CN115991920A - High-elasticity high-buffering sole material and preparation method thereof - Google Patents

High-elasticity high-buffering sole material and preparation method thereof Download PDF

Info

Publication number
CN115991920A
CN115991920A CN202111218917.5A CN202111218917A CN115991920A CN 115991920 A CN115991920 A CN 115991920A CN 202111218917 A CN202111218917 A CN 202111218917A CN 115991920 A CN115991920 A CN 115991920A
Authority
CN
China
Prior art keywords
elasticity
sole material
slip
shock
buffering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202111218917.5A
Other languages
Chinese (zh)
Inventor
郑普清
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingyuan Qingxin Huifeng New Material Technology Co ltd
Original Assignee
Qingyuan Qingxin Huifeng New Material Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingyuan Qingxin Huifeng New Material Technology Co ltd filed Critical Qingyuan Qingxin Huifeng New Material Technology Co ltd
Priority to CN202111218917.5A priority Critical patent/CN115991920A/en
Publication of CN115991920A publication Critical patent/CN115991920A/en
Pending legal-status Critical Current

Abstract

The invention relates to a high-elasticity high-buffering sole material and a preparation method thereof, wherein the high-elasticity high-buffering sole material comprises an acetic acid copolymer, an olefin block copolymer, an ethylene octene block copolymer, a polyolefin thermoplastic elastomer, isoprene rubber, ethylene propylene diene monomer rubber, talcum powder, calcium powder, a foaming agent, an antiwear agent, a slip inhibitor, a cross-linking agent, zinc oxide and a lubricant. The anti-slip high-elasticity shock-absorbing device has the advantages that the anti-slip shock-absorbing effect is achieved when the device is in motion, so that the shock of knees and joints is relieved, the shock is firstly absorbed and then is given, the injury caused in running and motion processes is avoided, meanwhile, the anti-slip high-elasticity shock-absorbing device has the anti-slip wear-resisting effect and can be directly contacted with the outer sole of the ground, and the safety in the motion process is protected.

Description

High-elasticity high-buffering sole material and preparation method thereof
Technical Field
The invention relates to the technical field of sole materials, in particular to a high-elasticity high-buffering sole material and a preparation method thereof.
Background
The concept of high-elasticity and high-elasticity is applied to the shoemaking field, and is a group of coherent concepts on the midsole and the outsole, and the sole on the market at present is either high-elasticity and low-elasticity, or the sole material with high-elasticity and high-elasticity is not very common in the shoemaking field.
Defects and deficiencies of the prior art:
1. when the shoes with high rebound are worn, leg stiffness can be increased and impact load can be amplified during running or sports;
2. the impact force of landing can be quickly transferred when the high-buffer shoes are worn in running or sports, but the sports state is required to be kept by the self-restoring force of the sportsman due to the lack of resilience force, so that the sportsman is tired when running, and the sports efficiency is reduced.
Disclosure of Invention
First, the technical problem to be solved
In view of the above-mentioned drawbacks and disadvantages of the prior art, the present invention provides a high-elasticity high-buffering sole material and a preparation method thereof, which solve the technical problems of high elasticity, low buffering or low elasticity and high buffering of soles in the market.
(II) technical scheme
In order to achieve the above purpose, the main technical scheme adopted by the invention comprises the following steps:
in a first aspect, embodiments of the present invention provide a high elasticity, high cushioning sole material comprising:
Figure BDA0003311823790000011
Figure BDA0003311823790000021
optionally, the foaming agent is an AC foaming agent.
Optionally, the crosslinking agent is a vulcanization accelerator BIPB.
In a second aspect, an embodiment of the present invention provides a method for preparing a high-elasticity and high-cushioning sole material, which is characterized by comprising the following steps:
s1, respectively weighing the components;
s2, respectively taking the components with the formula amount, putting the components into a kneader, and controlling the temperature of the kneader to be 120-125 ℃ and the kneading time to be 900-950S in the kneading process so that the components are fully fused together;
s3, putting the material obtained in the step S1 into an underwater pelletizer to produce particles with uniform size;
s4, standing the particles obtained in the step S2 for 8 hours at normal temperature;
s5, conveying the particles subjected to standing in the step S3 to an injection molding machine, injecting the particles into a mold through a charging barrel, controlling the temperature in the mold to be 175+/-3 ℃, vulcanizing in the process, and obtaining a high-elasticity and high-buffering finished product after the vulcanizing time is 450S.
(III) beneficial effects
The beneficial effects of the invention are as follows: the invention has the beneficial effects that: the invention has the advantages of high elasticity and high buffering, and can delay rebound to achieve the function of shock absorption and buffering during the movement, thereby relieving the impact of the knee and the joint, buffering and then giving rebound, avoiding the injury caused during the running and the movement, simultaneously having the anti-slip and wear-resistant outsoles which can directly contact the ground, and protecting the safety during the movement.
Drawings
FIG. 1 is a preparation flow chart.
Detailed Description
In order to better understand the above technical solution, an exemplary embodiment of the present invention will be described in more detail below with reference to fig. 1. While exemplary embodiments of the present invention are shown in the drawings, it should be understood that the present invention may be embodied in various forms and should not be limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art.
Examples 1 to 3
In the examples provided herein, the raw material formulations of 3 examples are provided, see for example the formulation table in table 1:
examples (parts by mass) Example 1 Example 2 Example 3
Acetic acid-acetic acid copolymer 40 50 60
Olefin block copolymers 25 20 30
Ethylene octene block copolymer 15 10 10
Polyolefin thermoplastic elastomer 10 5 5
Isoprene rubber 5 5 8
Ethylene propylene diene monomer 20 10 10
Talc powder 5 5 8
Calcium powder 4 4 4
Foaming agent 3 2.5 2.3
Wear-resistant agent 4 5 5
Anti-slip agent 2 2 1
Vulcanization accelerator BIPB 0.5 0.8 1
Zinc oxide 1 1.2 1.5
Lubricant 1 0.8 0.5
The preparation method comprises the following steps:
s1, respectively weighing the components;
s2, respectively taking the components with the formula amount, putting the components into a kneader, and controlling the temperature of the kneader to be 120-125 ℃ and the kneading time to be 900-950S in the kneading process so that the components are fully fused together;
s3, putting the material obtained in the step S1 into an underwater pelletizer to produce particles with uniform size;
s4, standing the particles obtained in the step S2 for 8 hours at normal temperature;
s5, conveying the particles subjected to standing in the step S3 to an injection molding machine, injecting the particles into a mold through a charging barrel, controlling the temperature in the mold to be 175+/-3 ℃, vulcanizing in the process, and obtaining a high-elasticity and high-buffering finished product after the vulcanizing time is 450S.
A high elasticity high cushioning sole material prepared in examples 1-3 has the test properties shown in Table 2:
Figure BDA0003311823790000041
from table 2, it can be seen that the performance test results of the above examples, wherein the data in example 2 are significantly better than the other two examples.
Similarly, the finished product prepared by the formula in the example 2 is further tested, and the following result is obtained: test 1. Resistance to repeated compression of shoe material (SATRA. TM. 156:2002, 870N).
(1) After 5 ten thousand cycles, observe: no change;
(2) Thickness variation: 1.0mm.
Test 2. Shock absorption test (SATRA TM 142:1992).
Front section
(1) Deceleration rate: 145m/s 2
(2) Permeability: 7.0mm
(3) Buffer ratio: 42.0%
Heel of shoe
(1) Deceleration rate: 75m/s 2
(2) Permeability: 10.5mm
(3) Buffer ratio: 44.0%
Test 3, test of pendulum resilience (DIN 53512:2000).
Test quantity: 2
Thickness: 12.5mm
Rebound rate: 60 percent of
The test data are from Shenzhen Tianxiang quality technical service Co.
From the data, the sole material provided by the invention completely meets the performance requirements of high elasticity and high buffering, and simultaneously meets the requirements of slip resistance and wear resistance and can be directly contacted with the ground.
Finally, it should be noted that: the above embodiments are only for illustrating the technical solution of the present invention, and not for limiting the same; although the invention has been described in detail with reference to the foregoing embodiments, it will be understood by those of ordinary skill in the art that: the technical scheme described in the foregoing embodiments can be modified or some or all of the technical features thereof can be replaced by equivalents; such modifications and substitutions do not depart from the spirit of the invention.

Claims (4)

1. The high-elasticity high-buffering sole material is characterized by comprising the following components in parts by mass:
Figure FDA0003311823780000011
2. the high resilience blast-resistant sole material as set forth in claim 1, wherein: the foaming agent is an AC foaming agent.
3. The high resilience blast-resistant sole material as set forth in claim 1, wherein: the cross-linking agent is a vulcanization accelerator BIPB.
4. The preparation method of the high-elasticity high-buffering sole material is characterized by comprising the following steps of:
s1, respectively weighing the components;
s2, respectively taking the components with the formula amount, putting the components into a kneader, and controlling the temperature of the kneader to be 120-125 ℃ and the kneading time to be 900-950S in the kneading process so that the components are fully fused together;
s3, putting the material obtained in the step S1 into an underwater pelletizer to produce particles with uniform size;
s4, standing the particles obtained in the step S2 for 8 hours at normal temperature;
s5, conveying the particles subjected to standing in the step S3 to an injection molding machine, injecting the particles into a mold through a charging barrel, controlling the temperature in the mold to be 175+/-3 ℃, vulcanizing in the process, and obtaining a high-elasticity and high-buffering finished product after the vulcanizing time is 450S.
CN202111218917.5A 2021-10-20 2021-10-20 High-elasticity high-buffering sole material and preparation method thereof Pending CN115991920A (en)