CN103232229A - Ultra-wear-resistant alumina ceramic ball and preparation method thereof - Google Patents
Ultra-wear-resistant alumina ceramic ball and preparation method thereof Download PDFInfo
- Publication number
- CN103232229A CN103232229A CN2013101742786A CN201310174278A CN103232229A CN 103232229 A CN103232229 A CN 103232229A CN 2013101742786 A CN2013101742786 A CN 2013101742786A CN 201310174278 A CN201310174278 A CN 201310174278A CN 103232229 A CN103232229 A CN 103232229A
- Authority
- CN
- China
- Prior art keywords
- ball
- ceramic ball
- wear
- weight
- alumina ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides an ultra-wear-resistant alumina ceramic ball. The ultra-wear-resistant alumina ceramic ball comprises the following chemical components: 90-95% by weight of Al2O3, 5-8% by weight of SiO2, 0.3-0.5% by weight of CaO, 0.5-0.9% by weight of MgO, 1-2% by weight of ZrO and 0.1-0.5% by weight of La2O3/Y2O3, wherein the equivalent wear loss is less than 72 per mil. A provided preparation method comprises the following process steps of: adopting alumina powder and other mineral raw materials for burdening, refining mud, drying, calcining, synthesizing, ball-milling, granulating, forming and firing to obtain a product. According to the invention, the wear resistance of the product can achieve the standard of the alumina ceramic ball; and furthermore, the ultra-wear-resistant alumina ceramic ball has the advantages of lower cost of the raw materials, better grinding performance and high performance-price ratio of the product, is more suitable for being applied in production, and can reduce the production cost of an enterprise and improve the production efficiency of the enterprise.
Description
Technical field
The invention belongs to ceramic (pottery) field, be specifically related to super wear-resisting alumina ceramic ball with the aluminum oxide preparation and preparation method thereof.
Background technology
Ball mill is widely used in fields such as metallurgy, mineral products, electric power, building materials, chemical industry, is a kind of use disintegrating apparatus very widely.Grinding medium is the key of ball mill comminuting matter, and its shape is generally spheroid or right cylinder, relies on the motion of various complexity such as the rolling of grinding medium in ball mill, bump, extruding, friction, and material is pulverized.The quality of grinding medium not only directly has influence on the height of production efficiency, but also can have influence on the quality of quality product.Grinding medium is generally classified by density, can be divided into: the low density mill is situated between by (as the conventional ceramic ball, cherty silica and pebbles etc.), and proportion is about 2.3～2.6; Middle density mill is situated between (being situated between as high alumina matter mill), and proportion is about 2.6～3.2; The high-density mill is situated between in (as corundum, zirconium matter mill Jie etc.), and proportion is generally greater than 3.2.
Along with the developing rapidly of ceramic industry, on the one hand, high-grade natural ground dielectric material (pebbles and flint) resource is exhausted just day by day in recent years, and on the other hand, lithotome is in the requirement that can't satisfy growing high-tech product qualitatively.And artificial grinding medium has physical strength height, hardness height, density is big, high-temperature behavior good, pollution-free or pollute very little, advantages such as the acid-alkali-corrosive-resisting ability is strong, wear resisting property excellence to material, artificial grinding medium substitutes natural abrasive just gradually.The ceramic media of China market sale at present mainly comprises series of productss such as aluminum oxide, zirconium white, silicon carbide, silicon nitride.What wherein aluminum oxide and zirconium white used is the most extensive.The alumina-ceramic ball since have suitable hardness, moderate density, wear-resisting, corrosion-resistant, price is low, therefore being widely used in the raw-material grinding of industry and processing such as white cement, mineral, pottery, electronic material, magneticsubstance and coating, paint, makeup, food, pharmacy, is a kind of grinding medium of high-quality.Yet the alumina-ceramic ball mainly exists at present: wear away bigger, undercapacity, problems such as grinding efficiency is low, compare with the zirconia ceramics ball, zirconic intensity, fracture toughness property are two to three times of alumina-ceramic, the little hundreds of times of zirconic equivalent wear resistance ratio alumina balls, but zirconia ceramics ball cost of material is very high, production cost is high, and the price of market sale is very high, so it is very considerable to prepare the application prospect of low abrasion, high performance Ceramic Balls.Therefore, provide a kind of new alumina-ceramic ball product, significantly improve the main performance index of product, make its standard that meets or exceeds the zirconia ceramics ball have great innovative significance.
Summary of the invention
One of purpose of the present invention provides a kind of super wear-resisting alumina ceramic ball, its main performance index meets or exceeds the salient features standard of zirconia ceramics ball, second purpose of the present invention provides the preparation method of this super wear-resisting alumina ceramic ball, solves the bigger problem of existing alumina ball abrasion.
For solving the problems of the technologies described above, the present invention introduces a small amount of rare earth La by the alumina ball composition of raw materials is optimized
2O
3/ Y
2O
3, material such as TZP, make the chemical constitution of alumina-ceramic ball be: Al
2O
3: 90～95 wt%, SiO
2: 5～8 wt%, CaO:0.3～0.5 wt%, MgO:0.5～0.9 wt%, ZrO:1～2 wt%, La
2O
3/ Y
2O
3: 0.1～0.5 wt%.Through containing of sintering above-mentioned composition and the alumina-ceramic ball of content, its equivalent abrasion are less than 0.072 ‰.
The invention provides the preparation method of the alumina-ceramic ball that contains above-mentioned composition and content, comprise and adopt alumina powder and other raw mineral materials to prepare burden, composition of raw materials is: aluminum oxide powder 90～95 wt%, kaolin 4～8 wt%, talcum 0.5～0.9 wt%, TZP 1～2 wt%, rare earth 0.1～0.5 wt%;
Adopt following technology to be prepared:
One, pugging
1. raw mix and water are proportionally put into the ball mill ball milling, move 15～30 hours blowings;
2. after mud is gone into the pond, start stirrer, take out pulp grinder, filter through vibratory screening apparatus, flow into the deironing stock tank simultaneously;
3. behind the deironing stock tank, again by take out stock pump with slush pump to slip drying press, make slurry dewatering make mud cake;
Two, oven dry: the mud cake of making is sent into drying room under 40～60 ℃, dry to moisture 3%;
Three, calcining is synthetic: the mud cake of oven dry is sent into kiln calcine synthetic at 1450～1550 ℃;
Four, ball milling: will calcine synthetic work in-process and put into ball mill again and grind;
Five, granulation: will send into through the slurry after grinding and carry out granulation in the mist projection granulating tower;
Six, moulding: will carry out moulding through mist projection granulating tower granulation powder, the forming method that applies among the present invention mainly contains rolling moulding and isostatic pressing;
Seven, burn till: the work in-process after the moulding are put into saggar, enter in the kiln, through after 2 hours, namely firing success 1450～1600 ℃ of insulations.
The present invention adopts industrial raw material, and raw material sources are all very wide.Compared with prior art, the present invention has following beneficial effect: the equivalent abrasion for existing alumina-ceramic ball are 0.1 ‰; The abrasion of the zirconic equivalent of optimal grinding medium are 0.072 ‰, yet the equivalent that alumina-ceramic ball of the present invention reaches abrasion are 0.062 ‰, and are obviously more superior than the abrasion of existing alumina-ceramic ball, also little than zirconia ceramics ball.The price of zirconia ceramics ball is than high tens of times of the super wear-resistant ceramic ball of the present invention preparation, so invention has very high value and creates meaning.
The embodiment of concrete formulation optimization:
Embodiment 1: aluminum oxide powder 90 %, and kaolin 7%, talcum 0.7%, TZP 2%, rare earth (La
2O
3/ Y
2O
3) 0.3%
One, pugging
1. raw mix and water are proportionally put into the ball mill ball milling, move 20 hours blowings;
2. after mud is gone into the pond, start stirrer, take out pulp grinder, filter through vibratory screening apparatus, flow into the deironing stock tank simultaneously;
3. behind the deironing stock tank, again by take out stock pump with slush pump to slip drying press, make slurry dewatering make mud cake;
Two, oven dry: the mud cake of making is sent into drying room under 45 ℃, dry to moisture 3%;
Three, calcining is synthetic: the mud cake of oven dry is sent into kiln calcine synthetic at 1450 ℃;
Four, ball milling: will calcine synthetic work in-process and put into ball mill again and grind;
Five, granulation: will send into through the slurry after grinding and carry out granulation in the mist projection granulating tower;
Six, moulding: static pressure such as mist projection granulating tower granulation powder employing are carried out moulding;
Seven, burn till: the work in-process after the moulding are put into saggar, enter in the kiln, through 1550 ℃ of insulations 2 hours, namely fire success.
Embodiment 2: aluminum oxide powder 92 %, and kaolin 6 %, talcum 0.5 %, TZP 1.2%, rare earth (La
2O
3/ Y
2O
3) 0.3 %
One, pugging
1. raw mix and water are proportionally put into the ball mill ball milling, move 22 hours blowings;
2. after mud is gone into the pond, start stirrer, take out pulp grinder, filter through vibratory screening apparatus, flow into the deironing stock tank simultaneously;
3. behind the deironing stock tank, again by take out stock pump with slush pump to slip drying press, make slurry dewatering make mud cake;
Two, oven dry: the mud cake of making is sent into drying room under 50 ℃, dry to moisture 3%;
Three, calcining is synthetic: the mud cake of oven dry is sent into kiln calcine synthetic at 1500 ℃;
Four, ball milling: will calcine synthetic work in-process and put into ball mill again and grind;
Five, granulation: will send into through the slurry after grinding and carry out granulation in the mist projection granulating tower;
Six, moulding: will carry out moulding through mist projection granulating tower granulation powder, the forming method that applies among the present invention mainly contains rolling moulding and isostatic pressing;
Seven, burn till: the work in-process after the moulding are put into saggar, enter in the kiln, through after 2 hours, namely firing success 1580 ℃ of insulations.
Embodiment 3: aluminum oxide powder 94 %, and kaolin 4 %, talcum 0.5 %, TZP 1.4%, rare earth (La
2O
3/ Y
2O
3) 0.1 %
One, pugging
1. raw mix and water are proportionally put into the ball mill ball milling, move 25 hours blowings;
2. after mud is gone into the pond, start stirrer, take out pulp grinder, filter through vibratory screening apparatus, flow into the deironing stock tank simultaneously;
3. behind the deironing stock tank, again by take out stock pump with slush pump to slip drying press, make slurry dewatering make mud cake;
Two, oven dry: the mud cake of making is sent into drying room under 48 ℃, dry to moisture 3%;
Three, calcining is synthetic: the mud cake of oven dry is sent into kiln calcine synthetic at 1550 ℃;
Four, ball milling: will calcine synthetic work in-process and put into ball mill again and grind;
Five, granulation: will send into through the slurry after grinding and carry out granulation in the mist projection granulating tower;
Six, moulding: will carry out moulding through mist projection granulating tower granulation powder, the forming method that applies among the present invention mainly contains rolling moulding and isostatic pressing;
Seven, burn till: the work in-process after the moulding are put into saggar, enter in the kiln, through after 2 hours, namely firing success 1600 ℃ of insulations.
According to the industrial ceramics industry standard, the super wear-resisting alumina ceramic ball of preparation is placed in the urethane jar with the defined terms impact grinding, the wear resisting property of examination alumina-ceramic ball, the wear resisting property test data values of alumina-ceramic ball sees the following form:
By The above results as can be known: adopting the equivalent abrasion of the best of the Ceramic Balls that this formulation goes out is 0.062 ‰, and the average equivalent abrasion of the Ceramic Balls of employing regular convention formula preparation are 0.15 ‰ on the market, improved 240% on year-on-year basis, so the alumina-ceramic ball of manufacturing of the present invention surmounts the alumina-ceramic ball of regular convention formula preparation in certain limit.And the abrasion of the equivalent of zirconium oxide abrasive medium are 0.072 ‰, Ceramic Balls of the present invention even surmounted the performance of zirconia ceramics ball, this invention can not only reduce enterprise's production cost, and mill efficiency is higher, prolong the work-ing life of alumina-ceramic ball, improved the production efficiency of enterprise.
Claims (2)
1. super wear-resisting alumina ceramic ball, it is characterized in that: the chemical constitution of alumina-ceramic ball is: Al
2O
3: 90～95 wt%, SiO
2: 5～8 wt%, CaO:0.3～0.5 wt%, MgO:0.5～0.9 wt%, ZrO:1～2 wt%, La
2O
3/ Y
2O
3: 0.1～0.5 wt%, the equivalent abrasion behind sintering are less than 0.072 ‰.
2. the preparation method of a super wear-resisting alumina ceramic ball comprises and adopts alumina powder and other raw mineral materials to prepare burden, and it is characterized in that composition of raw materials is: aluminum oxide powder 90～95 wt%, kaolin 4～8 wt%, talcum 0.5～0.9 wt%, TZP 1～2 wt%, rare earth La
2O
3/ Y
2O
30.1～0.5 wt%; Adopt following technology to be prepared:
One, pugging:
1. raw mix and water are proportionally put into the ball mill ball milling, move 15～30 hours blowings;
2. after mud is gone into the pond, start stirrer, take out pulp grinder, filter through vibratory screening apparatus, flow into the deironing stock tank simultaneously;
3. behind the deironing stock tank, again by take out stock pump with slush pump to slip drying press, make slurry dewatering make mud cake;
Two, oven dry: the mud cake of making is sent into drying room under 40～60 ℃, dry to moisture 3%;
Three, calcining is synthetic: the mud cake of oven dry is sent into kiln calcine synthetic at 1450～1550 ℃;
Four, ball milling: will calcine synthetic work in-process and put into ball mill again and grind;
Five, granulation: will send into through the slurry after grinding and carry out granulation in the mist projection granulating tower;
Six, moulding: will be through mist projection granulating tower granulation powder roll moulding or isostatic pressing;
Seven, burn till: the work in-process after the moulding are put into saggar, enter in the kiln, through at 1450～1600 ℃ of sintering, be incubated and obtain goods after 2 hours.