CN103132620A - Integrated closed-cell perlite insulation board - Google Patents
Integrated closed-cell perlite insulation board Download PDFInfo
- Publication number
- CN103132620A CN103132620A CN2013100726150A CN201310072615A CN103132620A CN 103132620 A CN103132620 A CN 103132620A CN 2013100726150 A CN2013100726150 A CN 2013100726150A CN 201310072615 A CN201310072615 A CN 201310072615A CN 103132620 A CN103132620 A CN 103132620A
- Authority
- CN
- China
- Prior art keywords
- parts
- side fascia
- raw material
- perlite
- pvc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An integrated closed-cell perlite insulation board is composed of an outer wallboard and a perlite layer according to the mass ratio of 100:1. The insulation board is manufactured by coating fluorocarbon paint on the manufactured outer wallboard, then coating bi-component polyurethane sealant on the outer wallboard, adhering the perlite on the outer wallboard, and pressing the perlite and the outer wallboard together through a pressing machine with 25Mpa pressure. Further, after being fused at the temperature of 80-100 DEG C, the insulation board is conveyed into a microwave drying channel 30 meters long through a conveying belt, and is finished. The integrated closed-cell perlite insulation board has functions of heat insulation and fire proofing and is safer to use, more convenient to mount, low in manufacturing cost and attractive in appearance and can be colorful, and the service life is greatly prolonged to more than 25 years.
Description
Technical field
The present invention relates to building material field, specifically relate to a kind of closed perlite integrated heat-preservation hanging plate.
Background technology
The warming plate of skin adopts the materials such as EPS plate, ASPS plate to make more at present, though this kind material can play insulation effect, but because it is all the lipid material, burning-point is low, can not play fireproofing function, can accelerate fire spreading when the building breaking out of fire, safety factor is not high, and this kind materials'use life-span is not high, the slag-off phenomenon of generally can fading after exterior wall arranges 3-5 years, the construction technology relative complex of its making, the cost cost is high.
Summary of the invention
The object of the invention is to overcome the deficiency of above-mentioned technology, provide a kind of can the fireproof warming plate, and long service life, cost of manufacture is cheap.
For achieving the above object, the technical solution used in the present invention is: a kind of closed perlite integrated heat-preservation hanging plate, it by side fascia and pearl rock stratum according to the 100:1 mass ratio in conjunction with forming, described side fascia is comprised of the raw material of following weight portion: 200 ~ 300 parts of pvc, 700 ~ 800 parts of calcium powders, 5 ~ 8 parts of stearic acid, 3 ~ 7 parts of dibutyl esters, CPE30 ~ 40 part, 3 ~ 7 parts, pe wax, 33 ~ 37 parts of pvc stabilizing agents, 9 ~ 11 parts of AC blowing agents, 20 ~ 30 parts of PVC foaming control agents; Described pearl rock stratum is comprised of the raw material of following weight portion: 120 ~ 180 parts of beads, 2.1 ~ 2.6 parts of hydrophober, 90 ~ 110 parts of water glass, 6 ~ 10 parts of silicon phosphates, 22 ~ 26 parts of calcium bicarbonates, 95 ~ 105 parts, water, 0.4 ~ 0.6 part of polypropylene, 1.2 ~ 1.8 parts of hydroxypropyl methylcelluloses.
The manufacture craft of described side fascia is above-mentioned side fascia raw material components to be taken raw material mix, and the temperature that controls environment makes the softening mixing of raw material at 185 ~ 220 degrees centigrade, by extruding machine, raw material is expressed into and carries out cooling forming in the condensation mould and get final product.
Described a kind of closed perlite integrated heat-preservation hanging plate manufacture craft is: coat fluorine carbon paint on the side fascia that makes, and then coat the dual-component polyurethane fluid sealant on side fascia, perlite is bonded on side fascia, and use 25Mpa pressure with perlite and the side fascia composition warming plate that forces together by press, and fuse through 80-100 degree celsius temperature, then warming plate is delivered into the microwave drying passage of 30 meters long by conveyer belt and dries, and get final product.
The raw material components of the better weight portion of side fascia of the present invention is: 250 parts of pvc, 750 parts of calcium powders, 7 parts of stearic acid, 5 parts of dibutyl esters, CPE35 part, 5 parts, pe wax, 35 parts of pvc stabilizing agents, 10 parts of AC blowing agents, 25 parts of PVC foaming control agents;
The raw material components of the better weight portion of pearl of the present invention rock stratum is: 150 parts of beads, 2.4 parts of hydrophober, 100 parts of water glass, 8 parts of silicon phosphates, 24 parts of calcium bicarbonates, 100 parts, water, 0.5 part of polypropylene, 1.5 parts of hydroxypropyl methylcelluloses.
Beneficial effect of the present invention is: also has fire-proof function in insulation, uses safelyr, and greatly increase application life, can reach more than 25 years, and easier for installation, and cost of manufacture is low, and good looking appearance can be made shades of colour.
The specific embodiment
The present invention will be further described below in conjunction with embodiment.
Embodiment 1
A kind of closed perlite integrated heat-preservation hanging plate, it by side fascia and pearl rock stratum according to the 100:1 mass ratio in conjunction with forming, described side fascia is comprised of the raw material of following weight portion: 200 parts of pvc, 700 parts of calcium powders, 5 parts of stearic acid, 3 parts of dibutyl esters, CPE30 part, 3 parts, pe wax, 33 parts of pvc stabilizing agents, 9 parts of AC blowing agents, 20 parts of PVC foaming control agents; Described pearl rock stratum is comprised of the raw material of following weight portion: 120 parts of beads, 2.1 parts of hydrophober, 90 parts of water glass, 6 parts of silicon phosphates, 22 parts of calcium bicarbonates, 95 parts, water, 0.4 part of polypropylene, 1.2 parts of hydroxypropyl methylcelluloses.
The manufacture craft of described side fascia is above-mentioned side fascia raw material components to be taken raw material mix, and the temperature that controls environment makes the softening mixing of raw material at 185 ~ 220 degrees centigrade, by extruding machine, raw material is expressed into and carries out cooling forming in the condensation mould and get final product.
Described a kind of closed perlite integrated heat-preservation hanging plate manufacture craft is: coat fluorine carbon paint on the side fascia that makes, and then coat the dual-component polyurethane fluid sealant on side fascia, perlite is bonded on side fascia, and use 25Mpa pressure with perlite and the side fascia composition warming plate that forces together by press, and fuse through 80-100 degree celsius temperature, then warming plate is delivered into the microwave drying passage of 30 meters long by conveyer belt and dries, and get final product.
Embodiment 2
A kind of closed perlite integrated heat-preservation hanging plate, it by side fascia and pearl rock stratum according to the 100:1 mass ratio in conjunction with forming, described side fascia is comprised of the raw material of following weight portion: 300 parts of pvc, 800 parts of calcium powders, 8 parts of stearic acid, 7 parts of dibutyl esters, CPE40 part, 7 parts, pe wax, 37 parts of pvc stabilizing agents, 11 parts of AC blowing agents, 30 parts of PVC foaming control agents; Described pearl rock stratum is comprised of the raw material of following weight portion: 180 parts of beads, 2.6 parts of hydrophober, 110 parts of water glass, 10 parts of silicon phosphates, 26 parts of calcium bicarbonates, 105 parts, water, 0.6 part of polypropylene, 1.8 parts of hydroxypropyl methylcelluloses.
Manufacture craft is with embodiment 1.
Embodiment 3
A kind of closed perlite integrated heat-preservation hanging plate, it by side fascia and pearl rock stratum according to the 100:1 mass ratio in conjunction with forming, described side fascia is comprised of the raw material of following weight portion: 250 parts of pvc, 750 parts of calcium powders, 7 parts of stearic acid, 5 parts of dibutyl esters, CPE35 part, 5 parts, pe wax, 35 parts of pvc stabilizing agents, 10 parts of AC blowing agents, 25 parts of PVC foaming control agents; Described pearl rock stratum is comprised of the raw material of following weight portion: 150 parts of beads, 2.4 parts of hydrophober, 100 parts of water glass, 8 parts of silicon phosphates, 24 parts of calcium bicarbonates, 100 parts, water, 0.5 part of polypropylene, 1.5 parts of hydroxypropyl methylcelluloses.
Claims (5)
1. closed perlite integrated heat-preservation hanging plate, it is characterized in that: it by side fascia and pearl rock stratum according to the 100:1 mass ratio in conjunction with forming, described side fascia is comprised of the raw material of following weight portion: 200 ~ 300 parts of pvc, 700 ~ 800 parts of calcium powders, 5 ~ 8 parts of stearic acid, 3 ~ 7 parts of dibutyl esters, CPE30 ~ 40 part, 3 ~ 7 parts, pe wax, 33 ~ 37 parts of pvc stabilizing agents, 9 ~ 11 parts of AC blowing agents, 20 ~ 30 parts of PVC foaming control agents; Described pearl rock stratum is comprised of the raw material of following weight portion: 120 ~ 180 parts of beads, 2.1 ~ 2.6 parts of hydrophober, 90 ~ 110 parts of water glass, 6 ~ 10 parts of silicon phosphates, 22 ~ 26 parts of calcium bicarbonates, 95 ~ 105 parts, water, 0.4 ~ 0.6 part of polypropylene, 1.2 ~ 1.8 parts of hydroxypropyl methylcelluloses.
2. a kind of closed perlite integrated heat-preservation hanging plate according to claim 1, it is characterized in that: the manufacture craft of described side fascia is above-mentioned side fascia raw material components to be taken raw material mix, the temperature that controls environment makes the softening mixing of raw material at 185 ~ 220 degrees centigrade, by extruding machine, raw material is expressed into and carries out cooling forming in the condensation mould and get final product.
3. a kind of closed perlite integrated heat-preservation hanging plate according to claim 1, it is characterized in that: described a kind of closed perlite integrated heat-preservation hanging plate manufacture craft is: coat fluorine carbon paint on the side fascia that makes, and then coat the dual-component polyurethane fluid sealant on side fascia, perlite is bonded on side fascia, and use 25Mpa pressure with perlite and the side fascia composition warming plate that forces together by press, and fuse through 80-100 degree celsius temperature, then warming plate is delivered into the microwave drying passage of 30 meters long by conveyer belt and dries, and get final product.
4. a kind of closed perlite integrated heat-preservation hanging plate according to claim 1, it is characterized in that: the raw material components of described side fascia is: 250 parts of pvc, 750 parts of calcium powders, 7 parts of stearic acid, 5 parts of dibutyl esters, CPE35 part, 5 parts, pe wax, 35 parts of pvc stabilizing agents, 10 parts of AC blowing agents, 25 parts of PVC foaming control agents.
5. a kind of closed perlite integrated heat-preservation hanging plate according to claim 1, it is characterized in that: the raw material components of described pearl rock stratum is: 150 parts of beads, 2.4 parts of hydrophober, 100 parts of water glass, 8 parts of silicon phosphates, 24 parts of calcium bicarbonates, 100 parts, water, 0.5 part of polypropylene, 1.5 parts of hydroxypropyl methylcelluloses.