CN116035927A - 一种仿花蕊结构的天然粉体的制备方法和一种持妆控油散粉 - Google Patents
一种仿花蕊结构的天然粉体的制备方法和一种持妆控油散粉 Download PDFInfo
- Publication number
- CN116035927A CN116035927A CN202211731494.1A CN202211731494A CN116035927A CN 116035927 A CN116035927 A CN 116035927A CN 202211731494 A CN202211731494 A CN 202211731494A CN 116035927 A CN116035927 A CN 116035927A
- Authority
- CN
- China
- Prior art keywords
- powder
- weight
- parts
- natural
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种仿花蕊结构的天然粉体的制备方法，包括以下步骤：将酒精和肉豆蔻酸镁混合再加入软玉粉、羟基磷灰石、氧化锌，得到混合粉末；在所述混合粉末中加入酒精至奶昔状，再研磨，干燥后粉碎得到天然粉体。本申请还提供了一种持妆控油散粉。本发明提供了一种仿花蕊结构的天然粉体，其通过制备过程中分散剂酒精的引入，使得天然羟基磷灰石交错成类网结构包裹在软玉粉上，并使氧化锌粉体均匀分布在类网结构上，使得形成的粉体很难重叠，交叉分布，呈花蕊形状，由此拥有更大的接触面积，充分发挥羟基磷灰石选择性吸附油脂的特性，拥有了更强的油脂吸附能力和持妆效果。
Description
技术领域
本发明涉及化妆品技术领域，尤其涉及一种仿花蕊结构的天然粉体的制备方法和一种持妆控油散粉。
背景技术
随着人民生活提高，大家开始了对美的追求，于是化妆对于大多数爱美的女性是必不可少的功课，然而想要保持一整天美美的妆容，需要选用控油力强的产品，尤其在夏天，人的皮肤油脂分泌比较强烈，容易脱妆，皮肤暗沉。现在市场上出现化妆品类中，大多添加硅石、PMMA、尼龙-12等吸油强的球形粉体实现控油，可是球形粉体吸油后透明，导致妆效暗沉，还具有一定流动性，就会有脱妆现象，没有解决根本问题。部分球形粉体还是塑料微粒，研究发现，这些塑料微粒进入海洋后，在海水中会吸收并依附海水中的持久性有机污染物(POPs)，这些携带有害物质的塑料微粒，被海洋生物食入后，有机会通过食物链再进入人类体内，从而对自然环境和人体健康均造成严重危害，因此天然的持妆控油组分在化妆品里非常有研究的必要。
中国的玉石养生历史悠久，据《神农本草》、《本草纲目》中记载：玉石可“除中热，解烦懑，助声喉，滋毛发，养五脏，安魂魄，疏血脉，明耳目”；而据现代科学测定，玉材本身含有多种微量元素，如锌、铁、铜、锰、镁、钴、硒、铬、钛、锂、钙、钾、钠等，这些元素能通过皮肤被人体吸收，如镁元素具有维持组织功能和结构完整性的作用，锰元素可以对抗自由基对人体造成的损伤，参与蛋白质、维生素的合成，促进血液循环，加速新城代谢、抗衰老等。软玉粉取自中国四大玉种的岫玉，经过锆石研磨技术，不断打磨，得到天然的矿物粉体-软玉粉，它在电子显微结构中呈现薄透的片状结构，非常有利于在皮肤表面的铺展，贴附性很好。
氧化锌在化妆品里主要作用是物理防晒剂，收敛剂，并具有一定的遮盖力。微粒氧化锌作为收敛剂，对皮肤有弱收敛、干燥和保护的作用，常用作有渗出的急性或亚急性湿疹、皮炎、汗疹、痱子和小面积的皮肤溃疡的治疗。而纳米氧化锌是化妆品中一种重要且广泛使用的物理防晒剂，它屏蔽紫外线的原理是吸收和散射紫外线。相关实验数据表明，纳米氧化锌在355～380nm的波长内，纳米氧化锌的屏蔽紫外线能了高于常用的纳米二氧化钛。正是由于这一特性，纳米氧化锌在化妆品中逐渐得以应用。
羟基磷灰石(HAP)，又称羟磷灰石或碱式磷酸钙，是钙磷灰石(Ca5(PO4)3(OH))的自然矿物化，但是经常被写成(Ca10(PO4)6(OH)2)的形式以突出它由羟基与磷灰石两部分组成的。它是人体骨牙的主要成分，人体骨骼的65％、牙本质的70％、牙釉质的95％都是羟基磷灰石，总含量达到人体的20％。羟基磷灰石也是易于消化的磷酸钙的丰富来源，并被用作饮食补充剂和食品添加剂。肉豆蔻酸镁是一种白色粉末，熔点131.6℃；由肉豆蔻酸钠与硫酸镁溶液皂化反应制得，天然指数为1。
直接将软玉粉、羟基磷灰石和氧化锌进行物理高速混合后，粉体容易重叠，不能增大其接触面积来最大发挥羟基磷灰石对不饱和脂肪酸的选择性吸收能力，且吸油后不能固化凝固。因此，市面上化妆品级的复合粉体大多粉体间重叠情况明显，无法增加其接触面以达到更好的控油效果，且大多不是天然组分。
发明内容
本发明解决的技术问题在于提供一种仿花蕊结构的天然粉体的制备方法，本申请提供的天然粉体具有较高的安全性，且具有较好的控油效果。
有鉴于此，本申请提供了一种仿花蕊结构的天然粉体的制备方法，包括以下步骤：
将酒精和肉豆蔻酸镁混合再加入软玉粉、羟基磷灰石、氧化锌，得到混合粉末；
在所述混合粉末中加入酒精至奶昔状，再研磨，干燥后粉碎得到天然粉体。
优选的，所述肉豆蔻酸镁、软玉粉、羟基磷灰石和氧化锌的质量比为(1～10)：(60～90)：(10～30)：(1～20)。
优选的，所述研磨的研磨球为锆珠，时间为5～10h。
优选的，所述干燥的温度为50～120℃，时间为1～5h。
优选的，在得到混合粉末的步骤中，所述酒精和所述肉豆蔻酸镁的质量比为(9～12)：(1～10)。
本申请还提供了一种持妆控油散粉，包括：
所述天然粉体为上述方案所述的制备方法所制备的天然粉体。
优选的，所述活性物质选自丁二醇、丹参根提取物、丁香花蕾提取物、黄芩根提取物、当归根提取物、甘草根提取物和积雪草提取物中的一种或多种。
优选的，所述天然粉体的含量为3～8重量份。
优选的，所述乙烯基聚二甲基硅氧烷/聚甲基硅氧烷硅倍半氧烷交联聚合物的含量为12～18重量份，所述合成氟金云母的含量为15～20重量份，所述甲基烷基化硅石0.2～0.8重量份，所述月桂酰赖氨酸的含量为2～4重量份。
优选的，所述一氮化硼的含量为2～4重量份，所述苯氧乙醇/乙基己基甘油的含量为0.5～1.5重量份，所述鲸蜡基聚二甲基硅氧烷的含量为2～4重量份，所述活性物质的含量为0.1～0.8重量份。
本申请提供了一种仿花蕊结构的天然粉体的制备方法，其首先将酒精和肉豆蔻酸镁混合再加入软玉粉、羟基磷灰石、氧化锌，得到混合粉末；再在所述混合粉末中加入酒精至奶昔状，再研磨，干燥后粉碎得到天然粉体。在天然粉体制备过程中，本申请引入了酒精作为溶剂，可以实现原料的良好分散，使得天然羟基磷灰石交错成类网结构包裹在天然的片状软玉粉上，并使天然氧化锌粉体均匀地分布在类网结构上，如此得到的粉体很难重叠，它们交叉分布，呈“花蕊”形状；使得到的粉体具有对不饱和脂肪酸超强选择性吸附能力，且不会吸附化妆品配方中的其他油脂类物质；且可快速凝固固化皮脂中的不饱和脂肪酸；吸油后颜色不会暗沉等特点，从而使妆容更持久。本发明的制备方法采用天然矿物氧化锌与生物相容性好的生物基羟基磷灰石、天然无毒的软玉粉等搭配使用，满足了化妆品体系需要，产品安全性能更佳。
附图说明
图1为本发明制备的仿花蕊结构的天然粉体的SEM照片；
图2为本发明不同组分制备的粉体吸油后的照片。
具体实施方式
为了进一步理解本发明，下面结合实施例对本发明优选实施方案进行描述，但是应当理解，这些描述只是为进一步说明本发明的特征和优点，而不是对本发明权利要求的限制。
鉴于现有技术中化妆品级的复合粉体粉体间重叠而控油效果有限的问题，本发明提供了一种仿花蕊结构的天然粉体，其通过制备过程中分散剂酒精的引入，使得天然羟基磷灰石交错成类网结构包裹在软玉粉上，并使氧化锌粉体均匀分布在类网结构上，使得形成的粉体很难重叠，交叉分布，呈花蕊形状，由此拥有更大的接触面积，充分发挥羟基磷灰石选择性吸附油脂的特性，拥有了更强的油脂吸附能力和持妆效果。具体的，本发明实施例首先公开了一种仿花蕊结构的天然粉体的制备方法，包括以下步骤：
将酒精和肉豆蔻酸镁混合再加入软玉粉、羟基磷灰石、氧化锌，得到混合粉末；
在所述混合粉末中加入酒精至奶昔状，再研磨，干燥后粉碎得到天然粉体。
在天然粉体制备过程中，所述肉豆蔻酸镁、软玉粉、羟基磷灰石和氧化锌的质量比为(1～10)：(60～90)：(10～30)：(1～20)；具体的，所述肉豆蔻酸镁、软玉粉、羟基磷灰石和氧化锌的质量比为(2～8)：(70～85)：(10～20)：(5～10)。
在天然粉体制备过程中，本申请首先将酒精和肉豆蔻酸镁混合，以使肉豆蔻酸镁分散于酒精中；所述酒精和所述肉豆蔻酸镁的质量比为(9～12)：(1～10)，具体的，所述酒精和所述肉豆蔻酸镁的质量比为(10～11)：(3～8)；所述酒精的浓度为75～100％。
本申请然后加入软玉粉、羟基磷灰石、氧化锌，得到混合粉末；再在所述混合粉末中加入酒精至呈奶昔状，以保证得到的天然粉体能够具有花蕊形状；所述酒精的浓度为75～100％。
按照本发明，将上述得到的奶昔状混合物研磨、干燥，即得到天然粉体。所述研磨采用锆珠作为研磨球，所述干燥以将其中的酒精挥发；所述研磨的时间为5～10h，更具体的，所述研磨的时间为6～8h；所述干燥的温度为50～120℃，时间为1～5h，更具体的，所述干燥的温度为60～110℃，时间为2～4h。
本申请还提供了一种持妆控油散粉，包括：
所述天然粉体为上述方案所述的制备方法所制备的天然粉体。
在所述散粉中，所述乙烯基聚二甲基硅氧烷/聚甲基硅氧烷硅倍半氧烷交联聚合物作为增稠剂，其还可以进一步增加保湿效果，其含量为10～20重量份，具体的，所述乙烯基聚二甲基硅氧烷/聚甲基硅氧烷硅倍半氧烷交联聚合物的含量为12～18重量份。
所述硅石具有润滑效果，其含量为20～60重量份。
所述月桂酰赖氨酸作为保湿剂、柔润剂，其可调理皮肤；所述月桂酰赖氨酸的含量为1～5重量份，具体的，所述月桂酰赖氨酸的含量为2～4重量份。
所述合成氟金云母具有较好的光泽，可增加皮肤质感和触感，其含量为10～25重量份，具体的，所述合成氟金云母的含量为15～20重量份。
所述一氮化硼具有遮瑕功效，且可增加皮肤的顺滑性，其含量为1～5重量份，具体的，所述一氮化硼的含量为2～4重量份。
所述甲基烷基化硅石作为柔润剂和吸附剂，其含量为0.01～1重量份，具体的，所述甲基烷基化硅石的含量为0.2～0.8重量份。
所述苯氧乙醇/乙基己基甘油作为柔润剂、保湿剂和防腐剂，可更近以提高其效果，其含量为0.1～2重量份，具体的，所述苯氧乙醇/乙基己基甘油的含量为0.5～1.5重量份。
所述鲸蜡基聚二甲基硅氧烷作为柔润剂，其含量为1～5重量份，具体的，所述鲸蜡基聚二甲基硅氧烷的含量为2～4重量份。
天然粉体的含量为1～10重量份，具体的，所述天然粉体的含量为2～8重量份。
所述活性物质具体选自丁二醇、丹参根提取物、丁香花蕾提取物、黄芩根提取物、当归根提取物、甘草根提取物和积雪草提取物中的一种或多种；其含量为0.01～1重量份，具体的，所述活性物质的含量为0.1～0.8重量份。
本申请提供的散粉由于天然粉体的加入，提高了其持久控油性。
本发明提供的天然粉体由于分散剂以及加入量的控制，使得天然羟基磷灰石交错呈类网结构包裹在天然的片状软玉粉上，并使天然氧化锌粉体均匀地分布在类网结构上，使得到的粉体很难重叠，它们交叉分布，呈“花蕊”形状；呈“花蕊”形状能增大接触面积，更加控油；进一步的，采用天然矿物的软玉粉、生物基羟基磷灰石、矿物氧化锌、肉豆蔻酸镁原料进行创新组合，不仅有利于对环境的保护，也有利于对肌肤吸油后不暗沉，从而使得妆容更加持久。
为了进一步理解本发明，下面结合实施例对本发明提供的仿花蕊结构的天然粉体的制备方法和持妆控油散粉进行详细说明，本发明的保护范围不受以下实施例的限制。
实施例1
1)用10g浓度为75％的酒精分散肉豆蔻酸镁；
2)将步骤1)得到的混合物中混合加入软玉粉、羟基磷灰石和氧化锌，搅拌均匀；
3)在步骤2)得到的混合粉末中加入一定量浓度为75％的酒精直至奶昔状；
4)在加入一定量锆珠，研磨8h；
5)将步骤4)研磨后的粉末于65℃干燥2h；
6)将步骤5)得到的粉体粉碎，得到天然粉体混合物；
图1为天然粉体混合物的SEM照片，从图片可以看出，粉体间交错分布，呈“花蕊”形状，大大增加了粉体与油脂的接触面。
按照上述制备方法制备不同的粉体，区别在于：原料或原料的混合比例发生变化，分别标记为组分1～组分11，粉体的成分具体为：
组分1：软玉粉：羟基磷灰石：氧化锌：肉豆蔻酸镁＝70：15：10：5；
组分2：软玉粉：羟基磷灰石：氧化锌：肉豆蔻酸镁＝70：20：5：5；
组分3：软玉粉：羟基磷灰石:氧化锌：肉豆蔻酸镁＝75：15：5：5；
组分4：软玉粉：羟基磷灰石:氧化锌：肉豆蔻酸镁＝78：10：10：2；
组分5：软玉粉；
组分6：天然云母；
组分7：合成氟金云母；
组分8：氧化锌；
组分9：球形硅石；
组分10：羟基磷灰石；
组分11：肉豆蔻酸镁；
检测上述制备的粉体的凝固时间、控油力和持妆时间，检测方法和检测结果具体为如下；
A)凝固时间测试：
1)透明玻璃小瓶中称量6g去离子水和12g油酸，模拟人体汗液；
2)称量2g上述组分，蜜密封，上下摇动60s，静置后，观察油脂凝固时间，凝固时间越小，说明吸油能力越强。具体结果如表1所示。
B)控油力测试:
将人工皮酯(油酸:角鲨烷:橄榄油＝1:2:2)滴入4g的组方中，并搅拌使其成团，待其无法在吸取皮酯后停止滴入，并测试其总吸取的皮酯量，计算吸油值，吸油值越大，控油力越强，具体结果如表1所示。吸收油后，越透越亮，则越有暗沉的缺陷，如图2所示；
表1不同组分制备的粉体的凝固时间数据表
表1不同组分制备的粉体的凝固时间数据表(续表)
C)持妆力测试：
散粉配方内容
乙烯基聚二甲基硅氧烷/聚甲基硅氧烷硅倍半氧烷交联聚合物10～20份、硅石20～56份、月桂酰赖氨酸1～4份、合成氟金云母10～23份、实例样品1～10份、一氮化硼1～5份、甲基烷基化硅石0.01～1份、苯氧乙醇/乙基己基甘油0.1～2份、鲸蜡基聚二甲基硅氧烷1～5份、活性物0.01～1份；持妆控油散粉的制备方法，其包括如下步骤：
(1)按选定重量份称取所述片状填充粉料(月桂酰赖氨酸、合成氟金云母、一氮化硼、天然粉体)，球状填充粉料(乙烯基聚二甲基硅氧烷/聚甲基硅氧烷硅倍半氧烷交联聚合物、硅石、甲基烷基化硅石)，均匀混合，加入到打粉锅内进行高速搅拌一段时间，作为A相；
(2)往A相里面继续加入油脂(鲸蜡基聚二甲基硅氧烷)，防腐剂(苯氧乙醇/乙基己基甘油)，活性物质(丁二醇、丹参根提取物、丁香花蕾提取物、黄芩根提取物、当归根提取物、甘草根提取物和积雪草提取物)，进行再次充分高速搅拌混合，混合均匀后即可出料。
按照上述方法制备散粉，原料具体配方如表2所示；
表2不同散粉的成分数据表
检测上述实施例制备的散粉的持妆力，测试方法：选取60例女性，平均年龄25±10岁，随机分成6组，每组10人，首先分别在左脸和右脸涂抹等同分量的本发明的实施例样品和对比例样品，测试者依据涂抹过程及涂抹后的效果进行评价测试比较；
测试评分标准如下：
贴肤程度：1分：不贴肤，严重卡粉；2分：不贴肤，卡粉较明显；3分：贴肤一般，卡粉一般；4分：贴肤较好，基本不卡粉；5分：非常贴肤，不卡粉；
隐匿毛孔度：1分：差；2分：较差；3分：一般；4分：较好；5分：好；
持久度：1分：差；2分：较差；3分：一般；4分：较好；5分：好；
控油程度：1分：差；2分：较差；3分：一般；4分：较好；5分：好；
粉质细腻度：1分：粗糙；2分：较粗糙；3分：细腻度一般；4分：细腻度较好；5分：非常细腻；
妆效喜爱度：1分：差；2分：较差；3分：一般；4分：较好；5分：好；
测试者按照以上评分标准进行评分，最后统计全部评分计算平均值，具体评分结果如表3所示：
表3不同实施例持妆力性能数据表
以上实施例的说明只是用于帮助理解本发明的方法及其核心思想。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以对本发明进行若干改进和修饰，这些改进和修饰也落入本发明权利要求的保护范围内。
对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (10)
1.一种仿花蕊结构的天然粉体的制备方法，包括以下步骤：
将酒精和肉豆蔻酸镁混合再加入软玉粉、羟基磷灰石、氧化锌，得到混合粉末；
在所述混合粉末中加入酒精至奶昔状，再研磨，干燥后粉碎得到天然粉体。
2.根据权利要求1所述的制备方法，其特征在于，所述肉豆蔻酸镁、软玉粉、羟基磷灰石和氧化锌的质量比为(1～10)：(60～90)：(10～30)：(1～20)。
3.根据权利要求1所述的制备方法，其特征在于，所述研磨的研磨球为锆珠，时间为5～10h。
4.根据权利要求1所述的制备方法，其特征在于，所述干燥的温度为50～120℃，时间为1～5h。
5.根据权利要求1所述的制备方法，其特征在于，在得到混合粉末的步骤中，所述酒精和所述肉豆蔻酸镁的质量比为(9～12)：(1～10)。
6.一种持妆控油散粉，包括：
乙烯基聚二甲基硅氧烷/聚甲基硅氧烷硅倍半氧烷交联聚合物10～20重量份；
所述天然粉体为权利要求1～5任一项所述的制备方法所制备的天然粉体。
7.根据权利要求6所述的持妆控油散粉，其特征在于，所述活性物质选自丁二醇、丹参根提取物、丁香花蕾提取物、黄芩根提取物、当归根提取物、甘草根提取物和积雪草提取物中的一种或多种。
8.根据权利要求6所述的持妆控油散粉，其特征在于，所述天然粉体的含量为3～8重量份。
9.根据权利要求6所述的持妆控油散粉，其特征在于，所述乙烯基聚二甲基硅氧烷/聚甲基硅氧烷硅倍半氧烷交联聚合物的含量为12～18重量份，所述合成氟金云母的含量为15～20重量份，所述甲基烷基化硅石0.2～0.8重量份，所述月桂酰赖氨酸的含量为2～4重量份。
10.根据权利要求6或9所述的持妆控油散粉，其特征在于，所述一氮化硼的含量为2～4重量份，所述苯氧乙醇/乙基己基甘油的含量为0.5～1.5重量份，所述鲸蜡基聚二甲基硅氧烷的含量为2～4重量份，所述活性物质的含量为0.1～0.8重量份。