CN103085146A - Method for manufacturing blue and white porcelain staircase - Google Patents
Method for manufacturing blue and white porcelain staircase Download PDFInfo
- Publication number
- CN103085146A CN103085146A CN2011103505856A CN201110350585A CN103085146A CN 103085146 A CN103085146 A CN 103085146A CN 2011103505856 A CN2011103505856 A CN 2011103505856A CN 201110350585 A CN201110350585 A CN 201110350585A CN 103085146 A CN103085146 A CN 103085146A
- Authority
- CN
- China
- Prior art keywords
- idiosome
- blue
- ultraviolet light
- paint
- white porcelain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A method for manufacturing a blue and white porcelain staircase comprises the following steps: step a, selecting the blue and white porcelain process to manufacture a blank body, and performing first grinding and dust removal treatment on the blank body; manufacturing a tread plate, a vertical plate, a stand column, a handrail, a crossbeam and a samson post, wherein at least the vertical plate and the stand column are selected to manufacture the blank body through the blue and white porcelain process; and performing mechanical or manual sanding and dust removal on the blank body. The method for manufacturing the blue and white porcelain staircase has the advantages that a paint film gradually enters into wood fibers layer by layer and is performed with high-temperature ultraviolet light polymerization, the paint surface is strong in adhesive force, the paint film is high in hardness and has strong abrasion resistance and scraping resistance, a layer of porcelain glaze paint surface which is solid in texture and clear in color is formed on the paint surface, the paint film is full and smooth and enough in light sensation, presents blue and white porcelain like natural innervation and texture, and the blue and white porcelain staircase is strong in porcelain texture, obvious in three-dimensional color, rich in layering, capable of resisting ultraviolet radiation and not apt to fade.
Description
Technical field
The present invention relates to the stair manufacture technology field, especially relate to a kind of preparation method of blue and white porcelain Wooden stair.
Background technology
No matter Wooden stair is at residence, house, office space, or all be subject to liking of more and more people in the decorations of used by hotels and restaurants by, especially in the decorations of high-grade compound apartment and villa, generally adopted especially, Wooden stair is not only serious elegant, noble generous, and more meets the Times ' Demand that people get close to nature, raising quality of the life and taste.Yet, be accompanied by the aggravation of product homogeneity degree, and the daytime of international competition, the competitive advantage of the domestic stair product of China more and more is in weak state, color and pattern single, and traditional old stuff of manufacture craft, the person's that is difficult to satisfy the top-grade consumption demand is the Main Bottleneck of restriction China stair industry development.
In view of the above problems, this case inventor adopts Chinese distinctive blue and white porcelain technology to make riser and the column of Wooden stair, reaches fresh and new effect on the stair color, also than traditional stair, largely raising is arranged on the rub proofness of use.
Summary of the invention
The present invention is to provide a kind of preparation method of in bright gay color blue and white porcelain Wooden stair for solving the problems of the technologies described above.
Technical problem solved by the invention realizes by the following technical solutions:
A kind of preparation method of blue and white porcelain Wooden stair, the method comprises the steps:
Step a, selection blue and white porcelain technology are made idiosome, and described idiosome is carried out first polishing, dust removal process;
Make tread, riser, column, handrail, crossbeam and kingpost, wherein, select at least described riser and described column to make idiosome as blue and white porcelain technology, and described idiosome is carried out machinery or manual sanding, and dust removal process.
1, sanding:
Use 180～240 purpose emery wheel or sand paper, polishing is repeatedly carried out on the idiosome surface, remove spot, burr and oil stain, make its any surface finish.
2, dedusting:
After sanding finishes, use the dried compressed air jet gun of pressure more than 0.3Mpa, take first reverse forward more alternately to purge the mode on described idiosome surface, carry out dust removal process, avoid dust adhesion in described idiosome surface, when purging, 10mm～30mm apart between jet gun and described idiosome surface keeps 15 °～60 ° inclination angles.
Step b, coat the UV putty layer for described idiosome surface;
The UV putty that stirs is coated with is formed on described idiosome surface, and to utilize temperature be that the ultraviolet light of 160～180 millijoules carries out the half-dried curing of moment ultraviolet light to being coated with the described idiosome that is shaped with UV putty.
Wherein, the method that coats UV putty comprises mechanical roller coat and showering, and the time of the half-dried curing of UV putty moment ultraviolet light is≤3 seconds, and the consumption of described UV putty is every square metre of 20～30 gram.
Step c, upper UV priming paint;
Effects on surface scribbles the described idiosome of the half-dried UV curing putty of ultraviolet light, coat UV priming paint, again carry out with being coated with the described idiosome that is shaped with UV priming paint the half-dried curing of ultraviolet light that temperature is 160～180 millijoules, again coat UV priming paint after the half-dried curing of ultraviolet light, coat the laggard trip temperature of UV priming paint at 100～220 millijoules, amount of radiation is solidization of ultraviolet light of 65～120mj/ square meter.
Wherein, the consumption of each UV priming paint is every square metre of 20～40 gram, overall consumption≤200 grams.
Steps d, idiosome is carried out second polishing dust removal process;
To the described idiosome surface that scribbles the dried UV curing priming paint of ultraviolet light again polish, dedusting, the processing of filling a vacancy.
Utilize oil abrasion equipment to carry out sanding again to described idiosome surface, utilize equally jet gun to carry out dust removal process again, check correction of the defect after dust removal process.
Step e, upper UV finish paint;
Will be through the described idiosome after oil abrasion equipment and jet gun grinding process after standing 20～30 minutes, utilize roller coat or showering method to coat the UV finish paint to described idiosome surface, and utilize temperature at 100～250 millijoules, amount of radiation is that the ultraviolet light of 65～150mj/ square meter carry out solidization to described UV finish paint.Wherein, the consumption of UV finish paint is every square metre of≤200 gram.
Step f, Freehandhand-drawing bottoming;
The described idiosome that scribbles the UV finish paint is standing more than 8 hours, after again purging described idiosome surface with jet gun, carry out pencil Freehandhand-drawing bottoming.
Step g, conditioned pigment and colouring;
Mix well mixing according to the ratio of 1: 2.5 between zapon and diluent, paint and push away rhythm to desirable effect with writing brush.
Step h, the fixation of spraying paint;
After standing 7～8 hours of described idiosome after colouring is completed, its surperficial spray one deck paint is carried out fixation, the consumption of institute's spray paint is every square metre of≤200 gram, has reached good anti-oxidation purpose.
Step I, polishing and the fixation of again spraying paint;
Effects on surface is sprayed with the described idiosome of fixation paint and polishes for the last time, realize to eliminate by fixation bubbling or the out-of-flatness of condensing and being caused, and after polishing, the paint of spray fixation is again carried out on the surface of described idiosome, and utilize temperature at 100～250 millijoules, amount of radiation is that the ultraviolet light of 65～150mj/ square meter carries out solidization to desirable state to described fixation paint.
The beneficial effect that the present invention has is: make paint film successively go deep into wood-fibred inside by this method, and through the high temperature ultraviolet light polymerization, lacquer painting strong adhesion, hardness of paint film are high, have stronger wearability and scraping and wiping resistance performance, form the clear enamel lacquer painting of the hard look of one deck matter at painted surface, its paint film is full, smooth, and light sensation is pure, present natural innervation and texture as blue and white porcelain, porcelain texture is strong, and three-dimensional color is obvious, and stereovision is abundant, and uvioresistant is difficult for fading.
Description of drawings
Fig. 1 is the present invention: a kind of schematic flow sheet of preparation method of blue and white porcelain Wooden stair.
The specific embodiment
For technological means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, below in conjunction with concrete diagram, further set forth the present invention.
With reference to shown in Figure 1, technical problem solved by the invention realizes by the following technical solutions:
A kind of preparation method of blue and white porcelain Wooden stair, the method comprises the steps:
Step a, selection blue and white porcelain technology are made idiosome, and described idiosome is carried out first polishing, dust removal process;
Make tread, riser, column, handrail, crossbeam and kingpost, wherein, select at least described riser and described column to make idiosome as blue and white porcelain technology, and described idiosome is carried out machinery or manual sanding, and dust removal process.
1, sanding:
Use 180～240 purpose emery wheel or sand paper, polishing is repeatedly carried out on the idiosome surface, remove spot, burr and oil stain, make its any surface finish.
2, dedusting:
After sanding finishes, use the dried compressed air jet gun of pressure more than 0.3Mpa, take first reverse forward more alternately to purge the mode on described idiosome surface, carry out dust removal process, avoid dust adhesion in described idiosome surface, when purging, 10mm～30mm apart between jet gun and described idiosome surface keeps 15 °～60 ° inclination angles.
Step b, coat the UV putty layer for described idiosome surface;
The UV putty that stirs is coated with is formed on described idiosome surface, and to utilize temperature be that the ultraviolet light of 160～180 millijoules carries out the half-dried curing of moment ultraviolet light to being coated with the described idiosome that is shaped with UV putty.
Wherein, the method that coats UV putty comprises mechanical roller coat and showering, and the time of the half-dried curing of UV putty moment ultraviolet light is≤3 seconds, and the consumption of described UV putty is every square metre of 20～30 gram.
Step c, upper UV priming paint;
Effects on surface scribbles the described idiosome of the half-dried UV curing putty of ultraviolet light, coat UV priming paint, again carry out with being coated with the described idiosome that is shaped with UV priming paint the half-dried curing of ultraviolet light that temperature is 160～180 millijoules, again coat UV priming paint after the half-dried curing of ultraviolet light, coat the laggard trip temperature of UV priming paint at 100～220 millijoules, amount of radiation is solidization of ultraviolet light of 65～120mj/ square meter.
Wherein, the consumption of each UV priming paint is every square metre of 20～40 gram, overall consumption≤200 grams.
Steps d, idiosome is carried out second polishing dust removal process;
To the described idiosome surface that scribbles the dried UV curing priming paint of ultraviolet light again polish, dedusting, the processing of filling a vacancy.
Utilize oil abrasion equipment to carry out sanding again to described idiosome surface, utilize equally jet gun to carry out dust removal process again, check correction of the defect after dust removal process.
Step e, upper UV finish paint;
Will be through the described idiosome after oil abrasion equipment and jet gun grinding process after standing 20～30 minutes, utilize roller coat or showering method to coat the UV finish paint to described idiosome surface, and utilize temperature at 100～250 millijoules, amount of radiation is that the ultraviolet light of 65～150mj/ square meter carry out solidization to described UV finish paint.Wherein, the consumption of UV finish paint is every square metre of≤200 gram.
Step f, Freehandhand-drawing bottoming;
The described idiosome that scribbles the UV finish paint is standing more than 8 hours, after again purging described idiosome surface with jet gun, carry out pencil Freehandhand-drawing bottoming.
Step g, conditioned pigment and colouring;
Mix well mixing according to the ratio of 1: 2.5 between zapon and diluent, paint and push away rhythm to desirable effect with writing brush.
Step h, the fixation of spraying paint;
After standing 7～8 hours of described idiosome after colouring is completed, its surperficial spray one deck paint is carried out fixation, the consumption of institute's spray paint is every square metre of≤200 gram, has reached good anti-oxidation purpose.
Step I, polishing and the fixation of again spraying paint;
Effects on surface is sprayed with the described idiosome of fixation paint and polishes for the last time, realize to eliminate by fixation bubbling or the out-of-flatness of condensing and being caused, and after polishing, the paint of spray fixation is again carried out on the surface of described idiosome, and utilize temperature at 100～250 millijoules, amount of radiation is that the ultraviolet light of 65～150mj/ square meter carries out solidization to desirable state to described fixation paint.
Above demonstration and described basic principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; that describes in above-described embodiment and specification just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (7)
1. the preparation method of a blue and white porcelain Wooden stair, the method comprises the steps:
Step a, selection blue and white porcelain technology are made idiosome, and described idiosome is carried out first polishing, dust removal process;
Step b, for described idiosome surface coats the UV putty layer that every square metre of consumption is 20～30 grams, and described UV putty layer is carried out the half-dried curing of ultraviolet light;
Step c, effects on surface scribble the described idiosome of the half-dried UV curing putty of ultraviolet light, coat UV priming paint, the half-dried curing of ultraviolet light, again coat UV priming paint, solidization of ultraviolet light;
Steps d, utilize oil abrasion equipment and jet gun to carry out second polishing dust removal process to described idiosome;
Step e, will be through the described idiosome after oil abrasion equipment and jet gun grinding process after standing 20～30 minutes, utilize roller coat or showering method to coat the UV finish paint to described idiosome surface, and with solidization of ultraviolet light;
Step f, the described idiosome that will scribble the UV finish paint are standing more than 8 hours, after again purging described idiosome surface with jet gun, carry out pencil Freehandhand-drawing bottoming;
Step g, mix well mixing according to the ratio of 1: 2.5 between zapon and diluent, paint with writing brush;
Step h, the described idiosome after colouring is completed carry out fixation to its surperficial spray one deck paint after standing 7～8 hours;
The paint of spray fixation again after the described idiosome that step I, effects on surface are sprayed with fixation paint is polished for the last time, purged, and carry out last solidization with ultraviolet light.
2. the preparation method of a kind of blue and white porcelain Wooden stair according to claim 1, is characterized in that;
Blue and white porcelain technology described in step a is made idiosome and is comprised tread, riser, column, handrail, crossbeam and kingpost;
Described in step a, idiosome being carried out machinery or manual sanding, is to use 180～240 purpose emery wheel or sand paper, and polishing is repeatedly carried out on the idiosome surface, goes spot, flash removed and oil stain to make the processing of its any surface finish;
Described in step a, idiosome is carried out dust removal process, after sanding finishes, use the dried compressed air jet gun of pressure more than 0.3Mpa, take first oppositely again forward alternately to purge described idiosome surface, and when purging, at a distance of 10mm～30mm, keep 15 °～60 ° inclination angles between jet gun and described idiosome surface.
3. the preparation method of a kind of blue and white porcelain Wooden stair according to claim 1, is characterized in that;
The method that coats UV putty described in step b comprises mechanical roller coat and showering;
The time of the half-dried curing of UV putty moment ultraviolet light is≤3 seconds;
During the half-dried UV curing putty of moment ultraviolet light, the temperature of ultraviolet light is 160～180 millijoules.
4. the preparation method of a kind of blue and white porcelain Wooden stair according to claim 3 is characterized in that:
The described idiosome of twice couple described in step c coats UV priming paint, and wherein the consumption of each UV priming paint is every square metre of 20～40 gram, overall consumption≤200 grams;
During the half-dried curing of ultraviolet light, its temperature is 160～180 millijoules;
During solidization of ultraviolet light, its temperature is 100～220 millijoules, and amount of radiation is 65～120mj/ square meter.
5. the preparation method of a kind of blue and white porcelain Wooden stair according to claim 1, is characterized in that;
The consumption of the UV finish paint described in step e is every square metre of≤200 gram;
When described UV finish paint is carried out solidization, the temperature of ultraviolet light is 100～250 millijoules.
6. the preparation method of a kind of blue and white porcelain Wooden stair according to claim 1, is characterized in that;
The consumption of the fixation paint described in step h is every square metre of≤200 gram.
7. the preparation method of a kind of blue and white porcelain Wooden stair according to claim 1, is characterized in that;
Temperature during last solidization of ultraviolet light described in step I is at 100～250 millijoules, and amount of radiation is 65～150mj/ square meter.