anti-slip agent is not destroyed. Preferably the anti-slip agent, however, on the covering made of a nonwoven Fabric applied. It is usually made of polyethylene fibers len, polypropylene and / or viscose.

Das Antislipmittel wird in der Regel in einer Menge von 15 bis 150 g/m² aufgetragen, vorzugsweise in einer Menge von 50 bis 100 g/m². Die Form der Antislipmittel-Flächen kann im Prinzip beliebig sein. Vorzugsweise wird das Antislipmittel jedoch streifenförmig oder wellenförmig aufgetragen, wobei auch Zeichen oder Wörter geschrie ben werden können. Ein punktförmiger Auftrag ist besonders zu emp fehlen. Falls das Antislipmittel auch wasserundurchlässig ist, empfiehlt sich ein vollflächiger Auftrag, so daß auch auf die Ver wendung der wasserundurchlässigen Folie verzichtet werden kann.The anti-slip agent is usually used in an amount of 15 to 150 g / m² applied, preferably in an amount of 50 to 100 g / m². In principle, the shape of the anti-slip surfaces can be any. However, the anti-slip agent is preferably in the form of a strip or applied in a wave shape, with signs or words also screaming can be used. A punctiform order is particularly too emp absence. If the anti-slip agent is also impermeable to water, A full-surface order is recommended, so that the Ver the waterproof film can be dispensed with.

Die Erfindung wird anhand eines Beispiels im folgenden einzeln er läutert:The invention is based on an example in the following he purifies:

1. Preparation of the anti-slip agent

30 Gew.-Teile eines Copolymeren aus einem Poly-α-Olefin (Vestoplast 703) werden mit 49,5 Gew.-Teilen Kohlenwasserstoffharz (Escorez 5300) und 20 Gew.-Teilen Paraffin 60/62 sowie 0,5 Gew.-Teilen Irga nox 1010 in der Schmelze homogenisiert.30 parts by weight of a copolymer of a poly-α-olefin (vestoplast 703) with 49.5 parts by weight of hydrocarbon resin (Escorez 5300) and 20 parts by weight of paraffin 60/62 and 0.5 parts by weight of Irga nox 1010 homogenized in the melt.

Es wird ein Antislipmittel erhalten, das durch folgende Merkmale gekennzeichnet ist:An anti-slip agent is obtained which has the following characteristics is marked:

Viscosity (Brookfield 140 ° C, RVT, 27): 500-1000 mPas,
- softening temperature (ring ball): 105-115 ° C.

2. Apply the anti-slip agent to a film

Das obige Antislipmittel wird mit einer Rotations-Siebdruckmaschine auf eine Folie aus PE bei 140°C und einer Produktionsgeschwindig keit von 40 m/min aufgetragen.The above anti-slip agent is used with a rotary screen printing machine on a PE film at 140 ° C and a production speed speed of 40 m / min.

Es wird eine rutschfeste Folie erhalten mit geometrischen Figuren des Antislipmittels. Die Streifen und Schriftzüge bestehen aus lau ter kleinen einzelnen Punkten. Das Antislipmittel fühlt sich trok ken an und führt mit normalem Papier zu keiner Verklebung. Die Folie ist ausreichend rutschfest. Daher verrutscht eine Damenbinde, bei der diese Folie die wasserundurchlässige Schicht bildet, beim Tra gen nicht.A non-slip film with geometric figures is obtained of the anti-slip agent. The stripes and lettering consist of lukewarm small individual points. The anti-slip agent feels dry and does not stick to normal paper. The foil is sufficiently non-slip. Therefore, a sanitary napkin slips, at that this film forms the water-impermeable layer in the case of the tra not enough.

Claims

1. Hygiene articles, especially sanitary napkins and panty liners, characterized by the use of anti-slip agents.

2. Hygiene article according to claim 1, characterized by an anti slip agent with so little stickiness that a silicone paper is not liable for this.

3. Hygiene article according to claim 1 or 2, characterized by an anti-slip agent with the following composition: 30 to 100 wt .-% of at least one polymer,
0 to 60% by weight of at least one resin,
0 to 30% by weight of at least one wax,
0 to 30% by weight of at least one plasticizer,
0 to 2% by weight of at least one stabilizer,
0 to 2% by weight of at least pigment and
0 to 15% by weight of at least one filler, the percentages adding up to 100.

4. Hygiene article according to claim 1, 2 or 3, characterized net that the anti-slip agent on a poly-α-olefin, in particular another an ethylene / vinyl acetate copolymer, or a chew tschuk, especially styrene copolymers.

5. hygiene article according to at least one of claims 1 to 4, characterized by the full application of a moist anti-slip agent on one side of the hygi enearticles.

6. Process for the manufacture of a hygiene article according to at least one of claims 1 to 5, characterized by the order of Anti-slip agent with rotary screen printing machines.

7. The method according to claim 6, characterized by the order of Anti-slip agent directly on the liquid-permeable cover treatment of the hygiene article.