CN103132196A - Bedding fabric with antibacterial and cool functions and post-finishing process thereof - Google Patents
Bedding fabric with antibacterial and cool functions and post-finishing process thereof Download PDFInfo
- Publication number
- CN103132196A CN103132196A CN2013100313247A CN201310031324A CN103132196A CN 103132196 A CN103132196 A CN 103132196A CN 2013100313247 A CN2013100313247 A CN 2013100313247A CN 201310031324 A CN201310031324 A CN 201310031324A CN 103132196 A CN103132196 A CN 103132196A
- Authority
- CN
- China
- Prior art keywords
- fabric
- antibiotic
- cooling function
- polyester filament
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses bedding fabric with antibacterial and cool functions and a post-finishing process thereof. The bedding fabric is formed by weaving blended yarn with antibacterial and cool functions. The blended yarn with antibacterial and cool functions is formed by blending linen fiber, chitin fiber staple and polyester filament yarn according to sirofil spinning technology. In the blended yarn with antibacterial and cool functions, the linen fiber and the chitin fiber staple are both wrapped on the surface of the polyester filament yarn. The post-finishing process includes the following steps: desizing and scouring-singeing-bleaching repeatedly through chlorine oxygen-cellulase washing-dying-washing and gentle stretching-preshrinking-finished products. The fabric finished products has cool touch, excellent antibacterial performance and good crease resistance. Compared with pure linen fabric, the fabric is soft. Simultaneously compared with chitin fabric, the fabric has a certain body and is appropriate for bedding fabric in spring and summer.
Description
Technical field
The present invention relates to a kind of bed necessaries fabric with antibiotic cooling function, belong to household textiles fabric field.
The invention still further relates to a kind of postfinishing process with bed necessaries fabric of antibiotic cooling function, belong to the rear finishing field of household textiles fabric.
Background technology
Summer, aerial temperature and humidity was large, and bacterium very easily grows, and therefore developing a kind of existing cool feeling of skin that contacts has again the bed necessaries fabric of antimicrobial health care function particularly important.Linen fibre is described as " fiber queen ", have ventilative good, the salubrious perspire of moisture absorption, antibacterial bacteriostatic, stronger natural anti-ultraviolet and excellent antistatic behaviour performance, but the degree of crystallinity of fiber is high, the degree of orientation is large, the rigidity of fiber is large, poor flexibility, therefore coherent is poor, is unfavorable for yarn strength and produces high-count yarn.Chitin fiber has antibiotic, biodegradable and good moisture retentive heat insulation function, but the chitin fiber fineness is thick, brute force is little, coefficient of friction is little, fibre cohesion is little, and spinnability is relatively poor.At present, the fabric that chitin fiber and fiber crops, cotton, viscose glue are interweaved is arranged; Mainly there are powerful lower, problem that washing shrinkage is large in it silk and chitin fiber blended fabric, these fabrics, and brute force and lower washing shrinkage that family's textile fabric is had relatively high expectations, these all fabric all can not satisfy, and there is the poor shortcoming of wrinkle resistance in pure linen fabric.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, a kind of bed necessaries fabric with antibiotic cooling function is provided, this fabric adopts the Seluofle weaving yarns of flax, chitin fiber, polyester filament to form, because the spinnability of linen fibre and chitin fiber is poor, there is the poor shortcoming of wrinkle resistance in linen fibre, and the outstanding feature of polyester filament just has high-tenacity and good rebound performance.Therefore in order to solve the poor and poor problem of wrinkle resistance of flax and chitin fiber spinnability, introduce the polyester filament fiber, utilize the Seluofle spinning technology, can produce high-count yarn, can guarantee again the brute force of yarn.Simultaneously, polyester filament is covered by the inside of chitin fiber and linen fibre, can not affect the outward appearance feel of fabric, the filoplume of Seluofle yam surface is few, and the surface is brighter and cleaner, and the fabric that is made into of yarn has nice and cool sense of touch, excellent bacteria resistance thus, good wrinkle resistance, this fabric feel is soft than pure linen fabric, has possessed again certain body bone compared with the chitin fabric simultaneously, is well suited for the bed necessaries fabric as spring and summer.
For realizing above technical purpose, the present invention takes following technical scheme:
A kind of bed necessaries fabric with antibiotic cooling function, described bed necessaries fabric adopts the blended yarn with antibiotic cooling function to weave and forms, this blended yarn with antibiotic cooling function is formed according to the blending of Seluofle spinning technique by linen fibre, chitin fiber short fiber and polyester filament, and in described blended yarn with antibiotic cooling function, linen fibre, chitin fiber short fiber all are coated on the surface of polyester filament.
In described every 100 parts of blended yarns with antibiotic cooling function, the mass fraction of linen fibre, chitin fiber short fiber and polyester filament is respectively: 30-60,20-50,20.
Another technical purpose of the present invention is to provide a kind of above-mentioned postfinishing process with bed necessaries fabric of antibiotic cooling function, comprises the following steps: destarch kiering → singe → chlorine oxygen repeatedly bleaches → cellulase washes → dye → and wash and add gentle tentering → preshrunk → finished product; In described destarch kiering operation, the working solution of employing comprises solute NaOH, Na
2SiO
3, refining agent ZTO, bleeding agent section woods and chelating agent, and NaOH, Na
2SiO
3, refining agent ZTO, bleeding agent section woods and chelating agent concentration be followed successively by 50g/ L, 3g/ L, 25g/ L, 88 2g/ L, 1 g/L, solvent is water; In the described operation of singing, the speed of a motor vehicle is at 80m/min～100m/min, and flame temperature is more than 1200 ℃; Described chlorine oxygen is repeatedly in bleaching process, comprise chlorine bleaching process, acid cleaning process and oxygen bleaching process, in the chlorine bleaching process: going out to float effective chlorine is 4g/ L～5g/ L, pH value 6.0～7.0, floats again effective chlorine and be 2g/ L～3g/ L, pH value and be 9.3～10.5, the H in acid cleaning process
2SO
4Concentration is 35g/l; In oxygen bleaching process: the working solution solute that adopts comprises 100%H
2HO
2, Na
2SiO
3, ZTO
2And NaOH, and 100%H
2HO
2, Na
2SiO
3, ZTO
2And the concentration of NaOH is followed successively by 4g/L, 4g/ L, 1 g/ L, 1 g/ L, and solvent is water; In described cellulase treatment process, process conditions are: the o.w.f value of cellulase is 1.5%, the pH value is that 4.5-5.0, temperature are 55 ℃～60 ℃, 60 minutes time; Described washing adds in gentle tentering operation, adopt the complex preparation of ZJ-G10 Hydrophilic Silicone Micro Emulsion and TK-CR50 fatty acid softening agent, and the concentration of ZJ-G10 Hydrophilic Silicone Micro Emulsion and TK-CR50 fatty acid softening agent is respectively: 10-15g/l, 10-20g/l; The process conditions of described shrinking processes are: the dewing amount be fabric heavy 20%～30% between, spray steam pressure 3kg/cm
3
According to above technical scheme, the present invention can realize following advantage:
The present invention adopts the blended yarn of linen fibre, chitin fiber and polyester filament to weave and forms, because linen fibre has natural gas permeability, hygroscopicity, salubrious property and perspire, make it become the textiles of freely breathing, the human body effective temperature is descended, be called as " natural air conditioner ", linen fibre has excellent bacteria resistance and anti-ultraviolet function simultaneously, and chitin fiber is a kind of environmental protection fiber, has excellent antibacterial functions.But there are the poor and poor problem of wrinkle resistance of spinnability in linen fibre and chitin fiber, polyester filament add the problem that has just solved powerful deficiency and creased easily.The Seluofle spinning line that contains polyester filament, flax and chitin fiber are coated on the surface of polyester filament, the fabric that is made into of yarn thus, combine the premium properties of linen fibre, chitin fiber and polyster fibre, compare with the chitin fabric and have better permeability, compare with sodolin and have good wrinkle resistance.Fabric has good antibacterial bacteriostatic function, moisture permeability, salubrious perspire, anti-ultraviolet function, and therefore the fabric that is made into of yarn is fit to use very much summer thus.
Description of drawings
Fig. 1 is the institutional framework schematic diagram of the embodiment of the present invention 1 described twill fabric;
Fig. 2 is the institutional framework schematic diagram of the described satin weave fabric of the embodiment of the present invention 2;
Wherein: being laterally weft yarn, is vertically warp thread, and grid represents to float on the interlacing point on fabric surface, and the grid of black is through interlacing point, and white grid is the latitude interlacing point.
The specific embodiment
Accompanying drawing discloses the structural representation of preferred embodiment involved in the present invention without limitation; Explain technical scheme of the present invention below with reference to accompanying drawing.
As depicted in figs. 1 and 2, the bed necessaries fabric that possesses antibiotic cooling function of the present invention, this fabric is weaved with blended yarn, and described blended yarn is mixed by linen fibre, chitin fiber and polyester filament, and yarn adopts the Seluofle spinning technology to make.
In described every 100 parts of blended yarns with antibiotic cooling function, the mass fraction of linen fibre, chitin fiber short fiber and polyester filament is respectively: 30-60,20-50,20, because flax and chitin fiber have excellent antibiotic property, and spinnability is poor, be difficult to spin the yarn of high, and the high-tenacity of polyester filament has just in time made up the two shortcoming, and such three kinds of fibers are given full play to its advantage.
Fabric tissue employing twills etc. are tissue comparatively closely.
Technological process is as follows: spinning → winder → warping → sizing → weave
Postfinishing process: destarch kiering → singe → chlorine oxygen repeatedly bleaches → cellulase washes → dye → and wash and add gentle tentering → preshrunk → finished product.
The destarch kiering: the destarch kiering can be removed residual slurries on the commensal of fiber and numb skin and cloth, improves the wettability of fabric, is convenient to absorption and the diffusion of dyestuff.Working solution forms: NaOH 50g/l; Na
2SiO
33g/l; Refining agent ZTO 25g/l; Woods 88 2g/l of bleeding agent section; Phosphoric acid salt chelating agent 1 g/l.
Singe: the cohesive force of linen fibre is poor, and fiber easily stretches out the yarn surface, and the operation of singing is mainly to remove the purpose of fiber crops grain, and the speed of a motor vehicle is at 80m/min～100m/min, and flame temperature is more than 1200 ℃.
Chlorine oxygen is repeatedly bleached: flax whiteness is not high, and the bleaching main purpose is to improve whiteness and remove impurity.Process route is: just float-float again-oxygen floats.Just float: effective chlorine 4g/l～5g/l, pH value 6.0～7.0; Float again: effective chlorine 2g/l～3g/l, pH value 9.3～10.5, pickling H
2SO
435g/l.Oxygen floats: 100%H
2O
24g/l, Na
2SiO
34g/l; ZTO
21 g/l, NaOH 1 g/l.
Cellulase is processed: this technique main purpose is to make the hydrolysis of fabric face fine hair, reduces prodding and itching feeling, and fabric feeling is more soft.Process conditions: cellulase o.w.f 1.5%, pH value 4.5-5.0,55 ℃～60 ℃ of temperature, 60 minutes time.
Washing adds gentle tentering: water-washing method by machinery rub, rubbing makes fabric fluffy soft at a certain temperature.Adopt silicone softening agent and fatty acid formulation of softener, in the application, adopt the complex preparation of ZJ-G10 Hydrophilic Silicone Micro Emulsion and TK-CR50 fatty acid softening agent, and the concentration of ZJ-G10 Hydrophilic Silicone Micro Emulsion and TK-CR50 fatty acid softening agent is respectively: 10-15g/l, 10-20g/l; Make fabric feeling smooth, reduce prodding and itching feeling.
Preshrunk: the main purpose of preshrunk is to make cloth cover soft plentiful, the dewing amount be fabric heavy 20%～30% between, spray steam pressure 3kg/cm
3
By above operation, make meet a textile fabric soft, have the antibacterial bacteriostatic functional fabric without prodding and itching feeling.
Embodiment 1
Specification: (flax 30%+ chitin fiber 50%+ polyester filament 20%) 40S*(flax 30%+ chitin fiber 50%+ polyester filament 20%) 40S/133*76, door width 250cm, twill-weave once on two, organization chart is as shown in Figure 1.
Embodiment 2
Specification: (flax 45%+ chitin fiber 35%+ polyester filament 20%) 60S*(flax 45%+ chitin fiber 35%+ polyester filament 20%) 60S/182*120, door width 250cm, florentine drill tissue, organization chart are as shown in Figure 2.
Embodiment 3
Specification: (flax 60%+ chitin fiber 20%+ polyester filament 20%) 60S*(flax 60%+ chitin fiber 20%+ polyester filament 20%) 60S/182*120, door width 250cm, florentine drill tissue, organization chart are as shown in Figure 2.
The technology path of Seluofle spinning: flax and chitin fiber are carried out the rove that blending becomes feed fine spining machine from rear roller, polyester filament is fed fine spining machine from front roller, mix with polyester filament after drawing-off at front roller chitin fiber rove, and and front roller grip and to keep a fixed range between point, thereby the formation twist triangle zone forms the Seluofle composite yarn together after twisting.The long filament of Seluofle spinning is without draw zone, but directly feeds from front roller, and its feeding route is: lever jack → twizzle → anti-bouncing device → tension controller → yarn guiding wheel → front roller nip.The concrete technology parameter is: the blended roving of Spinning Draft Zone chitin fiber and linen fibre and the spacing of polyester filament are at 2-13mm; Twist factor is at 300-400; Thread-tension 12-15g; The total draft multiple is at 18-22; Back zone drafting multiple is at 1.2-1.5; Ingot speed 4500r/min; Front roller rotating speed 80r/min; Steel traveler weight is 0.09g, front middle roller centre-to-centre spacing 78mm, front and back ratch 132 mm.
Wherein, the process of roving of flax and chitin fiber blended is: opening picking → comb and parallel cotton fibers prior to spinning → drafting → rove.
The opening and cleaning step major parameter: comprehensive Beater Speed is 900r/min; The rolling fan speed is 1200r/min; The lap roller rotating speed is 8.2r/min; Space between pedal roller and comprehensive hired roughneck and be 10mm; Cotton rolling quantity is 437g/m; Lap length is 31.4m.
The carding step major parameter: the cylinder rotating speed is 330r/min; Licker-in speed is 980r/min; Cover plate speed is 162mm/min; Doffer speed is 18.9r/min; Feed plate and licker-in space and are 0.3mm; 5, cover plate and cylinder space and are 0.38mm, 0.36mm, 0.36mm, 0.36mm, 0.38mm; The mote knife height is-0.3mm, 95 ℃ of the mote knife knife back and horizontal line angles; Licker-in and little bottom drain (import * outlet) are spaced and are 0.8mm * 1.2mm; Weight of card sliver is 23.5g/5m.
Drafting: and the Process configuration that adopts 6, two road and close when closing, drawing-off divide mix adopt head and drawing-off is large, two and the little technique of drawing-off.Head and drafting multiple be 6.549, two and drafting multiple be 6.293, other are also identical with two also technological parameters: drafting radical 6; First break draft multiple 1.617; Roller gauge 10 * 20; Roller pressurization 32 * 6 * 35 * 32; Adjustable ring diameter 14mm; Loudspeaker diameter 3.2mm; Do quantitative 18.5g/5m; Sliver exporting speed 148m/min.
Rove: the total draft multiple is 7.609 times; The first break draft multiple is 1.33 times; Roller gauge is 26mm * 34mm; Nip gauge is 6.5mm; Twist factor is 113; Doing quantitatively is 4.72g/10m; Front roller speed is 130r/min.
Claims (3)
1. bed necessaries fabric with antibiotic cooling function, it is characterized in that, described bed necessaries fabric adopts the blended yarn with antibiotic cooling function to weave and forms, this blended yarn with antibiotic cooling function is formed according to the blending of Seluofle spinning technique by linen fibre, chitin fiber short fiber and polyester filament, and in described blended yarn with antibiotic cooling function, linen fibre, chitin fiber short fiber all are coated on the surface of polyester filament.
2. the bed necessaries fabric that has according to claim 1 antibiotic cooling function, it is characterized in that, in described every 100 parts of blended yarns with antibiotic cooling function, the mass fraction of linen fibre, chitin fiber short fiber and polyester filament is respectively: 30-60,20-50,20.
3. the described postfinishing process with bed necessaries fabric of antibiotic cooling function of claim 1, is characterized in that, comprises the following steps: destarch kiering → singe → chlorine oxygen repeatedly bleaches → cellulase washes → dye → and wash and add gentle tentering → preshrunk → finished product; In described destarch kiering operation, the working solution of employing comprises solute NaOH, Na
2SiO
3, refining agent ZTO, bleeding agent section woods and chelating agent, and NaOH, Na
2SiO
3, refining agent ZTO, bleeding agent section woods and chelating agent concentration be followed successively by 50g/ L, 3g/ L, 25g/ L, 88 2g/ L, 1 g/L, solvent is water; In the described operation of singing, the speed of a motor vehicle is at 80m/min～100m/min, and flame temperature is more than 1200 ℃; Described chlorine oxygen is repeatedly in bleaching process, comprise chlorine bleaching process, acid cleaning process and oxygen bleaching process, in the chlorine bleaching process: going out to float effective chlorine is 4g/ L～5g/ L, pH value 6.0～7.0, floats again effective chlorine and be 2g/ L～3g/ L, pH value and be 9.3～10.5, the H in acid cleaning process
2SO
4Concentration is 35g/l; In oxygen bleaching process: the working solution solute that adopts comprises 100%H
2HO
2, Na
2SiO
3, ZTO
2And NaOH, and 100%H
2HO
2, Na
2SiO
3, ZTO
2And the concentration of NaOH is followed successively by 4g/L, 4g/ L, 1 g/ L, 1 g/ L, and solvent is water; In described cellulase treatment process, process conditions are: the o.w.f value of cellulase is 1.5%, the pH value is that 4.5-5.0, temperature are 55 ℃～60 ℃, 60 minutes time; Described washing adds in gentle tentering operation, adopt the complex preparation of ZJ-G10 Hydrophilic Silicone Micro Emulsion and TK-CR50 fatty acid softening agent, and the concentration of ZJ-G10 Hydrophilic Silicone Micro Emulsion and TK-CR50 fatty acid softening agent is respectively: 10-15g/l, 10-20g/l; The process conditions of described shrinking processes are: the dewing amount be fabric heavy 20%～30% between, spray steam pressure 3kg/cm
3