DE3140292A1 - Process for producing a coloured relief on a sheet-like, fibre-reinforced, plastic-containing support - Google Patents

Process for producing a coloured relief on a sheet-like, fibre-reinforced, plastic-containing support

Info

Publication number
DE3140292A1
DE3140292A1 DE19813140292 DE3140292A DE3140292A1 DE 3140292 A1 DE3140292 A1 DE 3140292A1 DE 19813140292 DE19813140292 DE 19813140292 DE 3140292 A DE3140292 A DE 3140292A DE 3140292 A1 DE3140292 A1 DE 3140292A1
Authority
DE
Germany
Prior art keywords
carrier
cover sheet
relief
cover
pressing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19813140292
Other languages
German (de)
Other versions
DE3140292C2 (en
Inventor
Helmut 6930 Eberbach Albers
Friedrich 6932 Hirschorn Oelkers
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HIRSCHHORN DEKORPLATTENWERK
Original Assignee
HIRSCHHORN DEKORPLATTENWERK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HIRSCHHORN DEKORPLATTENWERK filed Critical HIRSCHHORN DEKORPLATTENWERK
Priority to DE3140292A priority Critical patent/DE3140292C2/en
Publication of DE3140292A1 publication Critical patent/DE3140292A1/en
Application granted granted Critical
Publication of DE3140292C2 publication Critical patent/DE3140292C2/en
Expired legal-status Critical Current

Abstract

For producing a relief-decorated, fibre-reinforced plastic sheet, a plastic-impregnated, transparent top film is used. Layers of colour pigments are incorporated which, upon embossing the decoration, are displaced with the formation of a coloured pattern corresponding to the relief.

Description

Bezeichnung: - Verfahren zur HerstellungDesignation: - Method of manufacture

eines farbigen Reliefs auf einem plattenförmigen, faserverstärkten, kunststoffhaltigen Träger Verfahren zur Herstellung eines farbigen Reliefs auf einem plattenförmigen, faserverstärkten, kunststoffhaltigen Träger Die erfindung betrifft ein Verfahren zur Herstellung eines farbigen Reliefs auf einem plattenförmigen, faserverstärkten, kunststoffhaltigen Träger durch Auflegen einer mit Färbung versehenen Deckfolie aus faserverstärktem, melaminharzhaltigem Kunststoff und eindrücken einer Reliefstruktur in die Deckseite unter gleichzeitigem Verdrängten von Farbe aus den Reliefvertiefungen in die Relieferhöhungen und Verbinden der Deckfolie mit dem Träger.of a colored relief on a plate-shaped, fiber-reinforced, plastic-containing carrier Method of making a colored Reliefs on a plate-shaped, fiber-reinforced, plastic-containing carrier Die The invention relates to a method for producing a colored relief on a plate-shaped, fiber-reinforced, plastic-containing carrier by placing a Colored cover sheet made of fiber-reinforced plastic containing melamine resin and pressing a relief structure into the cover side while simultaneously displacing it of color from the relief depressions in the relief elevations and connecting the cover sheet with the carrier.

Bei einem aus der DE-OS 23 57 831 bekannten Verfahren dieser Art sind Farbpigmente der Färbung in die Kunststoffmasse der Deckfolie eingefüllt. Aufgabe der erfindung ist es, ein Verfahren der eingangs genannten Art so auszugestalten, daß die SinSarbung der Deckfolie einfarbig oder mehrfarbig, einheitlich oder im Muster einfach möglich ist.In a method of this type known from DE-OS 23 57 831 Color pigments of the color are poured into the plastic mass of the cover sheet. task The invention is to design a method of the type mentioned at the outset in such a way that that the SinSarbung of the cover sheet is monochrome or multicolored, uniform or in Pattern is easily possible.

Die erfindung ist dadurch gekennzeichnet, daß die Färbung der Deckfolie auf diese oder unter diese oberflächlich aufgetragen ist und daß die Deckfolie durchscheinend ist.The invention is characterized in that the coloring of the cover sheet is superficially applied to these or under them and that the cover sheet is translucent is.

Da die Färbung der Deckfolie durch oberflächlichen Auftrag erfolgt, kann sie mit bekannten Farbauftragstechniken, zum Beispiel durch Siebdruck, Flexodruck, Tiefdruck, mit Rakel oder ähnlichem Verfahren, aufgebracht werden. Die erfindung macht sich dabei den Umstand zunutze, daß die beim Reliefeinpressen gewünschte Verdrängung der Farbe in die erhabenen Teile des Reliefs auch bei oberflachlich aufgetragener Farbe erfolgt, indem diese von dem verdrängten Kunststoff mitgerissen wird.Since the cover sheet is colored by superficial application, it can be applied using known paint application techniques, for example screen printing, flexographic printing, Gravure printing, with a squeegee or similar method, can be applied. The invention makes use of the fact that the displacement desired when pressing in relief the color in the raised parts of the relief even when applied superficially Color takes place by being carried away by the displaced plastic.

i)ie erfindung hat gegenüber dem Stand der Technik den Vorteil, di relativ kleine Serien in verschiedenen Farbtönungen hergestellt werden können. 1\uf3erdem wird eine exakte Gleichmäßigkeit erreicht und auch die Farbintensität kann variiert werden.i) The invention has the advantage over the prior art, ie relatively small series in different shades can be produced. 1, moreover an exact uniformity is achieved and the color intensity can also be varied will.

Der Parbauftrag auf die Deckfolie kann einseitig odc beidseitig erfolgen, zweckmäßig erfolgt er.einseitig auf der dem Träger zugekehrten Seite, weil dann die Deckfolie die Farbschicht in der fertigen Platte schützt.The parquet can be applied to the cover sheet on one side or on both sides, expediently it takes place on one side on the side facing the wearer, because then the cover film protects the layer of paint in the finished panel.

In manchen Fällen hat der Träger keine für das Eindrücken des Reliefs befriedigende Oberflächenqualität. Dem trägt eine Weiterbildung Rechnung, die dadurch gekennzeichnet ist, daß zwischen Träger und Deckfolie vor dem Verpressen eine Zwischenfolie gelegt ist, die aus faserverstärktem, melaminharzhaltigen Kunststoff besteht, der beim Verpressen in den Plattenverband eingebunden wird.In some cases the carrier does not have one to impress the relief satisfactory surface quality. A further training takes this into account, which thereby is characterized in that an intermediate film between the carrier and cover film before pressing is laid, which consists of fiber-reinforced, melamine resin-containing plastic, the is integrated into the panel structure during pressing.

Das SIelaminharz der Zwischenfolie kann gewünschte Nachsiebigkeit für das einbringen der Reliefstruktur bieten.und ist auch als Verbindungselement zwischen dem Kunststoff des Trägers und dem der Deckfolie günstig. Man kann diese Zwischenfolie einfärben und auf diese eise für die Färbung des Reliefmusters einen Farbhintergrund bieten, der den möglicherweise nicht so ansehnlichen Träger abdeckt. In einem solchen Fall setzt man zweckmäßig eine Zwischenfolie ein, deren Fasern eingefärbt sind. Durch die Fasern wird dann diese Färbung daran gehindert, bei Sinpragen des Reliefs zur Seite zu fließen.The sealing resin of the intermediate film can have the desired compliance for the introduction of the relief structure and is also available as a connecting element between the plastic of the carrier and that of the cover film. You can do this Color the intermediate film and use this to color the relief pattern Provide a color background that covers the possibly not so attractive carrier. In such a case, it is expedient to use an intermediate film, the fibers of which are colored. The fibers then prevent this coloration from occurring in Sinpragen of the relief to flow to the side.

Derjenige Farbauftrag, dessen Farbe beim Einprägen des Reliefs verdrängt werden soll, kann ein- oder beidseitig auP der Deckfolie aufgebracht werden oder aber auf der der Deckfolie zugekehrten Seite der Zwischenfolie. Vorzugsweise w.ird dieser Farbe auf trag nur auf der der Zwischenfolie zugekehrten Seite der Deckfolie oder auf der der Deckfolie zugekehrten Seite der Zwischenfolie aufgetragen, weil dann im fertigen Träger dieser Farbauftrag durch die Deckfolie geschützt ist.The color application whose color is displaced when the relief is impressed is to be applied to one or both sides of the cover film or but on the side of the intermediate film facing the cover film. Preferably w. Will this color to wear only on the side of the cover sheet facing the intermediate sheet or applied to the side of the intermediate film facing the cover film, because then in the finished carrier this paint application is protected by the cover film.

Der >uStrag der Farbpigmente auf die Deckfolie und/oder die Zwischenfolle erfolgt zweckmäßig mit einem den Farbpigmenten beigemischten, flüchtigen Haft- und Bindemittel, zum Beispiel Wasser, das vor dem Verpressen ganz oder teilweise zum größten Teil entfernt ist, was im Falle von naser durch ,ibdampEen geschehen kann.The application of the color pigments to the cover film and / or the intermediate film is expediently carried out with a volatile adhesive and added to the color pigments Binder, for example water, which is wholly or partly used before pressing For the most part removed is what can happen in the case of nasal through, ibdampEen.

Der Träger ist ein solcher, der im Endzustand einen Faserstoff, insbesondere Papierfaserstoff, zum Beispiel in Schichtform, und ein gehartetes Harz, zum Beispiel ein Phenolformaldehydharz, Harnstofformaldehydharz und/oder Melaminformaldehydharz, enthalt und durch Verpressen hergestellt ist. Vorzugsweise besteht der Träger aus mehreren, harzgetränkten Papierbögen, die durch Pressen miteinander verbunden sind.The carrier is one that in the final state is a fiber material, in particular Paper pulp, for example in sheet form, and a hardened resin, for example a phenol formaldehyde resin, urea formaldehyde resin and / or melamine formaldehyde resin, contains and is made by pressing. The carrier preferably consists of several resin-impregnated sheets of paper that are pressed together.

Man kann den zur Herstellung des Trägers erforderlichen Preßvorgang mit dem für die Sinbringung des Reliefs -erforderlichen Freßvorgang zu einem einzigen PreE.vorgang vereinigen.The pressing process required to produce the carrier can be used with the feeding process required for the creation of the relief into a single one Combine the pre-E. process.

Das Fressen kann im Formatpreßverfahren mit Preßstempeln oder im Durchlaufverfahren mit Pre2Jwalzen erfolgen.The milling can be done in the format pressing process with press rams or in the continuous process done with Pre2Jwalzen.

Bei einem faserverstärkten Träger mit einer strukturabhängig gefärbten Reliefstruktur der Deckschicht ist erfindungsgemäß eine Deckschicht vorgesehen, die ungefärbt durchscheinend ist und aus faserverstärktem, melaminharzhaltigen Kunststoff besteht und als Schutzschicht-für die darunterliegenden Farbpigmente dIent.In the case of a fiber-reinforced carrier with a structure-dependent colored In accordance with the invention, a cover layer is provided in relief structure of the cover layer, which is undyed, translucent and made of fiber-reinforced plastic containing melamine resin exists and serves as a protective layer for the underlying color pigments.

Die gesamte kunststofEgetränkte Folienstärke der Deckfolie dient dabei als Schutz des unter der Deckfolie befindlichen rarbaufträges.The entire plastic-soaked film thickness of the cover film is used here to protect the paint job under the cover sheet.

Die erfindung wird nun anhand der beigefügten Zeichnung und einiger Verfahrensbeispiele näher erläutert.The invention will now be based on the accompanying drawing and some Process examples explained in more detail.

In der Zeichnung zeigt: Figur 1 Schichten eines fertigen Trägers in Sxplosionsansicht dargestellt, und Figur 2 in der gleichen Ansicht wie in Figur 1 ein abgecindertes Ausführungsbeispiel.The drawing shows: FIG. 1 layers of a finished carrier in FIG Exploded view shown, and Figure 2 in the same view as in Figure 1 shows an exemplary embodiment.

Der Träger 1 besteht aus mehreren mit Phenolharz oder anderen Polymeren beharzten Papierbögen 2 bis, 5. Uber diesem Träger liegt eine Zwischenfolie 6 aus mit melaminharzhaltigem Sunststoff getränktem Dekorpapier. Di.e Zwischenfoli.e ist nicht durchscheinend und durch Sinfårbung des Dekorpapiers farbig.The carrier 1 consists of several with phenolic resin or other polymers Resin-coated sheets of paper 2 to 5. An intermediate film 6 lies over this carrier Decorative paper impregnated with melamine resin. The intermediate sheet is not translucent and colored by the color of the decor paper.

Über der Zwischenfolie liegt eine durchscheinende Deckfolie 8 aus beharztem Papier, die auf ihrer Unterseite mit einer. Färbung 9 beschichtet ist. Der Träger.1 Wird mit den Folien 6 und 8 verpreßt, was durch die beiden Preßstempel angedeutet ist, die in Pfeilrichtung 12, 13 einwirken. Der von oben auf die Deckseite 15 einwirkende Preßstempel 11 weist eine Reliefstruktur 16 auf, die in die Deckseite eingeprägt wird.A translucent cover sheet 8 lies over the intermediate sheet Resin paper with a. Coloring 9 is coated. The carrier.1 is pressed with the foils 6 and 8, which is done by the two rams is indicated, which act in the direction of arrow 12, 13. The one from above on the cover side 15 acting press ram 11 has a relief structure 16 which is in the cover side is imprinted.

Dabei wird der Farbauftrag der Färbung 9 aus den vertieften Reliefstellen in die erhabenen Reliefstellen verdrängt, indem er durch den zur Seite flief3enden Kunststoff der Deckfolie 8 und/oder der Zwischenfolie 6 mitgerissen wird. Man kann das daß der Farbverdrdngung des Farbauftrages 9 vorbestimmen durch die Fließfähigkeit der eingesetzten Kunststoffe. Für den Farbauftrag 9 ist eine möglichst hohe Verdrängung wünschenswert, um in der Reliefstruktur entsprechende Farbkonturen zu erzielen.The color application of the color 9 from the recessed relief areas displaced into the raised relief areas by being pushed through the flowing to the side Plastic of the cover sheet 8 and / or the intermediate sheet 6 is entrained. One can that the color displacement of the paint application 9 predetermined by the flowability the plastics used. A displacement as high as possible is required for the application of paint 9 desirable in order to achieve corresponding color contours in the relief structure.

Bemerkenswert ist, daß der gesamte Farbauftrag sich unterhalb der durchscheinenden Deckfolie 8 befindet, und in der fertig verpreßten ReRiefornamentplatte durch die Deckfolie vor -äußerer Beschädigung geschützt ist.It is noteworthy that the entire application of paint is below the translucent cover sheet 8 is located, and in the ready-pressed ReRie ornament plate is protected from external damage by the cover film.

In Abänderung des ersten Ausführungsbeispiels aus Figur 1 ist der zu verdrängende rarbauftrag 7 bei dem'zweiten Ausführungsbeispiel nach Figur 2 auf der der Deckfolie 8 zugckehrten Seite der Zwischenfolie 6 aufgetragen, während die l)eckfolie 8 keinen Farbauftrag aufweist.. Weitere Unterschiede bestehen zwischen diesen beiden Ausführungsbeispielen nicht.In a modification of the first exemplary embodiment from FIG. 1, the In the second exemplary embodiment according to FIG applied to the side of the intermediate film 6 facing the cover film 8, while the l) the corner foil 8 does not show any paint. Other differences exist not between these two exemplary embodiments.

Man kann den Träger 1 in einem gesonderten Vorgang vorpressen und erst dann mit den Folien 6 und 8 verpressen und mit dem Ornament versehen. Man kann diese PreSbvorgänge aber auch in einem einzigen Arbeitsgang vornehmen.The carrier 1 can be pre-pressed and in a separate process only then press the foils 6 and 8 and apply the ornament. One can but also carry out these PreSbvorgangs in a single operation.

Nachfolgend sind für einige bevorzugte Ausführungsbeispiele Angaben tabellarisch aufgeführt. Soweit nicht in der Tabelle etwas Besonderes angegeben ist, ist bei diesen kusführungsbeispielen wie im Text zu den Figuren 1 und 2 verfahren. Die Ausführungsbeispiele 1 und 2 der Tabelle entsprechen den Figuren 1 und 2.Information is given below for some preferred exemplary embodiments listed in a table. Unless otherwise specified in the table is, the procedure for these examples is the same as in the text for FIGS. 1 and 2. Embodiments 1 and 2 of the table correspond to FIGS. 1 and 2.

T,i3.LT,., - Teil 1 Beispiel 1 2 TRÄGER: Aufbau 4 beharzte Bögen 4 beharzte Bogen Faserstoff Papier, 40 g . m Papier, 40 g . m-² Kunststoff Phenolharz Phenolharz vorgepreßt nein nein ZWISCHENFOLIE : Aufbau bharzter Bogen beharzter Bogen Faserstoff Papier, 40 g . m 2 Papier, 40 g . m-² Kunststoff Melaminharz Melaminharz Farbauftrag auf nein ja Deckseite Färbung der ja ja Fasern DECKFOLIE: Aufbau harzgetränkter Bogen harzgetrankter Bogen Faserstoff Papier, durchschei- Papier, durchschei--2 -2 nend, 30 g . m -2 nend, 30 g . m Kunststoff Melaminharz Melaminharz rarbauftrag auf nein nein Deckseite Farbauftrag auf ja nein Unterseite TABELLE - Teil 2 1 Beispiel 3 TRÄGER: Aufbau 4 beharzte Bögen beharzte Späne Faserstoff Papier, 100 g . m-2 Holz, 60 .T, i3.LT,., - Part 1 Example 1 2 BEAM: Structure 4 resin-coated arches 4 Resin-coated sheets of fibrous paper, 40 g. m paper, 40 g. m-² plastic phenolic resin Phenolic resin pre-pressed no no INTERMEDIATE FILM: Structure of resin-coated sheets of resinous Sheet of fibrous paper, 40 g. m 2 paper, 40 g. m-² plastic melamine resin melamine resin Color application on no yes cover side Coloring of yes yes fibers COVER FILM: Structure of resin-soaked Sheet of resin-soaked sheet of fibrous material paper, translucent paper, translucent - 2 -2 nend, 30 g. m -2 nend, 30 g. Plastic melamine resin melamine resin paint application on no no cover side Paint application on yes no underside TABEL - Part 2 1 Example 3 CARRIER: Structure of 4 resin-coated sheets of resin-coated wood chips Paper, 100 g. m-2 wood, 60.

Kunststoff Phenolharz Harnstoffharz vorgepreßt nein ja ZWISCHENFOLIE: Aufbau beharzter Bogen beharzter Bogen Faserstoff Papier, 100 g . m 2 Papier, 40 g . m 2 Kunststoff 80 7o Melaminharz Melaminharz 20 % Harnstoffharz Farbauftrag auf nein nein Deckseite Färbung der ja ja Fasern Di'CKFOLIE: Aufbau harzgetränkter Bogen harzgetränkter Bogen Faserstoff Papier, durchschei- Papier, durchscheinend, 18 g . m-² nend, 30 g . m 2 Kunststoff Melaminharz Melaminharz Farbauftrag auf nein nein Deckseite -Farbauftrag auf ja nein Unterseite Für die Beispiele 1 bis 3 sind im Träger Papierstärken von 20 bis 220 g . m 2 einsetzbar. Für den Träger äus Beispiel 4 ist ein Holzanteil von 50 bis 90 % und ein Harzanteil von 5 bis 25 % einsetzbar. Für'die Beispiele 1 bis 4 sind für die Zwischenfolie Papierstärken von 40 bis 150 g . m-² und für die Deckfolie Papierstärken von 18 bis 50 g . m 2 einsetzbar.Plastic phenolic resin urea resin pre-pressed no yes INTERMEDIATE FILM: Structure of resinated sheets of resinated sheets of fibrous paper, 100 g. m 2 paper, 40 g. m 2 plastic 80 7o melamine resin melamine resin 20% urea resin paint application on no no cover side coloring of yes yes fibers THICK FILM: structure of resin-soaked Sheet of resin-impregnated sheet of fibrous paper, translucent paper, translucent, 18 g. m-² nend, 30 g. m 2 plastic melamine resin melamine resin paint application on no no cover side - paint application on yes no underside For the examples 1 to 3 are paper thicknesses of 20 to 220 g in the carrier. m 2 can be used. For the Carrier according to Example 4 is a wood content of 50 to 90% and a resin content of 5 to 25% usable. For examples 1 to 4, paper thicknesses are used for the intermediate film from 40 to 150 g. m-² and paper thicknesses from 18 to 50 g for the cover film. m 2 applicable.

Claims (10)

patentanstrüche: 1. Verfahren zur Merstellung eines farbigen Reliefs auf einem plattenförmigen, Barerverstärkten, kunststoffhaltigen Träger durch Auflegen einer mit Farbung versehenen Deckfolie aus faserverstvrktem, melaminharzhaltigen Kunststoff und Eindrücken einer Reliefstruktur in die Deckseite unter gleichzeitigem Verdrängen von Farbe aus den Reliefvertiefungen in die Relieferhö'<ungen und Verbinden der Deckfolie mit dem Träger, dadurch gekennzeichnet, daß die färbung ( 9 ) der Deckfolie ( 8 ) auf diese oder unter diese oberflächlich aufgetragen ist und daß die Deckfolie durchscheinend ist. Claims for patent: 1. Process for creating a colored relief on a plate-shaped, Barer-reinforced, plastic-containing carrier by placing a colored cover sheet made of fiber-reinforced, melamine resin-containing Plastic and pressing a relief structure into the cover side at the same time Displacement of color from the relief depressions into the relief elevations and Connecting the cover sheet to the carrier, characterized in that the coloring (9) the cover sheet (8) is applied to the surface of this or under it and that the cover sheet is translucent. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß der Farbauftrag auf der Deckfolie ( 8 ) ist und daß die Deckfolie ( d ) mit ihrem Farbauftrag dem Trager ( 1 ) zugekehrt auf diesen aufgelegt wird. 2. The method according to claim 1, characterized in that the paint application on the cover sheet (8) and that the cover sheet (d) with its color application to the Carrier (1) is placed facing on this. 3. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß der rarbauftrag beidseitig auf die Deckfolie aufgetragen ist. 3. The method according to claim 1, characterized in that the paint job is applied to both sides of the cover sheet. 4. Verfahren nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die Farbpigmente der Farbe mit Hilfe eines flüchtigen Haft- und Bindemittels auf die Deckfolie aufgetragen sind, das vor dem Pressen der Deckfolie wenigstens zum größten Teil entfernt wird.4. The method according to any one of claims 1 to 3, characterized in that that the color pigments of the paint with the help of a volatile adhesive and binding agent are applied to the cover sheet, at least before pressing the cover sheet for the most part is removed. 5. Verfahren nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß zwischen Träger ( 1 )und Deckfolie ( 8 ) vor dem Verpressen eine zwischenfolie ( -6 ) gelegt ist, die aus faserverstärktem, meleiminharzhaltigen Kunststoff besteht, der beim Verpressen in den Plattenverband eingebunden wird. 5. The method according to any one of the preceding claims, characterized in, that between the carrier (1) and cover film (8) an intermediate film before pressing (-6) is laid, which consists of fiber-reinforced plastic containing melamine, which is integrated into the panel structure during pressing. 6. Verfahren nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß eine Zwischenfolie ( 6 ) eingesetzt wird, deren Fasern eingefärbt sind.6. The method according to any one of the preceding claims, characterized in, that an intermediate film (6) is used, the fibers of which are colored. 7. Verfahren nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß ein Farbauftrag ( 7 ) auf der der Deckfolie ( 8 ) zugekehrten Seite der Zwischenfolie ( 6 ) vor gesehen ist.7. The method according to any one of the preceding claims, characterized in, that an application of paint (7) on the side of the intermediate film facing the cover film (8) (6) is seen before. 8. Verfahren nach einem der vorhergehenden Anspruche, dadurch gekennzeichnet, daß der Träger aus mehreren, harzgetränkten Papierbögen besteht, die durch Pressen miteinander verbunden sind.8. The method according to any one of the preceding claims, characterized in that that the carrier consists of several resin-impregnated sheets of paper, which by pressing are connected to each other. 9. Verfahren nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß bei Verwendung eines durch Pressen hergestellten Tragers dieser Preßvorgang gleichzeitig mit dem Preßvorgang für die Reliefstruktur vorgenommen wird.9. The method according to any one of the preceding claims, characterized in, that when using a carrier made by pressing this pressing process is carried out simultaneously with the pressing process for the relief structure. 10. Faserverstärkter Träger mit einer strukturabhängig gefärbten Reliefstruktur seiner Deckschicht, dadurch gekennzeichnet, daß eine leckschicht ( 8 ) vorgesehen ist, die ungefärbt durchscheinend ist, aus faserverstärktem, melaminharzhaltigen htmststoff besteht und als Schutzschicht für die darunterliegenen llrbpigmentc dient.10. Fiber-reinforced carrier with a structure-dependent colored relief structure its cover layer, characterized in that a leakage layer (8) is provided is, which is undyed, translucent, made of fiber-reinforced, melamine resin-containing htmststoff and serves as a protective layer for the underlying color pigments.
DE3140292A 1981-10-10 1981-10-10 Process for the production of a colored relief on a plate-shaped, fiber-reinforced, plastic-containing decorative body Expired DE3140292C2 (en)