CN204495189U - A kind of flexible ballistic-resistant stab-resistance body armor - Google Patents
A kind of flexible ballistic-resistant stab-resistance body armor Download PDFInfo
- Publication number
- CN204495189U CN204495189U CN201520181317.XU CN201520181317U CN204495189U CN 204495189 U CN204495189 U CN 204495189U CN 201520181317 U CN201520181317 U CN 201520181317U CN 204495189 U CN204495189 U CN 204495189U
- Authority
- CN
- China
- Prior art keywords
- stab
- overcoat
- resistant
- cloth
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of flexible ballistic-resistant stab-resistance body armor, and described bulletproof stab-resistant clothes inside arranges bulletproof anti-puncturing chip, outer setting multifunctional protection overcoat.Described chip ecto-entad comprises antipricking layer, transition zone, burster course and cushion, and described antipricking layer is the sheet metal of thickness 0.1-0.4mm, and described antipricking layer also can be grammes per square metre 300g/m
2--800g/m
2aramid fiber gummed cloth; Described burster course is grammes per square metre 150g/m
2-190g/m
2ultra-high molecular weight polyethylene PEUD fiber cloth; Described burster course also can be grammes per square metre 190g/m
2--500g/m
2aryl fiber cloth; Described transition zone is ultrahigh molecular weight (UHMW) polyethylene material, and described cushion is expanded material; Described protective coat comprises the overcoat nexine be made up of polyester compound net eye cloth and the overcoat be made up of aramid fabric is outer.Adopt block of metal thin plate as protection chip, hardness is high, deformability good, can not produce safety defect because of seam; Because the hardness of sheet metal exceedes macromolecular material, alleviate the weight of clothes, improve flexibility and the comfortableness of protective garment.
Description
Technical field
The utility model relates to protective garment, particularly relates to a kind of flexible ballistic-resistant stab-resistance body armor.
Background technology
Ballistic protective clothing, is commonly called as flak jackets, being a kind of individual soldier protection clothes, for keeping out the injury of bullet to trunk, mostly being vest shape.Stab-resistance body armor, also claims anti-sword to take, and wearer can be protected not to be subject to the incised wound of the sharp objects such as sharp knife etc. or to chop wound.Due to the continuous evolving development of security protection equipment, the bulletproof stab-resistant clothes of present stage be a kind of can shellproof again can be anti-stab protective clothes, possess two kinds of protective capacities simultaneously.The conventional protective materials of general bulletproof stab-resistant clothes is metal and macromolecular material, comprises kevlar fabric, ultra-high molecular weight polyethylene two class material.
As in prior art, publication number is: 201819624U, title: a kind of bulletproof stab-resistant clothes, this utility model discloses a kind of bulletproof stab-resistant clothes, it comprises from outside to inside successively: the first composite bed, intermediate layer and the second composite bed, described intermediate layer is 1 layer of titanium alloy sheet, and described first composite bed and the second composite bed all comprise from outside to inside successively: 18 aspect density be 135g/cm2 without latitude cloth and 1 layer of titanium alloy sheet, adjacent is 0 °/20 ° arrangements without fiber in latitude cloth.The first composite bed in this bulletproof stab-resistant clothes and the second composite bed all have higher anti-cutting and impact resistance, internal layer titanium alloy sheet is used for improving ballistic performance further, is enough to the bulletproof stab-resistant clothes after the first composite bed, middle titanium alloy sheet and the second composite bed compound to resist repeatedly attacking.
And for example publication number is: 201497429U, name is called: bulletproof stab-resistant clothes, this utility model relates to a kind of bulletproof stab-resistant clothes, comprise bulletproof anti-puncturing layer and protective coat, it is characterized in that described bulletproof anti-puncturing layer is spliced to form by chip, each sheet chip described is made up of internal layer, skin and laminboard layer, and described internal layer and skin are metal level, described laminboard layer is that laminboard layer is filled between internal layer and skin for shellproof flexible ballistic-resistant material.This utility model utilizes the little metal material of a kind of hard density and ballistic fiber cloth to combine, and is combined into bulletproof anti-puncturing layer, adopts extraordinary combination process both to be combined, more in addition protective coat composition has the bulletproof stab-resistant clothes of bulletproof anti-puncturing performance concurrently.Can prevent real silk from going bad, again there is effect of heat insulation, be greater than 8 years service life.Ballistic performance meets 4 grades of GA141 standard-required, and anti-stab performance meets GA68-2008 standard-required.
But conventional metals sheet used in the prior art or metallic plate, because hardness is high, flexibility is poor causes not yielding, bending, and therefore snugness of fit is not high, and human body puts on not flexible protective garment, and movable inconvenient, dexterity of action is poor; When sheet metal is connected by platelet splicing, lap joint process in addition, its seam crossing possibility existing defects, can not reach good bulletproof effect.Simultaneously in order to possess better shellproof, anti-stab function, all materials are more thick and heavy for conventional protective materials such as kevlar fabric etc., easily cause wearer handicapped.
Mostly be due to bulletproof stab-resistant clothes the special personnel such as public security cadres and police, army soldier, bank note transport car supercargo dailyly executing the task, on duty or indispensable under being in operational state protective gear, therefore its security and practicality are particularly important.Based on above-mentioned deficiency of the prior art, how ensureing that wearer is when wearing for a long time, can either feel light and comfortablely can have again good bulletproof anti-puncturing function, becoming problem demanding prompt solution in bulletproof stab-resistant clothes evolution.
Utility model content
In order to make up the defect of prior art, the utility model provides a kind of flexible ballistic-resistant stab-resistance body armor, propose first to use sheet metal as stab-resistant material, metal material is made the thin plate that thickness is 0.1-0.4mm, protection chip is made by entire plate, overcome the problem that metal plate is hard, flexibility is poor, sheet metal is overall as protective materials simultaneously, overcomes splicing, overlaps the seam crossing existing defects brought.In bulletproof stab-resistant clothes inside, bulletproof anti-puncturing chip is set, described chip comprises four layers altogether, ecto-entad order arrangement: the antipricking layer be made up of titanium-alloy thin-plate, the transition zone that nonmetal bulletproof stab-resistant material is formed, the burster course that bullet resistant material is formed and the cushion that padded coaming is formed.Described antipricking layer also can use aramid fiber gummed cloth as stab-resistant material, described aramid fiber gummed cloth uses aramid fiber woven fabric as base material, with resins such as epoxy, phenolic aldehyde, urea aldehyde, temperature-pressure is made, can on the basis of anti-stab function, have bulletproof function concurrently, also can reduce the weight of bulletproof anti-puncturing chip.The outside of bulletproof stab-resistant clothes adopts aramid fabric to make overcoat, increases bulletproof stab-resistant clothes fire protection flame retarding function; Adopt the overcoat interior layer material of polyester compound net eye cloth structure, there is buffering effect, strengthen the moisture-inhibiting of protective garment, permeability, the comfortableness of bulletproof stab-resistant clothes can be improved, the overcoat of this kind of structure also can be used for various protective garment, as: flak jackets, stab-resistance body armor, Antiriot dress, Protective dress for removing explosive etc.
To achieve these goals, the technical solution that flexible ballistic-resistant stab-resistance body armor described in the utility model is taked is: a kind of flexible ballistic-resistant stab-resistance body armor inside described in the utility model arranges bulletproof anti-puncturing chip, outer setting multifunctional protection overcoat.Described shellproof protection chip comprises ecto-entad order and arranges antipricking layer, transition zone, burster course and cushion totally 4 layers, and the density of described bulletproof anti-puncturing chip is 6.0-11kg/m
2, described antipricking layer is the sheet metal 1-6 layer of thickness 0.1-0.4mm, and described sheet metal is a monoblock sheet material, is formed by the rolling of bulk metallic materials plate; Described antipricking layer also can be grammes per square metre 300g/m
2--800g/m
2aramid fiber gummed cloth 5-15 layer; Described aramid fiber gummed cloth uses aramid fiber woven fabric as base material, and with resins such as epoxy, phenolic aldehyde, urea aldehyde, temperature-pressure is made; Described burster course is grammes per square metre 150g/m
2-190g/m
2ultra-high molecular weight polyethylene PEUD (fiber is 0 °/90 ° arrangements) fiber cloth 20-35 layer; Described burster course also can be grammes per square metre 190g/m
2--500g/m
2aryl fiber cloth 15-50 layer; Described transition zone is ultrahigh molecular weight (UHMW) polyethylene material (fiber is 0 °/45 °/90 °/135 ° arrangements) 5-50 layer, described transition zone is arranged between antipricking layer and burster course, as the transition of burster course and antipricking layer, described ultrahigh molecular weight (UHMW) polyethylene material can be both shellproof also anti-stab; Described cushion is expanded material, includes but not limited to the materials such as PU, PE, XPE, PVC, EVA, and described expanded material can improve the blunt trauma performance of bulletproof stab-resistant clothes; Described multifunctional protection overcoat comprises overcoat nexine and overcoat is outer, and described overcoat nexine is polyester compound net eye cloth, and described overcoat skin is aramid fabric.
Further, whole described bulletproof anti-puncturing chip adopts waterproof gummed cloth integral sealing.
Further, the material of described antipricking layer material can be latten or aramid fiber gummed cloth;
Further, the material of described transition zone can be multidirectional PEUD fiber cloth;
Further, the material of described burster course can be PEUD fiber cloth or aramid fiber woven fabric;
The beneficial effect of a kind of flexible ballistic-resistant stab-resistance body armor described in the utility model is: novel structure, safe and reliable, convenient comfortable.Adopt block of metal thin plate as protection chip, sheet metal is better than slab (thickness 1.5mm-6mm) deformability, overcome metal thick plate because of good rigidly, flexibility difference and cannot be out of shape, human body puts on not flexible protective garment, and movable inconvenient, dexterity of action is poor; Adopt whole plate structure, there is no seam, also just saved material without defect, thus alleviate the weight of whole clothing.And the hardness of sheet metal is much larger than the hardness of macromolecular material, its anti-stab performance, also far above the anti-stab performance of general conventional macromolecular material.This design significantly can reduce the weight of protective materials, reduces thickness, improves flexibility and the comfortableness of protective garment.The utility model adopts new frame mode, antipricking layer, transition zone, institute's metal-containing material in burster course and cushion, aramid fiber gummed cloth, ultrahigh molecular weight (UHMW) polyethylene material, expanded materials etc. are coordinated by certain proportion, cooperative effect between above-mentioned material is good, save material usage, alleviate the weight of bulletproof anti-puncturing chip, increase its safety coefficient, have bulletproof ability woven fabric or without latitude cloth after dipping process, integral material becomes well-pressed, quality is harder, anti-stab function can be had concurrently, the woven fabric good with ballistic performance or combine without latitude cloth and can reach good two anti-effect, reduce thickness simultaneously, improve the comfortableness of dress.There is the cushion that flexible expanded material makes, the external impacts that human body is subject to can be reduced, alleviate the weight of bulletproof stab-resistant clothes, increase its safety coefficient, improve the blunt trauma performance of bulletproof stab-resistant clothes.The outside of bulletproof stab-resistant clothes adopts polyester compound net eye cloth structure as back boxing, has buffering effect, strengthens the moisture-inhibiting of protective garment, permeability, and adopt aramid fiber material as outer lining, have good fire protection flame retarding effect.The utility model can meet anti-stab performance and the GA141-2010 of GA68-2008 police stab-resistance body armor regulation, 2 grades of regulation and 3 grades of ballistic performances.
Accompanying drawing explanation
Fig. 1 is the structural representation of the bulletproof anti-puncturing chip of bulletproof stab-resistant clothes described in the utility model.
Reference numeral:
1-antipricking layer; 2-transition zone; 3-burster course; 4-cushion.
Detailed description of the invention
For making the object of the utility model embodiment, technical scheme and advantage clearly, below in conjunction with the accompanying drawing in the utility model embodiment, technical scheme in the utility model embodiment is clearly and completely described, obviously, described embodiment is the utility model part embodiment, instead of whole embodiments.
As shown in Figure 1, a kind of flexible ballistic-resistant stab-resistance body armor inside described in the utility model arranges bulletproof anti-puncturing chip, outer setting multifunctional protection overcoat (not shown); Described shellproof protection chip comprises ecto-entad order and arranges antipricking layer 1, transition zone 2, burster course 3 and cushion 4 totally four layers; Described multifunctional protection overcoat comprises overcoat nexine (not shown) and the outer (not shown) of overcoat, and described overcoat nexine is polyester compound net eye cloth, and described overcoat skin is aramid fabric.
Described bulletproof anti-puncturing chip adopts waterproof gummed cloth integral sealing.
The density of described bulletproof anti-puncturing chip is 6.0-11kg/m
2, anti-stab performance and the GA141-2010 of GA68-2008 police stab-resistance body armor regulation can be met, 2 grades of regulation and 3 grades of ballistic performances.
1) described antipricking layer 1 for thickness be the sheet metal 1-6 layer of 0.1-0.4mm, described sheet metal is a monoblock sheet material;
Described antipricking layer 1 also can be grammes per square metre 300g/m
2--800g/m
2aramid fiber gummed cloth 5-15 layer;
Described aramid fiber gummed cloth uses aramid fiber woven fabric as base material, and with resins such as epoxy, phenolic aldehyde, urea aldehyde, temperature-pressure is made.
2) described burster course 3 is grammes per square metre 150g/m
2-190g/m
2ultra-high molecular weight polyethylene PEUD (fiber is 0 °/90 ° arrangements) fiber cloth 20-35 layer;
Described burster course 3 also can be grammes per square metre 190g/m
2--500g/m
2aryl fiber cloth 15-50 layer;
3) described transition zone 2 is ultrahigh molecular weight (UHMW) polyethylene material (fiber is 0 °/45 °/90 °/135 ° arrangements) 5-50 layer, described transition zone 2 is arranged between antipricking layer 1 and burster course 3, as the transition of burster course 3 with antipricking layer 1, described ultrahigh molecular weight (UHMW) polyethylene material can be both shellproof also anti-stab;
4) described cushion 4 is expanded material, includes but not limited to the expanded materials such as PU, PE, XPE, PVC, EVA, and described expanded material can improve the blunt trauma performance of bulletproof stab-resistant clothes.
(1) described shellproof detailed description of the invention of putting puncturing chip is:
Example 1:
Described antipricking layer 1 adopts 1 piece of 0.3mm stainless steel thin slice, and described transition zone 2 adopts 25 layers, grammes per square metre 150g/m
2ultra-high molecular weight polyethylene multidirectional (fiber is 0 °/45 °/90 °/135 ° arrangements) PEUD, described burster course 3 adopts 25 layers, grammes per square metre 160g/m
2ultra-high molecular weight polyethylene common (fiber is 0 °/90 ° arrangements) PEUD, described cushion 4 adopts the foaming EVA material of 3.5mm, and above-mentioned each layer is coordinated by certain proportion, and cooperative effect is remarkable.Adopt the bulletproof stab-resistant clothes that above-mentioned 4 Rotating fields are made, protection level can reach 2 grades (FDC-2), can stop the 51 formula 7.62mm lead for retractable pencil bullets that 79 formula light submachine guns are launched, and stop the puncture of code test cutter 24 joules of kinetic energy.
Example 2:
Described overcoat 1 adopts 2 pieces of 0.2mm titanium alloy thin slices, described transition zone 2 adopts 25 layers, grammes per square metre 170g/m ultra-high molecular weight polyethylene multidirectional (fiber is 0 °/45 °/90 °/135 ° arrangements) PEUD, and described burster course 3 adopts 20 layers, grammes per square metre 160g/m
2ultra-high molecular weight polyethylene common (fiber is 0 °/90 ° arrangements) PEUD, described cushion 4 adopts the foaming XPE material of 3.5mm, and above-mentioned each layer is coordinated by certain proportion, and cooperative effect is remarkable.Adopt the bulletproof stab-resistant clothes that above-mentioned 4 Rotating fields are made, protection level can reach 2 grades (FDC-2), can stop the 51 formula 7.62mm lead for retractable pencil bullets that 79 formula light submachine guns are launched, and stop the puncture of code test cutter 24 joules of kinetic energy.
Example 3:
Described overcoat 1 adopts 4 pieces of 0.1mm titanium alloy thin slices, and described transition zone 2 adopts grammes per square metre 170g/m
2, 30 layers of ultra-high molecular weight polyethylene multidirectional (fiber is 0 °/45 °/90 °/135 ° arrangements) PEUD, described burster course 3 adopts 15 layers, grammes per square metre 190g/m
2aryl fiber cloth is as burster course, and described cushion 4 adopts the foaming PU of 4mm, and above-mentioned each layer is coordinated by certain proportion, and cooperative effect is remarkable.Adopt the bulletproof stab-resistant clothes that above-mentioned 4 Rotating fields are made, protection level can reach 2 grades (FDC-2), can stop the 51 formula 7.62mm lead for retractable pencil bullets that 79 formula light submachine guns are launched, and stop the puncture of code test cutter 24 joules of kinetic energy.
Example 4:
Described overcoat 1 adopts 5 layers of common PE UD, described transition zone 2 adopts 52 layers of ultra-high molecular weight polyethylene multidirectional (fiber is 0 °/45 °/90 °/135 ° arrangements) PEUD, described burster course 3 adopts 13 layers of ultra-high molecular weight polyethylene common (fiber is 0 °/90 ° arrangements) PEUD, described cushion 4 adopts the foaming EVA material of 3.5mm, above-mentioned each layer is coordinated by certain proportion, and cooperative effect is remarkable.Adopt the bulletproof stab-resistant clothes that above-mentioned 4 Rotating fields are made, protection level can reach 2 grades (FDC-2), can stop the 51 formula 7.62mm lead for retractable pencil bullets that 79 formula light submachine guns are launched, and stop the puncture of code test cutter 24 joules of kinetic energy.
Example 5:
Described overcoat 1 adopts 10 layers of grammes per square metre 380g/m
2aramid fiber gummed cloth, described transition zone 2 adopts 25 layers, grammes per square metre 170g/m
2ultra-high molecular weight polyethylene multidirectional (fiber is 0 °/45 °/90 °/135 ° arrangements) PEUD, described burster course 3 adopts 14 layers, grammes per square metre 200g/m
2common PE UD, described cushion 4 adopts the foaming PU of 4mm, and above-mentioned each layer is coordinated by certain proportion, and cooperative effect is remarkable.Adopt the bulletproof stab-resistant clothes that above-mentioned 4 Rotating fields are made, protection level can reach 2 grades (FDC-2), can stop the 51 formula 7.62mm lead for retractable pencil bullets that 79 formula light submachine guns are launched, and stop the puncture of code test cutter 24 joules of kinetic energy.
Example 6:
Described overcoat 1 adopts 5 layers of grammes per square metre 750g/m
2aramid fiber gummed cloth, described transition zone 2 is 15 layers of grammes per square metre 150g/m
2ultra-high molecular weight polyethylene multidirectional (fiber is 0 °/45 °/90 °/135 ° arrangements) PEUD, described burster course 3 adopts 30 layers of grammes per square metre 160g/m
2aryl fiber cloth, described cushion 4 adopts the foaming PU of 4mm, and above-mentioned each layer is coordinated by certain proportion, and cooperative effect is remarkable.Adopt the bulletproof stab-resistant clothes that above-mentioned 4 Rotating fields are made, protection level can reach 2 grades (FDC-2), can stop the 51 formula 7.62mm lead for retractable pencil bullets that 79 formula light submachine guns are launched, and stop the puncture of code test cutter 24 joules of kinetic energy.
(2) detailed description of the invention of described Multifunctional coat is as follows:
Example 1:
Described overcoat outer shell fabric adopts grammes per square metre 200g/m
2nOMEX IIIA fiber cloth makes, char length 85mm, after flame time 0.5S; Ultimate strength 953N, through 260 DEG C of high temperature, size changing rate is 0, and its performance meets GA10 fireman and to put out a fire the requirement of protective garment; Described overcoat nexine fabric adopts the lining of compound eyelet fabric structure, can either improve the moisture-penetrable ventilated performance of material, have pooling feature again.
Example 2:
Described overcoat outer shell fabric adopts grammes per square metre 240g/m
2nOMEX IIIA fiber cloth makes, char length 75mm, after flame time 0.3S; Ultimate strength 1105N, through 260 DEG C of high temperature, size changing rate is 0, and its performance meets GA10 fireman and to put out a fire the requirement of protective garment.
Described overcoat skin also can be grammes per square metre 180-250g/m
2tai Meida, Mei Tasi aramid fiber fire protection flame retarding cloth.
The structure of bulletproof stab-resistant clothes described in the utility model also can be applied to flak jackets, stab-resistance body armor, Antiriot dress, Protective dress for removing explosive etc.
Last it is noted that above embodiment only illustrates the technical solution of the utility model, be not intended to limit; Although be described in detail the utility model with reference to previous embodiment, those of ordinary skill in the art is to be understood that: it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature; And these amendments or replacement, do not make the essence of appropriate technical solution depart from the spirit and scope of each embodiment technical scheme of the utility model.
Claims (9)
1. a flexible ballistic-resistant stab-resistance body armor, it is characterized in that: bulletproof stab-resistant clothes arranges bulletproof anti-puncturing chip by inside, outer setting multifunctional protection overcoat, described shellproof protection chip from outside to inside order arranges antipricking layer, transition zone, burster course and cushion, and described multifunctional protection overcoat comprises overcoat nexine and overcoat is outer; The sheet metal of described antipricking layer to be 1-6 layer thickness be 0.1-0.4mm, described burster course is 20-35 layer grammes per square metre 150g/m
2-190g/m
2ultra-high molecular weight polyethylene PEUD fiber cloth, the fiber of described fiber cloth adopts 0 °/90 ° arrangements, described transition zone is the multidirectional PEUD fiber cloth of 5-50 layer ultra-high molecular weight polyethylene, the fiber of described multidirectional PEUD fiber cloth adopts 0 °/45 °/90 °/135 ° arrangements, and described cushion is expanded material; Described overcoat nexine is polyester compound net eye cloth, and described overcoat skin is aramid fabric.
2. flexible ballistic-resistant stab-resistance body armor according to claim 1, is characterized in that: the density of described bulletproof anti-puncturing chip is 6.0-11kg/m
2.
3. flexible ballistic-resistant stab-resistance body armor according to claim 1, is characterized in that: described bulletproof anti-puncturing chip adopts waterproof gummed cloth integral sealing.
4. flexible ballistic-resistant stab-resistance body armor according to claim 1, is characterized in that: the sheet metal in described antipricking layer is formed by entire plate rolling.
5. flexible ballistic-resistant stab-resistance body armor according to claim 1, is characterized in that: described antipricking layer also can be 5-15 layer grammes per square metre 300g/m
2--800g/m
2aramid fiber gummed cloth.
6. flexible ballistic-resistant stab-resistance body armor according to claim 1, is characterized in that: described burster course also can be 15-50 layer grammes per square metre 190g/m
2--500g/m
2aryl fiber cloth.
7. flexible ballistic-resistant stab-resistance body armor according to claim 1, is characterized in that: described overcoat skin is grammes per square metre 200g/m
2nOMEX IIIA fiber cloth.
8. flexible ballistic-resistant stab-resistance body armor according to claim 1, is characterized in that: described overcoat skin also can be grammes per square metre 240g/m
2nOMEX IIIA fiber cloth.
9. flexible ballistic-resistant stab-resistance body armor according to claim 1, is characterized in that: described overcoat skin also can be grammes per square metre 180-250g/m
2aramid fiber fire protection flame retarding cloth.