CN1223331C - 美甲产品 - Google Patents
美甲产品 Download PDFInfo
- Publication number
- CN1223331C CN1223331C CNB018041558A CN01804155A CN1223331C CN 1223331 C CN1223331 C CN 1223331C CN B018041558 A CNB018041558 A CN B018041558A CN 01804155 A CN01804155 A CN 01804155A CN 1223331 C CN1223331 C CN 1223331C
- Authority
- CN
- China
- Prior art keywords
- quality
- nail
- gloss
- polyester resin
- nitroncellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及美甲产品。本发明的目的是提供易于涂布指甲，涂布指甲所形成的涂膜的强度、光泽优良而且涂膜经时耐久、光泽不减的溶剂基美甲产品。解决课题的手段是含有以下(a)-(d)的美甲产品，其中(a)硝基纤维素、(b)三苯六甲酸新戊二醇己二酯聚酯树脂，(c)选自含有甲基丙烯酸烷基酯·丙烯酸烷基酯的共聚物、苯甲酸蔗糖酯和玻璃化转变温度为50～80℃的高分子化合物的一种或多两种以上物质、(d)溶剂。根据本发明，能够获得具有易于涂布指甲，涂布指甲所形成的涂膜强度、光泽优良而且涂膜历时难于剥落、光泽不减的溶剂基美甲产品。
Description
技术领域：
本发明涉及美甲产品。更详细地说就是涉及易于涂布指甲、涂布指甲所形成涂膜的强度、光泽优良而且涂膜历时不易剥落、光泽不减的溶剂基美甲产品。
背景技术
以往，对于溶剂基美甲产品，为了改良涂布简便性、光泽、剥离特性等特性，配合使用各种树脂。这当中有很多以硝基纤维素作为涂膜剂的技术，例如特开昭61-246113号公报中，公开了在含有硝基纤维素的美甲产品中，同时使用Versatic酸缩水甘油酯改性醇酸树脂等的改性醇酸树脂和苯甲酸蔗糖酯以改良剥离特性等的美甲产品。特开平5-213719号公报中，公开了在上述特开昭61-246113号公报记载技术基础上，进一步含有硅氧烷类接枝共聚物以改良剥离特性等的美甲产品。
更进一步，已开发了很多代替硝基纤维素的涂膜形成剂，特开昭54-129137号公报中，公开了含有甲基丙烯酸甲酯和/或甲基丙烯酸乙酯35～65质量％和甲基丙烯酸丙酯和/或甲基丙烯酸丁酯65～35质量％构成的甲基丙烯酸酯共聚物，甲基丙烯酸甲酯和/或甲基丙烯酸乙酯50-85质量％和丙烯酸甲酯和/或丙烯酸乙酯50～15质量％构成的甲基丙烯酸酯-丙烯酸酯共聚物等的丙烯酸树脂(优选数均分子量15000～200000)混合物作为涂膜形成剂的美甲产品。此外，特开平6-279239号公报中，公开了使用苯乙烯和/或甲基丙烯酸甲酯20-85质量％、丙烯酸烷基酯(烷基链长1～8)5～60质量％和丙烯酸7～30质量％构成的分子量10000～70000的共聚物作为涂膜形成剂的美甲产品。
像这样，对于提高美甲产品所要求各种特性的制品的研究正方兴未艾。特别是最近，消费者对美甲产品有更高的品质要求，其嗜好向多样化发展，所以对于同时具有多种优良特性的美甲产品的期望比以往都迫切。
本发明鉴于上述情况，以提供易于涂布指甲、涂布指甲所形成皮膜(涂膜)的强度、光泽优良而且涂膜耐久、光泽不减的溶剂基美甲产品作为目的。
发明的公开
本发明者们为了解决上述课题进行了反复深入研究，结果发现含有硝基纤维素的溶剂基美甲产品中，以特定的聚酯树脂配合特定的丙烯酸类树脂、蔗糖衍生物或具有特定玻璃化转变温度的高分子化合物，就解决了上述课题，从而完成了本发明。
即，本发明就是含有(a)硝基纤维素和(b)偏苯三酸新戊二醇己二酸聚酯树脂和(c)选自含有甲基丙烯酸烷基酯·丙烯酸烷基酯的共聚物、苯甲酸蔗糖酯和玻璃化转变温度为50～80℃的高分子化合物的一种或两种以上物质和(d)溶剂的美甲产品。
上述偏苯三酸新戊二醇己二酸聚酯树脂的酸价优选10～30mgKOH/g。在此范围内，能够更好地发挥防止涂膜历时剥落的效果。
构成上述含有甲基丙烯酸烷基酯·丙烯酸烷基酯的共聚物的甲基丙烯酸酯和丙烯酸烷基酯的烷基的碳数，分别优选1～8。在此范围内，能够更好地发挥涂膜强度和光泽的效果。
上述含有甲基丙烯酸烷基酯·丙烯酸烷基酯的共聚物的质均分子量优选1000～9000。在此范围内，能够更好地发挥涂膜强度、光泽优良和防止涂膜历时剥落的效果。此外，涂布的容易程度也特别优良。
实施发明的最佳形式
下面详细说明本发明的实施方式。
(a)作为成分的硝基纤维素，可以使用以往所用并广为人知的，一种或两种以上组合使用。作为硝基纤维素的例子，例如有硝基纤维素1/16秒、硝基纤维素1/8秒、硝基纤维素1/4秒、硝基纤维素1/2秒、硝基纤维素1秒、硝基纤维素2秒、硝基纤维素7秒、硝基纤维素20秒等。其中优选硝基纤维素1/16秒、硝基纤维素1/8秒、硝基纤维素1/4秒、硝基纤维素1/2秒。
硝基纤维素的配比量取决于其他的配比成分，在30质量％的异丙醇湿润状态(下面称为30％IPA)下，优选为美甲产品总量的5～25质量％，即折算成硝基纤维素的配比量为3.5～17.5质量％。如不足5质量％，有历时光泽减低的问题，另一方面，如果超过25质量％则有涂布变得困难的问题。特别优选10～20质量％。在此范围内能够充分发挥本发明的效果。
作为成分(b)的偏苯三酸新戊二醇己二酸聚酯树脂，是将偏苯三酸、新戊二醇和己二酸反应所得的聚合物。以上述3种成分以各种的比例混合得到的聚合物中，优选酸价10～30mg KOH/g的。在此范围内，能够很好发挥防止涂膜历时剥落的效果。本发明的偏苯三酸新戊二醇己二酸聚酯树脂，下面简称为己二酸聚酯树脂。己二酸聚酯树脂，例如可以使用市售品“UNIPLEX670-P”(UNITEX化学公司制造)。
己二酸聚酯树脂的配比量同时取决于其他的配比成分，但优选美甲产品总量的3.0～20.0质量％。不足3.0质量％，则有历时剥落效果变差的倾向，超过20.0质量％时，则有光泽、强度不良的倾向。特别优选5～15质量％。在此范围内，能充分发挥本发明的效果。
作为构成(c)成分的含有甲基丙烯酸烷基酯·丙烯酸烷基酯的共聚物中的甲基丙烯酸烷基酯和丙烯酸烷基酯的烷基，均选碳数1～8的。在此范围内，能够更好地发挥涂膜的强度和光泽的效果。
甲基丙烯酸烷基酯，例如有甲基丙烯酸甲酯、甲基丙烯酸乙酯、甲基丙烯酸丙酯、甲基丙烯酸丁酯、甲基丙烯酸辛酯、甲基丙烯酸2-乙基己酯等。丙烯酸烷基酯，例如有丙烯酸甲酯、丙烯酸乙酯、丙烯酸丙酯、丙烯酸丁酯、丙烯酸辛酯、丙烯酸2-乙基己酯等。
作为构成含有甲基丙烯酸烷基酯·丙烯酸烷基酯的共聚物的甲基丙烯酸烷基酯和丙烯酸烷基酯以外的单体，例如有苯乙烯、甲基丙烯酸、丙烯酸、丙烯腈等，但并不是必需的。
含有甲基丙烯酸烷基酯·丙烯酸烷基酯的共聚物可按一般的制造方法合成。例如，将构成共聚物的单体进行游离基聚合而得到产物。当然，可以使用市售的共聚物，作为市售品，例如有JONCRYL611(销售商Johnson聚合物株式会社)等。JONCRYL611是具有玻璃化转变温度64℃的高分子化合物。含有甲基丙烯酸烷基酯·丙烯酸烷基酯的共聚物可以一种或两种以上配合使用。
含有甲基丙烯酸烷基酯·丙烯酸烷基酯共聚物的分子量，优选质均分子量为1000～20000者。为显著发挥本发明的效果，特别优选低分子量的1000～9000。在此范围内，能够显著发挥增强涂膜强度和光泽、防止经时涂膜脱落的效果。
含有甲基丙烯酸烷基酯·丙烯酸烷基酯的共聚物的配比量，取决于该共聚物的物理性质，以及其他的配比成分，但优选占美甲产品总量的1～25质量％。不足1质量％时，有涂膜强度低、经时光泽减弱等问题，另一方面，超过25质量％时，有历时剥落性降低的倾向，此外涂布也变得不容易。特别优选8～20质量％，在此范围内，能够充分地发挥本发明的效果。
本发明的所用的(c)成分的其它成分苯甲酸蔗糖酯，作为以往美甲产品用的树脂是广为人知的。苯甲酸蔗糖酯也可以使用市售品，作为市售品，例如有第一工业制药株式会社生产的商品名为单百多(モノペツト)SB以及苯甲酸蔗糖酯(美国威鲁西考路化学公司生产)。单百多(モノペツト)SB(第一工业制药株式会社)是玻璃化转变温度为64℃的高分子化合物。
苯甲酸蔗糖酯的配比量取决于和其它成分配合的情况，优选占美甲产品总量的0.5-25质量％的范围。不足0.5质量％时，有涂膜强度低下，历时光泽减弱的问题，另一方面，超过25质量％时，有历时剥落性降低的倾向，此外也变得不易涂布。更优选3-15质量％。在此范围内，能够充分发挥本发明的效果。
本发明所用的(c)成分中的另一种，是玻璃化转变温度为50～80℃的高分子化合物。更优选玻璃化转变温度为55～75℃的高分子化合物。还有，玻璃化转变温度的测定，应用DSC(示差扫描热量计)(精工仪表公司制造的SSC5100)，在样品量10mg、升温条件5℃/分、范围-20℃～120℃内进行测定，将所得的图中的DSC的峰直立上升的温度作为玻璃化转变温度。在本发明中，上述其他(c)的成分中可含有玻璃化转变温度50～80℃的物质，但也可以使用除此以外的高分子化合物。玻璃化转变温度为50～80℃的高分子化合物可以一种或两种以上配合使用。
玻璃化转变温度为50～80℃的高分子化合物的配比量同时取决于其他配比成分，但优选与美甲产品总量的0.5～25质量％的范围。不足0.5质量％时，有涂膜强度降低、经时光泽降低等问题，另一方面，超过25质量％时，有经时不耐久的倾向，而且涂布变得不容易。更优选3～15质量％。在此范围内，能充分发挥本发明的效果。
(c)成分的含有甲基丙烯酸烷基酯·丙烯酸烷基酯的共聚物、苯甲酸蔗糖酯和玻璃化转变温度50～80℃的高分子化合物混合使用时，优选三者合计的配比在25质量％以下。
作为(d)成分的溶剂，可以使用以往所用的酯类、醇类、烃类等周知的溶剂。例如，乙酸甲酯、乙酸乙酯、乙酸丁酯、乙酸戊酯、乳酸乙酯、乳酸丁酯、乙醇、异丙醇、丁醇、甲苯、乙酸异丁酯、乙酸丙酯、乙酸异丙酯、丙醇等。其中优选乙酸丁酯、乙酸乙酯、异丙醇、丁醇、乙醇等。溶剂可以一种或两种以上组合使用。
溶剂的配比量因使用性、颜色等的不同而不同，一般为美甲产品总量的50～85质量％。
本发明的美甲产品，在不损害本发明的效果下，除了上述组成成分，还可以根据需要加入本发明必需成分树脂外的树脂、增塑剂、颜料、香料、染料、珠光(パ-ル)剂、层化(ラメ)剂、药物、保湿剂、紫外线吸收剂、消艳剂、填充剂、表面活性剂、增粘剂、金属皂、有机酸等的粘土调节剂等一般美甲产品配比的原料。在这其中，增塑剂可提高剥离性、涂膜强度等涂膜特性，任选配合于本发明美甲产品优选中。
作为增塑剂，可以使用樟脑、邻苯二甲酸酯类、柠檬酸酯类等周知的物质。例如有邻苯二甲酸二丁酯、邻苯二甲酸二辛酯、柠檬酸三丁酯、柠檬酸乙酰基三乙酯、柠檬酸乙酰基三丁酯等。在这其中可以任意选择一种或两种以上。其配比量一般美甲产品总量的1～10质量％。
作为本发明必需成分树脂以外的树脂，有Versatic酸缩水甘油酯改性醇酸树脂等的改性醇酸树脂、甲苯磺酰胺树脂、蔗糖乙酸异丁酸酯、硅氧烷类接枝共聚物等。配合这些树脂，能够不损害涂布的容易程度和光泽等，而进一步改良剥离特性减少对指甲的压迫感等。
这些树脂的配比量优选与美甲产品总量的0.1～10质量％。
本发明的溶剂基美甲产品为包括化妆品业界中一般作为修饰指甲用品类、美甲用品等使用的指甲被覆剂，例如有除指甲油底(ベ-スコ-ト)、指甲油、外涂油(顶涂油(オ-バ-コ-ト))之外、护甲油(ネ-ルガ-ド)等指甲养护(ネ-ルケア)用品等，但并不仅限于这些例子。
下面基于实施例对本发明进行详细的说明。还有，配比量为质量％。
在说明实施例之前，先说明本实施例所用的各种评价方法。
〔涂布的容易程度〕
填充于带刷的10毫升玻璃瓶的各样品，涂布于20名专门评判员的指甲(一次涂布、二次涂布)，涂布时的容易程度进行5级评价。接着合计各人的评价分数。评价标准如后述。
(评价分数)
5分：非常润滑地涂布
4分：润滑地涂布
3分：普通
2分：难于涂布
1分：非常难于涂布
〔涂膜的强度〕
填充于带刷的10毫升玻璃瓶的各样品，涂布于20名专门评判员的指甲，在生活环境下4天后对指甲涂膜损伤的情况进行5级评价。接着合计各人的评价分数。评价标准如后述。
(评价分数)
5分：非常难于受损
4分：难于受损
3分：普通
2分：容易受损
1分：非常容易受损
〔光泽〕
填充于带刷的10毫升玻璃瓶的各样品，涂布于20名专门评判员的指甲，对10分钟后和生活环境下4天后涂膜的光泽进行5级评价。接着合计各人的评价分数。评价标准如后述。
(评价分数)
5分：非常有光泽
4分：有光泽
3分：普通
2分：没有光泽
1分：非常没有光泽
〔历时剥落性〕
填充于带刷的10毫升玻璃瓶的各样品，涂布于20名专门评判员的指甲，在生活环境下4天后对涂膜的剥落进行5级评价。接着合计各人的评价分数。评价标准如后述。
(评价分数)
5分：非常难于剥落
4分：难于剥落
3分：普通
2分：容易剥落
1分：非常容易剥落
(上述各项目的评价标准)
◎：合计分数90以上
○：合计分数70以上，小于90
□：合计分数50以上，小于70
△：合计分数30以上，小于50
×：合计分数低于30
(实施例1～45、比较例1～4)
如表1～10所示，按常法调制美甲产品，分别根据上述评价方法，对涂布容易程度、涂膜强度、光泽、历时剥落性等进行评价。结果分别表示在表1～10中。
表1
| 实施例 | 比较例 | |||||||
| 1 | 2 | 3 | 1 | 2 | 3 | 4 | ||
| 硝基纤维素1/4秒(30％IPA)(a) | 12 | 12 | 12 | 12 | 12 | 12 | 12 | |
| 己二酸聚酯树脂(b) | 10 | 10 | 10 | 10 | - | - | - | |
| 甲基丙烯酸甲酯·丙烯酸丁酯共聚物(c) | 10 | - | - | - | 10 | - | - | |
| 苯甲酸蔗糖酯(c) | - | 10 | - | - | - | 10 | - | |
| JONCRYL611(c) | - | - | 10 | - | - | - | 10 | |
| 柠檬酸乙酰基三乙酯 | 5 | 5 | 5 | 5 | 5 | 5 | 5 | |
| 正丁醇 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | |
| 乙酸乙酯 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | |
| 乙酸正丁酯 | 残余 | 残余 | 残余 | 残余 | 残余 | 残余 | 残余 | |
| 有机改性粘土矿物 | 适量 | 适量 | 适量 | 适量 | 适量 | 适量 | 适量 | |
| 珠光剂 | 2 | 2 | 2 | 2 | 2 | 2 | 2 | |
| 颜料 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | |
| 涂布的容易程度 | ◎ | ◎ | ◎ | ○ | △ | △ | △ | |
| 涂膜强度 | ◎ | ◎ | ◎ | △ | ○ | ○ | ○ | |
| 光泽 | 10分钟后 | ◎ | ◎ | ◎ | △ | ○ | ○ | ○ |
| 4天后 | ○ | ○ | ○ | △ | □ | □ | □ | |
| 历时剥落性 | ◎ | ◎ | ◎ | ○ | × | × | × | |
表1中，己二酸聚酯树脂使用UNIPLEX670-P。此外，甲基丙烯酸甲酯·丙烯酸丁酯共聚物的分子量为质均分子量8100。
从表1可见，配合硝基纤维素1/4秒、己二酸聚酯树脂和甲基丙烯酸甲酯·丙烯酸丁酯共聚物的实施例1、配合硝基纤维素1/4秒、己二酸聚酯树脂和苯甲酸蔗糖酯的实施例2、配合硝基纤维素1/4秒、己二酸聚酯树脂和JONCRYL611的实施例3，涂布的容易程度、涂膜强度、光泽、历时剥落性等任何一项指标都很优良。
与此相反，没有配合(c)成分的比较例1，在涂膜强度、光泽等方面不足。此外，没有配合(b)成分己二酸聚酯树脂的比较例2、3和4，在涂布的容易程度、历时剥落性等方面特别不足。
表2
| 实施例 | |||||
| 4 | 5 | 6 | 7 | ||
| 硝基纤维素1/4秒(30％IPA)(a) | 5 | 10 | 20 | 25 | |
| 己二酸聚酯树脂(b) | 10 | 10 | 10 | 10 | |
| 甲基丙烯酸甲酯·丙烯酸丁酯共聚物(c) | 10 | 10 | 10 | 10 | |
| 柠檬酸乙酰基三乙酯 | 5 | 5 | 5 | 5 | |
| 正丁醇 | 1 | 1 | 1 | 1 | |
| 乙酸乙酯 | 20 | 20 | 20 | 20 | |
| 乙酸正丁酯 | 残余 | 残余 | 残余 | 残余 | |
| 有机改性粘土矿物 | 适量 | 适量 | 适量 | 适量 | |
| 珠光(パ-ル)剂 | 2 | 2 | 2 | 2 | |
| 颜料 | 1 | 1 | 1 | 1 | |
| 涂布容易程度 | ◎ | ◎ | ◎ | ○ | |
| 涂膜强度 | ○ | ◎ | ◎ | ◎ | |
| 光泽 | 10分钟后 | ○ | ◎ | ◎ | ◎ |
| 4天后 | ○ | ○ | ○ | ○ | |
| 历时剥落性 | ○ | ◎ | ◎ | ○ | |
表2中，己二酸聚酯树脂使用UNIPLEX670-P。此外，甲基丙烯酸甲酯·丙烯酸丁酯共聚物的分子量为质均分子量8100。
如表2所示，硝基纤维素的配比量在5～25质量％的范围可得到优良的效果。还有，特别优选10～20质量％。
表3
| 实施例 | |||||
| 8 | 9 | 10 | 11 | ||
| 硝基纤维素1/4秒(30％IPA)(a) | 5 | 10 | 20 | 25 | |
| 己二酸聚酯树脂(b) | 10 | 10 | 10 | 10 | |
| 苯甲酸蔗糖酯(c) | 10 | 10 | 10 | 10 | |
| 柠檬酸乙酰基三乙酯 | 5 | 5 | 5 | 5 | |
| 正丁醇 | 0.5 | 0.5 | 0.5 | 0.5 | |
| 乙酸乙酯 | 20 | 20 | 20 | 20 | |
| 乙酸正丁酯 | 残余 | 残余 | 残余 | 残余 | |
| 有机改性粘土矿物 | 适量 | 适量 | 适量 | 适量 | |
| 珠光剂 | 2 | 2 | 2 | 2 | |
| 颜料 | 1 | 1 | 1 | 1 | |
| 涂布容易程度 | ◎ | ◎ | ◎ | ○ | |
| 涂膜强度 | ○ | ◎ | ◎ | ◎ | |
| 光泽 | 10分钟后 | ○ | ◎ | ◎ | ◎ |
| 4天后 | ○ | ○ | ○ | ○ | |
| 历时剥落性 | ○ | ◎ | ◎ | ○ | |
表3中，己二酸聚酯树脂使用UNIPLEX670-P。如表3所示，硝基纤维素的配比量在5～25质量％的范围可得到优良的效果。还有，特别优选10～20质量％。
表4
| 实施例 | |||||
| 12 | 13 | 14 | 15 | ||
| 硝基纤维素1/4秒(30％IPA)(a) | 5 | 10 | 20 | 25 | |
| 己二酸聚酯树脂(b) | 10 | 10 | 10 | 10 | |
| JONCRYL611(c) | 10 | 10 | 10 | 10 | |
| 柠檬酸乙酰基三乙酯 | 5 | 5 | 5 | 5 | |
| 正丁醇 | 0.5 | 0.5 | 0.5 | 0.5 | |
| 乙酸乙酯 | 20 | 20 | 20 | 20 | |
| 乙酸正丁酯 | 残余 | 残余 | 残余 | 残余 | |
| 有机改性粘土矿物 | 适量 | 适量 | 适量 | 适量 | |
| 珠光剂 | 2 | 2 | 2 | 2 | |
| 颜料 | 1 | 1 | 1 | 1 | |
| 涂布容易程度 | ◎ | ◎ | ◎ | ○ | |
| 涂膜强度 | ○ | ◎ | ◎ | ◎ | |
| 光泽 | 10分钟后 | ○ | ◎ | ◎ | ◎ |
| 4天后 | ○ | ○ | ○ | ○ | |
| 历时剥落性 | ○ | ◎ | ◎ | ○ | |
表4中，己二酸聚酯树脂使用UNIPLEX670-P。如表4所示，硝基纤维素的配比量在5～25质量％的范围可得到优良的效果。还有，特别优选10～20质量％。
表5
| 实施例 | ||||||
| 16 | 17 | 18 | 19 | 20 | ||
| 硝基纤维素1/4秒(30％IPA)(a) | 12 | 12 | 12 | 12 | 12 | |
| 己二酸聚酯树脂(b) | 3 | 5 | 7 | 15 | 20 | |
| 甲基丙烯酸甲酯·丙烯酸丁酯共聚物(c) | 10 | 10 | 10 | 10 | 10 | |
| 柠檬酸乙酰基三乙酯 | 5 | 5 | 5 | 5 | 5 | |
| 正丁醇 | 1 | 1 | 1 | 1 | 1 | |
| 乙酸乙酯 | 20 | 20 | 20 | 20 | 20 | |
| 乙酸正丁酯 | 残余 | 残余 | 残余 | 残余 | 残余 | |
| 有机改性粘土矿物 | 适量 | 适量 | 适量 | 适量 | 适量 | |
| 珠光剂 | 2 | 2 | 2 | 2 | 2 | |
| 颜料 | 3 | 3 | 3 | 3 | 3 | |
| 涂布容易程度 | ◎ | ◎ | ◎ | ◎ | ◎ | |
| 涂膜强度 | ◎ | ◎ | ◎ | ◎ | ○ | |
| 光泽 | 10分钟后 | ◎ | ◎ | ◎ | ◎ | ○ |
| 4天后 | ○ | ○ | ○ | ○ | ○ | |
| 历时剥落性 | ○ | ◎ | ◎ | ◎ | ◎ | |
表5中，己二酸聚酯树脂使用UNIPLEX670-P。此外，甲基丙烯酸甲酯·丙烯酸丁酯共聚物的分子量为质均分子量8000。
如表5所示，己二酸聚酯树脂的配比量在3～20质量％的范围可得到优良的效果。还有，特别优选5～15质量％。
表6
| 实施例 | ||||||
| 21 | 22 | 23 | 24 | 25 | ||
| 硝基纤维素1/4秒(30％IPA)(a) | 12 | 12 | 12 | 12 | 12 | |
| 己二酸聚酯树脂(b) | 3 | 5 | 7 | 15 | 20 | |
| 苯甲酸蔗糖酯(c) | 10 | 10 | 10 | 10 | 10 | |
| 柠檬酸乙酰基三乙酯 | 5 | 5 | 5 | 5 | 5 | |
| 正丁醇 | 1 | 1 | 1 | 1 | 1 | |
| 乙酸乙酯 | 20 | 20 | 20 | 20 | 20 | |
| 乙酸正丁酯 | 残余 | 残余 | 残余 | 残余 | 残余 | |
| 有机改性粘土矿物 | 适量 | 适量 | 适量 | 适量 | 适量 | |
| 珠光剂 | 2 | 2 | 2 | 2 | 2 | |
| 颜料 | 1 | 1 | 1 | 1 | 1 | |
| 涂布容易程度 | ○ | ◎ | ◎ | ◎ | ○ | |
| 涂膜强度 | ◎ | ◎ | ◎ | ◎ | ○ | |
| 光泽 | 10分钟后 | ○ | ◎ | ◎ | ◎ | ◎ |
| 4天后 | ○ | ○ | ○ | ○ | ○ | |
| 历时剥落性 | ○ | ◎ | ◎ | ◎ | ◎ | |
表6中，己二酸聚酯树脂使用UNIPLEX670-P。如表6所示，己二酸聚酯树脂的配比量在3～20质量％的范围可得到优良的效果。还有，特别优选5～15质量％。
表7
| 实施例 | ||||||
| 26 | 27 | 28 | 29 | 30 | ||
| 硝基纤维素1/4秒(30％IPA)(a) | 12 | 12 | 12 | 12 | 12 | |
| 己二酸聚酯树脂(b) | 3 | 5 | 7 | 15 | 20 | |
| JONCRYL611(c) | 10 | 10 | 10 | 10 | 10 | |
| 柠檬酸乙酰基三乙酯 | 5 | 5 | 5 | 5 | 5 | |
| 正丁醇 | 1 | 1 | 1 | 1 | 1 | |
| 乙酸乙酯 | 20 | 20 | 20 | 20 | 20 | |
| 乙酸正丁酯 | 残余 | 残余 | 残余 | 残余 | 残余 | |
| 有机改性粘土矿物 | 适量 | 适量 | 适量 | 适量 | 适量 | |
| 珠光剂 | 2 | 2 | 2 | 2 | 2 | |
| 颜料 | 1 | 1 | 1 | 1 | 1 | |
| 涂布容易程度 | ○ | ◎ | ◎ | ◎ | ○ | |
| 涂膜强度 | ◎ | ◎ | ◎ | ◎ | ○ | |
| 光泽 | 10分钟后 | ○ | ◎ | ◎ | ◎ | ◎ |
| 4天后 | ○ | ○ | ○ | ○ | ○ | |
| 历时剥落性 | ○ | ◎ | ◎ | ◎ | ◎ | |
表7中，己二酸聚酯树脂使用UNIPLEX670-P。如表7所示，己二酸聚酯树脂的配比量在3～20质量％的范围可得到优良的效果。还有，特别优选5～15质量％。
表8
| 实施例 | ||||||
| 31 | 32 | 33 | 34 | 35 | ||
| 硝基纤维素1/4秒(30％IPA)(a) | 10 | 10 | 10 | 10 | 10 | |
| 己二酸聚酯树脂(b) | 10 | 10 | 10 | 10 | 10 | |
| 甲基丙烯酸乙酯·丙烯酸丁酯共聚物(c) | 1 | 8 | 15 | 20 | 25 | |
| 柠檬酸乙酰基三乙酯 | 5 | 5 | 5 | 5 | 5 | |
| 正丁醇 | 1 | 1 | 1 | 1 | 1 | |
| 乙酸乙酯 | 20 | 20 | 20 | 20 | 20 | |
| 乙酸正丁酯 | 残余 | 残余 | 残余 | 残余 | 残余 | |
| 有机改性粘土矿物 | 适量 | 适量 | 适量 | 适量 | 适量 | |
| 珠光剂 | 2 | 2 | 2 | 2 | 2 | |
| 颜料 | 3 | 3 | 3 | 3 | 3 | |
| 涂布容易程度 | ◎ | ◎ | ◎ | ◎ | ○ | |
| 涂膜强度 | ○ | ◎ | ◎ | ◎ | ◎ | |
| 光泽 | 10分钟后 | ○ | ◎ | ◎ | ◎ | ◎ |
| 4天后 | ○ | ○ | ○ | ○ | ○ | |
| 历时剥落性 | ◎ | ◎ | ◎ | ◎ | ◎ | |
表8中，己二酸聚酯树脂使用UNIPLEX670-P。此外，甲基丙烯酸甲酯·丙烯酸丁酯共聚物的分子量为质均分子量8000。
如表8所示，甲基丙烯酸甲酯·丙烯酸丁酯共聚物的配比量在1～25质量％的范围可得到优良的效果。还有，特别优选8～20质量％。
表9
| 实施例 | ||||||
| 36 | 37 | 38 | 39 | 40 | ||
| 硝基纤维素1/4秒(30％IPA)(a) | 10 | 10 | 10 | 10 | 10 | |
| 己二酸聚酯树脂(b) | 10 | 10 | 10 | 10 | 10 | |
| 苯甲酸蔗糖酯(c) | 0.5 | 3 | 6 | 15 | 25 | |
| 柠檬酸乙酰基三乙酯 | 5 | 5 | 5 | 5 | 5 | |
| 正丁醇 | 1 | 1 | 1 | 1 | 1 | |
| 乙酸乙酯 | 20 | 20 | 20 | 20 | 20 | |
| 乙酸正丁酯 | 残余 | 残余 | 残余 | 残余 | 残余 | |
| 有机改性粘土矿物 | 适量 | 适量 | 适量 | 适量 | 适量 | |
| 珠光剂 | 2 | 2 | 2 | 2 | 2 | |
| 颜料 | 1 | 1 | 1 | 1 | 1 | |
| 涂布容易程度 | ◎ | ◎ | ◎ | ◎ | ○ | |
| 涂膜强度 | ○ | ◎ | ◎ | ◎ | ◎ | |
| 光泽 | 10分钟后 | ○ | ◎ | ◎ | ◎ | ◎ |
| 4天后 | ○ | ○ | ○ | ○ | ○ | |
| 历时剥落性 | ◎ | ◎ | ◎ | ◎ | ◎ | |
表9中，己二酸聚酯树脂使用UNIPLEX670-P。如表9所示，苯甲酸蔗糖酯的配比量在0.5～25质量％的范围可得到优良的效果。还有，特别优选3～15质量％。
表10
| 实施例 | ||||||
| 41 | 42 | 43 | 44 | 45 | ||
| 硝基纤维素1/4秒(30％IPA)(a) | 10 | 10 | 10 | 10 | 10 | |
| 己二酸聚酯树脂(b) | 10 | 10 | 10 | 10 | 10 | |
| JONCRYL611(c) | 0.5 | 3 | 6 | 15 | 25 | |
| 柠檬酸乙酰基三乙酯 | 5 | 5 | 5 | 5 | 5 | |
| 正丁醇 | 1 | 1 | 1 | 1 | 1 | |
| 乙酸乙酯 | 20 | 20 | 20 | 20 | 20 | |
| 乙酸正丁酯 | 残余 | 残余 | 残余 | 残余 | 残余 | |
| 有机改性粘土矿物 | 适量 | 适量 | 适量 | 适量 | 适量 | |
| 珠光剂 | 2 | 2 | 2 | 2 | 2 | |
| 颜料 | 1 | 1 | 1 | 1 | 1 | |
| 涂布容易程度 | ◎ | ◎ | ◎ | ◎ | ○ | |
| 涂膜强度 | ○ | ◎ | ◎ | ◎ | ◎ | |
| 光泽 | 10分钟后 | ○ | ◎ | ◎ | ◎ | ◎ |
| 4天后 | ○ | ○ | ○ | ○ | ○ | |
| 历时剥落性 | ◎ | ◎ | ◎ | ◎ | ◎ | |
表10中，己二酸聚酯树脂使用UNIPLEX670-P。如表10所示，JONCRYL611的配比量在0.5～25质量％的范围可得到优良的效果。还有，特别优选3～15质量％。
下面按常法得到实施例46～54的指甲油。任何一个美甲产品都具有优良的涂布容易程度、涂膜强度、光泽，历时难以剥落。此外，干燥性很好，对指甲的压迫感也小。
实施例46：指甲油
配合成分 配比量
硝基纤维素1/4秒(30％IPA) 15质量％
己二酸聚酯树脂 5
甲基丙烯酸甲酯·甲基丙烯酸丁
酯·丙烯酸2-乙基己酯·甲基丙烯酸共聚物 20
柠檬酸乙酰基三乙酯 5
正丁醇 1
乙酸乙酯 20
乙酸正丁酯 残余
颜料 1
有机改性粘土矿物 适量
己二酸聚酯树脂使用UNIPLEX670-P。此外，甲基丙烯酸甲酯·甲基丙烯酸丁酯·丙烯酸2-乙基己酯·甲基丙烯酸共聚物的分子量为质均分子量8000。
实施例47：指甲油
配合成分 配比量
硝基纤维素1/2秒(30％IPA) 15质量％
己二酸聚酯树脂 10
甲基丙烯酸甲酯·丙烯酸2-乙基
己酯·甲基丙烯酸共聚物 8
柠檬酸乙酰基三丁酯 5
正丁醇 1
乙酸乙酯 20
乙酸正丁酯 残余
颜料 1
有机改性粘土矿物 适量
己二酸聚酯树脂使用UNIPLEX670-P。此外，甲基丙烯酸甲酯·丙烯酸2-乙基己酯·甲基丙烯酸共聚物的分子量为质均分子量8100。
实施例48：指甲油
配合成分 配比量
硝基纤维素1/2秒(30％IPA) 10质量％
己二酸聚酯树脂 15
甲基丙烯酸辛酯·丙烯酸
甲酯·甲基丙烯酸共聚物 15
改性醇酸树脂 10
柠檬酸乙酰基三乙酯 5
正丁醇 1
乙酸乙酯 20
乙酸正丁酯 残余
颜料 1
有机改性粘土矿物 适量
己二酸聚酯树脂使用UNIPLEX670-P。此外，甲基丙烯酸辛酯·丙烯酸甲酯·甲基丙烯酸共聚物的分子量为质均分子量8100。
实施例49：指甲油
配合成分 配比量
硝基纤维素1/4秒(30％IPA) 10质量％
己二酸聚酯树脂 5
甲基丙烯酸甲酯·丙烯酸丁酯共聚物 8
苯甲酸蔗糖酯 3
甲苯磺酰胺树脂 4
柠檬酸乙酰基三丁酯 5
正丁醇 1
乙酸乙酯 20
乙酸正丁酯 残余
颜料 1
有机改性粘土矿物 适量
己二酸聚酯树脂使用UNIPLEX670-P。此外，甲基丙烯酸甲酯·丙烯酸丁酯共聚物的分子量为质均分子量5000。
实施例50：指甲油
配合成分 配比量
硝基纤维素1/2秒(30％IPA) 15质量％
己二酸聚酯树脂 10
苯甲酰蔗糖酯 9
柠檬酸乙酰基三丁酯 5
正丁醇 1
乙酸乙酯 20
乙酸正丁酯 残余
颜料 1
有机改性粘土矿物 适量
己二酸聚酯树脂使用UNIPLEX670-P。
实施例51：指甲油
配合成分 配比量
硝基纤维素1/4秒(30％IPA) 18质量％
己二酸聚酯树脂 15
苯甲酸蔗糖酯 15
柠檬酸乙酰基三丁酯 5
正丁醇 1
乙酸乙酯 20
乙酸正丁酯 残余
颜料 1
有机改性粘土矿物 适量
己二酸聚酯树脂使用UNIPLEX670-P。
实施例52：指甲油
配合成分 配比量
硝基纤维素1/2秒(30％IPA) 5质量％
硝基纤维素1/8秒(30％IPA) 12
己二酸聚酯树脂 12
苯甲酸蔗糖酯 2
柠檬酸乙酰基三丁酯 5
颜料 1
有机改性粘土矿物 适量
正丁醇 0.5
乙酸乙酯 8.5
乙酸正丁酯 残余
柠檬酸 适量
己二酸聚酯树脂使用UNIPLEX670-P。
实施例53：指甲油
配合成分 配比量
硝基纤维素1/2秒(30％IPA) 5质量％
硝基纤维素1/16秒(30％IPA) 13
己二酸聚酯树脂 12
苯甲酸蔗糖酯 2
柠檬酸乙酰基三丁酯 5
颜料 1
有机改性粘土矿物 适量
正丁醇 0.5
乙酸乙酯 8.5
乙酸正丁酯 残余
柠檬酸 适量
己二酸聚酯树脂使用UNIPLEX670-P。
实施例54：指甲油
配合成分 配比量
硝基纤维素1/4秒(30％IPA) 7质量％
硝基纤维素1/2秒(30％IPA) 5
己二酸聚酯树脂(*1) 8
甲基丙烯酸烷基酯·丙烯酸烷基酯共聚物(*2) 8
苯甲酸蔗糖酯(*3) 4
甲苯磺酰胺树脂 4
柠檬酸乙酰基三丁酯 5
正丁醇 1
乙酸乙酯 20
乙酸正丁酯 残余
颜料 1
有机改性粘土矿物 适量
(*1)UNIPLEX670-P
(*2)JONCRYL611
(*3)单百多(ノペツト)SB
实施例55：顶涂油
配合成分 配比量
硝基纤维素1/2秒(30％IPA) 12质量％
己二酸聚酯树脂 10
甲基丙烯酸甲酯·丙烯酸丁酯共聚物 10
苯甲酸蔗糖酯 5
甲苯磺酰胺树脂 4
柠檬酸乙酰基三乙酯 5
正丁醇 1
乙酸乙酯 25
乙酸正丁酯 残余
颜料 1
有机改性粘土矿物 适量
按常规方法得到顶涂油。指甲的涂布容易程度、涂膜强度、光泽优良，历时难于剥落，光泽不减。此外干燥性好，对指甲的压迫感小。还有，己二酸聚酯树脂使用UNIPLEX670-P。此外，甲基丙烯酸甲酯·丙烯酸丁酯共聚物的分子量为质均分子量8100。
实施例56：顶涂油
配合成分 配比量
硝基纤维素1/2秒(30％IPA) 12质量％
己二酸聚酯树脂(*1) 10
甲基丙烯酸烷基酯·丙烯酸烷基酯共聚物(*2) 15
甲苯磺酰胺树脂 4
柠檬酸乙酰基三乙酯 5
正丁醇 1
乙酸乙酯 25
乙酸正丁酯 残余
颜料 1
有机改性粘土矿物 适量
(*1)UNIPLEX670-P
(*2)JONCRYL611
按常规方法得到顶涂油。指甲的涂布容易程度、涂膜强度、光泽优良，历时难于剥落，光泽不减。此外干燥性好，对指甲的压迫感小。
实施例57：顶涂油
配合成分 配比量
硝基纤维素1/4秒(30％IPA) 7质量％
硝基纤维素1/2秒 5
己二酸聚酯树脂 10
甲基丙烯酸甲酯·丙烯酸丁酯共聚物 7
苯甲酸蔗糖酯 6
醇酸树脂(Versatic酸缩水甘油酯改性) 6
柠檬酸乙酰基三乙酯 5
正丁醇 1
乙酸乙酯 25
乙酸正丁酯 残余
颜料 1
有机改性粘土矿物 适量
按常规方法得到顶涂油。指甲的涂布容易程度、涂膜强度、光泽优良，历时难于剥落，光泽不减。此外干燥性好，对指甲的压迫感小。还有，己二酸聚酯树脂使用UNIPLEX670-P。此外，甲基丙烯酸甲酯·丙烯酸丁酯共聚物的分子量为质均分子量8000。
实施例58：顶涂油
配合成分 配比量
硝基纤维素1/4秒(30％IPA) 7质量％
硝基纤维素1/2秒(30％IPA) 5
己二酸聚酯树脂(*1) 10
苯甲酸蔗糖酯(*2) 13
醇酸树脂(Versatic酸缩水甘油酯改性) 6
柠檬酸乙酰基三乙酯 5
正丁醇 1
乙酸乙酯 25
乙酸正丁酯 残余
颜料 1
有机改性粘土矿物 适量
(*1)UNIPLEX670-P
(*2)单百多(モノペツト)SB
按常规方法得到顶涂油。指甲的涂布容易程度、涂膜强度、光泽优良，历时难于剥落，光泽不减。此外干燥性好，对指甲的压迫感小。
产业上的利用可能性
根据如上所述的本发明，得到指甲涂布容易、涂膜强度好、光泽优良，历时难于剥落，光泽不减的溶剂基美甲产品，可以作为化妆品使用。
Claims (1)
1.美甲产品，含有(a)硝基纤维素3.5～17.5质量％、(b)酸价为14～20mg KOH/g的偏苯三酸新戊二醇己二酸聚酯树脂5～15质量％、(c)含有甲基丙烯酸的碳数为1～8的烷基酯·丙烯酸的碳数为1～8的烷基酯的质均分子量为1000～9000的共聚物1～25质量％、和/或苯甲酸蔗糖酯0.5～25质量％，和(d)溶剂。