DE2917563A1

DE2917563A1 - Brown coal drying process - in drying drum after pelletising with mineral oil as dispersing agent and centrifuging

Info

Publication number: DE2917563A1
Application number: DE19792917563
Authority: DE
Inventors: Ryoji Harihara; Minoru Tanaka
Original assignee: Electric Power Development Co Ltd; Nagata Seisakusho Co Ltd
Current assignee: Electric Power Development Co Ltd; Nagata Seisakusho Co Ltd
Priority date: 1979-04-30
Filing date: 1979-04-30
Publication date: 1980-11-13
Also published as: DE2917563C2

Abstract

Low-grade brown coal which occurs in large quantities in the USSR and in Australia is upgraded by mining and stirring together with a dispersing agent in presence of a binder. Pref. dispensing agent is a mineral oil and the pref. binder is the water which is already present in the brown coal. Pellets are dried in a drying drum. This greatly facilitates the drying of the very fine particles of brown coal which also cause environmental dust pollution. The greater density of pellets lowers the transport costs.

Description

"Verfahren zum Trocknen von Braunkohle". "Method for drying lignite".

Es wird ein Verfahren zum Trocknen von Braunkohle vorgeschlagen, wobei die Braunkohle vor dem Trocknen in Pellets mit einem Durchmesser von 2 - 5 mm mit Hilfe eines Naßpelletisierungsverfahrens pelletisiert wird, wobei das Wasser als Bindemittel verwendet wird, das in der Kohle selbst enthalten ist. Die Braunkohle in der Form von getrockneten Pellets hat ein größeres Schüttgewicht als die Braunkohle in der Form von feinen Pulvern, welche erhalten werden, wenn die Braunkohle nach dem Abbau direkt getrocknet wird. Somit trägt sie zur Herabsetzung der Transportkosten bei. Zusätzlich kann die getrocknete Braunkohle in der Form von Pellets af sehr leichte Weise im Vergleich mit pulverförmiger Braunkohle gehandhabt und transportiert werden.A method for drying lignite is proposed, wherein the brown coal into pellets with a diameter of 2 - 5 mm before drying Using a wet pelletizing process, the water is pelletized as Binder is used, which is contained in the coal itself. The brown coal in the form of dried pellets has a greater bulk density than brown coal in the form of fine powders, which are obtained when the brown coal is after is dried directly after the breakdown. Thus, it contributes to lowering the transportation cost at. In addition, the dried lignite can be in the form of pellets af very easily handled and transported in comparison with powdered brown coal will.

Dank der verbesserten Ventilation auf Grund der Spalte zwischen den Pellets ist die Möglichkeit oder die Wahrscheinlichkeit ei ner unerwünschten spontanen Verbrennung weitgehendst reduziert Die vorliegende Erfindung betrifft ein Verfahren zum Trocknen von Braunkohle und insbesondere ein Verfahren zum Trocknen von Braunkohle, mit welchem verschiedene Probleme beim Handhaben und Transportieren von getrockneter Braunkohle beseitigt werden können.Thanks to the improved ventilation due to the gap between the Pellets is the possibility or the probability of an undesirable spontaneous Combustion reduced to a great extent The present invention relates to a method for drying lignite and in particular a method for drying lignite, with which various problems in handling and transporting dried Lignite can be eliminated.

Heutzutage ergibt sich die in der zivilisierten Welt gebraucht Energie hauptsächlich aus Erdöl. 1960 wurde ein zusätzliches Erdölvorkommen von 5 Billionen K1 als Mittel jedes Jahr festgestellt. Dieser zusätzliche Erdölvorrat führt zu einer Erdöllieferung für 35 Jahre, errechnet auf der Basis der augenblick lichen jährlichen Gewinnung. Jedoch wird von nun an das neue Fördern des Erdöles auf Bereiche konzentriert werden, in denen die natürlichen Bedingunyen äußerst schwierig sind. Diese schwierigen Bedingungen beeinträchtigen das Entdecken neuer Erdöllager sowohl hinsichtlich des Förderns als auch des Kapitals.Nowadays the energy used in the civilized world arises mainly from petroleum. 1960 was an additional oil reserve of 5 trillion K1 determined as a mean each year. This additional oil supply leads to a Oil supply for 35 years, calculated on the basis of the current annual Extraction. However, from now on, the new production of oil will be concentrated in areas where the natural conditions are extremely difficult. These difficult ones Conditions affect the discovery of new oil deposits in terms of both Funding as well as the capital.

Selbst wenn in der Zukunft eine zusätzliche Ermittlung von 5 Billionen K1 Erdöl pro Jahr möglich ist, werden die Erdölreserven in den nächsten 20 bzw. 28 Jahren erheblich reduziert sein. Demzufolge wird sich die Welt sowohl technisch als auch finanziell innerhalb einiger Jahrzehnte einer Förderbegrenzung von Erdölgegenüberstehen. So wird es äußerst schwierig sein, Erdöl in einer Menge zu erhalten, die den Energieanforderungen genügt, insbesondere für solche Länder, die lediglich über kleine Erdölvorräte bzw. Quellen verfügen.Even if in the future an additional determination of 5 trillion K1 crude oil per year is possible, the crude oil reserves will be in the next 20 resp. 28 years can be reduced considerably. As a result, the world becomes both technical as well as financially within a few decades, a production limit for crude oil. So it will be extremely difficult To get petroleum in abundance which meets the energy requirements, especially for those countries that only have small oil reserves or sources.

Unter diesen Umständen besteht zunehmender Bedarf für neue Energietechniken, um zukünftige Energiekrisen zu verhindern.Under these circumstances there is an increasing need for new energy technologies, to prevent future energy crises.

Ein Weg besteht in dem Gewinnen und Verwenden von Braunkohle als neue Energiequelle. Die Anwendung von Braunkohle ist trotz ihres niedrigen Preises und ihres häufigen Vorkommens noch nicht entwickelt. Es wird geschätzt, daß es Holzkohle- und Braunkohlelager von 2 Trillionen Tonnen in der Welt gibt. Tatsächlich wurde eine Ablagerung von 2700 Billionen Tonnen Holzkohle und Braunkohle, entsprechend 1350 Billionen Tonnen Kohle bestätigt, von denen 39% zur UdSSR, 34% zu europäischen Ländern und 18% zu Australien gehören.One way is to extract and use lignite as new Energy source. The application of lignite is in spite of its low price and their common occurrence not yet developed. It is estimated that there is charcoal and there are lignite stocks of 2 trillion tons in the world. Indeed it was a deposit of 2,700 trillion tons of charcoal and lignite, accordingly 1350 trillion tons of coal confirmed, of which 39% to the USSR, 34% to European Countries and 18% belong to Australia.

Die beispielsweise unter Australien lagernde Braunkohle enthält 66.7 bis 50% Wasser, o,7 bis 4,9% Asche, 16,8 bis 24,8% flüchtige Bestandteile und 15,8 bis 23,5% feste Kohle.The lignite stored under Australia, for example, contains 66.7 up to 50% water, 0.7 to 4.9% ash, 16.8 to 24.8% volatiles, and 15.8 up to 23.5% solid coal.

Ein wesentlicher Mangel der Braunkohle besteht in dem großen Wassergehalt, Die Transportkosten werden ansteigen, wenn nicht der Wassergehalt zweckmässig entfernt wird. Es ist demzufolge wesentlich, die Braunkohle zu trocknen und zu entwässern, wenn sie für industrielle Zwecke verwendet wird.A major deficiency of lignite is its high water content, The transport costs will increase if the water content is not removed appropriately will. It is therefore essential to dry and dewater the lignite, when used for industrial purposes.

In dem meisten Fällen besteht natürliche Braunkohle in der Form von extrem feinen Partikeln einer Partikelgröße von ungefähr 40 f oder geringer, die miteinander verbunden sind. Demzufolge werden, wenn die natürliche Braunkohle getrocknet und entwässert wird, diese feinen Partikel voneinander gelöst, um die Form von Pulvern einzunehmen, woraus sich verschiedene Probleme wie beispielsweise Umweltverschmutzung durch Ausbreiten der feinen Partikel, Schwierigkeit in der Handhabung u.dgl. ergeben. Zusätzlich ist das Schüttgewicht der Braunkohle in dem getrockneten Zustand so niedrig wie ungefähr o,3, woraus sich eine beträchtliche Steigerung der Transportkosten ergibt. Weiterhin besteht eine Gefahr einer spontanen Verbrennung der Pulver aus Braunkohle während des Transportes und des Lagerns.In most cases, natural lignite exists in the form of extremely fine particles with a particle size of about 40 f or less, the are connected to each other. As a result, if the natural brown coal are dried and dehydrated, these fine particles are detached from each other to take the form of powders ingesting, giving rise to various problems such as pollution by spreading the fine particles, difficulty in handling and the like. In addition, the bulk density of the brown coal in the dried state is so low like about o, 3, resulting in a considerable increase in the cost of transportation results. Furthermore, there is a risk of spontaneous combustion of the powder Lignite during transportation and storage.

Demzufolge ist ein Gegenstand der Erfindung ein Verfahren zum Trocknen von Braunkohle, welches verschiedenç*obenerwähnte Probleme verhüten kann.Accordingly, one object of the invention is a method of drying of lignite, which can prevent various problems mentioned above.

Zu diesem Zweck wird erfindungsgemäss ein Verfahren zum Trocknen von Braunkohle vorgeschlagen, wobei die Braunkohle in Pellets durch ein Naßpelletisierungsverfahren pelletisiert wird und dann die Pellets getrocknet werden.For this purpose, according to the invention, a method for drying Lignite proposed, the lignite in pellets by a wet pelletization process is pelletized and then the pellets are dried.

Das Naßpelletisierverfahren ist ein Verfahren dum Erhalten von Pellets direkt aus der Suspension durch Rühren und Mischen der Bestandteile der dispergierten Phase der Suspension mittels eines zweckmässigen Verfahrens, um ein Trennen der dispergierten Phase und Dispersionsmittels der Suspension voneinander oder ein bevorzugtes Pellitisieren der dispergierten Phase zu bewirken.The wet pelletizing method is a method of obtaining pellets directly from the suspension by stirring and mixing the ingredients of the dispersed Phase of the suspension by means of an expedient method in order to separate the dispersed Phase and dispersant of the suspension from each other or to cause preferential pellitization of the dispersed phase.

Da die Braunkohle "wassersüchtig" ist, ist es vorteilhaft, Wasser als eine Brücke bildende Substanz, d.h. als Bindemittel zu verwenden. Zusätzlich kann, da die Braunkohle selbst unmittelbar nach dem Abbau wasserreich ist, das pellitisieren erzielt werden, ohne ein besonderes Additiv außer Wasser zu verwenden; dies trägt weitgehend zu der Herabsetzung der Kosten bei.Since the lignite is "addicted to water", it is beneficial to use water to be used as a bridge-forming substance, i.e. as a binder. Additionally can, as the lignite itself is rich in water immediately after mining, pellitize it can be achieved without using any particular additive other than water; this carries largely contributes to lowering costs.

Eine organische Flüssigkeit wird als Dispersionsmittel verwendet in einem solchen Fall, in dem Wasser als das Bindemittel verwendet wird. Insbesondere können Mineralöle wie beispielsweise Schweröl, Kerosin u.dgl geeignet als Dispersionsmittel verwendet werden.An organic liquid is used as a dispersant in such a case where water is used as the binder. In particular Mineral oils such as heavy oil, kerosene and the like can be suitable as dispersants be used.

Die Erfindung wird nachfolgend an einem Ausführungsbeispiel an Hand der beigefügten Zeichnung näher erläutert.The invention is illustrated below using an exemplary embodiment the accompanying drawing explained in more detail.

In der Zeichnung ist ein Flußdiagramm gezeigt, welches das erfindungsgemässe Verfahren zum Trocknen von Braunkohle wieder-Gemäß einer bevorzugten Ausführungsform sind die Braunkohle (trocken), ein Dispersionsmittel und ein Bindemittel in einem Verhältnis von 1 : 4 : 2 gemischt und kräftig in einer Rührkammer während einiger Minuten gerührt. Als Ergebnis wird die Braunkohle in Pellets mit einem Durchmesser von ungefähr 5 bis 2 mm pelletisiert, wobei das Wasser als Bindemittel wirkt.In the drawing, a flow chart is shown, which the inventive Method for drying lignite again-According to a preferred embodiment are the brown coal (dry), a dispersing agent and a binding agent in one relationship mixed at 1: 4: 2 and stirred vigorously in a stirring chamber for a few minutes. As a result, the brown coal turns into pellets with a diameter of about 5 pelletized up to 2 mm, the water acting as a binder.

Diese Pellets können leicht von dem Dispersionsmittel mit Hilfe eines Siebes getrennt werden.These pellets can easily be removed from the dispersant with the help of a Sieves are separated.

Die so erhaltenen Pellets mit einem Durchmesser von 5 bis 2 mm werden dann in einer Trockenvorrichtung getrocknet. Da die Pellets ein beträchtliches Gewicht haben, werden sie nicht wie Pulver oder Staub nach dem Trocknen verstreut werden. Zusätzlici können diese getrockneten Pellets mit geringen Kosten gehandhabt und mittels eines Förderbandes o.dgl. transportiert werden, ohne eine besondere Transportvorrichtung verwenden zu müssen.The pellets thus obtained have a diameter of 5 to 2 mm then dried in a dryer. Because the pellets are of considerable weight they will not be scattered like powder or dust after drying. In addition, these dried pellets can be handled and processed at low cost by means of a conveyor belt or the like. be transported without a special transport device having to use.

Die Braunkohlenpellets weisen nach dem Trocknen eine ausreichende Härte auf, und demzufolge tritt während des Handhabens kein Zerkleinern der Pellets auf. Auch ist das Schüttgewicht der Braunkohle in der Form getrockneter Pellets ungefähr 1,4 bis 1,7 mal so hoch wie das der Braunkohle in der Form von Pulvern, die erhalten werden, wenn die abgebaute Braunkohle direkt getrocknet wird. Somit werden die Transportkosten entsprechend reduziert. Zusätzlich schaffen die Spalten in der Braunkohle in der Form von Pelletansammlungen ins DurchmePBr von 5 bis 2 mm gute Ventilationsdurchgänge und unterdrücken natürlichen Temperaturanstieg, so daß die Möglichkeit oder die Chance einer spontanen Verbrennung größtenteils reduziert ist.After drying, the lignite pellets have sufficient Hardness, and accordingly, the pellet does not break down during handling on. Also, the bulk density of lignite is in the form of dried pellets about 1.4 to 1.7 times as high as that of lignite in the form of powder, which are obtained when the extracted lignite is dried directly. Consequently the transport costs are reduced accordingly. Additionally create the crevices in lignite in the form of pellet accumulations in the diamPBr from 5 to 2 mm good ventilation passages and suppress natural temperature rise, so that the possibility or the chance of one spontaneous combustion is largely reduced.

Nach der Zeichnung wird das Kohlematerial in einem Brecher 1 zerkleinert und wird dann einer Vorbereitungskammer 2 zusammen mit einem Mineralöl als Dispersionsmittel zugeführt. Das Material und das Mineralöl werden dann vermischt, verrührt und dann in der Vorbereitungskammer 2 zerkleinert. Das flüssige Gemisch von Braunkohle und Mineralöl wird dann einer Naßpelletisier-Maschine 5 über einen Pumpensumpf 3, eine Zuführpumpe 4 und einen Einlaßdurchgang 6 zugeführt. Das der pelletisierten Vorrichtung zugeführte Gemisch wird dann innig gerührt und zu einem ueberlauf 7 hin bewegt, während sich das Gemisch in Braunkohlepellets in einem Durchmesser von 5 bis 2 mm ändert. Das Gemisch von Pellets und Mineralöl wird dann aus dem Überfluß 7 der Pelletisiervorrichtung gegossen und dann voneinander mit Hilfe eines Siebes 8 abgetrennt.According to the drawing, the coal material is crushed in a crusher 1 and then becomes a preparation chamber 2 together with a mineral oil as a dispersant fed. The material and mineral oil are then mixed, stirred, and then crushed in the preparation chamber 2. The liquid mixture of brown coal and Mineral oil is then a wet pelletizing machine 5 via a pump sump 3, a Feed pump 4 and an inlet passage 6 are supplied. That of the pelletized device The mixture supplied is then thoroughly stirred and moved to an overflow 7, while the mixture is in lignite pellets with a diameter of 5 to 2 mm changes. The mixture of pellets and mineral oil is then extracted from the overflow 7 of the pelletizer poured and then separated from one another with the aid of a sieve 8.

Die Braunkohlenpellets, die von dem Sieb 8 zurückgehalten werden, werden dann einem-Zentrifugalabscheider 9 zugefüErt, welcher das Öl von den Pellets vollständig entfernen kann. Nach der Entfernung des Öls werden die Pellets mit Hilfe einer Trockenvorrichtung 1o getrocknet und dann über einen Förderer 11 zu einem Ort transportiert, an welchem die Pellets gelagert werden sollen.The lignite pellets retained by the sieve 8 are then fed to a centrifugal separator 9, which removes the oil from the pellets can remove completely. After removing the oil, the pellets are using a drying device 1o dried and then via a conveyor 11 to a Transported to the place where the pellets are to be stored.

Zwischenzeitlich wird das in dem Sieb 8 und dem Zentrifugalabscheider 9 getrennte Mineralöl gesammelt und der Vorbereitungs-¢nC Z durch einen blpumpensump! 12 und einer blwiederumlaufpumpe 13 wieder zurückgeführt, so daß es wiederholt als Dispersionsmittel verwendet werden kann.In the meantime, this is in the sieve 8 and the centrifugal separator 9 separate mineral oil collected and the preparation ¢ nC Z through a blpumpensump! 12 and a circulation pump 13 returned again, so that it is repeated as Dispersant can be used.

Obwohl die Erfindung an einem bevorzugten Ausführungsbeispiel erläutert worden ist, sind Änderungen und Modifikationen möglich, ohne sich jedoch dabei vom Kern der Erfindung zu entfernen.Although the invention is explained using a preferred exemplary embodiment changes and modifications are possible without, however, deviating from the Remove essence of the invention.

Claims

Claims 1. A method for drying lignite, thereby characterized that the lignite after its extraction into pellets with the help of a Wet pelletization is pelletized, and that these brown coal pellets are dried will.

2. Process @@@@ Claim 1, Because @@@@@ gekenneke @@ nnets that pelletizing mixing and stirring the lignite together with a dispersing agent the presence of a binder.

3. The method according to claim 2, characterized in that the dispersant is a mineral oil.

4. The method according to claim 2, characterized in that the binder is the water that is naturally present in the lignite after mining.