CN103709914A - Fireproof flame-retardant paint composition - Google Patents
Fireproof flame-retardant paint composition Download PDFInfo
- Publication number
- CN103709914A CN103709914A CN201310679912.1A CN201310679912A CN103709914A CN 103709914 A CN103709914 A CN 103709914A CN 201310679912 A CN201310679912 A CN 201310679912A CN 103709914 A CN103709914 A CN 103709914A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- paint composition
- epoxy resin
- favorable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fireproof flame-retardant paint composition which is prepared from the following components in parts by weight: 30-50 parts of alkyd resin, 10-30 parts of polyurethane paint, 5-15 parts of methyl isobutyl ketone, 5-10 parts of chlorinated paraffin, 3-8 parts of thickener, 5-10 parts of ethanol aether acetate, 1-3 parts of cyclohexanone and 10-15 parts of coal tar. The paint composition is modified by an epoxy resin. The epoxy resin contains the hydroxy group, and the epoxy group and ether group with medium molecular weight above have polarity, so the paint composition has very high adhesive force, optimal alkali resistance, favorable acid resistance, small film-forming contractility (within 1%), favorable stability and favorable insulativity, and thus, is called chemical alloy. After adopting the epoxy resin, the adhesive force of the paint is greatly improved from Grade 3 to Grade 1-2, and the paint film has high corrosion resistance, high impact resistance and high hardness.
Description
Technical field
The present invention relates to paint field, particularly, the present invention relates to a kind of fireproof flame-retardant coating composition.
Background technology
Current numerous frie retardant coating, no matter be the common defects that has of solvent-borne type or water-based: poor water resistance, and can only be used in indoor scenarios, be rarely used in outdoor, because wet, chance water (snowy and rainy day) paint film meeting bubbling, paint film can be damaged in the course of time, and the life-span is protected in impact, more seriously run into fire alarm, because the inefficacy of fire prevention resistance fire material or the meeting impact rescue of running off in paint film.The defect of existing frie retardant coating is: poor water resistance, can only be used in indoor scenarios, and not fire-resistant, poor adhesive force, anti-intensity difference.Major cause is: in formula, fire retardant, the agent of one-tenth carbon skeleton have water-soluble and not water-fast mostly.Resin glue is organism, has incendivity and not fire-resistant.Certainly, chlorinated rubber, supervinyi chloride resin, because it contains chlorine atom, have burning difficulty and can extend one section of light-off time, but eventually can burn.And all there is the drawbacks such as poor adhesive force, anti-intensity difference deficiency in above-mentioned base-material.
Summary of the invention
The deficiency existing for prior art, technical problem to be solved by this invention is, a kind of fireproof flame-retardant coating composition that solves the technological deficiency of currently available products poor water resistance, not fire-resistant, poor adhesive force and anti-intensity difference is provided.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of fireproof flame-retardant coating composition, is grouped into by the one-tenth of following weight part:
Synolac 30～50;
Polyurethane paint 10～30;
Methyl iso-butyl ketone (MIBK) 5～15;
Clorafin 5～10;
Thickening material 3～8;
Ethanol ether acetic ester 5～10;
Cyclohexanone 1～3;
Coal tar 10～15.
The advantage of fireproof flame-retardant coating composition of the present invention is: with epoxy resin, carry out modification.Epoxy resin contains hydroxyl because of it, and the above epoxy group(ing) of intermediate molecular weight, ether polarity are large, sticking power extra-heavy, alkali resistance is best, acidproof better, film forming convergent force in 1%, stability, the fine chemical industry alloy that is referred to as of insulativity.Adopt after epoxy resin, paint adhesion all reaches great improvement, rises to 1～2 grade from 3 grades, and the anticorrosion anti-impact force of paint film is strong, and the hardness that tends to become strong is good.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further details;
A fireproof flame-retardant coating composition, is grouped into by the one-tenth of following weight part:
Synolac 30～50;
Polyurethane paint 10～30;
Methyl iso-butyl ketone (MIBK) 5～15;
Clorafin 5～10;
Thickening material 3～8;
Ethanol ether acetic ester 5～10;
Cyclohexanone 1～3;
Coal tar 10～15.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, remodeling, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (1)
1. a fireproof flame-retardant coating composition, is characterized in that, by the one-tenth of following weight part, is grouped into:
Synolac 30～50;
Polyurethane paint 10～30;
Methyl iso-butyl ketone (MIBK) 5～15;
Clorafin 5～10;
Thickening material 3～8;
Ethanol ether acetic ester 5～10;
Cyclohexanone 1～3;
Coal tar 10～15.