Abstract

A color wax fragrant clay and its production are disclosed. The process is carried out by taking refinery paraffin, palmic acid, mineral butter, ceresine wax and candle essence as raw materials, heating, dissolving, and mixed freezing to obtain final product. It costs low and has better quality.

Description

A kind of color candle clay with fragrance and preparation method thereof

Affiliated technical field

The present invention relates to a kind of color candle clay with fragrance and preparation method thereof.

Background technology

But the candle clay is a kind of soft wax of sculpture just, with the feel temperature softening just arbitrarily sculpture become the moulding of arbitrary shape, the insertion match is exactly a combustible candle, is that to have common candle now incomparable.Affablely hand-madely make various intention moulding and in red-letter day, birthday, party, give making a present of relatives and friends with it.It also is applied to make by hand, candle DIY etc., has very vast market development prospect improving in people's manipulative ability and culture, the recreation.

The method of making of relevant candle clay has had report in patent documentation: as disclosing a kind of method among the disclosed patent application CN93118145.3 March 29 nineteen ninety-five, this method is to be frozen into the candle clay with refining Chinese wax, stearic acid, tackifier and Vaseline or flaxseed wet goods raw material through heating for dissolving, mixing, the shortcoming of band cigarette and British plain spirits, no color when its prescription exists raw materials cost height, burning.The present invention is the color candle clay making method of another kind of band fragrance, and its prescription is optimized and improved, and smokeless and band fragrance has reduced raw materials cost during burning, adds an amount of candle dyestuff and just can produce versicolor color candle clay.

Summary of the invention

The object of the present invention is to provide a kind of color candle clay with fragrance.

Another object of the present invention provides the preparation method of the color candle clay of band fragrance.

For achieving the above object, the solution that the present invention adopts is: the present invention is frozen into wax stone by raw materials such as Refined Paraffin Wax, palmitinic acid, Microcrystalline Wax and Vaseline and candle essence, candle dyestuffs through heating for dissolving, mixing, at last wax stone is put into the color candle clay of the band fragrance of extrusion molding in the extrusion machine.It is to be main component with Refined Paraffin Wax 70%-80%, adds palmitinic acid 3%-10% and has replaced stearic acid, thereby make the smokeless generation when burning of candle clay; Thereby improved the plasticity-of candle clay and increased its viscosity by adding Microcrystalline Wax 8%-10% and Vaseline 8%-10%; Added an amount of candle essence 1%-2.5%, can produce comfortable fragrance when making the burning of candle clay and make us relaxed and joyful.More than can adjust according to the practical use increase or the minimizing ratio of product.

The present invention is made up of following component by weight percentage:

Refined Paraffin Wax: 70%-80%

Palmitinic acid: 3%-10%

Vaseline: 8%-10%

Microcrystalline Wax: 8%-10%

Candle essence: 1%-2.5%

As a further improvement on the present invention, can add an amount of candle dyestuff, produce versicolor candle clay according to the actual needs of product.

Above-mentioned each component is made production method of the present invention is:

1, Refined Paraffin Wax, candle dyestuff, palmitinic acid being put into pot successively heats;

When 2, stirring fusion, put into Microcrystalline Wax to 100 ℃, Vaseline stirs until whole fusions;

3, stop heating and continue stirring during Heating temperature to 120 ℃;

Add candle essence when 4, the temperature cooling is reduced to 90 ℃-100 ℃, pour the coolship cooling after stirring into up to being solidified into wax stone;

5, wax stone is put into extrusion molding in the extrusion machine.

The present invention has following advantage:

1. improved the usage ratio of paraffin in the prescription, reduced palmitinic acid, Microcrystalline Wax, Vaseline usage ratio, thereby reduced raw-material cost.

2. used palmitinic acid in the prescription, made the candle clay in the smokeless generation of when burning.

3. add candle essence in the prescription, can produce comfortable fragrance when making the burning of candle clay.

4. add an amount of candle dyestuff in the prescription and can produce versicolor candle clay.

5. reduce product cost, improved the class and the selling price of product.

Description of drawings

The invention will be further described below in conjunction with drawings and Examples.

Fig. 1 is a preparation method's of the present invention process flow sheet.

Embodiment

Take by weighing raw material (weight percent) by following proportioning:

1. lotus odor type white candle clay is filled a prescription

Refined Paraffin Wax: 78%

Palmitinic acid: 5%

Vaseline: 8%

Microcrystalline Wax: 8%

Lotus essence (candle essence): 1%

2. rose scent light red candle clay is filled a prescription

Refined Paraffin Wax: 77%

Palmitinic acid: 5.5%

Vaseline: 8%

Microcrystalline Wax: 8%

Rose compound (candle essence): 1.4%

Rose-red (candle dyestuff): 0.1%

Other color of the present invention and odor type can be allocated on demand voluntarily.Every can the adjustment in the prescription according to the practical use increase or the minimizing ratio of product.

Production method is as follows:

With reference to Fig. 1, Refined Paraffin Wax, candle dyestuff, palmitinic acid are put into pot successively heat, when stirring fusion, put into Microcrystalline Wax, Vaseline stirs until whole fusions to 100 ℃.Stop heating during Heating temperature to 120 ℃ and continue to stir, the temperature cooling adds candle essence when reducing to 90 ℃-100 ℃, pours the coolship cooling after stirring into up to being solidified into wax stone, at last wax stone is put into extrusion molding in the extrusion machine.

Claims

1, a kind of color candle clay with fragrance, it is characterized in that it makes (consumption is a per-cent) by the following weight proportion raw material: Refined Paraffin Wax: 70%-80%, palmitinic acid: 3%-10%, Vaseline: 8%-10%, Microcrystalline Wax: 8%-10%, candle essence: 1%-2.5%.

2, a kind of color candle clay with fragrance according to claim 1 is characterized in that: can add an amount of candle dyestuff according to the actual needs of product.

3, the preparation method of a kind of color candle clay with fragrance according to claim 1 and 2 is characterized in that: Refined Paraffin Wax, candle dyestuff, palmitinic acid are put into pot successively heat; When stirring fusion, put into Microcrystalline Wax to 100 ℃, Vaseline stirs until whole fusions; Stop heating during Heating temperature to 120 ℃ and continue to stir; The temperature cooling adds candle essence when reducing to 90 ℃-100 ℃, pours the coolship cooling after stirring into up to being solidified into wax stone; Wax stone is put into extrusion molding in the extrusion machine.