CN103265252A - Attapulgite binder for light strips used for building walls - Google Patents
Attapulgite binder for light strips used for building walls Download PDFInfo
- Publication number
- CN103265252A CN103265252A CN2013101356023A CN201310135602A CN103265252A CN 103265252 A CN103265252 A CN 103265252A CN 2013101356023 A CN2013101356023 A CN 2013101356023A CN 201310135602 A CN201310135602 A CN 201310135602A CN 103265252 A CN103265252 A CN 103265252A
- Authority
- CN
- China
- Prior art keywords
- parts
- attapulgite
- powder
- binder
- binding agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an attapulgite binder for light strips used for building walls. The binder is composed of the following raw materials by weight parts: 120-150 parts of 32.5 rapid-hardening aluminum sulfate cement, 10-15 parts of copolymer rubber powder of styrene and butadiene, 100-150 parts of quartz sand, 4-6 parts of vegetable fibers, 3-5 parts of alum stone powder, 4-8 parts of limestone powder, 15-20 parts of instant powdered sodium silicate, 5-10 parts of dolomite powder, 10-15 parts of the attapulgite and 4-8 parts of slag powder. The attapulgite binder for the light strips used for the building walls is strong in bond strength, and can reduce layering and spalling, guarantee engineering quality, prevent problems of hollowing, cracking and other problems after a long-term use, and thus improve endurance. The binder provided by the invention is pre-mixed in a dry way, is stable in quality, can be added with a proper amount of water to stir for using, and thus is simple and convenient to construct. The binder effectively utilizes the slag powder and other waste materials, is free of poisonous and harmful additives, totally meets requirements of environmental protection, and is safe and non-polluted.
Description
Technical field
The present invention relates to a kind of material of construction binding agent, be specifically related to a kind of light lath for building partition wall attapulgite binding agent.
Background technology
Light lath for building partition wall is to be gelling material with the ordinary Portland cement, is main raw material with light-weight aggregates such as haydite, pearlstone, industrial residues, the porous air core type batten of producing by extrusion molding.Need a certain amount of binding agent to fix during its construction and installation.Shortcomings such as yet existing binding agent exists, and operating efficiency is low, cementability is poor, useful life longevity difference and poor stability have not satisfied the bonding requirement of light lath for building partition wall.Therefore, be badly in need of a kind of brand-new high performance light lath for building partition wall tackiness agent of research and development.
Summary of the invention
The objective of the invention is at the deficiencies in the prior art, provide that a kind of cohesive strength height, good endurance, construction are simple, the light lath for building partition wall attapulgite binding agent of safety non-toxic evil.
The technical solution used in the present invention is as follows:
A kind of light lath for building partition wall attapulgite binding agent, formed by the raw material of following weight part:
32.5 fast hard aluminum sulfate salt cement 120-150
Vinylbenzene and butadiene copolymer rubber powder 10-15
Quartz sand 100-150
Vegetable fibre 4-6
Alum stone flour 3-5
Limestone powder 4-8
Instant powdery sodium silicate 15-20
Ground dolomite 5-10
Attapulgite 10-15
Pulverized slag 4-8
Sodium lignosulfonate 1-2.
Preferably, a kind of light lath for building partition wall attapulgite binding agent, formed by the raw material of following weight part:
32.5 fast hard aluminum sulfate salt cement 120
Vinylbenzene and butadiene copolymer rubber powder 12
Quartz sand 140
Vegetable fibre 5
Alum stone flour 4
Limestone powder 6
Instant powdery sodium silicate 18
Ground dolomite 8
Attapulgite 10
Pulverized slag 6
Sodium lignosulfonate 1.5.
The above-mentioned raw materials dry mixing is even, and ball milling is crossed the 200-300 mesh sieve, and pack gets final product.
Beneficial effect of the present invention:
Light lath for building partition wall attapulgite binding agent cohesive force of the present invention is strong, and the chance that reduces layering and peel off ensures construction quality, avoids hollowing, problems of crack behind the life-time service, thus the raising weather resistance; Tackiness agent of the present invention dry mixing in advance mixes, steady quality, and the stirring that adds suitable quantity of water during use gets final product, and it is simple and convenient to construct; The present invention effectively utilizes waste materials such as pulverized slag, no poisonous and harmful additive, complete compliance with environmental protection requirements, safety non-pollution.
Embodiment
A kind of light lath for building partition wall attapulgite binding agent, formed by the raw material of following weight part (kilogram):
32.5 fast hard aluminum sulfate salt cement 120
Vinylbenzene and butadiene copolymer rubber powder 12
Quartz sand 140
Vegetable fibre 5
Alum stone flour 4
Limestone powder 6
Instant powdery sodium silicate 18
Ground dolomite 8
Attapulgite 10
Pulverized slag 6
Sodium lignosulfonate 1.5.
The above-mentioned raw materials dry mixing is even, and ball milling is crossed the 200-300 mesh sieve, and pack gets final product.
Binding agent Specifeca tion speeification of the present invention is as follows:
Tensile bond strength (Mpa): 1.1
Tensile bond strength after the immersion (Mpa): 0.9
Tensile bond strength after the thermal ageing (Mpa): 0.8
Tensile bond strength behind the freeze-thaw cycle (Mpa): 0.6.
Claims (3)
1. a light lath for building partition wall attapulgite binding agent is characterized in that, is made up of the raw material of following weight part:
32.5 fast hard aluminum sulfate salt cement 120-150
Vinylbenzene and butadiene copolymer rubber powder 10-15
Quartz sand 100-150
Vegetable fibre 4-6
Alum stone flour 3-5
Limestone powder 4-8
Instant powdery sodium silicate 15-20
Ground dolomite 5-10
Attapulgite 10-15
Pulverized slag 4-8
Sodium lignosulfonate 1-2.
2. a kind of light lath for building partition wall attapulgite binding agent according to claim 1 is characterized in that, is made up of the raw material of following weight part:
32.5 fast hard aluminum sulfate salt cement 120
Vinylbenzene and butadiene copolymer rubber powder 12
Quartz sand 140
Vegetable fibre 5
Alum stone flour 4
Limestone powder 6
Instant powdery sodium silicate 18
Ground dolomite 8
Attapulgite 10
Pulverized slag 6
Sodium lignosulfonate 1.5.
3. light lath for building partition wall attapulgite binding agent according to claim 1 is characterized in that the preparation method of described binding agent is as follows: the above-mentioned raw materials dry mixing is even, and ball milling is crossed the 200-300 mesh sieve, and pack gets final product.