CN1443798A - Rubber tire containing pyrolyzed carbon black - Google Patents
Rubber tire containing pyrolyzed carbon black Download PDFInfo
- Publication number
- CN1443798A CN1443798A CN 02111000 CN02111000A CN1443798A CN 1443798 A CN1443798 A CN 1443798A CN 02111000 CN02111000 CN 02111000 CN 02111000 A CN02111000 A CN 02111000A CN 1443798 A CN1443798 A CN 1443798A
- Authority
- CN
- China
- Prior art keywords
- carbon black
- rubber
- butadiene
- accelerant
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a rubber tyre containing pyrolytic carbon black. It substitutes the existent carbon black obtained from natural gas, petroleum and ethylene tar with the pyrolytic carbon black, and utilizes the pyrolytic carbon black to produce rubber tyre. It has higher crosslinking property and dispersing property.
Description
Technical field:
The present invention relates to contain the processing of rubber tyre, particularly a kind of rubber tyre that contains pyrolytic carbon black.
Background technology:
In the prior art, need add carbon black during the processing rubber tire, carbon black is the reinforcement filler in the rubber tyre, can improve tensile strength, tearing force intensity and the wear hardness of rubber tyre, strengthen physicals and the work-ing life of containing rubber tyre, can increase the rubber volume.
Summary of the invention:
Technical problem to be solved by this invention is:because in the prior art, need add carbon black during the processing rubber tire, carbon black is the reinforcement filler in the rubber tyre, can improve tensile strength, tearing force intensity and the wear hardness of rubber tyre, the physicals of Reinforced Rubber tire and work-ing life, can increase the rubber volume.But needed carbon black is from Sweet natural gas, oil and ethylene bottom oil etc. during the processing rubber tire, and these material prices are more expensive. the present invention is that the technical scheme that solves the problems of the technologies described above employing is: a kind of rubber tyre that contains pyrolytic carbon black is provided; The described this rubber tyre that contains pyrolytic carbon black comprises inner liner glue; Inner ply compound; Outer cord ply compound; Triangle rubber; The steel wire doubling; The inner tube of a tyre and tire shoulder glue; Described inner liner glue is by natural rubber; Cis-butadiene cement; Butadiene-styrene rubber; Zinc oxide; Stearic acid; Sulfur; Pine tar; Pyrolytic carbon black; Carbon black N330; Altax; Accelerant CZ; Promoter T.T.; Antioxidant 4010 Na; Calcium carbonate; Chinese wax; Form with RH; Wherein, In described inner liner glue; The mass ratio of each component is---natural rubber: cis-butadiene cement: butadiene-styrene rubber: zinc oxide: stearic acid: Sulfur: pine tar: pyrolytic carbon black: carbon black N330: altax: accelerant CZ: promoter T.T.: antioxidant 4010 Na: calcium carbonate: Chinese wax: RH=35～45: 25～35: 25～35: 4～6: 1～2: 1～2: 3～6: 30～40: 7～13: 0.1～0.5: 0.3～0.8: 0.03～0.08: 0.2～0.7: 55～60: 0.5～1.5: 0.5～1.5; Described inner ply compound is by natural rubber; Cis-butadiene cement; Butadiene-styrene rubber; Zinc oxide; Stearic acid; Sulfur; Pine tar; Pyrolytic carbon black; Carbon black N330; Altax; Accelerant CZ; C9; Anti-aging agent RD; Antioxidant BLE; White carbon; RH and XB-10 form; In described inner ply compound; The mass ratio of each component is---natural gum: cis-butadiene cement: butadiene-styrene rubber: zinc oxide: stearic acid: Sulfur: pine tar: pyrolytic carbon black: carbon black N330: altax: accelerant CZ: C9: anti-aging agent RD: antioxidant BLE: white carbon: RH: XB-10=60～80: 15～25: 8～12: 3～9: 1～2: 2～3: 1～3: 25～30: 3～10: 0.1～0.3: 0.2～0.5: 0.5～1.5: 0.5～1.3: 1～1.5: 2～4: 0.3～0.8: 2～5; Described outer cord ply compound is by natural gum; Cis-butadiene cement; Butadiene-styrene rubber; Zinc oxide; Stearic acid; Sulfur; Pine tar; Pyrolytic carbon black; Carbon black N330; Altax; Accelerant CZ; C9; Anti-aging agent RD; RH and CTP form; In described outer cord ply compound; The mass ratio of each component is---natural gum: cis-butadiene cement: butadiene-styrene rubber: zinc oxide: stearic acid: Sulfur: pine tar: pyrolytic carbon black: carbon black N330: altax: accelerant CZ: C9: anti-aging agent RD: RH: CTP=70～90: 8～13: 8～12: 3～9: 0.5～1.5: 1～3: 3～8: 25～35: 8～12: 0.1～0.4: 0.5～1: 0.5～1.5: 0.8～1.2: 0.5～0.8: 0.08～0.12; Described triangle rubber is by natural gum; Butadiene-styrene rubber; Reclaimed rubber; Zinc oxide; Stearic acid; Sulfur; Machinery oil; Abrasion resistant carbon black; Pyrolytic carbon black; Accelerant CZ; Vulcanization accelerator TMTD; C9; Anti-aging agent RD; Calcium carbonate; Mineral glue and potter's clay form; In described triangle rubber; The mass ratio of each component is---natural gum: butadiene-styrene rubber: reclaimed rubber: zinc oxide: stearic acid: Sulfur: machinery oil: abrasion resistant carbon black: pyrolytic carbon black: accelerant CZ: Vulcanization accelerator TMTD: C9: anti-aging agent RD: calcium carbonate: mineral glue: potter's clay=65～75: 25～35: 98～102: 4～7: 2.6～3.2: 3～3.5: 1.6～2.3: 70～78: 23～28: 1～1.8: 0.03～0.06: 5～8: 1.6～2.1: 115～123: 8～12: 56～63; Described steel wire doubling is by natural gum; Zinc oxide; Sulfur; Pine tar; Pyrolytic carbon black; Accelerant NOBS; Antioxidant BLE; Calcium carbonate; Iron oxide red and solid cobaltic naphthenate form; In described steel wire doubling; The mass ratio of each component is---natural gum: zinc oxide: Sulfur: pine tar: pyrolytic carbon black: accelerant NOBS: antioxidant BLE: calcium carbonate: iron oxide red: solid cobaltic naphthenate=98～103: 10～13: 3～5: 15～16: 74～78: 0.6～1.0: 1.6～2.3: 198～203: 8～12: 2～2.6; The described inner tube of a tyre is by natural gum; Butadiene-styrene rubber; Zinc oxide; Stearic acid; Sulfur; Machinery oil; Pyrolytic carbon black; Accelerant CZ; Vulcanization accelerator TMTD; Anti-aging agent RD; Antioxidant 4010 Na and calcium carbonate form; In the described inner tube of a tyre; The mass ratio of each component is---natural gum: butadiene-styrene rubber: zinc oxide: stearic acid: Sulfur: machinery oil: pyrolytic carbon black: accelerant CZ: Vulcanization accelerator TMTD: anti-aging agent RD: antioxidant 4010 Na: calcium carbonate=66～75: 26～33: 3～6: 1.5～2.3: 1.5～2.2: 4～7: 36～44: 0.15～0.22: 0.06～0.12: 1.3～1.8: 0.4～0.6: 3～7; Described tire shoulder glue is by natural gum; Cis-butadiene cement; Zinc oxide; Stearic acid; Sulfur; Machinery oil; Pyrolytic carbon black; Carbon black N330; Accelerant NOBS; Vulcanization accelerator TMTD; Anti-aging agent RD; Antioxidant 4010 Na and DTDM form; In described tire shoulder glue; The mass ratio of each component is natural gum: cis-butadiene cement: zinc oxide: stearic acid: Sulfur: machinery oil: pyrolytic carbon black: carbon black N330: captax OBS: Vulcanization accelerator TMTD: anti-aging agent RD: antioxidant 4010 Na: DTDM=77～83: 18～22: 4～6: 2～2.8: 1.4～1.8: 4～6: 22～28: 18～23: 0.6～1.2: 0.06～0.12: 1.2～1.7: 0.8～1.3: 0.2～0.6. The technology that manufacturing contains the rubber tyre of pyrolytic carbon black adopts the manufacturing process manufacturing in the prior art.In described a kind of rubber tyre that contains pyrolytic carbon black, the vocabulary of terms of each component and chemical name correspondence are as follows:described natural rubber is an isoprene, described cis-butadiene cement is a polyhutadiene, described butadiene-styrene rubber is the multipolymer of vinylbenzene and divinyl, described reclaimed rubber is the reclaimed rubber of waste old through Physical Processing, described Stockholm tar is mixtures such as abietene class and resinous acid, and described zinc oxide is ZnO, and described stearic acid is CH3(CH
2)
16COOH, described machinery oil is the refining of petroleum oil product, described accelerant N OBS is a kind of benzothiazole sulphenamide, altax is a benzothiazyl disulfide, described accelerant CZ is a kind of benzothiazole sulphenamide, described TM monex TD is a tetramethyl-thiuram disulfide, described promotor T.T. is a tetramethylthiuram tetrasulfide, described antioxidant BLE is acetone and diphenylamine reaction resultant, described antioxidant 4010 Na is a sec.-propyl p-methylphenyl Ursol D, described anti-aging agent RD is a trimethylammonium dihyaroquinoline polymer, described white carbon black is a silicon-dioxide, described XB-10 is poly-dehydration two lubanols, described CTP is a cyclohexylthiophthalimide, described mineral glue is petroleum pitch, described potter's clay is the china clay in powder that rubber industry is used, described DTDM is a dithiodimorpholine, described abrasion resistant carbon black is (a GB3778-94 rubber grade carbon black), described carbon black N330 is (a GB3778-94 rubber grade carbon black), described C9 is resin PR2-90 (available from a U.S. FIRESTONE company), and described lime carbonate is CaCO
3The present invention contrasts prior art, owing to adopted pyrolytic carbon black, described pyrolytic carbon black is by nothing is peeled off, little negative pressure pyrolytic technique obtains product with junked tire, make rubber tyre have higher degree of crosslinking and diffustivity, than tire low price of the prior art, have identical reinfocing effect, tensile strength, tear strength.
Embodiment:
A kind of rubber tyre that contains pyrolytic carbon black of the present invention; Comprise inner liner glue; Inner ply compound; Outer cord ply compound; Triangle rubber; The steel wire doubling; The inner tube of a tyre and tire shoulder glue; In a preferred embodiment of the present invention; Described inner liner glue is by natural gum; Cis-butadiene cement; Butadiene-styrene rubber; Zinc oxide; Stearic acid; Sulfur; Pine tar; Pyrolytic carbon black; Carbon black N330; Altax; Accelerant CZ; Promoter T.T.; Antioxidant 4010 Na; Calcium carbonate; Chinese wax; Form with RH; Wherein, In described inner liner glue; The mass ratio of each component is---natural gum: cis-butadiene cement: butadiene-styrene rubber: zinc oxide: stearic acid: Sulfur: pine tar: pyrolytic carbon black: carbon black N330: altax: accelerant CZ: promoter T.T.: antioxidant 4010 Na: calcium carbonate: Chinese wax: RH=40: 30: 30: 5: 1.5: 1.2: 5: 35: 10: 0.3: 0.6: 0.05: 0.5: 57: 1: 1; Described inner ply compound is by natural gum; Cis-butadiene cement; Butadiene-styrene rubber; Zinc oxide; Stearic acid; Sulfur; Pine tar; Pyrolytic carbon black; Carbon black N330; Altax; Accelerant CZ; C9; Anti-aging agent RD; Antioxidant BLE; White carbon; RH and XB-10 form; In described inner ply compound; The mass ratio of each component is---natural gum: cis-butadiene cement: butadiene-styrene rubber: zinc oxide: stearic acid: Sulfur: pine tar: pyrolytic carbon black: carbon black N330: altax: accelerant CZ: C9: anti-aging agent RD: antioxidant BLE: white carbon: RH: XB-10=70: 20: 10: 5: 1.5: 2.5: 2: 27: 5: 0.2: 0.3: 1: 1: 1.29: 3: 0.5: 3; Described outer cord ply compound is by natural gum; Cis-butadiene cement; Butadiene-styrene rubber; Zinc oxide; Stearic acid; Sulfur; Pine tar; Pyrolytic carbon black; Carbon black N330; Altax; Accelerant CZ; C9; Anti-aging agent RD; RH and CTP form; In described outer cord ply compound; The mass ratio of each component is---natural gum: cis-butadiene cement: butadiene-styrene rubber: zinc oxide: stearic acid: Sulfur: pine tar: pyrolytic carbon black: carbon black N330: altax: accelerant CZ: C9: anti-aging agent RD: RH: CTP=80: 10: 10: 5: 1: 2: 5: 30: 10: 0.2: 0.7: 1: 1: 0.52: 0.1; Described triangle rubber is by natural gum; Butadiene-styrene rubber; Reclaimed rubber; Zinc oxide; Stearic acid; Sulfur; Machinery oil; Abrasion resistant carbon black; Pyrolytic carbon black; Accelerant CZ; Vulcanization accelerator TMTD; C9; Anti-aging agent RD; Calcium carbonate; Mineral glue and potter's clay form; In described triangle rubber; The mass ratio of each component is---natural gum: butadiene-styrene rubber: reclaimed rubber: zinc oxide: stearic acid: Sulfur: machinery oil: abrasion resistant carbon black: pyrolytic carbon black: accelerant CZ: Vulcanization accelerator TMTD: C9: anti-aging agent RD: calcium carbonate: mineral glue: potter's clay=70: 30: 100: 5: 3: 3.25: 2: 75: 25: 1.4: 0.05: 6: 2: 120: 10: 60; Described steel wire doubling is by natural gum; Zinc oxide; Sulfur; Pine tar; Pyrolytic carbon black; Accelerant NOBS; Antioxidant BLE; Calcium carbonate; Iron oxide red and solid cobaltic naphthenate form; In described steel wire doubling; The mass ratio of each component is---natural gum: zinc oxide: Sulfur: pine tar: pyrolytic carbon black: accelerant NOBS: antioxidant BLE: calcium carbonate: iron oxide red: solid cobaltic naphthenate=100: 12: 4: 15.5: 75: 0.8: 2: 200: 10: 2.4; The described inner tube of a tyre is by natural gum; Butadiene-styrene rubber; Zinc oxide; Stearic acid; Sulfur; Machinery oil; Pyrolytic carbon black; Accelerant CZ; Vulcanization accelerator TMTD; Anti-aging agent RD; Antioxidant 4010 Na and calcium carbonate form; In the described inner tube of a tyre; The mass ratio of each component is---natural gum: butadiene-styrene rubber: zinc oxide: stearic acid: Sulfur: machinery oil: pyrolytic carbon black: accelerant CZ: Vulcanization accelerator TMTD: anti-aging agent RD: antioxidant 4010 Na: calcium carbonate=70: 30: 4: 2: 1.8: 5: 40: 0.2: 0.1: 1.5: 0.5: 6; Described tire shoulder glue is by natural gum; Cis-butadiene cement; Zinc oxide; Stearic acid; Sulfur; Machinery oil; Pyrolytic carbon black; Carbon black N330; Accelerant NOBS; Vulcanization accelerator TMTD; Anti-aging agent RD; Antioxidant 4010 Na and DTDM form; In described tire shoulder glue; The mass ratio of each component is natural gum: cis-butadiene cement: zinc oxide: stearic acid: Sulfur: machinery oil: pyrolytic carbon black: carbon black N330: accelerant NOBS: Vulcanization accelerator TMTD: anti-aging agent RD: antioxidant 4010 Na: DTDM=80: 20: 5: 2.5: 1.5: 5: 25: 20: 1: 0.1: 1.5: 1: 0.5. The technology that manufacturing contains the rubber tyre of pyrolytic carbon black adopts the manufacturing process manufacturing in the prior art.The present invention contrasts prior art, owing to adopted pyrolytic carbon black, described pyrolytic carbon black is by nothing is peeled off, little negative pressure pyrolytic technique obtains product with junked tire, make rubber tyre have higher degree of crosslinking and diffustivity, than tire low price of the prior art, identical reinfocing effect, tensile strength, tear strength are arranged.
Claims (1)
1; A kind of rubber tyre that contains pyrolytic carbon black; Comprise inner liner glue; Inner ply compound; Outer cord ply compound; Triangle rubber; The steel wire doubling; The inner tube of a tyre and tire shoulder glue; It is characterized in that: described inner liner glue is by natural rubber; Cis-butadiene cement; Butadiene-styrene rubber; Zinc oxide; Stearic acid; Sulfur; Pine tar; Pyrolytic carbon black; Carbon black N330; Altax; Accelerant CZ; Promoter T.T.; Antioxidant 4010 Na; Calcium carbonate; Chinese wax and RH form; Wherein, In described inner liner glue; The mass ratio of each component is---natural rubber: cis-butadiene cement: butadiene-styrene rubber: zinc oxide: stearic acid: Sulfur: pine tar: pyrolytic carbon black: carbon black N330: altax: accelerant CZ: promoter T.T.: antioxidant 4010 Na: calcium carbonate: Chinese wax: RH=35～45: 25～35: 25～35: 4～6: 1～2: 1～2: 3～6: 30～40: 7～13: 0.1～0.5: 0.3～0.8: 0.03～0.08: 0.2～0.7: 55～60: 0.5～1.5: 0.5～1.5; Described inner ply compound is by natural gum; Cis-butadiene cement; Butadiene-styrene rubber; Zinc oxide; Stearic acid; Sulfur; Pine tar; Pyrolytic carbon black; Carbon black N330; Altax; Accelerant CZ; C9; Anti-aging agent RD; Antioxidant BLE; White carbon; RH and XB-10 form; In described inner ply compound; The mass ratio of each component is---natural gum: cis-butadiene cement: butadiene-styrene rubber: zinc oxide: stearic acid: Sulfur: pine tar: pyrolytic carbon black: carbon black N330: altax: accelerant CZ: C9: anti-aging agent RD: antioxidant BLE: white carbon: RH: XB-10=60～80: 15～25: 8～12: 3～9: 1～2: 2～3: 1～3: 25～30: 3～10: 0.1～0.3: 0.2～0.5: 0.5～1.5: 0.5～～1.3: 1～1.5: 2～4: 0.3～0.8: 2～5; Described outer cord ply compound is by natural gum; Cis-butadiene cement; Butadiene-styrene rubber; Zinc oxide; Stearic acid; Sulfur; Pine tar; Pyrolytic carbon black; Carbon black N330; Altax; Accelerant CZ; C9; Anti-aging agent RD; RH and CTP form; In described outer cord ply compound; The mass ratio of each component is---natural gum: cis-butadiene cement: butadiene-styrene rubber: zinc oxide: stearic acid: Sulfur: pine tar: pyrolytic carbon black: carbon black N330: altax: accelerant CZ: C9: anti-aging agent RD: RH: CTP=70～90: 8～13: 8～12: 3～9: 0.5～1.5: 1～3: 3～8: 25～35: 8～12: 0.1～0.4: 0.5～1: 0.5～1.5: 0.8～1.2: 0.5～0.8: 0.08～0.12; Described triangle rubber is by natural gum; Butadiene-styrene rubber; Reclaimed rubber; Zinc oxide; Stearic acid; Sulfur; Machinery oil; Abrasion resistant carbon black; Pyrolytic carbon black; Accelerant CZ; Vulcanization accelerator TMTD; C9; Anti-aging agent RD; Calcium carbonate; Mineral glue and potter's clay form; In described triangle rubber; The mass ratio of each component is---natural gum: butadiene-styrene rubber: reclaimed rubber: zinc oxide: stearic acid: Sulfur: machinery oil: abrasion resistant carbon black: pyrolytic carbon black: accelerant CZ: Vulcanization accelerator TMTD: C9: anti-aging agent RD: calcium carbonate: mineral glue: potter's clay=65～75: 25～35: 98～102: 4～7: 2.6～3.2: 3～3.5: 1.6～2.3: 70～78: 23～28: 1～1.8: 0.03～0.06: 5～8: 1.6～2.1: 115～123: 8～12: 56～63; Described steel wire doubling is by natural gum; Zinc oxide; Sulfur; Pine tar; Pyrolytic carbon black; Accelerant NOBS; Antioxidant BLE; Calcium carbonate; Iron oxide red and solid cobaltic naphthenate form; In described steel wire doubling; The mass ratio of each component is---natural gum: zinc oxide: Sulfur: pine tar: pyrolytic carbon black: accelerant NOBS: antioxidant BLE: calcium carbonate: iron oxide red: solid cobaltic naphthenate=98～103: 10～13: 3～5: 15～16: 74～78: 0.6～1.0: 1.6～2.3: 198～203: 8～12: 2～2.6; The described inner tube of a tyre is by natural gum; Butadiene-styrene rubber; Zinc oxide; Stearic acid; Sulfur; Machinery oil; Pyrolytic carbon black; Accelerant CZ; Vulcanization accelerator TMTD; Anti-aging agent RD; Antioxidant 4010 Na and calcium carbonate form; In the described inner tube of a tyre; The mass ratio of each component is---natural gum: butadiene-styrene rubber: zinc oxide: stearic acid: Sulfur: machinery oil: pyrolytic carbon black: accelerant CZ: Vulcanization accelerator TMTD: anti-aging agent RD: antioxidant 4010 Na: calcium carbonate=66～75: 26～33: 3～6: 1.5～2.3: 1.5～2.2: 4～7: 36～44: 0.15～0.22: 0.06～0.12: 1.3～1.8: 0.4～0.6: 3～7; Described tire shoulder glue is by natural gum; Cis-butadiene cement; Zinc oxide; Stearic acid; Sulfur; Machinery oil; Pyrolytic carbon black; Carbon black N330; Accelerant NOBS; Vulcanization accelerator TMTD; Anti-aging agent RD; Antioxidant 4010 Na and DTDM form; In described tire shoulder glue; The mass ratio of each component is natural gum: cis-butadiene cement: zinc oxide: stearic acid: Sulfur: machinery oil: pyrolytic carbon black: carbon black N330: accelerant NOBS: Vulcanization accelerator TMTD: anti-aging agent RD: antioxidant 4010 Na: DTDM=77～83: 18～22: 4～6: 2～2.8: 1. 4～1.8: 4～6: 22～28: 18～23: 0.6～1.2: 0.06～0.12: 1.2～1.7: 0.8～1.3: 0.2～0.6. Wherein, described natural rubber is an isoprene, described cis-butadiene cement is a polyhutadiene, described butadiene-styrene rubber is the multipolymer of vinylbenzene and divinyl, described reclaimed rubber is the reclaimed rubber of waste old through Physical Processing, described Stockholm tar is mixtures such as abietene class and resinous acid, and described zinc oxide is ZnO, and described stearic acid is CH3(CH
2)
16COOH, described machinery oil is the refining of petroleum oil product, described accelerant N OBS is a kind of benzothiazole sulphenamide, altax is a benzothiazyl disulfide, described accelerant CZ is a kind of benzothiazole sulphenamide, described TM monex TD is a tetramethyl-thiuram disulfide, described promotor T.T. is a tetramethylthiuram tetrasulfide, described antioxidant BLE is acetone and diphenylamine reaction resultant, described antioxidant 4010 Na is a sec.-propyl p-methylphenyl Ursol D, described anti-aging agent RD is a trimethylammonium dihyaroquinoline polymer, described white carbon black is a silicon-dioxide, described XB-10 is poly-dehydration two lubanols, described CTP is a cyclohexylthiophthalimide, described mineral glue is petroleum pitch, described potter's clay is the china clay in powder that rubber industry is used, described DTDM is a dithiodimorpholine, described abrasion resistant carbon black is (a GB3778-94 rubber grade carbon black), described carbon black N330 is (a GB3778-94 rubber grade carbon black), described C9 is resin PR2-90 (available from a U.S. FIRESTONE company), and described lime carbonate is CaCO
3