CN110396335A - A kind of environment-friendly water-based oil polish of high glaze and preparation method thereof - Google Patents
A kind of environment-friendly water-based oil polish of high glaze and preparation method thereof Download PDFInfo
- Publication number
- CN110396335A CN110396335A CN201910562349.7A CN201910562349A CN110396335A CN 110396335 A CN110396335 A CN 110396335A CN 201910562349 A CN201910562349 A CN 201910562349A CN 110396335 A CN110396335 A CN 110396335A
- Authority
- CN
- China
- Prior art keywords
- water
- environment
- high glaze
- based oil
- oil polish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of environment-friendly water-based oil polish of high glaze, including following component and its parts by weight percentage: water-based acrylic resin 30%-34%；Ethyl acrylate modified aqueous polyurethane 7%-10%；High-melting-point oxidized polyethylene wax emulsion 5%-7%；Deionized water 21%-24%；Ethylene glycol 10%-14%；Propylene glycol 8%-10%；Ethyl alcohol 2%-4%；Glycerol 1%-1.5%；Dioctyl phthalate 1%-1.5%；Water-soluble aldehyde ketone resin liquid 1.5%-2%；Optical brightener 0.5%-1%；Water lustering oil of the present invention can not only keep its feature of environmental protection but also glossiness can be improved；Separately the present invention also provides a kind of implementations to be easy, quick, and the water lustering oil preparation method of high glaze is made.
Description
Technical field
The present invention relates to environment-friendly water-based oil polish technical field, the environment-friendly water-based oil polish of especially a kind of high glaze and its system
Preparation Method.
Background technique
With the continuous improvement of economic progress and living standards of the people, quality requirement and printing industry to printed matter
Environmental requirement is continuously improved；Glazing is printing industry using one of maximum technique, is indispensable one in printing industry
Point, it is imperative to be developed and improved to it.Water lustering oil belongs to environmental type product, its solvent for use is mainly water
With some alcohols, volatile matter does not pollute the environment, and is constantly increased and gradually develops recently as the cry of people's environmental protection
Get up, its technology is not mature enough at present, and main problem shows that surface finish is ineffective, and glossiness cannot reach reason
Think effect etc..
Summary of the invention
Not only its feature of environmental protection can be kept the object of the present invention is to provide one kind but also the water lustering oil of glossiness can be improved.
Another object of the present invention also reside in provide it is a kind of implement to be easy, be quick, and the environment-friendly water-based glazing of high glaze is made
The preparation method of oil.
The object of the present invention is achieved like this:
A kind of environment-friendly water-based oil polish of high glaze, which is characterized in that including following component and its parts by weight percentage:
Water-based acrylic resin 30%-34%；
Ethyl acrylate modified aqueous polyurethane 7%-10%；
High-melting-point oxidized polyethylene wax emulsion 5%-7%；
Deionized water 21%-24%；
Ethylene glycol 10%-14%；
Propylene glycol 8%-10%；
Ethyl alcohol 2%-4%；
Glycerol 1%-1.5%；
Dioctyl phthalate 1%-1.5%；
Water-soluble aldehyde ketone resin liquid 1.5%-2%；
Optical brightener 0.5%-1%.
Water lustering oil includes above-mentioned host agent, solvent and auxiliary agent composition；
Wherein, water-based acrylic resin, with good guarantor's light colour retention, water-fast chemical resistance, fast drying, price is low, uses
Safety saves resource and the energy, reduces environmental pollution and is the most important ingredient of water lustering oil the advantages that public hazards；And propylene
Acetoacetic ester modified aqueous polyurethane, mixed the good Physical Mechanical of aqueous polyurethane, cold resistance, elasticity, thermal adaptability,
The feature of environmental protection and acrylic acid ester emulsion high mechanical strength, it is ageing-resistant, fast light do not turn yellow, water-tolerant the advantages that, the two is learnt from other's strong points to offset one's weaknesses；
High-melting-point oxidized polyethylene wax emulsion has outstanding anti scuffing, wear-resisting, gloss and waterproof performance, above-mentioned three kinds of component conducts
Host agent.
Deionized water, ethylene glycol, propylene glycol and ethyl alcohol are as solvent, and due to the slow drying speed of water, contemporary solvent is
Good gloss, it is most of with 80% ethylene glycol and propylene glycol substitution water, and ignore the excellent of water lustering oil Traditional Environmental-protection
Point；In order to keep the feature of environmental protection when optimizing gloss, we reduce the amount of ethylene glycol and propylene glycol, and ethyl alcohol is added in right amount
Improve the drying property of solvent.
Glycerol is that wetting agent has good wetting to pigment, increases water solubility；Dioctyl phthalate is plasticizer, energy
Make ink that there is soffening, ink itself is made to form the effect of more stable plasticizing film；Water-soluble aldehyde ketone resin liquid is to water down
Agent mainly plays desalination color；The brightness that form and aspect can be increased makes color more highlight gorgeous, optical brightener addition and optimizes and revises in right amount
Gloss.
It is another object of the present invention to what is be achieved:
A kind of preparation method of the environment-friendly water-based oil polish of high glaze, which comprises the following steps:
S1, water-based acrylic resin, ethyl acrylate modified aqueous polyurethane, the poly- second of high-melting-point oxidation are weighed according to deal proportion
Alkene wax emulsion sequentially adds above-mentioned component in reaction kettle, is sufficiently stirred at 70-90 DEG C, persistently stirs 40-80min;
S2, be warming up to 85-95 DEG C to S1, keep the temperature 25-35min, be cooled to 35-45 DEG C thereafter, according to deal proportion weigh from
Sub- water, ethylene glycol, propylene glycol, ethyl alcohol are put into reaction kettle, mix slowly 25-35min at 35-45 DEG C；
S3, glycerol, dioctyl phthalate, water-soluble aldehyde ketone resin liquid, optical brightener are put into reaction kettle, at 35-45 DEG C
Lower stirring 15-25min；
S4., stand after the completion, filtering and discharging, the environment-friendly water-based oil polish of this high glaze can be obtained.
Beneficial effects of the present invention are as follows:
(1) water lustering oil of the present invention can not only keep its feature of environmental protection but also glossiness can be improved.
(2) preparation method of water lustering oil of the present invention has implementation and is easy, is quick, and it is environment-friendly water-based that high glaze is made
The effect of oil polish.
Specific embodiment
The present invention is further described combined with specific embodiments below.
A kind of environment-friendly water-based oil polish of high glaze, including following component and its parts by weight percentage: water-based acrylic resin
30%-34%；Ethyl acrylate modified aqueous polyurethane 7%-10%；High-melting-point oxidized polyethylene wax emulsion 5%-7%；Deionized water
21%-24%；Ethylene glycol 10%-14%；Propylene glycol 8%-10%；Ethyl alcohol 2%-4%；Glycerol 1%-1.5%；Dioctyl phthalate 1%-
1.5%；Water-soluble aldehyde ketone resin liquid 1.5%-2%；Optical brightener 0.5%-1%.
A kind of preparation method of the environment-friendly water-based oil polish of high glaze, which comprises the following steps:
S1, water-based acrylic resin, ethyl acrylate modified aqueous polyurethane, the poly- second of high-melting-point oxidation are weighed according to deal proportion
Alkene wax emulsion sequentially adds above-mentioned component in reaction kettle, is sufficiently stirred at 70-90 DEG C, persistently stirs 40-80min;
S2, be warming up to 85-95 DEG C to S1, keep the temperature 25-35min, be cooled to 35-45 DEG C thereafter, according to deal proportion weigh from
Sub- water, ethylene glycol, propylene glycol, ethyl alcohol are put into reaction kettle, mix slowly 25-35min at 35-45 DEG C；
S3, glycerol, dioctyl phthalate, water-soluble aldehyde ketone resin liquid, optical brightener are put into reaction kettle, at 35-45 DEG C
Lower stirring 15-25min；
S4., stand after the completion, filtering and discharging, the environment-friendly water-based oil polish of this high glaze can be obtained.
Below with regard to above-mentioned preparation method, make following several embodiments:
Embodiment one: a kind of preparation method of the environment-friendly water-based oil polish of high glaze includes the following:
S1, water-based acrylic resin 31%, ethyl acrylate modified aqueous polyurethane 8%, high-melting-point oxygen are weighed according to deal proportion
Change polythene wax emulsion 7%, above-mentioned raw materials are sequentially added in reaction kettle, is sufficiently stirred at 80 DEG C, persistently stirs 60min；
S2, it is warming up to 90 DEG C to S1, keeps the temperature 30min, is cooled to 40 DEG C thereafter, weigh deionized water 23%, second according to deal proportion
13.5 glycol 9% of glycol, ethyl alcohol 3 are answered in kettle, 40 DEG C at a temperature of mix slowly 30min；
S3, glycerol 1.5%, dioctyl phthalate 1%, water-soluble aldehyde ketone resin liquid 2%, optical brightener 1% are put into reaction kettle,
20min is stirred at 40 DEG C；
S4., stand after the completion, filtering and discharging, the environment-friendly water-based oil polish of this high glaze can be obtained.
Example two: a kind of preparation method of the environment-friendly water-based oil polish of high glaze includes the following:
S1, water-based acrylic resin 32%, ethyl acrylate modified aqueous polyurethane 9%, high-melting-point oxygen are weighed according to deal proportion
Change polythene wax emulsion 6.5%, above-mentioned raw materials are sequentially added in reaction kettle, is sufficiently stirred at 80 DEG C, persistently stirs 60min；
S2,90 DEG C are warming up to S1,30min is kept the temperature, is cooled to 40 DEG C thereafter, according to deal proportion weigh deionized water 22.5%,
Ethylene glycol 14%, propylene glycol 8.5%, ethyl alcohol 2.5% are put into reaction kettle, 40 DEG C at a temperature of mix slowly 30min；
S3, glycerol 1%, dioctyl phthalate 1.5%, water-soluble aldehyde ketone resin liquid 1.7%, optical brightener 0.8% are put into reaction
In kettle, 40 DEG C at a temperature of stir 20min；
S4., stand after the completion, filtering and discharging, the environment-friendly water-based oil polish of this high glaze can be obtained.
Example three: a kind of preparation method of the environment-friendly water-based oil polish of high glaze includes the following:
S1, water-based acrylic resin 33%, ethyl acrylate modified aqueous polyurethane 8.5%, high-melting-point are weighed according to deal proportion
Oxidized polyethylene wax emulsion 5%, above-mentioned raw materials are sequentially added in reaction kettle, are sufficiently stirred at 80 DEG C, are persistently stirred 60min；
S2, it is warming up to 90 DEG C to S1, keeps the temperature 30min, is cooled to 40 DEG C thereafter, weigh deionized water 24%, second according to deal proportion
Glycol 13%, propylene glycol 8%, ethyl alcohol 4% are put into reaction kettle, 40 DEG C at a temperature of mix slowly 30min；
S3, glycerol 1.3%, dioctyl phthalate 1.1%, water-soluble aldehyde ketone resin liquid 1.6%, optical brightener 0.5% are put into instead
Answer in kettle, 40 DEG C at a temperature of stir 20min；
S4., stand after the completion, filtering and discharging, the environment-friendly water-based oil polish of this high glaze can be obtained.
Example four: a kind of preparation method of the environment-friendly water-based oil polish of high glaze includes the following:
S1, water-based acrylic resin 34%, ethyl acrylate modified aqueous polyurethane 10%, high-melting-point oxygen are weighed according to deal proportion
Change polythene wax emulsion 6%, above-mentioned raw materials sequentially added in reaction kettle, 80 DEG C at a temperature of be sufficiently stirred, it is lasting to stir
60min；
S2,90 DEG C are warming up to S1,30min is kept the temperature, is cooled to 40 DEG C thereafter, according to deal proportion weigh deionized water 21.5%,
Ethylene glycol 11.5%, propylene glycol 10%, ethyl alcohol 2% are put into reaction kettle, mix slowly 30min at 40 DEG C；
S3, glycerol 1.2%, dioctyl phthalate 1.4%, water-soluble aldehyde ketone resin liquid 1.8%, optical brightener 0.6% are put into instead
It answers in kettle, stirs 20min at a temperature of 40;
S4., stand after the completion, filtering and discharging, the environment-friendly water-based oil polish of this high glaze can be obtained.
Certainly, the above description is only a specific example of the present invention, be not to limit practical range of the invention, it is all according to
The equivalent change or modification that structure, feature and principle described in scope of the present invention patent is done should be included in Shen of the present invention
It please be in the scope of the patents.
Claims (2)
1. a kind of environment-friendly water-based oil polish of high glaze, which is characterized in that including following component and its parts by weight percentage:
Water-based acrylic resin 30%-34%；
Ethyl acrylate modified aqueous polyurethane 7%-10%；
High-melting-point oxidized polyethylene wax emulsion 5%-7%；
Deionized water 21%-24%；
Ethylene glycol 10%-14%；
Propylene glycol 8%-10%；
Ethyl alcohol 2%-4%；
Glycerol 1%-1.5%；
Dioctyl phthalate 1%-1.5%；
Water-soluble aldehyde ketone resin liquid 1.5%-2%；
Optical brightener 0.5%-1%.
2. a kind of preparation method of the environment-friendly water-based oil polish of high glaze as described in claim 1, which is characterized in that including following step
It is rapid:
S1, water-based acrylic resin, ethyl acrylate modified aqueous polyurethane, the poly- second of high-melting-point oxidation are weighed according to deal proportion
Alkene wax emulsion sequentially adds above-mentioned component in reaction kettle, is sufficiently stirred at 70-90 DEG C, persistently stirs 40-80min;
S2, be warming up to 85-95 DEG C to S1, keep the temperature 25-35min, be cooled to 35-45 DEG C thereafter, according to deal proportion weigh from
Sub- water, ethylene glycol, propylene glycol, ethyl alcohol are put into reaction kettle, mix slowly 25-35min at 35-45 DEG C；
S3, glycerol, dioctyl phthalate, water-soluble aldehyde ketone resin liquid, optical brightener are put into reaction kettle, at 35-45 DEG C
Lower stirring 15-25min；
S4., stand after the completion, filtering and discharging, the environment-friendly water-based oil polish of this high glaze can be obtained.