CN110003785A - A kind of security door aqueous metallic paint - Google Patents
A kind of security door aqueous metallic paint Download PDFInfo
- Publication number
- CN110003785A CN110003785A CN201910383386.1A CN201910383386A CN110003785A CN 110003785 A CN110003785 A CN 110003785A CN 201910383386 A CN201910383386 A CN 201910383386A CN 110003785 A CN110003785 A CN 110003785A
- Authority
- CN
- China
- Prior art keywords
- metallic paint
- security door
- aqueous metallic
- aqueous
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of security door aqueous metallic paint, each component including following mass percent: water-base resin 50-90%, flatting silica 0.1-10%, defoaming agent 0.1-6%, moistening flatting agent 0.1-6%, thickener 0.1-6%, coalescing agent 0.6-10%, deionized water 2-20%.Security door aqueous metallic paint of the invention is free of amino resins, and the organic solvents such as containing benezene, formaldehydeless release, and aqueous polyurethane used do not have extremely low volatile organic content, and obtained aqueous metallic paint has very high environmental benefit；In addition, its adhesive force is good, glossiness is high, good weatherability.
Description
Technical field
The present invention relates to metallic paint technical field, in particular to a kind of security door aqueous metallic paint.
Background technique
In recent years, for security door coating with the growth that quickly grows of real-estate market, existing security door coating has amino
Coating, because its form of construction work is easy, quick, and film performance is excellent, can satisfy the requirement of various occasions, thus
Security door field of coating occupies larger share.But amido coatings volatile organic matter is more, and there are problems that Form aldehyde release,
It is difficult to meet environmental requirements.There are also waterborne epoxy coatings for existing security door metallic paint, and poor, flexibility that there is also weatherabilities is not
The problems such as sufficient.
Summary of the invention
The present invention in order to solve problems in the prior art, provides a kind of environmental protection, high durable, high performance security door water
Property metallic paint.
Specific technical solution is as follows: a kind of security door aqueous metallic paint, each component including following mass percent: water
Property resin 50-90%, flatting silica 0.1-10%, defoaming agent 0.1-6%, moistening flatting agent 0.1-6%, thickener 0.1-6%, at
Film auxiliary agent 0.6-10%, deionized water 2-20%.
The following are attached technical schemes of the invention.
Preferably, the water-base resin is in waterborne polyurethane resin or acrylic resin modified by aqueous polyaminoester
Any one or two kinds of mixed with arbitrary proportion.
Preferably, the flatting silica is superfine silicon dioxide, talcum powder, aluminum stearate, one in calcium stearate
Kind or several mixed with arbitrary proportion.
Preferably, the defoaming agent is silicone emulsion, polypropylene glycerol aether, polyoxyethylene polyoxypropylene glycerol
One or more of ether is mixed with arbitrary proportion.
Preferably, the moistening flatting agent is any one of organic silicon, esters of acrylic acid or two kinds to appoint
The mixing of meaning ratio.
Preferably, the thickener is polyacrylic ester thickener, any in association type polyurethane thickener
It plants or two kinds is mixed with arbitrary proportion.
Preferably, the coalescing agent is alcohol ester-12, propylene glycol monomethyl ether, propandiol butyl ether, dipropylene glycol list first
Any one or more of ether, Dipropylene glycol mono-n-butyl Ether, dimethyl ether, propylene glycol phenylate, hexylene glycol monobutyl ether acetate
It is mixed with arbitrary proportion.
Technical effect of the invention: security door aqueous metallic paint of the invention is free of amino resins, and containing benezene etc. does not have
Solvent, formaldehydeless release, and aqueous polyurethane used have extremely low volatile organic content, obtained water-based metal
Paint has very high environmental benefit；In addition, its adhesive force is good, glossiness is high, good weatherability.
Specific embodiment
In the following, in conjunction with example, property feature and advantage is further described for the essence of the present invention, but the present invention not office
It is limited to listed embodiment.
A kind of security door aqueous metallic paint of the present embodiment includes each component of following mass percent: water-base resin
50-90%, flatting silica 0.1-10%, defoaming agent 0.1-6%, moistening flatting agent 0.1-6%, thickener 0.1-6%, coalescing agent
0.6-10%, deionized water 2-20%.Using said ratio security door with aqueous metallic paint mainly by special water-base resin,
The composition such as functional aid, deionized water, is mono-component aqueous baking vanish, has the advantages that the organic solvents such as 1, not containing benezene,
Belong to environmentally friendly machine；2, adhesive force is good, glossiness is high, good weatherability；3, using advanced waterborne polyurethane resin, properties of product
It is superior.
In the present embodiment, the water-base resin is in waterborne polyurethane resin or acrylic resin modified by aqueous polyaminoester
It is any one or two kinds of to be mixed with arbitrary proportion, so that aqueous metallic paint has extremely low volatile organic content, so that aqueous
The feature of environmental protection of metallic paint is more preferable.
In the present embodiment, the flatting silica is one of superfine silicon dioxide, talcum powder, aluminum stearate, calcium stearate
Or it several is mixed with arbitrary proportion.
In the present embodiment, the defoaming agent is silicone emulsion, polypropylene glycerol aether, polyoxyethylene polyoxypropylene glycerin ether
One or more of mixed with arbitrary proportion, to inhibit the foam of aqueous metallic paint.
In the present embodiment, the moistening flatting agent is any one of organic silicon, esters of acrylic acid or two kinds with any
Ratio mixing.
In the present embodiment, the thickener is any one of polyacrylic ester thickener, association type polyurethane thickener
Or two kinds mixed with arbitrary proportion.
In the present embodiment, the coalescing agent is alcohol ester-12, propylene glycol monomethyl ether, propandiol butyl ether, dipropylene glycol list first
Any one or more of ether, Dipropylene glycol mono-n-butyl Ether, dimethyl ether, propylene glycol phenylate, hexylene glycol monobutyl ether acetate
It is mixed with arbitrary proportion.
Embodiment 1
Security door aqueous metallic paint of the invention includes following component in parts by mass: 72 parts of waterborne polyurethane resin,
3.2 parts of flatting silica, 1.1 parts of defoaming agent, 4 parts of moistening flatting agent, 2.5 parts of thickener, 5 parts of coalescing agent, 12.2 parts of deionized water.
According to GB/T1728-1979, GB/T1732-1993, GB/T9286-1998, GB/T9754-2007, GB/T1733-
1993, GB/T1771-2007 etc. is tested for the property the security door of the present embodiment with aqueous metallic paint paint film, meets security door
With metallic paint standard requirements, as a result such as following table.
Embodiment 2
The security door aqueous metallic paint of the present embodiment includes following component: waterborne polyurethane resin 50 in parts by mass
Part, 6.7 parts of flatting silica, 2.3 parts of defoaming agent, 6 parts of moistening flatting agent, 5 parts of thickener, 10 parts of coalescing agent, 20 parts of deionized water.
According to GB/T1728-1979, GB/T1732-1993, GB/T9286-1998, GB/T9754-2007, GB/T1733-
1993, GB/T1771-2007 etc. is tested for the property the security door of the present embodiment with aqueous metallic paint paint film, meets security door
With metallic paint standard requirements, as a result such as following table.
The security door aqueous metallic paint of the present embodiment is free of amino resins, formaldehydeless release, and aqueous polyurethane used
With extremely low volatile organic content, obtained aqueous metallic paint has very high environmental benefit.
It is pointed out that the technical concepts and features of above-mentioned preferred embodiment only to illustrate the invention, its object is to
Those skilled in the art can understand the contents of the present invention and implements accordingly, and protection of the invention can not be limited with this
Range.Any equivalent change or modification in accordance with the spirit of the invention should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of security door aqueous metallic paint, which is characterized in that each component including following mass percent: water-base resin
50-90%, flatting silica 0.1-10%, defoaming agent 0.1-6%, moistening flatting agent 0.1-6%, thickener 0.1-6%, coalescing agent
0.6-10%, deionized water 2-20%.
2. security door aqueous metallic paint according to claim 1, which is characterized in that the water-base resin is aqueous poly- ammonia
Any one of ester resin or acrylic resin modified by aqueous polyaminoester or two kinds are mixed with arbitrary proportion.
3. security door aqueous metallic paint according to claim 1, which is characterized in that the flatting silica is ultra-fine titanium dioxide
One or more of silicon, talcum powder, aluminum stearate, calcium stearate are mixed with arbitrary proportion.
4. security door aqueous metallic paint according to claim 1, which is characterized in that the defoaming agent be silicone emulsion,
One or more of polypropylene glycerol aether, polyoxyethylene polyoxypropylene glycerin ether are mixed with arbitrary proportion.
5. security door aqueous metallic paint according to claim 1, which is characterized in that the moistening flatting agent is organosilicon
Any one of class, esters of acrylic acid or two kinds are mixed with arbitrary proportion.
6. security door aqueous metallic paint according to claim 1, which is characterized in that the thickener is polyacrylate
Any one of thickener, association type polyurethane thickener or two kinds are mixed with arbitrary proportion.
7. security door aqueous metallic paint according to claim 1, which is characterized in that the coalescing agent be alcohol ester-12,
Propylene glycol monomethyl ether, propandiol butyl ether, dipropylene glycol monomethyl ether, Dipropylene glycol mono-n-butyl Ether, dimethyl ether, propylene glycol phenyl
Any one or more of ether, hexylene glycol monobutyl ether acetate are mixed with arbitrary proportion.