CN103556074A - Production method of hardened and tempered high-strength Q500E super-thick steel plate - Google Patents

Production method of hardened and tempered high-strength Q500E super-thick steel plate Download PDF

Info

Publication number
CN103556074A
CN103556074A CN201310559278.8A CN201310559278A CN103556074A CN 103556074 A CN103556074 A CN 103556074A CN 201310559278 A CN201310559278 A CN 201310559278A CN 103556074 A CN103556074 A CN 103556074A
Authority
CN
China
Prior art keywords
steel plate
rolling
temperature
slab
speed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310559278.8A
Other languages
Chinese (zh)
Other versions
CN103556074B (en
Inventor
杨云清
张爱兵
翟运涛
蒋德阳
吴清明
袁仁平
张青学
杜江
李玉路
高擎
张勇伟
朱胡军
张计谋
李仕一
黄远涛
胡振华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hunan Valin Xiangtan Iron and Steel Co Ltd
Hunan Hualing Xiangtan Iron and Steel Co Ltd
Original Assignee
Hunan Hualing Xiangtan Iron and Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hunan Hualing Xiangtan Iron and Steel Co Ltd filed Critical Hunan Hualing Xiangtan Iron and Steel Co Ltd
Priority to CN201310559278.8A priority Critical patent/CN103556074B/en
Publication of CN103556074A publication Critical patent/CN103556074A/en
Application granted granted Critical
Publication of CN103556074B publication Critical patent/CN103556074B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a production process of a hardened and tempered high-strength Q500E super-thick steel plate. The production method comprises process steps of molten iron pre-treating, converter steelmaking, external refining, continuous casting (dynamic soft pressing and electromagnetic stirring), heating, rolling, pre-straightening, online quenching, offline quenching, tempering, finishing, performance examining and ultrasonic-wave flaw detecting. The steel comprises the chemical components in percentage by mass: not greater than 0.15% of C, 0.20%-0.40% of Si, 1.00%-1.30% of Mn, not greater than 0.015% of P, not greater than 0.003% of S, 0.03%-0.06% of AlT, not greater than 0.10% of Nb+Ti+V, not greater than 1.0% of Cu+Ni, 0.40%-0.70% of Cr, 0.30%-0.60% of Mo, not greater than 0.0025% of B, and the balance of Fe and inevitable impurities. CEV is controlled to be not greater than 0.58, and the CEV is calculated according to a formula of CEV=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15. The produced high-performance hardened and tempered high-strength Q500E super-thick steel plate which is 100mm-120mm thick satisfies needs of manufacturing heavy machinery of a mine, a port, and the like.

Description

A kind of production method of modified high strength Q500E super-thick steel plate
Technical field
The invention belongs to smelting iron and steel technology, particularly a kind of production method of modified high strength Q500E super-thick steel plate.
Background technology
Super-thick steel plate refers to the steel plate of thickness >=60mm.The method that prior art is produced super-thick steel plate mainly contains: static ingot and electroslag remelting steel ingot method, continuously cast bloom slab method, weld compound strand method, vertical continuous metal cast process.
General steel mill continuously cast bloom maximum ga(u)ge is 300mm, and only a few steel mill also has thick 400mm continuously cast bloom to produce.Along with the development of Wide and Thick Slab production technology, use the common intensity rank special heavy plate technology of 260～300mm slab production, 60～100mm very universal; Thickness is greater than 100mm common intensity rank super-thick steel plate, is all in the world to adopt steel ingot rolling, and the technique of this respect has relevant report; Thickness is greater than the modified high strength special heavy plate of 100mm, and after the rolling of employing steel ingot, modifier treatment is produced.
The high strength special heavy plate heart portion rolling deformation of continuous casting billet milling modifier treatment is not deep and thorough, produces many bad consequences: properties percent of pass is low, particularly poor impact toughness, performance at thickness direction is inhomogeneous, Z-direction poor performance, steel plate heart portion ballistic work is low, and steel plate inspection qualification rate is low.Thickness is greater than the modified high strength special heavy plate of 100mm, uses thick 300mm continuous casting billet milling modifier treatment to produce and has no relevant report.The steel ingot rolling super-thick steel plate rate of becoming a useful person is low, and general Wide and Thick Slab factory can not produce.
In the conventional special heavy plate operation of rolling of prior art, blank temperature is even, the temperature distribution T of its thickness direction ncan think uniformly approximate.If reduce blank skin temperature, the temperature T of sotck thinkness direction sbe cooled heterogeneous through forcing, after blank skin temperature reduces, can make resistance to deformation or the yield strength σ of top layer metal sincrease, distortion difficulty increases, thereby suppresses the flow of metal of blank top layer, and increases the distortion of central zone with this, thereby makes the compression stress ot of thickness direction tsurpass yielding stress σ s, produce distortion more uniformly.Adopt sotck thinkness direction thermograde to control the technology of deformation of rolled wire, be referred to as thermograde rolling technique (Fig. 1, Fig. 2).
Thermograde rolling method is that steel slab surface temperature is reduced, and improves the deformation resistance of steel slab surface, and the heart portion of slab is introduced in the distortion during by rolling, but necessary high-speed rolling concentrates on slab top layer otherwise slab returns red after strain.The rolling method of thermograde rolling special heavy plate provides possibility for improving steel plate heart portion performance, and this technology can improve heart portion performance and the Z-direction performance of modified high strength special heavy plate.
Chinese patent CN200710193023.9 " a kind of high tensile steel plate and preparation method thereof " discloses a kind of 100Kg level yield strength and has been not less than 890MPa, the production method of the high tensile steel plate that thickness is 8～100mm, and its 70mm adopts steel ingot stocking with upper steel plate.Chinese patent CN201110093666.2 " quenched and tempered high tensile strength plate and production method thereof for wood based panel equipment " discloses a kind of actual NM400 of being steel plate, thickness is the production method of 70～120mm steel plate, steel plate adopts continuously cast bloom stocking, after quenching, tempering temperature is 300～350 ℃, and this type of steel plate can not be used as structural part.Chinese patent CN201210387796.1 " a kind of large for thickness oceanographic engineering quenched and tempered high tensile strength plate and production method thereof " discloses a kind of yield strength 480MPa, tensile strength 600MPa, the production method of maximum ga(u)ge 140mm steel plate, steel plate adopts steel ingot stocking.Chinese patent 201310178923.1 " a kind of heat treating method of super-thick steel plate " discloses the above high tensile steel plate heat treating method of a kind of thickness 100mm, steel plate low-pressure stage in quenching press adopt to swing cooling to solve the super-thick steel plate not saturating problem of quenching, it is that steel plate length is less than 9 meters that steel plate maximum length can not surpass low-pressure stage length, and this patent publish data is No. 45 steel of high-carbon for Mould Machining.
The improvement of the heavy equipment manufacturing technologies such as world's pick coal machine, with welded construction, replace steel casting, use in yield strength 500～890MPa modified high strength special heavy plate of series (100～120mm) delivery technical qualification, except meeting the routine inspection intensity, unit elongation, impelling strength of steel plate requires, propose steel plate yield tensile ratio simultaneously and be less than 0.92, the transverse impact merit at steel plate center is greater than 27J, and thickness directional properties reaches Z25, and it is qualified that steel plate carries out UT (Ultrasonic Testing) one-level one by one.For above-mentioned technical requirements, existing domestic and international manufacturing enterprise does not also have production report and the production actual achievement of continuously cast bloom stocking at present.After continuously cast bloom stocking, in the super-thick steel plate of modifier treatment production low compression ratio, there are many defects:
A. armor plate strength is qualified but toughness is low, can not meet standard-required;
B. steel plate is difficult to meet the requirement that heart portion transverse impact merit is greater than 27J;
C. steel plate is difficult to meet the requirement that thickness directional properties reaches Z25;
D. High Strength Steel Plate evenly extends low (≤6%), and strength and ductility product is little;
E. steel-plate ultrasound wave inspection qualification rate is low.
Summary of the invention
This patent purport has the production method that a kind of modified high strength Q500E super-thick steel plate is provided: the thick Clean Steel continuously cast bloom of employing 300mm is aided with heat and thermograde is depressed greatly fast speed rolling change rolled piece center texturizing condition, increase the strong deformation of steel plate heart portion, and it is cooling as conditioning heat treatment to utilize press quenching to force, the tissue of steel plate refinement after reservation controlled rolling, steel plate carries out the technology such as off-line modifier treatment and produces the modified high strength special heavy plate of thickness 100～120mm.Require steel plate yield strength to be not less than 490MPa, tensile strength is not less than 610 MPa, and yield tensile ratio is less than 0.92, and unit elongation is not less than 18%, and uniform elongation is not less than 8% ,-40 ℃ of KV 2(laterally) is not less than 47J, steel plate heart portion-40 ℃ KV 2(laterally) is not less than 47J, and thickness directional properties reaches Z25, and UT (Ultrasonic Testing) one-level is qualified, meets the needs that the heavy-duty machineries such as mine, harbour are manufactured.
Technical scheme of the present invention:
A production method for modified high strength Q500E super-thick steel plate, the production process route of steel is hot metal pretreatment → converter steelmaking → external refining → continuous casting (dynamic soft-reduction+induction stirring) → heating → rolling → pre-straightening → press quenching → off-line quenching → tempering → finishing → service check → UT (Ultrasonic Testing).
The chemical constitution quality percentage composition of steel is: C≤0.15, Si=0.20～0.40, Mn=1.00～1.30, P≤0.015, S≤0.003, AlT=0.03～0.06, Nb+ Ti+ V≤0.10, Cu+Ni≤1.0, Cr=0.40～0.70, Mo=0.30～0.60, B≤0.0025, surplus is Fe and inevitable impurity.Control CEV≤0.58, CEV is by CEV=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15 formula calculate.
(1) continuous casting: according to the mode of production of Clean Steel, produce 300 * 2280mm section continuously cast bloom, wherein in continuous casting, wrap superheating temperature and be less than 10 ℃, light draught 4mm, induction stirring electric current is by 295～305A(6.9～7.1Hz) control.
(2) heating: 1280～1300 ℃ of heating of plate blanks, heat-up time 10～15min/cm, soaking time is greater than 60min, upper surface temperature is higher than 10 ~ 20 ℃ of lower surfaces, slab heart portion temperature >=1250 ℃ of coming out of the stove.
(3) rolling:
Figure 888160DEST_PATH_IMAGE001
stage start rolling temperature>=1200 ℃, 980～1050 ℃ of finish to gauge red temperatures, roughing adopts thermograde, depresses greatly, fast speed rolling, after slab broadening, use milling train de-scaling high pressure water continuously slab sky to be crossed to passage cooling, during 950～900 ℃ of steel slab surface temperature, depress greatly fast speed rolling, every time opens the cooling rolled piece of high pressure water, roughing speed is 2.0 ~ 2.5m/s, roughing guarantees that the last average draft of continuous two passage is not less than 16%, and workpiece thickness is controlled by guaranteeing after slab broadening that two percentage pass reductions are not less than 16% thickness.
Figure 710623DEST_PATH_IMAGE002
stage finish rolling adopts thermograde, depresses greatly, fast speed rolling, 830 ~ 850 ℃ of start rolling temperatures, intermediate blank is empty to be crossed passage and uses milling train de-scaling high pressure water cooling to intermediate blank continuously, during 800～820 ℃ of intermediate blank surface temperatures, depress greatly fast speed rolling, finish rolling roll speed is 4.3 ~ 5.5m/s, every time opens the cooling rolled piece of high pressure water, 810 ~ 830 ℃ of controls of finish to gauge red temperature, open the according to target lower limit set of finishing temperature of cold temperature, every time draft must>=12%, last three passages accumulative total drafts are not less than 40%.
(4) pre-straightening: steel plate rolls rear pre-straightening machine roll gap number, speed 0.23 ~ 0.25m/s identical with steel plate nominal thickness is set, and steel plate carries out pre-straightening before entering water.
(5) press quenching: steel plate enters 810 ~ 830 ℃ of water temps, rolls rear DQ section roller speed 0.23 ~ 0.25m/s, a, b, c, each section of upper and lower water yield 180 ~ 190 m of d 3/ min, speed of cooling is greater than 20 ℃/s; The water yield 390 ~ 400 m in ACC section 3/ min, the lower water yield 870 ~ 900m 3/ min, roller speed 0.80 ~ 0.85m/s steel plate swings and is cooled to room temperature.
(6) off-line quenches: 920 ~ 930 ℃ of quenching temperatures, and time inside furnace thickness of slab mm * (2.0 ~ 2.2) min/mm, steel plate should be greater than 15min in stove soaking time; Quenching press roller speed 2.25 ~ 2.35m/s, the high pressure section gap nozzle water yield 645 ~ 655m 3/ min.
(7) tempering: 650 ~ 670 ℃ of temperature, time inside furnace thickness of slab mm * (3.0 ~ 3.5) min/mm, air cooling.
(8) service check and UT (Ultrasonic Testing).
By present method, produce the modified high strength special heavy plate of thickness 100～120mm, steel plate yield strength is not less than 490MPa, and tensile strength is not less than 610 MPa, and yield tensile ratio is less than 0.92, and unit elongation is not less than 18%, and uniform elongation is not less than 8% ,-40 ℃ of KV 2(laterally) is not less than 47J, steel plate heart portion-40 ℃ KV 2(laterally) is not less than 47J, and thickness directional properties reaches Z25, and UT (Ultrasonic Testing) one-level is qualified, met the needs that the heavy-duty machineries such as mine, harbour are manufactured.Therefore, compared with prior art, the present invention has the following advantages:
A. adopt the thick continuously cast bloom of 300mm to produce the thick modified high strength special heavy plate of high performance 100 ~ 120mm, reduced production cost, met the requirement that mine, harbour machinery are manufactured.
B. heat and thermograde, depress fast speed rolling greatly and strongly increased steel plate heart portion distortion, improved steel plate heart portion's performance and Z-direction performance, improved the ultrasonic flaw detection qualification rate of steel plate.
C. utilize press quenching to force cooling as conditioning heat treatment, the tissue of steel plate heart portion refinement after the rolling of retention temperature gradient and controlled rolling, improves hardened and tempered steel plate heart portion performance, has improved modified rear steel plate plasticity and toughness.
D. steel plate evenly extends and is greater than 8%, and strength and ductility product improves more than 30%, and high-strength steel workpiece opposing shock load ability improves.
E. use continuously cast bloom to produce high performance modified high strength special heavy plate, operation is simple, technique easily realizes, and generally Wide and Thick Slab factory all can produce.
Accompanying drawing explanation
Fig. 1 is for forcing the temperature profile of cooling rear sotck thinkness direction.
Fig. 2 is for forcing the stress pattern of cooling rear sotck thinkness direction.
Fig. 3 is the modified high strength special heavy plate microstructure picture figure that the inventive method is produced.
In figure: the blank uniform temperature of Tn-tradition rolling distributes; Ts-adopts the non-homogeneous temperature distribution of blank; σ s-retrains yielding stress; σ t-thickness direction stress.
Embodiment
Below in conjunction with embodiment, further illustrate content of the present invention.
Embodiment 1: refining thickness of slab is the modified high strength Q500E super-thick steel plate of 100mm.
The chemical constitution quality percentage composition of steel is: C=0.13, Si=0.26, Mn=1.10, P=0.010, S=0.001, Al s=0.041, Nb=0.030, Ti=0.015, V=0.046, Ni=0.50, Cr=0.40, Mo=0.51, B=0.0018, surplus is Fe and inevitable impurity; CEV=0.54.
The production craft step of steel and parameter are:
(1) continuous casting: produce 300X2280mm section continuously cast bloom according to the mode of production of Clean Steel, wherein wrap superheating temperature in continuous casting and be less than 10 ℃, light draught 4mm, induction stirring electric current by 300A(7Hz) control.
(2) heating: 1290～1300 ℃ of heating of plate blanks, heat-up time 11min/cm, soaking time 70min, upper surface temperature is higher than 16 ℃ of lower surfaces, come out of the stove 1257 ℃ of heart portion temperature of slab.
(3) rolling:
Figure 39973DEST_PATH_IMAGE001
1218 ℃ of stage start rolling temperatures, 1023 ℃ of finish to gauge red temperatures; After slab broadening, to slab, empty to cross 15 passages cooling continuously to use milling train de-scaling high pressure water, during 932 ℃ of steel slab surface temperature, depresses greatly fast speed rolling, and every time opens the cooling rolled piece of high pressure water, and roughing roll speed is 2.1m/s.Roughing guarantees the last average draft 16.2%, 17.8% of continuous two passage.After slab broadening, two passages are rolled into 150mm workpiece thickness.
Figure 802655DEST_PATH_IMAGE002
840 ℃ of stage start rolling temperatures, empty 8 passages of crossing of intermediate blank are also used milling train de-scaling high pressure water cooling to intermediate blank continuously, and 812 ℃ of intermediate blank surface temperatures are depressed greatly fast speed rolling, and finish rolling roll speed is 4.8m/s.Every time opens the cooling rolled piece of high pressure water, and 824 ℃ of finish to gauge red temperatures are opened the according to target lower limit set of finishing temperature of cold temperature, every time draft must >=12%, last three passages accumulative total drafts are not less than 40%.
(4) pre-straightening: pre-straightening machine roll gap arranges 100mm, speed 0.25 m/s, and steel plate carries out pre-straightening before entering water.
(5) press quenching: steel plate enters 880 ℃ of water temps; Roll rear DQ section, roller speed 0.25m/s, a, b, c, each section of upper and lower water yield 185m of d 3/ min, 30 ℃/s of speed of cooling; ACC section is by upper water yield 406m 3/ min, lower water yield 890m 3/ min, roller speed swing and are cooled to room temperature by 0.85m/s steel plate.
(6) off-line quenches: 930 ℃ of temperature; Time inside furnace 200min, steel plate is at stove soaking time 18min; Quenching press roller speed 2.3m/s, the high pressure section gap nozzle water yield 650 m 3/ min.
(7) tempering: 670 ℃ of temperature; Time inside furnace 348min; Air cooling.
Actual measurement the present embodiment 100mm plate property: yield strength 567MPa, tensile strength 669MPa, unit elongation 22.3%, evenly extend 8.9%, yield tensile ratio 0.85 ,-40 ℃ of KV 2(laterally) mean value 210J, steel plate heart portion-40 ℃ KV 2(laterally) mean value 178J, thickness directional properties Ψ mean value 45.3%, clod wash are qualified; Steel plate is qualified according to GB2970 standard flaw detection one-level.
Embodiment 2: refining thickness of slab is the modified high strength Q500E super-thick steel plate of 120mm.
The chemical constitution mass percent of steel is: C=0.13, Si=0.24, Mn=1.10, P=0.011, S=0.001, Al s=0.043, Nb=0.030, Ti=0.017, V=0.045, Ni=0.49, Cr=0.41, Mo=0.52, B=0.0017, surplus is Fe and inevitable impurity; CEV=0.56.
The production craft step of steel and parameter are:
(1) continuous casting: produce 300X2280mm section continuously cast bloom according to the mode of production of Clean Steel, wherein wrap superheating temperature in continuous casting and be less than 10 ℃, light draught 4mm, induction stirring electric current by 300A(7Hz) control.
(2) heating: 1290～1300 ℃ of heating of plate blanks, heat-up time 12min/cm, soaking time 65min, upper surface temperature is higher than 17 ℃ of lower surfaces, come out of the stove 1258 ℃ of heart portion temperature of slab.
(3) rolling:
Figure 533850DEST_PATH_IMAGE001
1227 ℃ of stage start rolling temperatures, 1018 ℃ of finish to gauge red temperatures; After slab broadening, to slab, empty to cross 14 passages cooling continuously to use milling train de-scaling high pressure water, during 943 ℃ of steel slab surface temperature, depresses greatly fast speed rolling, and every time opens the cooling rolled piece of high pressure water, and roughing roll speed is 2.1m/s.Roughing guarantees the last average draft 16.2%, 16.9% of continuous two passage.After slab broadening, two passages are rolled into 160mm workpiece thickness.
Figure 589531DEST_PATH_IMAGE002
835 ℃ of stage start rolling temperatures, empty 8 passages of crossing of intermediate blank are also used milling train de-scaling high pressure water cooling to intermediate blank continuously, and 819 ℃ of intermediate blank surface temperatures are depressed greatly fast speed rolling, and finish rolling roll speed is 4.7m/s.Every time opens the cooling rolled piece of high pressure water, and 821 ℃ of finish to gauge red temperatures are opened the according to target lower limit set of finishing temperature of cold temperature, every time draft must >=12%, last three passages accumulative total drafts are not less than 40%.
(4) pre-straightening: pre-straightening machine roll gap arranges 120mm, speed 0.23 m/s, and steel plate carries out pre-straightening before entering water.
(5) press quenching: steel plate enters 816 ℃ of water temps; Roll rear DQ section, roller speed 0.23m/s, a, b, c, each section of upper and lower water yield 187 m of d 3/ min, 29 ℃/s of speed of cooling; ACC section is by upper water yield 3904m 3/ min, lower water yield 893m 3/ min, roller speed swing and are cooled to room temperature by 0.85m/s steel plate.
(6) off-line quenches: 930 ℃ of temperature; Time inside furnace 240min, steel plate is at stove soaking time 17min; Quenching press roller speed 2.3m/s, the high pressure section gap nozzle water yield 650 m 3/ min.
(7) tempering: 650 ℃ of temperature; Time inside furnace 400min; Air cooling.
Actual measurement the present embodiment 120mm plate property: yield strength 537MPa, tensile strength 679MPa, unit elongation 23.4%, evenly extend 9.1%, yield tensile ratio 0.791 ,-40 ℃ of KV 2(laterally) mean value 221J, steel plate heart portion-40 ℃ KV 2(laterally) mean value 187J, thickness directional properties Ψ mean value 43.5%, clod wash are qualified; Steel plate is qualified according to GB2970 standard flaw detection one-level.

Claims (1)

1. the production method of a modified high strength Q500E super-thick steel plate, processing step is hot metal pretreatment → converter steelmaking → external refining → continuous casting (dynamic soft-reduction+induction stirring) → heating → rolling → pre-straightening → press quenching → off-line quenching → tempering → finishing → service check → UT (Ultrasonic Testing), it is characterized in that:
The chemical constitution percentage composition of steel is C≤0.15, Si=0.20～0.40, Mn=1.00～1.30, P≤0.015, S≤0.003, AlT=0.03～0.06, Nb+ Ti+ V≤0.10, Cu+Ni≤1.0, Cr=0.40～0.70, Mo=0.30～0.60, B≤0.0025, surplus is Fe and inevitable impurity, controls CEV≤0.58, and CEV is by CEV=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15 formula calculate;
Critical process step is:
(1) continuous casting: according to the mode of production of Clean Steel, produce 300 * 2280mm section continuously cast bloom, wherein in continuous casting, wrap superheating temperature and be less than 10 ℃, light draught 4mm, induction stirring electric current is by 295～305A(6.9～7.1Hz) control;
(2) heating: 1280～1300 ℃ of heating of plate blanks, heat-up time 10～15min/cm, soaking time is greater than 60min, upper surface temperature is higher than 10 ~ 20 ℃ of lower surfaces, slab heart portion temperature >=1250 ℃ of coming out of the stove;
(3) rolling:
Figure 512446DEST_PATH_IMAGE001
stage start rolling temperature>=1200 ℃, 980～1050 ℃ of finish to gauge red temperatures, roughing adopts thermograde, depresses greatly, fast speed rolling, after slab broadening, use milling train de-scaling high pressure water continuously slab sky to be crossed to passage cooling, during 950～900 ℃ of steel slab surface temperature, depress greatly fast speed rolling, every time opens the cooling rolled piece of high pressure water, roughing speed is 2.0 ~ 2.5m/s, roughing guarantees that the last average draft of continuous two passage is not less than 16%, and workpiece thickness is controlled by guaranteeing after slab broadening that two percentage pass reductions are not less than 16% thickness;
Figure 608578DEST_PATH_IMAGE002
stage finish rolling adopts thermograde, depresses greatly, fast speed rolling, 830 ~ 850 ℃ of start rolling temperatures, intermediate blank is empty to be crossed passage and uses milling train de-scaling high pressure water cooling to intermediate blank continuously, during 800～820 ℃ of intermediate blank surface temperatures, depress greatly fast speed rolling, finish rolling roll speed is 4.3 ~ 5.5m/s, every time opens the cooling rolled piece of high pressure water, 810 ~ 830 ℃ of controls of finish to gauge red temperature, open the according to target lower limit set of finishing temperature of cold temperature, every time draft must>=12%, last three passages accumulative total drafts are not less than 40%;
(4) pre-straightening: steel plate roll rear pre-straightening machine roll gap arrange number identical with steel plate nominal thickness, speed 0.23 ~ 0.25m/s, steel plate carries out pre-straightening before entering water;
(5) press quenching: steel plate enters 810 ~ 830 ℃ of water temps, rolls rear DQ section roller speed 0.23 ~ 0.25m/s, a, b, c, each section of upper and lower water yield 180 ~ 190 m of d 3/ min, speed of cooling is greater than 20 ℃/s; The water yield 390 ~ 400 m in ACC section 3/ min, the lower water yield 870 ~ 900m 3/ min, roller speed 0.80 ~ 0.85m/s steel plate swings and is cooled to room temperature;
(6) quench: 920 ~ 930 ℃ of quenching temperatures, time inside furnace thickness of slab mm * (2.0 ~ 2.2) min/mm, steel plate should be greater than 15min in stove soaking time; Quenching press roller speed 2.25 ~ 2.35m/s, the high pressure section gap nozzle water yield 645 ~ 655m 3/ min;
(7) tempering: 650 ~ 670 ℃ of temperature, time inside furnace thickness of slab mm * (3.0 ~ 3.5) min/mm, air cooling;
(8) service check and UT (Ultrasonic Testing).
CN201310559278.8A 2013-11-12 2013-11-12 Production method of hardened and tempered high-strength Q500E super-thick steel plate Active CN103556074B (en)