CN103422024B - A kind of chromium manganese nitrogen Alloy And Preparation Method - Google Patents
A kind of chromium manganese nitrogen Alloy And Preparation Method Download PDFInfo
- Publication number
- CN103422024B CN103422024B CN201310179016.9A CN201310179016A CN103422024B CN 103422024 B CN103422024 B CN 103422024B CN 201310179016 A CN201310179016 A CN 201310179016A CN 103422024 B CN103422024 B CN 103422024B
- Authority
- CN
- China
- Prior art keywords
- chromium
- nitrogen
- manganese
- alloy
- nitrogen alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of chromium manganese nitrogen alloy, be made up of the following material according to weight percent meter: chromium 2-6%, manganese 3-5%, nitrogen 0.8-1.2%, carbon 0.6-2%, silicon 0.3-0.7%, all the other are iron.Beneficial effect of the present invention is: chromium manganese nitrogen alloy provided by the invention, can effectively increase alloy toughness, with liquid nitrogen fast cooling, decrease alloy hole, be more applicable for aerospace field.
Description
Technical field
The present invention relates to alloy field, be specifically related to a kind of chromium manganese nitrogen alloy.
Background technology
Chromium manganese nitrogen alloy, is emerging a kind of alloy in this year, is mainly used in aerospace field, has hardness high, the features such as corrosion-resistant and high-temperature resistant.But the general lacking toughness of chromium manganese nitrogen alloy in the past, in use, easily ruptures.
Summary of the invention
Object of the present invention is exactly for above-mentioned defect of the prior art, provides not easy fracture, the chromium manganese nitrogen alloy that toughness is high.
To achieve these goals, technical scheme provided by the invention is: a kind of chromium manganese nitrogen alloy, be made up of the following material according to weight percent meter: chromium 2-6%, manganese 3-5%, nitrogen 0.8-1.2%, carbon 0.6-2%, silicon 0.3-0.7%, all the other are iron.
Further, above-mentioned a kind of chromium manganese nitrogen alloy, be made up of the following material according to weight percent meter: chromium 4%, manganese 4%, nitrogen 1%, carbon 1.2%, silicon 0.5%, all the other are iron.
Second object of the present invention there is provided the preparation method of above-mentioned chromium manganese nitrogen alloy, is by roll forming after each metallics melting, then with liquid nitrogen cooling.
Beneficial effect of the present invention is: chromium manganese nitrogen alloy provided by the invention, can effectively increase alloy toughness, with liquid nitrogen fast cooling, decrease alloy hole, be more applicable for aerospace field.
Embodiment
embodiment 1:
A kind of chromium manganese nitrogen alloy, be made up of the following material according to weight percent meter: chromium 2%, manganese 3%, nitrogen 0.8%, carbon 0.6%, silicon 0.3%, all the other are iron, and preparation method is by roll forming after each metallics melting, then with liquid nitrogen cooling.
embodiment 2:
A kind of chromium manganese nitrogen alloy, be made up of the following material according to weight percent meter: chromium 6%, manganese 5%, nitrogen 1.2%, carbon 2%, silicon 0.7%, all the other are iron, and preparation method is by roll forming after each metallics melting, then with liquid nitrogen cooling.
embodiment 3:
A kind of chromium manganese nitrogen alloy, be made up of the following material according to weight percent meter: chromium 4%, manganese 4%, nitrogen 1%, carbon 1.2%, silicon 0.5%, all the other are iron, and preparation method is by roll forming after each metallics melting, then with liquid nitrogen cooling.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. a chromium manganese nitrogen alloy, is characterized in that, is made up of: chromium 2-6%, manganese 3-5%, nitrogen 0.8-1.2%, carbon 0.6-2%, silicon 0.3-0.7% the following material according to weight percent meter, and all the other are iron.
2. a kind of chromium manganese nitrogen alloy according to claim 1, it is characterized in that, be made up of the following material according to weight percent meter: chromium 4%, manganese 4%, nitrogen 1%, carbon 1.2%, silicon 0.5%, all the other are iron.
3. the preparation method of a kind of chromium manganese nitrogen alloy according to claim 1 and 2, is characterized in that, is by roll forming after each metallics melting, then with liquid nitrogen cooling.