CN103413491A - Discoloring anodized-aluminum adhesive sticker anti-counterfeiting paste manufacture method - Google Patents
Discoloring anodized-aluminum adhesive sticker anti-counterfeiting paste manufacture method Download PDFInfo
- Publication number
- CN103413491A CN103413491A CN2013103840321A CN201310384032A CN103413491A CN 103413491 A CN103413491 A CN 103413491A CN 2013103840321 A CN2013103840321 A CN 2013103840321A CN 201310384032 A CN201310384032 A CN 201310384032A CN 103413491 A CN103413491 A CN 103413491A
- Authority
- CN
- China
- Prior art keywords
- layer
- adhesive sticker
- aluminium
- discoloring
- variable color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a discoloring anodized-aluminum adhesive sticker anti-counterfeiting paste manufacture method. A discoloring layer is overlapped on a plastic polyester film base layer. Connecting materials containing photosensitive materials are evenly mixed and processed to form a sticky coating, the sticky coating is evenly printed and coated on the surface of the film base layer through an anilox roller and baked and dried through a five-section type drying oven so as to improve the brightness and plumpness of products, and color inversion occurs under the irradiation of ultraviolet light and sunlight. A holographic anti-counterfeiting mould pressing layer is overlapped on the discoloring layer. A laser-printing information layer passes through a roller wrapped with laser engraving laser printing plate and forms invisible laser printing patterns and information serving as anti-counterfeiting graphics and text information at the 150 DEG C surface temperature and under the 30pa pressure. A printing layer is overlapped. A vacuum aluminium plating layer is overlapped on the printing layer. A gum application layer is overlapped. Finally, slitting and rewinding are performed. A discoloring anodized-aluminum adhesive sticker anti-counterfeiting paste manufactured by means of the method has the original characteristics of high gloss and high brightness and the discoloring characteristic, has an anti-counterfeiting function and is not easily counterfeited.
Description
Technical field
The present invention relates to pressure sensitive adhesive, be specifically related to a kind of method for making of anodized aluminium adhesive sticker anti-fake card of changeable colour.
Background technology
The surface of at present comparatively general anodized aluminium adhesive sticker anti-fake card only has false proof word and pattern, and color is also more single, and does not possess colour change function.
In view of this, anodized aluminium adhesive sticker anti-fake card of seeking a kind of changeable colour and preparation method thereof becomes pursuing a goal of these those skilled in the art.
Summary of the invention
Task of the present invention is to provide a kind of variable color anodized aluminium adhesive sticker anti-fake card method for making, it has solved the existing problem of above-mentioned prior art, after making, has colour change function, when having special light or ultra violet lamp rear surface word and pattern can produce change color, the variation of color perhaps also can occur at the temperature of appointment, possessed thus antiforge function.
Technical solution of the present invention is as follows:
A kind of variable color anodized aluminium adhesive sticker anti-fake card method for making, the plastics mylar of take is basic unit, comprises the following steps:
(1) photochromic layer that superposes in basic unit: the binder that will contain photosensitive material mixes, be processed into adherent coatings, by anilox printing, be coated with and be coated in equably the base film layer surface, and dry by the baking of five-part form baking oven, to increase luminance brightness and the plumpness of product, and color produces inversion under ultraviolet light and solar radiation;
(2) stack holographic false proof embossed plies on photochromic layer: laser information layer, through being wrapped in the cylinder of laser engraving laser plate, is formed to visual laser pattern and information, as Antiforge information under the surface temperatures of 150 ℃ and 30pa pressure;
(3) printed layers that superposes on the holographic false proof embossed plies: stencil machine at coating surface printing word and pattern by intaglio process, wherein should regulate scraper, adjust impression cylinder, and control baking temperature;
(4) vacuum aluminium coated layer that superposes on printed layers: evaporation boat is heated to 1400 ℃-1500 ℃, deliver to continuously the cold aluminium steam that changes into of high-purity aluminium wire on evaporation boat, the aluminium molecule is sprayed on surface equably, forms aluminum membranous layer, so that product sets off out metallic luster;
(5) gum layer that superposes on vacuum aluminium coated layer: the soft or hard resin is added to auxiliary agent and powder filler is prepared, then thermoprint is on the vacuum aluminium coated layer surface;
Last cutting and rewinding.
In described step (1), the temperature sequence of five-part form baking oven is 110 ℃-120 ℃-130 ℃-140 ℃-150 ℃, and pressure is 20pa, and the speed of a motor vehicle is 120m/min.
Viscosity size according to coating in described step (1) is added thinning agent, and this thinning agent is quick-dry type solvent and slow curing type solvent, needs mix and match to use.
While in described step (3), regulating scraper, scraper scrapes off the required pressure of forme surface ink and print speed printing speed is directly proportional, and general speed is fast, and pressure is corresponding wants large, and the angle of scraper and forme is 30 °-70 °.
While in described step (3), adjusting impression cylinder, squeegee pressure is controlled at 1pa-5pa.
While regulating the ink setting temperature in described step (3), baking temperature is controlled between 80 ℃-90 ℃, the highlyest is no more than 100 ℃.
In described step (4), the thickness of vacuum aluminium coated layer is 2-5 μ m.
In described step (5) by the thermoprint of soft or hard resin on the vacuum aluminium coated layer surface, blocking point is 100 ℃-110 ℃, the speed of a motor vehicle is 100m/min, anilox roll is 40R or 60R, coating weight is 3.50-4.0g/m
2.
The color of traditional common anodized aluminium adhesive sticker anti-fake card is allocated by common dye, and changeable colour anodized aluminium adhesive sticker anti-fake card of the present invention is to substitute common pigments with sensitization or temperature-sensitive material; By the electron transfer type organic compound, prepared by this reversible sensitization discoloration pigment, itself is a kind of organic color development system with special chemical structure, under specific illumination or through temperature variation, cause that the electronics transfer changes this organic molecule structure, thereby realize color transition; This electrochromic substance is not only bright-colored, and can realize the change color of " from coloured to colourless " and " from colourless to coloured ", and this is that common anodized aluminium adhesive sticker anti-fake card is not available.
By variable color anodized aluminium adhesive sticker anti-fake card method for making of the present invention, improved traditional common anodized aluminium adhesive sticker anti-fake card manufacturing technology, pressure sensitive adhesive and electron transfer type combination of organic compounds are integral, form novel changeable colour anodized aluminium adhesive sticker anti-fake card.Variable color anodized aluminium adhesive sticker anti-fake card of the present invention not only has the function of common anti-fake card, characteristics with original high glaze high brightness, and have the characteristics of changeable colour, under the UV-irradiation of specific wavelength or under the temperature conditions in appointment, change color can occur; By a series of change color, improved the class of product, also made product have certain antiforge function and be difficult for by counterfeit.
Changeable colour anodized aluminium adhesive sticker anti-fake card of the present invention can be widely used in the packing box of all kinds of cosmetics, commodity, cigarette, wine and food etc.
Embodiment
Below in conjunction with embodiment, the present invention is elaborated.
A kind of variable color anodized aluminium adhesive sticker anti-fake card method for making of the present invention comprises the following steps:
(1) photochromic layer that superposes in basic unit, also claim dyed layer: the binder that will contain photosensitive material mixes, be processed into adherent coatings, by anilox printing, be coated with and be coated in equably the base film layer surface, and dry by the baking of five-part form baking oven, to increase luminance brightness and the plumpness of product, and color produces inversion under ultraviolet light and solar radiation.Wherein the temperature sequence of five-part form baking oven is 110 ℃-120 ℃-130 ℃-140 ℃-150 ℃, and pressure is 20pa, and the speed of a motor vehicle is 120m/min.
In this step, should fully take into account the compatibility of photosensitive material and binder, the viscosity size of solution, can add thinning agent according to the viscosity size of coating, this thinning agent is quick-dry type solvent and slow curing type solvent, need mix and match to use, otherwise when coating, can affect levelability and the color effects of coating surface.The solvent of this class coating is high, and solid content is low, so viscosity is generally lower, and rate of drying is slow, so baking temperature is higher, otherwise can cause the not dry viscosity on the contrary of coating.
(2) stack holographic false proof embossed plies on photochromic layer: laser information layer, through being wrapped in the cylinder of laser engraving laser plate, is formed to visual laser pattern and information, as Antiforge information under the surface temperatures of 150 ℃ and 30pa pressure.
(3) printed layers that superposes on the holographic false proof embossed plies: stencil machine at coating surface printing word and pattern by intaglio process.Wherein: regulate scraper, scraper scrapes off the required pressure of forme surface ink and print speed printing speed is directly proportional, and general speed is fast, and pressure is corresponding wants large; The angle of scraper and forme is 30 °-70 °.Adjust impression cylinder, squeegee pressure is controlled at 1pa-5pa.Regulate the ink setting temperature: baking temperature is controlled between 80 ℃-90 ℃, the highlyest is no more than 100 ℃.
(4) vacuum aluminium coated layer that superposes on printed layers: evaporation boat is heated to 1400 ℃-1500 ℃, deliver to continuously the cold aluminium steam that changes into of high-purity aluminium wire on evaporation boat, the aluminium molecule is sprayed on surface equably, forms aluminum membranous layer, so that product sets off out metallic luster.The thickness of vacuum aluminium coated layer is generally 2-5 μ m.
(5) gum layer that superposes on vacuum aluminium coated layer: the soft or hard resin is added to auxiliary agent and powder filler is prepared, then thermoprint is on the vacuum aluminium coated layer surface.When vacuum aluminium coated layer was surperficial, blocking point was 100 ℃-110 ℃ by the thermoprint of soft or hard resin, and the speed of a motor vehicle is 100m/min, and anilox roll is 40R or 60R, and coating weight is 3.50-4.0g/m
2.
Last cutting and rewinding.
By variable color anodized aluminium adhesive sticker anti-fake card method for making of the present invention, all technological processes on base film layer plastics mylar by being layering.
Ground floor---photochromic layer (painted) layer, effect: increase luminance brightness and the plumpness of product, and color produces inversion under ultraviolet light and solar radiation.Manufacture craft is as follows:
Photosensitive material and corresponding binder are mixed, be processed into the coating of modest viscosity, be coated with and be coated in equably the base film layer surface by anilox printing, and dry by the baking of five-part form baking oven.The temperature sequence of five-part form baking oven is 110 ℃-120 ℃-130 ℃-140 ℃-150 ℃, and pressure is 20pa, and the speed of a motor vehicle is 120m/min.
In manufacturing process, fully take into account the compatibility of photoactive substance and binder; The viscosity size of solution; Select simultaneously thinning agent, quick-dry type and the collocation of slow curing type solvent to use, otherwise when coating, can affect levelability and the color effects of coating surface.The solvent of this class coating is high, and solid content is low, so viscosity is generally lower, and rate of drying is slow, so baking temperature is higher, otherwise can cause the not dry viscosity on the contrary of coating.
Because the dyed layer transparency is higher, after printing, coating surface need to cover aluminium coated, and the own gloss of the gloss of aluminium lamination and coating mutually combines and reflects comparatively gay colours.Dyed layer make and the formula Design process in to fully take into account form and aspect, the transparency of coating, volatility and the peel strength of solvent, so just can obtain gratifying effect.
The second layer---holographic false proof embossed plies, effect: produce a kind of visual Antiforge information at product surface by laser holograph plate-making technology and moulding replication technology.Manufacture craft: laser information layer, through being wrapped in the cylinder of laser engraving laser plate, is formed to visual laser pattern and information under the surface temperatures of 150 ℃ and 30pa pressure.
The 3rd layer---printed layers, effect: stencil machine by intaglio process and print out word and the pattern of various finenesses at coating surface, require word and clear patterns, bright-coloured.Manufacture craft is as follows:
The adjusting of scraper: scraper scrapes off the required pressure of forme surface ink and print speed printing speed is directly proportional.General speed is fast, and pressure is corresponding wants large.The angle of scraper and forme is 30 °-70 °, can keep like this scraper edge not hinder the space of a whole page, also can make the product quality of printing off comparatively desirable.
Adjust impression cylinder: because base material is plastic sheeting, it is comparatively desirable that squeegee pressure is controlled at 1pa-5pa.
The adjusting of ink setting temperature: select solvent type ink, will be according to the size of actual print speed printing speed, picture and text area, the baking temperature that ink film thickness is adjusted each unit when printing.Baking temperature is unsuitable too high, and general control is between 80 ℃-90 ℃, the highest over 100 ℃, otherwise can cause the drawdown deformation of plastic basis material, affects the accuracy of coating; The too low ink setting of baking temperature is bad.
The 4th layer---vacuum aluminium coated layer, effect: make product set off out metallic luster.Manufacture craft: evaporation boat is heated to 1400 ℃ of-1500 ℃ of left and right, delivers to continuously the cold aluminium steam that changes into of high-purity aluminium wire on evaporation boat, the aluminium molecule is sprayed on surface equably, forms the aluminum membranous layer as mirror.Aluminum layer thickness is generally 2-5 μ m.
Layer 5---gum layer, effect: be coated with the anodized aluminium of this tackifier, both can thermoprint at material surface, while needing, can wipe off from material surface is complete again.Its manufacture craft is:
Formula Design: select the soft or hard resin of property, add auxiliary agent and powder filler, add the solvent preparation.Taken into account the diversity of thermoprint, can increase again and be scalded the adhesive fastness between the thing surface.
Production technology: temperature is 100 ℃-110 ℃; The speed of a motor vehicle is 100m/min; Anilox roll is 40R or 60R; Coating weight is 3.50-4.0g/m
2.
Adapt to the thermoprint material: be applicable to various paperboard classes and the surface thermoprints of overlay film class such as smooth smooth hard PVC paperboard, copper coin paperboard, offset printing pattern paperboard, UV gloss oil paperboard.
Blocking point: 100 ℃-110 ℃.
By variable color anodized aluminium adhesive sticker anti-fake card method for making of the present invention, photoactive substance and corresponding binder are mixed, through manufacturing the coating of modest viscosity, by anilox printing, be coated with and be coated in equably the base film layer surface, and dry by the baking of five-part form baking oven.In manufacturing process, fully take into account the compatibility of photoactive substance and binder, the viscosity size of solution, select thinning agent simultaneously, quick-dry type and the collocation of slow curing type solvent to use, otherwise when coating, can affect levelability and the color effects of coating surface.The solvent of this class coating is high, and solid content is low, so viscosity is generally lower, and rate of drying is slow, so baking temperature is higher, otherwise can cause the not dry viscosity on the contrary of coating.Because the photochromic layer transparency is higher, after printing, coating surface need to cover aluminium coated, and the own gloss of the gloss of aluminium lamination and coating mutually combines and reflects comparatively gay colours.In a word, photochromic layer make and the formula Design process in to fully take into account form and aspect, the transparency of coating, volatility and the peel strength of solvent, so just can obtain gratifying effect.
In sum, variable color anodized aluminium adhesive sticker anti-fake card of the present invention not only has the characteristics of original high glaze high brightness, and has the characteristics of changeable colour, under the UV-irradiation of specific wavelength or under the temperature conditions in appointment, change color can occur; By a series of change color, improved the class of product, also made product have certain antiforge function and be difficult for by counterfeit.
Certainly, those skilled in the art in the art will be appreciated that, above-described embodiment is only that the present invention is described, and not as limitation of the invention, as long as in connotation scope of the present invention, all will drop in the scope of the claims in the present invention the variation of above-described embodiment, modification etc.
Claims (8)
1. variable color anodized aluminium adhesive sticker anti-fake card method for making, the plastics mylar of take is basic unit, it is characterized in that, comprises the following steps:
(1) photochromic layer that superposes in basic unit: the binder that will contain photosensitive material mixes, be processed into adherent coatings, by anilox printing, be coated with and be coated in equably the base film layer surface, and dry by the baking of five-part form baking oven, to increase luminance brightness and the plumpness of product, and color produces inversion under ultraviolet light and solar radiation;
(2) stack holographic false proof embossed plies on photochromic layer: laser information layer, through being wrapped in the cylinder of laser engraving laser plate, is formed to visual laser pattern and information, as Antiforge information under the surface temperatures of 150 ℃ and 30pa pressure;
(3) printed layers that superposes on the holographic false proof embossed plies: stencil machine at coating surface printing word and pattern by intaglio process, wherein should regulate scraper, adjust impression cylinder, and control baking temperature;
(4) vacuum aluminium coated layer that superposes on printed layers: evaporation boat is heated to 1400 ℃-1500 ℃, deliver to continuously the cold aluminium steam that changes into of high-purity aluminium wire on evaporation boat, the aluminium molecule is sprayed on surface equably, forms aluminum membranous layer, so that product sets off out metallic luster;
(5) gum layer that superposes on vacuum aluminium coated layer: the soft or hard resin is added to auxiliary agent and powder filler is prepared, then thermoprint is on the vacuum aluminium coated layer surface;
Last cutting and rewinding.
2. variable color anodized aluminium adhesive sticker anti-fake card method for making according to claim 1, it is characterized in that: in described step (1), the temperature sequence of five-part form baking oven is 110 ℃-120 ℃-130 ℃-140 ℃-150 ℃, pressure is 20pa, and the speed of a motor vehicle is 120m/min.
3. variable color anodized aluminium adhesive sticker anti-fake card method for making according to claim 1 is characterized in that: the viscosity size according to coating in described step (1) is added thinning agent, and this thinning agent is quick-dry type solvent and slow curing type solvent, needs mix and match to use.
4. variable color anodized aluminium adhesive sticker anti-fake card method for making according to claim 1, it is characterized in that: while in described step (3), regulating scraper, scraper scrapes off the required pressure of forme surface ink and print speed printing speed is directly proportional, general speed is fast, pressure is corresponding wants large, and the angle of scraper and forme is 30 °-70 °.
5. variable color anodized aluminium adhesive sticker anti-fake card method for making according to claim 1 is characterized in that: while in described step (3), adjusting impression cylinder, squeegee pressure is controlled at 1pa-5pa.
6. variable color anodized aluminium adhesive sticker anti-fake card method for making according to claim 1 is characterized in that: while in described step (3), regulating the ink setting temperature, baking temperature is controlled between 80 ℃-90 ℃, the highlyest is no more than 100 ℃.
7. variable color anodized aluminium adhesive sticker anti-fake card method for making according to claim 1 is characterized in that: in described step (4), the thickness of vacuum aluminium coated layer is 2-5 μ m.
8. variable color anodized aluminium adhesive sticker anti-fake card method for making according to claim 1, it is characterized in that: in described step (5) by the thermoprint of soft or hard resin on the vacuum aluminium coated layer surface, blocking point is 100 ℃-110 ℃, the speed of a motor vehicle is 100m/min, anilox roll is 40R or 60R, and coating weight is 3.50-4.0g/m
2.