DE19817726A1 - Catalyst system for production of polypropylene - Google Patents

Catalyst system for production of polypropylene

Info

Publication number
DE19817726A1
DE19817726A1 DE1998117726 DE19817726A DE19817726A1 DE 19817726 A1 DE19817726 A1 DE 19817726A1 DE 1998117726 DE1998117726 DE 1998117726 DE 19817726 A DE19817726 A DE 19817726A DE 19817726 A1 DE19817726 A1 DE 19817726A1
Authority
DE
Germany
Prior art keywords
cyclopentadienyl
different
catalyst system
trifluoroethyl
fluorine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE1998117726
Other languages
German (de)
Inventor
Gerhard Erker
Johannes Ruwwe
Cornelia Fritze
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Basell Polyolefine GmbH
Original Assignee
Aventis Research and Technologies GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Aventis Research and Technologies GmbH and Co KG filed Critical Aventis Research and Technologies GmbH and Co KG
Priority to DE1998117726 priority Critical patent/DE19817726A1/en
Priority to DE59910526T priority patent/DE59910526D1/en
Priority to PCT/EP1999/002562 priority patent/WO1999054367A1/en
Priority to JP2000544705A priority patent/JP2002512275A/en
Priority to US09/673,147 priority patent/US6537943B1/en
Priority to EP99919244A priority patent/EP1084159B1/en
Publication of DE19817726A1 publication Critical patent/DE19817726A1/en
Withdrawn legal-status Critical Current

Abstract

A catalyst system for the polymerization of propylene contains special metallocene(s) with fluorinated substituents, together with cocatalyst(s) and optional support(s) is new. A catalyst system contains: (a) cocatalyst(s); (b) organometallic compound(s) of formula (I); and optionally (c) at least one support; M<1> = a Group 3, 4, 5 or 6 metal, or a lanthanide or actinide; R<1> = H, a 1-30C carbon-containing group or SiR<3>, or 2 or more R<1> groups with the linking atoms may form an optionally substituted 4-24C ring system; R<3> = H or a 1-40C group; R<2> = a fluorine-containing 1-25C alkyl, 1-25C alkenyl, 6-24C aryl, 7-30C aralkyl or 7-30C alkaryl group; r, n = 1, 2, 3, 4 or 5; m, q = 0, 1, 2, 3 or 4; (q+r) = 5 with v = 0, or 4 with v = 1; (m+n) = 5 with v = 0, or 4 with v = 1; s, t = 1-20; L = halogen or a 1-20C hydrocarbon group; x = 1-4, preferably 2 if M<1> = titanium, zirconium or hafnium; Z = a bridging element; v = 0 or 1. An Independent claim is also included for a process for the production of polypropylene by polymerisation of propylene in presence of this catalyst system.

Description

Die vorliegende Erfindung betrifft ein Katalysatorsystem aus Metallocenen mit fluorhaltigen Substituenten, ein Verfahren zur Herstellung sowie seine Verwendung zur Polymerisation von Propylen.The present invention relates to a catalyst system comprising metallocenes fluorine-containing substituents, a process for their preparation and their use for the polymerization of propylene.

Eine der ersten Reaktionen, bei der ein Metallocen der vierten Nebengruppe mit fluorhaltigen Liganden umgesetzt wird, beschreibt die Flash-Pyrolyse von Cp2Ti(C6F5)2 (J. Organomet. Chem. 1963, 1, 98; J. Organomet. Chem. 1964, 2, 206). Dabei tritt die Wanderung eines Fluoratoms ein. Eine wichtige Rolle spielen perfluorierte Liganden für die Stabilisierung elektronendefizienter Metallzentren. Beispielsweise erfolgt die Stabilisierung von kationischen Metallocenen bei der Ziegler-Natta-Polymerisation durch perfluorierte Tetraphenylborate (M. Bochmann, Nachr. Chem. Lab. Techn. 1993, 41, 1220).One of the first reactions in which a metallocene of the fourth subgroup is reacted with fluorine-containing ligands describes the flash pyrolysis of Cp 2 Ti (C 6 F 5 ) 2 (J. Organomet. Chem. 1963, 1, 98; J. Organomet Chem. 1964, 2, 206). The migration of a fluorine atom occurs. Perfluorinated ligands play an important role in the stabilization of electron-deficient metal centers. For example, the stabilization of cationic metallocenes in Ziegler-Natta polymerization is carried out by perfluorinated tetraphenylborates (M. Bochmann, Nachr. Chem. Lab. Techn. 1993, 41, 1220).

Ein elektronendefizientes Metallzentrum zu stabilisieren, gelingt auch mit einem teilweise fluorierten Anion in der Reaktion von Dimethylzirconocenverbindungen mit [PhMe2NH]⁺[B(C6H4F)4]⁻ (Organometallics 1991, 10, 3910). Die Koordination eines F-Atoms des Anions an das Metallzentrum kann mittels 19F-NMR-Spektroskopie nachgewiesen werden.Stabilizing an electron-deficient metal center is also possible with a partially fluorinated anion in the reaction of dimethyl zirconocene compounds with [PhMe 2 NH] ⁺ [B (C 6 H 4 F) 4 ] ⁻ (Organometallics 1991, 10, 3910). The coordination of an F atom of the anion to the metal center can be demonstrated using 19 F NMR spectroscopy.

Durch die Umsetzung von Butadien(zirconocen) mit der Lewissäure B(C6F5)3 entsteht ein Betain, in dem das kationische Metallzentrum durch die Koordination eines Fluoratoms des Pentafluorphenylrestes stabilisiert wird (Angew. Chem. 1995, 107, 1867). In diesem Falle ist die Koordination nur schwach, so daß der labile Ligand durch Monomere verdrängt werden kann.The reaction of butadiene (zirconocene) with the Lewis acid B (C 6 F 5 ) 3 creates a betaine in which the cationic metal center is stabilized by the coordination of a fluorine atom of the pentafluorophenyl radical (Angew. Chem. 1995, 107, 1867). In this case the coordination is weak so that the labile ligand can be displaced by monomers.

Die bisher genannten Verbindungen beschreiben Wechselwirkungen kationischer Metallocene mit aromatischen fluorhaltigen Liganden. Die Verwendung von teilweise fluorierten oder perfluorierten aliphatischen Substituenten an Cyclopentadienylliganden der Metallocene ist nur in Einzelfällen beschrieben.The compounds mentioned so far describe interactions in a more cationic manner Metallocenes with aromatic fluorine-containing ligands. The use of partial  fluorinated or perfluorinated aliphatic substituents Cyclopentadienyl ligands of metallocenes have only been described in isolated cases.

So ist ein Titanocen bekannt, bei dem eine Trifluormethylgruppe an einen Cyclopentadienylliganden gebunden ist (JACS 1986, 108, 4228).A titanocene is known in which a trifluoromethyl group is attached to one Cyclopentadienyl ligands is bound (JACS 1986, 108, 4228).

Eine intramolekulare Koordination eines Fluoratoms an das Metallzentrum ist hier aufgrund der Geometrie kaum möglich.An intramolecular coordination of a fluorine atom to the metal center is here hardly possible due to the geometry.

Es bestand nun die Aufgabe ein Katalysatorsystem, das Metallocene mit fluorhaltigen Substituenten enthält, zur Verfügung zu stellen.The task now was a catalyst system, the metallocenes with contains fluorine-containing substituents.

Gegenstand der vorliegenden Erfindung ist ein Katalysatorsystem, das mindestens ein Metallocen mit fluorhaltigen Substituenten und mindestens eine Cokatalysatorkomponente enthält und gegebenenfalls geträgert sein kann, sowie ein Verfahren zu seiner Herstellung und seine Verwendung in der Polymerisation von Propylen.The present invention relates to a catalyst system which at least a metallocene with fluorine-containing substituents and at least one Contains cocatalyst component and can optionally be supported, and a Process for its preparation and its use in the polymerization of Propylene.

Das erfindungsgemäße Katalysatorsystem enthält
The catalyst system according to the invention contains

  • (a) mindestens einen Cokatalysator,(a) at least one cocatalyst,
  • (b) mindestens eine metallorganische Verbindung der Formel (I)
    worin,
    M1 ein Metall der Gruppe 3, 4, 5 oder 6 des Periodensystems der Elemente sowie Lanthanide oder Actinide bedeutet,
    R1 gleich oder verschieden sind und ein Wasserstoffatom, eine C1-C30- kohlenstoffhaltige Gruppe wie C1-C25-Alkyl, z. B. Methyl, Ethyl, tert.-Butyl, Cyclohexyl oder Octyl, C2-C25-Alkenyl, C3-C15-Alkylalkenyl, C6-C24-Aryl, C5-C24-Heteroaryl wie Pyridyl, Furyl oder Chinolyl, C7-C30-Arylalkyl, C7-C30- Alkylaryl, C1-C12-Alkoxy, SiR3, worin R3 gleich oder verschieden ein Wasserstoffatom oder eine C1-C40-kohlenstoffhaltige Gruppe wie C1-C20- Alkyl, C1-C10-Fluoralkyl, C1-C10-Alkoxy, C6-C20-Aryl, C6-C10-Fluoraryl, C6- C10-Aryloxy, C2-C10-Alkenyl, C7-C40-Arylalkyl, C7-C40-Alkylaryl oder C8- C40-Arylalkenyl sind, oder zwei oder mehrere Reste R1 können so miteinander verbunden sein, daß die Reste R1 und die sie verbindenden Atome des Cyclopentadienylringes ein C4-C24-Ringsystem bilden, welches seinerseits substituiert sein kann,
    R2 gleich oder verschieden sind und ein fluorhaltiges C1-C25-Alkyl, fluorhaltiges C1-C25-Alkenyl, fluorhaltiges C6-C24-Aryl, fluorhaltiges C7-C30-Arylalkyl, fluorhaltiges C7-C30-Alkylaryl bedeuten,
    r, n gleich oder verschieden sind und 1, 2, 3, 4 oder 5 bedeuten,
    m, q gleich oder verschieden sind und 0, 1, 2, 3 oder 4 bedeuten,
    q+r gleich 5 für v = 0, und q+r gleich 4 für v = 1 ist,
    m+n gleich 5 für v = 0, und m+n gleich 4 für v = 1 ist,
    s, t gleich oder verschieden sind und eine ganze Zahl von 1 bis 20 bedeuten,
    L gleich oder verschieden sind und ein Halogenatom oder einen kohlenwasserstoffhaltigen Rest mit 1-20 Kohlenstoffatomen bedeuten, z. B. C1-C20-Alkyl, C2-C20-Alkenyl, C6-C14-Alkoxy, C6-C14-Aryloxy oder C6-C40-Aryl,
    x eine ganze Zahl von 1 bis 4 ist, wobei im Falle von M1 = Ti, Zr oder Hf x bevorzugt gleich 2 ist,
    Z ein verbrückendes Strukturelement zwischen den beiden Cyclopentadienylringen bezeichnet, und v ist 0 oder 1, bedeutet,
    sowie gegebenenfalls    (b) at least one organometallic compound of the formula (I)
    wherein,
    M 1 is a metal from group 3, 4, 5 or 6 of the periodic table of the elements and also lanthanides or actinides,
    R 1 are the same or different and represent a hydrogen atom, a C 1 -C 30 carbon-containing group such as C 1 -C 25 alkyl, e.g. B. methyl, ethyl, tert-butyl, cyclohexyl or octyl, C 2 -C 25 alkenyl, C 3 -C 15 alkylalkenyl, C 6 -C 24 aryl, C 5 -C 24 heteroaryl such as pyridyl, furyl or quinolyl, C 7 -C 30 arylalkyl, C 7 -C 30 alkylaryl, C 1 -C 12 alkoxy, SiR 3 , in which R 3, identical or different, represents a hydrogen atom or a C 1 -C 40 carbon-containing group such as C 1 -C 20 alkyl, C 1 -C 10 fluoroalkyl, C 1 -C 10 alkoxy, C 6 -C 20 aryl, C 6 -C 10 fluoroaryl, C 6 - C 10 aryloxy, C 2 - C 10 alkenyl, C 7 -C 40 arylalkyl, C 7 -C 40 alkylaryl or C 8 - C 40 arylalkenyl, or two or more radicals R 1 may be joined together so that the radicals R 1 and the they connecting atoms of the cyclopentadienyl ring form a C 4 -C 24 ring system, which in turn can be substituted,
    R 2 are the same or different and are a fluorine-containing C 1 -C 25 alkyl, fluorine-containing C 1 -C 25 alkenyl, fluorine-containing C 6 -C 24 aryl, fluorine-containing C 7 -C 30 arylalkyl, fluorine-containing C 7 -C 30 Alkylaryl mean
    r, n are the same or different and are 1, 2, 3, 4 or 5,
    m, q are the same or different and are 0, 1, 2, 3 or 4,
    q + r is 5 for v = 0, and q + r is 4 for v = 1,
    m + n is 5 for v = 0, and m + n is 4 for v = 1,
    s, t are the same or different and are an integer from 1 to 20,
    L are the same or different and represent a halogen atom or a hydrocarbon-containing radical having 1-20 carbon atoms, e.g. B. C 1 -C 20 alkyl, C 2 -C 20 alkenyl, C 6 -C 14 alkoxy, C 6 -C 14 aryloxy or C 6 -C 40 aryl,
    x is an integer from 1 to 4, where M 1 = Ti, Zr or Hf x is preferably 2,
    Z denotes a bridging structural element between the two cyclopentadienyl rings, and v is 0 or 1,
    and if necessary
  • (c) mindestens einen Träger.(c) at least one carrier.

Besonders bevorzugt bedeutet Z eine Gruppe M2R4R5, worin M2 Kohlenstoff, Silizium, Germanium oder Zinn ist und R4 und R5 gleich oder verschieden eine C1- C20-Kohlenwasserstoffgruppe wie C1-C10-Alkyl oder C6-C14-Aryl bedeuten.Particularly preferably, Z is a group M 2 R 4 R 5, wherein M 2 is carbon, silicon, germanium or tin and R 4 and R 5 are identical or different and are a C 1 - C 20 -hydrocarbon group such as C 1 -C 10 alkyl or C 6 -C 14 aryl.

Bevorzugt ist Z gleich CH2, CH2CH2, CH(CH3)CH2, CH(C4H9)C(CH3)2, C(CH3)2, (CH3)2Si, (CH3CH2)2Si, (CH3)((CH3)3C)Si,(CH3)2Ge, (CH3)2Sn, (C6H5)2Si, (C6H5)(CH3)Si, (C6H5)2Ge, (C6H5)2Sn, (CH2)4Si, CH2Si(CH3)2, o-C6H4 oder 2,2'-(C6H4)2.Z is preferably CH 2 , CH 2 CH 2 , CH (CH 3 ) CH 2 , CH (C 4 H 9 ) C (CH 3 ) 2 , C (CH 3 ) 2 , (CH 3 ) 2 Si, (CH 3 CH 2 ) 2 Si, (CH 3 ) ((CH 3 ) 3 C) Si, (CH 3 ) 2 Ge, (CH 3 ) 2 Sn, (C 6 H 5 ) 2 Si, (C 6 H 5 ) (CH 3 ) Si, (C 6 H 5 ) 2 Ge, (C 6 H 5 ) 2 Sn, (CH 2 ) 4 Si, CH 2 Si (CH 3 ) 2 , oC 6 H 4 or 2,2'- (C 6 H 4 ) 2 .

Z kann auch mit einem oder mehreren Resten R1 und/oder R2 ein mono- oder polycyclisches Ringsystem bilden.Z can also form a mono- or polycyclic ring system with one or more radicals R 1 and / or R 2 .

Bevorzugt sind chirale verbrückte Metallocene der Formel I, insbesondere solche in denen v gleich 1 ist und einer oder beide Cyclopentadienylringe so substituiert sind, daß sie einen Indenylring darstellen. Der Indenylring ist bevorzugt substituiert, insbesondere in 2-, 4-, 2,4,5-, 2,4,6-, 2,4,7 oder 2,4,5,6-Stellung, mit C1-C20- kohlenstoffhaltigen Gruppen, wie C1-C10-Alkyl oder C6-C20-Aryl, wobei auch zwei oder mehrere Substituenten des Indenylrings zusammen ein Ringsystem bilden können.Chiral bridged metallocenes of the formula I are preferred, in particular those in which v is 1 and one or both cyclopentadienyl rings are substituted so that they represent an indenyl ring. The indenyl ring is preferably substituted, in particular in the 2-, 4-, 2,4,5-, 2,4,6-, 2,4,7 or 2,4,5,6-position, with C 1 -C 20 - Carbon-containing groups, such as C 1 -C 10 alkyl or C 6 -C 20 aryl, where two or more substituents of the indenyl ring can together form a ring system.

Besonders bevorzugt sind in Formel (I)
M1 ein Metall der Gruppe 4 des Periodensystems der Elemente wie Ti, Zr, oder Hf,
R1 gleich oder verschieden sind und ein Wasserstoffatom, eine C1-C30- kohlenstoffhaltige Gruppe wie C1-C25-Alkyl, insbesondere Methyl, Ethyl, tert.- Butyl, Cyclohexyl oder Octyl, C2-C25-Alkenyl, C3-C15-Alkylalkenyl, C6-C24- Aryl, C5-C24-Heteroaryl wie Pyridyl, Furyl oder Chinolyl, C7-C30-Arylalkyl, C7-C30-Alkylaryl, oder C1-C12-Alkoxy ist, SiR3, worin R3 gleich oder verschieden ein Wasserstoffatom oder eine C1-C40-kohlenstoffhaltige Gruppe wie C1-C20-Alkyl, C1-C10-Fluoralkyl, C1-C10-Alkoxy, C6-C20-Aryl, C6-C10-Fluoraryl, C6-C10-Aryloxy, C2-C10-Alkenyl, C7-C40-Arylalkyl, C7-C40-Alkylaryl oder C8-C40-Arylalkenyl sind, oder zwei oder mehrere Reste R1 können so miteinander verbunden sein, daß die Reste R1 und die sie verbindenden Atome des Cyclopentadienylringes ein C4-C24-Ringsystem bilden, welches seinerseits substituiert sein kann,
R2 gleich oder verschieden sind und ein fluorhaltiges C1-C25-Alkyl fluorhaltiges C1-C25-Alkenyl, fluorhaltiges C6-C24-Aryl, fluorhaltiges C7-C30-Arylalkyl, fluorhaltiges C7-C30-Alkylaryl bedeuten,
r, n gleich oder verschieden sind und 1, 2, 3, 4 oder 5 bedeuten,
m, q gleich oder verschieden sind und 0, 1, 2, 3 oder 4 bedeuten,
q+r gleich 5 für v = 0, und q+r gleich 4 für v = 1 ist,
m+n gleich 5 für v = 0, und m+n gleich 4 für v = 1 ist,
s, t gleich oder verschieden sind und eine ganze Zahl von 1 bis 20 bedeuten,
L gleich oder verschieden sind und ein Halogenatom oder einen kohlenwasserstoffhaltigen Rest mit 1-20 Kohlenstoffatomen bedeuten, insbesondere C1-C20-Alkyl, C2-C20-Alkenyl, C1-C20-Alkoxy, C6-C14-Aryloxy oder C6-C40-Aryl,
x eine ganze Zahl von 1 bis 4 ist, wobei im Falle von M1 = Ti, Zr oder Hf x bevorzugt gleich 2 ist,
Z ein verbrückendes Strukturelement zwischen den beiden Cyclopentadienylringen bezeichnet, und v ist 0 oder 1.Particularly preferred in formula (I)
M 1 is a metal from group 4 of the periodic table of the elements, such as Ti, Zr or Hf,
R 1 are the same or different and represent a hydrogen atom, a C 1 -C 30 carbon-containing group such as C 1 -C 25 alkyl, in particular methyl, ethyl, tert-butyl, cyclohexyl or octyl, C 2 -C 25 alkenyl, C 3 -C 15 alkylalkenyl, C 6 -C 24 aryl, C 5 -C 24 heteroaryl such as pyridyl, furyl or quinolyl, C 7 -C 30 arylalkyl, C 7 -C 30 alkylaryl, or C 1 - Is C 12 alkoxy, SiR 3 , in which R 3, identical or different, represents a hydrogen atom or a C 1 -C 40 carbon-containing group such as C 1 -C 20 alkyl, C 1 -C 10 fluoroalkyl, C 1 -C 10 - Alkoxy, C 6 -C 20 aryl, C 6 -C 10 fluoroaryl, C 6 -C 10 aryloxy, C 2 -C 10 alkenyl, C 7 -C 40 arylalkyl, C 7 -C 40 alkylaryl or Are C 8 -C 40 arylalkenyl, or two or more radicals R 1 can be linked to one another in such a way that the radicals R 1 and the atoms of the cyclopentadienyl ring connecting them form a C 4 -C 24 ring system, which in turn can be substituted,
R 2 are the same or different and are a fluorine-containing C 1 -C 25 alkyl, fluorine-containing C 1 -C 25 alkenyl, fluorine-containing C 6 -C 24 aryl, fluorine-containing C 7 -C 30 arylalkyl, fluorine-containing C 7 -C 30 - Alkylaryl mean
r, n are the same or different and are 1, 2, 3, 4 or 5,
m, q are the same or different and are 0, 1, 2, 3 or 4,
q + r is 5 for v = 0, and q + r is 4 for v = 1,
m + n is 5 for v = 0, and m + n is 4 for v = 1,
s, t are the same or different and are an integer from 1 to 20,
L are identical or different and represent a halogen atom or a hydrocarbon-containing radical having 1-20 carbon atoms, in particular C 1 -C 20 alkyl, C 2 -C 20 alkenyl, C 1 -C 20 alkoxy, C 6 -C 14 - Aryloxy or C 6 -C 40 aryl,
x is an integer from 1 to 4, where M 1 = Ti, Zr or Hf x is preferably 2,
Z denotes a bridging structural element between the two cyclopentadienyl rings, and v is 0 or 1.

Exemplare aber nicht limitierende Beispiele für die erfindungsgemäße metallorganische Verbindung sind:
Bis(η5-2',2',2',-trifluorethyl)cyclopentadienyl)titandichlorid
Bis(η5-1'H,1'H,2'H,2'H-perfluoroctylcyclopentadienyl)titandichlorid
Bis(η5-1'H,1'H,2'H,2'H-perfluorhexylcyclopentadienyl)titandichlorid
Bis(η5-3'-(trifluormethyl)-3',4',4',4'-tetrafluorbutylcyclopentadienyl)titandichlorid
Bis(η5-2',2',2',-trifluorethyl)cyclopentadienyl)zirconiumdichlorid
Bis(η5-1'H,1'H,2'H,2'H-perfluoroctylcyclopentadienyl)zirconiumdichlorid
Bis(η5-1'H,1'H,2'H,2'H-perfluorhexylcyclopentadienyl)zirconiumdichlorid
Bis(η5-3'-(trifluormethyl)-3',4',4',4'-tetrafluorbutyl­ cyclopentadienyl)zirconiumdichlorid
Bis(η5-2',2',2',-trifluorethyl)cyclopentadienyl)hafniumdichlorid
Bis(η5-1'H,1'H,2'H,2,H-perfluoroctylcyclopentadienyl)hafniumdichlorid
Bis(η5-1'H,1'H,2'H,2'H-perfluorhexylcyclopentadienyl)hafniumdichlorid
Bis(η5-3'-(trifluormethyl)-3',4',4',4'-tetrafluorbutylcyclopentadienyl)­ hafniumdichlorid
(η5-2',2',2',-Trifluorethyl)cyclopentadienyl)(η5-cyclopentadienyl)titandichlorid
(η5-1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)(η5-cyclopentadienyl)­ titandichlorid
(η5-1'H,1'H,2'H,2'H-Perfluorhexylcyclopentadienyl)(η5-cyclopentadienyl)­ titandichlorid
(η5-3'-(Trifluormethyl)-3',4',4',4'-tetrafluorbutylcyclopentadienyl)(η5-cyclo­ pentadienyl)titandichlorid
(η5-2',2',2',-Trifluorethyl)cyclopentadienyl)(η5-cyclopentadienyl)­ zirconiumdichlorid
(η5-1'H,1'H,2'H,2'H-Perfluorctylcyclopentadienyl)(η5-cyclopentadienyl)­ zirconiumdichlorid
(η5-1'H,1'H,2'H,2'H-Perfluorhexylcyclopentadienyl)(η5-cyclopentadienyl)­ zirconiumdichlorid
(η5-3'-(Trifluormethyl)-3',4',4',4'-tetrafluorbutylcyclopentadienyl)(η5-cyclo­ pentadienyl)zirconiumdichlorid
(η5-2',2',2',-Trifluorethyl)cyclopentadienyl)(η5-cyclopentadienyl)hafniumdichlorid
(η5-1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)(η5-cyclopentadienyl)­ hafniumdichlorid
(η5-1'H,1'H,2'H,2'H-Perfluorhexylcyclopentadienyl)(η5-cyclopentadienyl)­ hafniumdichlorid
(η5-3'-(Trifluormethyl)-3',4',4',4'-tetrafluorbutylcyclopentadienyl)(η5-cyclo­ pentadienyl)hafniumdichlorid
(η5-2',2',2',-Trifluorethyl)cyclopentadienyl)(η5-pentamethylcyclopentadienyl)­ titandichlorid
(η5-1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)(η5-pentamethyl­ cyclopentadienyl)titandichlorid
(η5-2',2',2',-Trifluorethyl)cyclopentadienyl)(η5pentamethylcyclopentadienyl)­ zirconiumdichlorid
(η5-1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)(η5-pentamethyl­ cyclopentadienyl)zirconiumdichlorid
(η5-2',2',2',-Trifluorethyl)cyclopentadienyl)(η5-pentamethylcyclopentadienyl)­ hafniumdichlorid
(η5-1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)(η5-pentamethyl­ cyclopentadienyl)hafniumdichlorid
(η5-2',2',2',-Trifluorethyl)cyclopentadienyl)(η5-methylcyclopentadienyl)­ titandichlorid
(η5-1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)(η5-methylcyclopentadienyl)­ titandichlorid
(η5-2',2',2',-Trifluorethyl)cyclopentadienyl)(η5-methylcyclopentadienyl)­ zirconiumdichlorid
(η5-1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)(η5-methylcyclopentadienyl)­ zirconiumdichlorid
(η5-2',2',2',-Trifluorethyl)cyclopentadienyl)(η5-methylcyclopentadienyl)­ hafniumdichlorid
(η5-1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)(η5-methylcyclopentadienyl)­ hafniumdichlorid
Dimethylsilandiyl(η5-3-(2',2',2',-trifluorethyl)cyclopentadienyl)(η5-3-methyl­ cyclopentadienyl)titandichlorid
Dimethylsilandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-3- methylcyclopentadienyl)titandichlorid
Dimethylsilandiyl(η5-3-(2',2',2',-trifluorethyl)cyclopentadienyl)(η5-3- methylcyclopentadienyl)zirconiumdichlorid
Dimethylsilandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-3- methylcyclopentadienyl)zirconiumdichlorid
Dimethylsilandiyl(η5-3-(2',2',2',-trifluorethyl)cyclopentadienyl)(η5-3- methylcyclopentadienyl)hafniumdichlorid
Dimethylsilandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-3- methylcyclopentadienyl)hafniumdichlorid
Dimethylsilandiyl(η5-3-(2',2',2',-trifluorethyl)cyclopentadienyl)(η5-cyclo­ pentadienyl)titandichlorid
Dimethylsilandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5cyclo­ pentadienyl)titandichlorid
Dimethylsilandiyl(η5-3-(2',2',2',-trifluorethyl)cyclopentadienyl)(η5-cyclo­ pentadienyl)zirconiumdichlorid
Dimethylsilandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-cyclo­ pentadienyl)zirconiumdichlorid
Dimethylsilandiyl(η5-3-(2',2',2',-trifluorethyl)cyclopentadienyl)(η5-cyclo­ pentadienyl)hafniumdichlorid
Dimethylsilandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-cyclo­ pentadienyl)hafniumdichlorid
1,2-Ethandiyl(η5-3-(2',2',2',-trifluorethyl)cyclopentadienyl)(η5-3-methyl­ cyclopentadienyl)titandichlorid
1,2-Ethandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-3-butyl­ cyclopentadienyl)titandichlorid
1,2-Ethandiyl(η5-3-(2',2',2',-trifluorethyl)cyclopentadienyl)(η5-3-butyl­ cyclopentadienyl)zirconiumdichlorid
1,2-Ethandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-3-butyl­ cyclopentadienyl)zirconiumdichlorid
1,2-Ethandiyl(η5-3-(2',2',2',-trifluorethyl)cyclopentadienyl)(η5-3-butyl­ cyclopentadienyl)hafniumdichlorid
1,2-Ethandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-3-butyl­ cyclopentadienyl)hafniumdichlorid
1,2 Ethandiyl(η5-3-(2',2',2',-trifluorethyl)cyclopentadienyl)(η5-3-methyl­ cyclopentadienyl)titandichlorid
1,2-Ethandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-3-methyl­ cyclopentadienyl)titandichlorid
1,2-Ethandiyl(η5-3-(2',2',2'-trifluorethyl)cyclopentadienyl)(η5-3-methyl­ cyclopentadienyl)zirconiumdichlorid
1,2-Ethandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-3-methyl­ cyclopentadienyl)zirconiumdichlorid
1,2-Ethandiyl(η5-3-(2',2',2'-trifluorethyl)cyclopentadienyl)(η5-3-methyl­ cyclopentadienyl)hafniumdichlorid
1,2-Ethandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-3-methyl­ cyclopentadienyl)hafniumdichlorid
1,2-Ethandiyl(η5-3-(2',2',2'-trifluorethyl)cyclopentadienyl)(η5-cyclopentadienyl)­ titandichlorid
1,2-Ethandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-cyclo­ pentadienyl)titandichlorid
1,2-Ethandiyl(η5-3-(2',2',2'-trifluorethyl)cyclopentadienyl)(η5-cyclopentadienyl)­ zirconiumdichlorid
1,2-Ethandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-cyclo­ pentadienyl)zirconiumdichlorid
1,2-Ethandiyl(η5-3-(2',2',2'-trifluorethyl)cyclopentadienyl)(η5-cyclopentadienyl)­ hafniumdichlorid
1,2-Ethandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-cyclo­ pentadienyl)hafniumdichlorid
1,2-Ethandiyl(η5-3-(2',2',2'-trifluorethyl)cyclopentadienyl)(η5-3-methyl-cyclo­ pentadienyl)titandichlorid
1,2-Ethandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-butyl­ cyclopentadienyl)titandichlorid
1,2-Ethandiyl(η5-3-(2',2',2'-trifluorethyl)cyclopentadienyl)(η5-3-butyl­ cyclopentadienyl)zirconiumdichlorid
1,2-Ethandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-3-butyl­ cyclopentadienyl)zirconiumdichlorid
1,2-Ethandiyl(η5-3-(2',2',2'-trifluorethyl)cyclopentadienyl)(η5-3-butyl­ cyclopentadienyl)hafniumdichlorid
1,2-Ethandiyl(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)(η5-3-butyl­ cyclopentadienyl)hafniumdichlorid
Dimethylsilandiylbis(η5-3-(2',2',2'-trifluorethyl)cyclopentadienyl)-zirconiumdichlorid
Dimethylsilandiylbis(η5-3-(2',2',2'-trifluorethyl)cyclopentadienyl)titandichlorid
Dimethylsilandiylbis(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)­ titandichlorid
Dimethylsilandiylbis(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)­ zirconiumdichlorid
Dimethylsilandiylbis(η5-3-(2',2',2'-trifluorethyl)cyclopentadienyl)hafniumdichlorid
Dimethylsilandiylbis(η5-3-(1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)­ hafniumdichlorid
(η5-2',2',2',-Trifluorethyl)cyclopentadienyl)(η5-butylcyclopentadienyl)titandichlorid
(η5-1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)(η5-butylcyclopentadienyl)­ titandichlorid
(η5-1'H,1'H,2'H,2'H-Perfluorhexylcyclopentadienyl)(η5-butylcyclopentadienyl)­ titandichlorid
(η5-3'-(Trifluormethyl)-3',4',4',4'-tetrafluorbutylcyclopentadienyl)(η5-butyl­ cyclopentadienyl)titandichlorid
(η5-2',2',2'-Trifluorethyl)cyclopentadienyl)(η5-butylcyclopentadienyl)­ zirconiumdichlorid
(η5-1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)(η5-butylcyclopentadienyl)­ zirconiumdichlorid
(η5-1'H,1'H,2'H,2'H-Perfluorhexylcyclopentadienyl)(η5-butylcyclopentadienyl)­ zirconiumdichlorid
(η5-3'-(Trifluormethyl)-3',4',4',4'-tetrafluorbutylcyclopentadienyl)(η5-butyl­ cyclopentadienyl)zirconiumdichlorid
(η5-2',2',2'-Trifluorethyl)cyclopentadienyl)(η5-butylcyclopentadienyl)­ hafniumdichlorid
(η5-1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)(η5-butylcyclopentadienyl)­ hafniumdichlorid
(η5-1'H,1'H,2'H,2'H-Perfluorhexylcyclopentadienyl)(η5-butylcyclopentadienyl)­ hafniumdichlorid
(η5-3'-(Trifluormethyl)-3',4',4',4'-tetrafluorbutylcyclopentadienyl)(η5-butyl­ cyclopentadienyl)hafniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(2',2',2'-trifluorethyl)benzoindenyl)zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(2',2',2'-trifluorethyl)indenyl)zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(2',2',2'-trifluorethyl)-4-(1-naphthyl)-indenyl)­ zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(2',2',2'-trifluorethyl)-4-(2-naphthyl)-indenyl)­ zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(2',2',2'-trifluorethyl)-4-phenyl-indenyl)­ zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(2',2',2'-trifluorethyl)-4-phenyl-indenyl)­ zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(2',2',2'-trifluorethyl)-4,5-benzo-indenyl)­ zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(2',2',2'-trifluorethyl)-4-(4'-tert.-butyl-phenyl)-indenyl)­ zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(1'H,1'H,2'H,2'H-perfluoroctyl)benzoindenyl)­ zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(1'H,1'H,2'H,2'H-perfluoroctyl)indenyl)­ zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(1'H,1'H,2'H,2'H-perfluoroctyl)-4-(1-naphthyl)­ indenyl)zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(1'H,1'H,2'H,2'H-perfluoroctyl)-4-(2-naphthyl)­ indenyl)zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(1'H,1'H,2'H,2'H-perfluoroctyl)-4-phenyl-indenyl)­ zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(1'H,1'H,2'H,2'H-perfluoroctyl)-4-phenyl-indenyl)­ zirkoniumdichlorid
Dimethylsilandiy-bis-(η5-2-(1'H,1'H,2'H,2'H-perfluoroctyl)-4,5-benzo-indenyl)­ zirkoniumdichlorid
Dimethylsilandiyl-bis-(η5-2-(1'H,1'H,2'H,2'H-perfluoroctyl)-4-(4'-tert.-butyl-phenyl)­ indenyl)zirkoniumdichloridExamples but not limiting examples of the organometallic compound according to the invention are:
Bis (η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) titanium dichloride
Bis (η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) titanium dichloride
Bis (η 5 -1'H, 1'H, 2'H, 2'H-perfluorohexylcyclopentadienyl) titanium dichloride
Bis (η 5 -3 '- (trifluoromethyl) -3', 4 ', 4', 4'-tetrafluorobutylcyclopentadienyl) titanium dichloride
Bis (η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) zirconium dichloride
Bis (η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) zirconium dichloride
Bis (η 5 -1'H, 1'H, 2'H, 2'H-perfluorohexylcyclopentadienyl) zirconium dichloride
Bis (η 5 -3 '- (trifluoromethyl) -3', 4 ', 4', 4'-tetrafluorobutyl cyclopentadienyl) zirconium dichloride
Bis (η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) hafnium dichloride
Bis (η 5 -1'H, 1'H, 2'H, 2, H-perfluorooctylcyclopentadienyl) hafnium dichloride
Bis (η 5 -1'H, 1'H, 2'H, 2'H-perfluorohexylcyclopentadienyl) hafnium dichloride
Bis (η 5 -3 '- (trifluoromethyl) -3', 4 ', 4', 4'-tetrafluorobutylcyclopentadienyl) hafnium dichloride
(η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -cyclopentadienyl) titanium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (η 5 -cyclopentadienyl) titanium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorohexylcyclopentadienyl) (η 5 -cyclopentadienyl) titanium dichloride
(η 5 -3 '- (trifluoromethyl) -3', 4 ', 4', 4'-tetrafluorobutylcyclopentadienyl) (η 5 -cyclo pentadienyl) titanium dichloride
(η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -cyclopentadienyl) zirconium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (η 5 -cyclopentadienyl) zirconium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorohexylcyclopentadienyl) (η 5 -cyclopentadienyl) zirconium dichloride
(η 5 -3 '- (trifluoromethyl) -3', 4 ', 4', 4'-tetrafluorobutylcyclopentadienyl) (η 5 -cyclo pentadienyl) zirconium dichloride
(η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -cyclopentadienyl) hafnium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (η 5 -cyclopentadienyl) hafnium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorohexylcyclopentadienyl) (η 5 -cyclopentadienyl) hafnium dichloride
(η 5 -3 '- (trifluoromethyl) -3', 4 ', 4', 4'-tetrafluorobutylcyclopentadienyl) (η 5 -cyclo pentadienyl) hafnium dichloride
(η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -pentamethylcyclopentadienyl) titanium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (η 5 -pentamethyl cyclopentadienyl) titanium dichloride
(η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 pentamethylcyclopentadienyl) zirconium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (η 5 -pentamethyl cyclopentadienyl) zirconium dichloride
(η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -pentamethylcyclopentadienyl) hafnium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (η 5 -pentamethyl cyclopentadienyl) hafnium dichloride
(η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -methylcyclopentadienyl) titanium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (η 5 -methylcyclopentadienyl) titanium dichloride
(η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -methylcyclopentadienyl) zirconium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (η 5 -methylcyclopentadienyl) zirconium dichloride
(η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -methylcyclopentadienyl) hafnium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (η 5 -methylcyclopentadienyl) hafnium dichloride
Dimethylsilanediyl (η 5 -3- (2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -3-methyl cyclopentadienyl) titanium dichloride
Dimethylsilanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -3-methylcyclopentadienyl) titanium dichloride
Dimethylsilanediyl (η 5 -3- (2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -3- methylcyclopentadienyl) zirconium dichloride
Dimethylsilanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -3-methylcyclopentadienyl) zirconium dichloride
Dimethylsilanediyl (η 5 -3- (2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -3- methylcyclopentadienyl) hafnium dichloride
Dimethylsilanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -3-methylcyclopentadienyl) hafnium dichloride
Dimethylsilanediyl (η 5 -3- (2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -cyclopentadienyl) titanium dichloride
Dimethylsilanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 cyclo pentadienyl) titanium dichloride
Dimethylsilanediyl (η 5 -3- (2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -cyclopentadienyl) zirconium dichloride
Dimethylsilanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -cyclopentadienyl) zirconium dichloride
Dimethylsilanediyl (η 5 -3- (2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -cyclopentadienyl) hafnium dichloride
Dimethylsilanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -cyclopentadienyl) hafnium dichloride
1,2-ethanediyl (η 5 -3- (2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -3-methyl cyclopentadienyl) titanium dichloride
1,2-ethanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -3-butyl cyclopentadienyl) titanium dichloride
1,2-ethanediyl (η 5 -3- (2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -3-butyl cyclopentadienyl) zirconium dichloride
1,2-ethanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -3-butyl cyclopentadienyl) zirconium dichloride
1,2-ethanediyl (η 5 -3- (2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -3-butyl cyclopentadienyl) hafnium dichloride
1,2-ethanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -3-butyl cyclopentadienyl) hafnium dichloride
1,2 ethanediyl (η 5 -3- (2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -3-methyl cyclopentadienyl) titanium dichloride
1,2-ethanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -3-methyl cyclopentadienyl) titanium dichloride
1,2-ethanediyl (η 5 -3- (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) (η 5 -3-methyl cyclopentadienyl) zirconium dichloride
1,2-ethanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -3-methyl cyclopentadienyl) zirconium dichloride
1,2-ethanediyl (η 5 -3- (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) (η 5 -3-methyl cyclopentadienyl) hafnium dichloride
1,2-ethanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -3-methyl cyclopentadienyl) hafnium dichloride
1,2-ethanediyl (η 5 -3- (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) (η 5 -cyclopentadienyl) titanium dichloride
1,2-ethanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -cyclopentadienyl) titanium dichloride
1,2-ethanediyl (η 5 -3- (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) (η 5 -cyclopentadienyl) zirconium dichloride
1,2-ethanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -cyclopentadienyl) zirconium dichloride
1,2-ethanediyl (η 5 -3- (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) (η 5 -cyclopentadienyl) hafnium dichloride
1,2-ethanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -cyclopentadienyl) hafnium dichloride
1,2-ethanediyl (η 5 -3- (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) (η 5 -3-methyl-cyclopentadienyl) titanium dichloride
1,2-ethanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -butyl cyclopentadienyl) titanium dichloride
1,2-ethanediyl (η 5 -3- (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) (η 5 -3-butyl cyclopentadienyl) zirconium dichloride
1,2-ethanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -3-butyl cyclopentadienyl) zirconium dichloride
1,2-ethanediyl (η 5 -3- (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) (η 5 -3-butyl cyclopentadienyl) hafnium dichloride
1,2-ethanediyl (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (η 5 -3-butyl cyclopentadienyl) hafnium dichloride
Dimethylsilanediylbis (η 5 -3- (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) zirconium dichloride
Dimethylsilanediylbis (η 5 -3- (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) titanium dichloride
Dimethylsilanediylbis (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) titanium dichloride
Dimethylsilanediylbis (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) zirconium dichloride
Dimethylsilanediylbis (η 5 -3- (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) hafnium dichloride
Dimethylsilanediylbis (η 5 -3- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) hafnium dichloride
(η 5 -2 ', 2', 2 ', - trifluoroethyl) cyclopentadienyl) (η 5 -butylcyclopentadienyl) titanium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (η 5 -butylcyclopentadienyl) titanium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorohexylcyclopentadienyl) (η 5 -butylcyclopentadienyl) titanium dichloride
(η 5 -3 '- (trifluoromethyl) -3', 4 ', 4', 4'-tetrafluorobutylcyclopentadienyl) (η 5 -butyl cyclopentadienyl) titanium dichloride
(η 5 -2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) (η 5 -butylcyclopentadienyl) zirconium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (η 5 -butylcyclopentadienyl) zirconium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorohexylcyclopentadienyl) (η 5 -butylcyclopentadienyl) zirconium dichloride
(η 5 -3 '- (trifluoromethyl) -3', 4 ', 4', 4'-tetrafluorobutylcyclopentadienyl) (η 5 -butyl cyclopentadienyl) zirconium dichloride
(η 5 -2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) (η 5 -butylcyclopentadienyl) hafnium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (η 5 -butylcyclopentadienyl) hafnium dichloride
(η 5 -1'H, 1'H, 2'H, 2'H-perfluorohexylcyclopentadienyl) (η 5 -butylcyclopentadienyl) hafnium dichloride
(η 5 -3 '- (trifluoromethyl) -3', 4 ', 4', 4'-tetrafluorobutylcyclopentadienyl) (η 5 -butyl cyclopentadienyl) hafnium dichloride
Dimethylsilanediylbis (η 5 -2- (2 ', 2', 2'-trifluoroethyl) benzoindenyl) zirconium dichloride
Dimethylsilanediyl bis (η 5 -2- (2 ', 2', 2'-trifluoroethyl) indenyl) zirconium dichloride
Dimethylsilanediyl bis (η 5 -2- (2 ', 2', 2'-trifluoroethyl) -4- (1-naphthyl) -indenyl) zirconium dichloride
Dimethylsilanediyl-bis- (η 5 -2- (2 ', 2', 2'-trifluoroethyl) -4- (2-naphthyl) -indenyl) zirconium dichloride
Dimethylsilanediyl-bis- (η 5 -2- (2 ', 2', 2'-trifluoroethyl) -4-phenyl-indenyl) zirconium dichloride
Dimethylsilanediyl-bis- (η 5 -2- (2 ', 2', 2'-trifluoroethyl) -4-phenyl-indenyl) zirconium dichloride
Dimethylsilanediyl-bis- (η 5 -2- (2 ', 2', 2'-trifluoroethyl) -4,5-benzo-indenyl) zirconium dichloride
Dimethylsilanediyl-bis- (η 5 -2- (2 ', 2', 2'-trifluoroethyl) -4- (4'-tert-butyl-phenyl) -indenyl) zirconium dichloride
Dimethylsilanediylbis (η 5 -2- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) benzoindenyl) zirconium dichloride
Dimethylsilanediyl-bis- (η 5 -2- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) indenyl) zirconium dichloride
Dimethylsilanediylbis (η 5 -2- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) -4- (1-naphthyl) indenyl) zirconium dichloride
Dimethylsilanediylbis- (η 5 -2- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) -4- (2-naphthyl) indenyl) zirconium dichloride
Dimethylsilanediyl-bis- (η 5 -2- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) -4-phenyl-indenyl) zirconium dichloride
Dimethylsilanediyl-bis- (η 5 -2- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) -4-phenyl-indenyl) zirconium dichloride
Dimethylsilandiy-bis- (η 5 -2- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) -4,5-benzo-indenyl) zirconium dichloride
Dimethylsilanediylbis (η 5 -2- (1'H, 1'H, 2'H, 2'H-perfluorooctyl) -4- (4'-tert-butylphenyl) indenyl) zirconium dichloride

Neben den Dichlorid-Verbindungen sind auch die Dimethyl-Verbindungen von Bedeutung.In addition to the dichloride compounds, the dimethyl compounds are also from Meaning.

Die Herstellung der Verbindung nach Formel (I) erfolgt durch Umsetzung eines substituierten Cyclopentadienids (II),das aus der Umsetzung eines Metallocens mit einem fluor- und iodhaltigen Alkyl erhalten wird, mit Metallverbindung (III) und soll durch das nachfolgende Reaktionschema beispielhaft veranschaulicht werden.The compound of formula (I) is prepared by reacting a substituted cyclopentadienide (II) resulting from the reaction of a metallocene with a fluorine and iodine-containing alkyl is obtained, with metal compound (III) and should are exemplified by the following reaction scheme.

In diesem Schema haben M1, R1, R2, L, Z, m, n, q, r, s, t, v und x die gleiche Bedeutung wie oben in Formel (I) angegeben. y ist gleich 1 oder 2 und M ist ein Metall, insbesondere bevorzugt ist Nickel. Die Base ist eine starke Base wie beispielsweise Butyllithium oder Kaliumhydrid. Die Umsetzung erfolgt bei Temperaturen von -50°C bis +150°C, bevorzugt bei 0°C bis 100°C in organischen Lösemitteln, wie z. B. Toluol, Benzol, Methylenchlorid, Tetrachlorkohlenstoff, Tetrahydrofuran, Diethylether und Benzin. Die Umsetzung dauert von 1 min bis zu 20 Tagen. Die Verbindung der Formel (I) kann isoliert oder direkt für weitere Umsetzungen eingesetzt werden. Die Verbindung der Formel (I) kann auch ohne Isolierung von Zwischen- und Endstufen in einer Eintopfreaktion hergestellt werden.In this scheme, M 1 , R 1 , R 2 , L, Z, m, n, q, r, s, t, v and x have the same meaning as given in formula (I) above. y is 1 or 2 and M is a metal, nickel is particularly preferred. The base is a strong base such as butyllithium or potassium hydride. The reaction takes place at temperatures from -50 ° C to + 150 ° C, preferably at 0 ° C to 100 ° C in organic solvents, such as. B. toluene, benzene, methylene chloride, carbon tetrachloride, tetrahydrofuran, diethyl ether and gasoline. The implementation takes from 1 min to 20 days. The compound of formula (I) can be isolated or used directly for further reactions. The compound of formula (I) can also be prepared in a one-pot reaction without isolation of intermediate and final stages.

Das erfindungsgemäße Katalysatorsystem enthält neben mindestens einem Metallocen der Formel (I) zusätzlich mindestens einen Cokatalysator (Komponente a).The catalyst system according to the invention contains at least one Metallocene of the formula (I) additionally at least one cocatalyst (component a).

Die Cokatalysatorkomponente enthält ein Aluminoxan, eine Lewis-Säure oder eine ionische Verbindung, die durch Reaktion mit dem Metallocen dieses in eine kationische Verbindung überführt.The cocatalyst component contains an aluminoxane, a Lewis acid or one ionic compound, which by reaction with the metallocene this in a cationic compound transferred.

Als Aluminoxan wird bevorzugt eine Verbindung der allgemeinen Formel (IV)
A preferred compound of the general formula (IV) is preferred as the aluminoxane

(R AlO)p (IV)
(R AlO) p (IV)

verwendet. Aluminoxane können cylisch wie in Formel (V)
used. Aluminoxanes can be cyclic as in formula (V)

oder linear wie in Formel (VI)
or linear as in formula (VI)

oder vom Cluster-Typ wie in Formel (VII) sein, wie sie in neuerer Literatur beschrieben werden, vgl. JACS 117 (1995), 6465-74, Organometallics 13 (1994),
or of the cluster type as in formula (VII), as described in more recent literature, cf. JACS 117 (1995), 6465-74, Organometallics 13 (1994),

Die Reste R in den Formeln (V), (VI) und (VII) können gleich oder verschieden sein und eine C1-C20-Kohlenwasserstoffgruppe wie eine C1-C6-Alkylgruppe, eine C6- C18-Arylgruppe, Benzyl oder Wasserstoff bedeuten, und p eine ganze Zahl von 2 bis 50, bevorzugt 10 bis 35 bedeuten.The radicals R in the formulas (V), (VI) and (VII) can be the same or different and a C 1 -C 20 hydrocarbon group such as a C 1 -C 6 alkyl group, a C 6 - C 18 aryl group, Are benzyl or hydrogen, and p is an integer from 2 to 50, preferably 10 to 35.

Bevorzugt sind die Reste R gleich und bedeuten Methyl, Isobutyl, n-Butyl, Phenyl oder Benzyl, besonders bevorzugt Methyl.The radicals R are preferably the same and are methyl, isobutyl, n-butyl or phenyl or benzyl, particularly preferably methyl.

Sind die Reste R unterschiedlich, so sind sie bevorzugt Methyl und Wasserstoff, Methyl und Isobutyl oder Methyl und n-Butyl, wobei Wasserstoff oder Isobutyl oder n- Butyl bevorzugt zu 0,01 bis 40% (Zahl der Reste R) enthalten sind.If the radicals R are different, they are preferably methyl and hydrogen, Methyl and isobutyl or methyl and n-butyl, where hydrogen or isobutyl or n- Butyl preferably 0.01 to 40% (number of radicals R) are contained.

Die Herstellung von Aluminoxan erfolgt nach Literaturvorschriften (vgl. Polyhedron 9 (1990) 429 und EP-A-302 424).The production of aluminoxane is carried out according to literature regulations (cf. Polyhedron 9 (1990) 429 and EP-A-302 424).

Unabhängig von der Art der Herstellung ist allen Aluminoxanlösungen ein wechselnder Gehalt an nicht umgesetzter Aluminiumausgangsverbindung, die in freier Form oder als Addukt vorliegt, gemeinsam.Regardless of the type of manufacture, all aluminoxane solutions are one changing content of unreacted aluminum starting compound, which in free form or as an adduct, together.

Als Lewis-Säure werden bevorzugt mindestens eine bor- oder aluminiumorganische Verbindung eingesetzt, die C1-C20-kohlenstoffhaltige Gruppen enthalten, wie verzweigte oder unverzweigte Alkyl- oder Halogenalkyl, wie Methyl, Propyl, Isopropyl, Isobutyl, Trifluormethyl, ungesättigte Gruppen, wie Aryl oder Halogenaryl, wie Phenyl, Tolyl, Benzylgruppen, p-Fluorophenyl, 3,5-Difluorophenyl, Pentachlorophenyl, Pentafluorophenyl, 3,4,5 Trifluorophenyl und 3,5 Di(trifluoromethyl)phenyl.The Lewis acid used is preferably at least one organoboron or organoaluminum compound which contains groups containing C 1 -C 20 carbon, such as branched or unbranched alkyl or haloalkyl, such as methyl, propyl, isopropyl, isobutyl, trifluoromethyl, unsaturated groups, such as Aryl or haloaryl such as phenyl, tolyl, benzyl groups, p-fluorophenyl, 3,5-difluorophenyl, pentachlorophenyl, pentafluorophenyl, 3,4,5 trifluorophenyl and 3,5 di (trifluoromethyl) phenyl.

Beispiele für Lewis-Säuren sind Trifluoroboran, Tris(4-fluorophenyl)boran, Tris(3,5-difluorophenyl)boran, Tris(4-fluoromethylphenyl)boran, Tris(pentafluorophenyl)boran, Tris(3,5-difluorophenyl)boran und/oder Tris(3,4,5- trifluorophenyl)boran, Di(bis(pentafluorophenyl)boroxy)methylalan, Di(bisphenylboroxy)methylalan, Di(bis(pentafluorophenyl)boroxy)isopropylalan.Examples of Lewis acids are trifluoroborane, tris (4-fluorophenyl) borane, Tris (3,5-difluorophenyl) borane, tris (4-fluoromethylphenyl) borane, Tris (pentafluorophenyl) borane, tris (3,5-difluorophenyl) borane and / or tris (3,4,5- trifluorophenyl) borane, di (bis (pentafluorophenyl) boroxy) methylalane, Di (bisphenylboroxy) methylalane, di (bis (pentafluorophenyl) boroxy) isopropylalane.

Als ionische Cokatalysatoren werden bevorzugt Verbindungen eingesetzt, die ein nicht koordinierendes Anion enthalten, wie Tetrakis(pentafluorophenyl)borate, Tetraphenylborate, SbF6-, CF3SO3- oder ClO4-. Als kationisches Gegenion werden Lewis-Basen wie Metyhlamin, Anilin, Dimethylamin, Diethylamin, N-Methylanilin, Diphenylamin, N,N-Dimethylanilin, Trimethylamin, Triethylamin, Tri-n-butylamin, Methyldiphenylamin, Pyridin, p-Bromo-N,N-dimethylanilin, p-Nitro-N,N-dimethylanilin, Triethylphosphin, Triphenylphosphin, Diphenylphosphin, Tetrahydrothiophen und Triphenylcarbenium eingesetzt.Compounds which contain a non-coordinating anion, such as tetrakis (pentafluorophenyl) borates, tetraphenylborates, SbF 6 -, CF 3 SO 3 - or ClO 4 - are preferably used as ionic cocatalysts. Lewis bases such as methylamine, aniline, dimethylamine, diethylamine, N-methylaniline, diphenylamine, N, N-dimethylaniline, trimethylamine, triethylamine, tri-n-butylamine, methyldiphenylamine, pyridine, p-bromo-N, N- are used as the cationic counterion. dimethylaniline, p-nitro-N, N-dimethylaniline, triethylphosphine, triphenylphosphine, diphenylphosphine, tetrahydrothiophene and triphenylcarbenium are used.

Beispiele für solche erfindungsgemäßen ionischen Verbindungen sind
Tributylammoniumtetra(pentafluorophenyl)borat,
Tributylammoniumtetra(pentafluorophenyl)aluminat,
Tributylammoniumtetra(trifluoromethylphenyl)borat,
Tributylammoniumtetra(4-fluorophenyl)borat,
N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)borate,
N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)aluminat,
Di(propyl)ammoniumtetrakis(pentafluorophenyl)borat,
Di(cyclohexyl)ammoniumtetrakis(pentafluorophenyl)borat,
Triphenylcarbeniumtetrakis(pentafluorophenyl)borat,
Triphenylcarbeniumtetrakis(pentafluorophenyl)aluminat,
Ferroceniumtetrakis(pentafluorophenyl)borat und/oder
Ferroceniumtetrakis(pentafluorophenyl)aluminat. Examples of such ionic compounds according to the invention are
Tributylammonium tetra (pentafluorophenyl) borate,
Tributylammonium tetra (pentafluorophenyl) aluminate,
Tributylammonium tetra (trifluoromethylphenyl) borate,
Tributylammonium tetra (4-fluorophenyl) borate,
N, N-dimethylanilinium tetrakis (pentafluorophenyl) borate,
N, N-dimethylanilinium tetrakis (pentafluorophenyl) aluminate,
Di (propyl) ammonium tetrakis (pentafluorophenyl) borate,
Di (cyclohexyl) ammonium tetrakis (pentafluorophenyl) borate,
Triphenylcarbenium tetrakis (pentafluorophenyl) borate,
Triphenylcarbenium tetrakis (pentafluorophenyl) aluminate,
Ferrocenium tetrakis (pentafluorophenyl) borate and / or
Ferrocenium tetrakis (pentafluorophenyl) aluminate.

Bevorzugt sind Triphenylcarbeniumtetrakis(pentafluorophenyl)borat und/oder N,N-Dimethylaniliniumtetrakis(pentafluorophenyl)borat.Triphenylcarbenium tetrakis (pentafluorophenyl) borate and / or are preferred N, N-Dimethylanilinium tetrakis (pentafluorophenyl) borate.

Es können auch Gemische mindestens einer Lewis-Säure und mindestens einer ionischen Verbindung eingesetzt werden.Mixtures of at least one Lewis acid and at least one can also be used ionic compound can be used.

Das erfindungsgemäße Katalysatorsystem kann zusätzlich einen Träger (Komponente c) enthalten. Der Träger kann ein beliebiger organischer oder anorganischer, inerter Feststoff sein, insbesondere ein poröser Träger wie Talk, anorganische Oxide und feinteilige Polymerpulver, wie Polyolefine.The catalyst system according to the invention can additionally be a carrier (Component c) included. The carrier can be any organic or be an inorganic, inert solid, in particular a porous carrier such as talc, inorganic oxides and finely divided polymer powders, such as polyolefins.

Geeignete anorganische Oxide sind beispielsweise Siliciumdioxid, Aluminiumoxid, sowie Mischoxide der beiden Elemente und entsprechende Oxid-Mischungen.Suitable inorganic oxides are, for example, silicon dioxide, aluminum oxide, and mixed oxides of the two elements and corresponding oxide mixtures.

Die verwendeten Trägermaterialien weisen eine spezifische Oberfläche im Bereich von 10 m2/g bis 1000 m2/g, ein Porenvolumen im Bereich von 0,1 ml/g bis 5 ml/g und eine mittlere Partikelgröße von 1 µm bis 500 µm auf. Bevorzugt sind Träger mit einer spezifischen Oberfläche im Bereich von 50 µm bis 500 µm, einem Porenvolumen im Bereich zwischen 0,5 ml/g und 3,5 ml/g und einer mittleren Partikelgröße im Bereich von 5 µm bis 350 µm. Besonders bevorzugt sind Träger mit einer spezifischen Oberfläche im Bereich von 200 m2/g bis 400 m2/g, einem Porenvolumen im Bereich zwischen 0,8 ml/g bis 3,0 ml/g und einer mittleren Partikelgröße von 10 µm bis 200 µm.The carrier materials used have a specific surface area in the range from 10 m 2 / g to 1000 m 2 / g, a pore volume in the range from 0.1 ml / g to 5 ml / g and an average particle size from 1 μm to 500 μm. Carriers with a specific surface area in the range from 50 μm to 500 μm, a pore volume in the range between 0.5 ml / g and 3.5 ml / g and an average particle size in the range from 5 μm to 350 μm are preferred. Carriers with a specific surface area in the range from 200 m 2 / g to 400 m 2 / g, a pore volume in the range between 0.8 ml / g to 3.0 ml / g and an average particle size of 10 μm to 200 are particularly preferred µm.

Wenn das verwendete Trägermaterial von Natur aus einen geringen Feuchtigkeitsgehalt oder Restlösemittelgehalt aufweist, kann eine Dehydratisierung oder Trocknung vor der Verwendung unterbleiben. Ist dies nicht der Fall, wie bei dem Einsatz von Silicagel als Trägermaterial, ist eine Dehydratisierung oder Trocknung empfehlenswert. Der Gewichtsverlust beim Glühen (LOI = Loss on ignition) sollte 1% oder weniger betragen. Die thermische Dehydratisierung oder Trocknung des Trägermaterials kann unter Vakuum und gleichzeitiger Inertgasüberlagerung, wie Stickstoff, erfolgen. Die Trocknungstemperatur liegt im Bereich zwischen 100°C und 1000°C, vorzugsweise zwischen 200°C und 800°C. If the carrier material used is inherently low Moisture content or residual solvent content can cause dehydration or do not dry before use. If not, as with the use of silica gel as a carrier material is dehydration or Drying recommended. The weight loss when glowing (LOI = Loss on ignition) should be 1% or less. Thermal dehydration or Drying of the carrier material can be carried out under vacuum and simultaneously Inert gas blanket such as nitrogen. The drying temperature is in the Range between 100 ° C and 1000 ° C, preferably between 200 ° C and 800 ° C.  

Der Parameter Druck ist in diesem Fall nicht entscheidend. Die Dauer des Trocknungsprozesses kann zwischen 1 und 24 Stunden betragen. Kürzere oder längere Trocknungsdauern sind möglich, vorausgesetzt, daß unter den gewählten Bedingungen die Gleichgewichtseinstellung mit den Hydroxylgruppen auf der Trägeroberfläche erfolgen kann, was normalerweise zwischen 4 und 8 Stunden erfordert.In this case, the pressure parameter is not critical. The duration of the Drying process can take between 1 and 24 hours. Shorter or longer drying times are possible, provided that among the selected Conditions the equilibrium with the hydroxyl groups on the Carrier surface can be done, which is usually between 4 and 8 hours required.

Eine Dehydratisierung oder Trocknung des Trägermaterials ist auch auf chemischem Wege möglich, indem das adsorbierte Wasser und die Hydroxylgruppen auf der Oberfläche mit geeigneten Modifizierungsmitteln zur Reaktion gebracht werden. Durch die Umsetzung mit dem Modifizierungsmittel können die Hydroxylgruppen vollständig oder auch teilweise in eine Form überführt werden, die zu keiner negativen Wechselwirkung mit den katalytisch aktiven Zentren führen. Geeignete Modifizierungsmittel sind beispielsweise Siliciumhalogenide und Silane, wie Siliciumtetrachlorid, Chlortrimethylsilan, Dimethylaminotrichlorsilan, Aminen wie Phenyldimethylamin, Pyridin oder metallorganische Verbindungen von Aluminium-, Bor und Magnesium wie Trimethylaluminium, Triethylaluminium, Triisobutylaluminium, Triethylboran, Dibutylmagnesium. Die chemische Dehydratisierung oder Modifizierung des Trägermaterials kann dadurch erfolgen, daß man unter Luft- und Feuchtigkeitsausschluß eine Suspension des Trägermaterials in einem geeigneten Lösemittel mit dem Modifizierungsmittel in reiner Form oder gelöst in einem geeigneten Lösemittel zur Reaktion bringt.Dehydration or drying of the carrier material is also chemical Possible by placing the adsorbed water and the hydroxyl groups on the Surface are reacted with suitable modifiers. The hydroxyl groups can be reacted with the modifier completely or partially converted into a form that does not lead to any lead to negative interaction with the catalytically active centers. Suitable Modifying agents are, for example, silicon halides and silanes, such as Silicon tetrachloride, chlorotrimethylsilane, dimethylaminotrichlorosilane, amines such as Phenyldimethylamine, pyridine or organometallic compounds of aluminum, Boron and magnesium such as trimethyl aluminum, triethyl aluminum, Triisobutylaluminium, triethylborane, dibutylmagnesium. The chemical Dehydration or modification of the carrier material can take place by that a suspension of the air and moisture Carrier material in a suitable solvent with the modifier in pure form or dissolved in a suitable solvent to react.

Geeignete Lösemittel sind aliphatische oder aromatische Kohlenwasserstoffe, wie Pentan, Hexan, Heptan, Toluol oder Xylol. Die Modifizierung erfolgt bei Temperaturen zwischen 25°C und 120°C, bevorzugt zwischen 50°C und 70°C. Höhere und niedrigere Temperaturen sind möglich. Die Dauer der Reaktion beträgt zwischen 30 Minuten und 20 Stunden, bevorzugt 1 bis 5 Stunden. Nach dem vollständigen Ablauf der chemischen Dehydratisierung wird das Trägermaterial durch Filtration unter Inertbedingungen isoliert, ein- oder mehrmals mit geeigneten inerten Lösemitteln wie sie bereits zuvor beschrieben worden sind gewaschen und anschließend im Inertgasstrom oder am Vakuum getrocknet.Suitable solvents are aliphatic or aromatic hydrocarbons, such as Pentane, hexane, heptane, toluene or xylene. The modification takes place at Temperatures between 25 ° C and 120 ° C, preferably between 50 ° C and 70 ° C. Higher and lower temperatures are possible. The duration of the reaction is between 30 minutes and 20 hours, preferably 1 to 5 hours. After this The complete process of chemical dehydration is carried out by the carrier material Filtration isolated under inert conditions, one or more times with suitable inert Solvents as already described have been washed and then dried in an inert gas stream or under vacuum.

Organische Trägermaterialien wie feinteilige Polyolefinpulver, wie Polyethylen, Polypropylen oder Polystyrol, können auch verwendet werden und sollten ebenfalls vor dem Einsatz von anhaftender Feuchtigkeit, Lösemittelresten oder anderen Verunreinigungen durch entsprechende Reinigungs- und Trocknungsoperationen befreit werden.Organic carrier materials such as finely divided polyolefin powders, such as polyethylene, Polypropylene, or polystyrene, can and should also be used  before the use of adhering moisture, solvent residues or others Contamination by appropriate cleaning and drying operations be freed.

Zur Darstellung des geträgerten Katalysatorsystems wird mindestens eine der oben beschriebenen Metallocenkomponenten, mindestens eine Cokatalysatorkomponente und mindestens ein Trägermaterial in einem geeigneten Lösemittel in beliebiger Reihenfolge in Kontakt gebracht. Das Lösemittel wird entfernt und das resultierende geträgerte Metallocen-Katalysatorsystem getrocknet, um sicherzustellen, daß das Lösemittel vollständig oder zum größten Teil aus den Poren des Trägermaterials entfernt wird. Der geträgerte Katalysator wird als frei fließendes Pulver erhalten.At least one of the above is used to illustrate the supported catalyst system described metallocene components, at least one cocatalyst component and at least one carrier material in a suitable solvent in any Order contacted. The solvent is removed and the resulting one supported metallocene catalyst system dried to ensure that the Solvent completely or for the most part from the pores of the carrier material Will get removed. The supported catalyst is obtained as a free-flowing powder.

Beispiele für geeignete Lösemittel umfassen Alkane wie Pentan, Isopentan, Hexan, Heptan, Octan, und Nonan, Cycloalkane wie Cyclopentan und Cyclohexan, und Aromaten wie Benzol, Toluol. Ethylbenzol und Diethylbenzol. Ganz besonders bevorzugt ist Toluol.Examples of suitable solvents include alkanes such as pentane, isopentane, hexane, Heptane, octane, and nonane, cycloalkanes such as cyclopentane and cyclohexane, and Aromatics such as benzene, toluene. Ethylbenzene and diethylbenzene. Most notably toluene is preferred.

Die bei der Präparation des geträgerten Katalysatorsystems eingesetzten Mengen an Cokatalysator und Metallocen können über einen weiten Bereich variiert werden. Bevorzugt wird ein molares Verhältnis von Cokatalysator zum Übergangsmetall im Metallocen von 1 : 1 bis 1000 : 1 eingestellt, ganz besonders bevorzugt ein Verhältnis von 1 : 1 bis 400 : 1.The amounts used in the preparation of the supported catalyst system of cocatalyst and metallocene can be varied over a wide range. A molar ratio of cocatalyst to transition metal is preferred Metallocene adjusted from 1: 1 to 1000: 1, very particularly preferably one Ratio from 1: 1 to 400: 1.

Das erfindungsgemäß dargestellte geträgerte Katalysatorsystem kann entweder direkt zur Polymerisation von Propylen eingesetzt oder vor seiner Verwendung in einem Polymerisationsprozeß mit einem oder mehreren olefinischen Monomeren vorpolymerisiert werden. Die Ausführung der Vorpolymerisation von geträgerten Katalysatorsystemen ist in WO 94/28034 beschrieben.The supported catalyst system shown according to the invention can either used directly for the polymerization of propylene or before its use in a polymerization process with one or more olefinic monomers be prepolymerized. Execution of prepolymerization of supported Catalyst systems are described in WO 94/28034.

Als Additiv kann während oder nach der Herstellung des geträgerten Katalysatorsystems eine geringe Menge eines α-Olefins, wie Styrol, als aktivitätssteigernde Komponente oder eines Antistatikums, wie in US Serial No. 08/365280 beschrieben, zugesetzt werden. The additive can be used during or after the preparation of the carrier Catalyst system as a small amount of an α-olefin, such as styrene activity-enhancing component or an antistatic, as in US Serial No. 08/365280 described, are added.  

Zudem wird ein Verfahren zur Herstellung von Polypropylen durch Polymerisation von Propylen in Gegenwart des erfindungsgemäßen Katalysators beschrieben. Die Polymerisation kann eine Homo- oder eine Copolymerisation sein.There is also a process for the production of polypropylene by polymerization of propylene in the presence of the catalyst of the invention. The Polymerization can be a homo- or a copolymerization.

Insbesondere wird Propylen homo- oder copolymerisiert.In particular, propylene is homo- or copolymerized.

Die Polymerisation wird bevorzugt bei einer Temperatur von -60 bis 300°C, besonders bevorzugt 30 bis 250°C, durchgeführt. Der Druck beträgt 0,5 bis 2500 bar, bevorzugt 2 bis 1500 bar.The polymerization is preferred at a temperature of -60 to 300 ° C, particularly preferably 30 to 250 ° C, carried out. The pressure is 0.5 to 2500 bar, preferably 2 to 1500 bar.

Die Polymerisation kann kontinuierlich oder diskontinuierlich, ein- oder mehrstufig, in Lösung, in Suspension, in der Gasphase oder in einem überkritischem Medium durchgeführt werden.The polymerization can be carried out continuously or batchwise, in one or more stages Solution, in suspension, in the gas phase or in a supercritical medium be performed.

Das geträgerte System kann als Pulver oder noch Lösemittel behaftet wieder resuspendiert und als Suspension in einem inerten Suspensionsmittel in das Polymerisationssystem eindosiert werden.The supported system can again be contaminated as a powder or solvent resuspended and as a suspension in an inert suspension medium in the Polymerization system be metered.

Mit Hilfe des erfindungsgemäßen Katalysators kann eine Vorpolymerisation erfolgen. Zur Vorpolymerisation wird bevorzugt das in der Polymerisation eingesetzte Propylen verwendet.A prepolymerization can be carried out using the catalyst according to the invention. For the prepolymerization, the propylene used in the polymerization is preferred used.

Zur Herstellung von Polypropylen mit breiter Molekulargewichtsverteilung werden bevorzugt Katalysatorsysteme verwendet, die zwei oder mehr verschiedene Metallocene enthalten.For the production of polypropylene with a broad molecular weight distribution preferably uses catalyst systems that are two or more different Contain metallocenes.

Zur Entfernung von im Propylen vorhandenen Katalysatorgiften ist eine Reinigung mit einem Aluminiumalkyl, beispielsweise Trimethylaluminium, Triethylaluminium oder Triisobutylaluminium vorteilhaft. Diese Reinigung kann sowohl im Polymerisationssystem selbst erfolgen, oder das Propylen wird vor der Zugabe in das Polymerisationssystem mit der Al-Verbindung in Kontakt gebracht und anschließend wieder getrennt. Cleaning is required to remove catalyst poisons present in the propylene with an aluminum alkyl, for example trimethyl aluminum, triethyl aluminum or triisobutyl aluminum advantageous. This cleaning can be done both in Polymerization system itself, or the propylene is added in before brought the polymerization system into contact with the Al compound and then separated again.  

Als Molmassenregler und/oder zur Steigerung der Aktivität wird, falls erforderlich, Wasserstoff zugegeben. Der Gesamtdruck im Polymerisationssystem beträgt 0,5 bis 2500 bar, bevorzugt 2 bis 1500 bar.As a molecular weight regulator and / or to increase the activity, if necessary, Hydrogen added. The total pressure in the polymerization system is 0.5 to 2500 bar, preferably 2 to 1500 bar.

Dabei wird die erfindungsgemäße Verbindung in einer Konzentration, bezogen auf das Übergangsmetall von bevorzugt 10-3 bis 10-8, vorzugsweise 10-4 bis 10-7 mol Übergangsmetall pro dm3 Lösemittel bzw. pro dm3 Reaktorvolumen angewendet.The compound according to the invention is used in a concentration, based on the transition metal, of preferably 10 -3 to 10 -8 , preferably 10 -4 to 10 -7 mol, transition metal per dm 3 solvent or per dm 3 reactor volume.

Vor Zugabe des Katalysatorsystems (enthaltend mindestens ein erfindungsgemäßes Metallocen) kann zusätzlich eine andere Alkylaluminiumverbindung wie beispielsweise Trimethylaluminium, Triethylaluminium, Triisobutylaluminium, Trioctylaluminium oder Isoprenylaluminium zur Inertisierung des Polymerisationssystems (beispielsweise zur Abtrennung vorhandener Katalysatorgifte im Propylen) in den Reaktor oder zum Katalysatorsystem gegeben werden. Diese wird in einer Konzentration von 100 bis 0,01 mmol Al pro kg Reaktorinhalt dem Polymerisationssystem zugesetzt. Bevorzugt werden Triisobutylaluminium und Triethylaluminium in einer Konzentration von 10 bis 01 mmol Al pro kg Reaktorinhalt eingesetzt. Dadurch kann bei der Synthese eines geträgerten Katalysatorsystems das molare Al/M-Verhältnis klein gewählt werden.Before adding the catalyst system (containing at least one according to the invention Metallocene) can also be another alkyl aluminum compound such as for example trimethyl aluminum, triethyl aluminum, triisobutyl aluminum, Trioctylaluminium or Isoprenylaluminium for inerting the Polymerization system (for example to separate existing Catalyst poisons in propylene) added to the reactor or to the catalyst system become. This is in a concentration of 100 to 0.01 mmol Al per kg Reactor contents added to the polymerization system. To be favoured Triisobutyl aluminum and triethyl aluminum in a concentration of 10 to 01 mmol Al used per kg reactor content. This allows the synthesis of a supported catalyst system, the molar Al / M ratio can be chosen small.

Beispiel 1example 1 Synthese von Bis(2',2',2'-trifluorethyl)cyclopentadienyl)titandichloridSynthesis of bis (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) titanium dichloride Synthese von NickelocenSynthesis of nickelocene

29.4 g Nickelpulver werden in 400 ml Dimethoxyethan suspendiert und unter Rühren mit 27.3 ml Brom versetzt. Man läßt 1 Stunde (h) rühren und entfernt das Lösemittel im Ölpumpenvakuum. Der erhaltene braune Rückstand wird unter Eiskühlung mit 400 ml Diethylamin aufgenommen und mit 98 ml frisch destilliertem Cyclopentadien versetzt. Die Suspension färbt sich grün. Nach 12 h Rühren bei Raumtemperatur werden Lösemittelreste im Ölpumpenvakuum entfernt und das Produkt mittels Soxhlet-Extraktion mit 700 ml Petrolether isoliert.
Ausbeute: 74 g (78%)
Schmelzpunkt: 173.0°C29.4 g of nickel powder are suspended in 400 ml of dimethoxyethane and 27.3 ml of bromine are added with stirring. The mixture is stirred for 1 hour (h) and the solvent is removed under an oil pump vacuum. The brown residue obtained is taken up in ice-cooling with 400 ml of diethylamine and 98 ml of freshly distilled cyclopentadiene are added. The suspension turns green. After stirring for 12 h at room temperature, solvent residues are removed in an oil pump vacuum and the product is isolated by Soxhlet extraction with 700 ml of petroleum ether.
Yield: 74 g (78%)
Melting point: 173.0 ° C

Synthese von 2',2',2'-TrifluorcyclopentadienSynthesis of 2 ', 2', 2'-trifluorocyclopentadiene

6,87 g Nickelocen und 9.51 g Triphenylphosphin werden in 60 ml Diethylether gelöst und mit 3,56 ml 2,2,2-Trifluorethyliodid versetzt. Die Lösung färbt sich violett und wird 48 h gerührt. Danach kondensiert man den Inhalt des Schlenkgefäßes in eine auf -196°C gekühlte Vorlage und destilliert aus dieser solange den Diethylether bei einer Badtemperatur von 45°C ab, bis die Temperatur des Destillats nicht mehr bei 35°C liegt und bestimmt mittels 1H-NMR den Anteil an verbliebenem Diethylether (1.95 eq).
Ausbeute: 8.95 g (81%).
1H-NMR: ([D]-Chloroform; 200.1 MHz; 300 K): d = 6.46 (m, 6H, = CH); 3.15 (m, 4H, CH2); 3.00 (m, 4H,CH2 (Ring), (Das Produkt besteht aus zwei Doppelbindungsisomeren)) ppm.
(Zusätzlich treten die Resonanzen des enthaltenen Diethylethers auf: 3.45 (q); 1.18 (t) ppm).
19F-NMR: ([D]-Chloroform; 282,4 MHz; 300K): d = -65,7 (t, 3JHF = 11.4Hz); -65.9 (t, 3JHF = 11.5H4 ppm.6.87 g of nickelocene and 9.51 g of triphenylphosphine are dissolved in 60 ml of diethyl ether and 3.56 ml of 2,2,2-trifluoroethyl iodide are added. The solution turns violet and is stirred for 48 h. The contents of the Schlenk vessel are then condensed into a receiver cooled to -196 ° C. and the diethyl ether is distilled off at a bath temperature of 45 ° C. until the temperature of the distillate is no longer at 35 ° C. and determined using 1 H NMR the proportion of remaining diethyl ether (1.95 eq).
Yield: 8.95 g (81%).
1 H NMR: ([D] chloroform; 200.1 MHz; 300 K): d = 6.46 (m, 6H, = CH); 3.15 (m, 4H, CH 2); 3.00 (m, 4H, CH 2 (ring), (The product consists of two double bond isomers)) ppm.
(In addition, the resonances of the contained diethyl ether occur: 3.45 (q); 1.18 (t) ppm).
19 F NMR: ([D] chloroform; 282.4 MHz; 300K): d = -65.7 (t, 3 J HF = 11.4Hz); -65.9 (t, 3 J HF = 11.5H4 ppm.

Synthese von Bis(2',2',2'-trifluorethyl)cyclopentadienyl)titandichloridSynthesis of bis (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) titanium dichloride

14.6 mmol 2',2',2'-Trifluorethylcyclopentadien werden in Tetrahydrofuran bei -78°C mit 8.8 ml 1.65M Butyllithium-Lösung versetzt. Parallel dazu werden 0.72 ml Titantetrachlorid in 50 ml Toluol gelöst und bei -78°C langsam mit 40 ml Tetrahydrofuran versetzt. Die erhaltene Suspension wird bei -78°C zu obiger Lösung gegeben. Man läßt langsam auf Raumtemperatur erwärmen, entfernt das Lösemittel im Ölpumpenvakuum und extrahiert das Produkt mit Methylenchlorid aus dem Rückstand.
Ausbeute: 1g (37%)
1H-NMR: ([D6]-Benzol; 200.1 MHz; 300 K): d = 5.91 (pt, 4H, RCpH); 5.28 (pt, 4H, RCpH); 3.52 (q, 3JFH = 11.0 Hz, 4H,1'-H) ppm.
19F-NMR: ([D6]-Benzol; 284.1 MHz; 300K): d = -65.17 (s (1H-entkoppelt)); (t, 3JHF=11.5Hz) (nicht entkoppelt)) ppm.14.6 mmol of 2 ', 2', 2'-trifluoroethylcyclopentadiene are added in tetrahydrofuran at -78 ° C with 8.8 ml of 1.65M butyllithium solution. At the same time, 0.72 ml of titanium tetrachloride are dissolved in 50 ml of toluene, and 40 ml of tetrahydrofuran are slowly added at -78 ° C. The suspension obtained is added to the above solution at -78 ° C. The mixture is allowed to warm slowly to room temperature, the solvent is removed in an oil pump vacuum and the product is extracted from the residue with methylene chloride.
Yield: 1g (37%)
1 H-NMR: ([D 6 ] -benzene; 200.1 MHz; 300 K): d = 5.91 (pt, 4H, RCpH); 5.28 (pt, 4H, RCpH); 3.52 (q, 3 J FH = 11.0 Hz, 4H, 1'-H) ppm.
19 F NMR: ([D 6 ] benzene; 284.1 MHz; 300K): d = -65.17 (s (1H decoupled)); (t, 3 JHF = 11.5Hz) (not decoupled)) ppm.

Beispiel 2Example 2 Synthese von Bis(2',2',2'-trifluorethyl)cyclopentadienyl)zirconiumdichloridSynthesis of bis (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) zirconium dichloride

11.7 mmol 2',2',2'-Trifluorethylcyclopentadien aus Beispiel 1 werden in 80 ml Tetrahydrofuran bei -78°C mit 7.1 ml 1.65M Butyllithium-Lösung in Hexan versetzt. Zu der erhaltenen Lösung gibt man bei -78°C 2.22 g Zirconiumtetrachlorid-THF- Addukt, gelöst in 30 ml Tetrahydrofuran. Man läßt langsam auf Raumtemperatur erwärmen, entfernt das Lösemittel im Ölpumpenvakuum und extrahiert das Produkt mit Methylenchlorid aus dem Rückstand. Ausbeute: 1.89 g (70%)
1H-NMR: ([D6]-Benzol; 300.1 MHz; 300 K): d = 5.82 (pt, 4H, RCpH); 5.39 (pt, 4H, RCpH); 3.24 (q, 3JFH = 12.5 Hz, 4H, 1'-H) ppm.
19F-NMR: ([D6]-Benzol; 284.1 MHz; 300K): d = -65.14 (s (1H-entkoppelt)); (t, 3JHF = 11.5Hz) (nicht entkoppelt)) ppm.11.7 mmol of 2 ', 2', 2'-trifluoroethylcyclopentadiene from Example 1 are mixed in 80 ml of tetrahydrofuran at -78 ° C with 7.1 ml of 1.65M butyllithium solution in hexane. 2.22 g of zirconium tetrachloride-THF adduct, dissolved in 30 ml of tetrahydrofuran, are added to the solution obtained at -78 ° C. The mixture is allowed to warm slowly to room temperature, the solvent is removed in an oil pump vacuum and the product is extracted from the residue with methylene chloride. Yield: 1.89 g (70%)
1 H-NMR: ([D 6 ] -benzene; 300.1 MHz; 300 K): d = 5.82 (pt, 4H, RCpH); 5.39 (pt, 4H, RCpH); 3.24 (q, 3 J FH = 12.5 Hz, 4H, 1'-H) ppm.
19 F NMR: ([D 6 ] benzene; 284.1 MHz; 300K): d = -65.14 (s (1H decoupled)); (t, 3 J HF = 11.5Hz) (not decoupled)) ppm.

Beispiel 3Example 3 Synthese von (2',2',2'-trifluorethyl)cyclopentadienyl)(cyclopentadienyl)­ zirconiumdichloridSynthesis of (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) (cyclopentadienyl) zirconium dichloride

1.8 mmol 2',2',2'-Trifluorethylcyclopentadien aus Beispiel 1 werden in Tetrahydrofuran bei -78°C mit 1.05 ml 1.65M Butyllithium-Lösung versetzt. Dazu gibt man eine gekühlte Suspension von 0,46 g Cyclopentadienylzirconiumtrichlorid in 50 ml Tetrahydrofuran. Man läßt langsam auf Raumtemperatur erwärmen, entfernt das Lösemittel im Ölpumpenvakuum und extrahiert das Produkt mit Methylenchlorid aus dem Rückstand.
Ausbeute: 0.47 g (70%)
1H-NMR: ([D]-Chloroform; 200.1 MHz; 300 K): d = 6.49 (s, 5H, CpH); 6.38 (m, 4H, RCpH); 3.46 (q, 3JFH = 10.8 Hz, 2H, 1'-H) ppm.
19F-NMR: ([D]-Chloroform; 282.4 MHz; 300K): d = -66.03 (s (1H-entkoppelt)); (t, 3JHF = 11.5Hz) (nicht entkoppelt)) ppm.1.8 mmol of 2 ', 2', 2'-trifluoroethylcyclopentadiene from Example 1 are added to tetrahydrofuran at -78 ° C with 1.05 ml of 1.65M butyllithium solution. A cooled suspension of 0.46 g of cyclopentadienylzirconium trichloride in 50 ml of tetrahydrofuran is added. The mixture is allowed to warm slowly to room temperature, the solvent is removed in an oil pump vacuum and the product is extracted from the residue with methylene chloride.
Yield: 0.47 g (70%)
1 H NMR: ([D] chloroform; 200.1 MHz; 300 K): d = 6.49 (s, 5H, CpH); 6.38 (m, 4H, RCpH); 3.46 (q, 3 J FH = 10.8 Hz, 2H, 1'-H) ppm.
19 F NMR: ([D] chloroform; 282.4 MHz; 300K): d = -66.03 (s ( 1 H-decoupled)); (t, 3 J HF = 11.5Hz) (not decoupled)) ppm.

Beispiel 4Example 4 Synthese von Bis(2',2',2'-trifluorethyl)cyclopentadienyl)hafniumdichloridSynthesis of bis (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) hafnium dichloride

5.18 mmol 2',2',2'-Trifluorethylcyclopentadien aus Beispiel 1 werden bei -78°C mit 3.14 ml 1.65M Butyllithium-Lösung in Hexan versetzt. Zu der erhaltenen Lösung gibt man bei -78°C 0,8 g Hafniumtetrachlorid. Man läßt langsam auf Raumtemperatur erwärmen, entfernt das Lösemittel im Ölpumpenvakuum und extrahiert das Produkt mit Methylenchlorid aus dem Rückstand. Ausbeute: 1.79 g (64%)
1H-NMR: ([D6]-Benzol; 300.1 MHz; 300 K): d = 5.73 (pt, 4H, RCpH); 5.31 (pt, 4H, RCpH); 3.24 (q, 3JFH = 10.8 Hz, 4H, 1'-H) ppm.
19F-NMR: ([D6]-Benzol; 282.4 MHz; 300K): d = -65.8 (s (1H-entkoppelt)); (t, 3JHF = 11.5Hz) (nicht entkoppelt)) ppm.5.18 mmol of 2 ', 2', 2'-trifluoroethylcyclopentadiene from Example 1 are mixed with 3.14 ml of 1.65M butyllithium solution in hexane at -78 ° C. 0.8 g of hafnium tetrachloride is added to the solution obtained at -78 ° C. The mixture is allowed to warm slowly to room temperature, the solvent is removed in an oil pump vacuum and the product is extracted from the residue with methylene chloride. Yield: 1.79 g (64%)
1 H NMR: ([D 6 ] -benzene; 300.1 MHz; 300 K): d = 5.73 (pt, 4H, RCpH); 5.31 (pt, 4H, RCpH); 3.24 (q, 3 J FH = 10.8 Hz, 4H, 1'-H) ppm.
19 F-NMR: ([D 6 ] -benzene; 282.4 MHz; 300K): d = -65.8 (s ( 1 H-decoupled)); (t, 3 J HF = 11.5Hz) (not decoupled)) ppm.

Beispiel 5Example 5 Synthese von Bis((1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)titandichloridSynthesis of bis ((1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) titanium dichloride Synthese von 1'H,1'H,2'H,2'H-PerfluoroctylcyclopentadienSynthesis of 1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadiene

2.29 g Nickelocen aus Beispiel 1 und 3.17 g Triphenylphosphin werden in 5 ml Diethylether gelöst und mit 3.0 ml 1H,1H,2H,2H-Perfluoroctyliodid versetzt. Die Lösung färbt sich violett und wird 48 h gerührt. Anschließend wird die überstehende Lösung filtriert, der Niederschlag sorgfältig nachgewaschen und dann das Lösemittel entfernt. Der Rückstand wird mit Pentan über eine kurze Säule chromatographiert und das Lösemittel im Ölpumpenvakuum entfernt.
Ausbeute: 3.67 g (74%)
1H-NMR: ([D]-Chloroform; 200.1 MHz; 300 K): d = 6.45; 6.39; 6.28; 6.22; 6.05 (je m, 3H, RCpH); 2.97 (pq, (1-Isomer), 2.91 (psext, (2-Isomer), zusammen 4 H, CH2); 2.67 (m, 4H,1'-H); 2.31 (m, 4H,2'-H) ppm.
19F-NMR: ([D]-Chloroform; 282,4 MHz; 300K): d = -81.24 (m, 3F, 8'-F); -114.77 (m, 2F, 3'-F); -122.07 (m, 2F, 4'-F); -123.06 (m, 2F, 7'-F); -123.67 (m, 2F, 6'-F) -126.37 (m, 2F, 5'F) ppm.2.29 g of nickelocene from Example 1 and 3.17 g of triphenylphosphine are dissolved in 5 ml of diethyl ether and mixed with 3.0 ml of 1H, 1H, 2H, 2H-perfluorooctyl iodide. The solution turns violet and is stirred for 48 h. The supernatant solution is then filtered, the precipitate is washed thoroughly and then the solvent is removed. The residue is chromatographed on a short column with pentane and the solvent is removed in an oil pump vacuum.
Yield: 3.67 g (74%)
1 H NMR: ([D] chloroform; 200.1 MHz; 300 K): d = 6.45; 6.39; 6.28; 6.22; 6.05 (each m, 3H, RCpH); 2.97 (pq, (1-isomer), 2.91 (psext, (2-isomer), together 4 H, CH2); 2.67 (m, 4H, 1'-H); 2.31 (m, 4H, 2'-H) ppm.
19 F NMR: ([D] chloroform; 282.4 MHz; 300K): d = -81.24 (m, 3F, 8'-F); -114.77 (m, 2F, 3'-F); -122.07 (m, 2F, 4'-F); -123.06 (m, 2F, 7'-F); -123.67 (m, 2F, 6'-F) -126.37 (m, 2F, 5'F) ppm.

Synthese von Bis((1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)titandichloridSynthesis of bis ((1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) titanium dichloride

Eine Lösung von 0,75 g 1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadien in 40 ml Tetrahydrofuran wird bei -78°C mit 1.04 ml 1.65M Butyllithium-Lösung versetzt und mit einer gekühlten Suspension von 0,168 g Titantetrachlorid-THF-Addukt in 45 ml Tetrahydrofuran versetzt. Man läßt auf Raumtemperatur erwärmen und entfernt das Lösemittel im Vakuum. Das Produkt wird mittels Extraktion mit Methylenchlorid isoliert.
Ausbeute: 0,1 g (12%)
1H-NMR: ([D]-Chloroform; 200.1 MHz; 300 K): d = 6.39 (pt, 4H, RCpH); 6.28 (pt, 4H, RCpH); 3.12 (m, 4H,1'-H); 2.48 (m, 4H,2'-H) ppm.
19F-NMR: ([D]-Chloroform; 282.4 MHz; 300K): d = -81.0 (m, 6F, 8'-F); -114.3 (m, 4F, 3'-F); -122.1 (m, 4F, 4'-F); -123.1 (m, 4F, 7'-F); -123.6 (m, 4F, 6'-F); -126.3 (m, 4F, 5'-F) ppm.A solution of 0.75 g of 1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadiene in 40 ml of tetrahydrofuran is mixed with 1.04 ml of 1.65M butyllithium solution at -78 ° C and with a cooled suspension of 0.168 g of titanium tetrachloride-THF adduct in 45 ml of tetrahydrofuran. The mixture is allowed to warm to room temperature and the solvent is removed in vacuo. The product is isolated by extraction with methylene chloride.
Yield: 0.1 g (12%)
1 H NMR: ([D] chloroform; 200.1 MHz; 300 K): d = 6.39 (pt, 4H, RCpH); 6.28 (pt, 4H, RCpH); 3.12 (m, 4H, 1'-H); 2.48 (m, 4H, 2'-H) ppm.
19 F NMR: ([D] chloroform; 282.4 MHz; 300K): d = -81.0 (m, 6F, 8'-F); -114.3 (m, 4F, 3'-F); -122.1 (m, 4F, 4'-F); -123.1 (m, 4F, 7'-F); -123.6 (m, 4F, 6'-F); -126.3 (m, 4F, 5'-F) ppm.

Beispiel 6Example 6 Synthese von Bis((1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)­ zirconiumdichloridSynthesis of bis ((1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) zirconium dichloride

Eine Lösung von 0,98 g 1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadien aus Beispiel 5 in 60 ml Tetrahydrofuran wird bei -78°C mit 1.49 ml 1.65M Butyllithium-Lösung versetzt und mit einer gekühlten Suspension von 0,426 g Zirconiumtetrachlorid-THF- Addukt in 40 ml Tetrahydrofuran versetzt. Man läßt auf Raumtemperatur erwärmen und entfernt das Lösemittel im Vakuum. Das Produkt wird mittels Extraktion mit Methylenchlorid isoliert.
Ausbeute: 0,56 g (50%)
1H-NMR: ([D]-Chloroform; 200.1 MHz; 300 K): d = 6.33 (pt, 4H, RCpH); 6.24 (pt, 4H, RCpH); 2.98 (m, 4H,1'-H); 2.09 (m, 4H,2'-H) ppm.
19F-NMR: ([D]-Chloroform; 282.4 MHz; 300K): d = -81.0 (m, 6F, 8'-F); -114.5 (m, 4F, 3'-F); -122.0 (m, 4F, 4'-F); -123.0 (m, 4F, 7'-F); -123.6 (m, 4F, 6'-F); -126.3 (m, 4F, 5'-F) ppm.A solution of 0.98 g of 1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadiene from Example 5 in 60 ml of tetrahydrofuran is mixed with 1.49 ml of 1.65M butyllithium solution at -78 ° C and cooled with a Suspension of 0.426 g of zirconium tetrachloride-THF adduct in 40 ml of tetrahydrofuran. The mixture is allowed to warm to room temperature and the solvent is removed in vacuo. The product is isolated by extraction with methylene chloride.
Yield: 0.56 g (50%)
1 H NMR: ([D] chloroform; 200.1 MHz; 300 K): d = 6.33 (pt, 4H, RCpH); 6.24 (pt, 4H, RCpH); 2.98 (m, 4H, 1'-H); 2.09 (m, 4H, 2'-H) ppm.
19 F NMR: ([D] chloroform; 282.4 MHz; 300K): d = -81.0 (m, 6F, 8'-F); -114.5 (m, 4F, 3'-F); -122.0 (m, 4F, 4'-F); -123.0 (m, 4F, 7'-F); -123.6 (m, 4F, 6'-F); -126.3 (m, 4F, 5'-F) ppm.

Beispiel 7Example 7 Synthese von Bis((1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)­ hafniumdichloridSynthesis of bis ((1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) hafnium dichloride

Eine Lösung von 0,87 g 1'H,1'H,2'H,2'H-PerfIuoroctylcyclopentadien aus Beispiel 5 in 60 ml Tetrahydrofuran wird bei -78°C mit 1.21 ml 1.65M Butyllithium-Lösung versetzt und mit einer gekühlten Suspension von 0,305 g Hafniumtetrachlorid in 40 ml Tetrahydrofuran versetzt. Man läßt auf Raumtemperatur erwärmen und entfernt das Lösemittel im Vakuum. Das Produkt wird mittels Extraktion mit Methylenchlorid isoliert.
Ausbeute: 0,38 g (38%)
1H-NMR: ([D6]-Benzol; 200.1 MHz; 300 K): d = 5.57 (pt, 4H, RCpH); 5.47 (pt, 4H, RCpH); 2.86 (m, 4H,1'-H); 2.10 (m, 4H,2'-H) ppm.
19F-NMR: ([D6]-Benzol; 282.4 MHz; 300K): d = -81.2 (m, 6F, 8'-F); -114.5 (m, 4F, 3'-F); -121.9 (m, 4F, 4'-F); -122.9 (in, 4F, 7'-F); -123.4 (m, 4F, 6'-F); -126.2 (m, 4F, 5'-F) ppm.A solution of 0.87 g of 1'H, 1'H, 2'H, 2'H-PerfIuoroctylcyclopentadien from Example 5 in 60 ml of tetrahydrofuran is mixed at -78 ° C with 1.21 ml of 1.65M butyllithium solution and with a cooled Suspension of 0.305 g of hafnium tetrachloride in 40 ml of tetrahydrofuran. The mixture is allowed to warm to room temperature and the solvent is removed in vacuo. The product is isolated by extraction with methylene chloride.
Yield: 0.38 g (38%)
1 H NMR: ([D 6 ] -benzene; 200.1 MHz; 300 K): d = 5.57 (pt, 4H, RCpH); 5.47 (pt, 4H, RCpH); 2.86 (m, 4H, 1'-H); 2.10 (m, 4H, 2'-H) ppm.
19 F-NMR: ([D 6 ] -benzene; 282.4 MHz; 300K): d = -81.2 (m, 6F, 8'-F); -114.5 (m, 4F, 3'-F); -121.9 (m, 4F, 4'-F); -122.9 (in, 4F, 7'-F); -123.4 (m, 4F, 6'-F); -126.2 (m, 4F, 5'-F) ppm.

Beispiel 8Example 8 Synthese von ((1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)­ (cyclopentadienyl)zirconiumdichloridSynthesis of ((1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (cyclopentadienyl) zirconium dichloride

Eine Lösung von 1.31 g 1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadien aus Beispiel 5 in 25 ml Tetrahydrofuran wird bei -78°C mit 2 ml 1.65M Butyllithium-Lösung versetzt und mit einer gekühlten Suspension von 1.28 g Cyclopentadienylzirconiumtrichlorid-THF-Addukt in 40 ml Tetrahydrofuran versetzt. Man läßt auf Raumtemperatur erwärmen und entfernt das Lösemittel im Vakuum. Das Produkt wird mittels Extraktion mit Methylenchlorid und Pentan isoliert.
Ausbeute: 1.73 g (86%)
1H-NMR: ([D]-Chloroform; 200.1 MHz; 300 K): d = 6.47 (s, 5H, CpH); 6.32 (pt, 2H, RCpH); 6.23 (pt, 2H, RCpH); 2.98 (m, 2H,1'H); 2.38 (m, 2H,2'H) ppm.
19F-NMR: ([D]-Chloroform; 282.4 MHz; 300K): d = -81.0 (m, 3F, 8'-F); -114.5 (m, 2F, 3'-F); -122.0 (m, 2F, 4'-F); -123.0 (m, 2F, 7'-F); -123.6 (m, 2F, 6'-F); -126.3 (m, 2F, 5'-F) ppm.A solution of 1.31 g of 1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadiene from Example 5 in 25 ml of tetrahydrofuran is mixed at -78 ° C with 2 ml of 1.65M butyllithium solution and with a cooled suspension of 1.28 g of cyclopentadienylzirconium trichloride-THF adduct in 40 ml of tetrahydrofuran. The mixture is allowed to warm to room temperature and the solvent is removed in vacuo. The product is isolated by extraction with methylene chloride and pentane.
Yield: 1.73 g (86%)
1 H NMR: ([D] chloroform; 200.1 MHz; 300 K): d = 6.47 (s, 5H, CpH); 6.32 (pt, 2H, RCpH); 6.23 (pt, 2H, RCpH); 2.98 (m, 2H, 1'H); 2.38 (m, 2H, 2'H) ppm.
19 F NMR: ([D] chloroform; 282.4 MHz; 300K): d = -81.0 (m, 3F, 8'-F); -114.5 (m, 2F, 3'-F); -122.0 (m, 2F, 4'-F); -123.0 (m, 2F, 7'-F); -123.6 (m, 2F, 6'-F); -126.3 (m, 2F, 5'-F) ppm.

Beispiel 9Example 9 Synthese von (1'H,1'H,2'H,2'H-perfluoroctylcyclopentadienyl)­ (pentamethylcyclopentadienyl)zirconiumdichloridSynthesis of (1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (pentamethylcyclopentadienyl) zirconium dichloride

Eine Lösung von 1.39 g 1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadien aus Beispiel 5 in 50 ml Tetrahydrofuran wird bei -78°C mit 2.1 ml 1.65M Butyllithium-Lösung versetzt und mit einer gekühlten Suspension von 1.11 g Pentamethylcyclopentadienylzirconiumtrichlorid in 30 ml Tetrahydrofuran versetzt. Man läßt auf Raumtemperatur erwärmen und entfernt das Lösemittel im Vakuum. Das Produkt wird mittels Extraktion mit Methylenchlorid und Pentan isoliert.
Ausbeute: 1.9g (81%)
1H-NMR: ([D]-Chloroform; 200.1 MHz; 300 K): d = 6.06 (pt, 2H,RCpH); 5.94 (pt, 2H, RCpH); 3.72 (m, 2H, 1'-H); 2.97 (m, 2H,2'-H); 2.02 (s, 15H, Cp(CH3)5) ppm.
19F-NMR: ([D]-Chloroform; 282.4 MHz; 300K): d = -80.9 (m, 3F, 8'-F); -114.5 (m, 2F, 3'-F); -122.2 (m, 2F, 4'-F); -123.0 (m, 2F, 7'-F); -123.6 (m, 2F, 6'-F); -126.3 (m, 2F, 5'-F) ppm.A solution of 1.39 g of 1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadiene from Example 5 in 50 ml of tetrahydrofuran is mixed at -78 ° C with 2.1 ml of 1.65M butyllithium solution and with a cooled suspension of 1.11 g of pentamethylcyclopentadienylzirconium trichloride in 30 ml of tetrahydrofuran. The mixture is allowed to warm to room temperature and the solvent is removed in vacuo. The product is isolated by extraction with methylene chloride and pentane.
Yield: 1.9g (81%)
1 H NMR: ([D] chloroform; 200.1 MHz; 300 K): d = 6.06 (pt, 2H, RCpH); 5.94 (pt, 2H, RCpH); 3.72 (m, 2H, 1'-H); 2.97 (m, 2H, 2'-H); 2:02 (s, 15H, Cp (CH 3) 5) ppm.
19 F NMR: ([D] chloroform; 282.4 MHz; 300K): d = -80.9 (m, 3F, 8'-F); -114.5 (m, 2F, 3'-F); -122.2 (m, 2F, 4'-F); -123.0 (m, 2F, 7'-F); -123.6 (m, 2F, 6'-F); -126.3 (m, 2F, 5'-F) ppm.

Beispiel 10Example 10 Synthese von Bis(2',2',2'-trifluorethyl)cyclopentadienyl)zirconiumdimethylSynthesis of bis (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) zirconium dimethyl

Zu einer Suspension von 1.05 g Bis(2',2',2'- trifluorethyl)cyclopentadienyl)zirkoniumdichlorid aus Beispiel 2 in 40 ml Diethylether gibt man bei -78°C langsam 2.79 ml 1.68M Methyllithium-Lösung in Diethylether. Man läßt auf Raumtemperatur erwärmen und entfernt das Lösemittel im Ölpumpenvakuum. Das Produkt wird mittels Extraktion mit Pentan isoliert. Ausbeute: 0,614 g (73%)
1H-NMR: ([D6]-Benzol; 200.1 MHz; 300 K): d = 5.62 (pt, 4H,RCpH); 5.21 (pt, 4H, RCpH); 2.87 (q, 3JFH = 10.6 Hz, 4H,1'-H); -0.52 (s, 6H,Zr-CH3) ppm.To a suspension of 1.05 g of bis (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) zirconium dichloride from Example 2 in 40 ml of diethyl ether, 2.79 ml of 1.68M methyl lithium solution in diethyl ether is slowly added at -78 ° C. The mixture is allowed to warm to room temperature and the solvent is removed in an oil pump vacuum. The product is isolated by extraction with pentane. Yield: 0.614 g (73%)
1 H NMR: ([D 6 ] -benzene; 200.1 MHz; 300 K): d = 5.62 (pt, 4H, RCpH); 5.21 (pt, 4H, RCpH); 2.87 (q, 3 J FH = 10.6 Hz, 4H, 1'-H); -0.52 (s, 6H, Zr-CH 3 ) ppm.

Beispiel 11Example 11 Synthese von (2',2',2'-Trifluorethylcyclopentadienyl)(cyclopentadienyl)­ zirconiumdimethylSynthesis of (2 ', 2', 2'-trifluoroethylcyclopentadienyl) (cyclopentadienyl) zirconium dimethyl

Zu einer Suspension von 0,252 g (2',2',2'-Trifluorethyl)cyclopentadienyl)­ (cyclopentadienyl)zirkoniumdichlorid aus Beispiel 3 in 25 ml Diethylether gibt man bei -78°C langsam 0,8 ml 1.68M Methyllithium-Lösung in Diethylether. Man läßt auf Raumtemperatur erwärmen und entfernt das Lösemittel im Ölpumpenvakuum. Das Produkt wird mittels Extraktion mit Pentan isoliert. Ausbeute: 0,162 g (73%)
1H-NMR: ([D6]-Benzol; 200.1 MHz; 300 K): d = 5.64 (s, 5H,CpH); 5.63 (pt, 2H, RCpH); 5.27 (pt, 2H, RCpH); 2.87 (q, 3JFH = 10.8 Hz, 2H, 1'-H); -0.32 (s, 6H, Zr- (CH3) ppm.To a suspension of 0.252 g (2 ', 2', 2'-trifluoroethyl) cyclopentadienyl) (cyclopentadienyl) zirconium dichloride from Example 3 in 25 ml diethyl ether, 0.8 ml 1.68M methyl lithium solution in diethyl ether is slowly added at -78 ° C . The mixture is allowed to warm to room temperature and the solvent is removed in an oil pump vacuum. The product is isolated by extraction with pentane. Yield: 0.162 g (73%)
1 H-NMR: ([D 6 ] -benzene; 200.1 MHz; 300 K): d = 5.64 (s, 5H, CpH); 5.63 (pt, 2H, RCpH); 5.27 (pt, 2H, RCpH); 2.87 (q, 3 J FH = 10.8 Hz, 2H, 1'-H); -0.32 (s, 6H, Zr (CH 3) ppm.

Beispiel 12Example 12 Synthese von Bis((1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)­ zirconiumdimethylSynthesis of bis ((1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) zirconium dimethyl

Zu einer Suspension von 0,51 g Bis((1'H,1'H,2'H,2'H-perfluoroctyl)­ cyclopentadienyl)titandichlorid aus Beispiel 5 in 50 ml Diethylether gibt man bei -78°C langsam 1,04 ml 1.68M Methyllithium-Lösung in Diethylether. Man läßt auf Raumtemperatur erwärmen und entfernt das Lösemittel im Ölpumpenvakuum. Das Produkt wird mittels Extraktion mit Pentan isoliert. Ausbeute: 0,302 g (65%)
1H-NMR: ([D6]-Benzol; 200.1 MHz; 300 K): d = 5.46 (pt, 4H,RCpH); 5.37 (pt, 4H, RCpH); 2.60 (m, 4H,1'-H); 2.05 (m, 4H,2'H); -0.29 (s, 6H,Zr-CH3) ppm. To a suspension of 0.51 g of bis ((1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) titanium dichloride from Example 5 in 50 ml of diethyl ether, 1.04 is slowly added at -78 ° C ml 1.68M methyl lithium solution in diethyl ether. The mixture is allowed to warm to room temperature and the solvent is removed in an oil pump vacuum. The product is isolated by extraction with pentane. Yield: 0.302 g (65%)
1 H-NMR: ([D 6 ] -benzene; 200.1 MHz; 300 K): d = 5.46 (pt, 4H, RCpH); 5.37 (pt, 4H, RCpH); 2.60 (m, 4H, 1'-H); 2.05 (m, 4H, 2'H); -0.29 (s, 6H, Zr-CH 3 ) ppm.

Beispiel 13Example 13 Synthese von (1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)­ (cyclopentadienyl)zirconiumdimethylSynthesis of (1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (cyclopentadienyl) zirconium dimethyl

Zu einer Suspension von 0,525 g (1'H,1'H,2'H,2'H-Perfluoroctyl­ cyclopentadienyl)(cyclopentadienyl)zirconiumdichlorid aus Beispiel 8 in 40 ml Diethylether gibt man bei -78°C langsam 1,03 ml 1.68M Methyllithium-Lösung in Diethylether. Man läßt auf Raumtemperatur erwärmen und entfernt das Lösemittel im Ölpumpenvakuum. Das Produkt wird mittels Extraktion mit Pentan isoliert. Ausbeute: 0,257 g (55%)
1H-NMR: ([D6]-Benzol; 200.1 MHz; 300 K): d = 5.70 (s, 5H,CpH); 5.45 pt, 2H, RCpH); 5.36 (pt, 2H, RCpH); 2.60 (m, 2H,1'-H); 2.09 (m, 2H,2'H); -0.21 (s, 6H, Zr- (CH3)2) ppm.To a suspension of 0.525 g (1'H, 1'H, 2'H, 2'H-perfluorooctyl cyclopentadienyl) (cyclopentadienyl) zirconium dichloride from Example 8 in 40 ml diethyl ether, 1.03 ml 1.68 are slowly added at -78 ° C M methyl lithium solution in diethyl ether. The mixture is allowed to warm to room temperature and the solvent is removed in an oil pump vacuum. The product is isolated by extraction with pentane. Yield: 0.257 g (55%)
1 H-NMR: ([D 6 ] -benzene; 200.1 MHz; 300 K): d = 5.70 (s, 5H, CpH); 5.45 pt, 2H, RCpH); 5.36 (pt, 2H, RCpH); 2.60 (m, 2H, 1'-H); 2.09 (m, 2H, 2'H); -0.21 (s, 6H, Zr- (CH 3 ) 2 ) ppm.

Beispiel 14Example 14 (1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)(pentamethylcyclopentadienyl)­ zirconiumdimethyl(1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (pentamethylcyclopentadienyl) zirconium dimethyl

Zu einer Suspension von 1,9 g (1'H,1'H,2'H,2'H-Perfluoroctylcyclopentadienyl)­ (pentamethylcyclopentadienyl)zirconiumdichlorid aus Beispiel 9 in 40 ml Diethylether gibt man bei -78°C langsam 2,7 ml 1.68M Methyllithium-Lösung in Diethylether. Man läßt auf Raumtemperatur erwärmen und entfernt das Lösemittel im Ölpumpenvakuum. Das Produkt wird mittels Extraktion mit Pentan isoliert. Ausbeute: 1,33g (74%)
1H-NMR: ([D6]-Benzol; 200.1 MHz; 300 K): d = 5.51 (pt, 2H, RCpH); 5.28 (pt, 2H, RCpH); 2.74 (m, 2H, 1'-H); 2.13 (m, 2H,2'-H); 1.67 (s, 15H, Cp(CH3)5); -0.44 (s, 6H, Zr-CH3) ppm. 2.7 ml is slowly added to a suspension of 1.9 g (1'H, 1'H, 2'H, 2'H-perfluorooctylcyclopentadienyl) (pentamethylcyclopentadienyl) zirconium dichloride from Example 9 in 40 ml diethyl ether at -78 ° C 1.68M methyl lithium solution in diethyl ether. The mixture is allowed to warm to room temperature and the solvent is removed in an oil pump vacuum. The product is isolated by extraction with pentane. Yield: 1.33 g (74%)
1 H-NMR: ([D 6 ] -benzene; 200.1 MHz; 300 K): d = 5.51 (pt, 2H, RCpH); 5.28 (pt, 2H, RCpH); 2.74 (m, 2H, 1'-H); 2.13 (m, 2H, 2'-H); 1.67 (s, 15H, Cp (CH 3) 5); -0.44 (s, 6H, Zr-CH 3 ) ppm.

Beispiel 15Example 15 Synthese von Bis((2,2',2'-trifluorethyl)cyclopentadienyl)hafniumdimethylSynthesis of bis ((2,2 ', 2'-trifluoroethyl) cyclopentadienyl) hafniumdimethyl

Zu einer Suspension von 0,5 g Bis((2,2',2',trifluorethyl)cyclopentadienyl)­ hafniumdichlorid aus Beispiel 4 in 50 ml Diethylether gibt man bei -78°C langsam 1,1 ml 1.68M Methyllithium-Lösung in Diethylether. Man läßt auf Raumtemperatur erwärmen und entfernt das Lösemittel im Ölpumpenvakuum. Das Produkt wird mittels Extraktion mit Pentan isoliert.
Ausbeute: 0,358 g (83%)
1H-NMR: ([D6]-Benzol; 200.1 MHz; 300 K): d = 5.52 (pt, 4H, RCpH); 5.16 (pt, 4H, RCpH); 2.87 (q, 3JFH = 10.7 Hz, 4H,1'-H); -0.71 (s, 6H, Hf-CH3) ppm.To a suspension of 0.5 g bis ((2,2 ', 2', trifluoroethyl) cyclopentadienyl) hafnium dichloride from Example 4 in 50 ml diethyl ether, 1.1 ml 1.68M methyl lithium solution in diethyl ether is slowly added at -78 ° C . The mixture is allowed to warm to room temperature and the solvent is removed in an oil pump vacuum. The product is isolated by extraction with pentane.
Yield: 0.358 g (83%)
1 H-NMR: ([D 6 ] -benzene; 200.1 MHz; 300 K): d = 5.52 (pt, 4H, RCpH); 5.16 (pt, 4H, RCpH); 2.87 (q, 3 J FH = 10.7 Hz, 4H, 1'-H); -0.71 (s, 6H, Hf-CH3) ppm.

Beispiel 16Example 16 Synthese von Bis((1'H,1'H,2'H,2'H-perfluoroctyl)cyclopentadienyl)­ hafniumdimethylSynthesis of bis ((1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) hafnium dimethyl

Zu einer Suspension von 0,222 g Bis((1'H,1 'H,2'H,2'H-perfluoroctyl)­ cyclopentadienyl)hafniumdichlorid aus Beispiel 7 in 40 ml Diethylether gibt man bei -78°C langsam 0,25 ml 1.68M Methyllithium-Lösung in Diethylether. Man läßt auf Raumtemperatur erwärmen und entfernt das Lösemittel im Ölpumpenvakuum. Das Produkt wird mittels Extraktion mit Pentan isoliert.
Ausbeute: 0,197 g (91%)
1H-NMR: ([D6]-Benzol; 200.1 MHz; 300 K): d = 5,38 (pt, 4H, RCpH); 5.31 (pt, 4H, RCpH); 2.59 (m, 4H,1'-H); 2.08 (m, 4H,2'-H); -0.47 (s, 6H, Hf-CH3) ppm.0.25 ml of 1.68 is slowly added to a suspension of 0.222 g of bis ((1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) hafnium dichloride from Example 7 in 40 ml of diethyl ether at -78 ° C M methyl lithium solution in diethyl ether. The mixture is allowed to warm to room temperature and the solvent is removed in an oil pump vacuum. The product is isolated by extraction with pentane.
Yield: 0.197 g (91%)
1 H-NMR: ([D 6 ] -benzene; 200.1 MHz; 300 K): d = 5.38 (pt, 4H, RCpH); 5.31 (pt, 4H, RCpH); 2.59 (m, 4H, 1'-H); 2.08 (m, 4H, 2'-H); -0.47 (s, 6H, Hf-CH3) ppm.

Beispiel 17Example 17 Polymerisation von PropenPolymerization of propene

In einem 1-l-Glasautoklaven werden 200 ml Toluol und 19 ml 10,5%ige Methylaluminoxanlösung in Toluol vorgelegt. Dazu wird eine Lösung von 1 ml 10,5%ige Methylaluminoxanlösung in Toluol und 40 mg Bis((1'H,1'H,2'H,2'H- perfluoroctyl)cyclopentadienyl)zirconiumdichlorid gegeben. Anschließend wird die Polymerisationstemperatur von 0°C eingestellt und 2 bar Propen aufgedrückt und im Verlauf der Polymerisation mittels Nachdosieren gehalten. Die Poylmerisation wird gestoppt durch Zugabe 20 ml Methanol/2N-Salzsäure (1 : 1). Das erhaltene Polypropylen wird abfiltriert und im Ölpumpenvakuum getrocknet.
Aktivität: 33 g/(mmol.bar.h)200 ml of toluene and 19 ml of 10.5% strength methylaluminoxane solution in toluene are placed in a 1 liter glass autoclave. A solution of 1 ml of 10.5% methylaluminoxane solution in toluene and 40 mg of bis ((1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) zirconium dichloride is added. The polymerization temperature is then set from 0 ° C. and 2 bar of propene are pressed in and kept in the course of the polymerization by means of subsequent metering. Polymerization is stopped by adding 20 ml of methanol / 2N hydrochloric acid (1: 1). The polypropylene obtained is filtered off and dried in an oil pump vacuum.
Activity: 33 g / (mmol.bar.h)

Beispiel 18Example 18 Polymerisation von PropenPolymerization of propene

In einem 1-l-Glasautoklaven werden 200 ml Toluol und 19 ml 10,5%ige Methylaluminoxanlösung in Toluol vorgelegt. Dazu wird eine Lösung von 1 ml 10,5%ige Methylaluminoxanlösung in Toluol und 15 mg (1'H,1'H,2'H,2'H- perfluoroctyl)cyclopentadienyl)(cyclopentadienyl)zirconiumdichlorid gegeben. Anschließend wird die Polymerisationstemperatur von 0°C eingestellt und 2 bar Propen aufgedrückt und im Verlauf der Polymerisation mittels Nachdosieren gehalten. Die Poylmerisation wird gestoppt durch Zugabe 20 ml Methanol/2N- Salzsäure (1 : 1). Das erhaltene Polypropylen wird abfiltriert und im Ölpumpenvakuum getrocknet.
Aktivität: 144 g/(mmol.bar.h)200 ml of toluene and 19 ml of 10.5% strength methylaluminoxane solution in toluene are placed in a 1 liter glass autoclave. A solution of 1 ml of a 10.5% methylaluminoxane solution in toluene and 15 mg (1'H, 1'H, 2'H, 2'H-perfluorooctyl) cyclopentadienyl) (cyclopentadienyl) zirconium dichloride is added. The polymerization temperature is then set from 0 ° C. and 2 bar of propene are pressed in and kept in the course of the polymerization by means of subsequent metering. Polymerization is stopped by adding 20 ml of methanol / 2N hydrochloric acid (1: 1). The polypropylene obtained is filtered off and dried in an oil pump vacuum.
Activity: 144 g / (mmol.bar.h)

Claims (7)

1. Katalysatorsystem enthaltend
  • (a) mindestens einen Cokatalysator,
  • (b) mindestens eine metallorganische Verbindung der Formel (I)
    worin,
    M1 ein Metall der Gruppe 3, 4, 5 oder 6 des Periodensystems der Elemente sowie Lanthanide oder Actinide bedeutet,
    R1 gleich oder verschieden sind und ein Wasserstoffatom, eine C1-C30- kohlenstoffhaltige Gruppe, SiR3, worin R3 gleich oder verschieden ein Wasserstoffatom oder eine C1-C40-kohlenstoffhaltige Gruppe sind, oder zwei oder mehrere Reste R1 können so miteinander verbunden sein, daß die Reste R1 und die sie verbindenden Atome des Cyclopentadienylringes ein C4-C24-Ringsystem bilden, welches seinerseits substituiert sein kann,
    R2 gleich oder verschieden sind und ein fluorhaltiges C1-C25-Alkyl, fluorhaltiges C1-C25-Alkenyl, fluorhaltiges C6-C24-Aryl, fluorhaltiges C7-C30-Arylalkyl, fluorhaltiges C7-C30-Alkylaryl bedeuten,
    r, n gleich oder verschieden sind und 1, 2, 3, 4 oder 5 bedeuten,
    m, q gleich oder verschieden sind und 0,1, 2, 3 oder 4 bedeuten,
    q+r gleich 5 für v = 0, und q+r gleich 4 für v = 1 ist,
    m+n gleich 5 für v = 0, und m+n gleich 4 für v = 1 ist,
    s, t gleich oder verschieden sind und eine ganze Zahl von 1 bis 20 bedeuten,
    L gleich oder verschieden sind und ein Halogenatom oder einen kohlenwasserstoffhaltigen Rest mit 1-20 Kohlenstoffatomen bedeuten,
    x eine ganze Zahl von 1 bis 4 ist, wobei im Falle von M1 = Ti, Zr oder Hf x bevorzugt gleich 2 ist,
    Z ein verbrückendes Strukturelement zwischen den beiden Cyclopentadienylringen bezeichnet, und v ist 0 oder 1, bedeutet,
    sowie gegebenenfalls
  • (c) mindestens einen Träger.
1. Containing catalyst system
  • (a) at least one cocatalyst,
  • (b) at least one organometallic compound of the formula (I)
    wherein,
    M 1 is a metal from group 3, 4, 5 or 6 of the periodic table of the elements and also lanthanides or actinides,
    R 1 are the same or different and are a hydrogen atom, a C 1 -C 30 carbon-containing group, SiR 3 , wherein R 3 are identical or different a hydrogen atom or a C 1 -C 40 carbon-containing group, or two or more radicals R 1 can be connected to one another in such a way that the radicals R 1 and the atoms of the cyclopentadienyl ring which connect them form a C 4 -C 24 ring system, which in turn can be substituted,
    R 2 are the same or different and are a fluorine-containing C 1 -C 25 alkyl, fluorine-containing C 1 -C 25 alkenyl, fluorine-containing C 6 -C 24 aryl, fluorine-containing C 7 -C 30 arylalkyl, fluorine-containing C 7 -C 30 Alkylaryl mean
    r, n are the same or different and are 1, 2, 3, 4 or 5,
    m, q are the same or different and are 0.1, 2, 3 or 4,
    q + r is 5 for v = 0, and q + r is 4 for v = 1,
    m + n is 5 for v = 0, and m + n is 4 for v = 1,
    s, t are the same or different and are an integer from 1 to 20,
    L are identical or different and represent a halogen atom or a hydrocarbon-containing radical having 1-20 carbon atoms,
    x is an integer from 1 to 4, where M 1 = Ti, Zr or Hf x is preferably 2,
    Z denotes a bridging structural element between the two cyclopentadienyl rings, and v is 0 or 1,
    and if necessary
  • (c) at least one carrier.
2. Katalysatorsystem gemäß Anspruch 1, dadurch gekennzeichnet, daß in Formel (I)
M1 gleich Titan, Zirkonium oder Hafnium,
R1 gleich oder verschieden sind und C1-C25-Alkyl, C2-C25-Alkenyl, C3-C15- Alkylalkenyl, C6-C24-Aryl, C5-C24-Heteroaryl, C7-C30-Arylalkyl, C7-C30- Alkylaryl, C1-C12-Alkoxy, SiR3,worin R3 gleich oder verschieden C1-C20- Alkyl, C1-C10-Fluoralkyl, C1-C10-Alkoxy, C6-C20-Aryl, C6-C10-Fluoraryl, C6- C10-Aryloxy, C2-C10-Alkenyl, C7-C40-Arylalkyl, C7-C40-Alkylaryl oder C8- C40-Arylalkenyl sind,
L gleich oder verschieden sind und C1-C20-Alkyl, C2-C20-Alkenyl, C1-C20- Alkoxy, C6-C14-Aryloxy oder C6-C40-Aryl, bedeuten.2. Catalyst system according to claim 1, characterized in that in formula (I)
M 1 is titanium, zirconium or hafnium,
R 1 are the same or different and are C 1 -C 25 alkyl, C 2 -C 25 alkenyl, C 3 -C 15 alkylalkenyl, C 6 -C 24 aryl, C 5 -C 24 heteroaryl, C 7 - C 30 arylalkyl, C 7 -C 30 alkylaryl, C 1 -C 12 alkoxy, SiR 3 , wherein R 3 are identical or different C 1 -C 20 alkyl, C 1 -C 10 fluoroalkyl, C 1 -C 10 alkoxy, C 6 -C 20 aryl, C 6 -C 10 fluoroaryl, C 6 - C 10 aryloxy, C 2 -C 10 alkenyl, C 7 -C 40 arylalkyl, C 7 -C 40 - Are alkylaryl or C 8 -C 40 arylalkenyl,
L are the same or different and are C 1 -C 20 alkyl, C 2 -C 20 alkenyl, C 1 -C 20 alkoxy, C 6 -C 14 aryloxy or C 6 -C 40 aryl. 3. Katalysatorsystem gemäß Anspruch 1, dadurch gekennzeichnet, daß in Formel (I)
R1 gleich oder verschieden sind und Methyl, Ethyl, tert.-Butyl, Cyclohexyl, Octyl, Pyridyl, Furyl oder Chinolyl, bedeuten.3. A catalyst system according to claim 1, characterized in that in formula (I)
R 1 are the same or different and are methyl, ethyl, tert-butyl, cyclohexyl, octyl, pyridyl, furyl or quinolyl. 4. Katalysatorsystem gemäß Anspruch 1, dadurch gekennzeichnet, daß in Formel (I)
Z gleich M2R4R5, worin M2 Kohlenstoff, Silizium, Germanium oder Zinn ist und R4 und R5 gleich oder verschieden eine C1-C20-Kohlenwasserstoffgruppe wie C1- C10-Alkyl oder C6-C14-Aryl bedeuten. 4. A catalyst system according to claim 1, characterized in that in formula (I)
Z is M 2 R 4 R 5 , where M 2 is carbon, silicon, germanium or tin and R 4 and R 5 are identical or different to a C 1 -C 20 hydrocarbon group such as C 1 - C 10 alkyl or C 6 -C 14 mean aryl. 5. Katalysatorsystem gemäß Anspruch 1, dadurch gekennzeichnet, daß in Formel (I) Z gleich CH2, CH2CH2, CH(CH3)CH2, CH(C4H9)C(CH3)2, C(CH3)2, (CH3)2Si, (CH3CH2)2Si, (CH3)((CH3)3C)Si, (CH3)2Ge, (CH3)2Sn, (C6H5)2Si, (C6H5)(CH3)Si, (C6H5)2Ge, (C6H5)2Sn, (CH2)4Si, CH2Si(CH3)2, o-C6H4 oder 2,2'-(C6H4)2 ist.5. A catalyst system according to claim 1, characterized in that in formula (I) Z is CH 2 , CH 2 CH 2 , CH (CH 3 ) CH 2 , CH (C 4 H 9 ) C (CH 3 ) 2 , C ( CH 3 ) 2 , (CH 3 ) 2 Si, (CH 3 CH 2 ) 2 Si, (CH 3 ) ((CH 3 ) 3 C) Si, (CH 3 ) 2 Ge, (CH 3 ) 2 Sn, ( C 6 H 5 ) 2 Si, (C 6 H 5 ) (CH 3 ) Si, (C 6 H 5 ) 2 Ge, (C 6 H 5 ) 2 Sn, (CH 2 ) 4 Si, CH 2 Si (CH 3 ) 2 , oC 6 H 4 or 2.2 '- (C 6 H 4 ) 2 . 6. Verfahren zur Herstellung von Polypropylen durch Polymerisation von Propylen in Gegenwart mindestens eines Katalysatorsystems nach einem der Ansprüche 1 bis 5.6. Process for the production of polypropylene by polymerization of Propylene in the presence of at least one catalyst system according to one of the Claims 1 to 5. 7. Verwendung eines Katalysatorsystems nach einem der Ansprüche 1 bis 5 zur Herstellung von Polypropylen.7. Use of a catalyst system according to one of claims 1 to 5 for Manufacture of polypropylene.
DE1998117726 1998-04-21 1998-04-21 Catalyst system for production of polypropylene Withdrawn DE19817726A1 (en)