DE10344442B3 - Oven door for a household oven comprises an inner pane made from borosilicate glass on which a colored layer made from a high temperature resistant non-enamel paint with organic or inorganic binder and an IR-reflecting layer are applied - Google Patents

Oven door for a household oven comprises an inner pane made from borosilicate glass on which a colored layer made from a high temperature resistant non-enamel paint with organic or inorganic binder and an IR-reflecting layer are applied Download PDF

Info

Publication number
DE10344442B3
DE10344442B3 DE10344442A DE10344442A DE10344442B3 DE 10344442 B3 DE10344442 B3 DE 10344442B3 DE 10344442 A DE10344442 A DE 10344442A DE 10344442 A DE10344442 A DE 10344442A DE 10344442 B3 DE10344442 B3 DE 10344442B3
Authority
DE
Germany
Prior art keywords
layer
inner pane
borosilicate glass
color
reflecting layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE10344442A
Other languages
German (de)
Inventor
Holger Haustein
Erhard Schwarz
Rainer Lebacher
Michael Wagner
Klemens Roch
Wolfgang Schnell
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Schott AG
BSH Hausgeraete GmbH
Original Assignee
BSH Bosch und Siemens Hausgeraete GmbH
Schott Glaswerke AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BSH Bosch und Siemens Hausgeraete GmbH, Schott Glaswerke AG filed Critical BSH Bosch und Siemens Hausgeraete GmbH
Priority to DE10344442A priority Critical patent/DE10344442B3/en
Priority to US10/939,601 priority patent/US20050092318A1/en
Priority to SE0402195A priority patent/SE0402195L/en
Priority to JP2004272665A priority patent/JP4312687B2/en
Priority to FR0410070A priority patent/FR2862373B1/en
Priority to CNB2004100826272A priority patent/CN1311202C/en
Application granted granted Critical
Publication of DE10344442B3 publication Critical patent/DE10344442B3/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Die Erfindung wendet sich an eine Gargerätetür sowie an Gargeräte mit einer derartigen Tür, die eine Innenscheibe (1) aus Borosilikat-Glas, auf der eine Farbschicht (2) aus einer hochtemperaturfesten Nicht-Emailfarbe mit organischen oder anorganischen Bindern und eine infrarot-reflektierende Schicht (3) aufgebracht sind, besitzen.
Um eine gute Haftfestigkeit und einen hohen Kratzschutz bezüglich der Farbschicht (2) zu erzielen, ist die Farbschicht (2) direkt auf einer Seite der Innenscheibe (1) und die infrarot-reflektierende Schicht (3) auf dieser Farbschicht (2) aufgebracht.
Durch die erfindungsgemäße Umkehr der üblichen Prozessreihenfolge erhält man eine widerstandsfähige Farbbedruckung, die eine hohe Haftfestigkeit am Glas hat und durch den Schutz der harten IR-Reflexionsschicht zusätzlich kratzfester ist.The invention relates to a cooking device door and to cooking devices with such a door, which has an inner pane (1) made of borosilicate glass, on which a color layer (2) made of a high-temperature-resistant non-enamel paint with organic or inorganic binders and an infrared-reflecting layer (3) are applied.
In order to achieve good adhesive strength and high scratch protection with respect to the color layer (2), the color layer (2) is applied directly to one side of the inner pane (1) and the infrared-reflecting layer (3) is applied to this color layer (2).
By reversing the usual process sequence according to the invention, a resistant color printing is obtained which has a high adhesive strength to the glass and is additionally more scratch-resistant due to the protection of the hard IR reflection layer.

Figure 00000001
Figure 00000001

Description

Die Erfindung bezieht sich auf eine Gargerätetür mit einer Innenscheibe aus Borosilikat-Glas, auf der eine Farbschicht aus einer hochtemperaturfesten Nicht-Emailfarbe mit organischen oder anorganischen Bindern und eine infrarot-reflektierende Schicht aufgebracht sind.The Invention relates to a cooking appliance door with an inner pane Borosilicate glass, on which a color layer made of a high-temperature resistant non-enamel paint with organic or inorganic binders and an infrared reflecting layer are upset.

Die Erfindung betrifft ferner ein Gargerät mit einer derartigen Tür.The The invention further relates to a cooking appliance with such a door.

Haushaltsgargeräte, insbesondere Garöfen, besitzen bestimmungsgemäß einen Garraum mit einer Beschickungsöffnung, die durch eine Tür mit einem Sichtfenster verschließbar ist. Auch Gargeräte mit Vollglastüren sind bekannt. Ein typisches Haushaltsgerät ist dabei der Backofen mit der Ofenmuffel als Garraum, der heutzutage bereits in beachtlichem Umfang mit einer pyrolytischen Selbstreinigung ausgestattet ist, durch die Garrückstände bei Pyrolysetemperaturen von über 500°C zu Asche zersetzt werden.Household cooking appliances, in particular Own ovens intended one Cooking space with a loading opening, through a door can be closed with a viewing window. Cooking appliances with full glass doors are also known. A typical household appliance is the oven the oven muffle as a cooking space, which is already considerable today is equipped with pyrolytic self-cleaning, by the cooking residues Pyrolysis temperatures of over 500 ° C too Ashes are decomposed.

Durch die relativ hohen Temperaturen im Garraum der Haushaltsgargeräte erhitzt sich auch die Gargerätetür und damit das Sichtfenster bzw. die Vollglastür, die typischerweise aus einem Glasscheibenpaket besteht, entsprechend. Dies gilt im besonderen Maße für die bei der Pyrolyse auftretenden extrem hohen Temperaturen in Pyrolyse-Backöfen. Wegen dieser Temperaturbelastungen werden daher bei Sichtfenstern oder Vollglastüren für Gargeräte, insbesondere für Backöfen mit pyrolytischer Selbstverbrennung, hochwertigere Gläser für die Türscheiben eingesetzt. Für die der Ofenmuffel am nächsten liegende Innenscheibe wird dazu ein Borosilikat-Glas eingesetzt, das vorzugs weise vorgespannt ist. Ein solches Glas zeichnet sich durch eine besondere Temperaturbeständigkeit aus.By the relatively high temperatures in the cooking space of the household cooking appliances the cooking appliance door and thus the viewing window or the full glass door, which typically consists of one Glass pane package exists, accordingly. This is especially true Dimensions for the at the extremely high temperatures that occur in pyrolysis ovens. Because of these temperature loads are therefore in viewing windows or Full glass doors for cooking devices, in particular for ovens with pyrolytic self-immolation, higher quality glasses used for the door panes. For the the furnace muffle closest the inner pane is a borosilicate glass, which is preferably biased. Such a glass stands out with a special temperature resistance.

Um die Temperatur an der Außenseite der Sichtfenster oder Vollglastüren der Gargeräte wegen der Gefahr von Brandverletzungen beim Berühren der Außenscheibe des Sichtfensters möglichst gering zu halten, ist es bekannt, am Sichtfenster eine zum Garraum hin wärme- d.h. infrarot-reflektierende Beschichtung vorzusehen. So wird in der US 4 898 147 ein Beobachtungsfenster beschrieben, dessen aus Borosilikat-Glas bestehende Innenscheibe mit einer Infrarotstrahlen reflektierenden Mehrfachbeschichtung versehen ist, um zusammen mit einer zwischen Außen- und Innenscheibe vorgesehenen Edelgasschicht den Wärmeübergang zu reduzieren. Mit dieser Maßnahme soll eine so genannte „Kalte Tür" für Pyrolysebacköfen geschaffen werden, die nach GIFAM DOC 266/01 definiert ist durch Angabe der Grenztemperaturen, die bei ca. 500°C im Garraum an der Berührungsfläche der Tür bei Raumtemperatur von 23°C herrschen dürfen (bei Glas <70°C).In order to keep the temperature on the outside of the viewing window or full glass doors of the cooking appliances as low as possible due to the risk of fire injuries when the outer pane of the viewing window is touched, it is known to provide the viewing window with a coating which is heat-reflecting towards the cooking chamber, ie infrared. So in the US 4,898,147 described an observation window, the inner pane made of borosilicate glass is provided with an infrared radiation-reflecting multiple coating in order to reduce the heat transfer together with a noble gas layer provided between the outer and inner pane. This measure is intended to create a so-called "cold door" for pyrolysis ovens, which is defined in accordance with GIFAM DOC 266/01 by specifying the limit temperatures that are at approx. 500 ° C in the cooking space on the contact surface of the door at room temperature of 23 ° C may prevail (with glass <70 ° C).

Ferner ist es bekannt, auf der Innenscheibe aus Borosilikat-Glas eine Bedruckung aus Emailfarben vorzusehen, um im speziellen Schrift (Buchstaben, Wörter) und Symbole darzustellen, insbesondere als Gebrauchshinweise für den Benutzer, beispielsweise verschiedene Garprogramme. Diese Bedruckung kann sowohl auf der dem Türinneren zugewandten Seite als auch auf der dem Garraum zugewandten Seite der Borosilikat-Innenscheibe erfolgen, wie in der DE 100 07 923 C1 beschrieben wird. Auch die DE 101 43 925 A1 zeigt eine entsprechende, mit Emailfarben bedruckte Borosilikat-Innenscheibe für Gargerätetüren.Furthermore, it is known to provide printing on enamel colors on the inner pane made of borosilicate glass in order to represent special writing (letters, words) and symbols, in particular as instructions for use for the user, for example various cooking programs. This printing can take place both on the side facing the inside of the door and on the side facing the cooking space of the inner borosilicate pane, as in FIG DE 100 07 923 C1 is described. Also the DE 101 43 925 A1 shows a corresponding borosilicate inner pane printed with enamel colors for cooking appliance doors.

Übliche Emailfarben verschmelzen beim Aufbrennen auf die Borosilikat-Innenscheibe mit der Glasoberfläche. Bei starker Temperaturbelastung kann es daher aufgrund der unterschiedlichen Wärmeausdehnung von Glasscheibe und Bedruckung zu Spannungen in der Glasscheibe kommen, die in Verbindung mit Wechselwirkungen (Ionenaustausch) zwischen der Emailfarbe, einer glasfluss-basierten Druckfarbe, und dem Borosilikat-Glas, die Schlagfestigkeit der Glasscheibe herabsetzen wenn der Schlag auf der der Bedruckung abgewandten Seite erfolgt. Daher wird in der vorgenannten DE 100 07 923 C1 vorgeschlagen, die Bedruckung mit der Emailfarbe auf der dem Garraum zugewandten, schlaggefährdeten Außenseite der Innenscheibe aufzubringen. Da derzeitige Emailfarben nicht schwermetallfrei, insbesondere nicht bleifrei sind, besteht durch die Bedruckung auf der offenen, mit dem Garraum im direkten Kontakt stehenden Seite der Innenscheibe die Gefahr, dass bei hoher Temperaturbelastung Schwermetalle, insbesondere Blei, in den Garraum „abdampfen" können. Außerdem besitzt die Emailfarbschicht eine rauhe, wenig ästhetisch anmutende Oberfläche.Common enamel colors fuse with the glass surface when they are burned onto the borosilicate inner pane. At high temperature loads, the different thermal expansion of the glass pane and the printing can lead to tensions in the glass pane, which, in conjunction with interactions (ion exchange) between the enamel paint, a glass flow-based printing ink, and the borosilicate glass, reduce the impact resistance of the glass pane if the stroke occurs on the side facing away from the printing. Therefore, in the aforementioned DE 100 07 923 C1 proposed to apply the printing with the enamel paint on the outside of the inner pane, which is at risk of impact and faces the cooking space. Since current enamel paints are not free of heavy metals, especially not lead-free, the printing on the open side of the inner pane, which is in direct contact with the cooking space, means that heavy metals, especially lead, can "evaporate" into the cooking space when exposed to high temperatures the enamel color layer has a rough, unattractive surface.

Da es somit derzeit für Borosilikat-Glas keine Emailbedruckung gibt, die

  • 1. schwermetallfrei ist
  • 2. eine glatte ästhetisch anmutende Oberfläche hat, und
  • 3. die Schlagfestigkeit der Borosilikat-Glasscheibe erhält, wenn der Schlag auf der der Beschichtung abgewandten Seite aufgebracht wird,
wurde eine Nicht-Emailfarbe mit organischen (z.B. Silikonen oder Fluorpolymere) oder anorganischen (Wasserglas; Sol-Gel-Binder) Bindern entwickelt, die im Gegensatz zur üblichen Emailfarbe nicht durch Verschmelzen mit der Glasoberfläche verbunden wird. Diese nicht-keramische Farbe wird in der älteren Patentanmeldung DE 103 13 630 beschrieben, deren Offenbarung mit zum Offenbarungsinhalt dieser Patentanmeldung durch Bezugnahme gemacht wird.Since there is currently no enamel printing for borosilicate glass, the
  • 1. is free of heavy metals
  • 2. has a smooth, aesthetically pleasing surface, and
  • 3. maintains the impact resistance of the borosilicate glass pane when the impact is applied to the side facing away from the coating,
a non-enamel paint with organic (e.g. silicones or fluoropolymers) or inorganic (water glass; sol-gel binder) binders was developed, which, in contrast to the usual enamel paint, is not fused to the glass surface. This non-ceramic paint is used in the earlier patent application DE 103 13 630 described, the disclosure of which is made by reference to the disclosure content of this patent application becomes.

Es handelt sich bei dieser Farbe letztlich um eine SiO2-basierte Farbe mit Kohlenstoff als Pigment, die vom SiO2 umhüllt sind, wie es z.B. in der DE 195 25 658 C1 beschrieben ist.Ultimately, this color is an SiO 2 -based color with carbon as a pigment, which is coated with SiO 2 , as is the case, for example, in DE 195 25 658 C1 is described.

Beim Farbbedrucken von infrarot-reflektierend beschichteten Innenscheiben von Sichtfenstern aus Borosilikat-Glas mit der vorgesehenen Nicht-Emailfarbe hat man bislang versucht die Farbschicht direkt auf die infrarot-reflektierende Schicht aufzubringen. Dies führte zu einer gewissen Prozessunsicherheit, da die Haftung der für die direkte Haftung auf Borosilikat-Glas entwickelte Farbe auf einer die Infrarotstrahlung reflektierenden Schicht, die üblicherweise aus einem Zinnoxid-Material besteht, nicht sicher gestellt ist. Außerdem ist die vorgenannte Farbbeschichtung nicht sehr beständig gegen Verkratzen.At the Color printing of infrared reflective coated inner panes of viewing windows made of borosilicate glass with the intended non-enamel color So far, one has tried the color layer directly on the infrared reflecting layer Apply layer. This resulted to a certain process uncertainty, since the liability for direct Adhesion to borosilicate glass developed color on an infrared radiation reflective layer, which is usually consists of a tin oxide material, is not ensured. In addition the aforementioned color coating is not very resistant to Scratch.

Der Erfindung liegt die Aufgabe zugrunde, die eingangs bezeichnete Gargerätetür mit Innenscheibe aus Borosilikat-Glas hinsichtlich der Beschichtung der Innenscheibe mit einer infrarot-reflektierenden Schicht und einer Bedruckung so auszubilden, dass die Bedruckung sicher haftet und beständig gegen Verkratzen ist.Of the The invention is based on the object, the cooking appliance door described at the beginning with an inner pane made of borosilicate glass with regard to the coating of the inner pane with an infrared reflecting layer and a print to be trained so that the printing adheres securely and is resistant to Is scratching.

Die Lösung dieser Aufgabe gelingt erfindungsgemäß bei einer Gargerätetür mit einer Innenscheibe aus Borosilikat-Glas, auf der eine Farbschicht aus einer hochtemperaturfesten Nicht-Emailfarbe mit organischen oder anorganischen Bindern und eine infrarot-reflektierende Schicht aufgebracht sind, bzw. bei dem zugehörigen Gargerät mit einer derartigen Tür, überraschenderweise dadurch, dass die Farbschicht direkt auf einer Seite der Innenscheibe und die infrarot-reflektierende Schicht auf dieser Farbschicht aufgebracht ist.The solution this object is achieved according to the invention in a cooking appliance door with a Inner pane made of borosilicate glass, on which a layer of paint a high temperature resistant non-enamel paint with organic or inorganic binders and an infrared reflecting layer are applied, or the associated one Cooking appliance with such a door, surprisingly in that the layer of paint directly on one side of the inner pane and the infrared reflective Layer is applied to this color layer.

Durch die erfindungsgemäßen Maßnahmen, d.h. die infrarot-reflektierende Schicht erst nach dem Auftragen der Farbe aufzubringen, erhält man mit großem Vorteil eine widerstandfähigere Farbbedruckung der Innenscheibe aus Borosilikat-Glas. Neben der höheren Haftfähigkeit der Farbe auf dem Glassubstrat wird die Farbbedruckung zusätzlich kratzfester, da die infrarot-reflektierende Schicht sehr hart ist und damit die Farbbedruckung insoweit mechanisch schützt. Da aufgrund der eingesetzten Farbe für die Farbbedruckung die Schlagfestigkeit auch erhalten bleibt, wenn der Schlag auf der der Bedruckung abgewandten Seite der Innenscheibe erfolgt, kann die Bedruckung auch auf der dem Garraum abgewandten Seite der Innenscheibe erfolgen, d.h. es ist dann insoweit keine Wechselwirkung zwischen den Schichten und dem Garraum vorhanden.By the measures according to the invention, i.e. the infrared reflective Applying the layer only after applying the paint is a great advantage a more resilient Color printing of the inner pane made of borosilicate glass. In addition to the higher adhesiveness the color on the glass substrate, the color printing is also more scratch-resistant, because the infrared reflecting layer is very hard and therefore the Color printing mechanically protects. Because due to the used Color for the color printing the impact resistance is retained even if the blow on the side of the inner pane facing away from the printing printing can also be carried out on the side facing away from the cooking space Side of the inner pane, i.e. then it is not so far Interaction between the layers and the cooking space.

Natürlich kann die Bedruckung auch auf der dem Garraum zugewandten Seite der Innenscheibe erfolgen, zumal die infrarot-reflektierende Schicht die Farbbedruckung abdeckt und das Austreten von Farbanteilen der Bedruckung in den Garraum zumindest mindert.Of course you can the printing also takes place on the side of the inner pane facing the cooking space, especially the infrared reflective Layer covers the color printing and the leakage of color components at least reduces the printing in the cooking space.

Durch die DE 101 62 220 A1 ist es bekannt, auf der Glasscheibe einer Gargerätetür eine zweilagige Beschichtung, bestehend aus einer ersten dunklen, insbesondere schwarz eingefärbten, wärmeabstrahlenden und einer darüber angeordneten zweiten weiß eingefärbten, wärmereflektierenden Schicht aufzubringen. Die zweite Schicht soll einen wesentlichen Teil der Strahlungswärme in den Ofen zurückreflektieren, woge gen durch die erste dunkle Schicht Wärme, welche die Glasscheibe erreicht, gut abgestrahlt werden soll.Through the DE 101 62 220 A1 it is known to apply a two-layer coating on the glass pane of a cooking appliance door, consisting of a first dark, in particular black-colored, heat-radiating layer and a second white-colored, heat-reflecting layer arranged above it. The second layer should reflect a substantial part of the radiant heat back into the furnace, whereas the first dark layer should radiate heat that reaches the glass pane.

Hinweise auf eine Farbschicht aus einer Nicht-Emailfarbe und die zugehörigen Haftungsprobleme finden sich in dieser Schrift aufgrund der unterschiedlichen Problemstellungen nicht.Hints on a layer of paint from a non-enamel paint and the associated liability problems can be found in this document due to the different problems Not.

Ausgestaltungen der Erfindung sind in Unteransprüchen gekennzeichnet und ergeben sich zudem aus der Figurenbeschreibung.refinements of the invention are in subclaims marked and also result from the description of the figures.

Die einzige Figur der Patentzeichnung zeigt schematisch eine Innenscheibe 1 eines Sichtfensters für eine Gargerätetür oder einer Vollglastür, insbesondere für einen Garofen. Diese Innenscheibe 1 ist durch ihre unmittelbare Nähe zur im Betrieb des Garofens heißen Ofenmuffel den höchsten Temperaturen ausgesetzt, insbesondere wenn der Garofen eine pyrolytische Selbstreinigung aufweist, bei der Temperaturen von über 500°C auftreten. Aus diesem Grund besteht die Innenscheibe 1 aus einem Borosilikat-Glas, vorzugsweise aus einem vorgespannten Borosilikat-Glas, das auch bei diesen Temperaturen beständig ist und eine niedrige Wärmeausdehnung aufweist. Auf einer Seite der Innenscheibe ist eine Farbbedruckung 2 aufgedruckt, die eine getönte Fläche sein kann oder auch Schrift oder Symbole als Hinweise für den Benutzer, beispielsweise über verschiedene Garprogramme, aufweisen kann. Die Bedruckung 2 wird aus den eingangs beschriebenen Nicht-Emailfarben hergestellt, die direkt auf die Oberfläche des Borosilikat-Glases der Innenscheibe 1 mittels eines Druckverfahrens, insbesondere eines Siebdruckverfahrens, aufgebracht und danach eingebrannt werden. Die Schichtdicke liegt vorzugsweise im Bereich von 10–15μm. Die Bedruckung erfolgt vorzugsweise in einem Punktraster.The only figure in the patent drawing schematically shows an inner pane 1 a viewing window for a cooking appliance door or a full glass door, in particular for a cooking oven. This inner pane 1 is exposed to the highest temperatures due to its close proximity to the oven muffle that is hot during operation of the oven, especially if the oven has pyrolytic self-cleaning at temperatures of over 500 ° C. For this reason there is the inner pane 1 from a borosilicate glass, preferably from a toughened borosilicate glass, which is stable even at these temperatures and has a low thermal expansion. There is color printing on one side of the inner pane 2 printed, which can be a tinted surface or can also have writing or symbols as information for the user, for example about different cooking programs. The printing 2 is made from the non-enamel paints described above, which are applied directly to the surface of the borosilicate glass on the inner pane 1 by means of a printing process, in particular a screen printing process, applied and then baked. The layer thickness is preferably in the range of 10-15 μm. The printing is preferably done in a dot matrix.

Anschließend wird auf die Farbdruckschicht 2 eine infrarot-reflektierende Schicht 3 aufgetragen, z.B. im Heißsprühverfahren. Diese Schicht 3 enthält typischerweise Zinnoxid als „Wirkstoff" und ist im Übrigen, z.B. hinsichtlich Schichtdicke etc., in bekannter Weise ausgebildet. Diese IR-Reflexionsschichten sind insbesondere aus der Anwendung für Wärmeschutzverglasungen (z.B. K-Glas® oder OPTIFLOAT® Spiegelglas) bekannt, und werden beispielsweise in der DE 198 25 437 A1 beschrieben. Da die infrarot-reflektierende Schicht 3 sehr hart ist, wird dadurch auch die Kratzfestigkeit der Farbbeschichtung 2 erhöht, deren Haftfestigkeit unmittelbar auf der Glasoberfläche sehr hoch ist.Then apply to the color print layer 2 an infrared reflective layer 3 applied, for example by hot spraying. This layer 3 contains typically tin oxide as the "active ingredient" and is otherwise such as with regard to layer thickness, etc., formed in a known manner. These IR reflecting layers are known in particular from the application for thermal insulation glazing (eg, K-Glass ® or Optifloat ® mirror glass), and, for example, in of the DE 198 25 437 A1 described. Because the infrared reflective layer 3 is very hard, it also increases the scratch resistance of the color coating 2 increased, the adhesive strength of which is very high directly on the glass surface.

Die einzige Figur zeigt jeweils nur eine einzige IR-Reflexions- und Farbschicht. Es versteht sich, dass die jeweilige Schicht auch mehr als nur eine Schicht umfassen kann.The single figure shows only a single IR reflection and Coat of paint. It is understood that the respective layer also more than just one layer.

Claims (6)

Gargerätetür mit einer Innenscheibe (1) aus Borosilikat-Glas, auf der mindestens eine Farbschicht (2) aus einer hochtemperaturfesten Nicht-Emailfarbe mit organischen oder anorganischen Bindern und mindestens eine infrarot-reflektierende Schicht (3) in der Weise aufgebracht sind, dass die Farbschicht (2) direkt auf einer Seite der Innenscheibe (1) und die infrarot-reflektierende Schicht (3) auf dieser Farbschicht (2) aufgebracht ist.Cooking appliance door with an inner pane ( 1 ) made of borosilicate glass, on which at least one color layer ( 2 ) made of a high temperature resistant non-enamel paint with organic or inorganic binders and at least one infrared reflecting layer ( 3 ) are applied in such a way that the color layer ( 2 ) directly on one side of the inner pane ( 1 ) and the infrared reflecting layer ( 3 ) on this layer of paint ( 2 ) is applied. Gargerätetür nach Anspruch 1, dadurch gekennzeichnet, dass die Farbschicht (2) eine Dicke im Bereich von 10–15 μm hat.Cooking appliance door according to claim 1, characterized in that the color layer ( 2 ) has a thickness in the range of 10-15 μm. Gargerätetür nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass die Farbschicht (2) auf die Innenscheibe (1) aufgedruckt ist.Cooking appliance door according to claim 1 or 2, characterized in that the color layer ( 2 ) on the inner pane ( 1 ) is printed. Gargerätetür nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass die infrarot-reflektierende Schicht (3) Zinnoxid enthält.Cooking appliance door according to one of claims 1 to 3, characterized in that the infrared-reflecting layer ( 3 ) Contains tin oxide. Gargerätetür nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass die infrarot-reflektierende Schicht (3) nach dem Heißsprüh-Verfahren auf die Farbschicht (2) aufgebracht ist.Cooking appliance door according to one of claims 1 to 4, characterized in that the infrared-reflecting layer ( 3 ) after the hot spray process on the color layer ( 2 ) is applied. Gargerät mit – einem Garraum mit einer Beschickungsöffnung zum Einbringen von Gargut und – einer Gargerätetür nach einem der vorhergehenden Ansprüche zum Verschließen der Beschickungsöffnung des Garraumes.Cooking appliance With - one Cooking space with a loading opening for Placing food and - one Cooking appliance door after one of the preceding claims to lock the loading opening of the cooking space.
DE10344442A 2003-09-25 2003-09-25 Oven door for a household oven comprises an inner pane made from borosilicate glass on which a colored layer made from a high temperature resistant non-enamel paint with organic or inorganic binder and an IR-reflecting layer are applied Expired - Lifetime DE10344442B3 (en)