CN112264278A - Surface treatment process of three-dimensional pattern aluminum veneer - Google Patents
Surface treatment process of three-dimensional pattern aluminum veneer Download PDFInfo
- Publication number
- CN112264278A CN112264278A CN202010995139.XA CN202010995139A CN112264278A CN 112264278 A CN112264278 A CN 112264278A CN 202010995139 A CN202010995139 A CN 202010995139A CN 112264278 A CN112264278 A CN 112264278A
- Authority
- CN
- China
- Prior art keywords
- aluminum veneer
- treatment process
- paint
- layer
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a surface treatment process of a three-dimensional pattern aluminum veneer, which adopts the steps of firstly rolling and then pressing, or firstly pressing and then spraying color. According to the invention, the surface of the aluminum veneer is treated by adopting a process of firstly rolling and then molding, or firstly molding and then spraying, so that the obvious surface effects of 3D wood grains, litchi surfaces and the like can be effectively created, and the attractiveness is improved; the provided process can be used for processing any conventional aluminum veneer, so that the production cost is obviously reduced; the adopted process is low in complexity, is suitable for direct popularization and use at the present stage, and contributes to rapidly improving enterprise income.
Description
Technical Field
The invention belongs to the field of plate treatment processes, and particularly relates to a surface treatment process of a three-dimensional pattern aluminum veneer.
Background
With the continuous development and improvement of the decoration industry and the design level, people have certain requirements on the aesthetic degree of the plate while pursuing the quality of the plate. Metal panel curtain walls have been used for decades in vertical form and have been used primarily with aluminum veneers. The aluminum veneer has excellent durability and corrosion resistance, but the surface of the aluminum veneer is flat and smooth, the color is single, and no effective and convenient treatment method exists at present in China.
Therefore, it is a problem to be solved by those skilled in the art to develop a process capable of performing surface stereo-design treatment on an aluminum veneer.
Disclosure of Invention
In order to solve the problems, the invention discloses a surface treatment process of a three-dimensional pattern aluminum veneer.
In order to achieve the purpose, the invention provides the following technical scheme:
a surface treatment process for a three-dimensional pattern aluminum veneer adopts the steps of firstly rolling and then pressing, or firstly pressing and then spraying color. Further, when the treatment process of firstly rolling and then pressing is adopted, the specific steps are as follows:
(1) taking an aluminum veneer, flattening the surface of the aluminum veneer, and cleaning;
(2) coating a layer of protective paint on the surface of the aluminum veneer;
(3) carrying out roller color together with the protective paint on the surface of the aluminum veneer, and coating a layer of brightening paint after the roller color is finished;
(4) together with the brightening varnish of the surface layer.
Further, when the treatment process of pressing and spraying color firstly, the specific steps are as follows:
(1) taking an aluminum veneer, flattening the surface of the aluminum veneer, and cleaning;
(2) after the surface of the aluminum veneer is molded, coating a layer of protective paint;
(3) spraying color on the surface of the protective paint;
(4) and coating a layer of brightening paint after the color spraying is finished.
Further, the protective paint is organic silicon protective paint; the brightening paint is wear-resistant brightening paint.
Further, the specific method of step (1) is as follows:
taking an aluminum veneer, and cleaning the surface of the aluminum veneer by using a neutral cleaning agent to remove attachments and pollutants on the surface; washing and removing the residual neutral detergent, and drying; polishing and flattening the surface of the aluminum veneer, washing again and drying; and finally, coating a layer of surface primer.
Further, the surface primer is a rubber alkyd primer.
Compared with the prior art, the invention has the following beneficial effects:
1. the surface of the aluminum veneer is treated by adopting a process of firstly rolling and then pressing or firstly pressing and then spraying, so that the obvious surface effects of 3D wood grains, litchi surfaces and the like can be effectively created, and the attractiveness is improved;
2. the provided process can be used for processing any conventional aluminum veneer, so that the production cost is obviously reduced;
3. the adopted process is low in complexity, is suitable for direct popularization and use at the present stage, and contributes to rapidly improving enterprise income.
Detailed Description
The technical solutions provided by the present invention will be described in detail below with reference to specific examples, and it should be understood that the following specific embodiments are only illustrative of the present invention and are not intended to limit the scope of the present invention.
Example 1:
the embodiment is a surface treatment process of a three-dimensional pattern aluminum veneer, and when the treatment process of firstly rolling color and then pressing is adopted, the specific steps are as follows:
(1) taking an aluminum veneer, and cleaning the surface of the aluminum veneer by using a neutral cleaning agent to remove attachments and pollutants on the surface; washing and removing the residual neutral detergent, and drying; polishing and flattening the surface of the aluminum veneer, washing again and drying; finally, coating a layer of surface primer;
(2) coating a layer of protective paint on the surface of the aluminum veneer;
(3) carrying out roller color together with the protective paint on the surface of the aluminum veneer, and coating a layer of brightening paint after the roller color is finished;
(4) together with the brightening varnish of the surface layer.
Wherein, the surface primer in the step (1) is rubber alkyd primer; the protective paint in the step (2) is organic silicon protective paint; the brightening paint in the step (3) is wear-resistant brightening paint.
Example 2:
the embodiment is a surface treatment process of a three-dimensional pattern aluminum veneer, and when the treatment process of pressing before spraying is adopted, the specific steps are as follows:
(1) taking an aluminum veneer, and cleaning the surface of the aluminum veneer by using a neutral cleaning agent to remove attachments and pollutants on the surface; washing and removing the residual neutral detergent, and drying; polishing and flattening the surface of the aluminum veneer, washing again and drying; finally, coating a layer of surface primer;
(2) after the surface of the aluminum veneer is molded, coating a layer of protective paint;
(3) spraying color on the surface of the protective paint;
(4) and coating a layer of brightening paint after the color spraying is finished.
Wherein, the surface primer in the step (1) is rubber alkyd primer; the protective paint in the step (2) is organic silicon protective paint; the brightening paint in the step (3) is wear-resistant brightening paint.
Through the treatment processes provided by the 2 embodiments, the 3D wood grain and litchi surface treatment is respectively and simultaneously carried out on the surface of the aluminum veneer, and obvious treatment effects are obtained, so that the two surface treatment processes provided by the invention for the three-dimensional pattern aluminum veneer are obvious and effective.
Finally, it should be noted that the above embodiments are only used for illustrating the technical solutions of the present invention and not for limiting the technical solutions, and those skilled in the art should understand that modifications or equivalent substitutions can be made on the technical solutions of the present invention without departing from the spirit and scope of the technical solutions, and all the modifications and equivalent substitutions should be covered by the claims of the present invention.
Claims (6)
1. A surface treatment process of a three-dimensional pattern aluminum veneer is characterized by comprising the following steps: firstly rolling and then pressing, or firstly pressing and then spraying.
2. The surface treatment process of the stereoscopic colored aluminum veneer according to claim 1, characterized in that: when the treatment process of firstly rolling color and then pressing is adopted, the method comprises the following specific steps:
(1) taking an aluminum veneer, flattening the surface of the aluminum veneer, and cleaning;
(2) coating a layer of protective paint on the surface of the aluminum veneer;
(3) carrying out roller color together with the protective paint on the surface of the aluminum veneer, and coating a layer of brightening paint after the roller color is finished;
(4) together with the brightening varnish of the surface layer.
3. The surface treatment process of the stereoscopic colored aluminum veneer according to claim 1, characterized in that: the treatment process of pressing before spraying color comprises the following specific steps:
(1) taking an aluminum veneer, flattening the surface of the aluminum veneer, and cleaning;
(2) after the surface of the aluminum veneer is molded, coating a layer of protective paint;
(3) spraying color on the surface of the protective paint;
(4) and coating a layer of brightening paint after the color spraying is finished.
4. The surface treatment process of the stereoscopic colored aluminum veneer according to claim 2 or 3, characterized in that: the protective paint is organic silicon protective paint; the brightening paint is wear-resistant brightening paint.
5. The surface treatment process of the stereoscopic colored aluminum veneer according to claim 2 or 3, characterized in that: the specific method of the step (1) is as follows:
taking an aluminum veneer, and cleaning the surface of the aluminum veneer by using a neutral cleaning agent to remove attachments and pollutants on the surface; washing and removing the residual neutral detergent, and drying; polishing and flattening the surface of the aluminum veneer, washing again and drying; and finally, coating a layer of surface primer.
6. The surface treatment process of the stereoscopic colored aluminum veneer according to claim 5, characterized in that: the surface primer is a rubber alkyd primer.