CN113394102A - NMOS device manufacturing method and NMOS device - Google Patents
NMOS device manufacturing method and NMOS device Download PDFInfo
- Publication number
- CN113394102A CN113394102A CN202110568331.5A CN202110568331A CN113394102A CN 113394102 A CN113394102 A CN 113394102A CN 202110568331 A CN202110568331 A CN 202110568331A CN 113394102 A CN113394102 A CN 113394102A
- Authority
- CN
- China
- Prior art keywords
- nmos device
- manufacturing
- nmos
- well region
- ion implantation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing an NMOS (N-channel metal oxide semiconductor) device, which comprises the step of performing P-type ion implantation to form a well region before performing thermal growth of an oxide layer on a silicon wafer. Compared with the prior art, the method effectively improves the electron mobility of the metal oxide semiconductor NMOS device, obtains higher saturation current, and realizes the improvement of the device speed under the same driving voltage. The method is compatible with the traditional process, only needs to change the sequence of the process flow without increasing or decreasing any process flow, is easy to realize and has low cost.
Description
Technical Field
The present invention relates to a method for manufacturing a semiconductor integrated circuit, and more particularly, to a method for manufacturing an NMOS device and an NMOS device.
Background
Since the advent of Metal Oxide Semiconductor Field Effect Transistor (MOSFET) devices, device sizes have been reduced following moore's law, and higher performance and lower cost have been achieved only by ever decreasing device sizes and increasing the integration density of integrated circuits. However, as the demand of integrated circuits is more and more diversified and the device size is smaller, the electron mobility in the device needs to be continuously improved, so as to reduce the power consumption and improve the current carrying capability of the device, and therefore how to improve the electron mobility of the device is a constant concern.
The electron mobility and the carrier concentration together determine the conductivity of the semiconductor material, and the larger the mobility is, the smaller the resistivity is, and the smaller the power consumption is and the larger the current carrying capacity is when the same current is passed. In addition, electron mobility can affect the operating frequency of the device, and the most significant limitation of the frequency response characteristic of a bipolar transistor is the time for minority carriers to transit the base region. The higher the mobility is, the shorter the required transit time is, and the cut-off frequency of the transistor is in direct proportion to the carrier mobility of the base region material, so that the carrier mobility is improved, the power consumption can be reduced, the current carrying capacity of the device is improved, and the switching conversion speed of the transistor is improved.
In the conventional CMOS process technology, theoretically, the electrical parameters of the device should be substantially the same on the premise that the well region ion implantation, the gate oxide thickness, the isolation sidewall, the shallow doped ion implantation, and the source/drain ion implantation are the same. However, experiments show that the threshold voltage of the NMOS device is too high and the saturation current (Idsat) is lower than the predicted target value, and as shown in the following graph, it can be clearly seen that Idsat of the NMOS device is lower than the target value. Therefore, it is an urgent problem to find a reason why the device driving current becomes low, that is, the electron mobility becomes low, and to improve the device performance.
Disclosure of Invention
The invention aims to solve the technical problem of how to improve the electron mobility of an NMOS device and achieve the purpose of increasing the saturation current.
The invention provides a method for manufacturing an NMOS (N-channel metal oxide semiconductor) device, which comprises the steps of carrying out P-type ion implantation to form a well region before carrying out thermal growth of an oxide layer on a silicon wafer. The thermal growth of the oxide layer changes the ion concentration of the well region.
Preferably, the P-type ions contain boron.
Preferably, the temperature of the thermal growth of the oxide layer is 800 ℃.
Preferably, the well region is plural.
The invention also provides an NMOS device manufactured by any one of the manufacturing methods.
Preferably, the channel length of the NMOS device is not less than 27 nanometers.
Compared with the prior art, the method effectively improves the electron mobility of the metal oxide semiconductor NMOS device, obtains higher saturation current, and realizes the improvement of the device speed under the same driving voltage. The method is compatible with the traditional process, only needs to change the sequence of the process flow without increasing or decreasing any process flow, is easy to realize and has low cost.
Drawings
FIG. 1 is a schematic diagram of a saturation current experiment in a prior art process.
FIG. 2 is a schematic diagram of a method of differentiating embodiments from the prior art.
Detailed Description
In the conventional CMOS process technology, theoretically, the electrical parameters of the device should be substantially the same on the premise that the well region ion implantation, the gate oxide thickness, the isolation sidewall, the shallow doped ion implantation, and the source/drain ion implantation are the same. However, experiments show that the threshold voltage of the NMOS device is too high and the saturation current (Idsat) is lower than the predicted target value, and as shown in fig. 1, it can be clearly seen that the saturation current Idsat of the NMOS device is lower than the target value. Therefore, it is an urgent problem to find a reason why the device driving current becomes low, that is, the electron mobility becomes low, and to improve the device performance.
The mobility (μ) and the speed (v) of the carriers are directly related to the external electric field (E) acting on it: v ═ μ · E, it follows that increasing the mobility of a carrier can increase its velocity, directly increasing the drive current of the device.
The conventional manufacturing method of the prior art CMOS process has the following flow:
step 1, ion implantation of a high voltage N well region (HVNW);
step 2, thermally growing an Oxide layer (Pad Oxide);
step 3, injecting P-type ions to form a well region;
step 4, forming a device oxide layer;
step 5, grid formation, shallow doped source and drain ion implantation and source and drain region ion implantation;
step 6, manufacturing metal silicide to form effective ohmic contact;
step 7, manufacturing a back-end metal interconnection process;
step 8, Wafer Acceptance Test (Wafer Acceptance Test WAT).
The present invention is described in the following with reference to the above-mentioned CMOS process, but it should be noted that the present invention is not limited to the above-mentioned CMOS process improvement. And in the following detailed description, numerous specific details are set forth in order to provide a more thorough understanding of the present invention. It will be apparent, however, to one skilled in the art that the practice of the invention may not necessarily be limited to these specific details. On the other hand, in order to avoid obscuring the present invention, the following examples will only describe the details of the manufacturing process flow which is different from the above.
Example 1:
in the manufacturing method of the NMOS device of this embodiment, the order of the step 2 and the step 3 is replaced. Because the process only needs to change the sequence of the process flow without increasing or decreasing any process flow, the overall electrical property of the device is not greatly influenced, and the improvement of the electron mobility enables the device to realize higher saturation current without influencing the overall performance of the device under the same working voltage.
In this embodiment, as shown in fig. 2, the left side is the steps 2 and 3 in the prior art, and the process steps in this embodiment are adjusted to the right side. The process flow sequence of thermal growth of the oxide layer (Pad oxide) and P-type ion implantation of the well region is adjusted, the P-type ion implantation of the well region is firstly carried out, and then the oxide layer (Pad oxide) is grown, wherein the P-type ions contain boron. The oxide layer (Pad oxide) grows in the thermal oxidation (800 ℃) process to absorb boron to change the ion concentration of the well region, so that the electron mobility of the device is improved, and the electron mobility of the narrow-width device is improved greatly.
The method is completed before shallow doping and source-drain ion implantation of the device, so that the saturation current of the device is improved on the premise of not causing great influence on the overall electrical property of the device.
The conventional process and the improved process flow obtain saturation current results, and saturation currents of different channel widths under the channel lengths of 0.0315um and 0.027um are measured respectively, and for a device with the channel length L of 0.0315um, the improved process saturation currents are respectively increased by 22.4%, 13.9%, 16% and 12.9% (for the channel width W of 0.09um,0.27um,0.54um and 2.7um) compared with those before the improvement. For the device with the channel length L being 0.027um, the process saturation current after improvement is respectively improved by 14.7%, 16.2%, 11.5% and 10.3% compared with that before improvement (for the channel width W being 0.09um,0.27um,0.54um and 2.7um), so that the saturation current is obviously improved no matter which channel length device is used, and the saturation current is improved more particularly for the narrow width device. Therefore, the electron mobility of the device can be improved by adjusting the sequence of the Pad oxide thermal growth and well region ion implantation process flow, so that the saturation current of the device is improved, and better device performance is realized.
Example 2:
this embodiment provides an NMOS device fabricated by the fabrication method of embodiment 1. The method is particularly suitable for the NMOS device with the channel length not less than 27 nanometers.
The present invention has been described in detail with reference to the specific embodiments and examples, but these are not intended to limit the present invention. Many variations and modifications may be made by one of ordinary skill in the art without departing from the principles of the present invention, which should also be considered as within the scope of the present invention.
Claims (7)
1. A manufacturing method of an NMOS device is characterized in that:
before the thermal growth of the oxide layer on the silicon chip, P-type ion implantation is carried out to form a well region.
2. The device manufacturing method of claim 1, wherein:
the P-type ions contain boron.
3. The device manufacturing method of claim 1, wherein:
the temperature of the thermal growth of the oxide layer is 800 ℃.
4. The device manufacturing method of claim 1, wherein:
the well region is a plurality of.
5. The device manufacturing method of claim 1, wherein:
the thermal growth of the oxide layer changes the ion concentration of the well region.
6. An NMOS device, characterized in that:
manufactured by the manufacturing method according to claims 1 to 4.
7. The NMOS device of claim 6, wherein:
the channel length of the NMOS device is not less than 27 nanometers.