CN103740102A - Conductive nylon composite material and preparation method thereof - Google Patents
Conductive nylon composite material and preparation method thereof Download PDFInfo
- Publication number
- CN103740102A CN103740102A CN201310745328.1A CN201310745328A CN103740102A CN 103740102 A CN103740102 A CN 103740102A CN 201310745328 A CN201310745328 A CN 201310745328A CN 103740102 A CN103740102 A CN 103740102A
- Authority
- CN
- China
- Prior art keywords
- graphene
- matrix material
- district
- nylon matrix
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a conductive nylon composite material and a preparation method thereof. The conductive nylon composite material comprises the following components by weight percent: 82-90% of PA1212, 1-5% of graphene, 0.1-1% of antioxidant, 0.5-1% of coupling agent, 8-13% of flexibilizer, and 0.5-1% of silicon oil. The coupling agent can be used for well improving the compatibility of the graphene and resin; due to the added flexibilizer, the toughness of the material is improved; a little graphene can cause the material to conduct electricity. The conductive nylon composite material has high electrical conductivity and good toughness, the preparation process is simple and the production technology is easy to control.
Description
[technical field]
The present invention relates to polymeric material field, relate in particular to a kind of electroconductive nylon matrix material and preparation method thereof.
[background technology]
Traditional PA6 and the PA66 of Performance Ratio that long carbon chain nylon possesses has better dimensional stability; and superior chemical resistance; traditional conductive nylon material; conventionally can add the conductive agent of some electrically conductive graphites or precipitation type; but PA6 and PA66 will accomplish conduction, and not only the conductive agent addition of graphite or precipitation type is large, and also large to the performance impact of PA6 and PA66 material; particularly shock strength aspect can weaken a lot, and material can be highly brittle.
[summary of the invention]
The technical problem to be solved in the present invention be to provide a kind ofly have that electric conductivity is high, the electroconductive nylon matrix material of good toughness and preparation method thereof.
In order to solve the problems of the technologies described above, the technical solution used in the present invention is that a kind of electroconductive nylon matrix material, is characterized in that, composed of the following components by weight percentage:
Electroconductive nylon matrix material according to claim 1, is characterized in that, described Graphene is Nanjing pioneer's carboxylated graphene powder.
Electroconductive nylon matrix material according to claim 1, is characterized in that, coupling agent is the Nanjing KH-550 of chemical industry forward, purity >=97%.
Electroconductive nylon matrix material according to claim 1, is characterized in that, described toughner is POE grafted maleic anhydride, and percentage of grafting is 0.8%.
Electroconductive nylon matrix material according to claim 1, is characterized in that, described oxidation inhibitor is N, N'-pair-(3-(3,5-di-tert-butyl-hydroxy phenyl) propionyl) hexanediamine, and fusing point 110-125 degree Celsius.
Described in claim 1, a preparation method for electroconductive nylon matrix material, is characterized in that, comprises the following steps:
1) by above-mentioned weight percent, take raw material;
2) PA1212 is mixed in mixing tank to 3-7 minute with silicone oil;
3) by step 2) in the PA1212 that mixes in mixing tank, mix 3-7 minute with silicon oil mixture with coupling agent, toughner, oxidation inhibitor, Graphene;
4) raw material mixing in step 3) is thrown in twin screw extruder, through melt extruding, granulation.Manufacturing condition is: twin screw extruder one district's temperature is 180-220 ℃, and two district's temperature are 180-220 ℃, and three district's temperature are 180-220 ℃, and four district's temperature are 180-220 ℃, and compound time of delivery in screw rod is 1-2 minute.
Coupling agent of the present invention can improve Graphene and resin compatible well. toughner add the toughness that has improved material, a small amount of Graphene just can be accomplished conduction, electroconductive nylon composite material conductive rate of the present invention is high, good toughness, preparation process are simple, and production technique is easily controlled.
[embodiment]
Below by embodiment, the present invention is further elaborated:
A kind of electroconductive nylon matrix material provided by the invention, its composition is by weight percentage:
PA1212 82-90%; Graphene 1-5%; Coupling agent KH-550 0.1-1%; Toughner POE-MAH 8-13%; Antioxidant 1010 0.1-1%; Silicone oil 0.5-1%;
Wherein, PA1212 is east, Shandong occasion AIVS01.Its shock strength (ASTM D256) is 25KJ/M3.
Oxidation inhibitor is the very easily N of chemical industry of Beijing, N'-pair-(3-(3,5-di-tert-butyl-hydroxy phenyl) propionyl) hexanediamine 1010, and fusing point 110-125 degree Celsius.
Coupling agent is the Nanjing KH-550 of chemical industry forward, and its purity is >=97%.
Toughner is homemade POE grafted maleic anhydride, and percentage of grafting is 0.8%.The preparation method of POE grafted maleic anhydride is: each component of following weight percent is mixed, and is to extrude under the condition of 140-200 ℃ in temperature with twin screw extruder:
Graphene is Nanjing pioneer's carboxylated graphene powder XF004
Silicone oil is common silicone oil.
The siloxanes coupling agent of PA1212 and Graphene in the present invention, can the inorganic and organic consistency of fine raising, and it is little to play addition, but can reach efficient perveance
Its manufacturing processed is as follows:
1) by above-mentioned weight percent, take raw material;
2) PA1212 is mixed in mixing tank to 3-7 minute with silicone oil;
3) by step 2) in the PA1212 that mixes in mixing tank, mix 3-7 minute with silicon oil mixture with coupling agent, toughner, oxidation inhibitor, Graphene;
4) raw material mixing in step 3) is thrown in twin screw extruder, through melt extruding, granulation.Manufacturing condition is: twin screw extruder one district's temperature is 180-220 ℃, and two district's temperature are 180-220 ℃, and three district's temperature are 180-220 ℃, and four district's temperature are 180-220 ℃, and compound time of delivery in screw rod is 1-2 minute.
Below in conjunction with specific embodiment, the present invention is explained in detail:
Embodiment 1
PA121286.9%; Graphene 1%; Coupling agent KH-5500.5%; Toughner POE-MAH10%; Antioxidant 1010 0.1%; Silicone oil 0.5%;
First add silicone oil and PA1212 fully mix all with, make silicone oil invest well PA1212 surface, and then add Graphene powder and other raw material mixes, Graphene can be dispersed in resin uniformly.
Through melt temperature, be that 200-260 ℃ of twin screw extruder extruded, granulation.
Wherein each zone temperatures is: 180 ℃, a district, and two 200 ℃, districts, three 220 ℃, districts, four 220 ℃, districts, five 220 ℃, districts, the residence time was 90 seconds.
Embodiment 2
PA121284.9%; Graphene 2%; Coupling agent KH-5500.5%; Toughner POE-MAH10%; Antioxidant 1010 0.1%; Silicone oil 0.5%;
First add silicone oil and PA1212 fully mix all with, make silicone oil invest well PA1212 surface, and then add Graphene powder and other raw material mixes, Graphene can be dispersed in resin uniformly.
Through melt temperature, be that 200-260 ℃ of twin screw extruder extruded, granulation.
Wherein each zone temperatures is: 180 ℃, a district, and two 200 ℃, districts, three 220 ℃, districts, four 220 ℃, districts, five 220 ℃, districts, the residence time was 90 seconds.
Embodiment 3
PA121282.9%; Graphene 3%; Coupling agent KH-5500.5%; Toughner POE-MAH10%; Antioxidant 1010 0.1%; Silicone oil 0.5%;
First add silicone oil and PA1212 fully mix all with, make silicone oil invest well PA1212 surface, and then add Graphene powder and other raw material mixes, Graphene can be dispersed in resin uniformly.
Through melt temperature, be that 200-260 ℃ of twin screw extruder extruded, granulation.
Wherein each zone temperatures is: 180 ℃, a district, and two 200 ℃, districts, three 220 ℃, districts, four 220 ℃, districts, five 220 ℃, districts, the residence time was 90 seconds.
Embodiment 4
PA121280.9%; Graphene 4%; Coupling agent KH-5500.5%; Toughner POE-MAH10%; Antioxidant 1010 0.1%; Silicone oil 0.5%;
First add silicone oil and PA1212 fully mix all with, make silicone oil invest well PA1212 surface, and then add Graphene powder and other raw material mixes, Graphene can be dispersed in resin uniformly.
Through melt temperature, be that 200-260 ℃ of twin screw extruder extruded, granulation.
Wherein each zone temperatures is: 180 ℃, a district, and two 200 ℃, districts, three 220 ℃, districts, four 220 ℃, districts, five 220 ℃, districts, the residence time was 90 seconds.
Embodiment 5
PA121283.9%; Graphene 1%; Coupling agent KH-5501%; Toughner POE-MAH13%; Antioxidant 1010 0.1%; Silicone oil 1%;
First add silicone oil and PA1212 fully mix all with, make silicone oil invest well PA1212 surface, and then add Graphene powder and other raw material mixes, Graphene can be dispersed in resin uniformly.
Through melt temperature, be that 200-260 ℃ of twin screw extruder extruded, granulation.
Wherein each zone temperatures is: 180 ℃, a district, and two 200 ℃, districts, three 220 ℃, districts, four 220 ℃, districts, five 220 ℃, districts, the residence time was 90 seconds.
Performance test:
Above-mentioned 5 embodiment are completed to particle dry 4-6 hour in the convection oven of 80-100 ℃ of granulation, then by the injection moulding sample preparation on 80T injection moulding machine of dry particle, in sample making course, keep mould temperature between 70-100 ℃.
Tensile strength is tested by GB/T1040 standard, and specimen types is I type, and batten size (mm): 170(is long) × (20 ± 0.2) (end width) × (4 ± 0.2) (thickness), draw speed is 50mm/min;
Flexural strength and modulus in flexure are tested by GB9341/T standard.Specimen types is specimen size (mm): (80 ± 2) × (10 ± 0.2) × (4 ± 0.2), and rate of bending is 20mm/min;
Notched Izod impact strength is tested by GB/T1043 standard, and specimen types is I type, specimen size (mm): (80 ± 2) × (10 ± 0.2) × (4 ± 0.2); Breach type is category-A, and breach residual thickness is 3.2mm;
Plastic cement antistatic (perveance) test is tested by GB/T15662-1995 standard.Table 1: the formula table of embodiment 1-5
| Component (weight percent) | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 |
| PA1212 | 87.9 | 86.9 | 85.9 | 84.9 | 83.9 |
| Graphene | 1 | 2 | 3 | 4 | 1 |
| Toughner | 10 | 10 | 10 | 10 | 13 |
| Coupling agent | 0.5 | 0.5 | 0.5 | 0.5 | 1 |
| Oxidation inhibitor | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 |
| Silicone oil | 0.5 | 0.5 | 0.5 | 0.5 | 1 |
Table 2: embodiment 1-5's can be in Table
| Performance | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 |
| Notched Izod impact strength (J/M) | 600 | 625 | 665 | 668 | 690 |
| Tensile strength (MPa) | 36 | 35 | 40 | 43 | 42 |
| Flexural strength (MPa) | 45 | 43 | 48 | 47 | 46 |
| (Ω m) for perveance | 10 6 | 10 4 | 10 3 | 10 2 | 10 2 |
| Modulus in flexure (MPa) | 1320 | 1600 | 1585 | 880 | 1450 |
Graphene be at present the thinnest be in the world the hardest nano material also, it is almost completely transparent, only absorbs 2.3% light; Thermal conductivity is up to 5300W/mK, and higher than carbon nanotube and diamond, under normal temperature, its electronic mobility * exceedes 15000cm & sup2; / Vs, higher than CNT (carbon nano-tube) or silicon crystal * again, and only about 10-6 Ω cm of resistivity is lower than copper or silver, is the current material of resistivity minimum in the world
By learning after the data analysis in above table, the interpolation of Graphene is to the overall performance of the matrix material effect that has a certain upgrade, particularly shock strength, the main still nanostructure of Graphene true qualities of reason, thereby to the effect of haveing a certain upgrade of overall composite property, from perveance, the general interpolation 1% of Graphene has just reached an antistatic effect, with respect to electrically conductive graphite, greatly reduced adding proportion, along with the increase of Graphene adding proportion, perveance also promotes, when adding proportion is more than or equal to 2%, integral material just can reach conductive effect, therefore, Graphene is filled PA1212 not only has castering action to the performance of material, and given good conductive effect.
The coupling agent of the siloxanes in the above embodiment of the present invention can improve Graphene and resin compatible well. before Graphene adds, first add a certain amount of silicone oil and resin fully mix all with, accomplish that silicone oil can be good at investing resin surface, and then add Graphene powder, Graphene can be dispersed in resin uniformly.Make the toughness that has directly improved material that adds of toughner by oneself.Just very superior of the impact of the original material of PA1212, and water-intake rate is low, the product high to some dimensional requirements is also applicable to, as long as add a small amount of Graphene, just can accomplish conduction, because Graphene belongs to Nano grade, therefore after adding, not only the performance of material is not reduced, aspect shock strength, can be improved on the contrary.
The composite conducting material its preparation method of above a kind of Graphene provided by the present invention being filled to PA1212 is described in detail, applied specific case herein principle of the present invention and embodiment are set forth, the explanation of above embodiment is just for helping to understand method of the present invention and core concept thereof; , for one of ordinary skill in the art, according to thought of the present invention, all will change in specific embodiments and applications, to sum up, this description should not be construed as limitation of the present invention meanwhile.
Claims (6)
1. an electroconductive nylon matrix material, is characterized in that, composed of the following components by weight percentage:
2. electroconductive nylon matrix material according to claim 1, is characterized in that, described Graphene is Nanjing pioneer's carboxylated graphene powder.
3. electroconductive nylon matrix material according to claim 1, is characterized in that, coupling agent is the Nanjing KH-550 of chemical industry forward, purity >=97%.
4. electroconductive nylon matrix material according to claim 1, is characterized in that, described toughner is POE grafted maleic anhydride, and percentage of grafting is 0.8%.
5. electroconductive nylon matrix material according to claim 1, is characterized in that, described oxidation inhibitor is N, N'-pair-(3-(3,5-di-tert-butyl-hydroxy phenyl) propionyl) hexanediamine, and fusing point 110-125 degree Celsius.
6. a preparation method for electroconductive nylon matrix material described in claim 1, is characterized in that, comprises the following steps:
1) by weight percent claimed in claim 1, take raw material;
2) PA1212 is mixed in mixing tank to 3-7 minute with silicone oil;
3) by step 2) in the PA1212 that mixes in mixing tank, mix 3-7 minute with silicon oil mixture with coupling agent, toughner, oxidation inhibitor, Graphene;
4) raw material mixing in step 3) is thrown in twin screw extruder, through melt extruding, granulation; Manufacturing condition is: twin screw extruder one district's temperature is 180-220 ℃, and two district's temperature are 180-220 ℃, and three district's temperature are 180-220 ℃, and four district's temperature are 180-220 ℃, and compound time of delivery in screw rod is 1-2 minute.