DE102006011666A1 - Grease composition for cable strands - Google Patents
Grease composition for cable strands Download PDFInfo
- Publication number
- DE102006011666A1 DE102006011666A1 DE102006011666A DE102006011666A DE102006011666A1 DE 102006011666 A1 DE102006011666 A1 DE 102006011666A1 DE 102006011666 A DE102006011666 A DE 102006011666A DE 102006011666 A DE102006011666 A DE 102006011666A DE 102006011666 A1 DE102006011666 A1 DE 102006011666A1
- Authority
- DE
- Germany
- Prior art keywords
- fat composition
- range
- weight
- grease composition
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Die vorliegende Erfindung betrifft eine Fettzusammensetzung zur Verwendung bei Kabelsträngen, welche ein Verdickungsmittel, eine Ölgrundlage und Additive umfasst, wobei die Ölgrundlage einen Polyoxyalkylenglykolether umfasst und die Additive eine Chinolinverbindung und eine Benzotriazolverbindung umfassen. Die Fettzusammensetzung ist bei der Korrosionsbeständigkeit, der Oxidationsstabilität und der Kompatibilität mit Materialien wie Olefinelastomer ganz ausgezeichnet.The present invention relates to a grease composition for use in cable harnesses which comprises a thickener, an oil base and additives, the oil base comprising a polyoxyalkylene glycol ether and the additives comprising a quinoline compound and a benzotriazole compound. The fat composition is quite excellent in corrosion resistance, oxidation stability and compatibility with materials such as olefin elastomer.
Description
Die vorliegende Erfindung betrifft eine Fettzusammensetzung zur Verwendung bei einem Kabelstrang.The The present invention relates to a fat composition for use in a cable harness.
Bei verschiedenen Kraftfahrzeugmotorzubehörvorrichtungen, insbesondere Kabelstrangbestandteilen, die in der Nähe eines Klimageräts angeordnet sind, kann das Kondenswasser, welches zum Beispiel von der in der Atmosphäre vorhandenen Feuchtigkeit herrührt, in zum Beispiel eine Verbindungsvorrichtung eindringen, wodurch metallische Teile, aus welchen dieselbe besteht (Materialien für Kontaktteile), korrodieren und deshalb sollten diese metallischen Teile sicher vor einer solchen Korrosion geschützt werden. Zusätzlich sollte ein Gleitmittel (eine Fettzusammensetzung, die durch Zugeben eines Verdickungsmittels zu einer Ölgrundlage und dann Formen der resultierenden Mischung zu einem halbfesten Produkt erhalten wird) zum Beispiel die folgenden Anforderungen erfüllen: es sollte eine ausgezeichnete Korrosionsbeständigkeit und Oxidationsstabilität aufweisen, damit diese Teile über einen langen Zeitraum verwendet werden können oder um die Nutzungsdauer der Teile auszuweiten. Darüber hinaus wurde kürzlich das Polyvinylchlorid als ein Beschichtungsmaterial für metallische Teile durch Olefinelastomere ersetzt, mit dem Zweck die Menge an Materialien zu verringern, von welchen es sein kann, dass sie nicht umweltfreundlich sind, und demgemäß war es gewünscht, eine solche Fettzusammensetzung zu gestalten, während die Kompatibilität davon mit den Beschichtungsmaterialien für solche Teile berücksichtigt wurde.at various motor vehicle engine accessory devices, in particular Wiring harness components located near an air conditioner are, can the condensation, which for example from in the the atmosphere existing moisture, in, for example, a connecting device, whereby metallic parts of which it consists (materials for contact parts), corrode and therefore these metallic parts should be safe be protected from such corrosion. In addition, should a lubricant (a fat composition obtained by adding a Thickener to an oil base and then forming the resulting mixture into a semi-solid Product is obtained), for example, the following requirements fulfill: it should have excellent corrosion resistance and oxidation stability so that these parts over can be used over a long period of time or around the useful life expand the parts. About that Beyond was recently the polyvinyl chloride as a coating material for metallic Parts replaced by olefin elastomers, with the purpose of the amount To reduce materials that it may not be Environmentally friendly, and accordingly, it was desired, a to make such fat composition while the compatibility thereof considered with the coating materials for such parts has been.
Herkömmlicherweise wurde als eine Fettzusammensetzung zum Auffüllen der Kabelverbindungsverteilervorrichtung eines Kabelbaums, der für Kraftfahrzeuge verwendet wird, eine Fettzusammensetzung mit ausgezeichneter Wärmebeständigkeit berichtet (Patentdokument 1: JP-B-6-99702). Jedoch verwendet diese Fettzusammensetzung ein gereinigtes Mineralöl als eine Ölgrundlage und deshalb wird diese Fettzusammensetzung als mit niedriger Kompatibilität mit zum Beispiel Olefinelastomeren angesehen und für diese Zusammensetzung ist keine ausreichende Berücksichtigung der Korrosionsbeständigkeit und der Oxidationsstabilität vorgesehen.traditionally, was used as a grease composition to fill up the cable joint manifold device of a wiring harness used for Motor vehicles is used, a fat composition with excellent heat resistance reported (Patent Document 1: JP-B-6-99702). However, this fat composition uses a purified mineral oil as an oil basis and therefore this fat composition is considered to have low compatibility with the Example olefinic elastomers and is for this composition insufficient consideration the corrosion resistance and the oxidation stability provided.
Zusätzlich wurde auch von einer Fettzusammensetzung zur Verwendung in einer geschwindigkeitsverringernden Vorrichtung (Getriebe) berichtet, die ausgezeichnete antikorrosive Eigenschaften aufweist und die Materialien wie Gummimaterialien nicht zu stark nachteilig beeinflusst (Patentdokument 2: JP-A-4-266995; Patentdokument 3: JP-A-63-309591; und Patentdokument 4: JP-A-64-29496). Diese Fettzusammensetzungen können die Anforderung für die Kompatibilität mit den Beschichtungsmaterialien für solche Teile, zum Beispiel Olefinelastomere, erfüllen, sie sind aber nicht immer bei der Korrosionsbeständigkeit und der Oxidationsstabilität ausreichend.In addition was also of a fat composition for use in a rate reducing Device (gearbox) reports that are excellent anticorrosive Features and materials such as rubber materials not too much adversely affected (Patent Document 2: JP-A-4-266995; 3: JP-A-63-309591; and Patent Document 4: JP-A-64-29496). These fat compositions can the requirement for the compatibility with the coating materials for such parts, for example Olefin elastomers, fulfill, but they are not always sufficient in corrosion resistance and oxidation stability.
Demgemäß ist es eine Aufgabe der vorliegenden Erfindung eine Fettzusammensetzung für Kabelstränge bereit zu stellen und genauer eine Fettzusammensetzung für Kabelstränge bereit zu stellen, die bei der Kompatibilität mit den Beschichtungsmaterialien für Teile der Kabelstränge wie Olefinelastomere, der Korrosionsbeständigkeit und der Beständigkeit gegen Oxidation ausgezeichnet ist.Accordingly, it is An object of the present invention is a fat composition ready for cable strands to provide and more precisely a grease composition for cable strands to ask for compatibility with the coating materials for parts the cable strands such as olefin elastomers, corrosion resistance and durability is excellent against oxidation.
Die Erfinder haben deshalb verschiedene Untersuchungen durchgeführt, um die vorstehenden Nachteile zu beseitigen, die mit den vorstehenden herkömmlichen Techniken in Zusammenhang stehen, welche Fettzusammensetzungen für insbesondere Kabelstränge betreffen, haben gefunden, dass die vorstehenden Nachteile wirksam durch die Verwendung einer Ölgrundlage beseitigt werden können, die eine spezielle Komponente und spezielle Verbindungen als Additive für die Fettzusammensetzung enthalten, und haben so die vorliegende Erfindung vervollständigt.The Inventors have therefore carried out various studies to to overcome the above disadvantages associated with the above usual Techniques related to which fat compositions for particular harnesses relate, have found that the above disadvantages are effective through the use of an oil base can be eliminated the one special component and special compounds as additives for the Contain fat composition, and so have the present invention completed.
Gemäß der vorliegenden Erfindung wird folglich eine Fettzusammensetzung zur Verwendung bei Kabelsträngen bereitgestellt, die ein Verdickungsmittel, eine Ölgrundlage und Additive umfasst, wobei die Ölgrundlage einen Polyoxyalkylenglykolether umfasst und die Additive eine Chinolinverbindung und eine Benzotriazolverbindung umfassen.According to the present The invention thus provides a fat composition for use in cable harnesses provided comprising a thickening agent, an oil base and additives, the oil base a polyoxyalkylene glycol ether and the additives include a quinoline compound and a benzotriazole compound.
In einer bevorzugten Ausführungsform der erfindungsgemäßen Fettzusammensetzung zur Verwendung bei Kabelsträngen ist das Verdickungsmittel mindestens ein aus Lithiumseifen und Bentonitmaterialien, die mit organischen Verbindungen modifiziert sind, (organisch modifizierten Bentonitmaterialien) ausgewähltes Verdickungsmittel.In a preferred embodiment the fat composition of the invention for use with cable harnesses For example, the thickening agent is at least one of lithium soaps and bentonite materials modified with organic compounds, (organically modified Bentonite materials) selected thickener.
In einer weiteren bevorzugten Ausführungsform der erfindungsgemäßen Fettzusammensetzung zur Verwendung bei Kabelsträngen weist der Polyoxyalkylenglykolether eine kinematische Viskosität, wie bei einer Temperatur von 40°C bestimmt, im Bereich von 30 bis 400 mm2/s auf.In a further preferred embodiment of the grease composition according to the invention for use in cable strands, the polyoxyalkylene glycol ether has a kinematic viscosity, as determined at a temperature of 40 ° C, in the range of 30 to 400 mm 2 / s.
In noch einer weiteren bevorzugten Ausführungsform der erfindungsgemäßen Fettzusammensetzung zur Verwendung bei Kabelsträngen liegt der Gehalt der Chinolinverbindung im Bereich von 0,1 bis 10 Gew.-%, bezogen auf das Gesamtgewicht der Fettzusammensetzung, und der Gehalt der Benzotriazolverbindung liegt im Bereich von 0,1 bis 10 Gew.-%, bezogen auf das Gesamtgewicht der Fettzusammensetzung.In Yet another preferred embodiment of the fat composition according to the invention Use with cable harnesses the content of the quinoline compound is in the range of 0.1 to 10 Wt .-%, based on the total weight of the fat composition, and the content of the benzotriazole compound is in the range of 0.1 to 10 wt .-%, based on the total weight of the fat composition.
Die erfindungsgemäße Fettzusammensetzung verwendet eine Polyoxyalkylenglykolether enthaltende Ölgrundlage und umfasst als Additive eine Chinolinverbindung und eine Benzotriazolverbindung und deshalb ist die Fettzusammensetzung bei der Kompatibilität mit den Beschichtungsmaterialien für Teile der Kabelstränge wie Olefinelastomere, der Korrosionsbeständigkeit und der Beständigkeit gegen Oxidation ausgezeichnet.The fat composition according to the invention uses a polyoxyalkylene glycol ether-containing oil base and includes as additives a quinoline compound and a benzotriazole compound and therefore the fat composition is in compatibility with the Coating materials for Parts of the cable strands such as olefin elastomers, corrosion resistance and durability excellent against oxidation.
Die
erfindungsgemäße Fettzusammensetzung
ist dadurch gekennzeichnet, dass sie als eine Ölgrundlage eine Ölgrundlage
verwendet, die einen Polyoxyalkylenglykolether enthält, der
die Olefinmaterialien nicht zu stark nachteilig beeinflusst. Bevorzugt
werden in der vorliegenden Erfindung Polyoxyalkylenglykolether verwendet,
die durch die folgende allgemeine Formel I dargestellt werden:
In Formel I stellen R1 und R3 jeweils unabhängig ein Wasserstoffatom oder einen Alkylrest mit 1 bis 20, bevorzugt 1 bis 6 Kohlenstoffatomen (wie eine Methylgruppe, eine Ethylgruppe, eine Propylgruppe, eine Isopropylgruppe, eine Butylgruppe, eine Isobutylgruppe, eine Pentylgruppe oder eine Hexylgruppe) dar; R2 stellt einen Alkylrest mit 1 bis 10, bevorzugt 1 bis 4 Kohlenstoffatomen (wie eine Methylgruppe, eine Ethylgruppe, eine Propylgruppe oder eine Butylgruppe) dar; und n stellt eine Zahl dar, die im Bereich von 5 bis 30 und bevorzugt 8 bis 20 liegt, mit der Maßgabe, dass R1 und R3 nicht gleichzeitig Wasserstoffatome darstellen.In formula I, R 1 and R 3 each independently represent a hydrogen atom or an alkyl group having 1 to 20, preferably 1 to 6 carbon atoms (such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a pentyl group or a Hexyl group); R 2 represents an alkyl group having 1 to 10, preferably 1 to 4 carbon atoms (such as a methyl group, an ethyl group, a propyl group or a butyl group); and n represents a number ranging from 5 to 30, and preferably 8 to 20, provided that R 1 and R 3 are not simultaneously hydrogen atoms.
Spezielle Beispiele der Polyoxyalkyleneinheiten der durch die allgemeine Formel I dargestellten Polyoxyalkylenglykolether schließen Polyoxyethylen, Polyoxypropylen, Poly(oxypropylenoxyethylen), Poly(oxybutylenoxyethylen), Poly(oxybutylenoxypropylen), Poly(oxypentylenoxyethylen) und Poly(oxypentylenoxypropylen) ein.Specific Examples of the polyoxyalkylene units represented by the general formula Polyoxyalkylene glycol ethers include polyoxyethylene, polyoxypropylene, poly (oxypropyleneoxyethylene), Poly (oxybutyleneoxyethylene), poly (oxybutyleneoxypropylene), poly (oxypentylenoxyethylene) and poly (oxypentylenoxypropylene).
Die durch die allgemeine Formel I dargestellten Polyoxyalkylenglykolether, die hier verwendet werden können, können ein Monoether oder ein Diether sein und spezielle Beispiele davon schließen Polyoxypropylenmonopropylether, Polyoxypropylenmonobutylether, Polyoxybutylenmonobutylether, Polyoxyethylenoxypropylenmonopropylether, Polyoxyethylenoxypropylenmonobutylether, Polyoxyethylenoxypropylenmonopentylether und Polyoxypropylendimethylether ein. Bevorzugt sind Polyoxypropylenmonobutylether und Polyoxypropylendimethylether, wobei Polyoxypropylendimethylether am stärksten bevorzugt ist.The polyoxyalkylene glycol ethers represented by general formula I, which can be used here can a monoether or a diether, and specific examples thereof shut down Polyoxypropylene monopropyl ether, polyoxypropylene monobutyl ether, polyoxybutylene monobutyl ether, Polyoxyethyleneoxypropylene monopropyl ether, polyoxyethyleneoxypropylene monobutyl ether, Polyoxyethyleneoxypropylene monopentyl ether and polyoxypropylene dimethyl ether one. Preference is given to polyoxypropylene monobutyl ether and polyoxypropylene dimethyl ether, wherein polyoxypropylene dimethyl ether is the most preferred.
Bevorzugt umfasst die in der vorliegenden Erfindung verwendete Ölgrundlage einen Polyoxyalkylenglykolether in einer Menge von bevorzugt nicht weniger als 50 Gew.-%, stärker bevorzugt nicht weniger als 80 Gew.-% und am stärksten bevorzugt 100 Gew.-%, bezogen auf das Gesamtgewicht der Ölgrundlage. Die in der vorliegenden Erfindung verwendete Ölgrundlage kann ferner andere Ölgrundlagematerialien, die momentan in der Fettzusammensetzung verwendet werden, wie Mineralöle, synthetische Kohlenwasserstoff-Öle und Alkyldiphenylether-Öle zusätzlich zum Polyoxyalkylenglykolether enthalten, aber die Menge davon beträgt bevorzugt weniger als 10 Gew.-%, bezogen auf das Gesamtgewicht der Ölgrundlage.Prefers includes the oil base used in the present invention a polyoxyalkylene glycol ether in an amount of preferably not less than 50% by weight, stronger preferably not less than 80% by weight, and most preferably 100% by weight, based on the total weight of the oil base. The present in the present Invention used oil base may also contain other base oil materials, currently used in the fat composition, such as mineral oils, synthetic Hydrocarbon oils and alkyl diphenyl ether oils additionally to the polyoxyalkylene glycol ether, but the amount thereof is preferable less than 10% by weight, based on the total weight of the oil base.
Die kinematische Viskosität des Polyoxyalkylenglykolethers, wie bei 40°C bestimmt, liegt bevorzugt im Bereich von 30 bis 400 mm2/s und stärker bevorzugt 80 bis 120 mm2/s.The kinematic viscosity of the polyoxyalkylene glycol ether, as determined at 40 ° C, is preferably in the range of 30 to 400 mm 2 / s, and more preferably 80 to 120 mm 2 / s.
Als das Verdickungsmittel, das in der erfindungsgemäßen Fettzusammensetzung für Kabelstränge verwendet wird, können zum Beispiel jene aufgelistet werden, die herkömmlich auf diesem Fachgebiet bekannt sind, wie Metallsalze von Fettsäuren, Bentonit, der mit organischen Verbindungen modifiziert ist, und PTFE, wobei Metallsalze von Fettsäuren und Bentonit, der mit organischen Verbindungen modifiziert ist, hier besonders bevorzugt verwendet werden.When the thickening agent used in the cable gland grease composition of the present invention will, can for example, those conventionally listed in the art known as metal salts of fatty acids, bentonite, organic Compounds is modified, and PTFE, wherein metal salts of fatty acids and Bentonite modified with organic compounds, here especially preferably used.
Als der Bestandteil Fettsäuren der vorstehenden Metallsalze von Fettsäuren werden hier bevorzugt jene mit 10 bis 30 und stärker bevorzugt 16 bis 20 Kohlenstoffatomen verwendet und Beispiele davon, die hier bevorzugt verwendet werden, sind Laurinsäure, Myristinsäure, Palmitinsäure, Stearinsäure, 12-Hydroxystearinsäure und Ölsäure. Darüber hinaus können als die Metallsalze dieser Fettsäuren zum Beispiel Alkalimetallsalze wie Natrium- und Lithiumsalze, Erdalkalimetallsalze wie Barium- und Calciumsalze und dreiwertige Metallsalze wie Aluminiumsalze erwähnt werden. Hier Verwendbare schließen ferner zum Beispiel Salze von Gemischen ein, die jeweils mindestens zwei Fettsäuren umfassen, welche zweibasische Säuren mit Metallen wie Aluminium, Calcium und Lithium einschließen, oder Komplexmetallseifen. Unter diesen Metallsalzen von Fettsäuren wird hier am stärksten bevorzugt Lithium-l2-hydroxystearat wegen seiner ausgezeichneten Wasserbeständigkeit, Wärmebeständigkeit und mechanischen Stabilität verwendet.As the constituent fatty acid of the above metal salts of fatty acids, those having 10 to 30 and more preferably 16 to 20 carbon atoms are preferably used here, and examples thereof preferably used herein are lauric acid, myristic acid, palmitic acid, stearic acid, 12-hydroxystea and oleic acid. In addition, as the metal salts of these fatty acids, there may be mentioned, for example, alkali metal salts such as sodium and lithium salts, alkaline earth metal salts such as barium and calcium salts and trivalent metal salts such as aluminum salts. As used herein, for example, also include salts of mixtures each comprising at least two fatty acids, which include dibasic acids with metals such as aluminum, calcium and lithium, or complex metal soaps. Among these metal salts of fatty acids, lithium-12-hydroxystearate is most preferably used because of its excellent water resistance, heat resistance and mechanical stability.
Die Menge des Verdickungsmittels, die in die erfindungsgemäße Fettzusammensetzung eingebracht wird, liegt bevorzugt im Bereich von 2 bis 35 Gewichtsteilen und stärker bevorzugt 5 bis 15 Gewichtsteilen, pro 100 Gewichtsteile der Ölgrundlage. Aus dem Grund, weil, wenn die Menge davon weniger als 2 Gewichtsteile beträgt, eine solche Neigung beobachtet werden würde, dass die resultierende Fettzusammensetzung in einem stark fluidisierten Zustand vorliegt und sie folglich zu weich ist, während, wenn die Menge davon 35 Gewichtsteile übersteigt, die resultierende Zusammensetzung dazu neigt, zu hart zu sein, um sie als eine Fettzusammensetzung für Kabelstränge zu verwenden.The Amount of thickening agent included in the fat composition of the invention is preferably in the range of 2 to 35 parts by weight and stronger preferably 5 to 15 parts by weight, per 100 parts by weight of the oil base. For the reason that if the amount thereof is less than 2 parts by weight, one such inclination would be observed that the resulting Fat composition is present in a highly fluidized state and therefore it is too soft while, if the amount thereof exceeds 35 parts by weight, the resulting Composition tends to be too hard to use as a fat composition to use for cable strands.
Beispiele von Chinolinverbindungen, die in der erfindungsgemäßen Fettzusammensetzung für Kabelstränge verwendet werden, sind Verbindungen, die durch die folgende allgemeine Formel II dargestellt werden, wie Trimethyldihydrochinolinoligomer.Examples of quinoline compounds present in the fat composition of the invention used for harnesses are compounds that are represented by the following general formula II, such as trimethyldihydroquinoline oligomer.
Formel
II:
In Formel II können R4, R5 und R6 gleich oder unterschiedlich sein und jeder Rest stellt bevorzugt einen Alkylrest, bevorzugt mit 1 bis 10 und stärker bevorzugt 1 bis 3 Kohlenstoffatomen, dar und n ist eine Zahl, die bevorzugt im Bereich von 1 bis 10 und stärker bevorzugt 1 bis 5 liegt.In formula II, R 4 , R 5 and R 6 may be the same or different and each group is preferably an alkyl group, preferably having 1 to 10 and more preferably 1 to 3 carbon atoms, and n is a number preferably in the range of 1 to 10, and more preferably 1 to 5.
Solche besonders bevorzugten Chinolinverbindungen sind zum Beispiel Trimethyldihydrochinolinoligomere (n = 2 bis 3).Such Particularly preferred quinoline compounds are, for example, trimethyldihydroquinoline oligomers (n = 2 to 3).
Die Menge dieser Chinolinverbindungen, die in die erfindungsgemäße Fettzusammensetzung eingebracht wird, liegt bevorzugt im Bereich von 0,1 bis 10 Gew.-%, stärker bevorzugt 0,5 bis 5 Gew.-% und am stärksten bevorzugt 1,0 bis 3 Gew.-%, bezogen auf das Gesamtgewicht der Fettzusammensetzung.The Amount of these quinoline compounds, which in the fat composition of the invention is preferably in the range of 0.1 to 10 wt .-%, stronger preferably 0.5 to 5 wt%, and most preferably 1.0 to 3 Wt .-%, based on the total weight of the fat composition.
Die erfindungsgemäße Fettzusammensetzung kann ferner andere Antioxidationsmittel, zum Beispiel eine Phenolverbindung wie 2,6-Di-t-butylcresol und/oder eine Aminverbindung wie Phenyl-α-naphthylamin, in Kombination mit den vorstehenden Komponenten umfassen. In dieser Hinsicht ist der Gehalt davon, der hier verwendet wird, wünschenswerterweise nicht höher als 5,0 Gew.-%, bezogen auf das Gesamtgewicht der Fettzusammensetzung.The fat composition according to the invention may further contain other antioxidants, for example a phenolic compound such as 2,6-di-t-butylcresol and / or an amine compound such as phenyl-α-naphthylamine, in combination with the above components. In this Regarding, the content thereof used here is desirably not higher as 5.0% by weight, based on the total weight of the fat composition.
Die erfindungsgemäße Fettzusammensetzung für Kabelstränge kann eine Benzotriazolverbindung als den Korrosionsinhibitor umfassen. Beispiele von solchen Benzotriazolverbindungen, die hier bevorzugt verwendet werden, sind jene, die durch die folgende allgemeine Formel III dargestellt werden:The fat composition according to the invention for harnesses can a benzotriazole compound as the corrosion inhibitor. Examples of such benzotriazole compounds, which are preferred here are those which are represented by the following general formula III:
In Formel III stellt R7 ein Wasserstoffatom oder einen Alkylrest mit 1 bis 10 und bevorzugt 1 bis 3 Kohlenstoffatomen wie eine Methyl-, Ethyl- oder Propylgruppe dar, R8 und R9 stellen jeweils unabhängig ein Wasserstoffatom oder einen Alkylrest mit 1 bis 20 und bevorzugt 1 bis 10 Kohlenstoffatomen wie eine Methyl-, Ethyl-, Propyl-, Isopropyl-, Butyl-, Isobutyl-, Pentyl-, Hexyl-, Heptyl- oder Octylgruppe dar. Besonders bevorzugt verwendet werden hier zum Beispiel Benzotriazolverbindungen, die durch die allgemeine Formel III dargestellt werden, wobei R7 eine Methylgruppe darstellt und R8 und R9 jeweils eine 2-Ethylhexylgruppe darstellen.In formula III, R 7 represents a hydrogen atom or an alkyl group having 1 to 10 and preferably 1 to 3 carbon atoms such as a methyl, ethyl or propyl group, R 8 and R 9 each independently represent a hydrogen atom or an alkyl group of 1 to 20 and preferably 1 to 10 carbon atoms such as a methyl, ethyl, propyl, isopropyl, butyl, isobutyl, pentyl, hexyl, heptyl or octyl group. Particular preference is given here, for example, Benzotriazolverbindungen by the general Formula III wherein R 7 represents a methyl group and R 8 and R 9 each represent a 2-ethylhexyl group.
Der Gehalt der Benzotriazolverbindung, der in der erfindungsgemäßen Fettzusammensetzung vorhanden ist, liegt bevorzugt im Bereich von 0,1 bis 10 Gew.-%, stärker bevorzugt 0,3 bis 5 Gew.-% und am stärksten bevorzugt 0,5 bis 3 Gew.-%, bezogen auf das Gesamtgewicht der Fettzusammensetzung.Of the Content of the benzotriazole compound used in the fat composition according to the invention is present is preferably in the range of 0.1 to 10 wt .-%, stronger preferably 0.3 to 5 wt%, and most preferably 0.5 to 3 Wt .-%, based on the total weight of the fat composition.
Die erfindungsgemäße Fettzusammensetzung kann einen von der vorstehenden Benzotriazolverbindung verschiedenen Korrosionsinhibitor, wie eine Bernsteinsäureverbindung, typischerweise von einem Alkenylbernsteinsäureanhydrid, und/oder eine Sulfonsäureverbindung, die durch eine Alkylnaphthalinsulfonsäure dargestellt wird, in Kombination mit dem Korrosionsinhibitor vom Triazol-Typ umfassen und die Menge davon, die verwendet wird, beträgt wünschenswerterweise nicht mehr als 5,0 Gew.-%, bezogen auf das Gesamtgewicht der Fettzusammensetzung.The fat composition according to the invention may be different from the above benzotriazole compound Corrosion inhibitor, such as a succinic acid compound, typically from an alkenyl succinic anhydride, and / or a sulfonic acid compound, which is represented by an alkylnaphthalenesulfonic acid, in combination with the triazole type corrosion inhibitor and the amount of which is used is desirably not more than 5.0% by weight based on the total weight of the fat composition.
Die vorliegende Erfindung wird hier nachstehend detaillierter mit Bezug auf die folgenden nichteinschränkenden Beispiele und Vergleichsbeispiele beschrieben, aber die vorliegende Erfindung ist überhaupt nicht auf diese speziellen Beispiele eingeschränkt.The The present invention will hereinafter be described in greater detail with reference to FIG to the following non-limiting Examples and Comparative Examples are described, but the present Invention is not at all limited to these specific examples.
Beispiele 1 bis 6 und Vergleichsbeispiele 1 bis 6Examples 1 to 6 and Comparative Examples 1 to 6
In diesen Beispielen wurde eine Vielzahl von Fettzusammensetzungen hergestellt, wobei jede ein Verdickungsmittel, eine Ölgrundlage und Additive umfasste, die speziell nachstehend aufgelistet sind, und dann wurden charakteristische Eigenschaften davon gemäß den nachstehend detailliert beschriebenen Verfahren bewertet:In These examples have been used in a variety of fat compositions each being a thickener, an oil base and additives specifically listed below, and then characteristic properties thereof became as below evaluated in detail:
(Fettzusammensetzungsproben)(Grease composition samples)
Verdickungsmittel:Thickener:
- Lithiumseife (Lithium-l2-hydroxystearat)Lithium soap (lithium-l2-hydroxystearate)
- Bentonit, welcher mit einer organischen Verbindung modifiziert wurde (organisch modifizierter Bentonit)Bentonite which is modified with an organic compound was (organically modified bentonite)
Ölgrundlage:Oil basis:
- Polyoxypropylendimethylether (n = 20): Kinematische Viskosität (bei 40°C): 95 mm2/s;Polyoxypropylene dimethyl ether (n = 20): Kinematic viscosity (at 40 ° C): 95 mm 2 / s;
- Polyoxypropylenmonobutylether (n = 10): Kinematische Viskosität (bei 40°C): 105 mm2/s;Polyoxypropylene monobutyl ether (n = 10): kinematic viscosity (at 40 ° C): 105 mm 2 / s;
- Dioctylsebacat: Kinematische Viskosität (bei 40°C): 12 mm2/s.Dioctyl sebacate: Kinematic viscosity (at 40 ° C): 12 mm 2 / s.
Additive:additives:
- Chinolinverbindung (Trimethyldihydrochinolinoligomer);Quinoline compound (trimethyldihydroquinoline oligomer);
- Benzotriazolverbindung (ein Gemisch, das 1-[N,N-Bis(2-ethylhexyl)aminomethyl]-4-methylbenzotriazol und 1-[N,N-Bis(2-ethylhexyl)aminomethyl]-5-methylbenzotriazol umfasst);Benzotriazole compound (a mixture containing 1- [N, N-bis (2-ethylhexyl) aminomethyl] -4-methylbenzotriazole and 1- [N, N-bis (2-ethylhexyl) aminomethyl] -5-methylbenzotriazole);
- Phenolverbindung (Octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionat);Phenol compound (octadecyl-3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate);
- Bernsteinsäureverbindung (Alkenylbernsteinsäureanhydrid).Succinic acid compound (Alkenyl succinic anhydride).
1. Test eines dünnen Films unter Bedingungen von hoher Temperatur und hoher Feuchtigkeit (Test auf Korrosionsbeständigkeit)1. Test a thin film under conditions of high temperature and high humidity (test on corrosion resistance)
Eine
Testfettzusammensetzung wurde auf die untere Hälfte der Oberfläche eines
Kupferflächengebildes,
eines Messingflächengebildes
oder Weißblechflächengebildes
in einer Dicke von 2 mm aufgebracht, gefolgt von Ermöglichen,
dass jedes Flächengebilde
bei 60°C,
80% RH für
168 Stunden stand, und der nachfolgenden Bestätigung, ob jedes Testmaterial
eine jedwede externe Farbänderung
erfuhr oder nicht. Die Korrosionsbeständigkeit von jedem Testmaterial
wurde gemäß den folgenden
Bewertungskriterien bewertet:
O: Das Testmaterial ist nicht
Gegenstand von jedweder Korrosion;
x: Das Testmaterial ist
in der Tat Gegenstand von Korrosion.A test fat composition was applied to the lower half of the surface of a copper sheet, a brass sheet or tinplate sheet in a thickness of 2 mm, followed by allowing each sheet to stand at 60 ° C, 80% RH for 168 hours, and then confirming whether each test material experienced any external color change or not. The corrosion resistance of each test material was evaluated according to the following evaluation criteria:
O: The test material is not subject to any corrosion;
x: The test material is indeed subject to corrosion.
2. Test auf Oxidationsstabilität2nd test on oxidation stability
Bestimmungsverfahren:
Diese wurde gemäß JIS K
2220. 12. (99°C,
100 Stunden) bestimmt und bezogen auf die folgenden Bewertungskriterien
bewertet:
O: Weniger als 50 kPa;
x: Nicht weniger als
50 kPa.Method of determination: This was determined according to JIS K 2220. 12. (99 ° C, 100 hours) and evaluated based on the following evaluation criteria:
O: Less than 50 kPa;
x: not less than 50 kPa.
3: Olefin-Tauchtest (Kompatibilität mit Material)3: olefin immersion test (compatibility with material)
Polypropylenelastomer
(mit einer Größe von 50
mm × 5
mm × 1
mm) wurde in jede Fettzusammensetzungsprobe (100 g) getaucht, für 96 Stunden
bei 80°C
gehalten und dann wurde jedes Olefinmaterial auf die Volumenänderung
gemäß der folgenden
Gleichung untersucht:
In
der Gleichung stellt A das Volumen von jedem Elastomer dar, das
vor dem Tauchtest beobachtet wurde, und B ist das Volumen davon,
das nach dem Tauchtest beobachtet wurde. Jede Probe wurde bezogen auf
die folgenden Kriterien bewertet:
O: Die Elastomerprobe wies
eine Volumenänderung
von weniger als ± 10%
auf;
x: Die Elastomerprobe wies eine Volumenänderung
von nicht weniger als ± 10%
auf.In the equation, A represents the volume of each elastomer observed before the immersion test, and B is the volume thereof observed after the immersion test. Each sample was evaluated based on the following criteria:
O: The elastomer sample had a volume change of less than ± 10%;
x: The elastomer sample had a volume change of not less than ± 10%.
Die so erhaltenen Ergebnisse sind in den folgenden Tabellen 1 und 2 zusammengefasst:The thus obtained results are shown in Tables 1 and 2 below summarized:
Tabelle
1
Tabelle
2
Die in den vorstehenden Tabellen 1 und 2 aufgelisteten Daten zeigen klar, dass die erfindungsgemäßen in den Beispielen 1 bis 6 hergestellten Fettzusammensetzungen ausgezeichnete Ergebnisse im Test eines dünnen Films unter Bedingungen von hoher Temperatur und hoher Feuchtigkeit, im Test auf Oxidationsstabilität und im Olefin-Tauchtest bereitstellen können oder dass diese Fettzusammensetzungen bei der Korrosionsbeständigkeit, der Oxidationsstabilität und der Kompatibilität mit Olefinmaterial ganz ausgezeichnet sind, da die erfindungsgemäße Fettzusammensetzung einen Polyoxyalkylenglykolether als die Ölgrundlage und eine Chinolinverbindung und eine Benzotriazolverbindung als die Additive umfasst.The in the above Tables 1 and 2 show clear that the invention in the Examples 1 to 6 produced fat compositions excellent Results in the test of a thin Films under conditions of high temperature and high humidity, in the test for oxidation stability and in the olefin immersion test or that these fat compositions in corrosion resistance, the oxidation stability and compatibility are very excellent with olefin material, since the fat composition according to the invention a polyoxyalkylene glycol ether as the base oil and a quinoline compound and a benzotriazole compound as the additives.
Im Gegensatz dazu zeigen die in den vorstehenden Tabellen 1 und 2 aufgelisteten Daten ebenso klar, dass die in den Vergleichsbeispielen 1 und 4 hergestellten Fettzusammensetzungen, die frei von jedweder Benzotriazolverbindung sind, bei der Korrosionsbeständigkeit minderwertig sind, dass die in den Vergleichsbeispielen 2 und 3 hergestellten Fettzusammensetzungen, die frei von jedweder Chinolinverbindung sind, bei der Korrosionsbeständigkeit und der Oxidationsstabilität nicht ausreichend sind und dass die in Vergleichsbeispiel 5 hergestellte Fettzusammensetzung, die Dioctylsebacat als die Ölgrundlage und eine Bernsteinsäureverbindung anstelle der Benzotriazolverbindung verwendet, bei der Korrosionsbeständigkeit und der Kompatibilität mit Olefinmaterial minderwertig ist. Darüber hinaus ist es aufgrund der vorstehenden Daten klar, dass die in Vergleichsbeispiel 6 hergestellt Fettzusammensetzung (eine kommerziell erhältliche Fettzusammensetzung), die frei von Verbindungen von sowohl vom Chinolin-Typ als auch vom Benzotriazol-Typ ist, sowohl bei der Korrosionsbeständigkeit als auch der Oxidationsstabilität minderwertig ist.in the In contrast, those listed in Tables 1 and 2 above Data just as clear that in Comparative Examples 1 and 4 produced fat compositions free from any benzotriazole compound are in corrosion resistance are inferior that in Comparative Examples 2 and 3 produced fat compositions free of any quinoline compound are in corrosion resistance and the oxidation stability are not sufficient and that produced in Comparative Example 5 Fat composition, the dioctyl sebacate as the base oil and a succinic acid compound used in place of the benzotriazole compound in corrosion resistance and compatibility with olefin material is inferior. In addition, it is due from the above data, that prepared in Comparative Example 6 Fat composition (a commercially available fat composition), free from quinoline-type compounds as well as from Benzotriazole type is, both in corrosion resistance as well as the oxidation stability is inferior.
Claims (8)