CN103333647A - Insulating adhesive - Google Patents
Insulating adhesive Download PDFInfo
- Publication number
- CN103333647A CN103333647A CN2013102607635A CN201310260763A CN103333647A CN 103333647 A CN103333647 A CN 103333647A CN 2013102607635 A CN2013102607635 A CN 2013102607635A CN 201310260763 A CN201310260763 A CN 201310260763A CN 103333647 A CN103333647 A CN 103333647A
- Authority
- CN
- China
- Prior art keywords
- insulating adhesive
- insulating
- acrylic resin
- present
- vinyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an insulating adhesive which comprises the following components in percentage by weight: 12-42% of acrylic resin, 10-20% of polyether glycol, 5-10% of dichloromethane, 25-35% of vinyl acetate, 0.5% of copolymerization catalyst, 0.5% of sodium hydrogen carbonate, 1-2% of toluene diisocynate and 16-20% of insulating compound. According to the above mode, the insulating adhesive provided by the invention has favorable adhesion property and good insulating property, and avoids the occurrence of potential safety hazards.
Description
Technical field
The present invention relates to the glue paste field, particularly relate to a kind of insulating adhesive.
Background technology
For a long time, can carry out combination by the mode of glue paste between the surface of variant production, the typical surface that combines by the glue paste mode comprises paper surface and paperboard surface.But, glue paste brand and of a great variety, of many uses, be difficult to select.
At present, the glue paste on the market, the viscosity deficiency comes off easily, and some glue paste does not reach the effect of insulation simultaneously, causes the generation of potential safety hazard.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of insulating adhesive, has good cementability, has good insulating property simultaneously, has avoided the generation of potential safety hazard.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of insulating adhesive is provided, and moiety and the weight ratio thereof of described insulating adhesive comprise:
Acrylic resin 12-42%
Polyether glycol 10-20%
Methylene dichloride 5-10%
Vinyl acetate between to for plastic 25-35%
Catalyst for copolymerization 0.5%
Sodium bicarbonate 0.5%
Toluene two different blue or green acid esters 1-2%
Insulating compound 16-20%.
In a preferred embodiment of the present invention, described acrylic resin is a kind of in methyl acrylate, ethyl propenoate, n-butyl acrylate or the n-BMA.
In a preferred embodiment of the present invention, described insulating compound adopts silica gel or rubber.
The invention has the beneficial effects as follows: insulating adhesive of the present invention, have good cementability, have good insulating property simultaneously, avoided the generation of potential safety hazard.
Embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
The invention provides a kind of insulating adhesive, moiety and the weight ratio thereof of described insulating adhesive comprise:
Acrylic resin 12-42%
Polyether glycol 10-20%
Methylene dichloride 5-10%
Vinyl acetate between to for plastic 25-35%
Catalyst for copolymerization 0.5%
Sodium bicarbonate 0.5%
Toluene two different blue or green acid esters 1-2%
Insulating compound 16-20%.
In above-mentioned, described acrylic resin is a kind of in methyl acrylate, ethyl propenoate, n-butyl acrylate or the n-BMA.
Thermosetting acrylic resin refers to have certain functional group in structure, the functional group reactions in the aminoresin that passes through when the system lacquer and add, Resins, epoxy, the urethane etc. forms reticulated structure, and the general relative molecular weight of thermosetting resin is lower.Thermosetting acrylic coating has excellent fullness ratio, gloss, hardness, solvent resistance, weathering resistance, nondiscoloration when high bake, brightness reversion not.Most important applications is to cooperate with aminoresin to make amino-vinylformic acid baking vanish, uses very extensive at products such as automobile, motorcycle, bike, coils at present.
Wherein, described insulating compound adopts silica gel or rubber, and silica gel is a kind of high reactivity sorbing material, belongs to amorphous substance, and its chemical molecular formula is mSiO2nH2O, and water insoluble and any solvent is nonpoisonous and tasteless, and chemical property is stable; Rubber has the snappiness polymer materials of reversible deformation.High resilience at room temperature can produce than large deformation under very little external force effect, removes resilient after the external force.Above-mentioned silica gel and rubber all have the good insulation performance effect.
Insulating adhesive provided by the invention has good cementability, has good insulating property simultaneously, has avoided the generation of potential safety hazard.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (3)
1. an insulating adhesive is characterized in that, moiety and the weight ratio thereof of described insulating adhesive comprise:
Acrylic resin 12-42%
Polyether glycol 10-20%
Methylene dichloride 5-10%
Vinyl acetate between to for plastic 25-35%
Catalyst for copolymerization 0.5%
Sodium bicarbonate 0.5%
Toluene two different blue or green acid esters 1-2%
Insulating compound 16-20%.
2. insulating adhesive according to claim 1 is characterized in that, described acrylic resin is a kind of in methyl acrylate, ethyl propenoate, n-butyl acrylate or the n-BMA.
3. insulating adhesive according to claim 1 is characterized in that, described insulating compound adopts silica gel or rubber.