CN111019466A - 一种儿童家具用涂料及其制备方法 - Google Patents
一种儿童家具用涂料及其制备方法 Download PDFInfo
- Publication number
- CN111019466A CN111019466A CN201911399881.8A CN201911399881A CN111019466A CN 111019466 A CN111019466 A CN 111019466A CN 201911399881 A CN201911399881 A CN 201911399881A CN 111019466 A CN111019466 A CN 111019466A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- children
- initiator
- added
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明要求保护一种儿童家具用涂料及其制备方法，其采用软单体、硬单体、石蜡、丁苯胶乳、降解淀粉液，与部分去离子水先制得预乳化液，再加入引发剂搅拌，反应至得到带蓝色光泽的乳液，开始滴加剩余预乳化液和双醛改性纳米纤维素、交联剂和引发剂，引发剂滴完后保温过滤出料，得到儿童涂料用乳液，最后加入去离子水和助剂制得具有核壳结构的儿童用木器涂料，双醛改性纳米纤维素和丁苯胶乳的加入协同提高了木器涂料的附着力、耐磨性、耐污染性和防涂鸦性。
Description
技术领域
本发明涉及一种儿童家具用涂料及其制备方法，属于木材加工技术领域。
背景技术
随着人们生活水平的提高，专供儿童使用的家具制品越来越常见。儿童作为身体正在发育的人群，对于所接触的家具制品的品质要求也较成年人更为严苛。儿童家具大多采用松木等实木加工而成，家具涂料的性能很大程度上决定了儿童家具制品的性能。
环保性是其中最为重要的指标，要保证儿童家具制品的甲醛及VOCs、重金属排放达标。一般地，采用更为环保的水性木器涂料能较好地解决这个问题，但水性涂料与生俱来物理强度低、耐沾污能力弱，儿童群体的行为特殊性，放大了水性涂料的相关缺陷。儿童家具在使用过程中经常因儿童的涂鸦、泼洒食品汤剂、玩耍碰撞等行为而遭到破坏。同时由于儿童在生活中难免磕磕碰碰，相较成人更容易受伤，家具制品不宜过“硬”。这就要求儿童家具用水性涂料具有较好的耐沾污性、耐刮擦性、耐磨性和适当的硬度。一般的水性涂料并不能很好地满足儿童家具的使用要求。为此，开发一种具有优异物理强度的弹性树脂，用以配制相关木器涂料，能较好地解决上述问题。
发明内容
本发明提供一种儿童家具用水性木器涂料，能解决儿童家具耐污染性差、过“软”的问题，使制备的儿童家具涂料同时具备较好的耐污染性、耐刮擦性、耐磨性和适当的硬度，环保性达到国家相关标准。
所述木器漆乳液由以下组分制备：各组分以重量份数计
所述软单体选自丙烯酸丁酯、丙烯酸乙酯、丙烯酸异辛酯中的一种或几种；
所述硬单体选择苯乙烯、甲基丙烯酸甲酯、醋酸乙烯、丙烯酸甲酯、丙烯酸、丙烯酰胺中的一种或几种；
所述的交联单体选择丙烯酰胺或丙烯腈。
所述引发剂选自过硫酸铵或过硫酸钾；
所述降解淀粉胶液由原淀粉经淀粉酶降解，固含量10-15％；
所述双醛改性纳米纤维素采用自制的双醛改性纳米纤维素，用0.1mol/L的盐酸溶液调节2-4wt％为纳米纤维素溶液的pH到4，在转速1000r/min，温度为40-60℃条件下加入6mmol/L高碘酸钠反应6-7h反应后降温，得到双醛改性纳米纤维素。
所述丁苯胶乳为制备口香糖用，pH＝6-7。
所述的儿童涂料的制备方法：
1.预乳化：称取软单体、硬单体、石蜡、丁苯胶乳、降解淀粉液，与1/3-1/2去离子水混合后均质搅拌处理10-30min制得预乳化液；
2.乳液制备：在装有搅拌装置、冷凝装置、氮气保护装置及加料装置的反应釜中加入pH调节剂，剩余去离子水，搅拌均匀，将1/3预乳液、1/3用量的引发剂倒入反应釜中，升温至80℃，搅拌，反应至得到带蓝色光泽的乳液，开始滴加剩余预乳化液和双醛改性纳米纤维素、交联剂和引发剂，预乳化液控制在3h-4h滴完，引发剂控制在4h-5h左右滴完，温度保持在80-85℃，搅拌转速控制在100r/min，引发剂滴完后保温30min，过滤出料，调节pH到7-8，封存待用；
3、木器漆调制：将制备好的乳液与去离子水、润湿流平剂、消泡剂、增稠剂、成膜助剂、蜡乳液按一定比例混合，制得具有核壳结构的水性木器漆，其固含量为30％-40％。
所述的润湿流平剂为BYK-346，所述的消泡剂为BYK-019，所述的增稠剂为PE-625、所述的成膜助剂为TEXNALA-12，所述的蜡乳液为BYK-513。
进一步地，相对于乳液100重量份计，步骤3中去离子水加入10-20重量份、润湿流平剂加入0.1-0.5重量份、消泡剂加入0.2-0.5重量份、增稠剂加入0.5-1.5重量份、成膜助剂加入3-5重量份、蜡乳液加入5-10重量份。
本发明所取得的效果：
1)本发明在制备涂料树脂的时候加入双醛改性纳米纤维素，此改性纤维素带有醛基和醇羟基，能同时与体系中的单体及木材基材中的活性基团反应，从而提高涂料的附着力和涂料涂膜的硬度等物理性能。
2)本发明在制备涂料树脂的时候加入丁苯胶乳，该成分能赋予涂料较好的弹性、耐刮擦性、耐污性和防涂鸦性。
3)本发明由于双醛改性纳米纤维素和丁苯胶乳的加入，二者通过协同的作用，提高了涂料附着力高、硬度和耐污染、耐刮擦能力较好，优于现行的儿童家具国家标准：GB/T33394-2016儿童房装饰用水性木器涂料。
具体实施方式
实施1
1)预乳化：称取丙烯酸丁酯80g、苯乙烯60g、甲基丙烯酸甲酯40g、石蜡2g、丁苯胶乳10g、降解淀粉液15g(固含量12％)，与135g去离子水混合后均质搅拌处理20min制得预乳化液；
2)乳液制备：在装有搅拌装置、冷凝装置、氮气保护装置及加料装置的反应釜中加入pH调节剂，去离子水135g，搅拌均匀，将1/3预乳液、0.5g过硫酸铵倒入反应釜中，升温至80℃，搅拌，反应至得到带蓝色光泽的乳液，开始滴加剩余预乳化液和双醛改性纳米纤维素0.3g、丙烯酰胺3g和过硫酸铵1g，预乳化液控制在3h滴完，引发剂控制在4h左右滴完，温度保持在85℃，搅拌转速控制在100r/min，引发剂滴完后保温30min，过滤出料，调节pH到7-8，封存待用；
3)木器漆调制：将制备好的乳液与50g去离子水、0.1g润湿流平剂BYK-346、0.2g消泡剂BYK-019、0.5g增稠剂PE-625、3g成膜助剂TEXNALA-12、5g蜡乳液BYK-513混合，制得具有核壳结构的水性木器漆，固含量为35％。
实施2
1)预乳化：称取丙烯酸乙酯100g、醋酸乙烯60g、丙烯酸甲酯60g、石蜡3g、丁苯胶乳8g、降解淀粉液20g(固含量12％)，与135g去离子水混合后均质搅拌处理30min制得预乳化液；
2)乳液制备：在装有搅拌装置、冷凝装置、氮气保护装置及加料装置的反应釜中加入pH调节剂，去离子水135g，搅拌均匀，将1/2预乳液、0.5g过硫酸钾倒入反应釜中，升温至80℃，搅拌，反应至得到带蓝色光泽的乳液，开始滴加剩余预乳化液和双醛改性纳米纤维素1g、丙烯腈3g和过硫酸钾1g，预乳化液控制在3h滴完，引发剂控制在4h左右滴完，温度保持在85℃，搅拌转速控制在100r/min，引发剂滴完后保温30min，过滤出料，调节pH到7-8，封存待用；
3)木器漆调制：将制备好的乳液与80g去离子水、0.2g润湿流平剂BYK-346、0.4g消泡剂BYK-019、0.7g增稠剂PE-625、5g成膜助剂TEXNALA-12、8g蜡乳液BYK-513混合，制得具有核壳结构的水性木器漆，固含量为35％。
对比例1
对比例1采用与实施例1相同的方法，区别仅在于不添加双醛改性纳米纤维素。
对比例2
对比例2采用与实施例1相同的方法，区别仅在于不添加丁苯胶乳。
对比例3
对比例3采用与实施例1相同的方法，区别仅在于不添加双醛改性纳米纤维素和丁苯胶乳。
测试效果
根据儿童家具国家标准：GB/T 33394-2016儿童房装饰用水性木器涂料分别对实施例和对比例进行测试。
测试结果如表1
表1
根据表1，可以得出，通过添加双醛改性纳米纤维素和丁苯胶乳获得的儿童乳胶漆，具有更好的附着力、耐磨性、耐污染性和防涂鸦性。
最后应说明的是：以上实施例仅用以说明本发明而并非限制本发明所描述的技术方案；因此，尽管本说明书参照上述的各个实施例对本发明已进行了详细的说明，但是，本领域的普通技术人员应当理解，仍然可以对本发明进行修改或等同替换；而一切不脱离本发明的精神和范围的技术方案及其改进，其均应涵盖在本发明的权利要求范围中。
Claims (9)
1.一种儿童用木器漆乳液，其特征在于，由以下组分制备，各组分以重量份数计：
2.根据权利要求1所述的乳液，其特征在于，所述软单体选自丙烯酸丁酯、丙烯酸乙酯、丙烯酸异辛酯中的一种或几种；所述硬单体选择苯乙烯、甲基丙烯酸甲酯、醋酸乙烯、丙烯酸甲酯、丙烯酸、丙烯酰胺中的一种或几种。
3.根据权利要求1所述的乳液，其特征在于，所述的交联单体选择丙烯酰胺或丙烯腈。
4.根据权利要求1所述的乳液，其特征在于，所述引发剂选自过硫酸铵或过硫酸钾。
5.根据权利要求1所述的乳液，其特征在于，所述降解淀粉胶液由原淀粉经淀粉酶降解获得，固含量10-15％。
6.根据权利要求1所述的乳液，其特征在于，所述双醛改性纳米纤维素制备方法如下：用0.1mol/L的盐酸溶液调节纳米纤维素溶液的pH到4，在转速1000r/min，温度为40-60℃条件下加入6mmol/L高碘酸钠反应6-7h反应后降温，得到双醛改性纳米纤维素。
7.一种儿童涂料的制备方法，其特征在于，其制备方法如下：
1)预乳化液的制备：称取权利要求1所述的各组分，将软单体、硬单体、石蜡、丁苯胶乳、降解淀粉液，与1/3-1/2去离子水混合后均质搅拌处理10-30min制得预乳化液；
2)乳液制备：在装有搅拌装置、冷凝装置、氮气保护装置及加料装置的反应釜中加入pH调节剂，剩余去离子水，搅拌均匀，将1/3用量的预乳液、1/3用量的引发剂倒入反应釜中，升温至80℃，搅拌，反应至得到带蓝色光泽的乳液，开始滴加剩余预乳化液和双醛改性纳米纤维素、交联剂混合液和引发剂，预乳化液控制在3h-4h滴完，引发剂控制在4h-5h滴完，温度保持在80-85℃，搅拌转速控制在100r/min，引发剂滴完后保温30min，过滤出料，调节pH到7-8，封存待用；
3)木器漆调制：将制备好的乳液与去离子水、润湿流平剂、消泡剂、增稠剂、成膜助剂、蜡乳液按一定比例混合，制得具有核壳结构的水性木器漆，固含量为30％-40％。
8.根据权利要求7所述的儿童涂料，其特征在于，所述的润湿流平剂为BYK-346，所述的消泡剂为BYK-019，所述的增稠剂为PE-625、所述的成膜助剂为TEXNALA-12，所述的蜡乳液为BYK-513。
9.根据权利要求7所述的儿童涂料，其特征在于，相对于乳液100重量份计，步骤3中去离子水加入10-20重量份、润湿流平剂加入0.1-0.5重量份、消泡剂加入0.2-0.5重量份、增稠剂加入0.5-1.5重量份、成膜助剂加入3-5重量份、蜡乳液加入5-10重量份。