CN103435993A - PC material - Google Patents
PC material Download PDFInfo
- Publication number
- CN103435993A CN103435993A CN2013103406243A CN201310340624A CN103435993A CN 103435993 A CN103435993 A CN 103435993A CN 2013103406243 A CN2013103406243 A CN 2013103406243A CN 201310340624 A CN201310340624 A CN 201310340624A CN 103435993 A CN103435993 A CN 103435993A
- Authority
- CN
- China
- Prior art keywords
- antioxidant
- lubricant
- mbs
- agent
- dripping agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PC (Poly Carbonate) material which comprises the following components by weight percentage: 77.8-90.9% of PC resin, 3-5% of MBS (Methyl Methacrylate Butadiene Styrene), 5-15% of TiO2, 0.2-0.4% of antioxidant, 0.1-0.3% of anti-drip agent, 0.3-0.5% of plasticizer and 0.5-1% of lubricant. The PC material with the component proportion can achieve high-reflection and high-light-resistance effects, and is high in glossiness, high in mobility and good in toughness.
Description
Technical field
The present invention relates to PC plastics technology field, relate in particular to a kind of PC material.
Background technology
In prior art, the white cover material of light guiding plate blank, LED lamp holder, charger case or other electronic apparatus accessories generally adopt ABS or ABS and PC mixing material to be prepared from; Yet the ABS that the white cover material of existing light guiding plate blank, LED lamp holder, charger case or other electronic apparatus accessories adopt or ABS and the reflection of PC mixing material ubiquity hinder light efficiency rate variance, low in glossiness, weathering resistance is not good and the defect of poor toughness.
Summary of the invention
The object of the invention is to provides a kind of PC material for the deficiencies in the prior art, and this PC material can reach high reflection high resistance light effect, and glossiness is high, mobility is high, toughness is good.
For achieving the above object, the present invention is achieved through the following technical solutions.
A kind of PC material, include the component of following weight part, is specially:
PC resin 77.8%-90.9%
MBS 3%-5%
TiO
2 5%-15%
Antioxidant 0.2%-0.4%
Anti-dripping agent 0.1%-0.3%
Softening agent 0.3%-0.5%
Lubricant 0.5%-1%.
Further, this PC material includes the component of following weight part, is specially:
PC resin 84%
MBS 4%
TiO
2 10.3%
Antioxidant 0.3%
Anti-dripping agent 0.2%
Softening agent 0.4%
Lubricant 0.8%.
Wherein, described antioxidant is phenol antioxidant 1010, phosphorous acid esters antioxidant 168 or phosphorous acid esters antioxidant 627A.
Wherein, described anti-dripping agent is tetrafluoroethylene class anti-dripping agent.
Wherein, described softening agent is phthalic ester plasticizer, phosphate plasticizer or polyalcohol ester plasticizer.
Wherein, described lubricant is fatty acid amide lubricant or dimethyl silicone oil.
Beneficial effect of the present invention is: a kind of PC material of the present invention, the component that it includes following weight part is specially: PC resin 77.8%-90.9%, MBS3%-5%, TiO
25%-15%, antioxidant 0.2%-0.4%, anti-dripping agent 0.1%-0.3%, softening agent 0.3%-0.5%, lubricant 0.5%-1%.PC with above component proportion can reach the effect of high reflection high resistance light, and glossiness is high, mobility is high, toughness is good.
Embodiment
Below in conjunction with concrete embodiment, the present invention will be described.
Embodiment mono-, a kind of PC material, and the component that it includes following weight part is specially:
PC resin 84%
MBS 4%
TiO
2 10.3%
Antioxidant 0.3%
Anti-dripping agent 0.2%
Softening agent 0.4%
Lubricant 0.8%.
Wherein, the hud typed impact modifier that MBS is a kind of copolymerization MBS, antioxidant is phenol antioxidant 1010, phosphorous acid esters antioxidant 168 or phosphorous acid esters antioxidant 627A etc.; Anti-dripping agent is tetrafluoroethylene class anti-dripping agent etc.; Softening agent is phthalic ester plasticizer, phosphate plasticizer or polyalcohol ester plasticizer etc.; Lubricant is fatty acid amide lubricant or dimethyl-silicon wet goods.
PC with above component proportion can reach the effect of high reflection high resistance light, and glossiness is high, mobility is high, toughness is good.
Embodiment bis-, a kind of PC material, and the component that it includes following weight part is specially:
PC resin 87%
MBS 3%
TiO
2 8%
Antioxidant 0.4%
Anti-dripping agent 0.1%
Softening agent 0.5%
Lubricant 1%.
Wherein, the hud typed impact modifier that MBS is a kind of copolymerization MBS, antioxidant is phenol antioxidant 1010, phosphorous acid esters antioxidant 168 or phosphorous acid esters antioxidant 627A etc.; Anti-dripping agent is tetrafluoroethylene class anti-dripping agent etc.; Softening agent is phthalic ester plasticizer, phosphate plasticizer or polyalcohol ester plasticizer etc.; Lubricant is fatty acid amide lubricant or dimethyl-silicon wet goods.
PC with above component proportion can reach the effect of high reflection high resistance light, and glossiness is high, mobility is high, toughness is good.
Embodiment tri-, a kind of PC material, and the component that it includes following weight part is specially:
PC resin 90%
MBS 3%
TiO
2 5.5%
Antioxidant 0.3%
Anti-dripping agent 0.2%
Softening agent 0.3%
Lubricant 0.7%.
Wherein, the hud typed impact modifier that MBS is a kind of copolymerization MBS, antioxidant is phenol antioxidant 1010, phosphorous acid esters antioxidant 168 or phosphorous acid esters antioxidant 627A etc.; Anti-dripping agent is tetrafluoroethylene class anti-dripping agent etc.; Softening agent is phthalic ester plasticizer, phosphate plasticizer or polyalcohol ester plasticizer etc.; Lubricant is fatty acid amide lubricant or dimethyl-silicon wet goods.
PC with above component proportion can reach the effect of high reflection high resistance light, and glossiness is high, mobility is high, toughness is good.
Above content is only preferred embodiment of the present invention, for those of ordinary skill in the art, according to thought of the present invention, all will change in specific embodiments and applications, and this description should not be construed as limitation of the present invention.
Claims (6)
1. a PC material, is characterized in that, includes the component of following weight part, is specially:
PC resin 77.8%-90.9%
MBS 3%-5%
TiO
2 5%-15%
Antioxidant 0.2%-0.4%
Anti-dripping agent 0.1%-0.3%
Softening agent 0.3%-0.5%
Lubricant 0.5%-1%.
2. a kind of PC material according to claim 1, is characterized in that, includes the component of following weight part, is specially:
PC resin 84%
MBS 4%
TiO
2 10.3%
Antioxidant 0.3%
Anti-dripping agent 0.2%
Softening agent 0.4%
Lubricant 0.8%.
3. a kind of PC material according to claim 2, it is characterized in that: described antioxidant is phenol antioxidant 1010, phosphorous acid esters antioxidant 168 or phosphorous acid esters antioxidant 627A.
4. a kind of PC material according to claim 3, it is characterized in that: described anti-dripping agent is tetrafluoroethylene class anti-dripping agent.
5. a kind of PC material according to claim 4, it is characterized in that: described softening agent is phthalic ester plasticizer, phosphate plasticizer or polyalcohol ester plasticizer.
6. a kind of PC material according to claim 5, it is characterized in that: described lubricant is fatty acid amide lubricant or dimethyl silicone oil.